JPH08225793A - 潤滑添加剤およびそれを含む潤滑グリース組成物 - Google Patents

潤滑添加剤およびそれを含む潤滑グリース組成物

Info

Publication number
JPH08225793A
JPH08225793A JP7302005A JP30200595A JPH08225793A JP H08225793 A JPH08225793 A JP H08225793A JP 7302005 A JP7302005 A JP 7302005A JP 30200595 A JP30200595 A JP 30200595A JP H08225793 A JPH08225793 A JP H08225793A
Authority
JP
Japan
Prior art keywords
borate
lubricating
carbon atoms
acid
grease
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP7302005A
Other languages
English (en)
Inventor
Yoshihisa Hachitsuka
嘉久 八塚
Masaru Murata
勝 村田
Tetsuo Tsuchiya
哲夫 土谷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Showa Shell Sekiyu KK
Original Assignee
Showa Shell Sekiyu KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Showa Shell Sekiyu KK filed Critical Showa Shell Sekiyu KK
Priority to JP7302005A priority Critical patent/JPH08225793A/ja
Priority to US08/575,224 priority patent/US5877129A/en
Priority to AU40633/95A priority patent/AU705469B2/en
Priority to BR9505986A priority patent/BR9505986A/pt
Priority to CA002165885A priority patent/CA2165885A1/en
Priority to KR1019950053303A priority patent/KR960022967A/ko
Priority to DE69520415T priority patent/DE69520415T2/de
Priority to EP95120425A priority patent/EP0718394B1/en
Priority to ES95120425T priority patent/ES2157286T3/es
Priority to CN95119492A priority patent/CN1050859C/zh
Publication of JPH08225793A publication Critical patent/JPH08225793A/ja
Priority to HK98113417A priority patent/HK1012409A1/xx
Pending legal-status Critical Current

Abstract

(57)【要約】 【目的】 新規なほう酸塩分散体よりなる潤滑添加剤、
とくに１３０℃以上の高温におけるグリースの使用条件
下でグリースに高い滴点を与えることができ、それ自体
が酸化防止能を有する新規なほう酸塩分散体よりなる潤
滑添加剤およびそれを含む潤滑グリース組成物の提供。 【構成】 サルチル酸類のアルカリ土類金属塩と、
アルケニルスクシンイミドとの混合物中に、ほう酸の
アルカリ金属塩を分散させたものであることを特徴とす
るほう酸塩分散体よりなる潤滑添加剤。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、潤滑添加剤およびそれ
を含む潤滑グリース組成物に関する。
【０００２】
【従来技術】従来リチウム石けんグリースは、耐熱性、
耐水性が比較的安定であり、またリチウム石けんの多く
は潤滑基剤に対する分散が容易で、価格的にも安価であ
る等の利点によって、広く用いられてきた。しかし、リ
チウム石けんグリースの場合、使用環境条件が１３０℃
以上の高温になると、熱によるミセルの破壊、付着力の
減少、軟化するなどグリースとしての特性が低下し、潤
滑作用が急速に低下する欠点がある。
【０００３】これらの欠点を補う耐熱性グリースとし
て、滴点が極めて高い非石けん基グリースや各種コンプ
ッレクス石けんグリースなどが開発されているが、長期
間の使用で増ちょう剤が硬化したり、極度に軟化したり
する等欠点がある。しかも極めて高価であるなど、用途
が自ずから限定されている。
【０００４】近年、グリースの使用環境は機械装置の小
型化や作動部の高速化に伴い厳しくなりつつある。例え
ば自動車などの電装部品用軸受のように、エンジンの熱
源を近くにひかえた部位で使用する場合、その軸受を潤
滑するグリースは特に高い温度条件に長時間さらされ
る。また前輪駆動車や四輪駆動車に多く見られる等速ジ
ョイント（ＣＶＪ）は、自動車の高出力、高速化やＣＶ
Ｊ自体の軽量化等により厳しい潤滑条件にさらされる。
こうした場合グリースは十分な耐熱性、耐久性を備えて
いる必要がある。
【０００５】さらに電化製品においては、エアーコンデ
ィショナーや換気扇などの小型モーターや、各種オーデ
ィオ部品等に使用される小型軸受の低振動、低騒音化が
要求され、潤滑性に優れかつ軸受音響特性の良い（騒音
を発生しない）グリースが必要となっている。
【０００６】一方、工業の発展に伴い各種産業機械は高
性能でコンパクト化し、より高荷重で過酷な条件で運転
されるようになり、それに耐え得る潤滑グリースを必要
としている。現在耐荷重性グリースとしては、高荷重の
条件を満たすために多量の極圧添加剤を添加している。
しかし極圧添加剤は、選択によっては環境を汚染したり
腐食を伴ったりする欠点を持っている。例えば、良好な
極圧性を有する添加剤のうちで、カドミウム、アンチモ
ン等を含むものは毒物として使用できなくなっている。
また塩素系の添加剤は腐食という点で、特に１００℃以
上で鉄、鋼等に対する悪影響が大きい。
【０００７】また、グリースの耐荷重性を向上するため
の他の添加剤として、特開昭５１−３３２６３号、Ｕ．
Ｓ．Ｐ．３，９９７，４５４号、特開昭５３−１１５７
０４号、特開昭５３−１１５７０５号、Ｕ．Ｓ．Ｐ．
４，１００，０８０号、特開昭５９−１０９５９５号な
どにより、ほう酸塩の使用が提案されている。このなか
でも、ＵＳＰ３，９９７，４５４号のほう酸塩分散体を
用いたグリースは優れたものではあるが、このほう酸塩
分散体は、スルホン酸アルカリ金属塩またはアルカリ土
類金属塩とアルケニルスクシンイミドとの混合物中にほ
う酸塩を分散させたものであり、このほう酸塩分散体そ
れ自体には酸化防止能力はもっていない。
【０００８】
【発明が解決しようとする課題】本発明の目的は、新規
なほう酸塩分散体よりなる潤滑添加剤、とくに１３０℃
以上の高温におけるグリースの使用条件下でグリースに
高い滴点を与えることができ、それ自体が酸化防止能を
有する新規なほう酸塩分散体よりなる潤滑添加剤および
それを含む潤滑グリース組成物を提供する点にある。
【０００９】
【課題を解決するための手段】本発明の第一は、サル
チル酸類のアルカリ土類金属塩と、アルケニルスクシ
ンイミドとの混合物中に、ほう酸のアルカリ金属塩を
分散させたものであることを特徴とするほう酸塩分散体
よりなる潤滑添加剤に関する。
【００１０】本発明の第二は、基油中に、（ａ）増ちょ
う剤および（ｂ）前記特定のほう酸塩分散体よりなる潤
滑添加剤を含有させたことを特徴とする潤滑グリース組
成物に関する。
【００１１】前記ほう酸塩分散体の潤滑油への使用量
は、全量に対し、０．０１〜２０重量％である。
【００１２】増ちょう剤としては、リチウム石鹸、ナト
リウム石鹸、カルシウム石鹸、バリウム石鹸、アルミニ
ウム石鹸、ウレア類、ベントン、クレーなどを使用する
ことができる。
【００１３】とくにリチウム石鹸としては、 炭素数１２〜２４のヒドロキシ脂肪酸のリチウム塩お
よび、 炭素数１２〜２４のヒドロキシ脂肪酸のリチウム塩と
炭素数１２〜２４の脂肪酸のリチウム塩との混合物 よりなる群から選ばれたものが好適であり、その使用量
は、通常全グリース量に対して２〜３０重量％である。
【００１４】とくに、前記ヒドロキシ脂肪酸のリチウム
塩を用いた本発明の潤滑グリース組成物は、基油中にサ
ルチル酸類のアルカリ土類金属塩とアルケニルスクシン
イミドよりなる分散剤中に、ほう酸塩が均一に分散した
微細なほう酸塩分散体と前記ヒドロキシ脂肪酸のリチウ
ム塩との相乗効果により従来のリチウム系グリースに較
べて高滴点（２３０℃以上、好ましくは２５０℃以上）
を有し、かつ耐荷重性、良好な音響特性等を有する。
【００１５】本発明の組成物に使用される基油は、従来
から潤滑油に使用されている、鉱油あるいは合成炭化水
素、合成エスエル油等の合成油のいずれかまたはこれら
の混合物である。これらは一般には４０℃で２〜５００
ｍｍ2／ｓ、好ましくは２０〜２００ｍｍ2／ｓの範囲内
の粘度を有することができる。
【００１６】合成油としては、例えば、４０℃の粘度が
４１．０ｍｍ2／ｓ、粘度指数１３０、流動点−６０
℃、引火点２２３℃のオクテン−１／デセン−１共重合
体のようなポリα−オレフィンオリゴマー；ジ−２−エ
チルヘキシルセバケートのようなジカルボン酸エステ
ル；トリメチロールプロパンカプリル酸エステルやペン
タエリスリトールカプロン酸エステルのようなヒンダー
ドエステル油を使用することができる。さらにポリグリ
コール油、シリコーン油、ポリフェニルエーテル油、ハ
ロゲン化炭化水素油、アルキルベンゼン油等の各種の合
成油も使用することができる。
【００１７】前記炭素数１２〜２４のヒドロキシ脂肪酸
は分子中にヒドロキシル基を有する通常は直鎖状の飽和
または不飽和の脂肪酸モノカルボン酸であり、具体的に
はたとえばリシノール酸、２−ヒドロキシドデカン酸、
２−ヒドロキシテトラデカン酸、２−ヒドロキシヘキサ
デカン酸、アンブレトリック酸、リシノール酸、リシノ
ステアロリック酸、９−ヒドロキシステアリン酸、１０
−ヒドロキシステアリン酸、１２−ヒドロキシステアリ
ン酸等が挙げられる。これらは単一化合物の形でも混合
物の形でも使用できる。
【００１８】前記炭素数１２〜２４の脂肪酸は飽和また
は不飽和の脂肪酸モノカルボン酸であり、具体的にはた
とえばラウリン酸、ミリスチン酸、パルミチン酸、ステ
アリン酸、リノール酸、リノレイン酸、ベヘニン酸等が
挙げられる。これらは単一化合物の形でも混合物の形で
も使用できる。
【００１９】これらヒドロキシ脂肪酸及び脂肪酸の中で
も炭素原子数が１８個のもの及びヒドロキシル基が９
−、１０−もしくは１２−に結合しているもの、とりわ
け１２−ヒドロキシステアリン酸が好適である。
【００２０】前記のヒドロキシ脂肪酸あるいは脂肪酸か
らそのリチウム塩を形成するに際しては、該ヒドロキシ
脂肪酸あるいは該脂肪酸は遊離酸の形のみならずグリセ
リドの形で水酸化リチウムと反応させることもできる。
【００２１】前記ほう酸のアルカリ金属塩におけるアル
カリ金属としては、カリウムやナトリウムが好ましく、
とりわけカリウムが最も好ましい。
【００２２】前記ほう酸塩化合物はメタほう酸塩、三ほ
う酸塩、四ほう酸塩および五ほう酸塩のように多くの異
なる形態を有する。本明細書中の用語「ほう酸塩化合
物」は、これら形態のすべてのほう酸塩を含有する。
【００２３】とくに好ましいほう酸塩は、下記式
【化３】Ｋ2Ｏ・ｘＢ2Ｏ3 または下記式
【化４】Ｋ2Ｏ・ｘＢ2Ｏ3・ｙＨ2Ｏ （上記中、ｘは２〜５好ましくは２．５〜４．５更に好
ましくは２．５〜３．５とくに３．０の正数であり、そ
してｙは１〜９好ましくは２〜４．８更に好ましくは
２．８〜４．４の正数であり、ｘの数はほう素対カリウ
ム比すなわちカリウム１部当たりのほう素の部数を表わ
す。）で表されるものを挙げることができる。
【００２４】前記サルチル酸類のアルカリ土類金属塩
は、下記一般式
【化５】 （式中、Ｒ1はＣ8〜Ｃ22のアルキル基を表わし、Ｍはア
ルカリ土類金属、例えばＣａ、Ｂａ、Ｍｇなどを表わ
し、とくにＣａやＭｇのときは清浄機能が高い。）で表
わされ、アルキル置換サルチル酸のアルカリ土類金属塩
であることが好ましく、ほう酸塩の分散剤としての機能
のほか、潤滑基油の酸化防止効果やエンジン油中の劣化
物の堆積を予防または抑制してエンジン内部を清浄に保
つ機能を有し、清浄剤として作用する。またグリースへ
応用した場合、増粘助剤としても有効であり、さらに摩
擦低減効果にも寄与する。
【００２５】前記アルケニルスクシンイミドは、下記一
般式
【化６】 （式中、Ｒ2は炭素数３０〜２００のポリイソブテニル
基であり、Ｒ3は炭素数２〜１０、好ましくは２〜６の
アルキレン基であり、Ｒ4は水素または炭素数１〜６の
アルキル基であり、ｍは０ないし６、好ましくは０〜３
の整数であり、ｎは０ないし１の整数であり、０である
のが好ましい。）で表わされるものが好ましく、このも
のはアルケニルコハク酸または酸無水物とポリアミンと
の反応によって合成することができる。
【００２６】前記アルケニルスクシンイミドは、ほう酸
塩の分散剤として作用するほか、通常エンジン油中に発
生するスラッジを油中に分散させる効果を有する。
【００２７】前記ほう酸塩分散体の調製は、ほう酸と
アルカリ金属水酸化物例えば水酸化カリウムの水溶液お
よびサルチル酸類のアルカリ土類金属塩とアルケニル
スクシンイミドを添加した油媒体とを混合してなる水／
油型エマルジョンから水を取り除くことにより行うこと
ができる。
【００２８】ほう酸塩分散体における油性分散媒は、ど
んな潤滑粘性を示す液体であってもよく、反応条件下で
不活性（特に非けん化性）であり、低い誘電率を示す。
これらは一般には４０℃で２〜５００ｍｍ2／ｓ、好ま
しくは２０〜２００ｍｍ2／ｓの範囲内の粘度を有する
ことができる。
【００２９】分散剤として使用することのできるサルチ
ル酸類のアルカリ土類金属塩およびアルケニルスクシン
イミドの濃度は、ほう酸塩化合物の濃度に左右されて広
い範囲にわたって変化することができる。しかしながら
ほう酸塩化合物分散体において一般にサルチル酸類のア
ルカリ土類金属塩の濃度は０．１重量％以上で、通常は
０．１〜２５重量％、好ましくは１．０〜１０重量％の
範囲とすることができ、アルケニルスクシンイミドの濃
度は０．１重量％以上で、通常は０．１〜２５重量％、
好ましくは１．０％〜１０重量％の範囲とすることがで
きる。さらに、ほう酸塩分散体において、ほう酸塩の濃
度は５〜８０重量％まで広い範囲にわたって変化させる
ことができるが、３０〜６５重量％が好ましい。
【００３０】本発明によるほう酸塩化合物分散体は潤滑
グリースの添加剤として極めて有効であるほか、各種自
動車エンジン油、ギヤー油、さらには工業用潤滑油等に
も添加することが可能である。したがって、本発明にお
ける潤滑添加剤とは、これらのすべての用途を包含する
意味で使用しているものである。
【００３１】本発明のグリース組成物は、既知の技術に
よりリチウム石けんグリースを製造する際、冷却工程中
に先に記載のほう酸塩化合物分散体を添加、分散するこ
とによって得ることができる。好ましくは１２５℃以上
で添加するとグリース組成物の滴点が向上するので好ま
しい。
【００３２】本発明のグリース組成物は、通常グリース
組成物に使用される他の添加剤成分、例えば極圧剤、耐
摩耗剤、酸化防止剤、腐食防止剤、油性向上剤等を含有
することができる。
【００３３】
【実施例と比較例】以下に製造例、実施例、比較例を挙
げて本発明を説明するが、本発明はこれにより限定され
るものではない。
【００３４】製造例１（ほう酸塩分散体の製造） 純度８５％の水酸化カリウム５９．４ｇおよびオルトほ
う酸１６６．９ｇを水４００ｇに溶解する。前記〔化
２〕の一般式におけるＲ1がＣ14〜Ｃ18のアルキル基で
あるサルチル酸カルシウム１０．１ｇ、ポリイソブテニ
ルスクシンイミド（平均分子量約２０００）１５．５ｇ
を４０℃で粘度１００ｍｍ2／ｓの精製鉱油１１６．７
ｇへ添加した後、上記の溶液（水酸化カリウム、オルト
ほう酸）と混合してけん濁液を作った。これを加熱、撹
拌して約１００℃で水分を蒸発させ、最終的には内容物
を１２５℃まで加熱し、その後冷却して暗褐色液体のほ
う酸カリウム分散体を得た。
【００３５】比較例１ 加熱可能な小型開放釜（内容量２，０００ｇ）に４０℃
で粘度１００ｍｍ2／ｓの鉱油８６０ｇを入れ、これに
増ちょう剤として１２−ヒドロキシステアリン酸リチウ
ム１２０ｇを加えた。内容物を撹拌しながら２２０℃ま
で昇温した後、内容物を冷却し、３本ロールミル処理を
行い、通常音響特性が良好となる製造方法で基リチウム
石けんグリースを得た。
【００３６】実施例１ 比較例１のグリース製造中、冷却工程１３０℃で前記製
造例で得たほう酸カリウム分散体を２．０重量％添加し
た。その後、３本ロールミルにより処理を行い淡黄色の
グリースを得た。
【００３７】製造例２（ほう酸塩分散体の製造） 純度８５％の水酸化カリウム５９．４ｇおよびオルトほ
う酸１６６．９ｇを水４００ｇに溶解する。前記〔化
２〕の一般式におけるＲ1がＣ14〜Ｃ18のアルキル基で
あるサルチル酸カルシウム２９．７ｇ、ポリイソブテニ
ルスクシンイミド（平均分子量約２０００）２９．７ｇ
を４０℃で粘度１００ｍｍ2／ｓの精製鉱油８５．３ｇ
へ添加した後、上記の溶液（水酸化カリウム、オルトほ
う酸）と混合してけん濁液を作った。これを加熱、撹拌
して約１００℃で水分を蒸発させ、最終的には内容物を
１２５℃まで加熱し、その後冷却して暗褐色液体のほう
酸カリウム分散体を得た。
【００３８】比較例２ 加熱可能な小型開放釜（内容量２，０００ｇ）に４０℃
で粘度１５０ｍｍ2／ｓの鉱油８６０ｇを入れ、これに
増ちょう剤として１２−ヒドロキシステアリン酸リチウ
ム１２０ｇを加えた。内容物を撹拌しながら２２０℃ま
で昇温した後、内容物を冷却し、３本ロールミル処理を
行い、通常音響特性が良好となる製造方法で基リチウム
石けんグリースを得た。
【００３９】実施例２ 比較例２のグリース製造中、冷却工程１３０℃で前記製
造例で得たほう酸カリウム分散体を２．０重量％添加し
た。その後、３本ロールミルにより処理を行い淡黄色の
グリースを得た。
【００４０】前記実施例と比較例の対比効果は下記表１
のとおりである。耐熱性向上の指数ともいうべき滴点が
比較例１のグリースに較べて実施例１のグリースが約９
０℃も高くなった。今まではせいぜい２２０℃位まで上
げるのが限度と考えられていたから、２５０℃以上の滴
点はおどろくべきことである。しかも音響特性に関する
指数ともいうべき音響試験１２０秒値はほとんど変化が
なく、ほう酸塩の添加にもかかわらず、騒音がほとんど
大きくなっていないことを示している。
【００４１】
【表１】
【００４２】滴点は、ＡＳＴＭ Ｄ５６６−８７グリー
ス滴点試験によるものであって、規定カップにグリース
を充填し、加熱浴中で規定条件で加熱し、グリースがカ
ップの口から滴下したときの温度である。シェル四球極
圧試験の融着荷重（ｋｇｆ）は、ＡＳＴＭ Ｄ２５９６
−８７によるものであり、つぎの条件で測定したもので
ある。 回転数 ： １７７０ｒ．ｐ．ｍ 荷 重 ： ＡＳＴＭ Ｄ２５９６−８７の規格によ
るステップ荷重 温 度 ： 室温 時 間 ： １０秒 シェル四球摩耗試験の摩耗痕径（ｍｍ）は、ＡＳＴＭ
Ｄ２２６６−９１によるものであり、つぎの条件で測定
したものである。 回転数 ： １２００ｒ．ｐ．ｍ 荷 重 ： ４０ｋｇｆ 温 度 ： ７５℃ 時 間 ： １時間 音響試験（１２０秒値）は、特公昭５３−２３５７号公
報記載の方法に基づいた日本精工（株）製の音響試験機
ＮＳＫ ＧＲＥＡＳＥ ＮＯＩＳＥ ＴＥＳＴＥＲを用
いて各グリースについて軸受騒音計数値を測定したもの
である。
【００４３】本発明のグリースと市販グリースとは、音
響特性上、下記表２のとおり大きな差を有する。
【表２】 ちょう度の測定方法は、ＪＩＳ Ｋ２２２０ ５．３に
よる。なお、リチウムＥＰグリースは、極圧剤（ＳＰ系
添加剤）が添加されている。
【００４４】以下に本発明の実施態様項を列記する。 １．サルチル酸類のアルカリ土類金属塩と、アルケ
ニルスクシンイミドとの混合物中に、ほう酸のアルカ
リ金属塩を分散させたものであることを特徴とするほう
酸塩分散体よりなる潤滑添加剤。 ２．前記アルケニルスクシンイミドが下記一般式
【化７】 （式中、Ｒ2は炭素数３０〜２００のポリイソブテニル
基であり、Ｒ3は炭素数２〜１０のアルキレン基であ
り、Ｒ4は水素または炭素数１〜６のアルキル基であ
り、ｍは０〜６、ｎは０〜１の整数である。）で表わさ
れる化合物である前項１記載のほう酸塩分散体よりなる
潤滑添加剤。 ３．前記式中、Ｒ2は炭素数３０〜２００のポリイソブ
テニル基であり、Ｒ3は炭素数２〜６のアルキレン基で
あり、Ｒ4は水素または炭素数１〜６のアルキル基であ
り、ｍは０〜３の整数、ｎは０である前項２記載のほう
酸塩分散体よりなる潤滑添加剤。 ４．前記サルチル酸類のアルカリ土類金属塩が下記一般
式
【化８】 （式中、Ｒ1は炭素数８〜２２のアルキル基を表わし、
Ｍはアルカリ土類金属を表わす。）で示される化合物で
ある前項１、２または３記載のほう酸塩分散体よりなる
潤滑添加剤。 ５．前記ほう酸塩分散体中におけるサルチル酸類のアル
カリ土類金属塩の濃度が０．１〜２５重量％であり、ア
ルケニルスクシンイミドの濃度が０．１〜２５重量％で
ある前項１、２、３または４記載のほう酸塩分散体より
なる潤滑添加剤。 ６．前記ほう酸塩分散体中におけるサルチル酸類のアル
カリ土類金属塩の濃度が１．０〜１０重量％であり、ア
ルケニルスクシンイミドの濃度が１．０〜１０重量％で
ある前項５記載のほう酸塩分散体よりなる潤滑添加剤。 ７．前記ほう酸塩が、下記式
【化９】Ｋ2Ｏ・ｘＢ2Ｏ3 または
【化１０】Ｋ2Ｏ・ｘＢ2Ｏ3・ｙＨ2Ｏ （式中、ｘは２〜５、ｙは１〜９の正数であり、ｘの数
はほう素対カリウム比である。）で示されるものである
前項１、２、３、４、５または６記載のほう酸塩分散体
よりなる潤滑添加剤。 ８．基油中に、（ａ）増ちょう剤および（ｂ）前項１、
２、３、４、５、６または７記載のほう酸塩分散体より
なる潤滑添加剤を含有させたことを特徴とする潤滑グリ
ース組成物。 ９．前記増ちょう剤が、リチウム石鹸、ナトリウム石
鹸、カルシウム石鹸、バリウム石鹸、アルミニウム石
鹸、ウレア類、ベントンおよびクレーよりなる群から選
らばれた増ちょう剤である前項８記載の潤滑グリース組
成物。 １０．前記増ちょう剤が 炭素数１２〜２４のヒドロキシ脂肪酸のリチウム塩お
よび、 炭素数１２〜２４のヒドロキシ脂肪酸のリチウム塩と
炭素数１２〜２４の脂肪酸のリチウム塩との混合物 よりなる群から選ばれた少なくとも１種の増ちょう剤を
含むものである前項８記載の潤滑グリース組成物。 １１．前記増ちょう剤を全量に対し２〜３０重量％使用
した前項１０記載の潤滑グリース組成物。 １２．前記ほう酸塩分散体の使用量が全量に対し０．０
１〜２０重量％である前項１０または１１記載の潤滑グ
リース組成物。 １３．前記ほう酸塩分散体におけるほう酸塩の濃度が５
〜８０重量％である前項１２記載の潤滑グリース組成
物。 １４．前記ほう酸塩分散体におけるほう酸塩の濃度が３
０〜６５重量％である前項１３記載の潤滑グリース組成
物。 １５．その滴点が２３０℃以上である前項１０、１１、
１２、１３または１４記載の潤滑グリース組成物。 １６．前記滴点が２５０℃以上である前項１５記載の潤
滑グリース組成物。
【００４５】
【効果】本発明のほう酸塩分散体よりなる潤滑添加剤
は、ほう酸塩を安定な状態で微細に分散させるのみでな
く、分散体が酸化防止剤としても作用するというすぐれ
た性能を発揮する。そのため、本発明の潤滑添加剤を含
むグリースは耐熱性、耐荷重性に優れているうえ、音響
特性の点でも優れている。本発明のリチウム系増ちょう
剤を含むグリース組成物は、リチウム石けんグリースで
あるのに通常のリチウム石けんグリースに較べてはるか
に耐熱性、耐荷重性に優れているうえ、ほう酸塩を添加
したにもかかわらずリチウム石けんグリースと同程度の
良好な音響特性を備えており、このような高性能特性が
必要であるような用途として自動車のＣＶＪ、ホイール
ベアリングやオルタネーター、工業用としては電化製品
等に使用する小型軸受用から鉄道車両や鉄鋼設備等の大
型軸受用として、さらには油井管に使用するスレッドコ
ンパウンドまで幅広い分野での応用が可能である。
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ１０Ｍ 129:54 133:44 133:58） Ｃ１０Ｎ 10:02 10:04 20:00 30:00 30:06 30:08 30:10 50:10

Claims (5)

    【特許請求の範囲】
  1. 【請求項１】 サルチル酸類のアルカリ土類金属塩
    と、アルケニルスクシンイミドとの混合物中に、ほ
    う酸のアルカリ金属塩を分散させたものであることを特
    徴とするほう酸塩分散体よりなる潤滑添加剤。
  2. 【請求項２】 前記アルケニルスクシンイミドが下記一
    般式 【化１】 （式中、Ｒ2は炭素数３０〜２００のポリイソブテニル
    基であり、Ｒ3は炭素数２〜１０のアルキレン基であ
    り、Ｒ4は水素または炭素数１〜６のアルキル基であ
    り、ｍは０〜６、ｎは０〜１の整数である。）で表わさ
    れる化合物である請求項１記載のほう酸塩分散体よりな
    る潤滑添加剤。
  3. 【請求項３】 前記サルチル酸類のアルカリ土類金属塩
    が下記一般式 【化２】 （式中、Ｒ1は炭素数８〜２２のアルキル基を表わし、
    Ｍはアルカリ土類金属を表わす。）で示される化合物で
    ある請求項１または２記載のほう酸塩分散体よりなる潤
    滑添加剤。
  4. 【請求項４】 基油中に、（ａ）増ちょう剤および
    （ｂ）請求項１、２または３記載のほう酸塩分散体より
    なる潤滑添加剤を含有させたことを特徴とする潤滑グリ
    ース組成物。
  5. 【請求項５】 前記増ちょう剤が 炭素数１２〜２４のヒドロキシ脂肪酸のリチウム塩お
    よび、 炭素数１２〜２４のヒドロキシ脂肪酸のリチウム塩と
    炭素数１２〜２４の脂肪酸のリチウム塩との混合物 よりなる群から選ばれた少なくとも１種の増ちょう剤を
    含むものである請求項４記載の潤滑グリース組成物。
JP7302005A 1994-12-22 1995-10-26 潤滑添加剤およびそれを含む潤滑グリース組成物 Pending JPH08225793A (ja)