JPH08229632A - Method for coating copper alloy casting mold - Google Patents
Method for coating copper alloy casting moldInfo
- Publication number
- JPH08229632A JPH08229632A JP6185795A JP6185795A JPH08229632A JP H08229632 A JPH08229632 A JP H08229632A JP 6185795 A JP6185795 A JP 6185795A JP 6185795 A JP6185795 A JP 6185795A JP H08229632 A JPH08229632 A JP H08229632A
- Authority
- JP
- Japan
- Prior art keywords
- mold
- copper alloy
- cavity surfaces
- mold coat
- coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】この発明は銅合金鋳型の塗型方法
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for coating a copper alloy mold.
【0002】[0002]
【従来の技術】従来、銅合金鋳型のキャビティ面に塗型
剤を塗布する場合には、鋳型を加熱した後、直ちに塗布
していた。2. Description of the Related Art Conventionally, when a mold coating agent is applied to the cavity surface of a copper alloy mold, it is applied immediately after heating the mold.
【0003】[0003]
【発明が解決しようとする課題】しかしながら、かかる
従来の方法にあっては、加熱によってキャビティ面に酸
化膜が形成されるため、塗型剤の密着性が悪く、この結
果、鋳造の際に塗型落ちが発生しやすいという不都合を
有した。However, in such a conventional method, since an oxide film is formed on the cavity surface by heating, the adhesiveness of the mold coating agent is poor, and as a result, the coating agent is not coated during casting. It had the inconvenience that the mold was easily dropped.
【0004】この発明の課題は、かかる不都合を解消す
ることである。An object of the present invention is to eliminate such inconvenience.
【0005】[0005]
【課題を解決するための手段】前記課題を達成するため
に、この発明に係る銅合金鋳型の塗型方法においては、
銅合金鋳型の少なくともキャビティ面を加熱した後、こ
のキャビティ面に生じた酸化物を除去し、その直後に前
記キャビティ面に塗型剤を塗布するものである。In order to achieve the above object, in the method of coating a copper alloy mold according to the present invention,
After heating at least the cavity surface of the copper alloy mold, the oxide generated on the cavity surface is removed, and immediately after that, a mold coating agent is applied to the cavity surface.
【0006】[0006]
【作用】この発明に係る銅合金鋳型の塗型方法は上記の
ように構成されているため、塗型膜とキャビティ面との
間に酸化膜は存在せず、この結果、塗型膜のキャビティ
面への密着性は良いものである。Since the copper alloy mold coating method according to the present invention is configured as described above, there is no oxide film between the mold coating film and the cavity surface. Adhesion to the surface is good.
【0007】[0007]
【実施例】図1は車両用ホイールの低圧鋳造用鋳型装置
の断面図、図2は図1におけるII部の拡大図である。DESCRIPTION OF THE PREFERRED EMBODIMENTS FIG. 1 is a cross-sectional view of a low pressure casting mold apparatus for a vehicle wheel, and FIG. 2 is an enlarged view of a portion II in FIG.
【0008】図1において、10はこの鋳造装置Dにおい
て車両用ホイ−ルを形成するための鋳型セットである。
この鋳型セット10は銅合金によって形成された鋳型の組
み合わせであり、下型20と一対の横型30,30 と上型40と
の組み合わせである。50はキャビティであり、前記鋳型
セット10によって形成されている。このキャビティ50は
車両用ホイ−ル状をしており、ディスク形成部51とスポ
−ク形成部52とリム形成部53とから構成される。21は下
型20の入子であり、ディスク部(車両用ホイ−ルの)の
表面を形成するためのものである。また、41は上型40の
補助型であり、411 はこの補助型の入子であり、各々デ
ィスク部(車両用ホイ−ルの)の裏面を形成するための
ものである。In FIG. 1, reference numeral 10 denotes a mold set for forming a vehicle wheel in this casting apparatus D.
The mold set 10 is a combination of molds made of a copper alloy, and is a combination of a lower mold 20, a pair of horizontal molds 30 and 30, and an upper mold 40. 50 is a cavity, which is formed by the mold set 10. The cavity 50 has a vehicle wheel shape and is composed of a disk forming portion 51, a spoke forming portion 52, and a rim forming portion 53. Reference numeral 21 is a nest of the lower mold 20, which is for forming the surface of the disk portion (of the vehicle wheel). Further, 41 is an auxiliary mold of the upper mold 40, and 411 is a nest of this auxiliary mold, which is for forming the back surface of the disk portion (of the vehicle wheel), respectively.
【0009】211 は堰であり、前記入子(下型20の)21
の略中心部に形成されている。70は溶湯補給管であり、
前記堰211 につながれ、下方に延びている。この溶湯補
給管70を介して溶湯保持炉(図示せず)の溶湯が低圧鋳
造によって前記キャビティ50に充填される。Reference numeral 211 denotes a weir, and the nest 21 (of the lower mold 20) 21
Is formed substantially at the center. 70 is a molten metal supply pipe,
It is connected to the weir 211 and extends downward. The molten metal of a molten metal holding furnace (not shown) is filled in the cavity 50 by low pressure casting through the molten metal supply pipe 70.
【0010】次に、この鋳型における塗型剤の塗布方法
を、横型30を例にして図2に基づき説明する。Next, the method of applying the mold coating agent in this mold will be described with reference to FIG.
【0011】横型30を組み合わせる前に、 200〜 250°
Cに加熱する。その後、キャビティ面50に発生した酸化
膜をサンドブラスト、ワイヤーブラシ等によって除去す
る。酸化膜を除去した後、キャビティ50面に塗型剤Mを
0.05〜0.3mm の厚さに塗布する。なお、塗型剤の例とし
ては、カオリン50%,水45%,珪酸ソーダ5%からなる
断熱用塗型剤、タルク15%,水84%,珪酸ソーダ1%か
らなる断熱用塗型剤が挙げられる。Before assembling the horizontal type 30, 200 to 250 °
Heat to C. Then, the oxide film generated on the cavity surface 50 is removed by sandblasting, a wire brush or the like. After removing the oxide film, a coating agent M is applied to the surface of the cavity 50.
Apply to a thickness of 0.05 to 0.3 mm. In addition, as an example of the coating agent, a heat insulating coating agent made of kaolin 50%, water 45%, sodium silicate 5%, a heat insulating coating agent made of talc 15%, water 84%, sodium silicate 1%. Can be mentioned.
【0012】[0012]
【発明の効果】この発明に係る銅合金鋳型の塗型方法
は、銅合金鋳型の少なくともキャビティ面を加熱した
後、このキャビティ面に生じた酸化物を除去し、その直
後に前記キャビティ面に塗型剤を塗布するものであるた
め、塗型膜とキャビティ面との間に酸化膜は存在せず、
この結果、塗型膜のキャビティ面への密着性は良いもの
である。EFFECTS OF THE INVENTION The method of coating a copper alloy mold according to the present invention comprises heating at least the cavity surface of the copper alloy mold, removing oxides generated on the cavity surface, and immediately after that, coating the cavity surface. Since a mold agent is applied, there is no oxide film between the mold coating film and the cavity surface,
As a result, the adhesiveness of the mold coating film to the cavity surface is good.
【0013】よって、この銅合金鋳型の塗型方法を使用
すれば、銅合金鋳型を用いた鋳造の際に、当該鋳型が溶
湯によって加熱されても、塗型落ちが無く、適正な鋳造
を行うことができる。Therefore, by using this copper alloy mold casting method, when casting using a copper alloy mold, even if the mold is heated by the molten metal, there is no mold drop-off and proper casting is performed. be able to.
【図1】車両用ホイールの低圧鋳造用鋳型装置の断面図
である。FIG. 1 is a cross-sectional view of a low pressure casting mold device for a vehicle wheel.
【図2】図1におけるII部の拡大図である。FIG. 2 is an enlarged view of a II portion in FIG.
20 … 下型(銅合金鋳型) 21 … 入子(銅合金鋳型) 30 … 横型(銅合金鋳型) 40 … 上型(銅合金鋳型) 41 … 補助型(銅合金鋳型) 411 … 入子(銅合金鋳型) 50 … キャビティ 20… Lower mold (copper alloy mold) 21… Nesting (copper alloy mold) 30… Horizontal mold (copper alloy mold) 40… Upper mold (copper alloy mold) 41… Auxiliary mold (copper alloy mold) 411… Nesting (copper) Alloy mold) 50… Cavity
Claims (1)
加熱した後、このキャビティ面に生じた酸化物を除去
し、その直後に前記キャビティ面に塗型剤を塗布するこ
とを特徴とする銅合金鋳型の塗型方法。1. A copper alloy mold characterized by heating at least a cavity surface of the copper alloy mold, removing oxides generated on the cavity surface, and immediately thereafter applying a mold coating agent to the cavity surface. Coating method.