JPH08262208A - Light reflecting body and light reflector using the same - Google Patents
Light reflecting body and light reflector using the sameInfo
- Publication number
- JPH08262208A JPH08262208A JP8011098A JP1109896A JPH08262208A JP H08262208 A JPH08262208 A JP H08262208A JP 8011098 A JP8011098 A JP 8011098A JP 1109896 A JP1109896 A JP 1109896A JP H08262208 A JPH08262208 A JP H08262208A
- Authority
- JP
- Japan
- Prior art keywords
- light
- protective layer
- light reflector
- sheet
- porous resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は光反射体及び光反射
装置に関する。さらに詳しくは、高い光反射効率を有す
る多孔性樹脂シートの少なくとも片表面に保護層が積層
され、耐光性、光反射率及び／又は形態保持性が改良さ
れた光反射体、及び該光反射体を使用した光反射装置に
関する。本発明に係わる光反射体及び光反射装置は、主
としてワードプロセッサー、パーソナルコンピュータ、
テレビジョン等の液晶表示装置のバックライトユニッ
ト、照明器具、複写機、プロジェクター方式のディスプ
レイ、ファクシミリ、電子黒板等に使用される光反射体
または光反射装置として適する。TECHNICAL FIELD The present invention relates to a light reflector and a light reflecting device. More specifically, a protective layer is laminated on at least one surface of a porous resin sheet having high light reflection efficiency, and the light reflector has improved light resistance, light reflectance and / or shape retention, and the light reflector. The present invention relates to a light reflecting device. The light reflector and the light reflecting device according to the present invention are mainly used in word processors, personal computers,
It is suitable as a light reflector or a light reflector used in a backlight unit of a liquid crystal display device such as a television, a lighting fixture, a copying machine, a display of a projector system, a facsimile, an electronic blackboard and the like.
【０００２】[0002]
【従来の技術】近年、光反射体は様々な分野で用いられ
てきており、特に、ワードプロセッサー、パーソナルコ
ンピュータ、テレビジョン等の液晶表示装置の主要部品
として数多く使用されている。液晶表示装置は、薄型で
省電力が図り得るものであることが重要である。また、
液晶表示装置の大面積化、表示品位の向上が望まれてお
り、この為には大容量の光量を液晶部分に供給すること
が必要とされる。液晶表示装置の省電力化を可能とし、
小型化、薄型化を図り、且つバックライトユニットから
供給される光量を多くするためには、光反射体の光反射
効率が高くなければならず、高輝度が得られる光反射体
が要求されている。2. Description of the Related Art In recent years, light reflectors have been used in various fields, and in particular, many are used as main parts of liquid crystal display devices such as word processors, personal computers, and televisions. It is important that the liquid crystal display device is thin and can save power. Also,
It is desired to increase the area of the liquid crystal display device and improve the display quality, and for this purpose, it is necessary to supply a large amount of light to the liquid crystal portion. Enables power saving of liquid crystal display devices,
In order to reduce the size and thickness and increase the amount of light supplied from the backlight unit, the light reflection efficiency of the light reflector must be high, and a light reflector that can obtain high brightness is required. There is.
【０００３】液晶表示装置のバックライトユニットに
は、光源を直接液晶部の下部に置く方式と、光源を透明
な導光板の横に置く方式がある。液晶表示装置を薄型化
するためには後者の方式が適している。後者の方式の問
題点は、導光板を経由する光の一部を液晶部に伝え、更
に導光板を経由する光の残部を光反射体で反射せしめて
再び導光板に戻して光を有効に利用するものであるた
め、導光板と光反射体の間の光の漏れや、導光板、光反
射体による光の吸収等により、直接光源を液晶部の後部
に置く方式よりも液晶部に伝わる光量が少なくなること
である。In the backlight unit of the liquid crystal display device, there are a method in which the light source is directly placed under the liquid crystal portion and a method in which the light source is placed next to the transparent light guide plate. The latter method is suitable for thinning the liquid crystal display device. The problem with the latter method is that part of the light that passes through the light guide plate is transmitted to the liquid crystal part, and the rest of the light that passes through the light guide plate is reflected by a light reflector and returned to the light guide plate again to make the light effective. Since it is used, light is transmitted to the liquid crystal part rather than directly placed in the rear part of the liquid crystal part due to light leakage between the light guide plate and the light reflector and absorption of light by the light guide plate and the light reflector. The amount of light is reduced.
【０００４】後者の方式では、光反射体がランプホルダ
ー部及び導光板下部の二箇所に配設される。ランプホル
ダー部の光反射体は、光の吸収及びリーク電流の発生が
あると液晶表示部へ供給される光量が少なくなる。従っ
て、導光板の横に配設されるランプホルダーの素材は、
光の反射効率が高く、且つ電気絶縁性の高いものが求め
られている。また、導光板の下に置く光反射体は、光線
の反射率がより高く、透過率の低いものが要求される。In the latter method, the light reflectors are arranged at two places, that is, the lamp holder part and the lower part of the light guide plate. The light reflector of the lamp holder part reduces the amount of light supplied to the liquid crystal display part when light is absorbed and a leak current is generated. Therefore, the material of the lamp holder arranged next to the light guide plate is
What has high light reflection efficiency and high electric insulation is required. Further, the light reflector placed under the light guide plate is required to have a higher reflectance of light rays and a lower transmittance.
【０００５】また、液晶表示面のカラー化や大型化が望
まれており、さらに液晶の表示品位を向上させる必要が
でてきており、この要望に応えるためにも、液晶表示装
置に用いるバックライトには少しでも多くの光を液晶部
に供給することが求められている。Further, there is a demand for colorization and size increase of the liquid crystal display surface, and it is necessary to further improve the display quality of the liquid crystal. In order to meet this demand, a backlight used in a liquid crystal display device. Is required to supply as much light as possible to the liquid crystal part.
【０００６】上記の課題に応えるため、種々の光反射シ
ート等が提案されている。例えば、特開昭６３−１６１
０２９号公報には、ポリエチレンテレフタレートに微粒
子状炭酸カルシウムを５〜３０重量％含有させたポリマ
ーチップを溶融押出し、二軸延伸したフィルムであっ
て、該ポリマーチップの白色度をａ％、二軸延伸後のフ
ィルムのボイド率をｂ％としたとき、ａ≧４５、７≦ｂ
≦３０、ａｌｏｇｂ≧６５を満足することを特徴とする
白色ポリエチレンテレフタレートフィルムが開示されて
いる。In order to meet the above problems, various light reflecting sheets and the like have been proposed. For example, JP-A-63-161
No. 029 discloses a film obtained by melt-extruding a polymer chip containing polyethylene terephthalate containing 5 to 30 wt% of particulate calcium carbonate and biaxially stretching the whiteness of the polymer chip is a%, and the biaxially stretching film. When the void ratio of the subsequent film is b%, a ≧ 45, 7 ≦ b
A white polyethylene terephthalate film characterized by satisfying ≦ 30 and alogb ≧ 65 is disclosed.
【０００７】該白色ポリエチレンテレフタレートフィル
ムは、微粒子状炭酸カルシウムの含有量が最大でも３０
重量％であり少ない。そのため、二軸延伸後のフィルム
のボイド率が最大でも３０％であり、光反射率が低い。
従って、該白色ポリエチレンテレフタレートフィルム
は、光反射体としては満足し得るものではない。The white polyethylene terephthalate film has a maximum content of particulate calcium carbonate of 30.
It is a small percentage by weight. Therefore, the void ratio of the film after biaxial stretching is at most 30%, and the light reflectance is low.
Therefore, the white polyethylene terephthalate film is not satisfactory as a light reflector.
【０００８】特開平５−２２９０５３号公報には、合成
樹脂フィルムの表面に金属薄膜層を有する光反射フィル
ムと、充填剤を含む合成樹脂フィルムを少なくとも一軸
方向に延伸されてなる光散乱フィルムとを、積層してな
る光反射体が開示されている。そして、上記金属薄膜層
として、銀または銀を含む合金等が好ましく用いられる
ことが記載されている。該光反射体は、銀等の金属薄膜
層を有する合成樹脂フィルムを光反射フィルムとし、且
つ、多孔性樹脂シートを光散乱フィルムとするため、高
い光反射効率を有する優れた光反射体である。JP-A-5-229053 discloses a light-reflecting film having a metal thin film layer on the surface of a synthetic resin film, and a light-scattering film obtained by stretching a synthetic resin film containing a filler in at least one axial direction. , A laminated light reflector is disclosed. It is described that silver or an alloy containing silver is preferably used as the metal thin film layer. The light reflector is an excellent light reflector having high light reflection efficiency because it uses a synthetic resin film having a metal thin film layer of silver or the like as a light reflection film and uses a porous resin sheet as a light scattering film. .
【０００９】しかし、該光反射体は、紫外線等に対する
耐光性の点で必ずしも満足し得るものとはいえない。ま
た、光散乱フィルムである多孔性樹脂シートに傷が付い
た場合に電気絶縁性が低下し、例えば、これを液晶表示
装置のバックライト部の光反射用部材として用いた場
合、リーク電流が発生し、消費電力が過大となることが
ある。また、導光板下の光反射シートとして用いた場合
は、金属薄膜層が入射光を正反射するため、光散乱フィ
ルムに傷が付いた場合には、傷が付いた箇所から正射し
た部分の表示部のみが特に明るくなり、他の部分が暗く
なるため、映像画面上に輝度ムラが発生する可能性があ
る。However, the light reflector is not always satisfactory in light resistance to ultraviolet rays and the like. In addition, when the porous resin sheet that is the light scattering film is scratched, the electrical insulation is deteriorated, and for example, when this is used as a light reflecting member of the backlight section of a liquid crystal display device, a leak current occurs. However, the power consumption may become excessive. Also, when used as a light reflection sheet under the light guide plate, the metal thin film layer specularly reflects the incident light. Since only the display portion becomes particularly bright and the other portions become dark, there is a possibility that luminance unevenness may occur on the video screen.
【００１０】また、二酸化チタン等の白色の無機充填剤
等を含有する白色ポリエチレンテレフタレートシートを
光反射板として用いる試みもある。There is also an attempt to use a white polyethylene terephthalate sheet containing a white inorganic filler such as titanium dioxide as a light reflecting plate.
【００１１】最近、液晶表示装置の消費電力、小型化等
で表示装置の光源として使用する蛍光灯が小型化し、ま
たランプホルダーが細くなる傾向にある。Recently, due to the power consumption and size reduction of liquid crystal display devices, fluorescent lamps used as light sources for display devices are becoming smaller and the lamp holders are becoming thinner.
【００１２】もし白色ポリエチレンテレフタレートフィ
ルムを曲がったランプホルダーとして使用すると剛性が
大きすぎてランプホルダーが不規則な形状になり、ラン
プホルダーが不規則な構造のために液晶表示装置の透明
な導光板に光を効率的に当てることができにくくなる欠
点が生じる。この欠点を解消するために、白色ポリエチ
レンテレフタレートシートの厚みを薄くする試みがなさ
れているが、該シートを透過する光が多くなり、その結
果、光の反射効率が低下するという新たな問題が生じて
いる。If a white polyethylene terephthalate film is used as a curved lamp holder, the rigidity is too high and the lamp holder has an irregular shape. Due to the irregular structure of the lamp holder, it becomes a transparent light guide plate of a liquid crystal display device. There is a drawback that it is difficult to efficiently apply light. In order to solve this drawback, attempts have been made to reduce the thickness of the white polyethylene terephthalate sheet, but the amount of light transmitted through the sheet increases, and as a result, a new problem occurs that the light reflection efficiency decreases. ing.
【００１３】特開平２−１３９２５号公報には、表面に
白色塗料が塗布されたアルミニウム等の金属板が記載さ
れており、該金属板が光反射体として用いられている。
しかし、該金属板は電気の良導体であり、光源からの誘
導電流によるリーク電流が発生し発光効率が低い欠点が
ある。Japanese Unexamined Patent Publication No. 2-13925 describes a metal plate such as aluminum whose surface is coated with white paint, and the metal plate is used as a light reflector.
However, since the metal plate is a good conductor of electricity, there is a drawback in that a leak current is generated by an induced current from the light source and the luminous efficiency is low.
【００１４】また、特開平４−２３２５４０号公報に
は、２〜２５重量％のポリオレフィンを含有するポリエ
ステルフィルムを延伸した多孔性フィルム、及び、多孔
性フィルムと、５〜２５重量％の無機粒子を含有するポ
リエステルフィルムを延伸した多孔性フィルムを積層し
た白色ポリエステルフィルムが開示されている。Further, in Japanese Patent Application Laid-Open No. 4-232540, a porous film obtained by stretching a polyester film containing 2 to 25% by weight of a polyolefin, and a porous film and 5 to 25% by weight of inorganic particles are described. A white polyester film in which a porous film obtained by stretching a contained polyester film is laminated is disclosed.
【００１５】そして、実施例には、該白色ポリエステル
フィルムの好ましい態様として、基材樹脂としてポリエ
チレンテレフタレートを用いた厚みが１８８μｍである
白色多孔性フィルムが記載されている。しかし、該多孔
性フィルムは、基材樹脂がポリエチレンテレフタレート
等のポリエステルであるため、剛性が大きい。そのた
め、例えば、これを液晶表示装置のランプホルダー等と
して使用した場合、剛性が大きすぎてランプホルダーが
不規則な形状になり、液晶表示装置の導光板に光を効果
的に照射することができ難くなる恐れがある。In the examples, a white porous film having a thickness of 188 μm and using polyethylene terephthalate as a base resin is described as a preferred embodiment of the white polyester film. However, the porous film has high rigidity because the base resin is polyester such as polyethylene terephthalate. Therefore, for example, when this is used as a lamp holder of a liquid crystal display device, the rigidity is too large and the lamp holder has an irregular shape, and the light guide plate of the liquid crystal display device can be effectively irradiated with light. It can be difficult.
【００１６】また、導光板下の光反射シートとして使用
した場合、単層の場合には無機粒子が全く充填されてい
ないため、あるいは、多層の場合にでも無機粒子の量が
５〜２５重量％と少ないため、無機粒子による光の反射
が極めて少なく、高反射率が得られない。When used as a light reflecting sheet under a light guide plate, the inorganic particles are not filled at all in the case of a single layer, or even in the case of a multilayer, the amount of the inorganic particles is 5 to 25% by weight. Therefore, the reflection of light by the inorganic particles is extremely small, and high reflectance cannot be obtained.
【００１７】また、特開平６−２９８９５７号公報に
は、屈折率が１．６未満である樹脂と７５〜２５重量部
と無機充填剤２５〜７５重量部からなる樹脂組成物を面
積延伸倍率１．２〜１５倍に延伸してなる光反射シート
が開示されている。該光反射体は、延伸により形成され
る空孔と樹脂との界面での光の乱反射および無機充填剤
自身の反射により高い光反射率を有する優れた光反射体
である。そして、他のフィルムを積層しても良いことが
記載されているが、いかなる特性を有するフィルムを積
層するかについては何らの開示も示唆もされていない。Further, in JP-A-6-298957, a resin composition comprising a resin having a refractive index of less than 1.6, 75 to 25 parts by weight and an inorganic filler 25 to 75 parts by weight is used. A light-reflecting sheet stretched by a factor of 2 to 15 is disclosed. The light reflector is an excellent light reflector having a high light reflectance due to diffuse reflection of light at the interface between the voids formed by stretching and the resin and reflection of the inorganic filler itself. Then, it is described that other films may be laminated, but there is no disclosure or suggestion as to what kind of characteristics the films should be laminated.
【００１８】[0018]
【発明が解決しようとする課題】本発明は、多孔性樹脂
シートを光反射層とする、紫外線等に対する耐光性、形
態保持性及び光線反射性に優れており、主としてワード
プロセッサー、パーソナルコンピュータ、テレビジョン
等の液晶表示装置のバックライトユニット、照明器具、
複写機、プロジェクター方式のディスプレイ、ファクシ
ミリ、電子黒板等に用いる光反射体を提供すること、ま
た、該光反射体を液晶表示装置のバックライトユニット
のランプホルダー部及び／または導光板下部に配設して
得られる、輝度向上が図り得る光反射装置を提供するこ
とを課題とする。DISCLOSURE OF THE INVENTION The present invention has a porous resin sheet as a light-reflecting layer and is excellent in light resistance to ultraviolet rays and the like, shape retention and light-reflecting ability, and is mainly used in word processors, personal computers and televisions. LCD unit backlight unit, lighting equipment,
To provide a light reflector for use in a copying machine, a projector type display, a facsimile, an electronic blackboard, etc., and to dispose the light reflector in a lamp holder part and / or a light guide plate lower part of a backlight unit of a liquid crystal display device. It is an object of the present invention to provide a light reflection device which can be obtained by improving the brightness.
【００１９】[0019]
【課題を解決するための手段】本発明の目的は、優れた
光反射率及び電気絶縁性を有し、形態保持性を有する光
反射体を提供することにある。本発明の第２の目的は上
記特性にさらに高い耐光性及び／又は更に優れた光反射
率を有する光反射体を提供することにある。また、本発
明の第３の目的は、上記２種の光反射体を用いた光反射
装置を提供することにある。SUMMARY OF THE INVENTION It is an object of the present invention to provide a light reflector having excellent light reflectance and electrical insulation properties and shape retention. A second object of the present invention is to provide a light reflector having higher light resistance and / or more excellent light reflectance in the above characteristics. A third object of the present invention is to provide a light reflecting device using the above two kinds of light reflectors.
【００２０】本発明者らは鋭意検討した結果、特定量の
無機充填剤を含むポリオレフィン樹脂シートを延伸して
得られた多孔性樹脂シートの片面または両面に、特定の
光線透過率を有する保護層を積層することにより、上記
課題を解決し得る光反射体が得られ、該光反射体が光反
射装置の資材として適することを見出し、本発明に到っ
た。As a result of intensive studies by the present inventors, a protective layer having a specific light transmittance on one or both sides of a porous resin sheet obtained by stretching a polyolefin resin sheet containing a specific amount of an inorganic filler. By laminating the above, a light reflector capable of solving the above problems was obtained, and it was found that the light reflector is suitable as a material for a light reflecting device, and the present invention has been completed.
【００２１】すなわち、本発明の第１発明は、多孔性樹
脂シートの少なくとも片表面に保護層が積層された光反
射体であって、該多孔性樹脂シートがポリオレフィン系
樹脂１００重量部に対して微粉末状の無機系充填剤１０
０〜３００重量部を含み、面積倍率で１．５〜２０倍に
延伸され、且つ、波長５５０ｎｍの光線の反射率が９５
％以上であり、該光反射体の剛性が少なくとも５０ｍｍ
であることを特徴とする光反射体を提供することにあ
る。That is, the first invention of the present invention is a light reflector in which a protective layer is laminated on at least one surface of a porous resin sheet, and the porous resin sheet is used with respect to 100 parts by weight of the polyolefin resin. Fine powder inorganic filler 10
0 to 300 parts by weight, stretched to an area ratio of 1.5 to 20 times, and has a reflectance of 95 at a wavelength of 550 nm of 95.
% Or more, and the rigidity of the light reflector is at least 50 mm.
The present invention is to provide a light reflector.
【００２２】この発明に係わる光反射体の特徴は、光線
の反射率の高い多孔性樹脂シートは柔軟であり極めて有
用な光反射体であるが、用途によっては剛性の高い光反
射体が必要であり多孔性樹脂シートの少なくとも片面に
剛性の高い保護層を積層して光反射体の剛性を向上させ
ることを特徴とする。The feature of the light reflector according to the present invention is that the porous resin sheet having a high light ray reflectance is flexible and is a very useful light reflector, but a light reflector having a high rigidity is required depending on the application. It is characterized in that a protective layer having high rigidity is laminated on at least one surface of the porous resin sheet to improve the rigidity of the light reflector.
【００２３】本発明の第２発明は、第１の発明の保護層
が光反射体の剛性を５０〜１５０ｍｍに高めると同時に
ＵＶ保護層としての機能も有するＵＶ保護層であり、該
ＵＶ保護層の全光線透過率が８０％以上、該光反射体の
ＵＶ保護層表面に照射した波長５５０ｎｍの光線の反射
率が９５％以上であり、且つ、該光反射体のＵＶ保護層
表面に８０℃において４００ＭＪ／ｍ2 の紫外線を照射
した後の該光反射体の波長４５０ｎｍ及び５５０ｎｍの
光線の反射率の低下率が共に１０％未満であることを特
徴とする光反射体を提供することにある。A second invention of the present invention is the UV protective layer, wherein the protective layer of the first invention enhances the rigidity of the light reflector to 50 to 150 mm and at the same time has a function as a UV protective layer. Has a total light transmittance of 80% or more, a reflectance of light having a wavelength of 550 nm irradiated on the surface of the UV protective layer of the light reflector is 95% or more, and the surface of the UV protective layer of the light reflector has a temperature of 80 ° C. In order to provide a light reflector characterized by having a reflectance reduction rate of light rays of wavelengths 450 nm and 550 nm after irradiation with ultraviolet rays of 400 MJ / m 2 at less than 10%. .
【００２４】この発明に係わる光反射体の特徴は、波長
５５０ｎｍの光線の反射率が９５％以上である多孔性樹
脂シートを光反射層とし、その少なくとも片表面に全光
線透過率が８０％以上である、紫外線等に対するＵＶ保
護層が積層された剛性が５０〜１５０ｍｍである光反射
体である点にある。光反射層が上記多孔性樹脂シートで
あるため、柔軟性に富む他、該シート表面及びその内部
に光反射層を多数含有しており優れた光反射率を有する
上、その反射が拡散反射である利点がある。しかも、多
孔性樹脂シートの少なくとも片表面に上記特性を有する
ＵＶ保護層が積層されているため、紫外線等に対する耐
光性、及び形態保持性が共に改善された光反射体であ
る。The feature of the light reflector according to the present invention is that a porous resin sheet having a reflectance of light having a wavelength of 550 nm of 95% or more is used as a light reflecting layer, and a total light transmittance of at least one surface thereof is 80% or more. That is, it is a light reflector having a rigidity of 50 to 150 mm in which a UV protection layer against ultraviolet rays is laminated. Since the light-reflecting layer is the above-mentioned porous resin sheet, in addition to being highly flexible, it contains a large number of light-reflecting layers on the surface and inside of the sheet and has an excellent light reflectance, and the reflection is diffuse reflection. There are some advantages. Moreover, since the UV protective layer having the above-mentioned properties is laminated on at least one surface of the porous resin sheet, the light reflector has improved light resistance to ultraviolet rays and the like and shape retention.
【００２５】本発明の第３の発明は第１の発明の保護層
が多孔性樹脂シートの裏面のみに積層された光反射体の
剛性が少なくとも１００ｍｍに高められると同時に漏光
防止機能も有する漏光防止保護層であり、該漏光防止保
護層の全光線透過率が２０％未満であり、該光反射体の
多孔性樹脂シート表面に照射された波長５５０ｎｍの光
線の反射率が９５％以上であることを特徴とする光反射
体を提供することにある。A third invention of the present invention is a light leakage preventive function which has a light leakage preventive function while increasing the rigidity of a light reflector in which the protective layer of the first invention is laminated only on the back surface of a porous resin sheet to at least 100 mm. It is a protective layer, the total light transmittance of the light leakage prevention protective layer is less than 20%, and the reflectance of light having a wavelength of 550 nm irradiated on the surface of the porous resin sheet of the light reflector is 95% or more. It is to provide a light reflector characterized by.
【００２６】この発明に係わる光反射体の特徴は、波長
５５０ｎｍの光線の反射率が９５％以上である多孔性樹
脂シートを光反射層とし、その裏面に全光線透過率が２
０％未満である、漏光防止及び形態保持のための漏光防
止保護層が積層された剛性が少なくとも１００ｍｍであ
る光反射体である点にある。光反射層が上記多孔性樹脂
シートであるため、柔軟性に富む他、該シート表面及び
その内部に光反射層を多数含有しており優れた光反射率
を有する上、その反射が拡散反射である利点がある。し
かも、多孔性樹脂シートの裏面に上記特性を有する漏光
防止保護層が積層されているため、多孔性樹脂シートを
透過した光があった場合でも漏光防止保護層によって効
率的に反射することができ、更に形態保持性も改善され
た光反射体である。The light reflector according to the present invention is characterized in that a porous resin sheet having a reflectance of light having a wavelength of 550 nm of 95% or more is used as a light reflecting layer, and the back surface thereof has a total light transmittance of 2%.
It is less than 0%, and is a light reflector having a rigidity of at least 100 mm in which a light leakage prevention protective layer for light leakage prevention and shape retention is laminated. Since the light-reflecting layer is the above-mentioned porous resin sheet, in addition to being highly flexible, it contains a large number of light-reflecting layers on the surface and inside of the sheet and has an excellent light reflectance, and the reflection is diffuse reflection. There are some advantages. Moreover, since the light leakage prevention protective layer having the above characteristics is laminated on the back surface of the porous resin sheet, even if there is light transmitted through the porous resin sheet, it can be efficiently reflected by the light leakage prevention protective layer. Further, it is a light reflector having improved shape retention.
【００２７】本発明の第４の発明は多孔性樹脂シートの
両面に保護層が積層され、該多孔性樹脂シートの表面の
保護層がＵＶ保護層としての機能も有しかつ全光線透過
率が８０％以上であるＵＶ保護層であり、また裏面の保
護層が漏光防止機能も有する漏光防止保護層が積層され
た積層体であって、該積層体のＵＶ保護層表面に照射し
た波長５５０ｎｍの光線の反射率が９５％以上であり、
且つ、該積層体のＵＶ保護層表面に８０℃において４０
０ＭＪ／ｍ2 の紫外線を照射した後の該光反射体の波長
４５０ｎｍ及び５５０ｎｍの光線の反射率の低下率が共
に１０％未満であり、且つ該積層体の剛性が少なくとも
５０ｍｍであることを特徴とする光反射体を提供するこ
とにある。In the fourth invention of the present invention, protective layers are laminated on both sides of the porous resin sheet, and the protective layer on the surface of the porous resin sheet also has a function as a UV protective layer and has a total light transmittance. It is a UV protective layer of 80% or more, and the back surface protective layer is a laminated body in which a light leakage preventing protective layer also having a light leakage preventing function is laminated, and the wavelength of 550 nm irradiated on the surface of the UV protective layer of the laminated body. The reflectance of light rays is 95% or more,
Moreover, the UV protection layer surface of the laminate is 40 at 80 ° C.
The reduction rate of the reflectance of light of wavelengths 450 nm and 550 nm of the light reflector after irradiating 0 MJ / m 2 of ultraviolet rays is both less than 10%, and the rigidity of the laminate is at least 50 mm. It is to provide a light reflector.
【００２８】この発明に係わる光反射体の特徴は第２の
発明と第３の発明の特徴を兼ね備えた光反射体である。The light reflector according to the present invention is a light reflector having both the features of the second invention and the third invention.
【００２９】上記各々の光反射体は液晶表示装置のバッ
クライトユニット、照明器具、複写機、プロジェクター
方式のディスプレイ、ファクシミリ及び電子黒板からな
る群から選ばれた装置の光反射体として好ましく使用す
ることができる。Each of the above light reflectors is preferably used as a light reflector of a device selected from the group consisting of a backlight unit of a liquid crystal display device, a lighting fixture, a copying machine, a display of a projector system, a facsimile and an electronic blackboard. You can
【００３０】上記第１、２又は第４発明の光反射体は液
晶表示装置のバックライトユニットを構成するランプホ
ルダーを形成する光反射体として好ましく使用できる。The light reflector of the first, second or fourth invention can be preferably used as a light reflector forming a lamp holder constituting a backlight unit of a liquid crystal display device.
【００３１】上記第１、３又は第４発明の光反射体は液
晶表示装置のバックライトユニットを構成する導光板下
光反射シートとして好ましく使用することができる。The light reflector of the first, third or fourth invention can be preferably used as a light reflecting sheet under a light guide plate which constitutes a backlight unit of a liquid crystal display device.
【００３２】本発明の第５の発明は、図１または図２に
おいて導光板４の片面に導光板下光反射シート３、他の
面に光拡散シート５が配置され、さらに該光拡散シート
５の表面にレンズシート６が配置された積層体の少なく
とも１側面に光源１が配設され、該光源１が湾曲状に形
成されたランプホルダー２により覆われている光反射装
置において、ランプホルダー２として第１、２又は４発
明の光反射体を使用し、及び／又は導光板下光反射シー
ト３には１、３又は４発明の光反射体を使用することを
特徴とする光反射装置を提供することにある。In the fifth aspect of the present invention, in FIG. 1 or 2, the light guide plate lower light reflection sheet 3 is arranged on one surface of the light guide plate 4, and the light diffusion sheet 5 is arranged on the other surface, and the light diffusion sheet 5 is further arranged. In the light reflection device, the light source 1 is disposed on at least one side surface of the laminated body in which the lens sheet 6 is disposed on the surface thereof, and the light source 1 is covered by the lamp holder 2 formed in a curved shape. The light reflector of the first, second, or fourth invention is used as the above, and / or the light reflector of the first, third, or fourth invention is used for the light guide plate lower light reflection sheet 3. To provide.
【００３３】また、本発明の第６発明は、上記第２また
は第４発明に係わる光反射体を光反射装置のランプホル
ダーに、上記第３または第４の発明に係わる光反射体を
光反射装置の導光板下光反射シートに使用した光反射装
置である。この発明に係わる光反射装置の特徴は、波長
５５０ｎｍの光線の反射率が９５％以上である多孔性樹
脂シートを光反射層とし、その少なくとも片表面に全光
線透過率が８０％以上である、紫外線等に対するＵＶ保
護層が積層された剛性が５０〜１５０ｍｍである光反射
体をランプホルダーに使用し、且つ、波長５５０ｎｍの
光線の反射率が９５％以上である多孔性樹脂シートを光
反射層とし、その裏面に全光線透過率が２０％未満であ
る、漏光防止及び形態保持のための漏光防止保護層が積
層された剛性が少なくとも５０ｍｍである光反射体を導
光板下光反射シートに使用した光反射装置である点にあ
る。ランプホルダー及び導光板下光反射シートの光反射
層が上記多孔性樹脂シートであるため、柔軟性に富む
他、該シート表面及びその内部に光反射層を多数含有し
ており優れた光反射率を有する上、その反射が拡散反射
である利点がある。しかも、ランプホルダーに使用する
光反射体を構成する多孔性樹脂シートの少なくとも片表
面に上記特性を有するＵＶ保護層が積層されているた
め、紫外線等に対する耐光性、及び形態保持性が共に改
善されている。また、導光板下光反射シートに使用する
光反射体を構成する多孔性樹脂シートの裏面には上記特
性を有する漏光防止保護層が積層されているため、多孔
性樹脂シートを透過した光があった場合でも漏光防止保
護層によって効率的に反射することができ、更に形態保
持性も改善されている。Further, a sixth invention of the present invention uses the light reflector according to the second or fourth invention as a lamp holder of a light reflecting device, and the light reflector according to the third or fourth invention as a light reflector. It is a light reflection device used for a light reflection sheet under a light guide plate of the device. The light reflecting device according to the present invention is characterized in that a porous resin sheet having a reflectance of light having a wavelength of 550 nm of 95% or more is used as a light reflecting layer, and at least one surface thereof has a total light transmittance of 80% or more. A light reflector having a rigidity of 50 to 150 mm, which is laminated with a UV protective layer against ultraviolet rays, is used for a lamp holder, and a porous resin sheet having a reflectance of light having a wavelength of 550 nm of 95% or more is used as a light reflecting layer. A light reflector having a total light transmittance of less than 20% and a rigidity of at least 50 mm laminated with a light leakage prevention protective layer for light leakage prevention and shape retention is used for a light guide sheet under a light guide plate. It is a light reflection device. Since the light-reflecting layer of the lamp holder and the light-reflecting sheet under the light guide plate is the above-mentioned porous resin sheet, it is excellent in flexibility and has a large number of light-reflecting layers on the surface of the sheet and inside thereof, and thus has an excellent light reflectance. And has the advantage that the reflection is diffuse reflection. Moreover, since the UV protective layer having the above characteristics is laminated on at least one surface of the porous resin sheet constituting the light reflector used for the lamp holder, both the light resistance to ultraviolet rays and the shape retention are improved. ing. Further, since the light leakage prevention protective layer having the above characteristics is laminated on the back surface of the porous resin sheet that constitutes the light reflector used for the light reflection sheet under the light guide plate, there is no light transmitted through the porous resin sheet. In this case, the light leakage prevention protective layer can efficiently reflect the light, and the shape retention is also improved.
【００３４】[0034]
【発明の実施の形態】本発明の実施形態をより詳細に説
明する。本発明の光反射体の多孔性樹脂シートはポリオ
レフィン系樹脂に特定量の微粉末状の無機系充填剤を添
加、混合して樹脂組成物となし、得られた樹脂組成物か
ら、例えば溶融押出成形等により未延伸シートを成形
し、次いで、得られた未延伸シートを一軸または二軸延
伸することにより製造される。基材樹脂として、ポリオ
レフィン系樹脂を採用することにより、後述する無機系
充填剤を多量に、且つ分散性良く含有させることができ
るものである。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described in more detail. The porous resin sheet of the light reflector of the present invention is made by adding a specific amount of a fine powdery inorganic filler to a polyolefin resin to form a resin composition, and from the obtained resin composition, for example, melt extrusion. The unstretched sheet is molded by molding or the like, and then the obtained unstretched sheet is uniaxially or biaxially stretched. By using a polyolefin resin as the base resin, a large amount of an inorganic filler described later can be contained with good dispersibility.
【００３５】多孔性樹脂シートの製造に使用するポリオ
レフィン系樹脂として、高密度ポリエチレン、低密度ポ
リエチレン、エチレンとα−オレフィンとの共重合体で
ある線形低密度ポリエチレン、ポリプロピレン、エチレ
ン−プロピレン共重合体、ポリ−４−メチルペンテン系
樹脂等が挙げられる。これらのポリオレフィン系樹脂
は、後述する微粉末状の無機系充填剤を分散性良く多量
に含有させることができ、しかも、得られる多孔性樹脂
シートが柔軟性に富んでいる利点がある。As the polyolefin resin used for producing the porous resin sheet, high density polyethylene, low density polyethylene, linear low density polyethylene which is a copolymer of ethylene and α-olefin, polypropylene, ethylene-propylene copolymer. , Poly-4-methylpentene resin and the like. These polyolefin resins are advantageous in that they can contain a fine powdery inorganic filler, which will be described later, in a large amount with good dispersibility, and the obtained porous resin sheet is highly flexible.
【００３６】ポリオレフィン系樹脂の分子量はシートへ
の成形性に影響を及ぼし、分子量が高過ぎても低過ぎて
もシートの成形性が低下する。かかる点を考慮すると、
分子量のパラメータであるメルトインデックス（以下、
ＭＩという）が、ポリエチレン系樹脂の場合には０．５
〜７ｇ／１０ｍｉｎ程度（１９０℃、荷重２．１６ｋ
ｇ）、ポリプロピレン樹脂の場合には１〜１０ｇ／１０
ｍｉｎ程度（２３０℃、荷重２．１６ｋｇ）、ポリ−４
−メチルペンテン系樹脂の場合には１０〜７０ｇ／１０
ｍｉｎ程度（２６０℃、荷重５．０ｋｇ）であることが
好ましい。The molecular weight of the polyolefin resin affects the formability of the sheet, and if the molecular weight is too high or too low, the sheet formability is reduced. Considering this point,
Melt index, which is a parameter of molecular weight (hereinafter,
0.5) in the case of polyethylene resin
~ 7g / 10min (190 ° C, load 2.16k
g), 1 to 10 g / 10 in the case of polypropylene resin
About min (230 ° C, load 2.16kg), poly-4
-In the case of methylpentene resin, 10-70 g / 10
It is preferably about min (260 ° C., load 5.0 kg).
【００３７】尚、本発明におけるポリオレフィン系樹脂
のＭＩは、ＡＳＴＭ Ｄ−１２３８に規定される方法に
より上記条件で測定した値である。The MI of the polyolefin resin of the present invention is a value measured under the above conditions by the method specified in ASTM D-1238.
【００３８】本発明に用いる微粉末状の無機系充填剤と
しては、金属塩、金属水酸化物、金属酸化物等が好まし
く用いられる。これらのものを例示すると、硫酸バリウ
ム、硫酸カルシウム、硫酸マグネシウム、硫酸アルミニ
ウム、炭酸バリウム、炭酸カルシウム、塩化マグネシウ
ム、炭酸マグネシウム、塩基性炭酸マグネシウム等の金
属塩、水酸化マグネシウム、水酸化アルミニウム、水酸
化カルシウム等の金属水酸化物、酸化カルシウム、酸化
亜鉛、酸化マグネシウム、酸化チタン、アルミナ、シリ
カ等の金属酸化物等が挙げられる。さらに、ケイ酸カル
シウム類、セメント類、ゼオライト類、タルク等の粘土
類も使用できる。As the fine powdery inorganic filler used in the present invention, metal salts, metal hydroxides, metal oxides and the like are preferably used. Examples of these are barium sulfate, calcium sulfate, magnesium sulfate, aluminum sulfate, barium carbonate, calcium carbonate, magnesium chloride, magnesium carbonate, basic magnesium carbonate, and other metal salts, magnesium hydroxide, aluminum hydroxide, and hydroxide. Examples thereof include metal hydroxides such as calcium, metal oxides such as calcium oxide, zinc oxide, magnesium oxide, titanium oxide, alumina and silica. Furthermore, clays such as calcium silicates, cements, zeolites and talc can also be used.
【００３９】これらの内、ポリオレフィン系樹脂との混
合性または分散性、シートの延伸性および得られる多孔
性樹脂シートの開孔性、開孔率等を総合的に勘案する
と、硫酸バリウム、炭酸カルシウム、酸化チタン、水酸
化マグネシウムが好ましい。さらに好ましくは硫酸バリ
ウム、炭酸カルシウムであり、最も好ましくは硫酸バリ
ウムである。硫酸バリウムまたは炭酸カルシウムを用い
る場合には、ポリオレフィン系樹脂との分散性、混合性
がよい沈降性硫酸バリウムまたは沈降性炭酸カルシウム
が好ましい。Of these, considering comprehensively the mixing or dispersibility with the polyolefin resin, the stretchability of the sheet, and the porosity and porosity of the resulting porous resin sheet, barium sulfate and calcium carbonate are taken into consideration. , Titanium oxide and magnesium hydroxide are preferred. More preferred are barium sulfate and calcium carbonate, and most preferred is barium sulfate. When barium sulfate or calcium carbonate is used, precipitated barium sulfate or precipitated calcium carbonate having good dispersibility and compatibility with the polyolefin resin is preferable.
【００４０】また、微粉末状の無機系充填剤の粒度は得
られる多孔性シートの表面状態に影響を及ぼすので、
０．１〜７μｍ程度の平均粒子径を有する微粉末状の無
機系充填剤が好ましい。さらに好ましくは０．２〜５μ
ｍである。Further, since the particle size of the finely powdered inorganic filler affects the surface condition of the obtained porous sheet,
A fine powder inorganic filler having an average particle diameter of about 0.1 to 7 μm is preferable. More preferably 0.2-5 μ
m.
【００４１】微粉末状の無機系充填剤の添加量は得られ
る多孔性樹脂シートの光線反射率に影響を及ぼす。微粉
末状の無機系充填剤の添加量が少ないと得られる多孔性
樹脂シートの開孔率が低くなり、逆に多いと開孔率が高
くなる。開孔率が低い多孔性樹脂シートは、樹脂層と空
気層との界面における光の反射量が減り、高い光線反射
率を有する多孔性樹脂シートが得られない。従って、光
反射体に適する多孔性樹脂シートは、適度の開孔率と高
い光線反射率を有するものが好ましい。また、微粉末状
の無機系充填剤の添加量が多いと多孔性シートの開孔率
が高くなり光線反射率は増すが、シートの生産性、多孔
性樹脂シートの強度が低下する。かかる点を総合して考
慮すると、微粉末状の無機系充填剤の添加量は、ポリオ
レフィン系樹脂１００重量部に対し１００〜３００重量
部である。The amount of the finely powdered inorganic filler added affects the light reflectance of the resulting porous resin sheet. If the amount of the fine powdery inorganic filler added is small, the porosity of the obtained porous resin sheet is low, and conversely, if the amount is large, the porosity is high. A porous resin sheet having a low porosity reduces the amount of light reflected at the interface between the resin layer and the air layer, and a porous resin sheet having a high light reflectance cannot be obtained. Therefore, it is preferable that the porous resin sheet suitable for the light reflector has an appropriate porosity and a high light reflectance. Further, when the amount of the fine powdery inorganic filler added is large, the porosity of the porous sheet increases and the light reflectance increases, but the productivity of the sheet and the strength of the porous resin sheet decrease. Taking these points into consideration, the amount of the finely powdered inorganic filler added is 100 to 300 parts by weight based on 100 parts by weight of the polyolefin resin.
【００４２】微粉末状の無機系充填剤が硫酸バリウムで
ある場合、好ましい添加量はポリオレフィン系樹脂１０
０重量部に対し１８０〜３００重量部である。さらに好
ましくは１８０〜２５０重量部である。また、それ以外
の微粉末状の無機系充填剤を使用する場合、好ましい添
加量はポリオレフィン系樹脂１００重量部に対し１２０
〜２００重量部である。When the finely powdered inorganic filler is barium sulfate, the preferred addition amount is the polyolefin resin 10.
180 to 300 parts by weight with respect to 0 parts by weight. More preferably, it is 180 to 250 parts by weight. When using other fine powdery inorganic fillers, the preferable addition amount is 120 per 100 parts by weight of the polyolefin resin.
~ 200 parts by weight.
【００４３】本発明の光反射体に使用する多孔性樹脂シ
ートには、上記ポリオレフィン系樹脂に特定量の上記微
粉末状の無機系充填剤を添加、混合した樹脂組成物が用
いられるが、本発明の目的を妨げない範囲内で、安定
剤、滑剤、分散剤、紫外線吸収剤、白色顔料、蛍光増白
剤等の他の添加剤を添加しても良い。For the porous resin sheet used in the light reflector of the present invention, a resin composition obtained by adding and mixing a specific amount of the fine powdery inorganic filler to the polyolefin resin is used. Other additives such as stabilizers, lubricants, dispersants, ultraviolet absorbers, white pigments and optical brighteners may be added within the range not impairing the object of the invention.
【００４４】これらの他の添加剤の内、紫外線吸収能を
有するものを添加することが好ましい。紫外線吸収能を
有する添加剤として、２，４−ジヒドロキシベンゾフェ
ノン、２−ヒドロキシ−４−メトキシベンゾフェノン、
２，２’−ジヒドロキシ−４−メトキシベンゾフェノ
ン、２，２’−ジヒドロキシ−４，４’−ジメトキシベ
ンゾフェノン、２−ヒドロキシ−４−メトキシ−２’−
カルボキシベンゾフェノン、２−ヒドロキシ−４−ｎ−
オクトキシベンゾフェノン、２，２’，４，４’−テト
ラヒドロキシベンゾフェノン、４−ドデシロキシ−２−
ヒドロキシベンゾフェノン、ビス（５−ベンゾイル−４
−ヒドロキシ−２−メトキシフェニル）メタン等のベン
ゾフェノン系化合物、２−（２’−ヒドロキシ−５’−
メチルフェニル）ベンゾトリアゾール、２−（２’−ヒ
ドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェニ
ル）ベンゾトリアゾール、２−（２’−ヒドロキシ−
３’−ｔｅｒｔ−ブチル−５’−メチルフェニル）−５
−クロロベンゾトリアゾール、２−（２’−ヒドロキシ
−３’，５’−ジ−ｔｅｒｔ−ブチルフェニル）−５−
クロロベンゾトリアゾール、２−（２’−ヒドロキシ−
５’−ｔｅｒｔ−オクチルフェニル）ベンゾトリアゾー
ル、２−（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒ
ｔ−アミルフェニル）ベンゾトリアゾール、２−［２’
−ヒドロキシ−３’−（３”，４”，５”，６”−テト
ラヒドロフタルイミドメチル）−５’−メチルフェニ
ル］ベンゾトリアゾール、２，２’−メチレンビス［４
−（１，１，３，３−テトラメチルブチル）−６−（２
Ｈ−ベンゾトリアゾール−２−イル）フェノール］等の
ベンゾトリアゾール系化合物等に代表される紫外線吸収
剤が挙げられる。Among these other additives, it is preferable to add one having an ultraviolet absorbing ability. 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, as an additive having an ultraviolet absorbing ability,
2,2'-dihydroxy-4-methoxybenzophenone, 2,2'-dihydroxy-4,4'-dimethoxybenzophenone, 2-hydroxy-4-methoxy-2'-
Carboxybenzophenone, 2-hydroxy-4-n-
Octoxybenzophenone, 2,2 ', 4,4'-tetrahydroxybenzophenone, 4-dodecyloxy-2-
Hydroxybenzophenone, bis (5-benzoyl-4)
Benzophenone compounds such as -hydroxy-2-methoxyphenyl) methane, 2- (2'-hydroxy-5'-
Methylphenyl) benzotriazole, 2- (2'-hydroxy-3 ', 5'-di-tert-butylphenyl) benzotriazole, 2- (2'-hydroxy-
3'-tert-butyl-5'-methylphenyl) -5
-Chlorobenzotriazole, 2- (2'-hydroxy-3 ', 5'-di-tert-butylphenyl) -5-
Chlorobenzotriazole, 2- (2'-hydroxy-
5'-tert-octylphenyl) benzotriazole, 2- (2'-hydroxy-3 ', 5'-di-ter
t-amylphenyl) benzotriazole, 2- [2 ′
-Hydroxy-3 '-(3 ", 4", 5 ", 6" -tetrahydrophthalimidomethyl) -5'-methylphenyl] benzotriazole, 2,2'-methylenebis [4
-(1,1,3,3-tetramethylbutyl) -6- (2
[H-benzotriazol-2-yl) phenol] and other ultraviolet absorbers represented by benzotriazole compounds.
【００４５】これらの添加量は、例えば紫外線吸収剤の
場合、ポリオレフィン系樹脂１００重量部に対し０．０
１〜５重量部、好ましくは０．０１〜２重量部である。For example, in the case of an ultraviolet absorber, the addition amount thereof is 0.0 with respect to 100 parts by weight of the polyolefin resin.
It is 1 to 5 parts by weight, preferably 0.01 to 2 parts by weight.
【００４６】ポリオレフィン系樹脂と微粉末状の無機系
充填剤、必要に応じて、紫外線吸収剤、安定剤、滑剤、
分散剤、紫外線吸収剤、白色顔料、蛍光増白剤等の他の
添加剤とを混合して樹脂組成物を製造する方法には特に
制限はない。例えば、リボンブレンダー、ヘンシェルミ
キサー、スーパーミキサー、タンブラーミキサー等を用
いて室温またはその近傍の温度において混合する方法が
挙げられる。Polyolefin resin and fine powder inorganic filler, if necessary, ultraviolet absorber, stabilizer, lubricant,
There is no particular limitation on the method for producing the resin composition by mixing with other additives such as a dispersant, an ultraviolet absorber, a white pigment and a fluorescent brightening agent. For example, a method of mixing at room temperature or a temperature in the vicinity thereof using a ribbon blender, a Henschel mixer, a super mixer, a tumbler mixer and the like can be mentioned.
【００４７】また、混合した後、ストランドダイが装着
された一軸または二軸スクリュー型押出機を用いて、ポ
リオレフィン系樹脂の融点または軟化点以上の温度、好
ましくは融点または軟化点＋２０℃以上、ポリオレフィ
ン系樹脂の分解温度未満の温度範囲において混練、溶融
押出して、溶融ストランドとし、冷却した後、切断して
ペレット状に成形する方法も挙げられる。ポリオレフィ
ン系樹脂に微粉末状の無機系充填剤を均一に分散、混合
するためにはペレット状に成形する方法が好ましい。After mixing, using a single-screw or twin-screw extruder equipped with a strand die, the temperature is not lower than the melting point or softening point of the polyolefin resin, preferably the melting point or softening point + 20 ° C. or higher, There is also a method of kneading and melt-extruding in a temperature range lower than the decomposition temperature of the system resin to form a molten strand, cooling, and then cutting and molding into pellets. In order to uniformly disperse and mix the finely powdered inorganic filler in the polyolefin resin, a method of molding in a pellet form is preferable.
【００４８】上記のようにして得られたポリオレフィン
系樹脂組成物からシートを成形する方法にも特に制限は
ない。例えば、Ｔダイが装着された一軸または二軸スク
リュー型押出機を用いる押出成形法、円形ダイが装着さ
れた押出機を用いるインフレーション成形法、カレンダ
ー成形法等の公知の方法が挙げられる。The method of molding a sheet from the polyolefin resin composition obtained as described above is not particularly limited. For example, known methods such as an extrusion molding method using a single-screw or twin-screw extruder equipped with a T die, an inflation molding method using an extruder equipped with a circular die, and a calender molding method can be mentioned.
【００４９】シートの成形温度は、用いるポリオレフィ
ン系樹脂により異なるが、通常、用いる樹脂の融点また
は軟化点以上の温度、好ましくは、融点または軟化点＋
２０℃以上、分解温度未満の温度範囲である。The molding temperature of the sheet varies depending on the polyolefin resin used, but is usually a temperature above the melting point or softening point of the resin used, preferably the melting point or softening point +
The temperature range is 20 ° C. or higher and lower than the decomposition temperature.
【００５０】得られた未延伸樹脂シートは、ロール法、
テンター法等の公知の方法で少なくとも一軸方向に延伸
される。延伸は一段で行ってもよいし、多段階に分けて
行っても良い。また、二軸方向に延伸しても良い。さら
に、延伸後必要に応じて、得られた開孔の形態を安定さ
せるために熱固定処理を行っても良い。The unstretched resin sheet thus obtained is subjected to the roll method,
It is stretched in at least a uniaxial direction by a known method such as a tenter method. The stretching may be carried out in one stage or may be carried out in multiple stages. Further, it may be biaxially stretched. Further, after stretching, if necessary, a heat setting treatment may be performed to stabilize the shape of the obtained pores.
【００５１】延伸中のシートの切断を防止して、且つ均
一な延伸を行い、好ましい開孔率を有する多孔性樹脂シ
ートを得るためには、延伸温度は、樹脂のビカット軟化
点（ＪＩＳ Ｋ−６７６０に規定される方法で測定した
値）未満であることが好ましい。In order to prevent the sheet from being cut during stretching and perform uniform stretching to obtain a porous resin sheet having a preferable porosity, the stretching temperature is set to the Vicat softening point (JIS K- It is preferably less than the value measured by the method defined in 6760).
【００５２】また、延伸倍率は、前記の微粉末状の無機
系充填剤の添加量と同様に、得られる延伸シートの開孔
率に影響を及ぼす。延伸倍率が低いと得られる延伸シー
トの開孔率が低下し、高いと開孔率が高くなる。しか
し、延伸倍率が高過ぎると延伸中にシートが切断するこ
とがあるので好ましくない。かかる観点から、延伸倍率
は面積倍率で１．５〜２０倍の範囲が好ましい。さらに
好ましくは２〜１５倍である。具体的には、一軸延伸の
場合には１．５〜８倍延伸することが好ましい。さらに
好ましくは２〜７．５倍である。また、二軸延伸の場合
には一軸方向に１．５〜７倍、その方向と直角方向に
１．１〜３倍延伸することが好ましい。さらに好ましく
は一軸方向に２〜６．５倍、その方向と直角方向に１．
１〜２．５倍程度である。Further, the stretching ratio affects the porosity of the obtained stretched sheet in the same manner as the amount of the fine powdery inorganic filler added. When the stretching ratio is low, the porosity of the obtained stretched sheet is low, and when it is high, the porosity is high. However, if the stretching ratio is too high, the sheet may be cut during stretching, which is not preferable. From this point of view, the stretching ratio is preferably in the range of 1.5 to 20 times in terms of area ratio. It is more preferably 2 to 15 times. Specifically, in the case of uniaxial stretching, it is preferable to stretch 1.5 to 8 times. More preferably, it is 2-7.5 times. In the case of biaxial stretching, it is preferable to stretch 1.5 to 7 times in the uniaxial direction and 1.1 to 3 times in the direction perpendicular to the direction. More preferably, it is 2 to 6.5 times in the uniaxial direction, and 1. in the direction perpendicular to that direction.
It is about 1 to 2.5 times.
【００５３】延伸する前にエンボスロール等を用いて未
延伸フィルムの表面にエンボス加工を施してもよい。ま
た、延伸した後、多孔性樹脂シートの表面にエンボス加
工を施してもよい。Before stretching, the surface of the unstretched film may be embossed using an embossing roll or the like. After stretching, the surface of the porous resin sheet may be embossed.
【００５４】多孔性樹脂シートの厚みが薄いと光の透過
率が高くなり光線の反射率が低下する傾向にある。ま
た、厚いと光の反射率は変わらないが、シートの生産性
が低下する。従って、光反射体として用いる多孔性樹脂
シートの厚みは、通常、５０〜５００μｍ程度である、
好ましくは５０〜４００μｍ、さらに好ましくは５０〜
３００μｍである。If the thickness of the porous resin sheet is thin, the light transmittance tends to increase and the light ray reflectance tends to decrease. Further, if the thickness is thick, the reflectance of light does not change, but the productivity of the sheet decreases. Therefore, the thickness of the porous resin sheet used as the light reflector is usually about 50 to 500 μm.
Preferably 50-400 μm, more preferably 50-
It is 300 μm.
【００５５】上記組成および製造条件で得られる多孔性
樹脂シートは、４０％以上の開孔率を有する多孔性樹脂
シートである。多孔性樹脂シートを光反射体として用い
るには、高い光線反射率を有することが望まれる。多孔
性樹脂シートの開孔率が４０％未満であると、樹脂層と
空気層との界面が減少するため光線反射率が低下する。The porous resin sheet obtained with the above composition and production conditions is a porous resin sheet having a porosity of 40% or more. In order to use the porous resin sheet as a light reflector, it is desired to have a high light ray reflectance. If the porosity of the porous resin sheet is less than 40%, the interface between the resin layer and the air layer is reduced, so that the light reflectance is reduced.
【００５６】光反射体として用いる多孔性樹脂シート
は、少なくとも４０％以上の開孔率を有し、波長が５５
０ｎｍの光線の反射率が９５％以上であることが好まし
い。光反射体として用いる多孔性樹脂シートの開孔率は
高ければ高いほど好ましいが、延伸シートの成形性、延
伸性等を勘案するとその上限は７０％程度である。従っ
て、好ましい多孔性樹脂シートは、上記方法で得られる
多孔性樹脂シートの内、開孔率が４０〜７０％、好まし
くは４０〜６０％のものである。The porous resin sheet used as the light reflector has a porosity of at least 40% or more and a wavelength of 55.
It is preferable that the reflectance of 0 nm light is 95% or more. The higher the porosity of the porous resin sheet used as the light reflector is, the more preferable. However, the upper limit is about 70% in consideration of the formability and stretchability of the stretched sheet. Therefore, a preferable porous resin sheet has a porosity of 40 to 70%, preferably 40 to 60% among the porous resin sheets obtained by the above method.
【００５７】多孔性樹脂シートの表面及び／または裏面
に積層する保護層としては、例えば、熱可塑性樹脂等を
Ｔダイが装着された一軸または二軸スクリュー型押出機
を用いる押出成形法、円形ダイが装着された押出機を用
いるインフレーション成形法、カレンダー成形法等の公
知の方法により成形された樹脂フィルムが使用される。
また、上記樹脂等を含む有機溶媒溶液を、多孔性樹脂シ
ートの表面及び／または裏面に塗布、乾燥することによ
り形成された樹脂フィルムであっても良い。As the protective layer to be laminated on the front surface and / or the back surface of the porous resin sheet, for example, an extrusion molding method using a single-screw or twin-screw extruder equipped with a T-die such as a thermoplastic resin, a circular die A resin film molded by a known method such as an inflation molding method or a calender molding method using an extruder equipped with is used.
Further, it may be a resin film formed by applying an organic solvent solution containing the above resin or the like on the front surface and / or the back surface of the porous resin sheet and drying the solution.
【００５８】上記保護層の形成に使用する樹脂として、
ポリエチレンテレフタレート、ポリブチレンテレフタレ
ート等に代表されるポリエステル系樹脂、ポリ酢酸ビニ
ル系樹脂、ポリアクリル酸メチル、ポリアクリル酸エチ
ルに代表されるポリアクリル酸エステル系樹脂、ポリメ
タクリル酸メチル等に代表されるポリメタクリル酸エス
テル系樹脂、ポリテトラフルオルエチレン、ポリクロル
トリフルオルエチレン、ポリフッ化ビニリデン、ポリフ
ッ化ビニル、テトラフルオルエチレンとヘキサフルオル
プロピレンとの共重合体等に代表されるフッ素系樹脂、
ポリアクリロニトリル系樹脂、シリコーン系樹脂、ナイ
ロン６、ナイロン６−６、ナイロン６−１０、ナイロン
１１、ナイロン１２等に代表されるポリアミド系樹脂、
等に代表される熱可塑性樹脂が挙げられる。As the resin used for forming the above-mentioned protective layer,
Polyester terephthalate, polybutylene terephthalate, and other polyester resins, polyvinyl acetate resin, polymethyl acrylate, polyacrylic ester resins, such as polyethyl acrylate, and polymethyl methacrylate Polymethacrylic acid ester-based resin, polytetrafluoroethylene, polychlorotrifluoroethylene, polyvinylidene fluoride, polyvinyl fluoride, fluorine-based resin typified by a copolymer of tetrafluoroethylene and hexafluoropropylene, and the like,
Polyacrylonitrile resin, silicone resin, polyamide resin such as nylon 6, nylon 6-6, nylon 6-10, nylon 11 and nylon 12,
And the like.
【００５９】これらの内、ポリエチレンテレフタレー
ト、ポリブチレンテレフタレート等に代表されるポリエ
ステル系樹脂、ポリアクリル酸メチル、ポリアクリル酸
エチル、ポリメタクリル酸メチル等に代表されるポリア
クリル系樹脂、シリコーン系樹脂等が好ましい。Among these, polyester resins represented by polyethylene terephthalate, polybutylene terephthalate, etc., polyacrylic resins represented by methyl polyacrylate, ethyl polyacrylate, polymethyl methacrylate, etc., silicone resins, etc. Is preferred.
【００６０】上記樹脂から樹脂フィルムを成形する温度
は、用いる熱可塑性樹脂により異なるが、通常、用いる
樹脂の融点または軟化点以上の温度、好ましくは、融点
または軟化点＋２０℃以上、分解温度未満の温度範囲で
ある。The temperature at which a resin film is formed from the above resin varies depending on the thermoplastic resin used, but is usually a temperature above the melting point or softening point of the resin used, preferably above the melting point or softening point + 20 ° C. and below the decomposition temperature. The temperature range.
【００６１】保護層に使用する樹脂フィルムは、未延伸
フィルムでも延伸フィルムであっても良い。延伸する場
合は、ロール法、テンター法等の公知の方法で少なくと
も一軸方向に延伸される。延伸は一段で行ってもよい
し、多段階に分けて行っても良い。また、二軸方向に延
伸しても良い。さらに、延伸後必要に応じて、得られた
開孔の形態を安定させるために熱固定処理を行っても良
い。延伸倍率は面積倍率で１．５〜１０倍程度の範囲が
好ましい。具体的には、一軸延伸の場合には１．５〜１
０倍延伸することが好ましい。さらに好ましくは２〜
７．５倍である。また、二軸延伸の場合には一軸方向に
１．５〜５倍、その方向と直角方向に１．１〜３倍延伸
することが好ましい。さらに好ましくは一軸方向に２〜
４倍、その方向と直角方向に１．１〜２．５倍程度であ
る。The resin film used for the protective layer may be an unstretched film or a stretched film. When it is stretched, it is stretched at least uniaxially by a known method such as a roll method or a tenter method. The stretching may be carried out in one stage or may be carried out in multiple stages. Further, it may be biaxially stretched. Further, after stretching, if necessary, a heat setting treatment may be performed to stabilize the shape of the obtained pores. The stretching ratio is preferably about 1.5 to 10 times in area ratio. Specifically, in the case of uniaxial stretching, 1.5 to 1
It is preferable to stretch 0 times. More preferably 2
It is 7.5 times. In the case of biaxial stretching, it is preferable to stretch 1.5 to 5 times in the uniaxial direction and 1.1 to 3 times in the direction perpendicular to the direction. More preferably in the uniaxial direction 2 to
4 times, and 1.1 to 2.5 times in the direction perpendicular to that direction.
【００６２】本発明の光反射体は、前記のようにして得
られた多孔性樹脂シートの少なくとも表面及び／または
裏面に上記のようにして得られた保護層を熱圧着法、ま
たは接着剤を用いる接着法により積層することにより製
造される。また、上記多孔性樹脂シートの少なくとも表
面及び／または裏面に、熱可塑性樹脂等を含む有機溶媒
の溶液等を塗布、乾燥することによって製造することも
できる。本明細書では多孔性樹脂シートの表面とは光が
当たって反射する面を意味する。In the light reflector of the present invention, the protective layer obtained as described above is applied on at least the front surface and / or the back surface of the porous resin sheet obtained as described above by a thermocompression bonding method or an adhesive. It is manufactured by laminating according to the adhesive method used. It can also be manufactured by applying a solution of an organic solvent containing a thermoplastic resin or the like to at least the front surface and / or the back surface of the porous resin sheet and drying. In the present specification, the surface of the porous resin sheet means a surface which is irradiated with light and reflected.
【００６３】上記樹脂フィルムを多孔性樹脂シートに積
層する方法としては、各種接着剤を用い接着する方法、
熱圧着により融着する方法等が挙げられる。このときの
接着剤は、耐光性が高く、無色透明のものが好ましい。
また、接着強度を上げるために、多孔性樹脂シート及び
／または熱可塑性樹脂フィルムのそれぞれの表面にコロ
ナ放電処理を施すことが好ましい。As a method for laminating the above-mentioned resin film on the porous resin sheet, a method of bonding using various adhesives,
Examples include a method of fusion bonding by thermocompression. It is preferable that the adhesive at this time has high light resistance and is colorless and transparent.
Further, in order to increase the adhesive strength, it is preferable to subject each surface of the porous resin sheet and / or the thermoplastic resin film to corona discharge treatment.
【００６４】多孔性樹脂シートに樹脂の有機溶媒溶液を
塗布する場合は、上記樹脂を溶解した溶液が使用され
る。溶液濃度は、塗布性等を考慮すると、５〜５０重量
％程度が好ましい。さらに好ましい濃度は５〜３５重量
％である。When the organic solvent solution of the resin is applied to the porous resin sheet, a solution in which the above resin is dissolved is used. The solution concentration is preferably about 5 to 50% by weight in consideration of coating properties and the like. A more preferable concentration is 5 to 35% by weight.
【００６５】有機溶媒としては、ベンゾール、トリオー
ル、キシロール、ソルベントナフサ、ハイソルベンシイ
ナフサ等に代表される芳香族系溶剤、メタノール、エタ
ノール、ブチルアルコール、アミルアルコール等に代表
されるアルコール類溶剤、酢酸メチル、酢酸エチル、酢
酸ブチル、酢酸アミル、酢酸オクチル、酢酸ベンジル、
酢酸シクロヘキシル等に代表されるエステル系溶剤、ア
セトン、メチルアセトン、メチルエチルケトン、シクロ
ヘキサノン、グリコールメチルエーテル、グリコールエ
チルエーテル、グリコールブチルエーテル、ジオキサン
等に代表されるケトン系またはエーテル系溶剤等が挙げ
られる。Examples of the organic solvent include aromatic solvents represented by benzol, triol, xylol, solvent naphtha, high solvene naphtha, alcohol solvents represented by methanol, ethanol, butyl alcohol, amyl alcohol and acetic acid. Methyl, ethyl acetate, butyl acetate, amyl acetate, octyl acetate, benzyl acetate,
Examples thereof include ester solvents represented by cyclohexyl acetate and the like, ketone solvents represented by acetone, methylacetone, methyl ethyl ketone, cyclohexanone, glycol methyl ether, glycol ethyl ether, glycol butyl ether, dioxane and the like, and ether solvents.
【００６６】塗布する方法には特に制限はなく公知の方
法が適用できる。例えば、ディップコート、バーコー
ト、スプレーコート、ロールコート、スクリーンコート
等が挙げられる。均一な厚みに塗布することが好まし
い。また、塗布した後の乾燥条件として、５０〜１００
℃において１秒間〜１時間乾燥する方法が挙げられる。The coating method is not particularly limited, and known methods can be applied. For example, dip coating, bar coating, spray coating, roll coating, screen coating and the like can be mentioned. It is preferable to apply it to a uniform thickness. Moreover, as a drying condition after coating, 50 to 100
The method of drying at 1 degreeC for 1 second-1 hour is mentioned.
【００６７】本発明において、多孔性樹脂シートに積層
される保護層には３種類のものを使用できる。In the present invention, three types of protective layers can be used as the protective layer laminated on the porous resin sheet.
【００６８】即ち、第１の発明では多孔性樹脂シートに
積層して光反射体の剛性を向上させることを目的とする
ものであり、多孔性樹脂シート（通常剛性は３０〜８０
ｍｍ程度である）の剛性より高い材料からなる保護層が
使用される。しかしながら本発明の方法では第２発明の
ＵＶから保護する機能、第３発明の漏光防止機能を備え
た保護層を使用する方法がより好ましい。That is, the first invention aims to improve the rigidity of the light reflector by laminating it on the porous resin sheet, and the porous resin sheet (usually the rigidity is 30 to 80).
A protective layer made of a material having a rigidity higher than (for example, mm) is used. However, in the method of the present invention, the method of using the protective layer having the UV protection function of the second invention and the light leakage prevention function of the third invention is more preferable.
【００６９】第２発明の光反射体では、全光線透過率が
８０％以上である透明性に優れたフィルムを使用し、且
つ、該フィルムを多孔性樹脂シートの表面または両面に
積層する。表面に積層する場合は、保護層側に光を照射
するようにして使用する。この保護層をＵＶ保護層とい
う。ＵＶ保護層は、全光線透過率が８０％以上の透明性
を有するものであり、無色に近いものが好ましい。ま
た、ＵＶ保護層の透明性、得られる光反射体の剛性、光
反射率等を考慮すると、ＵＶ保護層の厚みは、１〜１０
０μｍ程度である。好ましくは１〜７０μｍであり、さ
らに好ましくは１〜５０μｍである。かかるＵＶ保護層
を多孔性樹脂シートの片表面または両面に積層すること
により、多孔性樹脂シートが紫外線等により劣化するこ
とが防止されると共に、多孔性樹脂シートの形態保持性
が改善される。In the light reflector of the second invention, a film having a total light transmittance of 80% or more and excellent in transparency is used, and the film is laminated on the surface or both surfaces of the porous resin sheet. When laminated on the surface, the protective layer side is irradiated with light before use. This protective layer is called a UV protective layer. The UV protective layer has transparency with a total light transmittance of 80% or more, and is preferably colorless. Further, considering the transparency of the UV protective layer, the rigidity of the obtained light reflector, the light reflectance, etc., the thickness of the UV protective layer is 1 to 10.
It is about 0 μm. It is preferably 1 to 70 μm, more preferably 1 to 50 μm. By laminating such a UV protection layer on one surface or both surfaces of the porous resin sheet, the porous resin sheet is prevented from being deteriorated by ultraviolet rays and the like, and the shape retention of the porous resin sheet is improved.
【００７０】第２発明において、多孔性樹脂シートの両
面にＵＶ保護層を積層する場合は、裏面側の層は、ＵＶ
保護層というよりは寧ろ第１発明の保護層のような補強
効果を与えることとなるので全光線透過率が８０％未満
の熱可塑性樹脂フィルムであっても良い。In the second invention, when a UV protective layer is laminated on both sides of the porous resin sheet, the layer on the back side is UV.
A thermoplastic resin film having a total light transmittance of less than 80% may be used because it provides a reinforcing effect rather than that of the protective layer of the first invention.
【００７１】但し、積層後の光反射体の剛性が１５０ｍ
ｍを超えるようなものであってはならない。このような
保護層として、例えば、厚みが３０〜５０μｍ程度の白
色ポリエチレンテレフタレートシートが挙げられる。However, the rigidity of the laminated light reflector is 150 m.
It must not exceed m. Examples of such a protective layer include a white polyethylene terephthalate sheet having a thickness of about 30 to 50 μm.
【００７２】多孔性樹脂シートの片面または両面にＵＶ
保護層が積層された第２発明に係わる光反射体は、剛性
が大き過ぎると、例えば、これを液晶表示装置のランプ
ホルダー等に加工する場合、丸味を帯びた形状に加工し
難く、作業性が悪いだけでなく、ランプホルダーの形状
が不規則になって、液晶表示部等に伝わる光量が少なく
なる。そのため、該光反射体の剛性は、好ましくは５０
〜１５０ｍｍ程度、より好ましくは７３〜１５０ｍｍ程
度である。UV on one or both sides of the porous resin sheet
If the light reflector according to the second aspect of the present invention in which the protective layer is laminated has too high rigidity, for example, when it is processed into a lamp holder of a liquid crystal display device, it is difficult to process it into a rounded shape, and workability is improved. Not only is it bad, but the shape of the lamp holder is irregular, and the amount of light transmitted to the liquid crystal display unit is reduced. Therefore, the rigidity of the light reflector is preferably 50.
It is about 150 mm, more preferably about 73 mm to 150 mm.
【００７３】第２発明に係わる光反射体は、紫外線等に
対する耐光性、及び多孔性樹脂シートの形態保持性を改
善するためになされたものである。多孔性樹脂シートの
少なくとも片表面に保護層として熱可塑性樹脂フィルム
が積層されていることに特徴がある。紫外線等に対する
耐光性としては、光反射体の保護層表面に８０℃におい
て４００ＭＪ／ｍ2 （メガジュール／ｍ2 ）の紫外線を
照射した後の該光反射体の波長４５０ｎｍ及び５５０ｎ
ｍの光線の反射率の低下率が共に１０％未満であること
が好ましい。さらに好ましくは７％未満である。該低下
率が１０％以上であると、光反射体として実際に使用し
たときの輝度が経時低下し、明るさを維持するための消
費電力が過大となり好ましくない。The light reflector according to the second invention is made to improve the light resistance to ultraviolet rays and the like and the shape retention of the porous resin sheet. It is characterized in that a thermoplastic resin film is laminated as a protective layer on at least one surface of the porous resin sheet. The light resistance to ultraviolet rays and the like is as follows: the protective layer surface of the light reflector is irradiated with ultraviolet rays of 400 MJ / m 2 (megajoule / m 2 ) at 80 ° C., and the wavelength of the light reflector is 450 nm and 550 n.
It is preferable that both the reduction rates of the reflectance of the light rays of m are less than 10%. More preferably, it is less than 7%. When the reduction rate is 10% or more, the brightness when actually used as a light reflector decreases over time, and the power consumption for maintaining the brightness becomes excessive, which is not preferable.
【００７４】ここで４００ＭＪ／ｍ2の紫外線とは、例
えば、Ｑ−ＰＡＮＥＬ社製、ＵＶＡ３５１型紫外線発光
ランプ（主波長３５１ｎｍ）を用いて、約１０ｃｍ離れ
た位置から試料に対し、８０℃において約１０００時
間、紫外線を照射したときの紫外線量に相当する。通
常、液晶表示装置のバックライトユニットのランプホル
ダーは、紫外線に暴露され易い部位であるが、上記線量
の紫外線が照射された場合、波長４５０〜５５０ｎｍの
光線の反射率の低下率が１０％未満であれば実用上問題
がない。Here, 400 MJ / m 2 of ultraviolet light means, for example, using a UVA351 type ultraviolet light emitting lamp (main wavelength 351 nm) manufactured by Q-PANEL, at a temperature of about 10 cm from a position about 10 cm away from the sample at about 80 ° C. This corresponds to the amount of ultraviolet rays when irradiated with ultraviolet rays for 1000 hours. Usually, the lamp holder of the backlight unit of the liquid crystal display device is a part that is easily exposed to ultraviolet rays, but when irradiated with the above-mentioned dose of ultraviolet rays, the decrease rate of the reflectance of light having a wavelength of 450 to 550 nm is less than 10%. If so, there is no problem in practical use.
【００７５】第３発明では、保護層として、全光線透過
率が２０％未満である光線透過性の低いフィルムを使用
し、且つ、該フィルムを多孔性樹脂シートの裏面に積層
する。この場合、多孔性樹脂シート側に光を照射するよ
うにして使用する。この保護層を漏光防止保護層とい
う。漏光防止保護層は、光反射体の反射率をより一層高
めるために、光線透過性の低い不透明のものが好まし
い。具体的には、全光線透過率が２０％未満であるフィ
ルムである。好ましくは、全光線透過率が１５％未満で
ある。かかる光線透過性の低いフィルムを多孔性樹脂シ
ートの裏面に積層することにより、多孔性樹脂シート層
で反射されずに、これを透過する光線があった場合で
も、効率良く多孔性樹脂シート層へ反射することができ
る。また、漏光防止保護層を多孔性樹脂シートの裏面に
積層することにより、多孔性樹脂シートの形態保持性が
改善される。In the third invention, as the protective layer, a film having a total light transmittance of less than 20% and a low light transmittance is used, and the film is laminated on the back surface of the porous resin sheet. In this case, the porous resin sheet is used by irradiating it with light. This protective layer is called a light leakage prevention protective layer. The light leakage prevention protective layer is preferably opaque with low light transmittance in order to further increase the reflectance of the light reflector. Specifically, it is a film having a total light transmittance of less than 20%. Preferably, the total light transmittance is less than 15%. By laminating such a low light-transmitting film on the back surface of the porous resin sheet, even if there is a light ray that is transmitted through the porous resin sheet layer without being reflected by the porous resin sheet layer, the porous resin sheet layer can be efficiently transferred. Can be reflected. Further, by stacking the light leakage prevention protective layer on the back surface of the porous resin sheet, the shape retention of the porous resin sheet is improved.
【００７６】全光線透過率が２０％未満である漏光防止
保護層として、上記の保護層を形成する樹脂に無機充填
剤を５〜７０重量％含有させて得られたフィルムが挙げ
られる。無機充填剤としては、硫酸バリウム、硫酸カル
シウム、硫酸マグネシウム、硫酸アルミニウム、炭酸バ
リウム、炭酸カルシウム、塩化マグネシウム、炭酸マグ
ネシウム、塩基性炭酸マグネシウム等の金属塩、水酸化
マグネシウム、水酸化アルミニウム、水酸化カルシウム
等の金属水酸化物、酸化カルシウム、酸化亜鉛、酸化マ
グネシウム、酸化チタン、アルミナ、シリカ等の金属酸
化物等が挙げられる。これらの内、酸化チタン及び炭酸
カルシウムが好ましい。Examples of the light leakage prevention protective layer having a total light transmittance of less than 20% include a film obtained by adding 5 to 70% by weight of an inorganic filler to the resin forming the protective layer. Examples of the inorganic filler include barium sulfate, calcium sulfate, magnesium sulfate, aluminum sulfate, barium carbonate, calcium carbonate, magnesium chloride, magnesium carbonate, basic magnesium carbonate, and other metal salts, magnesium hydroxide, aluminum hydroxide, calcium hydroxide. And metal oxides such as calcium oxide, zinc oxide, magnesium oxide, titanium oxide, alumina, and silica. Of these, titanium oxide and calcium carbonate are preferred.
【００７７】また、第３発明及び第４発明に用いる全光
線透過率が２０％未満である漏光防止保護層として、上
記樹脂に該樹脂と非相溶性の樹脂を分散させたフィルム
を少なくとも１軸方向に延伸して、樹脂相互間に空孔を
発生させて白化させたフィルムが挙げられる。さらに、
上記樹脂から得られたフィルムの表面に白色塗料を塗布
したフィルムが挙げられる。Further, as the light leakage prevention protective layer having a total light transmittance of less than 20% used in the third and fourth inventions, a film in which the resin incompatible with the resin is dispersed in at least one axis A film that has been stretched in the direction and whitened by generating pores between the resins can be used. further,
A film obtained by applying a white paint on the surface of the film obtained from the above resin can be mentioned.
【００７８】漏光防止保護層の剛性、光反射率等を考慮
すると、漏光防止保護層の厚みは、３０〜１５０μｍ程
度、さらに好ましくは５０〜１５０μｍである。Considering the rigidity and light reflectance of the light leakage prevention protective layer, the thickness of the light leakage prevention protective layer is about 30 to 150 μm, and more preferably 50 to 150 μm.
【００７９】第３発明に係わる光反射体はその剛性が小
さ過ぎると、例えばこれを液晶表示装置の導光板下の光
反射シートとして使用した場合、形態保持性が充分でな
く、ユニットへの装着がし難く、作業性に問題がある。
かかる観点から、第３発明に係わる光反射体の剛性は少
なくとも１００ｍｍであることが好ましい。If the rigidity of the light reflector according to the third invention is too small, for example, when it is used as a light reflection sheet under the light guide plate of a liquid crystal display device, the shape retention is insufficient and the light reflector is mounted on the unit. It is difficult to remove and there is a problem in workability.
From this point of view, the rigidity of the light reflector according to the third invention is preferably at least 100 mm.
【００８０】漏光防止保護層の厚みは、得られる光反射
体の剛性に影響を及ぼす。第３発明に係わる光反射体の
剛性の上限には特に制限はないが、光反射体の剛性を高
くすると必然的に漏光防止保護層の厚みが厚くなる。こ
のことは、光反射装置全体の小型化、軽量化、薄肉化等
を考慮する場合には好ましくない。かかる観点から、漏
光防止保護層の厚みの上限は１５０μｍ程度及び剛性の
上限は約２００ｍｍであることが好ましい。第４発明の
光反射体に積層する漏光防止保護層についても同様であ
る。The thickness of the light leakage prevention protective layer affects the rigidity of the obtained light reflector. The upper limit of the rigidity of the light reflector according to the third invention is not particularly limited, but if the rigidity of the light reflector is increased, the thickness of the light leakage prevention protective layer inevitably increases. This is not preferable in consideration of downsizing, weight reduction, and thinning of the entire light reflecting device. From this viewpoint, the upper limit of the thickness of the light leakage prevention protective layer is preferably about 150 μm and the upper limit of the rigidity thereof is preferably about 200 mm. The same applies to the light leakage prevention protective layer laminated on the light reflector of the fourth invention.
【００８１】上記いずれの保護層にも、本発明の目的を
妨げない範囲内で紫外線吸収剤、安定剤等他の添加剤を
添加しても良い。Other additives such as an ultraviolet absorber and a stabilizer may be added to any of the above protective layers within a range that does not impair the object of the present invention.
【００８２】本発明の多孔性樹脂シートに保護層を積層
した光反射体は、例えば、液晶表示装置のバックライト
ユニットの光反射体等として好ましく用いられる。具体
的には、第１、第２及び第４発明に係わる光反射体は、
液晶表示装置のバックライトユニットを形成するランプ
ホルダー及び導光板下の光反射シートとして、また、第
１、第３及び第４発明に係わる光反射体は、液晶表示装
置のバックライトユニットを形成する導光板下の光反射
シートとして好ましく使用し得る。さらに好ましくは、
第２発明に係わる光反射体は、上記ランプホルダーとし
て、第３発明に係わる光反射体は、上記導光板下の光反
射シートとして好ましく使用し得る。The light reflector having the protective layer laminated on the porous resin sheet of the present invention is preferably used, for example, as a light reflector of a backlight unit of a liquid crystal display device. Specifically, the light reflector according to the first, second and fourth inventions is
The lamp holder and the light reflecting sheet under the light guide plate forming the backlight unit of the liquid crystal display device, and the light reflector according to the first, third and fourth inventions form the backlight unit of the liquid crystal display device. It can be preferably used as a light reflection sheet under a light guide plate. More preferably,
The light reflector according to the second invention can be preferably used as the lamp holder, and the light reflector according to the third invention can be preferably used as the light reflection sheet under the light guide plate.
【００８３】但し、第４発明に係わる光反射体を液晶表
示装置のバックライトユニットのランプホルダーとして
用いる場合は、光反射体の剛性が５０〜１５０ｍｍとな
るように、漏光防止保護層の厚みを上記範囲内の内に適
宜選択することが好ましい。また、導光板下の光反射シ
ートとして用いる場合は、光反射体の剛性が少なくとも
１００ｍｍとなるように、漏光防止保護層の厚みを上記
範囲内の内に適宜選択することが好ましい。However, when the light reflector according to the fourth invention is used as a lamp holder of a backlight unit of a liquid crystal display device, the thickness of the light leakage prevention protective layer is set so that the rigidity of the light reflector is 50 to 150 mm. It is preferable to appropriately select within the above range. When used as a light reflection sheet under the light guide plate, it is preferable to appropriately select the thickness of the light leakage prevention protective layer within the above range so that the rigidity of the light reflector is at least 100 mm.
【００８４】本発明で用いる多孔性ポリオレフィン樹脂
層は光反射性が極めて良好であり、しかも剛性が低く、
しかも保護層を積層することで剛性を自由に調節するこ
とができる。The porous polyolefin resin layer used in the present invention has extremely good light reflectivity and low rigidity,
Moreover, the rigidity can be freely adjusted by laminating the protective layer.
【００８５】特に光反射体を断面半径２ｍｍ以下の曲線
の光反射体として使用する場合は、自由に曲げられるよ
うな柔軟性と形状を保持できるような剛性を必要とす
る。Particularly when the light reflector is used as a light reflector having a curved line with a radius of 2 mm or less, it is necessary to have flexibility so that it can be freely bent and rigidity so as to maintain its shape.
【００８６】本発明の方法では保護層の材質及び／又は
厚さを調節して光反射体の剛性を望ましい値にすること
が可能であり、例えば液晶表示装置のバックライトユニ
ットのランプホルダーとして好ましく使用できる。In the method of the present invention, it is possible to adjust the material and / or the thickness of the protective layer to make the rigidity of the light reflector a desired value. For example, it is preferable for a lamp holder of a backlight unit of a liquid crystal display device. Can be used.
【００８７】次いで、上記のようにして得られた光反射
体を、例えば、液晶表示装置のバックライトユニットを
形成する光源部のランプホルダー用資材、および導光板
の下部に配設される光反射シートとして用いる代表的例
を図面に示して説明する。Next, the light reflector obtained as described above is used, for example, as a material for a lamp holder of a light source forming a backlight unit of a liquid crystal display device, and a light reflector disposed below a light guide plate. A typical example used as a sheet will be described with reference to the drawings.
【００８８】図１は、代表的な液晶表示装置のバックラ
イトユニットの断面図である。図において、光源１はそ
の側面が所定の間隔を置いてランプホルダー２により湾
曲状に覆われる。ランプホルダー２は、第２発明に係わ
る光反射体から形成されたランプホルダーを示し、多孔
性樹脂シート２１の片表面にＵＶ保護層２２が積層さ
れ、光源１とＵＶ保護層２２とが相対する向きに配設さ
れ、所定の間隔を置いて湾曲状に光源１を覆い、その両
端は導光板４に結合して固定される。導光板下光反射シ
ート３は、第２発明に係わる光反射体から形成された光
反射シートを示し、多孔性樹脂シート３１の片表面にＵ
Ｖ保護層３２が積層され、ＵＶ保護層３２を介して導光
板４の下方に配設される。導光板４の上方には光拡散シ
ート５が配設される。さらに、光拡散シート５の他の面
にはレンズシート６が配設される。光源１が図１のよう
に導光板４の片側面のみに配設される場合は、通常、導
光板４は光源１に近い部分の厚みを厚くし、光源１から
遠くなるにつれてその厚みを薄くする。この場合、漏光
防止のために、光源１が配設される側面以外の他の３側
面に側面用光反射シートを積層することが好ましい。側
面用光反射シートとして、本発明の第３及び第４発明に
係わる２種の光反射体が挙げられる。光源１が導光板４
の両側面に配設される場合は、通常、導光板４の厚みは
一定とされる。図２は、図１に示した液晶表示装置とラ
ンプホルダー部が同じ構造であり、導光板下光反射シー
トとして裏面に漏光防止保護層が積層された液晶表示装
置のバックライトユニットの斜視図である。図におい
て、ランプホルダー２は、第２発明または第４発明に係
わる光反射体から形成されたランプホルダーを示し、多
孔性樹脂シート２１の片表面にＵＶ保護層２２が積層さ
れ、光源１とＵＶ保護層２２とが相対する向きに配設さ
れる。導光板下光反射シート３は、第３発明に係わる光
反射体から形成された光反射シートを示し、多孔性樹脂
シート３１の裏面に漏光防止保護層３３が積層され、多
孔性樹脂シート３１を介して導光板４の下方に配設され
る。その他の構造は図１に示した液晶表示装置のバック
ライトユニットと同様である。FIG. 1 is a sectional view of a backlight unit of a typical liquid crystal display device. In the figure, a side surface of a light source 1 is covered with a lamp holder 2 in a curved shape at a predetermined interval. The lamp holder 2 is a lamp holder formed of the light reflector according to the second aspect of the invention. The UV protective layer 22 is laminated on one surface of the porous resin sheet 21, and the light source 1 and the UV protective layer 22 face each other. The light sources 1 are arranged so as to face each other and are curved at predetermined intervals, and both ends thereof are coupled and fixed to the light guide plate 4. The light reflecting sheet under the light guide plate 3 is a light reflecting sheet formed from the light reflector according to the second invention, and U is provided on one surface of the porous resin sheet 31.
The V protection layer 32 is laminated, and is disposed below the light guide plate 4 with the UV protection layer 32 interposed therebetween. A light diffusion sheet 5 is arranged above the light guide plate 4. Further, a lens sheet 6 is arranged on the other surface of the light diffusion sheet 5. When the light source 1 is arranged only on one side surface of the light guide plate 4 as shown in FIG. 1, the light guide plate 4 is usually made thicker in a portion close to the light source 1 and thinner as the distance from the light source 1 is increased. To do. In this case, in order to prevent light leakage, it is preferable to stack a side-face light reflection sheet on three side faces other than the side face on which the light source 1 is arranged. Examples of the side light reflection sheet include two types of light reflectors according to the third and fourth aspects of the present invention. Light source 1 is light guide plate 4
In the case where the light guide plates 4 are arranged on both side surfaces, the thickness of the light guide plate 4 is usually constant. FIG. 2 is a perspective view of a backlight unit of the liquid crystal display device having the same structure as the liquid crystal display device shown in FIG. 1 and a lamp holder part, and a light leakage prevention protective layer is laminated on the back surface as a light reflection sheet under the light guide plate. is there. In the figure, a lamp holder 2 is a lamp holder formed of a light reflector according to the second invention or the fourth invention, in which a UV protection layer 22 is laminated on one surface of a porous resin sheet 21, and the light source 1 and the UV The protective layer 22 and the protective layer 22 are disposed so as to face each other. The light guide sheet under the light guide plate 3 is a light reflection sheet formed from the light reflector according to the third invention, in which the light leakage prevention protective layer 33 is laminated on the back surface of the porous resin sheet 31, and the porous resin sheet 31 is provided. It is arranged below the light guide plate 4 via. Other structures are similar to those of the backlight unit of the liquid crystal display device shown in FIG.
【００８９】本発明の第２発明または第４発明に係わる
光反射体は、ランプホルダー２及び導光板下光反射シー
ト３として使用し得る。また、本発明の第３発明又は第
４発明に係わる光反射体は、導光板下光反射シート３と
して使用し得る。好ましい形態として、第２発明の光反
射体をランプホルダー２として、第３発明の光反射体を
導光板下光反射シート３として使用する形態が挙げられ
る。The light reflector according to the second or fourth invention of the present invention can be used as the lamp holder 2 and the light reflecting sheet 3 under the light guide plate. Further, the light reflector according to the third or fourth invention of the present invention can be used as the light guide plate lower light reflection sheet 3. As a preferred embodiment, the light reflector of the second invention is used as the lamp holder 2, and the light reflector of the third invention is used as the light guide plate lower light reflection sheet 3.
【００９０】光源１には、通常、冷陰極管が使用され
る。導光板４には、ポリメチルメタクリレートシートが
汎用される。光拡散シート５には、ポリエチレンテレフ
タレートシート、またはポリエチレンテレフタレートフ
ィルムの表面エンボス処理品が汎用される。また、レン
ズシート６には、ポリカーボネートシート、ポリエチレ
ンテレフタレートシートの表面にポリカーボネートまた
はポリアクリレート等を塗布したシートが汎用される。A cold cathode tube is usually used as the light source 1. A polymethylmethacrylate sheet is commonly used for the light guide plate 4. For the light diffusion sheet 5, a polyethylene terephthalate sheet or a surface-embossed polyethylene terephthalate film is generally used. As the lens sheet 6, a polycarbonate sheet or a polyethylene terephthalate sheet having a surface coated with polycarbonate or polyacrylate is generally used.
【００９１】光源１から生じた光線はランプホルダー
２、導光板下光反射シート３、導光板４および光拡散シ
ート５に照射される。光源１から生じた光線は、直接も
しくは、ランプホルダー２で反射され、導光板４を経由
し、光の一部を拡散シート５に照射し、更に導光板４を
経由する光の残部を導光板下光反射シート３で反射させ
て、再び導光板４に戻して光拡散シート５へ照射され、
レンズシート６から系外に照射される。The light beam generated from the light source 1 is applied to the lamp holder 2, the light guide plate lower light reflection sheet 3, the light guide plate 4 and the light diffusion sheet 5. The light beam generated from the light source 1 is directly or reflected by the lamp holder 2, passes through the light guide plate 4, irradiates a part of the light to the diffusion sheet 5, and further, the rest of the light passing through the light guide plate 4 is guided to the light guide plate. The light is reflected by the lower light reflection sheet 3, returned to the light guide plate 4 and irradiated onto the light diffusion sheet 5,
It is irradiated from the lens sheet 6 to the outside of the system.
【００９２】本発明に係わる光反射体は、ワードプロセ
ッサー、パーソナルコンピュータ、テレビジョン等の上
記の如き液晶表示装置のバックライトユニットを形成す
る光反射体の他、照明器具、複写機、プロジェクター方
式のディスプレイ、ファクシミリ、電子黒板等を形成す
る光反射体として使用し得る。また、本発明の光反射体
を使用した光反射装置および該光反射装置を備えたワー
ドプロセッサー、パーソナルコンピュータ、テレビジョ
ン等の上記の如き液晶表示装置のバックライトユニット
を形成する光反射体の他、照明器具、複写機、プロジェ
クター方式のディスプレイ、ファクシミリ、電子黒板等
を提供することができる。The light reflector according to the present invention is a light reflector forming a backlight unit of a liquid crystal display device such as a word processor, a personal computer, a television, etc., as well as a lighting fixture, a copying machine and a projector type display. , A facsimile, an electronic blackboard, or the like, and can be used as a light reflector. Further, in addition to a light reflector that uses the light reflector of the present invention and a light reflector that forms a backlight unit of the above-described liquid crystal display device such as a word processor, personal computer, or television equipped with the light reflector, It is possible to provide a lighting fixture, a copying machine, a projector-type display, a facsimile, an electronic blackboard, and the like.
【００９３】[0093]
【実施例】以下、実施例を示して本発明についてさらに
詳細に説明する。但し、本発明はこれらの実施例に限定
されるものではない。EXAMPLES The present invention will be described in more detail below with reference to examples. However, the present invention is not limited to these examples.
【００９４】尚、開孔率、輝度、光線反射率、光線透過
率、剛性、紫外線照射試験及び光線反射率の低下率は下
記の方法により測定した値である。The aperture ratio, brightness, light ray reflectance, light ray transmittance, rigidity, ultraviolet ray irradiation test and light ray reflectance decrease rate are values measured by the following methods.
【００９５】（１）開孔率の測定方法（％） 用いた樹脂組成物の真比重（Ａ）と得られた多孔性樹脂
シートの嵩比重（Ｂ）から数式（１）〔数１〕(1) Method of Measuring Porosity (%) From the true specific gravity (A) of the resin composition used and the bulk specific gravity (B) of the obtained porous resin sheet, the numerical formula (1) [Equation 1]
【００９６】[0096]
【数１】 Ｃ（％）＝（１−Ｂ／Ａ）Ｘ１００ ・・・（１） により開孔率（Ｃ）を算出する。## EQU1 ## The open area ratio (C) is calculated by C (%) = (1-B / A) X100 (1).
【００９７】（２）輝度の測定方法（相対値） 図１に示した、光源、ランプホルダー、導光板、導光板
下光反射シート、光拡散シート及びレンズシートを主要
構成部とする液晶表示装置のバックライトユニットのラ
ンプホルダー及び、導光板下光反射シートとして、本発
明の実施例または比較例で得られた光反射体を装着し、
導光板上での輝度を輝度計（ミノルタカメラ（株）製、
形式：ＬＳ−１１０型）を用いて測定する。光反射体を
装着するに際しては、ＵＶ保護層が積層された光反射体
はＵＶ保護層側に光が照射され、漏光防止保護層が積層
された光反射体は多孔性樹脂シート側に光が照射される
ように配設する。(2) Luminance Measuring Method (Relative Value) A liquid crystal display device shown in FIG. 1, which has the light source, the lamp holder, the light guide plate, the light guide sheet under the light guide plate, the light diffusing sheet and the lens sheet as main components. As a lamp holder of the backlight unit and a light reflection sheet under the light guide plate, the light reflector obtained in the example or the comparative example of the present invention is attached,
The luminance on the light guide plate is measured by a luminance meter (Minolta Camera Co., Ltd.,
Format: LS-110 type). When the light reflector is attached, the light reflector having the UV protection layer laminated is irradiated with light on the UV protection layer side, and the light reflector having the light leakage prevention protection layer laminated has light on the porous resin sheet side. Arranged to be irradiated.
【００９８】尚、輝度は、ランプホルダー部に厚み１１
３μｍの白色ポリエチレンテレフタレートシート
（（株）きもと製、商品名：レフホワイトＲＷ７５Ｃ）
を用い、導光板下に配設される光反射シートとして、厚
み１８８μｍの白色ポリエチレンテレフタレートシート
（東レ（株）製、商品名：Ｅ−６０）を用いた時の輝度
を１００とした相対値で示す。 測定条件： 光源：冷陰極管（蛍光灯）東芝ライテック製 形式：ＦＣ２ＥＸ／２００Ｔ２Ｆ 管直径：２．５ｍｍ、 管長：２００ｍｍ 電流 ：５ｍＡ 、 電圧：４５０Ｖ 試料の大きさ：２２０ｍｍ ｘ １６５ｍｍ 試料と輝度計の受光レンズの距離：１００ｍｍ （３）全光線透過率の測定方法（％） 霞度計（日本電色工業（株）製、形式：ＮＤＨ−３００
Ａ）を用いて測定する。尚、有機溶媒溶液を塗布、乾燥
させた保護層は、金属板に同条件下で塗布、乾燥して得
たフィルムについて測定する。The brightness of the lamp holder is 11
3 μm white polyethylene terephthalate sheet (manufactured by Kimoto Co., Ltd., product name: Ref White RW75C)
As a light-reflecting sheet disposed under the light guide plate, a relative value with a brightness of 100 when a white polyethylene terephthalate sheet (manufactured by Toray Industries, Inc., trade name: E-60) having a thickness of 188 μm was used. Show. Measurement conditions: Light source: cold cathode tube (fluorescent lamp) manufactured by Toshiba Lighting & Technology Model: FC2EX / 200T2F Tube diameter: 2.5 mm, tube length: 200 mm Current: 5 mA, voltage: 450 V Sample size: 220 mm x 165 mm Sample and luminance meter Distance of light receiving lens: 100 mm (3) Measuring method of total light transmittance (%) Humidity meter (Nippon Denshoku Industries Co., Ltd., model: NDH-300)
It measures using A). The protective layer coated with the organic solvent solution and dried is measured on the film obtained by coating and drying the metal plate under the same conditions.
【００９９】（４）剛性の測定方法（ｍｍ） ＪＩＳ−Ｌ１０９６に規定される方法（カンチレバー
法）に準拠して測定する。 （５）紫外線照射試験 紫外線照射試験機（（株）東洋精機製作所製、機種名：
ＡＴＬＡＳ−ＵＶＣＯＮ、形式：ＡＳＴＭ−Ｇ５３、紫
外線発光ランプ：Ｑ−ＰＡＮＥＬ社製、形式：ＵＶＡ３
５１、主波長：３５１ｎｍ）を用いて、８０℃におい
て、得られた光反射体の保護層側の表面１ｍ2当たり４
００ＭＪ（メガジュール）の紫外線を照射する。(4) Method of measuring rigidity (mm) The rigidity is measured according to the method (cantilever method) specified in JIS-L1096. (5) UV irradiation test UV irradiation tester (manufactured by Toyo Seiki Co., Ltd., model name:
ATLAS-UVCON, type: ASTM-G53, ultraviolet light emitting lamp: Q-PANEL, type: UVA3
51, dominant wavelength: 351 nm) at 80 ° C., 4 per 1 m 2 of the surface of the obtained light reflector on the protective layer side.
Irradiate with ultraviolet rays of 00 MJ (mega joule).
【０１００】（６）光線反射率の測定方法（％） ＪＩＳ−Ｋ７１０５の測定法Ｂに準拠して、分光光度計
（日立製作所（株）製、形式：Ｕ−３４００）を用いて
波長３００〜８００ｎｍの波長別反射率を測定し、波長
４５０及び５５０ｎｍの光の反射率を代表値として用い
る。尚、標準反射板として酸化アルミニウムを用いた時
の反射率を１００とした時の相対値で示す。ＵＶ保護層
が積層された光反射体については、ＵＶ保護層側に光を
照射し、漏光防止保護層が積層された光反射体について
は、多孔性樹脂シート側に光を照射して測定する。(6) Light reflectance measurement method (%) In accordance with JIS-K7105 measurement method B, a spectrophotometer (manufactured by Hitachi, Ltd., model: U-3400) having a wavelength of 300 to 300 is used. The reflectance for each wavelength of 800 nm is measured, and the reflectance of light of wavelengths 450 and 550 nm is used as a representative value. In addition, it shows with the relative value when the reflectance when aluminum oxide is used as a standard reflection plate is set to 100. For the light reflector having the UV protective layer laminated, the UV protective layer side is irradiated with light, and for the light reflector having the light leakage prevention protective layer laminated, the porous resin sheet side is irradiated with light. .
【０１０１】（７）光線反射率の低下率（％） 第（５）項に記載した紫外線照射試験の有無の試料につ
いて、第（６）項に記載した方法により光線反射率を測
定し、波長４５０及び５５０ｎｍの光の反射率の低下率
（％）を求める。(7) Reduction rate of light reflectance (%) The light reflectance of the sample with or without the ultraviolet irradiation test described in the item (5) was measured by the method described in the item (6) to determine the wavelength. A reduction rate (%) of reflectance of light at 450 and 550 nm is obtained.
【０１０２】実施例１ 密度０．９２ｇ／ｃｍ3、メルトインデックス（ＭＩ）
２ｇ／１０ｍｉｎの線状低密度ポリエチレン（三井石油
化学工業（株）製、商品名：ウルトゼックス２０２１
Ｌ：以下、ＬＬＤＰＥという）１００重量部に対し、平
均粒子径０．９４μｍの沈降性硫酸バリウム（バライト
工業（株）製、商品名：ＨＤ）２３０重量部、紫外線吸
収剤（アデカアーガス（株）製、商品名：ＭＡＲＫ Ｌ
Ａ−３６）０．５重量部、ステアリン酸カルシウム３重
量部をタンブラーミキサーを用いて混合して樹脂組成物
を得た。得られた樹脂組成物をベント型二軸押出機を用
いてペレット状に加工した。このペレットをＴダイが装
着された押出機を用いて、２３０℃において溶融押出し
て未延伸シートを得た。得られた未延伸シートを８５℃
に加熱した予熱ロールと延伸ロールとの間で６．５倍の
延伸倍率で一軸延伸し、表１に示した厚みを有する多孔
性樹脂シートを得た。Example 1 Density 0.92 g / cm 3 , melt index (MI)
2 g / 10 min linear low density polyethylene (manufactured by Mitsui Petrochemical Industry Co., Ltd., trade name: ULTOZEX 2021)
L: hereinafter referred to as LLDPE) 230 parts by weight of precipitated barium sulfate having an average particle diameter of 0.94 μm (manufactured by Barite Industry Co., Ltd., trade name: HD) per 100 parts by weight, an ultraviolet absorber (Adeka Argus Co., Ltd.) Product name: MARK L
A-36) 0.5 part by weight and 3 parts by weight of calcium stearate were mixed using a tumbler mixer to obtain a resin composition. The obtained resin composition was processed into pellets using a vent type twin-screw extruder. These pellets were melt-extruded at 230 ° C. using an extruder equipped with a T-die to obtain an unstretched sheet. The unstretched sheet obtained is 85 ° C.
The film was uniaxially stretched at a stretching ratio of 6.5 times between the preheating roll and the stretching roll, which were heated to 1, to obtain a porous resin sheet having the thickness shown in Table 1.
【０１０３】得られた多孔性樹脂シートの開孔率、およ
び光線反射率を前述の方法で評価した。評価結果を表１
に示す。The porosity and light reflectance of the obtained porous resin sheet were evaluated by the above-mentioned methods. Table 1 shows the evaluation results
Shown in
【０１０４】また、この多孔性樹脂シートの表面にＵＶ
保護層としてポリエチレンテレフタレート（以下、ＰＥ
Ｔという）フィルム（ダイアホイルヘキスト（株）製、
商品名：ダイアホイルＨ１００Ｃ、厚み：１２μｍ、全
光線透過率：９０％）を接着剤（大日精化工業（株）
製、商品名：セイカボンドＥ−２９５／Ｃ−７５Ｎ）を
用いて接着、積層して光反射体１を得た。この光反射体
１の光線反射率、剛性、及び光線反射率の低下率を上記
方法により測定し、その結果を表１に示す。Further, the surface of this porous resin sheet is exposed to UV.
Polyethylene terephthalate (hereinafter PE) as a protective layer
T) film (manufactured by Dia foil Hoechst Co., Ltd.,
Product name: Dia foil H100C, Thickness: 12 μm, Total light transmittance: 90%) Adhesive (Dainichi Seika Kogyo Co., Ltd.)
Product name: Seika Bond E-295 / C-75N) was used for adhesion and lamination to obtain a light reflector 1. The light reflectance, the rigidity, and the reduction rate of the light reflectance of this light reflector 1 were measured by the above methods, and the results are shown in Table 1.
【０１０５】また、得られた光反射体１を、液晶表示装
置のバックライトユニットのランプホルダー及び導光板
下の光反射シートとして使用して、図１に示したと同様
の構造の光反射装置を組み立てた。尚、この光反射装置
においてＵＶ保護層側に光が照射されるよう配設した。
得られた光反射装置の輝度を上記方法により測定し、結
果を表１に示す。Further, the obtained light reflector 1 is used as a lamp holder of a backlight unit of a liquid crystal display device and a light reflecting sheet under a light guide plate to obtain a light reflecting device having a structure similar to that shown in FIG. Assembled In addition, in this light reflecting device, the UV protective layer side was arranged so as to be irradiated with light.
The brightness of the obtained light reflecting device was measured by the above method, and the results are shown in Table 1.
【０１０６】実施例２ 実施例１と同様の方法で多孔性樹脂シートを得、得られ
た多孔性樹脂シートの表面にアクリル系コート剤（三宝
化学研究所製、商品名：ＳＡＮＢＯ−ＲＡＴＥ、溶媒：
酢酸エチル、溶液濃度：１０ｗｔ％）を塗工し、１００
℃で５分間乾燥して厚み５μｍ、全光線透過率９６％の
ＵＶ保護層を形成、積層して光反射体２を得た。得られ
た光反射体２を用いて実施例１と同様にして光反射装置
を組み立てた。得られた多孔性樹脂シート、ＵＶ保護
層、光反射体２及び光反射装置について実施例１と同様
にして評価し、その評価結果を表１に示す。Example 2 A porous resin sheet was obtained in the same manner as in Example 1, and an acrylic coating agent (manufactured by Sanpo Chemical Laboratory, trade name: SANBO-RATE, solvent) was obtained on the surface of the obtained porous resin sheet. :
Ethyl acetate, solution concentration: 10 wt%) was applied and 100
By drying at 5 ° C. for 5 minutes, a UV protective layer having a thickness of 5 μm and a total light transmittance of 96% was formed and laminated to obtain a light reflector 2. Using the obtained light reflector 2, a light reflecting device was assembled in the same manner as in Example 1. The obtained porous resin sheet, UV protective layer, light reflector 2 and light reflecting device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 1.
【０１０７】実施例３ ＬＬＤＰＥと硫酸バリウムの配合割合をそれぞれ表１に
示す重量割合とした以外、実施例１と同様の方法で厚み
１５０μｍ多孔性樹脂シートを得た。得られた多孔性樹
脂シートの片表面に実施例１と同様の方法で、ＵＶ保護
層として、ポリメチルメタアクリレート（以下、ＰＭＭ
Ａという）フィルム（三菱レイヨン（株）製、商品名：
アクリプレンＨＢＳ００１、厚み３５μｍ、全光線透過
率：９４％）を積層して光反射体３を得た。得られた光
反射体３を用いて実施例１と同様にして光反射装置を組
み立てた。得られた多孔性樹脂シート、ＵＶ保護層、光
反射体３及び光反射装置について実施例１と同様にして
評価し、その評価結果を表１に示す。Example 3 A porous resin sheet having a thickness of 150 μm was obtained in the same manner as in Example 1 except that the mixing ratios of LLDPE and barium sulfate were changed to the weight ratios shown in Table 1. Polymethylmethacrylate (hereinafter referred to as PMM) was used as a UV protective layer on one surface of the obtained porous resin sheet in the same manner as in Example 1.
A film (made by Mitsubishi Rayon Co., Ltd., trade name:
Acryprene HBS001, thickness 35 μm, total light transmittance: 94%) was laminated to obtain a light reflector 3. Using the obtained light reflector 3, a light reflecting device was assembled in the same manner as in Example 1. The obtained porous resin sheet, UV protective layer, light reflector 3 and light reflecting device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 1.
【０１０８】実施例４ ポリオレフィン樹脂として密度０．９ｇ／ｃｍ3、ＭＩ
１．５ｇ／１０ｍｉｎのプロピレンホモポリマー （三
井東圧化学（株）製、商品名：ノーブレン、ＦＯ−５０
Ｆ：以下、ＰＰという）を用いた以外、実施例１と同様
の方法で厚み１５０μｍの多孔性樹脂シートを得た。得
られた多孔性樹脂シートの片表面に実施例２と同様の方
法でポリエステル系コート剤（東洋紡績（株）製、商品
名：バイロン−２００）を塗工、乾燥して厚み４０μ
ｍ、全光線透過率９０％のＵＶ保護層を形成、積層して
光反射体４を得た。得られた光反射体４を用いて実施例
１と同様にして光反射装置を組み立てた。得られた多孔
性樹脂シート、ＵＶ保護層、光反射体４及び光反射装置
について実施例１と同様にして評価し、その評価結果を
表１に示す。Example 4 A polyolefin resin having a density of 0.9 g / cm 3 and MI
1.5 g / 10 min propylene homopolymer (Mitsui Toatsu Chemicals, Inc., trade name: Nobrene, FO-50
F: Hereinafter, referred to as PP) except that a porous resin sheet having a thickness of 150 μm was obtained by the same method as in Example 1. A polyester-based coating agent (manufactured by Toyobo Co., Ltd., trade name: Byron-200) was applied to one surface of the obtained porous resin sheet by the same method as in Example 2 and dried to a thickness of 40 μm.
m, a UV protective layer having a total light transmittance of 90% was formed and laminated to obtain a light reflector 4. A light reflecting device was assembled using the obtained light reflector 4 in the same manner as in Example 1. The obtained porous resin sheet, UV protective layer, light reflector 4 and light reflecting device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 1.
【０１０９】実施例５ ポリオレフィン樹脂として密度０．９ｇ／ｃｍ3、ＭＩ
１．５ｇ／１０ｍｉｎのプロピレン−エチレンコポリマ
ー（三井東圧化学（株）製、商品名：ＭＪＳ−Ｇ：以
下、以下、ＥＰという）を用いた以外、実施例１と同様
の方法で厚み７０μｍの多孔性樹脂シートを得た。得ら
れた多孔性樹脂シートの片表面に実施例２と同様の方法
で、シリコーン系コート剤（東亜合成化学（株）製、商
品名：サイマックＵＳ−３００）を塗工、乾燥し、厚み
２０μｍ、全光線透過率９１％のＵＶ保護層を形成、積
層して光反射体５を得た。得られた光反射体５を用いて
実施例１と同様にして光反射装置を組み立てた。得られ
た多孔性樹脂シート、ＵＶ保護層、光反射体５及び光反
射装置について実施例１と同様にして評価し、その評価
結果を表１に示す。Example 5 A polyolefin resin having a density of 0.9 g / cm 3 and MI
A propylene-ethylene copolymer (manufactured by Mitsui Toatsu Kagaku Co., Ltd., trade name: MJS-G: hereinafter, referred to as EP) of 1.5 g / 10 min was used in the same manner as in Example 1 except that a thickness of 70 μm was used. A porous resin sheet was obtained. A silicone-based coating agent (manufactured by Toagosei Kagaku Co., Ltd., trade name: Cymac US-300) was applied to one surface of the obtained porous resin sheet by the same method as in Example 2, dried, and had a thickness of 20 μm. Then, a UV protective layer having a total light transmittance of 91% was formed and laminated to obtain a light reflector 5. A light reflecting device was assembled using the obtained light reflector 5 in the same manner as in Example 1. The obtained porous resin sheet, UV protective layer, light reflector 5 and light reflecting device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 1.
【０１１０】実施例６ 微粉末状の無機系充填剤として平均粒子径１．１μｍの
炭酸カルシウム（同和カルファイン（株）製、商品名：
ＳＳＴ−４０）を表１に示す重量割合で用い、ステアリ
ン酸カルシウムの代わりにヒマシ油（伊藤製油（株）、
商品名：菱形特Ａ）を樹脂１００重量部に対し７．５重
量部用いた以外は、実施例１と同様の方法で厚み１５０
μｍの多孔性樹脂シートを得た。得られた多孔性樹脂シ
ートの片表面に実施例１と同様の方法でＵＶ保護層とし
て、ＰＥＴフィルム（帝人（株）製、商品名：Ｂ４Ｘ、
厚み：２５μｍ、全光線透過率：８９％）を積層して光
反射体６を得た。得られた光反射体６を用いて実施例１
と同様にして光反射装置を組み立てた。得られた多孔性
樹脂シート、ＵＶ保護層、光反射体６及び光反射装置に
ついて実施例１と同様にして評価し、その評価結果を表
１に示す。Example 6 Calcium carbonate having an average particle size of 1.1 μm as a fine powdery inorganic filler (trade name: manufactured by Dowa Calfine Co., Ltd.)
SST-40) in a weight ratio shown in Table 1, and castor oil (Ito Oil Co., Ltd.) in place of calcium stearate.
Product name: Rhombic special A) was used in the same manner as in Example 1 except that 7.5 parts by weight was used with respect to 100 parts by weight of the resin.
A porous resin sheet of μm was obtained. On one surface of the obtained porous resin sheet, a PET film (manufactured by Teijin Ltd., trade name: B4X, as a UV protective layer was prepared in the same manner as in Example 1.
A thickness of 25 μm and a total light transmittance of 89%) were laminated to obtain a light reflector 6. Example 1 using the obtained light reflector 6
A light reflection device was assembled in the same manner as in. The obtained porous resin sheet, UV protective layer, light reflector 6 and light reflecting device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 1.
【０１１１】実施例７ ポリオレフィン樹脂として密度０．９５４ｇ／ｃｍ3、
ＭＩ１．１ｇ／１０ｍｉｎの高密度ポリエチレン （三
井石油化学工業（株）製、商品名：ハイゼックス３３０
０Ｆ、以下、ＨＤＰＥという）を用いた以外、実施例１
と同様の方法で厚み１５０μｍの多孔性樹脂シートを得
た。得られた多孔性樹脂シートの片表面に実施例１と同
様の方法でＰＭＭＡフィルム（三菱レイヨン（株）製、
商品名：アクリプレンＨＢＣ０１１、厚み：１７μｍ、
全光線透過率：９５％）を積層して光反射体７を得た。
得られた光反射体７を用いて実施例１と同様にして光反
射装置を組み立てた。得られた多孔性樹脂シート、ＵＶ
保護層、光反射体７及び光反射装置について実施例１と
同様にして評価し、その評価結果を表２に示す。Example 7 A polyolefin resin having a density of 0.954 g / cm 3 ,
High density polyethylene with MI 1.1g / 10min (Mitsui Petrochemical Industry Co., Ltd., trade name: Hi-Zex 330
Example 1 except that 0F, hereinafter referred to as HDPE) was used.
A porous resin sheet having a thickness of 150 μm was obtained by the same method as described in (1). A PMMA film (manufactured by Mitsubishi Rayon Co., Ltd.) was formed on one surface of the obtained porous resin sheet by the same method as in Example 1.
Product name: Acryprene HBC011, Thickness: 17 μm,
The total light transmittance: 95%) was laminated to obtain a light reflector 7.
Using the obtained light reflector 7, a light reflecting device was assembled in the same manner as in Example 1. Obtained porous resin sheet, UV
The protective layer, the light reflector 7, and the light reflecting device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 2.
【０１１２】実施例８ 密度０．９２５ｇ／ｃｍ3、ＭＩ２ｇ／１０ｍｉｎの低
密度ポリエチレン（三井石油化学工業（株）製、商品
名：ミラソンＦ３１２、以下、ＬＤＰＥという）を用い
た以外、実施例１と同様の方法で厚み１００μｍの多孔
性樹脂シートを得た。得られた多孔性樹脂シートの片表
面に実施例１と同様の方法で、ＵＶ保護層として、ＰＥ
Ｔフィルム（帝人（株）製、商品名：Ｂ４Ｘ、厚み：２
５μｍ、全光線透過率：８９％）を積層して光反射体８
を得た。得られた光反射体８を用いて実施例１と同様に
して光反射装置を組み立てた。得られた多孔性樹脂シー
ト、ＵＶ保護層、光反射体８及び光反射装置について実
施例１と同様にして評価し、その評価結果を表２に示
す。Example 8 Example 1 was repeated except that low density polyethylene having a density of 0.925 g / cm 3 and MI 2 g / 10 min (manufactured by Mitsui Petrochemical Co., Ltd., trade name: Mirason F312, hereinafter referred to as LDPE) was used. A porous resin sheet having a thickness of 100 μm was obtained by the same method as described in (1). On one surface of the obtained porous resin sheet, PE was used as a UV protection layer by the same method as in Example 1.
T film (manufactured by Teijin Ltd., trade name: B4X, thickness: 2
5 μm, total light transmittance: 89%) are laminated to form a light reflector 8
I got A light reflecting device was assembled in the same manner as in Example 1 by using the obtained light reflector 8. The obtained porous resin sheet, UV protective layer, light reflector 8 and light reflecting device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 2.
【０１１３】実施例９ 実施例１で得られた多孔性樹脂シートの裏面に、漏光防
止保護層として、無機充填剤を含む白色ＰＥＴフィルム
（東レ（株）製、商品名：ルミラーＥ−２０、厚み７５
μｍ、全光線透過率９．８％）を積層して光反射体９を
得た。得られた光反射体９の多孔性樹脂シート側に光が
照射されるように配設して導光板下の光反射シートとし
て用い、実施例１で得られた光反射体１をランプホルダ
ーとして用いた以外、実施例１と同様にして光反射装置
を組み立てた。得られた多孔性樹脂シート、ＵＶ保護
層、漏光防止保護層、光反射体１及び９、並びに光反射
装置について、実施例１と同様にして評価し、その評価
結果を表２に示す。Example 9 On the back surface of the porous resin sheet obtained in Example 1, a white PET film containing an inorganic filler as a light leakage prevention protective layer (trade name: Lumirror E-20, manufactured by Toray Industries, Inc.) was used. Thickness 75
μm and total light transmittance of 9.8%) were laminated to obtain a light reflector 9. The obtained light reflector 9 is arranged so that light is irradiated to the porous resin sheet side, and is used as a light reflection sheet under the light guide plate. The light reflector 1 obtained in Example 1 is used as a lamp holder. A light reflecting device was assembled in the same manner as in Example 1 except that it was used. The obtained porous resin sheet, UV protection layer, light leakage prevention protection layer, light reflectors 1 and 9, and the light reflection device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 2.
【０１１４】実施例１０ 実施例１で得られた多孔性樹脂シートの裏面に、漏光防
止保護層として無機充填剤を含むＰＥＴフィルム（東レ
（株）製、商品名：ルミラーＥ−２０、厚み１２５μ
ｍ、全光線透過率５．１％）を積層して光反射体１０を
得た。得られた光反射体１０の多孔性樹脂シート側に光
が照射されるように配設して導光板下の光反射シートと
して用い、実施例１で得られた光反射体１をランプホル
ダーとして用いた以外、実施例１と同様にして光反射装
置を組み立てた。得られた多孔性樹脂シート、ＵＶ保護
層、漏光防止保護層、光反射体１及び１０、並びに光反
射装置について、実施例１と同様にして評価し、その評
価結果を表２に示す。Example 10 On the back surface of the porous resin sheet obtained in Example 1, a PET film (manufactured by Toray Industries, Inc., trade name: Lumirror E-20, thickness 125 μm) containing an inorganic filler as a light leakage prevention protective layer was formed.
m, total light transmittance 5.1%) were laminated to obtain a light reflector 10. The porous resin sheet side of the obtained light reflector 10 is disposed so as to be irradiated with light and is used as a light reflection sheet under the light guide plate. The light reflector 1 obtained in Example 1 is used as a lamp holder. A light reflecting device was assembled in the same manner as in Example 1 except that it was used. The obtained porous resin sheet, UV protection layer, light leakage prevention protection layer, light reflectors 1 and 10, and the light reflection device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 2.
【０１１５】実施例１１ 実施例１で得られた多孔性樹脂シートの裏面に、漏光防
止保護層として無機充填剤を含むＰＥＴフィルム（東レ
（株）製、商品名：ルミラーＥ−２０、厚み５０μｍ、
全光線透過率１２．５％）を積層して光反射体１１を得
た。得られた光反射体１１の多孔性樹脂シート側に光が
照射されるように配設して導光板下の光反射シートとし
て用い、実施例１で得られた光反射体１をランプホルダ
ーとして用いた以外、実施例１と同様にして光反射装置
を組み立てた。得られた多孔性樹脂シート、ＵＶ保護
層、漏光防止保護層、光反射体１及び１１、並びに光反
射装置について、実施例１と同様にして評価し、その評
価結果を表２に示す。Example 11 On the back surface of the porous resin sheet obtained in Example 1, a PET film (manufactured by Toray Industries, Inc., trade name: Lumirror E-20, thickness 50 μm) containing an inorganic filler as a light leakage prevention protective layer was formed. ,
A total light transmittance of 12.5%) was laminated to obtain a light reflector 11. The porous resin sheet side of the obtained light reflector 11 is arranged so that light is radiated and used as a light reflection sheet under the light guide plate. The light reflector 1 obtained in Example 1 is used as a lamp holder. A light reflecting device was assembled in the same manner as in Example 1 except that it was used. The obtained porous resin sheet, UV protection layer, light leakage prevention protection layer, light reflectors 1 and 11, and the light reflection device were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 2.
【０１１６】比較例１ ＬＬＤＰＥと硫酸バリウムの配合割合を表３に示す重量
比とした以外、実施例１と同様の方法で多孔性樹脂シー
トを得た。得られた多孔性樹脂シートの片表面に、ＵＶ
保護層として、実施例１と同様の方法でＰＥＴフィルム
（ダイアホイルヘキスト（株）製、商品名：ダイアホイ
ルＨ１００Ｃ、厚み：１２μｍ、全光線透過率：９０
％）を積層して光反射体１２を得た。得られた光反射体
１２を用いて実施例１と同様にして光反射装置を組み立
てた。得られた多孔性樹脂シート、ＵＶ保護層、光反射
体１２及び光反射装置について実施例１と同様にして評
価した。この光反射体１２は開孔率及び光線反射率が低
かった。また、光反射装置の輝度が低かった。評価結果
を表３に示す。Comparative Example 1 A porous resin sheet was obtained in the same manner as in Example 1 except that the blending ratio of LLDPE and barium sulfate was changed to the weight ratio shown in Table 3. UV on one surface of the obtained porous resin sheet
As a protective layer, a PET film (manufactured by DIAFOIL Hoechst Co., Ltd., trade name: DIAFOIL H100C, thickness: 12 μm, total light transmittance: 90) was used in the same manner as in Example 1.
%) To obtain a light reflector 12. Using the obtained light reflector 12, a light reflecting device was assembled in the same manner as in Example 1. The obtained porous resin sheet, UV protection layer, light reflector 12 and light reflecting device were evaluated in the same manner as in Example 1. The light reflector 12 had a low aperture ratio and a low light reflectance. In addition, the brightness of the light reflecting device was low. The evaluation results are shown in Table 3.
【０１１７】比較例２ 実施例１と同様の方法で多孔性樹脂シートを得た。得ら
れた多孔性樹脂シートの片表面に、ＵＶ保護層として、
実施例１と同様の方法でＰＭＭＡフィルム（三菱レイヨ
ン（株）製、商品名：アクリプレンＨＢＣ００１、厚
み：１２０μｍ、全光線透過率：８７％）を積層して光
反射体１３を得た。得られた光反射体１３を用いて実施
例１と同様にして光反射装置を組み立てた。得られた多
孔性樹脂シート、ＵＶ保護層、光反射体及び光反射装置
について実施例１と同様にして評価した。この光反射体
及び光反射装置の光反射率が低かった。評価結果を表３
に示す。Comparative Example 2 A porous resin sheet was obtained in the same manner as in Example 1. As a UV protection layer on one surface of the obtained porous resin sheet,
A PMMA film (manufactured by Mitsubishi Rayon Co., Ltd., trade name: Acryprene HBC001, thickness: 120 μm, total light transmittance: 87%) was laminated in the same manner as in Example 1 to obtain a light reflector 13. A light reflecting device was assembled in the same manner as in Example 1 using the obtained light reflector 13. The obtained porous resin sheet, UV protective layer, light reflector and light reflecting device were evaluated in the same manner as in Example 1. The light reflectance of this light reflector and the light reflecting device was low. Table 3 shows the evaluation results
Shown in
【０１１８】比較例３ 実施例１と同様の方法で厚さ５０μｍの多孔性樹脂シー
トを得、その表面にＵＶ保護層を積層せずに光反射体１
４を得た。得られた光反射体１４を用いて実施例１と同
様にして光反射装置を組み立てた。光反射体１４の多孔
性樹脂シートの表面に直接紫外線を照射した以外は、実
施例１と同様にして、多孔性樹脂シート、光反射体及び
光反射装置について実施例１と同様にして評価した。評
価結果を表３に示す。Comparative Example 3 A porous resin sheet having a thickness of 50 μm was obtained in the same manner as in Example 1, and the light reflector 1 was prepared without laminating a UV protective layer on the surface thereof.
Got 4. A light reflecting device was assembled using the obtained light reflector 14 in the same manner as in Example 1. The porous resin sheet, the light reflector and the light reflecting device were evaluated in the same manner as in Example 1 except that the surface of the porous resin sheet of the light reflector 14 was directly irradiated with ultraviolet rays. . The evaluation results are shown in Table 3.
【０１１９】比較例４ 市販の白色ＰＥＴシート（（株）きもと製、商品名：レ
フホワイトＲＷ７５Ｃ、ポリオレフィン樹脂を含むＰＥ
Ｔフィルムの両面に、炭酸カルシウムを含むＰＥＴフィ
ルムを積層した３層からなるフィルムを２軸延伸した厚
み７５μｍの延伸白色ＰＥＴフィルムの片表面に、厚み
約４０μｍの酸化チタンを塗布した白色ＰＥＴシート）
を光反射体１５とした。この光反射体１５を用いて実施
例１と同様にして光反射装置を組み立てた。得られた光
反射体１５及び光反射装置について実施例１と同様にし
て評価した。この光反射体１５は光線反射率が低いため
輝度が低かった。また、耐光性も低かった。評価結果を
表３に示す。尚、輝度、光線反射率及びその低下率は、
酸化チタンが塗布されていない側の面の特性を示す。Comparative Example 4 Commercially available white PET sheet (manufactured by Kimoto Co., Ltd., trade name: LEFF WHITE RW75C, PE containing polyolefin resin)
(A white PET sheet in which titanium oxide having a thickness of about 40 μm is applied to one surface of a stretched white PET film having a thickness of 75 μm obtained by biaxially stretching a film composed of three layers in which PET films containing calcium carbonate are laminated on both sides of a T film)
Was used as the light reflector 15. Using this light reflector 15, a light reflecting device was assembled in the same manner as in Example 1. The obtained light reflector 15 and the light reflection device were evaluated in the same manner as in Example 1. The light reflector 15 has a low light reflectance and thus a low luminance. Also, the light resistance was low. The evaluation results are shown in Table 3. In addition, the brightness, the light reflectance and the reduction rate are
The characteristics of the surface not coated with titanium oxide are shown.
【０１２０】実施例１２ 実施例１で得られた光反射体１の多孔性樹脂シート側に
漏光防止保護層として、無機充填剤を含む白色ＰＥＴフ
ィルム（東レ（株）製、商品名：ルミラー Ｅ−２０、
厚み；３８μｍ、全光線透過率：１８．４％）を積層し
て多孔性樹脂シートの表面にＵＶ保護層、裏面に漏光防
止保護層が積層された光反射体１６を得た。また、実施
例１で得られた光反射体１の多孔性樹脂シート側に漏光
防止保護層として、無機充填剤を含む白色ＰＥＴフィル
ム（東レ（株）製、商品名：ルミラー Ｅ−２０、厚
み：７５μｍ、全光線透過率：９．８％）を積層して多
孔性樹脂シートの表面にＵＶ保護層、裏面に漏光防止保
護層が積層された光反射体１７を得た。使用した多孔性
樹脂シートの特性、得られた光反射体１６及び光反射体
１７のＵＶ保護層側に照射した光線反射率及びその低下
率並びに、剛性を測定した結果を次に示す。Example 12 A white PET film containing an inorganic filler as a light leakage protection layer on the porous resin sheet side of the light reflector 1 obtained in Example 1 (trade name: Lumirror E manufactured by Toray Industries, Inc.) -20,
(Thickness: 38 μm, total light transmittance: 18.4%) were laminated to obtain a light reflector 16 in which a UV protective layer was laminated on the front surface of the porous resin sheet and a light leakage prevention protective layer was laminated on the rear surface. A white PET film containing an inorganic filler as a light leakage prevention protective layer on the porous resin sheet side of the light reflector 1 obtained in Example 1 (trade name: Lumirror E-20, manufactured by Toray Industries, Inc., thickness) : 75 μm, total light transmittance: 9.8%) to obtain a light reflector 17 in which a UV protective layer is laminated on the front surface of the porous resin sheet and a light leakage prevention protective layer is laminated on the rear surface thereof. The characteristics of the used porous resin sheet, the reflectance of the light rays irradiated to the UV protective layer side of the obtained light reflectors 16 and 17 and the reduction rate thereof, and the results of measuring the rigidity are shown below.
【０１２１】多孔性樹脂シート： ＬＬＤＰＥ；１００
重量部、ＢａＳＯ4；２３０重量部、延伸倍率；６.５
倍、厚み；２００μｍ、開孔率；４５％、光反射率；９
８.８%。 光 反射体１６： ＵＶ保護層：ＰＥＴフィルム（厚み；１２μｍ、全光線
透過率；９０％） 漏光防止保護層：無機充填剤を含む白色ＰＥＴフィルム
（厚み；３８μｍ、全光線透過率；１８.４％） 光反射率；９９.０％、剛性１３８ｍｍ、光反射率の低
下率；１.８％（４５０ｎｍ）、０.５％（５５０ｎ
ｍ）。 光 反射体１７： ＵＶ保護層：ＰＥＴフィルム（厚み；１２μｍ、全光線
透過率；９０％） 漏光防止保護層：無機充填剤を含む白色ＰＥＴフィルム
（厚み；７５μｍ、全光線透過率；９.８％） 光反射率；９９.３％、剛性１８５ｍｍ 次に、得られた光反射体１６を液晶表示装置のバックラ
イトユニットのランプホルダーとして使用し、光反射体
１７を液晶表示装置の導光板下の光反射シートとして使
用して、実施例１と同様にして光反射装置を組み立て
た。尚、この光反射装置において、光反射体１６及び１
７は、それぞれＵＶ保護層側に光が照射されるように配
設した。得られた光反射装置の輝度を測定したところ１
２５であった。Porous resin sheet: LLDPE; 100
Parts by weight, BaSO 4 ; 230 parts by weight, draw ratio; 6.5
Double, thickness: 200 μm, porosity: 45%, light reflectance: 9
8.8%. Light reflector 16: UV protective layer: PET film (thickness; 12 μm, total light transmittance; 90%) Light leakage prevention protective layer: White PET film containing inorganic filler (thickness: 38 μm, total light transmittance; 18.4) %) Light reflectance: 99.0%, rigidity 138 mm, reduction rate of light reflectance: 1.8% (450 nm), 0.5% (550n
m). Light reflector 17: UV protection layer: PET film (thickness; 12 μm, total light transmittance; 90%) Light leakage prevention protection layer: White PET film containing inorganic filler (thickness; 75 μm, total light transmittance; 9.8) %) Light reflectance: 99.3%, rigidity 185 mm Next, the obtained light reflector 16 is used as a lamp holder of a backlight unit of a liquid crystal display device, and the light reflector 17 is below a light guide plate of the liquid crystal display device. A light reflecting device was assembled in the same manner as in Example 1 by using it as the light reflecting sheet of. In this light reflecting device, the light reflectors 16 and 1
7 was disposed so that the UV protective layer side was irradiated with light. When the brightness of the obtained light reflecting device was measured, it was 1
It was 25.
【０１２２】[0122]
【表１】 [Table 1]
【０１２３】[0123]
【表２】 [Table 2]
【０１２４】[0124]
【表３】 [Table 3]
【０１２５】[0125]
【発明の効果】本発明の光反射体は紫外線等に対する耐
光性、形態保持性及び光線反射性に優れており、主とし
てワードプロセッサー、パーソナルコンピュータ、テレ
ビジョン等の液晶表示装置のバックライトユニット、照
明器具、複写機、プロジェクター方式のディスプレイ、
ファクシミリ、電子黒板等の光反射体として有用であ
る。The light reflector of the present invention is excellent in light resistance to ultraviolet rays and the like, shape retention and light ray reflectivity, and is mainly used as a backlight unit for liquid crystal display devices such as word processors, personal computers and televisions, and lighting equipment. , Copier, projector type display,
It is useful as a light reflector for facsimiles, electronic blackboards, etc.
【０１２６】また、本発明に係わる光反射体を、液晶表
示装置のバックライトユニットのランプホルダー部及び
／または導光板下部に配設して得られる光反射装置は従
来のバックライトユニットよりも光を有効に利用でき、
輝度向上が図り得る。Further, a light reflecting device obtained by arranging the light reflector according to the present invention under the lamp holder portion and / or under the light guide plate of the backlight unit of the liquid crystal display device is more light than the conventional backlight unit. Can be used effectively,
The brightness can be improved.
【図１】光源部を導光板の横に配設した液晶表示装置の
バックライトユニットの一例を示す断面図である。FIG. 1 is a cross-sectional view showing an example of a backlight unit of a liquid crystal display device in which a light source section is arranged beside a light guide plate.
【図２】図１に示した液晶表示装置とランプホルダー部
が同じ構造であり、導光板下光反射シートとして裏面に
漏光防止保護層が積層された液晶表示装置のバックライ
トユニットの斜視図である。FIG. 2 is a perspective view of a backlight unit of the liquid crystal display device having the same structure as the liquid crystal display device shown in FIG. 1 and a lamp holder portion, and a light leakage prevention protective layer laminated on the back surface as a light reflection sheet under the light guide plate. is there.
図１及び２で使用する符号は １ 光源 ２ ランプホルダー ２１ 多孔性樹脂シート ２２ ＵＶ保護層 ３ 導光板下光反射シート ３１ 多孔性樹脂シート ３２ ＵＶ保護層 ３３ 漏光防止保護層 ４ 導光板 ５ 光拡散シート ６ レンズシート Reference numerals used in FIGS. 1 and 2 are 1 light source 2 lamp holder 21 porous resin sheet 22 UV protection layer 3 light guide plate lower light reflection sheet 31 porous resin sheet 32 UV protection layer 33 light leakage protection layer 4 light guide plate 5 light diffusion Sheet 6 lens sheet
───────────────────────────────────────────────────── フロントページの続き (72)発明者 竹村 尚子 神奈川県横浜市神奈川区片倉１丁目17番地 片倉台団地３−２−501 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Naoko Takemura 1-17 Katakura, Kanagawa-ku, Yokohama, Kanagawa 3-2-501, Katakura housing complex
Claims (11)
保護層が積層された光反射体であって、該多孔性樹脂シ
ートがポリオレフィン系樹脂１００重量部に対して微粉
末状の無機系充填剤１００〜３００重量部を含み、面積
倍率で１．５〜２０倍に延伸され、且つ、波長５５０ｎ
ｍの光線反射率が９５％以上であり、該光反射体の剛性
が少なくとも５０ｍｍであることを特徴とする光反射
体。1. A light reflector in which a protective layer is laminated on at least one surface of a porous resin sheet, wherein the porous resin sheet is a fine powder inorganic filler with respect to 100 parts by weight of a polyolefin resin. Includes 100 to 300 parts by weight, is stretched to an area ratio of 1.5 to 20 times, and has a wavelength of 550n.
A light reflector having a light reflectance of m of 95% or more and a rigidity of the light reflector of at least 50 mm.
ｍｍに高めると同時にＵＶ保護層としての機能も有する
ＵＶ保護層であり、該ＵＶ保護層の全光線透過率が８０
％以上、該光反射体のＵＶ保護層表面に照射した波長５
５０ｎｍの光線の反射率が９５％以上であり、且つ、該
光反射体のＵＶ保護層表面に８０℃において４００ＭＪ
／ｍ2 の紫外線を照射した後の該光反射体の波長４５０
ｎｍ及び５５０ｎｍの光線の反射率の低下率が共に１０
％未満であることを特徴とする請求項１記載の光反射
体。2. The protective layer increases the rigidity of the light reflector from 50 to 150.
It is a UV protective layer which has a function as a UV protective layer at the same time as the thickness is increased to mm, and the total light transmittance of the UV protective layer is 80.
% Or more, the wavelength 5 irradiated on the surface of the UV protective layer of the light reflector.
The reflectance of light of 50 nm is 95% or more, and 400 MJ at 80 ° C. on the UV protective layer surface of the light reflector.
Wavelength 450 of the light reflector after irradiation with ultraviolet rays of / m 2
nm and 550 nm light rays both have a reduction rate of 10
%, The light reflector according to claim 1.
積層された光反射体の剛性が少なくとも１００ｍｍに高
められると同時に漏光防止機能も有する漏光防止保護層
であり、該漏光防止保護層の全光線透過率が２０％未満
であり、該光反射体の多孔性樹脂シート表面に照射され
た波長５５０ｎｍの光線の反射率が９５％以上であるこ
とを特徴とする請求項１記載の光反射体。3. A light-leakage-preventing protective layer in which the light-reflecting body laminated only on the back surface of the porous resin sheet has a rigidity increased to at least 100 mm and at the same time has a light-leakage preventing function. The light reflectance according to claim 1, wherein the total light transmittance is less than 20% and the reflectance of the light having a wavelength of 550 nm with which the surface of the porous resin sheet of the light reflector is irradiated is 95% or more. body.
され、該多孔性樹脂シートの表面の保護層がＵＶ保護層
としての機能も有しかつ全光線透過率が８０％以上であ
るＵＶ保護層であり、また裏面の保護層が漏光防止機能
も有する漏光防止保護層が積層された積層体であって、
該積層体のＵＶ保護層表面に照射した波長５５０ｎｍの
光線の反射率が９５％以上であり、且つ、該積層体のＵ
Ｖ保護層表面に８０℃において４００ＭＪ／ｍ2 の紫外
線を照射した後の該光反射体の波長４５０ｎｍ及び５５
０ｎｍの光線の反射率の低下率が共に１０％未満であ
り、且つ該積層体の剛性が少なくとも５０ｍｍであるこ
とを特徴とする請求項１記載の光反射体。4. A UV protective layer laminated on both sides of a porous resin sheet, the protective layer on the surface of said porous resin sheet also serving as a UV protective layer and having a total light transmittance of 80% or more. A protective layer, a protective layer on the back surface is a laminated body in which a light leakage prevention protective layer also having a light leakage prevention function is laminated,
The reflectance of the light having a wavelength of 550 nm irradiated on the surface of the UV protective layer of the laminate is 95% or more, and the U of the laminate is U.
After the surface of the V protective layer was irradiated with ultraviolet rays of 400 MJ / m 2 at 80 ° C., the wavelength of the light reflector was 450 nm and 55.
The light reflector according to claim 1, wherein both of the reduction rates of the reflectance of 0 nm light rays are less than 10%, and the rigidity of the laminate is at least 50 mm.
おいて、使用する多孔性樹脂シートがポリオレフィン系
樹脂１００重量部に対して微粉末状の無機系充填剤１０
０〜３００重量部を含み、面積倍率で１．５〜２０倍に
延伸され、波長５５０ｎｍの光線の反射率が９５％以上
であり、かつ（１）該ポリオレフィン系樹脂が、高密度
ポリエチレン、低密度ポリエチレン、ポリプロピレン、
エチレン−α−オレフィン共重合体、エチレン−プロピ
レン共重合体から選ばれた少なくとも一種の樹脂であ
り、（２）該微粉末状の無機系充填剤が、硫酸バリウ
ム、炭酸カルシウム、酸化チタン、炭酸マグネシウム、
アルミナ、水酸化マグネシウム及び酸化亜鉛から選ばれ
た少なくとも一種の充填剤であり、（３）該多孔性樹脂
シートの開孔率が４０〜７０％であり、また（４）該多
孔性樹脂シートの厚みが５０〜５００μｍであることを
特徴とする光反射体。5. The inorganic filler 10 according to any one of claims 1, 2, 3 or 4, wherein the porous resin sheet used is a fine powder of 100 parts by weight of a polyolefin resin.
0 to 300 parts by weight, stretched to an area ratio of 1.5 to 20 and having a reflectance of light having a wavelength of 550 nm of 95% or more, and (1) the polyolefin resin is high density polyethylene, low Density polyethylene, polypropylene,
At least one resin selected from ethylene-α-olefin copolymers and ethylene-propylene copolymers, and (2) the fine powdery inorganic filler is barium sulfate, calcium carbonate, titanium oxide, carbonic acid. magnesium,
At least one filler selected from alumina, magnesium hydroxide and zinc oxide, (3) the porosity of the porous resin sheet is 40 to 70%, and (4) the porous resin sheet A light reflector having a thickness of 50 to 500 μm.
ポリエステル系樹脂フィルム、ポリアクリル系樹脂フィ
ルム及びシリコーン系樹脂フィルムからなる群から選ば
れた厚み１〜１００μｍの樹脂フィルムであることを特
徴とする請求項２または４のいずれか記載の光反射体。6. A protective layer also having a function of protecting UV,
The light reflector according to claim 2, which is a resin film having a thickness of 1 to 100 μm selected from the group consisting of a polyester resin film, a polyacrylic resin film, and a silicone resin film.
填剤５〜７０重量％を含有するポリエステル系樹脂、ポ
リアクリル系樹脂及びシリコーン系樹脂からなる群から
選ばれた樹脂からなる厚み３０〜１５０μｍの樹脂フィ
ルムであることを特徴とする請求項３または４のいずれ
か記載の光反射体。7. A protective layer also having a light leakage prevention function, comprising a resin selected from the group consisting of a polyester resin containing 5 to 70% by weight of an inorganic filler, a polyacrylic resin and a silicone resin, and having a thickness of 30 to 30. The light reflector according to claim 3, which is a resin film having a thickness of 150 μm.
照明器具、複写機、プロジェクター方式のディスプレ
イ、ファクシミリ及び電子黒板からなる群から選ばれた
装置の光反射体として使用し得る請求項１〜７のいずれ
かに記載の光反射体。8. A backlight unit of a liquid crystal display device,
The light reflector according to any one of claims 1 to 7, which can be used as a light reflector of a device selected from the group consisting of a lighting fixture, a copying machine, a projector-type display, a facsimile, and an electronic blackboard.
構成するランプホルダーを形成する光反射体として使用
し得る請求項１、２、４、５または６のいずれかに記載
の光反射体。9. The light reflector according to claim 1, which can be used as a light reflector forming a lamp holder constituting a backlight unit of a liquid crystal display device.
を構成する導光板下光反射シートとして使用し得る請求
項１、３、４、５、６または７のいずれかに記載の光反
射体。10. The light reflector according to claim 1, which can be used as a light reflection sheet under a light guide plate which constitutes a backlight unit of a liquid crystal display device.
ト３、他の面に光拡散シート５が配設され、さらに該光
拡散シート５の表面にレンズシート６が配設された積層
体の少なくとも１側面に光源１が配設され、該光源１が
湾曲状に形成されたランプホルダー２により覆われてい
る光反射装置において、ランプホルダー２として請求項
１、２、４、５または６のいずれか記載の光反射体を使
用し、及び／又は導光板下光反射シート３に１、３、
４、５または７のいずれか記載の光反射体を使用するこ
とを特徴とする光反射装置。11. A laminated structure in which a light guide plate lower light reflection sheet 3 is provided on one surface of a light guide plate 4, a light diffusion sheet 5 is provided on the other surface, and a lens sheet 6 is provided on the surface of the light diffusion sheet 5. A light reflection device in which a light source 1 is disposed on at least one side surface of a body, and the light source 1 is covered with a lamp holder 2 formed in a curved shape. 6. The light reflector according to any one of 6 is used, and / or the light guide sheet under the light guide plate 3, 1, 3,
A light reflecting device comprising the light reflector according to any one of 4, 5, and 7.