JPH0825859A - Magnetic recording medium - Google Patents
Magnetic recording mediumInfo
- Publication number
- JPH0825859A JPH0825859A JP6185080A JP18508094A JPH0825859A JP H0825859 A JPH0825859 A JP H0825859A JP 6185080 A JP6185080 A JP 6185080A JP 18508094 A JP18508094 A JP 18508094A JP H0825859 A JPH0825859 A JP H0825859A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- magnetic recording
- recording medium
- printing
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、特に乗車券、定期券、
通行券等の券紙類、キャッシュカード、プリペードカー
ド、ＩＤカード、セーフティカード等のカード類として
好適に使用される磁気記録媒体の偽造防止技術に関し、
特にフルカラー複写機による複製防止に有効な磁気記録
媒体に関する。BACKGROUND OF THE INVENTION The present invention is particularly applicable to passenger tickets, commuter passes,
A technology for preventing forgery of a magnetic recording medium which is preferably used as a card such as a pass ticket, a cash card, a prepaid card, an ID card, a safety card,
In particular, the present invention relates to a magnetic recording medium that is effective in preventing duplication by a full-color copying machine.
【０００２】[0002]
【従来の技術】近年、乗車券、定期券、通行券等の券紙
類、キャッシュカード、プリペードカード、ＩＤカード
等のカード類は、磁気記録媒体方式により情報を入出力
することが一般化している。これらの券紙、カード類に
は、偽造、変造、複製を防止するために様々な防止策が
取られている。例えば、特開昭４７−３７８１１号公報
に記載されているような磁気のバーコードにより偽造を
防止する方法、特開平３−２５８５９４号公報に記載さ
れているような光学バーコードにより偽造を防止する方
法等が提案されている。しかしながら、これらの方法
は、検知装置により情報を識別する場合には有効である
が、例えば、定期券や入場券に代表されるように、視覚
情報を検査官の目によって識別する場合には、全く効果
を示さない。最近はフルカラー複写機の性能が著しく向
上したことに伴い、紙幣、金券、証券などを始め、定期
券や入場券などの分野においても複製券による不正入
場、不正乗車が大きな問題となっている。このフルカラ
ー複写機による複製を防止する方法としては、現行のフ
ルカラー複写機では色再現性が不可能な金属光沢を有す
るマークや、模様等の印刷層を金券等の全面もしくは一
部に設ける提案がなされている。この印刷層にはアルミ
ニウム等の金属粉を含有させた印刷インクが使用されて
いるが、従来の印刷インクは、金属光沢が不十分であ
り、改善が求められていた。さらに、ポリエチレンテレ
フタレート等のフィルム上に剥離層、アルミニウム等の
金属蒸着層、接着層が順次設けられた箔押紙を使用し、
金属光沢を有するマーク等を金券等に転写することによ
り、複製を防止する方法や、ホログラムを金券等に貼り
合わせることによって、複製を防止する提案がなされて
いる。しかしながら、これら複製を防止するための媒体
は、構成が複雑なために製造コストが高く、さらに、金
券等への加工には専用の装置が必要なため、この加工を
含めたトータルコストが高いという問題を有していた。2. Description of the Related Art In recent years, it has become general to input and output information on magnetic recording media for ticket papers such as boarding tickets, commuter tickets, pass tickets, and cards such as cash cards, prepaid cards, and ID cards. There is. Various preventive measures are taken on these ticket papers and cards in order to prevent forgery, alteration, and duplication. For example, a method of preventing forgery by a magnetic bar code as described in JP-A-47-37811, and a forgery by an optical bar code as described in JP-A-3-258594. Methods etc. have been proposed. However, although these methods are effective when identifying information by a detection device, for example, when visual information is identified by the eyes of an inspector, as typified by commuter passes and entrance tickets, Has no effect. Recently, as the performance of a full-color copying machine has been remarkably improved, unauthorized entry and unauthorized boarding with duplicate tickets have become a serious problem in fields such as banknotes, cash vouchers, securities, and commuter tickets and entrance tickets. As a method of preventing duplication by this full-color copying machine, there is a proposal to provide a printing layer such as a mark or a pattern having metallic luster, which cannot be color reproducible by the current full-color copying machine, on all or part of a gold voucher. Has been done. A printing ink containing a metal powder such as aluminum is used for this printing layer. However, the conventional printing ink has insufficient metallic luster and has been required to be improved. Further, using a foil stamping paper in which a release layer, a metal vapor deposition layer such as aluminum, and an adhesive layer are sequentially provided on a film such as polyethylene terephthalate,
There has been proposed a method of preventing duplication by transferring a mark having metallic luster onto a cash voucher or the like, and a method of preventing duplication by attaching a hologram to the cash voucher or the like. However, since the medium for preventing these duplications has a complicated structure, the manufacturing cost is high, and further, since a dedicated device is required for processing into a cash voucher or the like, the total cost including this processing is high. Had a problem.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、従来の技術
における上記事情に鑑みてなされたものであって、その
目的は、偽造が容易に判別できる磁気記録媒体、特にフ
ルカラー複写機による複製ができない安価な磁気記録媒
体を提供することにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances in the prior art, and an object thereof is to make a magnetic recording medium whose forgery can be easily discriminated, particularly a duplication by a full color copying machine. It is to provide an inexpensive magnetic recording medium that cannot be performed.
【０００４】[0004]
【課題を解決するための手段】本発明は上記の問題点の
解決のために鋭意検討の結果得られたものである。本発
明は、支持体上に磁気的に読み書き可能な磁気記録層と
視覚的に識別可能な可視画像情報とを少なくとも有する
磁気記録媒体において、光輝性物質を含有する層を、磁
気記録層上に、および／または支持体の磁気記録層を設
けた側とは反対面上に、全面にわたってまたは部分的に
設けたことを特徴とする。The present invention has been made as a result of extensive studies for solving the above problems. The present invention relates to a magnetic recording medium having at least a magnetically readable and writable magnetic recording layer and a visually distinguishable visible image information on a support, and a layer containing a glittering substance is provided on the magnetic recording layer. And / or on the surface of the support opposite to the side on which the magnetic recording layer is provided, over the entire surface or partially.
【０００５】以下、本発明の詳細について説明する。本
発明で用いられる磁気記録媒体の支持体には、ポリエチ
レンテレフタレート、ポリイミド、ポリカーボネート、
セロファン、芳香族ポリアミドなどの各種の耐熱性樹脂
フィルム、上質紙、コート紙、アート紙、合成樹脂フィ
ルム、織布シート、金属、ガラスなどが使用できる。The details of the present invention will be described below. The magnetic recording medium support used in the present invention, polyethylene terephthalate, polyimide, polycarbonate,
Various heat resistant resin films such as cellophane and aromatic polyamide, high quality paper, coated paper, art paper, synthetic resin film, woven fabric sheet, metal, glass and the like can be used.
【０００６】本発明における磁気記録層は、バインダー
中に磁性粉を均一分散して成層されたものである。前記
バインダーとしては、ポリエステル樹脂、塩化ビニル樹
脂、ポリウレタン樹脂、塩化ビニル・酢酸ビニル共重合
体等をあげることができるが、これらに限定されるもの
ではない。これらの樹脂は単独または２種以上を混合し
て用いることもできる。また、磁性粉としては、γ−Ｆ
ｅ2 Ｏ3 、バリウムフェライト、ストロンチウムフェラ
イト等の強磁性体があげられるが、磁気記録情報が通常
の永久磁石により消去または減衰することを防止するた
めには、バリウムフェライト、ストロンチウムフェライ
トのような保磁力が１５００〜５０００エルステッドの
高保磁力材料を使用することが好ましい。The magnetic recording layer in the present invention is formed by uniformly dispersing magnetic powder in a binder. Examples of the binder include, but are not limited to, polyester resin, vinyl chloride resin, polyurethane resin, and vinyl chloride / vinyl acetate copolymer. These resins may be used alone or in combination of two or more. Further, as magnetic powder, γ-F
Examples of ferromagnetic materials include e 2 O 3 , barium ferrite, and strontium ferrite. In order to prevent magnetic recording information from being erased or attenuated by an ordinary permanent magnet, protection such as barium ferrite or strontium ferrite is used. It is preferable to use a high coercive force material having a magnetic force of 1500 to 5000 Oersted.
【０００７】磁気記録層を形成するための塗料またはイ
ンクは、前記バインダー、磁性粉および必要に応じて分
散剤、硬化剤、顔料などを加え、適当な溶剤中に分散し
て得られる。得られた塗料またはインクは、ソルベント
コーティング法、グラビア印刷、スクリーン印刷等によ
り、支持体の少なくとも一面に１〜３０μｍ、好ましく
は３〜１５μｍの厚さになるように全面に塗布するか、
もしくは部分的に塗布してストライプやバー等のパター
ン状の磁気記録層が設定される。また、偽造防止を目的
として、センダスト、パーマロイ等の高透磁率磁気記録
層、さらに酸化鉄磁性粉の如く２００〜１０００エルス
テッド程度の低保磁力の磁気記録層を、上記方法により
複数層になるように積層させることも可能である。The paint or ink for forming the magnetic recording layer is obtained by adding the binder, magnetic powder and, if necessary, a dispersant, a curing agent, a pigment, etc., and dispersing them in a suitable solvent. The obtained paint or ink is applied to the entire surface by a solvent coating method, gravure printing, screen printing or the like so as to have a thickness of 1 to 30 μm, preferably 3 to 15 μm on at least one surface of the support, or
Alternatively, it is partially applied to set a patterned magnetic recording layer such as stripes or bars. For the purpose of preventing forgery, a high magnetic permeability magnetic recording layer such as sendust and permalloy, and a magnetic recording layer having a low coercive force of about 200 to 1000 Oersted such as iron oxide magnetic powder are formed into a plurality of layers by the above method. It is also possible to stack them.
【０００８】本発明における視覚的に識別可能な可視画
像情報とは、前記磁気記録層上または磁気記録層が設け
られていない側の支持体上に、或いは磁気記録媒体に設
けたインキ受像層または印字記録層上に、鉛筆、ボール
ペン、マジック等の筆記具によって、或いは、オフセッ
ト印刷、グラビア印刷、スクリーン印刷、フレキソ印刷
等の各種印刷方式により、固定情報として社名、注意書
き、コマーシャルおよび各種のマーク、模様等を設けた
モノカラーもしくはフルカラー画像、磁気記録媒体に設
けられた書き込み可能な印字記録層に、感熱ヘッド、放
電ヘッド、通電ヘッド、レーザー等により氏名、日付、
残金、乗降駅名等の情報が書き込まれて形成された画像
をいう。The visually identifiable visible image information in the present invention means the magnetic recording layer or the support on the side not provided with the magnetic recording layer, or the ink image receiving layer provided on the magnetic recording medium. On the print recording layer, pencils, ballpoint pens, writing instruments such as magic, or offset printing, gravure printing, screen printing, flexo printing, and other printing methods, as fixed information, company name, notes, commercials and various marks, A monochromatic or full-color image provided with a pattern, a writable print recording layer provided on a magnetic recording medium, a thermal head, a discharge head, an energizing head, a laser, etc.
An image formed by writing information such as the remaining balance and the name of a boarding / alighting station.
【０００９】本発明の磁気記録媒体の第１の態様は、光
輝性物質を含有する層が、磁気記録層上にまたは磁気記
録層が設けられていない側の支持体上に設けられた印字
記録が可能なインク受容層である場合である。この場
合、光輝性物質を含有するインク受容層形成用の塗料ま
たはインキを用いて、磁気記録層上にまたは磁気記録層
が設けられていない側の支持体上にインク受容層を形成
し、次いで、インク受容層上に、オフセット印刷、グラ
ビア印刷、スクリーン印刷、フレキソ印刷等の各種印刷
方式により、或いは熱転写記録により印字記録して、視
覚的に識別可能な可視画像情報を形成すればよい。A first aspect of the magnetic recording medium of the present invention is a print recording in which a layer containing a glittering substance is provided on the magnetic recording layer or on the support on the side where the magnetic recording layer is not provided. This is the case where the ink receiving layer is capable of In this case, an ink receiving layer is formed on the magnetic recording layer or on the support on which the magnetic recording layer is not provided, using a paint or ink for forming an ink receiving layer containing a glittering substance, and then On the ink receiving layer, various printing methods such as offset printing, gravure printing, screen printing, flexographic printing, or thermal transfer recording may be performed for recording to form visually identifiable visible image information.
【００１０】本発明の磁気記録媒体の第２の態様は、光
輝性物質を含有する層が、光輝性物質を含有する塗料ま
たはインクによって形成された印刷層である場合であ
る。この場合、光輝性物質を含有する塗料またはインキ
を用いて、磁気記録層上にまたは磁気記録層が設けられ
ていない側の支持体上に、またはそれらの上に設けられ
たインク受容層の上に、オフセット印刷、グラビア印
刷、スクリーン印刷、フレキソ印刷等の各種印刷方式に
より印刷して、印刷層を形成すればよい。A second aspect of the magnetic recording medium of the present invention is that the layer containing the glittering substance is a printing layer formed by a paint or ink containing the glittering substance. In this case, using a paint or ink containing a glittering substance, on the magnetic recording layer or on the support on the side where the magnetic recording layer is not provided, or on the ink receiving layer provided thereon. Then, the printing layer may be formed by printing by various printing methods such as offset printing, gravure printing, screen printing and flexographic printing.
【００１１】図１〜３は本発明の磁気記録媒体の代表的
な層構成を示す模式的断面図である。本発明の磁気記録
媒体はこれらの構成に限定されるものではない。図１
は、上記第１の態様の一例であって、熱転写記録によっ
て印刷可能な被熱転写層を有する磁気記録媒体の例を示
し、乗降車駅名や使用期間等の可視画像情報を熱転写記
録によって印刷可能な被熱転写層に表示して、感熱転写
型定期券等の用途に適用される。この磁気記録媒体は、
支持体１の片面に、磁気記録層２、保護層３が順次設け
られ、さらにその支持体の反対面に光輝性物質を含有
し、熱転写インクを受像できるインク受容層４、地紋印
刷層５が順次設けられた構成を有している。1 to 3 are schematic sectional views showing a typical layer structure of the magnetic recording medium of the present invention. The magnetic recording medium of the present invention is not limited to these configurations. FIG.
Is an example of the above-mentioned first aspect, showing an example of a magnetic recording medium having a heat transferable layer that can be printed by thermal transfer recording, in which visible image information such as a boarding / alighting station name and period of use can be printed by thermal transfer recording. Displayed on the heat transfer layer, it is applied to heat transfer type commuter pass. This magnetic recording medium
A magnetic recording layer 2 and a protective layer 3 are sequentially provided on one side of a support 1, and an ink receiving layer 4 and a tint block printing layer 5 containing a glittering substance and capable of receiving a thermal transfer ink are provided on the opposite side of the support. It has the structure provided in order.
【００１２】図２は、上記第２の態様の一例であって、
テレホンカード等一般のプリペードカード等の用途に使
用されているタイプの磁気記録媒体の例である。この磁
気記録媒体は、支持体１の片面に、磁気記録層２、隠蔽
層６、第１印刷層７１、第１保護層３１が順次設けら
れ、さらに支持体の反対面に、光輝性物質を含有するイ
ンクで形成された第２印刷層７２、第２保護層３２が順
次設けられた構成からなる。なお、上記の場合、光輝性
物質は、第２印刷層７２に含有されているが、第１印刷
層７１に含有させてもよく、或いは、第１および第２印
刷層の両者に含有させてもよい。図３は、上記第２の態
様の他の一例であって、感熱記録によって残金等の可視
画像情報を表示できる感熱記録層を有する磁気記録媒体
の例である。この磁気記録媒体は、支持体１の片面に、
磁気記録層２、隠蔽層６、印字記録可能な感熱記録層
８、第１保護層３１が順次設けられ、さらに支持体の反
対面に、光輝性物質を含有するインクで形成された多色
の印刷層７、第２保護層３２が順次設けられた構成から
なる。なお、上記の場合、光輝性物質は、印刷層７に含
有されているが、感熱記録層８に含有させてもよい。FIG. 2 shows an example of the second aspect,
It is an example of a magnetic recording medium of a type used for general prepaid cards such as telephone cards. In this magnetic recording medium, the magnetic recording layer 2, the concealing layer 6, the first printing layer 71, and the first protective layer 31 are sequentially provided on one surface of the support 1, and the luster material is further provided on the opposite surface of the support. The second print layer 72 and the second protective layer 32 formed of the contained ink are sequentially provided. In the above case, the glittering substance is contained in the second printing layer 72, but may be contained in the first printing layer 71, or may be contained in both the first and second printing layers. Good. FIG. 3 is another example of the above-described second aspect, and is an example of a magnetic recording medium having a heat-sensitive recording layer capable of displaying visible image information such as remaining money by heat-sensitive recording. This magnetic recording medium has one side of the support 1,
A magnetic recording layer 2, a concealing layer 6, a heat-sensitive recording layer 8 capable of recording and recording, and a first protective layer 31 are sequentially provided, and a multicolored ink formed with an ink containing a glittering substance is provided on the opposite surface of the support. The print layer 7 and the second protective layer 32 are sequentially provided. In the above case, the glittering substance is contained in the printing layer 7, but it may be contained in the thermosensitive recording layer 8.
【００１３】本発明において、光輝性物質としては、基
材として鱗片状ガラスフレークを用い、これに、銀、ニ
ッケル、金等の金属を無電解メッキ法によりコーティン
グしたものが使用される。光輝性物質に使用される金属
としては、可視光線反射率の高い金属、例えば、銀、ア
ルミニウム、ニッケル、クロム、錫、金、白金等が好適
に使用可能であるが、特に銀が好ましい。銀等でコーテ
ィングされた鱗片状ガラスフレークは、液相析出法によ
って着色コーティングされているのが好ましい。（「機
能材料」１９９２年７月号Ｖｏｌ．１２、Ｎｏ．７、第
３２〜３８頁参照）。In the present invention, as the glittering material, there is used a glass flakes as a substrate, which is coated with a metal such as silver, nickel or gold by an electroless plating method. As the metal used for the glittering substance, a metal having a high visible light reflectance, for example, silver, aluminum, nickel, chromium, tin, gold, platinum and the like can be preferably used, and silver is particularly preferable. The glass flakes coated with silver or the like are preferably color-coated by a liquid phase deposition method. (See "Functional Material" July 1992 Vol. 12, No. 7, pages 32-38).
【００１４】本発明において使用する光輝性物質の基材
の形状は、特に限定されるものではないが、形状が整っ
ている方が好ましく、その場合、形成された光輝性物質
を含有する部分の金属光沢がムラのない均一なものとな
る。光輝性物質に使用される基材の平均厚さは、１〜１
０μｍの範囲のものが好適に使用される。より好適に
は、２〜７μｍの範囲のものが使用される。厚さが１μ
ｍ未満の場合は、光輝性物質の物理的強度が低下するた
め、塗料分散時にかかるシェアー等により粉砕し、光輝
性物質が本来有している輝度の低下等、機能が低下す
る。また、１０μｍより大きい場合は、塗料、インクへ
の分散が困難となり、形成された光輝性物質を含有する
部分の金属光沢が低下する。また、基材の平均直径は、
１〜２００μｍの範囲のものが好適に使用される。より
好適には、１０〜１００μｍの範囲のものが使用され
る。平均直径が１μｍ未満の場合には、形成された光輝
性物質を含有する部分の金属光沢が小さくなる。また、
２００μｍより大きい場合は、塗料、インクへの分散性
が悪くなる。The shape of the base material of the glittering material used in the present invention is not particularly limited, but it is preferable that the shape is regular, and in that case, the portion containing the glittering material formed is formed. The metallic luster is uniform and uniform. The average thickness of the base material used for the glitter material is 1 to 1
Those in the range of 0 μm are preferably used. More preferably, those having a range of 2 to 7 μm are used. 1μ thick
If it is less than m, the physical strength of the glittering substance is lowered, so that the glittering substance is crushed by the shear applied during dispersion, and the function such as the reduction of the brightness originally possessed by the glittering substance is lowered. On the other hand, when it is larger than 10 μm, it becomes difficult to disperse it in a paint or an ink, and the metallic luster of the formed portion containing the glittering substance is lowered. The average diameter of the substrate is
Those having a range of 1 to 200 μm are preferably used. More preferably, those having a range of 10 to 100 μm are used. When the average diameter is less than 1 μm, the metallic luster of the formed portion containing the glittering substance becomes small. Also,
If it is larger than 200 μm, the dispersibility in paints and inks becomes poor.
【００１５】前記光輝性物質は、それを含有させる層を
形成するための塗料やインクに均一に分散して使用され
る。この光輝性物質の分散には必要に応じ、ニトロセル
ロース等の樹脂や界面活性剤等の分散剤が使用可能であ
る。光輝性物質の含有量は、形成された光輝性物質を含
有する部分の全固形分濃度で１〜７０％の範囲が好まし
い。より好ましくは、５〜３０％の範囲である。含有量
が１％未満の場合は、光輝性物質の金属光沢が十分発現
されず、７０％より大きい場合は、塗料化、インキ化が
極めて困難なものになってしまう。The glittering substance is used by being uniformly dispersed in a paint or ink for forming a layer containing the glittering substance. If necessary, a resin such as nitrocellulose or a dispersant such as a surfactant can be used to disperse the glittering substance. The content of the glittering substance is preferably in the range of 1 to 70% in terms of the total solid content concentration of the formed portion containing the glittering substance. More preferably, it is in the range of 5 to 30%. When the content is less than 1%, the metallic luster of the glittering substance is not sufficiently exhibited, and when it is more than 70%, it becomes extremely difficult to form a coating material or an ink.
【００１６】本発明の磁気記録媒体は、上記のように、
磁気記録層と視覚的に識別可能な可視画像情報を少なく
とも有しているが、さらに、必要に応じて、上記のよう
なインク受容層、印字記録可能な印字記録層を設けるこ
とができ、さらに隠蔽層、保護層等を有していてもよ
い。インク受容層としては、ポリエステル樹脂、ポリウ
レタン樹脂、（メタ）アクリル酸エステル系共重合体、
ポリ塩化ビニル、ポリ塩化ビニリデン、塩化ビニル−酢
酸ビニル系共重合体などの熱可塑性樹脂を主成分として
形成される。インク受容層には、上記のように光輝性物
質を含有させてもよい。なお、図１においては、熱転写
記録によって印刷可能なインク受容層を有するものを記
載したが、他の記録方法、例えば、インクジェットプリ
ンター、ドットプリンター、電子写真法によるプリンタ
ー或いは複写機により記録可能な受像層を有するもので
あってもよい。また、印字記録可能な印字記録層として
は、感熱記録層、放電記録層、通電記録層、光記録層等
があげられる。これらの印字記録層を構成する材料とし
ては、従来公知のものであれば、如何なるものでも使用
することができる。The magnetic recording medium of the present invention, as described above,
It has at least visible image information that can be visually distinguished from the magnetic recording layer, and, if necessary, can further include an ink receiving layer and a print recording layer capable of print recording as described above. You may have a concealing layer, a protective layer, etc. As the ink receiving layer, a polyester resin, a polyurethane resin, a (meth) acrylic acid ester-based copolymer,
It is formed mainly of a thermoplastic resin such as polyvinyl chloride, polyvinylidene chloride, or a vinyl chloride-vinyl acetate copolymer. The ink receiving layer may contain a glittering substance as described above. Although FIG. 1 shows the one having an ink receiving layer that can be printed by thermal transfer recording, an image that can be recorded by another recording method, for example, an inkjet printer, a dot printer, a printer by electrophotography or a copying machine. It may have a layer. Examples of the print recording layer capable of print recording include a heat sensitive recording layer, a discharge recording layer, an electric recording layer and an optical recording layer. As a material for forming these print recording layers, any conventionally known materials can be used.
【００１７】本発明の磁気記録媒体において、前記固定
情報を磁気記録層上に設ける場合には、磁気記録層の着
色を隠蔽するために磁気記録層の上に隠蔽層を設定する
のが好ましい。この場合、隠蔽層はインキ受容層として
の役目を果たすことになる。隠蔽層は、ポリエステル樹
脂、ポリウレタン樹脂等の樹脂中に、アルミニウムペー
ストや酸化チタン等の顔料を均一分散した塗料を用い、
塗工もしくは印刷して形成することができる。In the magnetic recording medium of the present invention, when the fixed information is provided on the magnetic recording layer, it is preferable to set a concealing layer on the magnetic recording layer in order to conceal the coloring of the magnetic recording layer. In this case, the hiding layer serves as an ink receiving layer. The concealing layer uses a paint in which a pigment such as aluminum paste or titanium oxide is uniformly dispersed in a resin such as polyester resin or polyurethane resin,
It can be formed by coating or printing.
【００１８】また、保護層は、磁気記録媒体の表面保護
を目的として、表裏両面に設けることができる。保護層
のバインダーとしては機械的に強度および安定性、耐熱
強度および安定性、並びに耐薬品性に優れた樹脂類が好
ましい。その具体例として、ポリエステル樹脂、ポリウ
レタン樹脂、ポリスチレン樹脂、各種繊維素系樹脂、ポ
リイミド樹脂、シリコーン樹脂、フッ素樹脂、ポリアリ
レート樹脂、ポリカーボネート樹脂、フェノール樹脂、
エポキシ樹脂、アルキッド樹脂、メラミン樹脂およびこ
れらの樹脂間の共重合体等の各種熱可塑性樹脂類および
熱硬化性樹脂類をあげることができる。これらの樹脂は
単独または２種以上を混合して用いることもできる。上
記のもので硬化が可能な場合、例えば、硬化の手段が熱
である場合、主剤樹脂中に硬化剤、鎖延長剤、触媒等を
添加させることができる。硬化の手段が光、特に紫外線
である場合には、主剤樹脂中に、樹脂モノマー（あるい
はオリゴマー）、光重合開始剤、熱重合禁止剤、各種増
感剤を添加させることができる。硬化の手段が電子線で
ある場合には、主剤樹脂中に各種増感剤を添加させるこ
とができる。保護層は、前記バインダーに必要に応じ、
ワックス、シリコーンおよび顔料等を加え混練するか、
適当な溶剤中に溶解もしくは分散させることによって得
られたインクもしくは塗料を、ソルベントコーティン
グ、グラビア印刷、フレキソ印刷、スクリーン印刷、オ
フセット印刷等により、磁気記録層上（印刷層を設定し
た場合は印刷層上）に０．０１〜１０μｍ、好ましくは
０．１〜５μｍの厚さになるように形成される。The protective layers may be provided on both the front and back sides for the purpose of protecting the surface of the magnetic recording medium. As the binder for the protective layer, resins that are mechanically excellent in strength and stability, heat resistance strength and stability, and chemical resistance are preferable. Specific examples thereof include polyester resin, polyurethane resin, polystyrene resin, various fiber-based resins, polyimide resin, silicone resin, fluororesin, polyarylate resin, polycarbonate resin, phenol resin,
Examples thereof include various thermoplastic resins and thermosetting resins such as epoxy resin, alkyd resin, melamine resin and copolymers between these resins. These resins may be used alone or in combination of two or more. When the above-mentioned one can be cured, for example, when the curing means is heat, a curing agent, a chain extender, a catalyst and the like can be added to the main resin. When the curing means is light, especially ultraviolet rays, a resin monomer (or oligomer), a photopolymerization initiator, a thermal polymerization inhibitor, and various sensitizers can be added to the main resin. When the curing means is an electron beam, various sensitizers can be added to the base resin. The protective layer, if necessary, to the binder,
Add wax, silicone, pigment, etc., or knead,
The ink or paint obtained by dissolving or dispersing it in an appropriate solvent is subjected to solvent coating, gravure printing, flexographic printing, screen printing, offset printing, etc., on the magnetic recording layer (or printing layer when the printing layer is set). It is formed to have a thickness of 0.01 to 10 μm, preferably 0.1 to 5 μm.
【００１９】本発明の磁気記録媒体は、上記のように磁
気記録媒体の片面もしくは両面の表面または表面近傍に
位置する層の一部もしくは全面に光輝性物質を含有させ
るものであり、それにより、磁気記録媒体の偽造を防止
することができる。光輝性物質を含有する層は、金属光
沢を有するが、現在のフルカラー複写機では金属光沢の
色再現はできない状況にあるため、磁気記録媒体の真偽
をこの部分の再現性を調べることによって判別すること
ができる。The magnetic recording medium of the present invention contains a glittering substance in a part or the whole of the surface located on one side or both sides of the magnetic recording medium or in the vicinity of the surface as described above. Forgery of the magnetic recording medium can be prevented. The layer containing the glittering material has metallic luster, but since the color reproduction of metallic luster is not possible with the current full-color copying machines, the authenticity of the magnetic recording medium is determined by examining the reproducibility of this part. can do.
【００２０】[0020]
【実施例】以下、実施例により本発明を具体的に説明す
るが、本発明はこれらに限定されるわけではない。な
お、配合部数は全て重量部を意味する。 実施例１ 図１に示す層構成をもち、感熱転写定期券の用途に使用
される磁気記録媒体を以下のようにして作製した。 （磁気記録層の形成） ・磁性粉：バリウムフェライト １００部 ＢａＯ・６（Ｆｅ2 Ｏ3 ） （保磁力 ２７５０エルステッド） ・バインダー：塩化ビニル−酢酸ビニル−ビニルアルコール共重合体 ２０部 （ＶＡＧＨ、ＵＣＣ社製） ポリウレタン樹脂 ２０部 （ニッポランＮ−２３０４、日本ポリウレタン社製） ・顔料： カーボンブラック ３部 ・分散剤：レシチン １部 ・溶剤： トルエン ６０部 メチルエチルケトン ６０部 メチルイソブチルケトン ６０部 上記混合液をボールミルで８時間分散した後、下記硬化
剤を加え、さらに１時間分散して磁気記録層用の塗料を
得た。 ・硬化剤：ポリイソシアネート ７５％酢酸エチル溶液 １２部 （コロネートＬ、日本ポリウレタン社製） 得られた塗料を、厚さ１８８μｍの乳白色のポリエチレ
ンテレフタレートフィルム（ルミラーＥ２４、東レ社
製）よりなる支持体上に、ソルベントコーティング法に
より塗布し、塗料が未乾燥状態の間に磁場配向処理装置
によって配向処理を行い、１００℃で５分間乾燥し、厚
さ１５μｍの磁気記録層を形成した。EXAMPLES The present invention will now be described in detail with reference to examples, but the present invention is not limited thereto. In addition, all the compounding parts mean a weight part. Example 1 A magnetic recording medium having the layer structure shown in FIG. 1 and used for the purpose of a heat-sensitive transfer commuter pass was produced as follows. (Magnetic formation of the recording layer) magnetic powder of barium ferrite 100 parts BaO · 6 (Fe 2 O 3 ) ( coercive force 2750 Oe) Binder: vinyl chloride - vinyl acetate - vinyl alcohol copolymer 20 parts (VAGH, UCC Polyurethane resin 20 parts (Nipporan N-2304, manufactured by Nippon Polyurethane Company) ・ Pigment: carbon black 3 parts ・ Dispersant: lecithin 1 part ・ Solvent: toluene 60 parts methyl ethyl ketone 60 parts methyl isobutyl ketone 60 parts After being dispersed by a ball mill for 8 hours, the following curing agent was added and further dispersed for 1 hour to obtain a coating material for a magnetic recording layer. Curing agent: Polyisocyanate 75% ethyl acetate solution 12 parts (Coronate L, manufactured by Nippon Polyurethane Co., Ltd.) The obtained coating material was applied on a support made of a milky-white polyethylene terephthalate film (Lumirror E24, manufactured by Toray) having a thickness of 188 μm. Was applied by a solvent coating method, and while the coating material was in an undried state, an orientation treatment was performed by a magnetic field orientation treatment apparatus and dried at 100 ° C. for 5 minutes to form a magnetic recording layer having a thickness of 15 μm.
【００２１】 （保護層の形成） ・バインダー：ニトロセルロース ７部 （ダイセル化学工業社製） ・溶剤： メチルエチルケトン ４３部 トルエン ５０部 上記の混合液をディスパーにて撹拌し、バインダーを溶
解した後、上記磁気記録層上に、ソルベントコーティン
グ法により塗布し、乾燥して、厚さ３．０μｍの保護層
を形成した。 （可視画像情報の形成）支持体上に設けた上記磁気記録
層とは反対の面に、下記の塗料をソルベントコーティン
グ法によって塗布し、乾燥して、感熱転写記録により乗
車降車駅名、使用期間等の可視画像情報を印刷できる厚
さ２．０μｍのインク受容層を形成した。 ・熱可塑性樹脂：ポリエステル樹脂 ８０部 （バイロン２００、東洋紡社製） ・光輝性物質：光輝性フレーク １０部 （メタシャインＲＣＦＳＸ、日本板硝子社製） ・滑剤： カルナバワックス １０部 ・溶剤： メチルエチルケトン／トルエン＝５０／５０ ６６７部 さらに、下記処方からなる印刷層用の塗料を、グラビア
印刷法によってパターン状に塗布し、乾燥して、厚さが
１．５μｍの可視画像情報よりなる印刷層を形成した。 ・バインダー：ポリウレタン樹脂 ２１７部 メチルエチルケトン４０％溶液 （ニッポラン２３０１、日本ポリウレタン社製） ・着色剤：シアン顔料 ５部 （ダイアセリトンファストブリリアントブル−Ｒ、三菱化成社製） ・ワックス：ポリエチレンワックス ３部 （三井ハイワックス１００Ｐ、三井石油化学社製） ・溶剤： メチルエチルケトン／トルエン＝５０／５０ １０６部(Formation of Protective Layer) Binder: Nitrocellulose 7 parts (manufactured by Daicel Chemical Industries, Ltd.) Solvent: Methyl ethyl ketone 43 parts Toluene 50 parts The above mixed solution is stirred with a disper to dissolve the binder, and then the above. It was applied on the magnetic recording layer by a solvent coating method and dried to form a protective layer having a thickness of 3.0 μm. (Formation of visible image information) On the surface opposite to the magnetic recording layer provided on the support, the following paints are applied by the solvent coating method, dried and subjected to thermal transfer recording to get on and off the station, the period of use, etc. An ink receiving layer having a thickness of 2.0 μm capable of printing the visible image information was formed. -Thermoplastic resin: 80 parts of polyester resin (Byron 200, manufactured by Toyobo Co., Ltd.)-Glittering material: 10 parts of glittering flakes (Metashine RCFSX, manufactured by Nippon Sheet Glass Co., Ltd.)-Lubricant: 10 parts of carnauba wax-Solvent: Methyl ethyl ketone / toluene = 50/50 667 parts Furthermore, a coating material for a printing layer having the following formulation was applied in a pattern by a gravure printing method, and dried to form a printing layer having a thickness of 1.5 μm and including visible image information. . -Binder: 217 parts of polyurethane resin Methyl ethyl ketone 40% solution (Nipporan 2301, manufactured by Nippon Polyurethane Company) -Colorant: 5 parts of cyan pigment (Diaceriton Fast Brilliant Bull-R, manufactured by Mitsubishi Kasei) -Wax: Polyethylene wax 3 parts (Mitsui High Wax 100P, manufactured by Mitsui Petrochemical Co., Ltd.)-Solvent: Methyl ethyl ketone / toluene = 50/50 106 parts
【００２２】実施例２ 図２に示す層構成をもつ磁気記録媒体を以下のようにし
て作製した。 （磁気記録層の形成）実施例１と同様にして、厚さ１８
８μｍの乳白色のポリエチレンテレフタレートフィルム
（ルミラーＥ２４、東レ社製）よりなる支持体上に、厚
さ１０μｍの磁気記録層を形成した。 （隠蔽層の形成）下記一般処方からなる隠蔽層用の塗料
を作製した。 ・バインダー：ポリエステル樹脂 １５部 （エリーテルＵＥ３２００、ユニチカ社製） ・顔料： 酸化チタン １５部 ・硬化剤：ポリイソシアネート ４部 （コロネートＬ、７５％酢酸エチル溶解液、 日本ポリウレタン社製） ・溶剤： メチルエチルケトン／トルエン＝５０／５０ ７０部 硬化剤を除いた上記混合液をサンドミルで３時間分散し
た後、硬化剤を加え、ディスパーで１５分間撹拌し、作
製した隠蔽層用塗料を、上記磁気記録層上にソルベント
コーティング法により塗布し、乾燥して、厚さ４μｍの
隠蔽層を形成した。Example 2 A magnetic recording medium having the layer structure shown in FIG. 2 was produced as follows. (Formation of magnetic recording layer) In the same manner as in Example 1, the thickness 18
A magnetic recording layer having a thickness of 10 μm was formed on a support made of an 8 μm milk-white polyethylene terephthalate film (Lumirror E24, manufactured by Toray Industries, Inc.). (Formation of Hiding Layer) A coating material for the hiding layer having the following general formulation was prepared. -Binder: Polyester resin 15 parts (Elitel UE3200, manufactured by Unitika Ltd.)-Pigment: Titanium oxide 15 parts-Curing agent: Polyisocyanate 4 parts (Coronate L, 75% ethyl acetate solution, manufactured by Nippon Polyurethane Company) -Solvent: Methyl ethyl ketone / Toluene = 50/50 70 parts The above mixture liquid excluding the curing agent was dispersed in a sand mill for 3 hours, then the curing agent was added, and the mixture was stirred for 15 minutes with a disper. Was coated by a solvent coating method and dried to form a hiding layer having a thickness of 4 μm.
【００２３】（第１印刷層の形成）Ｔ＆Ｋ ＴＯＫＡ社
製のプロセスインク墨をＵＶオフセット印刷法により所
望のパターンになるように塗布し、上記隠蔽層上に厚さ
１μｍの印刷層（１）を形成した。 （第１保護層の形成） ・バインダー：ニトロセルロース ７部 （ダイセル化学工業社製） ・溶剤： メチルエチルケトン ４３部 トルエン ５０部 上記の混合液を、ディスパーにて撹拌し、バインダーを
溶解した後、上記磁気記録層上に、ソルベントコーティ
ング法により塗布し、乾燥して、厚さ３．０μｍの第１
保護層を形成した。(Formation of First Printing Layer) Process ink made by T & K TOKA Co. is applied by UV offset printing in a desired pattern, and a printing layer (1) having a thickness of 1 μm is formed on the above-mentioned concealing layer. Formed. (Formation of first protective layer) -Binder: Nitrocellulose 7 parts (manufactured by Daicel Chemical Industries, Ltd.)-Solvent: Methyl ethyl ketone 43 parts Toluene 50 parts The above mixed solution is stirred with a disper to dissolve the binder, and then the above. The magnetic recording layer is coated with a solvent coating method and dried to form a first layer having a thickness of 3.0 μm.
A protective layer was formed.
【００２４】 （第２印刷層の形成） イエローインキ ・ＵＶインキ：Ｔ＆Ｋ ＴＯＫＡ社製 プロセスインキ黄 ９０部 ・光輝性物質：光輝性フレーク １０部 （メタシャインＲＣＦＳＸ、日本板硝子社製） マジェンタインキ ・ＵＶインキ：Ｔ＆Ｋ ＴＯＫＡ社製 プロセスインキ赤 ９０部 ・光輝性物質：光輝性フレーク １０部 （メタシャインＲＣＦＳＸ、日本板硝子社製） シアンインキ ・ＵＶインキ：Ｔ＆Ｋ ＴＯＫＡ社製 プロセスインキ藍 ９０部 ・光輝性物質：光輝性フレーク １０部 （メタシャインＲＣＦＳＸ、日本板硝子社製） ブラックインキ ・ＵＶインキ：Ｔ＆Ｋ ＴＯＫＡ社製 プロセスインキ墨 ９０部 ・光輝性物質：光輝性フレーク １０部 （メタシャインＲＣＦＳＸ、日本板硝子社製） 上記光輝性物質を加えた上記各色のＵＶインキを３本ロ
ールで混練し、印刷層用の４色の印刷インキを得た。得
られた印刷インキを、ＵＶオフセット印刷法により所望
のパターンになるように、上記磁気記録層とは反対の面
に塗布し、厚さ１μｍの第２印刷層を形成した。さら
に、Ｔ＆Ｋ ＴＯＫＡ社製ＵＶインキＵＰ−２を上記第
２印刷層上に、ＵＶオフセット印刷法により塗布して、
厚さ２．０μｍの第２保護層を形成した。(Formation of Second Printing Layer) Yellow Ink-UV Ink: T & K TOKA Process Ink Yellow 90 parts-Glittering substance: Glitter flakes 10 parts (Metashine RC FSX, Nippon Sheet Glass Co., Ltd.) Magenta ink-UV Ink: T & K TOKA process ink red 90 parts-Glittering substance: Glitter flakes 10 parts (Metashine RCFSX, Nippon Sheet Glass Co., Ltd.) Cyan ink-UV ink: T & K TOKA process ink indigo 90 parts-Glittering substance : Glitter flakes 10 parts (Metashine RCFSX, manufactured by Nippon Sheet Glass Co., Ltd.) Black ink-UV ink: T & K TOKA process ink 90 parts-Glittering substance: Glitter flakes 10 parts (Metashine RC FSX, manufactured by Nippon Sheet Glass Co., Ltd.) ) UV of each of the above colors to which the above-mentioned glittering substance is added The ink was kneaded with three rolls to obtain four colors of printing ink for the printing layer. The obtained printing ink was applied to the surface opposite to the magnetic recording layer by a UV offset printing method so as to have a desired pattern to form a second printing layer having a thickness of 1 μm. Further, UV ink UP-2 manufactured by T & K TOKA Co., Ltd. is applied onto the second printing layer by a UV offset printing method,
A second protective layer having a thickness of 2.0 μm was formed.
【００２５】実施例３ 図３に示す層構成をもつ磁気記録媒体を以下のようにし
て作製した。実施例２において、第１印刷層に代えて、
下記に示す感熱記録層用塗料を作製し、ソルベントコー
ティング法により塗布し、隠蔽層上に厚さ５μｍの感熱
記録層を形成した。 （Ａ液） ・３−Ｎ−エチル−Ｎ−（２−エトキシプロピル）アミノ− １０部 ６−メチル−７−アニリノフルオラン ・ポリメチルメタクリレート樹脂（Ｍｗ＝約３万） の２０％トルエン溶液 ５部 ・トルエン １０部 （Ｂ液） ・ビス（４−ヒドロキシフェニル）酢酸メチルエステル １０部 ・ポリメチルメタクリレート樹脂（Ｍｗ＝約３万） の２０％トルエン溶液 ５部 ・トルエン １０部 （感熱記録層用塗料） ・Ａ液 ２５部 ・Ｂ液 ５０部 ・ポリメチルメタクリレート樹脂（Ｍｗ＝約３万） の２０％トルエン溶液 ５０部 なお、上記Ａ液およびＢ液は、サンドグラインダーを用
いて分散処理した。さらに、実施例２における第１保護
層に代えて、下記に示す組成の第１保護層用塗料を用
い、上記感熱記録層上に厚さ２μｍの第１保護層を形成
した以外は、実施例２と同様に操作して、磁気記録媒体
を作製した。 （第１保護層用塗料） ・水酸化アルミニウム３０％トルエン分散液 ３部 ・フルオロカーボン１０％トルエン分散液 ５部 ・ポリメチルメタクリレート樹脂（Ｍｗ＝約３万） の２０％トルエン溶液 ５０部Example 3 A magnetic recording medium having the layer structure shown in FIG. 3 was produced as follows. In Example 2, instead of the first printing layer,
A coating material for a heat-sensitive recording layer shown below was prepared and applied by a solvent coating method to form a heat-sensitive recording layer having a thickness of 5 μm on the hiding layer. (Liquid A) 3-N-ethyl-N- (2-ethoxypropyl) amino-10 parts 6-methyl-7-anilinofluorane 20% toluene solution of polymethylmethacrylate resin (Mw = about 30,000) 5 parts-Toluene 10 parts (B liquid) -Bis (4-hydroxyphenyl) acetic acid methyl ester 10 parts-Polymethylmethacrylate resin (Mw = about 30,000) 20% toluene solution 5 parts-Toluene 10 parts (heat-sensitive recording layer Coating solution) -A solution 25 parts-B solution 50 parts-Polymethylmethacrylate resin (Mw = about 30,000) 20% toluene solution 50 parts In addition, the above-mentioned solutions A and B were dispersed using a sand grinder. . Further, instead of the first protective layer in Example 2, a coating material for the first protective layer having the composition shown below was used, and the first protective layer having a thickness of 2 μm was formed on the heat-sensitive recording layer. The same operation as in 2 was performed to produce a magnetic recording medium. (Coating for the first protective layer) -Aluminum hydroxide 30% toluene dispersion 3 parts-Fluorocarbon 10% toluene dispersion 5 parts-Polymethylmethacrylate resin (Mw = about 30,000) 20% toluene solution 50 parts
【００２６】比較例１ 実施例２の可視画像情報の形成における印刷インキにつ
いて、光輝性物質を除いた以外は、実施例２と同様にし
て磁気記録媒体を得た。 比較例２ 実施例１のインク受容層に用いられている光輝性物質に
代えて、アルミニウムペースト（Ｍ−８０１、旭化成社
製）を用いた以外は、実施例１と同様にして磁気記録媒
体を得た。COMPARATIVE EXAMPLE 1 A magnetic recording medium was obtained in the same manner as in Example 2 except that the glittering substance was omitted from the printing ink for forming visible image information in Example 2. Comparative Example 2 A magnetic recording medium was prepared in the same manner as in Example 1 except that an aluminum paste (M-801, manufactured by Asahi Kasei Co., Ltd.) was used in place of the glittering substance used in the ink receiving layer of Example 1. Obtained.
【００２７】以上のようにして得られた各磁気記録媒体
の視覚的に識別可能な可視画像情報を、キャノン社製の
フルカラープリンターピクセルデュオで５枚複写し、オ
リジナルとの真偽テストを次のように行った。判定はあ
らかじめオリジナルパターンを確認した後、複写したサ
ンプルの中にオリジナルをランダムに入れ、順繰りに数
秒間観察し、オリジナルか否かを視覚的に判別するテス
トを無作為に抽出したモニター１００人により行った。
表１にその正解率を示す。The visually identifiable visible image information of each magnetic recording medium obtained as described above was copied by five sheets with a full color printer pixel duo manufactured by Canon Inc., and the authenticity test with the original was performed as follows. So went. The judgment was made by checking the original pattern in advance, randomly putting the original in the copied sample, observing for several seconds in sequence, and randomly selecting a test to visually judge whether it was the original or not. went.
Table 1 shows the correct answer rate.
【表１】 [Table 1]
【００２８】[0028]
【発明の効果】本発明の磁気記録媒体は、光輝性物質を
含有する層を、磁気記録層上に、および／または支持体
の磁気記録層を設けた側とは反対面上に、全面にわたっ
てまたは部分的に設けたから、偽造の判別を容易に行う
ことができ、フルカラー複写機により複製が不可能であ
る。したがって、磁気記録媒体が有する視覚情報をフル
カラー複写機で複製し、不正に使用されることが簡便
に、かつ、安価に防止できるという効果を奏する。In the magnetic recording medium of the present invention, a layer containing a glittering substance is formed on the entire surface of the magnetic recording layer and / or on the surface of the support opposite to the side on which the magnetic recording layer is provided. Alternatively, since it is partially provided, it is possible to easily discriminate the forgery, and it is impossible to make a copy by a full-color copying machine. Therefore, there is an effect that it is possible to easily and inexpensively prevent the illegal use by copying the visual information of the magnetic recording medium by the full-color copying machine.
【図１】 本発明の磁気記録媒体の一例を示す模式的断
面図である。FIG. 1 is a schematic cross-sectional view showing an example of a magnetic recording medium of the present invention.
【図２】 本発明の磁気記録媒体の一例を示す模式的断
面図である。FIG. 2 is a schematic sectional view showing an example of a magnetic recording medium of the present invention.
【図３】 本発明の磁気記録媒体の一例を示す模式的断
面図である。FIG. 3 is a schematic sectional view showing an example of a magnetic recording medium of the present invention.
１…支持体、２…磁気記録層、３…保護層、３１…第１
保護層、３２…第２保護層、４…インク受容層、５…地
紋印刷層、６…隠蔽層、７…印刷層、７１…第１印刷
層、７２…第２印刷層、８…感熱記録層1 ... Support, 2 ... Magnetic recording layer, 3 ... Protective layer, 31 ... First
Protective layer, 32 ... Second protective layer, 4 ... Ink receiving layer, 5 ... Background pattern printing layer, 6 ... Hiding layer, 7 ... Printing layer, 71 ... First printing layer, 72 ... Second printing layer, 8 ... Thermal recording layer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 // Ｇ１１Ｂ 23/38 Ｚ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Office reference number FI technical display location // G11B 23/38 Z
Claims (4)
記録層と視覚的に識別可能な可視画像情報とを少なくと
も有する磁気記録媒体において、光輝性物質を含有する
層を、磁気記録層上に、および／または支持体の磁気記
録層を設けた側とは反対面上に、全面にわたって、また
は部分的に設けたことを特徴とする磁気記録媒体。1. A magnetic recording medium having at least a magnetically readable and writable magnetic recording layer and a visually distinguishable visible image information on a support, wherein a layer containing a glittering substance is provided on the magnetic recording layer. And / or on the surface of the support opposite to the surface on which the magnetic recording layer is provided, over the entire surface or partly.
で被覆したものであることを特徴とする請求項１記載の
磁気記録媒体。2. The magnetic recording medium according to claim 1, wherein the glittering material is glass flakes coated with a metal.
可能なインク受容層である請求項１記載の磁気記録媒
体。3. The magnetic recording medium according to claim 1, wherein the layer containing the glittering substance is an ink receiving layer capable of printing and recording.
を含有する塗料またはインクによって形成された印刷層
である請求項１記載の磁気記録媒体。4. The magnetic recording medium according to claim 1, wherein the layer containing the glittering substance is a printed layer formed by a paint or ink containing the glittering substance.