JPH08259982A - Lubricating fluid composition for dynamic pressure bearing - Google Patents
Lubricating fluid composition for dynamic pressure bearingInfo
- Publication number
- JPH08259982A JPH08259982A JP9155095A JP9155095A JPH08259982A JP H08259982 A JPH08259982 A JP H08259982A JP 9155095 A JP9155095 A JP 9155095A JP 9155095 A JP9155095 A JP 9155095A JP H08259982 A JPH08259982 A JP H08259982A
- Authority
- JP
- Japan
- Prior art keywords
- dynamic pressure
- lubricating fluid
- amine
- pressure bearing
- fluid composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、動圧により軸を支承す
る動圧軸受の潤滑流体として使用され、且つその磁気特
性をシール作用に利用する動圧軸受用潤滑流体組成物に
関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lubricating fluid composition for a dynamic pressure bearing, which is used as a lubricating fluid for a dynamic pressure bearing that supports a shaft by dynamic pressure and uses its magnetic characteristics for a sealing action. .
【０００２】[0002]
【従来の技術】近年、種々の装置、特にポリゴンミラ
ー、磁気ディスク、光ディスク等の各種回転板を高速回
転駆動させるモータ等の装置に関し、磁性潤滑流体を用
いた動圧軸受の提案がなされている。すなわち磁性流体
は、強磁性体微粒子を液体分散溶媒中に安定的に分散さ
せたコロイド溶液であり、その液体自体が見掛け上強い
磁性を示すという特性から、通常は玉軸受と組み合わせ
てシーリングとして用いられることが多いが、その玉軸
受よりも高速回転安定性及び静粛性等において優るもの
として磁性潤滑流体を用いた動圧軸受が有望視されてい
る。磁性流体を用いた動圧軸受の提案は、この様な背景
のもとになされており、例えば特開昭６０−８８２２３
号公報においては、動圧発生用の潤滑流体と磁気シール
用の磁性流体とを一つの流体で兼用するようにした装置
が開示されている。2. Description of the Related Art In recent years, a dynamic pressure bearing using a magnetic lubricating fluid has been proposed for various devices, particularly for devices such as a motor for driving various rotary plates such as a polygon mirror, a magnetic disk and an optical disk at high speed. . That is, a magnetic fluid is a colloidal solution in which ferromagnetic fine particles are stably dispersed in a liquid dispersion solvent, and because the liquid itself has apparently strong magnetism, it is usually used as a sealing in combination with a ball bearing. However, a dynamic pressure bearing using a magnetic lubricating fluid is considered to be promising because it is superior to the ball bearing in high-speed rotation stability and quietness. The proposal of a dynamic pressure bearing using a magnetic fluid has been made under such a background, for example, Japanese Patent Laid-Open No. 60-88223.
The publication discloses a device in which one fluid is used as both a lubricating fluid for generating a dynamic pressure and a magnetic fluid for magnetic sealing.
【０００３】しかしながらそのような装置においては、
磁性流体組成物に、シールとしての低蒸発特性と、軸受
ロスを低減するための低粘度性とを併せ持つことが要求
されるため、それに適合し得る磁性流体組成物の特性を
実際には得ることができないのが現状である。すなわち
軸受部では、シール部より遥かに大きなせん断力を受け
ると共に高温に曝され、また起動・停止時には金属同士
の接触・摩耗を生じて活性金属面に触れることがある。
磁性流体組成物は、「高速回転でも高気密性が得られる
（〜１０-6 Toor ）」という最大の利点から使用されて
いるものの、潤滑流体としての機能（低摩耗特性）と寿
命特性（低蒸発性、耐高温性）とを同時に十分と有した
ものは未だ開発されていない（ＰＥＴＲＯＴＥＣＨ 第
１３巻第１２号（１９８９）より）。However, in such a device,
The magnetic fluid composition is required to have both a low evaporation property as a seal and a low viscosity property for reducing a bearing loss. Therefore, it is necessary to actually obtain a characteristic of the magnetic fluid composition that can be adapted to it. The current situation is that it is not possible. That is, the bearing portion receives a much larger shearing force than the seal portion and is exposed to a high temperature, and at the time of starting and stopping, the metals may come into contact with each other and wear to contact the active metal surface.
Although the magnetic fluid composition is used with the greatest advantage that "high airtightness can be obtained even at high speed (-10-6 Toor)", it functions as a lubricating fluid (low wear characteristics) and life characteristics (low wear characteristics). Those having both sufficient evaporating property and high temperature resistance) have not yet been developed (from PETROTECH Vol. 13, No. 12 (1989)).
【０００４】[0004]
【発明が解決しようとする課題】このようにシール性だ
けでなく潤滑性および寿命特性をもカバーした動圧軸受
用潤滑流体組成物が要望されており、動圧発生用の潤滑
流体と磁気シール用の磁性流体とを一つの流体で兼用す
るためには、長期にわたる劣化防止、特にゲル化防止対
策が不可欠である。一般的には、潤滑油に対してフェノ
ール系、アミン系、イオウ系等の酸化防止剤を０．１〜
０．５重量％程度添加して酸化寿命を改善することが知
られてはいるが、磁性流体のゲル化防止対策としてどの
様なものをどの様に添加すれば良いかについては知られ
ていない。なお特開昭５９−１０５０９３号公報には、
磁性流体の酸化劣化に着目して酸化防止剤を添加するこ
とが記載されてはいるが、上述したと同様にゲル化防止
対策に関しての記載は全くない。Thus, there is a demand for a lubricating fluid composition for a dynamic pressure bearing that covers not only the sealing property but also the lubricity and life characteristics, and there is a need for a lubricating fluid for generating a dynamic pressure and a magnetic seal. In order to use a single magnetic fluid as a magnetic fluid, it is necessary to prevent deterioration over a long period of time, especially to prevent gelation. Generally, 0.1 to 0.1 of a phenolic, amine, or sulfur antioxidant is added to the lubricating oil.
It is known to add about 0.5% by weight to improve the oxidation life, but it is not known what kind of additive should be added and how to prevent gelation of magnetic fluid. . Incidentally, Japanese Patent Laid-Open No. 59-105093 discloses that
Although it is described that an antioxidant is added while paying attention to the oxidative deterioration of the magnetic fluid, there is no description about the anti-gelling measure as described above.
【０００５】そこで本発明は、長期にわたってゲル化防
止を良好に行うことができ、寿命信頼性を向上させるこ
とができるようにした動圧軸受用潤滑流体組成物を提供
することを目的とする。Therefore, an object of the present invention is to provide a lubricating fluid composition for a dynamic pressure bearing, which can prevent gelation satisfactorily for a long period of time and can improve the life reliability.
【０００６】[0006]
【課題を解決するための手段】本願発明者が検討した結
果、磁性流体の構造の複雑性、特に界面活性剤との相互
作用から、添加された酸化防止剤の作用は一般潤滑剤の
場合と異なっており、特定の種類のゲル化防止剤を添加
れば十分なゲル化防止効果が得られることを見出した。
そして特に動圧軸受用潤滑流体組成物として十分なゲル
化防止作用を得るためには、 １）基油に溶け、界面活性剤を添加して磁性流体化して
も析出しないこと、 ２）増粘作用が少ないこと、 ３）蒸発量が少ないこと、 ４）反応生成物が析出しないこと、等の条件が必要であ
ることを見い出した。As a result of the study by the inventors of the present application, the action of the added antioxidant is different from that of a general lubricant because of the complexity of the structure of the magnetic fluid, especially the interaction with the surfactant. It is different, and it was found that a sufficient anti-gelling effect can be obtained by adding a specific type of anti-gelling agent.
In order to obtain a sufficient gelation-preventing action as a lubricating fluid composition for dynamic pressure bearings, in particular, 1) it should dissolve in the base oil and should not be precipitated even if it is made into a magnetic fluid by adding a surfactant. It has been found that conditions are required such that the action is small, 3) the evaporation amount is small, 4) the reaction product does not precipitate.
【０００７】このような観点から、請求項１ないし請求
項３の発明にかかる動圧軸受用潤滑流体組成物には、磁
性微粒子を基油溶媒中に分散させてなる磁性流体組成物
であって、上記基油溶媒としてアミン系ゲル化防止剤を
添加した潤滑剤が用いられている。From this point of view, the lubricating fluid composition for a dynamic pressure bearing according to the invention of claims 1 to 3 is a magnetic fluid composition obtained by dispersing magnetic fine particles in a base oil solvent. A lubricant containing an amine-based antigelling agent is used as the base oil solvent.
【０００８】そして本発明にかかるアミン系ゲル化防止
剤としては、例えば請求項４のようにアミン系酸化防止
剤が用いられ、アミン系酸化防止剤としては、アルキル
ジフェニルアミン（商品名；イルガノックスＬ０１，Ｌ
５７，Ｌ０６等）や、フェニル−α−ナフチルアミン
（商品名；イルガノックスＬ０５等）が採用される。こ
れらアルキルジフェニルアミン、フェニル−α−ナフチ
ルアミンは蒸発特性及び基油との相溶性の点で好適であ
る。As the amine-based gelling agent according to the present invention, for example, an amine-based antioxidant is used, and as the amine-based antioxidant, an alkyldiphenylamine (trade name; Irganox L01 is used. , L
57, L06 etc.) and phenyl-α-naphthylamine (trade name; Irganox L05 etc.) are adopted. These alkyldiphenylamines and phenyl-α-naphthylamines are preferable in terms of evaporation characteristics and compatibility with base oils.
【０００９】一方、基油溶媒としては、例えばポリ−α
−オレフィン水素化物とポリオールエステル油を混合し
てなる基油が好適に用いられる。このポリ−α−オレフ
ィン水素化物としては、例えば、１−デセン、イソブチ
レン等をルイス酸等で重合させて得られた重合物を水素
化することにより得られる。これらには数平均分子量が
２００〜１６００程度のものがあるが、蒸発特性等から
数平均分子量４００程度のものが好ましい。なお水素化
は完全に行われなくとも良いが、水素化の程度が低いと
劣化しやすい。On the other hand, examples of the base oil solvent include poly-α.
-A base oil obtained by mixing an olefin hydride and a polyol ester oil is preferably used. This poly-α-olefin hydride can be obtained, for example, by hydrogenating a polymer obtained by polymerizing 1-decene, isobutylene or the like with a Lewis acid or the like. Some of these have a number average molecular weight of about 200 to 1,600, but those having a number average molecular weight of about 400 are preferable in view of evaporation characteristics and the like. Although the hydrogenation does not have to be performed completely, it is likely to deteriorate when the degree of hydrogenation is low.
【００１０】またポリオールエステルとしては、例えば
ネオペンチルグリコール（ＮＰＧ）、トリメチロールプ
ロパン（ＴＭＰ）、ペンタエリスリトール（ＰＥ）等の
多価アルコールと、炭素数５〜１８の長鎖または分岐脂
肪酸とをエステル化した構造を有するものであり、例え
ばＣＨ3 ＣＨ2 −Ｃ−（ＣＨ2 ＯＯＣＲ）3 のＲ（Ｒは
アルキル基）をＣ５〜Ｃ２０の範囲内で変化させた各種
トリメチロールプロパン混合エステルが用いられる。よ
り具体的には、バレリン酸、へプタン酸の混合トリメチ
ロールプロパンエステル（新日鐵化学（株）社製；商品
名ＨＡＴＣＯＬ２９１５，２９２５，２９３７等）やト
リメチロールプロパンのデカン酸やヘプタン酸との混合
エステル油（新日鐵化学（株）社製；ＨＡＴＣＯＬ２９
３８等）である。As the polyol ester, for example, a polyhydric alcohol such as neopentyl glycol (NPG), trimethylolpropane (TMP), pentaerythritol (PE), and a long-chain or branched fatty acid having 5 to 18 carbon atoms are used. And various trimethylolpropane mixed esters in which R (R is an alkyl group) of CH 3 CH 2 —C— (CH 2 OOCR) 3 is changed within the range of C5 to C20 are used. To be More specifically, valeric acid, a mixed trimethylolpropane ester of heptanoic acid (manufactured by Nippon Steel Chemical Co., Ltd .; trade name HATCOL 2915, 2925, 2937, etc.) and trimethylolpropane with decanoic acid and heptanoic acid Mixed ester oil (manufactured by Nippon Steel Chemical Co., Ltd .; HATCOL29)
38).
【００１１】本発明における全体の配合割合は、基油溶
媒１００重量部に対し、アミン系ゲル防止剤１〜１５重
量部の範囲とすることがよく、粘度を１００ｃｐ以下、
飽和磁化を１５０ガウス以上とすることがよい。磁性微
粒子が２５重量部以下では１５０ガウスに足らず、３５
重量部以上では増粘に影響を与える。また、潤滑油と同
様に防錆剤、粘度指数向上剤、金属不活性剤等の各種添
加剤を使用することができる。In the present invention, the total blending ratio is preferably in the range of 1 to 15 parts by weight of the amine gel inhibitor to 100 parts by weight of the base oil solvent, and the viscosity is 100 cp or less,
It is preferable that the saturation magnetization is 150 gauss or more. If the amount of magnetic particles is 25 parts by weight or less, it is less than 150 gauss
If it is more than part by weight, it will affect the thickening. Further, various additives such as a rust preventive agent, a viscosity index improver, and a metal deactivator can be used in the same manner as the lubricating oil.
【００１２】[0012]
【作用】このような請求項１にかかる手段によれば、ア
ミン系ゲル化防止剤を添加した潤滑剤を基油溶媒として
用いることによって、粘度・蒸発の特性を良好に維持し
つつ、特に高温ゲル化の物理特性を向上させることがで
き、もって、動圧発生用の潤滑流体として寿命信頼性の
高い組成物を提供することができる。According to the above-mentioned means, by using the lubricant containing the amine-based gelation inhibitor as the base oil solvent, it is possible to maintain excellent viscosity and evaporation characteristics, and especially at high temperature. It is possible to improve the physical properties of gelation, and thus it is possible to provide a composition having a long service life as a lubricating fluid for generating dynamic pressure.
【００１３】この場合、請求項２及び請求項３の発明の
ようにアミン系ゲル化防止剤を０．５重量％超及び１〜
５重量％添加し、または請求項４の発明のようにアミン
系ゲル化防止剤としてアミン系酸化防止剤を採用するこ
ととすれば、上記作用が一層向上されるようになってい
る。In this case, as in the inventions of claims 2 and 3, the amine-based antigelling agent is added in an amount of more than 0.5% by weight and 1 to
If 5% by weight is added or if an amine antioxidant is used as the amine gelling agent as in the invention of claim 4, the above-mentioned action is further improved.
【００１４】[0014]
【実施例】以下、本発明の実施例を説明する。本発明の
各実施例においては、磁性微粒子として共沈法により得
られた飽和磁化２５０ガウスのＭｎ−Ｚｎフェライトを
用いた。硫酸マンガン０．１ｍｏｌ、硫酸亜鉛０．４ｍ
ｏｌ、硫酸第２鉄０．５ｍｏｌを１ｌの水に溶解し、こ
の水溶性の液温を９０℃に保ち、攪拌しつつ、６Ｎ水酸
化ナトリウムを滴下して、水溶液のＰＨを１１として、
Ｍｎ−Ｚｎフェライトのコロイドを生成させた後、液温
を８０℃として、さらに攪拌を続けながら、オレイン酸
ナトリウムの１０％溶液２５０ｍｌを加えたこの溶液を
室温に冷却した後、３Ｎの塩酸水溶液を加えてＰＨを６
とした。凝集したコロイド粒子を十分水洗、さらに脱水
乾燥させて、オレイン酸で被覆されたＭｎ−Ｚｎフェラ
イト微粒子を得た。Embodiments of the present invention will be described below. In each example of the present invention, Mn-Zn ferrite with a saturation magnetization of 250 gauss obtained by the coprecipitation method was used as the magnetic fine particles. Manganese sulfate 0.1 mol, zinc sulfate 0.4 m
ol, 0.5 mol of ferric sulfate was dissolved in 1 liter of water, the water-soluble liquid temperature was maintained at 90 ° C., and 6N sodium hydroxide was added dropwise with stirring to adjust the pH of the aqueous solution to 11,
After the colloid of Mn-Zn ferrite was generated, the solution temperature was set to 80 ° C, 250 ml of a 10% solution of sodium oleate was added to the solution while continuing to stir, and the solution was cooled to room temperature. In addition PH 6
And The aggregated colloidal particles were thoroughly washed with water and further dehydrated and dried to obtain Mn-Zn ferrite fine particles coated with oleic acid.
【００１５】ついで上記のオレイン酸で被覆されたＭｎ
−Ｚｎフェライトから１４．８ｇを採り、下記の基油溶
媒１５ｇを加えて、十分攪拌して分散させた後、遠心分
離によって未分散物を除去、さらに比重１．１６となる
よう基油を加えて、流体を得た。こうして得られた流体
のフェライト濃度は、３５ｗｔ％、飽和磁化は２５０ガ
ウスであった。Then, the Mn coated with the above-mentioned oleic acid was used.
-Take 14.8 g of Zn ferrite, add 15 g of the following base oil solvent, sufficiently stir to disperse, then remove undispersed substance by centrifugation, and further add base oil to have a specific gravity of 1.16. To obtain the fluid. The thus obtained fluid had a ferrite concentration of 35 wt% and a saturation magnetization of 250 gauss.
【００１６】さらに上記磁性微粒子としてのＭｎ−Ｚｎ
フェライトを分散させる基油溶媒として、ポリ−α−オ
レフィン水素化物［Ｃ３０〜Ｃ４０］（新日鐵化学
（株）社製；シンフルード４０１）、ポリ炭酸エステル
（ＲＯＣＯＯＲ）［ＲはＣ５〜Ｃ１０のアルキル基］
（三井石油化学（株）社製；ＤＩＡＬＣＡＲＢ ＳＲ１
０００／Ｒ）、アジピン酸ジイソデシル油（新日鐵化学
（株）社製；ＨＡＴＣＯＬ２９１０）、トリメリット酸
トリオクチルエステル油（新日鐵化学（株）社製；ＨＡ
ＴＣＯＬ２９２０）の混合物に、ゲル化防止剤としてア
ミン系酸化防止剤、具体的にはアルキルジフェニルアミ
ン（商品名；イルガノックスＬ５７）を添加した。そし
てこのゲル化防止剤としてのアルキルジフェニルアミン
を下表１のように種々変えることにより、実施例１〜５
及び比較例１〜４にかかる潤滑流体組成物をそれぞれ作
成した。Further, Mn-Zn as the above-mentioned magnetic fine particles
As a base oil solvent for dispersing ferrite, poly-α-olefin hydride [C30 to C40] (manufactured by Nippon Steel Chemical Co., Ltd .; Shinflude 401), polycarbonate (ROCOOR) [R is C5 to C10. Alkyl group]
(Mitsui Petrochemical Co., Ltd .; DIALCARB SR1
000 / R), diisodecyl adipate oil (Nippon Steel Chemical Co., Ltd .; HATCOL2910), trimellitic acid trioctyl ester oil (Nippon Steel Chemical Co., Ltd .; HA)
To the mixture of TCOL2920), an amine-based antioxidant as a gelling agent, specifically, alkyldiphenylamine (trade name; Irganox L57) was added. Then, by changing the alkyldiphenylamine as the antigelling agent variously as shown in Table 1 below, Examples 1 to 5 were obtained.
The lubricating fluid compositions according to Comparative Examples 1 to 4 were prepared.
【００１７】[0017]
【表１】 [Table 1]
【００１８】得られた各潤滑流体組成物はシャーレに入
れ、析出、凝集、分離等の外観確認によって分散安定性
を評価するとともに、温度８０℃・５２０時間における
重量減により蒸発量を比較し、さらに温度１４０℃下で
放置した場合の酸化劣化による高温ゲル化時間を比較し
た。また粘度については、２５℃における粘度及び粘度
温度指数を比較した。その評価結果を表２に示す。Each of the obtained lubricating fluid compositions was put in a petri dish, and the dispersion stability was evaluated by confirming the appearance such as precipitation, aggregation, separation, etc., and the evaporation amount was compared by weight reduction at a temperature of 80 ° C. for 520 hours. Further, the high temperature gelling time due to oxidative deterioration when left at a temperature of 140 ° C. was compared. Regarding the viscosity, the viscosity at 25 ° C and the viscosity temperature index were compared. Table 2 shows the evaluation results.
【００１９】[0019]
【表２】 [Table 2]
【００２０】表２において、まずゲル化防止剤を添加し
なかった比較例１に対して、実施例３及び実施例４では
ゲル化防止剤としてのアミン系酸化防止剤を少量だけ添
加している。すなわち実施例３では、アミン系酸化防止
剤（ゲル化防止剤）としてアルキルジフェニルアミン
（Ｌ５７）を０．１重量％、実施例４ではアルキルジフ
ェニルアミン（Ｌ５７）を０．５重量％だけ添加してい
る。このようにアミン系酸化防止剤（ゲル化防止剤）を
少量だけ添加した場合には、粘度及び蒸発量の各特性に
対する改善はほとんど見られなかったが、高温ゲル化防
止効果（酸化防止効果）については僅かながら向上し
た。これは、アミン系ゲル化防止剤としてのアミン系酸
化防止剤と界面活性剤との相互作用によるものと考えら
れる。また、アミン系酸化防止剤（ゲル化防止剤）を
０．５重量％超添加した場合には、後述するように、粘
度、蒸発量、及び高温ゲル化防止の各特性についても、
共に優れた効果を奏することが判った。In Table 2, first, in comparison with Comparative Example 1 in which no gelling agent was added, in Examples 3 and 4, only a small amount of an amine antioxidant as a gelling agent was added. . That is, in Example 3, 0.1% by weight of alkyldiphenylamine (L57) was added as an amine-based antioxidant (antigelling agent), and in Example 4, only 0.5% by weight of alkyldiphenylamine (L57) was added. . Thus, when only a small amount of the amine-based antioxidant (anti-gelling agent) was added, almost no improvement was observed in each property of viscosity and evaporation amount, but high temperature anti-gelling effect (antioxidant effect) As for the above, it improved slightly. It is considered that this is due to the interaction between the amine antioxidant as the amine anti-gelling agent and the surfactant. Further, when the amine-based antioxidant (antigelling agent) is added in an amount of more than 0.5% by weight, as will be described later, the viscosity, the amount of evaporation, and the high temperature antigelling properties are
It was found that both have excellent effects.
【００２１】これに対して、アミン系以外の系のゲル化
防止剤（酸化防止剤）を少量添加した場合には、高温ゲ
ル化防止効果（酸化防止効果）は全く得られなかった。
例えばフェノール系のゲル化防止剤（酸化防止剤）とし
て、２，６−ジ−ｔ−ブチル・フェノール（商品名；エ
チル７０１、イルガノックスＬ１０８等）を少量（０．
５重量％）添加した比較例４のものや、イオウ系の酸化
防止剤として４，４’−チオビス（２−ｔ−ブチル−４
メチルフェノール（Ｌ１１５））を少量（０．５重量
％）添加した比較例６のものにおいては、粘度及び蒸発
量の各特性が顕著に向上することはなく、特にゲル化防
止（高温ゲル化時間）の特性については全く改善されな
かった。On the other hand, when a small amount of an anti-gelling agent (antioxidant) other than the amine type was added, no high temperature anti-gelling effect (antioxidant effect) was obtained.
For example, as a phenolic gelling agent (antioxidant), 2,6-di-t-butyl phenol (trade name; ethyl 701, Irganox L108, etc.) in a small amount (0.
5% by weight) of Comparative Example 4, or 4,4′-thiobis (2-t-butyl-4) as a sulfur-based antioxidant.
In Comparative Example 6 in which a small amount (0.5 wt%) of methylphenol (L115) was added, the properties of viscosity and evaporation did not significantly improve, and gelation prevention (high temperature gelation time) The characteristics of () were not improved at all.
【００２２】一方、本発明にかかる実施例１及び実施例
２における磁性流体組成物では、アミン系ゲル化防止
剤、具体的にはアミン系酸化防止剤としてアルキルジフ
ェニルアミン（Ｌ５７）を、１．０重量％及び５．０重
量％それぞれ添加している。このようにアミン系ゲル化
防止剤（アミン系酸化防止剤）を多量に添加した本発明
にかかる実施例１及び実施例２では、粘度、蒸発量及び
高温ゲル化防止（酸化寿命）の各特性のいずれも好まし
い値を示し、特に、高温ゲル化防止効果（酸化防止効
果）の特性向上が著しく、従って高温安定性に優れてい
ることが判明した。On the other hand, in the magnetic fluid compositions of Examples 1 and 2 according to the present invention, an amine-based gelling agent, specifically, alkyldiphenylamine (L57) as an amine-based antioxidant was added to 1.0 % And 5.0% by weight, respectively. In Examples 1 and 2 according to the present invention in which a large amount of the amine-based anti-gelling agent (amine-based antioxidant) was added in this manner, the respective properties of viscosity, evaporation amount and high-temperature gelation prevention (oxidation life) were obtained. It was found that all of them exhibited preferable values, and in particular, the characteristics of the high temperature gelation prevention effect (antioxidation effect) were remarkably improved, and therefore the high temperature stability was excellent.
【００２３】ところが、比較例５あるいは比較例７のよ
うに、アミン系ゲル化防止剤以外の他の系のゲル化防止
剤を多量に添加した場合には、強磁性体微粒子を液体分
散溶媒中に溶解させることができず、磁性流体組成物自
体を得ることができなかった。However, as in Comparative Example 5 or Comparative Example 7, when a large amount of anti-gelling agent other than the amine-based anti-gelling agent is added, the ferromagnetic fine particles are dispersed in the liquid dispersion solvent. However, the magnetic fluid composition itself could not be obtained.
【００２４】以上本発明者によってなされた発明を実施
例に基づき具体的に説明したが、本発明は上記実施例に
限定されるものではなく、その要旨を逸脱しない範囲で
種々変形可能であるというのはいうまでもない。例えば
磁性微粒子として、Ｍｎ−Ｚｎフェライトの他に、Ｎｉ
−Ｚｎフェライトやマグネタイトを同様に用いることが
できる。また界面活性剤も、他のあらゆる高級脂肪酸を
採用することができる。さらにアミン系ゲル化防止剤と
しては、酸化防止剤以外のあらゆる種類のアミン系のも
のを同様に採用することができる。Although the invention made by the present inventor has been specifically described based on the embodiments, the invention is not limited to the above embodiments, and various modifications can be made without departing from the scope of the invention. Needless to say. For example, as the magnetic fine particles, in addition to Mn-Zn ferrite, Ni
-Zn ferrite or magnetite can be used as well. Further, as the surfactant, any other higher fatty acid can be adopted. Further, as the amine-based gelling agent, all kinds of amine-based ones other than the antioxidant can be similarly employed.
【００２５】[0025]
【発明の効果】以上述べたように請求項１の発明にかか
る動圧軸受用潤滑流体組成物は、アミン系ゲル化防止
剤、例えば請求項４のような酸化防止剤を添加した潤滑
剤を基油溶媒として用いることによって、粘度・蒸発の
特性を良好に維持しつつ、特に高温ゲル化の物理特性を
向上させたものであるから、簡易な構造で良好な特性を
得ることができ、特に動圧発生用の潤滑流体と磁気シー
ル用の流体とを一つの流体で兼用するようにした動圧軸
受用潤滑流体組成物及びそれを用いたモータの実現性お
よび信頼性を向上させることができる。As described above, the lubricating fluid composition for a dynamic pressure bearing according to the invention of claim 1 contains an amine-based gelling agent, for example, a lubricant containing an antioxidant as described in claim 4. By using as a base oil solvent, while maintaining good properties of viscosity and evaporation, in particular, the physical properties of high-temperature gelation is improved, it is possible to obtain good properties with a simple structure, A lubricating fluid composition for a dynamic pressure bearing in which one fluid is used both as a lubricating fluid for generating a dynamic pressure and a fluid for a magnetic seal, and the feasibility and reliability of a motor using the same can be improved. .
【００２６】さらに請求項２及び請求項３の発明のよう
に、ゲル化防止剤を所定量にわたって添加することによ
り、動圧軸受を用いたモータの実現性及び信頼性をさら
に向上させることができる。Further, as in the inventions of claims 2 and 3, by adding the gelling inhibitor over a predetermined amount, it is possible to further improve the feasibility and reliability of the motor using the dynamic pressure bearing. .
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ１０Ｎ 10:02 10:14 10:16 30:02 30:08 40:02 40:14 (72)発明者 小林 敏宏 長野県諏訪郡下諏訪町5329番地 株式会社 三協精機製作所内 (72)発明者 清水 和也 神奈川県藤沢市桐原町９番地 タイホー工 業株式会社中央研究所内 (72)発明者 松村 雄介 東京都港区高輪二丁目21番44号 タイホー 工業株式会社内 (72)発明者 長野 克己 愛知県知多市つつじが丘４丁目４番地の12 (72)発明者 小野山 益弘 神奈川県伊勢原市東大竹997−10─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical indication C10N 10:02 10:14 10:16 30:02 30:08 40:02 40:14 (72) Inventor Toshihiro Kobayashi 5329 Shimosuwa-cho, Suwa-gun, Nagano Sankyo Seiki Co., Ltd. (72) Inventor Kazuya Shimizu 9 Kirihara-cho, Fujisawa-shi, Kanagawa Central Research Institute, Taiho Industrial Co., Ltd. (72) Yusuke Matsumura 2-21-44, Takanawa, Minato-ku, Tokyo Within Taiho Industries Co., Ltd. (72) Inventor Katsumi Nagano 12 4-4 Tsutsujigaoka, Chita City, Aichi Prefecture (72) Inventor Masuhiro Onoyama 997-10 Higashi Ohtake, Isehara City, Kanagawa Prefecture
Claims (4)
流体として用いられるものであって、磁性粒子を基油溶
媒中に分散させてなる動圧軸受用潤滑流体組成物におい
て、 上記基油溶媒には、アミン系ゲル化防止剤が添加されて
いることを特徴とする動圧軸受用潤滑流体組成物。1. A lubricating fluid composition for a dynamic pressure bearing, which is used as a lubricating fluid for a dynamic pressure bearing which supports a shaft by dynamic pressure, wherein magnetic particles are dispersed in a base oil solvent. A lubricating fluid composition for a dynamic pressure bearing, wherein an amine-based antigelling agent is added to the oil solvent.
が、０．５重量％超添加されていることを特徴とする動
圧軸受用潤滑流体組成物。2. A lubricating fluid composition for a dynamic pressure bearing, wherein the amine-based antigelling agent according to claim 1 is added in an amount of more than 0.5% by weight.
が、１〜５重量％添加されていることを特徴とする動圧
軸受用潤滑流体組成物。3. A lubricating fluid composition for a dynamic pressure bearing, comprising 1 to 5% by weight of the amine-based antigelling agent according to claim 1.
のアミン系ゲル化防止剤が、アミン系酸化防止剤である
ことを特徴とする動圧軸受用潤滑流体組成物。4. A lubricating fluid composition for a dynamic pressure bearing, wherein the amine-based antigelling agent according to claim 1, 2 or 3 is an amine-based antioxidant.