JPH0825594A - Multilayer sealant film for laminate - Google Patents
Multilayer sealant film for laminateInfo
- Publication number
- JPH0825594A JPH0825594A JP16344294A JP16344294A JPH0825594A JP H0825594 A JPH0825594 A JP H0825594A JP 16344294 A JP16344294 A JP 16344294A JP 16344294 A JP16344294 A JP 16344294A JP H0825594 A JPH0825594 A JP H0825594A
- Authority
- JP
- Japan
- Prior art keywords
- sealant film
- layer
- density
- film
- multilayer sealant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、120℃におけるレト
ルト処理が可能なラミネート用の多層シーラントフィル
ムに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a multilayer sealant film for laminating which can be retort treated at 120 ° C.
【0002】[0002]
【従来の技術】従来からレトルト食品の包装にはポリエ
ステル樹脂フィルム、ポリアミド樹脂フィルム、エチレ
ン・ビニールアルコール共重合体フイルム、アルミニウ
ム箔等の基材フィルムにポリオレフィン樹脂系のシーラ
ントフィルムを積層したラミネートフィルムが広く用い
られている。特に、レトルト処理条件が通常120℃前
後であることから、このような目的に使用するラミネー
トフィルムに使用するシーラントフィルムも120℃以
上の耐熱性を有している必要がある。したがって、従来
シーラントフィルムとしては耐熱性とシール性に優れて
いるポリプロピレン系樹脂や高密度ポリエチレン樹脂等
が用いられていた。2. Description of the Related Art Conventionally, a laminated film in which a polyolefin resin sealant film is laminated on a base film such as a polyester resin film, a polyamide resin film, an ethylene / vinyl alcohol copolymer film, and an aluminum foil has been used for packaging retort foods. Widely used. In particular, since the retort treatment condition is usually around 120 ° C, the sealant film used for the laminate film used for such a purpose also needs to have heat resistance of 120 ° C or higher. Therefore, conventionally, as the sealant film, polypropylene-based resin, high-density polyethylene resin, or the like, which has excellent heat resistance and sealability, has been used.
【0003】ところが、レトルト食品包装用ラミネート
フィルムにおいては、シール強度をある程度以上にする
ためにラミネートフィルム全体の厚みに占めるシーラン
ト層の厚みの割合を大きくしている関係上、シーラント
層の性質がラミネートフィルム全体の性質に大きく影響
を及ぼす。例えば、ポリプロピレン系樹脂や高密度ポリ
エチレン樹脂のように低温時の耐衝撃強度が弱い樹脂を
シーラントフィルムとして用いた場合には低温輸送時等
に包装袋が破袋するという問題点があった。However, in the laminated film for packaging retort food, since the ratio of the thickness of the sealant layer to the total thickness of the laminated film is increased in order to obtain a certain level of sealing strength, the property of the sealant layer is a laminate. It greatly affects the properties of the entire film. For example, when a resin having a low impact strength at low temperature such as polypropylene resin or high-density polyethylene resin is used as the sealant film, there is a problem that the packaging bag is broken during transportation at low temperature.
【0004】更に、ポリプロピレン系樹脂として、プロ
ピレン・エチレンランダム共重合体樹脂をシーラントフ
ィルムとして用いた場合は、レトルト処理時の熱により
シーラント層同士が熱融着して開口性が低下し内容物が
取り出しにくくなるという欠点があり、プロピレン・エ
チレンブロック共重合体樹脂や高密度ポリエチレン樹脂
をシーラント層として用いた場合は、これらの樹脂の融
点が高いことから、安定したヒートシールが困難であ
り、シール抜けによる破袋トラブル等が発生しやすいと
いう欠点があった。Furthermore, when a propylene / ethylene random copolymer resin is used as the polypropylene resin as the sealant film, the heat during the retort treatment causes the sealant layers to be heat-sealed to each other, resulting in a decrease in the opening property and the content of the product. There is a drawback that it is difficult to take out, and when propylene / ethylene block copolymer resin or high-density polyethylene resin is used as the sealant layer, stable melting is difficult because of the high melting point of these resins. There was a drawback that bag breakage problems and the like due to falling out were likely to occur.
【0005】一方、直鎖状低密度ポリエチレンは透明
性、低温時の衝撃強度、シール性に優れており、従来か
ら100℃位までのボイル殺菌用途のシーラントフィル
ムとしては使用されている。しかしながら直鎖状低密度
ポリエチレンは融点が125℃前後と低いので120℃
でのレトルト処理によって、プロピレン・エチレンラン
ダム共重合体の場合に比べて更にシーラント層同士が熱
融着しやすいため、レトルト食品包装用ラミネートフィ
ルムのシーラント層としては使用できなかった。On the other hand, linear low-density polyethylene is excellent in transparency, impact strength at low temperature, and sealing property, and has been conventionally used as a sealant film for boiling sterilization up to about 100 ° C. However, linear low-density polyethylene has a low melting point of around 125 ° C, so 120 ° C
Since the sealant layers were more likely to be heat-sealed by the retort treatment in Example 1 as compared with the case of the propylene / ethylene random copolymer, it could not be used as the sealant layer of the laminated film for retort food packaging.
【0006】このような問題点を解決するものとして、
本出願人は先にアンチブロッキング剤を添加した密度が
0.930〜0.945g/cm3 の直鎖状低密度ポリエチ
レンからなるシーラント層を有するレトルト食品包装用
ラミネートフィルム(特開平5−261871号公報)
を提案した。しかしながら、このフィルムを用いて12
0℃以上のレトルト処理を行った場合、熱融着の問題は
解決できるが、レトルト処理後にフィルムが白化すると
いう問題があった。As a solution to such a problem,
The applicant of the present invention has previously disclosed a laminated film for packaging retort foods, which has a sealant layer made of linear low-density polyethylene having a density of 0.930 to 0.945 g / cm 3 to which an anti-blocking agent has been added (JP-A-5-261871). Gazette)
Suggested. However, with this film 12
When the retort treatment is performed at 0 ° C. or higher, the problem of heat fusion can be solved, but there is a problem that the film is whitened after the retort treatment.
【0007】[0007]
【発明が解決しようとする課題】本発明の目的とすると
ころは、耐衝撃性、耐熱融着性、安定したシール性およ
び透明性の優れた、即ち、従来の技術の問題点をカバー
することのできるレトルト用途に適したラミネート用多
層シーラントフィルムを提供することにある。DISCLOSURE OF THE INVENTION The object of the present invention is to provide excellent impact resistance, heat fusion resistance, stable sealability and transparency, that is, to cover the problems of the prior art. It is to provide a multilayer sealant film for laminating suitable for retort applications.
【0008】[0008]
【課題を解決するための手段】本発明によれば、内層側
をシール面としたポリエチレン系樹脂からなる三層構成
のラミネート用多層シーラントフィルムにおいて、
(A)内層がアンチブロッキング剤を0.4〜5重量%
含有した、密度が0.945g/cm3 以上の高密度ポリエ
チレンと軟質ポリマーの樹脂組成物からなり、該軟質ポ
リマーの含有量が5〜30重量%であり、(B)中間層
が造核剤を0.1〜0.5重量%含有した密度が0.9
35g/cm3 以上の直鎖状低密度ポリエチレンを主成分と
する樹脂組成物からなり、(C)外層が中間層と同程度
の耐熱性と耐衝撃性を有するポリエチレン系樹脂からな
るラミネート用多層シーラントフィルムが提供され、更
に、中間層の厚みが全体厚みの40〜90%である前記
ラミネート用多層シーラントフィルムが提供され、更
に、中間層の厚みが全体厚みの60〜90%である前記
ラミネート用多層シーラントフィルムが提供され、更
に、外層に使用するポリエチレン系樹脂が密度が0.9
35g/cm3 以上の直鎖状低密度ポリエチレン又は高密度
ポリエチレンである前記ラミネート用多層シーラントフ
ィルムが提供され、更に、軟質ポリマーが密度が0.9
00g/cm3 以下のエチレンとα−オレフィンの共重合体
である前記ラミネート用多層シーラントフィルムが提供
され、更にまた、造核剤がソルビトール系誘導体又はそ
の核置換体である前記ラミネート用多層シーラントフィ
ルムが提供される。According to the present invention, in a multi-layer sealant film for laminating having a three-layer structure comprising a polyethylene resin having an inner layer side as a sealing surface,
(A) The inner layer contains 0.4-5% by weight of an anti-blocking agent
The resin composition comprises a high density polyethylene having a density of 0.945 g / cm 3 or more and a soft polymer, the content of the soft polymer is 5 to 30% by weight, and the intermediate layer (B) is a nucleating agent. Containing 0.1 to 0.5% by weight has a density of 0.9
A multi-layer for laminating comprising a resin composition containing 35 g / cm 3 or more of linear low-density polyethylene as a main component, and (C) an outer layer made of a polyethylene resin having heat resistance and impact resistance comparable to those of the intermediate layer. A sealant film is provided, and further, the multilayer sealant film for laminating wherein the thickness of the intermediate layer is 40 to 90% of the total thickness is provided, and further the thickness of the intermediate layer is 60 to 90% of the total thickness. A multilayer sealant film is provided for the outer layer, and the polyethylene resin used for the outer layer has a density of 0.9.
A multilayer sealant film for lamination, which is linear low-density polyethylene or high-density polyethylene of 35 g / cm 3 or more, is provided, and the soft polymer has a density of 0.9.
Provided is the multilayer sealant film for lamination, which is a copolymer of ethylene and α-olefin of 00 g / cm 3 or less, and further, the multilayer sealant film for laminate, wherein the nucleating agent is a sorbitol derivative or a nucleus substitution product thereof. Will be provided.
【0009】すなわち、直鎖状低密度ポリエチレンに造
核剤を添加すれば、レトルト処理後の白化が防止でき、
しかも造核剤を含有する中間層の両側に造核剤を含有し
ていない外層及び内層を配することにより造核剤がブリ
ードアウトすることが防止できること、更にシール面で
ある内層に高密度ポリエチレンと軟質ポリマーの混合物
に、更にアンチブロッキング剤を配合することにより熱
融着が防止でき、低温ヒートシール性も付与できること
を見いだし本発明に到達した。That is, by adding a nucleating agent to linear low-density polyethylene, whitening after retort treatment can be prevented,
Moreover, it is possible to prevent the nucleating agent from bleeding out by arranging the outer layer and the inner layer containing no nucleating agent on both sides of the intermediate layer containing the nucleating agent. The present invention has been accomplished by discovering that heat fusion can be prevented and low-temperature heat sealability can be imparted by further blending an anti-blocking agent in a mixture of a soft polymer and a soft polymer.
【0010】以下、本発明を図面に基づいて具体的に説
明する。本発明のラミネート用多層シーラントフィルム
1の内層(A)は高密度ポリエチレン、軟質ポリマー及
びアンチブロッキング剤からなる樹脂組成物で形成され
ている。高密度ポリエチレンは内層(A)に耐熱性を付
与する作用があり、軟質ポリマーは耐衝撃性とシール
性、アンチブロッキング剤は熱融着性を防止する作用を
有している。したがって、高密度ポリエチレンとしては
密度が0.945g/cm3 以上、特に、0.950〜0.
960g/cm3 が好ましい。密度が0.945g/cm3 未満
の場合は耐熱性が不足し、0.965g/cm3 を超えると
低温時の耐衝撃性やシール性が悪くなる。The present invention will be specifically described below with reference to the drawings. The inner layer (A) of the multilayer sealant film 1 for laminating according to the present invention is formed of a resin composition comprising high density polyethylene, a soft polymer and an antiblocking agent. The high-density polyethylene has an effect of imparting heat resistance to the inner layer (A), the soft polymer has an impact resistance and a sealing property, and the antiblocking agent has an effect of preventing heat fusion property. Therefore, the density of the high-density polyethylene is 0.945 g / cm 3 or more, and particularly 0.950-0.
960 g / cm 3 is preferred. If the density is less than 0.945 g / cm 3 , the heat resistance will be insufficient, and if it exceeds 0.965 g / cm 3 , the impact resistance at low temperatures and the sealing property will be poor.
【0012】また、軟質ポリマーとしては、通常、ポリ
オレフィン系樹脂の耐衝撃性やシール性の改良に使用さ
れているものが使用でき、例えば、密度が0.900g/
cm3以下のエチレン−プロピレン共重合体、エチレン−
ブテン共重合体等のエチレン・α−オレフィン共重合
体、スチレン・ブタジエン共重合体又はその水素添加
物、あるいはオレフィン系の各種ゴム状ポリマー等が挙
げられる。本発明においては、特に、エチレン・α−オ
レフィン共重合体が好ましい。本発明においては内層
(A)における高密度ポリエチレンの密度及び軟質ポリ
マーの配合割合が特に重要であり、軟質ポリマーの使用
量は5〜30重量%の範囲とすることが好ましい。使用
量が5重量%未満であると衝撃強度とシール性の改良効
果が十分ではなく、30重量%を越えるとシーラントフ
ィルム1の耐熱性が不足して、特に、レトルト時のフィ
ルム同士の内面が融着するので好ましくない。As the soft polymer, those generally used for improving impact resistance and sealing property of polyolefin resin can be used. For example, the density thereof is 0.900 g /
cm 3 or less ethylene-propylene copolymer, ethylene-
Examples thereof include ethylene / α-olefin copolymers such as butene copolymers, styrene / butadiene copolymers or hydrogenated products thereof, and various olefin-based rubber-like polymers. In the present invention, an ethylene / α-olefin copolymer is particularly preferable. In the present invention, the density of the high-density polyethylene and the blending ratio of the soft polymer in the inner layer (A) are particularly important, and the amount of the soft polymer used is preferably in the range of 5 to 30% by weight. If the amount used is less than 5% by weight, the effect of improving impact strength and sealability is not sufficient, and if it exceeds 30% by weight, the heat resistance of the sealant film 1 is insufficient, and especially the inner surfaces of the films during retort It is not preferable because it is fused.
【0013】更に、内面の熱融着を防止する目的で使用
するアンチブロッキング剤としては、シリカ系、シリコ
ーン系、ゼオライト系等の通常のアンチブロッキング剤
が特に制限なく使用できる。アンチブロッキング剤の含
有量は0.4〜5重量%、好ましくは1.0〜3重量%
であり、0.4重量%未満の場合は熱融着の防止効果が
不十分であり、5重量%を越えて用いると透明性が悪化
するので好ましくない。Further, as the antiblocking agent used for the purpose of preventing heat fusion of the inner surface, usual antiblocking agents such as silica type, silicone type and zeolite type can be used without particular limitation. The content of the anti-blocking agent is 0.4 to 5% by weight, preferably 1.0 to 3% by weight
If it is less than 0.4% by weight, the effect of preventing heat fusion is insufficient, and if it exceeds 5% by weight, the transparency is deteriorated, which is not preferable.
【0014】中間層(B)は造核剤を含有する密度が
0.935g/cm3 以上、好ましくは0.940〜0.9
45g/cm3 の直鎖状低密度ポリエチレンを主成分とする
樹脂組成物から形成される。直鎖状低密度ポリエチレン
の密度が0.935g/cm2 未満の場合はシーラントフィ
ルム全体の耐熱性が低下して変形しやすくなるので好ま
しくない。また、密度が0.945g/cm3 を超える場合
は耐衝撃強度が低下するので好ましくない。なお、本発
明においては全体の耐衝撃性を向上させるために必要に
応じて前記軟質ポリマーを0〜30重量%の範囲で混合
したり、特性を代えない程度で高密度ポリエチレン等の
他の熱可塑性樹脂を混合することも可能である。The intermediate layer (B) contains a nucleating agent and has a density of 0.935 g / cm 3 or more, preferably 0.940 to 0.9.
It is formed from a resin composition containing 45 g / cm 3 of linear low-density polyethylene as a main component. If the density of the linear low-density polyethylene is less than 0.935 g / cm 2 , the heat resistance of the sealant film as a whole is lowered and the sealant film is easily deformed, which is not preferable. Further, if the density exceeds 0.945 g / cm 3 , the impact strength decreases, which is not preferable. In the present invention, in order to improve the overall impact resistance, the soft polymer is mixed in the range of 0 to 30% by weight as required, or other heat such as high density polyethylene is used as long as the characteristics are not changed. It is also possible to mix a plastic resin.
【0015】本発明に使用する造核剤としては、特に、
制限はないが、通常、ソルビトール系誘導体もしくはそ
の核置換体が好ましく使用できる。特に、臭気等を考慮
すればジベンジリデンソルビトールを使用することが好
ましい。その中間層(B)における含有量は0.1〜
0.5重量%、好ましくは0.15〜0.5重量%であ
る。含有量が0.1重量%未満であると造核剤の白化防
止効果が少なくなり、0.5重量%以上添加しても効果
は変わらない。The nucleating agent used in the present invention is, in particular,
There is no limitation, but usually, a sorbitol derivative or a nuclear substitution product thereof can be preferably used. In particular, it is preferable to use dibenzylidene sorbitol in consideration of odor and the like. The content of the intermediate layer (B) is 0.1 to
It is 0.5% by weight, preferably 0.15 to 0.5% by weight. If the content is less than 0.1% by weight, the whitening-preventing effect of the nucleating agent is reduced, and the effect remains unchanged even if 0.5% by weight or more is added.
【0016】外層(C)は、中間層(B)に使用した造
核剤のブリードアウトを防止する役割を有する層であっ
て、中間層と同程度の耐熱性と耐衝撃性を有するポリエ
チレン系樹脂から形成される。特に、中間層(B)との
接着性を考慮した場合中間層(B)と同種のポリマーと
するのが好ましい。したがって、最も好ましいポリエチ
レン系樹脂は密度が0.935g/cm3 以上、好ましくは
0.940〜0.945g/cm3 の直鎖状低密度ポリエチ
レンもしくは高密度ポリエチレンである。The outer layer (C) is a layer having a role of preventing bleed-out of the nucleating agent used for the intermediate layer (B), and is a polyethylene type having the same heat resistance and impact resistance as the intermediate layer. Formed from resin. Particularly, in consideration of the adhesiveness with the intermediate layer (B), it is preferable to use the same kind of polymer as the intermediate layer (B). Thus, the most preferred polyethylene resin density of 0.935 g / cm 3 or more, preferably linear low density polyethylene or high density polyethylene 0.940~0.945g / cm 3.
【0017】本発明のラミネート用多層シーラントフィ
ルム1は上述した樹脂構成とするのであるが、製膜性を
考慮した場合、更に各層の樹脂のメルトフローレートを
内層(A):MFRi、中間層(B):MFRm、外層
(C):MFRoとした場合、MFRo/MFRmが
0.1以上、好ましくは0.5以上、MFRi/MFR
mが0.1以上好ましくは0.5以上となるよう選定す
るのが望ましい。MFRo/MFRmあるいはMFRi
/MFRmが0.1未満の場合は厚み構成比によっても
異なるが、製膜時に外層(C)と中間層(B)あるいは
内層(A)と中間層(B)との間に流れむらが生じて、
均一な層厚みのフィルムが得られず、極端な場合は製膜
困難となるので好ましくない。The multilayer sealant film 1 for laminating according to the present invention has the above-mentioned resin constitution. However, in consideration of film forming properties, the melt flow rate of the resin of each layer is further determined by the inner layer (A): MFRi, the intermediate layer ( B): MFRm and outer layer (C): MFRo, MFRo / MFRm is 0.1 or more, preferably 0.5 or more, MFRi / MFR
It is desirable to select so that m is 0.1 or more, preferably 0.5 or more. MFRo / MFRm or MFRi
When / MFRm is less than 0.1, flow unevenness occurs between the outer layer (C) and the intermediate layer (B) or between the inner layer (A) and the intermediate layer (B), although it varies depending on the thickness composition ratio. hand,
A film having a uniform layer thickness cannot be obtained, and in an extreme case, film formation becomes difficult, which is not preferable.
【0018】また、本発明のラミネート用多層シーラン
トフィルム1の中間層(B)には前述したように造核剤
が添加されているので、この中間層(B)の全体厚みに
占める割合を大きくすることが全体の白化防止につなが
る。したがって、中間層(B)の厚みを全体厚みの40
〜90%、特に60〜90%とすることが好ましい。な
お、造核剤を各層に添加して白化防止効果を大きくする
ことも可能であるが、製膜時に造核剤がフィルム表面に
ブリードアウトして商品価値を損なうため好ましくな
い。Further, since the nucleating agent is added to the intermediate layer (B) of the multilayer sealant film 1 for laminating of the present invention as described above, the ratio of the intermediate layer (B) to the total thickness is large. Doing so will prevent whitening as a whole. Therefore, the thickness of the intermediate layer (B) is set to 40% of the total thickness.
˜90%, particularly preferably 60 to 90%. It is possible to add a nucleating agent to each layer to enhance the whitening prevention effect, but it is not preferable because the nucleating agent bleeds out on the surface of the film during the film formation to impair the commercial value.
【0019】本発明のラミネート用多層シーラントフィ
ルム1の成形方法については特に制限はなく、通常の多
層インフレーション法、キャスト法が用いられ、本発明
の目的を損なわない範囲で、滑剤、酸化防止剤等の通常
ポリオレフィン系フィルムに使用される添加剤を添加し
ても良い。The method for molding the multilayer sealant film 1 for laminating of the present invention is not particularly limited, and a conventional multilayer inflation method or casting method is used, and a lubricant, an antioxidant, etc. are used within a range not impairing the object of the present invention. You may add the additive normally used for the polyolefin film of.
【0020】[0020]
【作用】本発明によれば、ラミネート用多層シーラント
フィルムの全体厚みの大部分を占める中間層に造核剤が
添加されているので、フィルム成形時に結晶が微細化し
て透明性が向上するのと同様に、レトルト処理において
もポリオレフィン系樹脂の一部分に再結晶化が起こり、
その際造核剤により結晶が微細化されるため白化防止効
果が得られるものと考えられる。また、外層と内層には
造核剤を添加していないのでフイルム成形時の造核剤の
ブリードアウトを防止することも可能となった。また、
シール面となる内層には融点の高い高密度ポリエチレン
と柔軟性とシール性に優れた軟質ポリマーがそれぞれ相
乗効果を発揮し、更にアンチブロッキング剤の効果によ
って熱融着の防止とヒートシール性の向上という二律背
反する作用を付与することが可能となった。According to the present invention, since the nucleating agent is added to the intermediate layer which occupies most of the whole thickness of the multilayer sealant film for laminating, the crystal is made finer during the film forming and the transparency is improved. Similarly, in the retort treatment, recrystallization occurs in a part of the polyolefin resin,
At that time, the crystals are refined by the nucleating agent, and thus it is considered that the whitening preventing effect can be obtained. Further, since no nucleating agent is added to the outer layer and the inner layer, it is possible to prevent bleed-out of the nucleating agent during film forming. Also,
High density polyethylene with a high melting point and soft polymer with excellent flexibility and sealability exert synergistic effects on the inner layer that forms the sealing surface. Furthermore, the effect of an antiblocking agent prevents heat fusion and improves heat sealability. It has become possible to add the opposite effect.
【0021】[0021]
【実施例】以下の実施例にて、本発明を更に詳しく説明
するが、本発明はその要旨を越えない限り、これらの例
に何等制約されるものではない。The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples as long as the gist thereof is not exceeded.
【0022】以下の実施例および比較例における評価方
法を説明する。 <レトルト後外観>ラミネートフィルムから製造された
袋に内容物を充填せずに真空密封して得られたサンプル
(14cm×20cm)を、120℃で30分間レトルト処
理を行い、以下評価を行った。 1)白 化 フィルムの透明性の悪化(白化状態)を目視にて評価を
行った。 評価基準 ○:白化現象無し。 △:僅かに白化現象あり。 ×:白化現象有り。 2)耐融着性 内面融着の有無で評価を行った。 評価基準 ○:融着無し。 ×:融着有り。 3)変 形 フィルムの変形(皺、歪み等)の有無で評価を行った。 評価基準 ○:変形無し ×:変形有り <耐衝撃性>ラミネートフィルムから製造された袋に飽
和食塩水800ccを充填密封して得られたサンプル(2
0cm×25cm)を120℃で30分間レトルト処理を行
った後、−10℃雰囲気下で3.4kgの重りを22cmの
高さから落下させ各サンプルが破袋するまでの平均落下
回数を求めた。Evaluation methods in the following examples and comparative examples will be described. <Appearance after retort> A sample (14 cm x 20 cm) obtained by vacuum-sealing a bag made of a laminate film without filling the contents was subjected to retort treatment at 120 ° C for 30 minutes and evaluated as follows. . 1) Whitening The deterioration of the transparency of the film (whitening state) was visually evaluated. Evaluation criteria ○: No whitening phenomenon. Δ: There is a slight whitening phenomenon. X: There is a whitening phenomenon. 2) Fusion resistance The evaluation was made by the presence or absence of internal fusion. Evaluation criteria ○: No fusion. X: There is fusion. 3) Deformation The film was evaluated for the presence of deformation (wrinkles, distortion, etc.). Evaluation Criteria ◯: No deformation X: Deformation <Impact resistance> Sample (2) obtained by filling and sealing a bag made of a laminated film with 800 cc of saturated saline solution
(0 cm × 25 cm) was subjected to retort treatment at 120 ° C. for 30 minutes, then a 3.4 kg weight was dropped from a height of 22 cm in an atmosphere of −10 ° C., and the average number of drops until each sample was broken was calculated. .
【0023】なお、本発明の実施例および比較例で使用
する原材料は以下の記号で示した。 LL :直鎖状低密度ポリエチレン(メルトフローレート
2.0g/10min、密度0.940g/cm3) HD :高密度ポリエチレン(メルトフローレート1.0
g/10min、密度0.954g/cm3) EPR :エチレン・プロピレン共重合体(メルトフローレ
ート2.9g/10min、密度0.870g/cm3) DBS :造核剤(ジベンジリデンソルビトール) ABA :アンチブロッキング剤(シリカ) PP1 :プロピレン・エチレンランダム共重合体 PP2 :プロピレン・エチレンブロック共重合体Raw materials used in Examples and Comparative Examples of the present invention are indicated by the following symbols. LL: Linear low-density polyethylene (melt flow rate 2.0 g / 10 min, density 0.940 g / cm 3 ) HD: High-density polyethylene (melt flow rate 1.0
g / 10min, density 0.954g / cm 3) EPR: ethylene-propylene copolymer (melt flow rate 2.9 g / 10min, density 0.870g / cm 3) DBS: nucleating agent (dibenzylidene sorbitol) ABA: Anti-blocking agent (silica) PP1: Propylene / ethylene random copolymer PP2: Propylene / ethylene block copolymer
【0024】実施例1、2および比較例1、2 表1に示す樹脂組成物をダイス径300mm、ダイスリッ
プクリアランス3.0mmの多層ダイスを備えたインフレ
ーション多層成形機にて加工温度200℃、ブローアッ
プレシオ1.7で厚み60μのラミネート用多層シーラ
ントフィルムを得、表面張力が約48dyne/cm となる様
にラミネート時に接着面となる面(外層側)にコロナ放
電処理を施した。次いで、このシーラントフィルムを厚
み15μの2軸延伸ポリアミドフィルムとエステル系接
着剤を用いてドライラミネート加工後、40℃雰囲気下
で2日間エージングを行うことによりラミネートフィル
ムを得た。評価結果を表1に示す。Examples 1 and 2 and Comparative Examples 1 and 2 The resin compositions shown in Table 1 were blown with an inflation multilayer molding machine equipped with a multilayer die having a die diameter of 300 mm and a die slip clearance of 3.0 mm at a processing temperature of 200 ° C. A multilayer sealant film for lamination having an up ratio of 1.7 and a thickness of 60 μm was obtained, and the surface (outer layer side) to be the adhesive surface during lamination was subjected to corona discharge treatment so that the surface tension was about 48 dyne / cm. Then, this sealant film was dry laminated using a biaxially stretched polyamide film having a thickness of 15 μm and an ester adhesive, and then aged for 2 days at 40 ° C. to obtain a laminated film. Table 1 shows the evaluation results.
【0025】比較例3 プロピレン・エチレンランダム共重合体を主成分とする
厚み60μの無延伸ポリプロピレンシーラントフィルム
を実施例1と同様の方法でドライラミネート加工を行
い、ラミネートフィルムを得た。評価結果を表1に示
す。Comparative Example 3 A non-stretched polypropylene sealant film having a thickness of 60 μ and containing propylene / ethylene random copolymer as a main component was dry laminated in the same manner as in Example 1 to obtain a laminated film. Table 1 shows the evaluation results.
【0026】比較例4 プロピレン・エチレンブロック共重合体を主成分とする
厚み60μの無延伸ポリプロピレンシーラントフィルム
を実施例1と同様の方法でドライラミネート加工を行
い、ラミネートフィルムを得た。評価結果を表1に示
す。Comparative Example 4 An unstretched polypropylene sealant film having a thickness of 60 μm and containing a propylene / ethylene block copolymer as a main component was dry laminated in the same manner as in Example 1 to obtain a laminated film. Table 1 shows the evaluation results.
【0027】[0027]
【表1】 [Table 1]
【0028】表1の結果から、レトルト食品包装用ラミ
ネートフィルムのシーラント層に従来から使用されてい
るポリプロピレン系樹脂を使用した場合(比較例3、
4)は耐衝撃性が悪い。また、造核剤及びアンチブロッ
キング剤を添加していない場合(比較例1)はレトルト
後の白化現象及び融着現象が認められ、内層に軟質ポリ
マーであるエチレン・α−オレフィン共重合体を添加し
ていない場合(比較例2)は十分な耐衝撃性が得られな
いことが分かる。また、造核剤を含有している中間層
(B)の構成厚みが60%以上(実施例1)にした場
合、構成厚みが43%(実施例2)のものよりも白化防
止効果が大きいことが分かる。From the results shown in Table 1, the case where a polypropylene resin conventionally used is used for the sealant layer of the laminated film for packaging retort foods (Comparative Example 3,
4) has poor impact resistance. Further, when the nucleating agent and the anti-blocking agent were not added (Comparative Example 1), the whitening phenomenon and the fusion phenomenon after the retort were observed, and the soft polymer ethylene / α-olefin copolymer was added to the inner layer. It can be seen that when not performed (Comparative Example 2), sufficient impact resistance cannot be obtained. Further, when the constituent thickness of the intermediate layer (B) containing the nucleating agent is 60% or more (Example 1), the whitening prevention effect is larger than that of the constituent thickness of 43% (Example 2). I understand.
【0029】[0029]
【発明の効果】以上説明したように、本発明のラミネー
ト用多層シーラントフィルムを用いることにより、耐衝
撃性、耐熱融着性、シール性および透明性に優れた、即
ち、従来の技術の問題点をカバーしたレトルト食品包装
用ラミネートフィルムを得ることが可能であり、120
℃までのレトルト食品包装用として好適に使用すること
ができる。As described above, by using the multi-layer sealant film for laminating of the present invention, it is possible to obtain excellent impact resistance, heat fusion resistance, sealability and transparency, that is, the problems of the prior art. It is possible to obtain a laminated film for retort food packaging covering
It can be suitably used for packaging retort foods up to ℃.
【図1】本発明のラミネート用多層シーラントフィルム
を説明する断面図である。FIG. 1 is a cross-sectional view illustrating a multilayer sealant film for lamination according to the present invention.
1 ラミネート用多層シーラントフィルム A 内層 B 中間層 C 外層 1 Multilayer sealant film for lamination A Inner layer B Middle layer C Outer layer
Claims (6)
脂からなる三層構成のラミネート用多層シーラントフィ
ルムにおいて、 (A)内層がアンチブロッキング剤を0.4〜5重量%
含有した、密度が0.945g/cm3 以上の高密度ポリエ
チレンと軟質ポリマーの樹脂組成物からなり、該軟質ポ
リマーの含有量が5〜30重量%であり、 (B)中間層が造核剤を0.1〜0.5重量%含有した
密度が0.935g/cm3 以上の直鎖状低密度ポリエチレ
ンを主成分とする樹脂組成物からなり、 (C)外層が中間層と同程度の耐熱性と耐衝撃性を有す
るポリエチレン系樹脂からなるラミネート用多層シーラ
ントフィルム。1. A multi-layer sealant film for laminating having a three-layer structure comprising a polyethylene-based resin having an inner layer side as a sealing surface, wherein (A) the inner layer contains an anti-blocking agent in an amount of 0.4 to 5% by weight.
The resin composition comprises a high-density polyethylene having a density of 0.945 g / cm 3 or more and a soft polymer, the content of the soft polymer is 5 to 30% by weight, and (B) the intermediate layer is a nucleating agent. Of 0.1% to 0.5% by weight of a linear low density polyethylene having a density of 0.935 g / cm 3 or more as a main component, and (C) the outer layer has the same degree as that of the intermediate layer. Multilayer sealant film for lamination made of polyethylene resin having heat resistance and impact resistance.
ある請求項1記載のラミネート用多層シーラントフィル
ム。2. The multilayer sealant film for laminating according to claim 1, wherein the thickness of the intermediate layer is 40 to 90% of the total thickness.
ある請求項1記載のラミネート用多層シーラントフィル
ム。3. The multilayer sealant film for laminating according to claim 1, wherein the thickness of the intermediate layer is 60 to 90% of the total thickness.
が0.935g/cm3以上の直鎖状低密度ポリエチレン又
は高密度ポリエチレンである請求項1記載のラミネート
用多層シーラントフィルム。4. The multilayer sealant film for laminating according to claim 1, wherein the polyethylene resin used in the outer layer is a linear low density polyethylene or a high density polyethylene having a density of 0.935 g / cm 3 or more.
下のエチレンとα−オレフィンの共重合体である請求項
1記載のラミネート用多層シーラントフィルム。5. The multilayer sealant film for laminating according to claim 1, wherein the soft polymer is a copolymer of ethylene and α-olefin having a density of 0.900 g / cm 3 or less.
置換体である請求項1記載のラミネート用多層シーラン
トフィルム。6. The multilayer sealant film for laminating according to claim 1, wherein the nucleating agent is a sorbitol-based derivative or a nucleus substitution product thereof.