Abstract

PURPOSE: To facilitate securement of a sealed property as anticipated by a method wherein form design is easily carried out when a weatherstrip having an extrusion molded part and a die molded part is molded. CONSTITUTION: A mold device 9 for molding of a die molded part is equipped with a fixed mold 21, a moving mold 22, an inner mold 23, and a core 24. A projection 26 having a pointed tip is integrally molded with the core 24 to make the projection 26 jut out to a space part forming a base part in a cavity 25. An end part of an extrusion molded part is fixed to the mold device 9, and a rubber in a plasticized state is filled into the cavity 25 by injection. After curing by vulcanization, a precursor 6A of the die molded part together with the core 24 is detached, and the detached part 27 is pulled by holding. Since a part corresponding to the projection 26 in a part corresponding to the base part in the precursor 6A of the die molded part comes to be of a thin wall at that time, the core 24 is easily taken out from an opening part by being torn. Thereafter, relative opposed surfaces of the opening part are bonded to each other. Since the opening part is narrow in width, a width of the base part when bonded is not shortened from the width in molding.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は 押出成形部と、その押
出成形部に対し金型により連続的に接続成形された型成
形部とを備えたウエザストリップの製造方法に関するも
のである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a weather strip having an extrusion molding section and a molding section continuously connected to the extrusion molding section by a mold.

【０００２】[0002]

【従来の技術】従来、この種のウエザストリップを製造
するに際しては、公知の押出成形法により、押出成形部
が予めほぼ直線状に形成される。そして、当該押出成形
部の先端部が型成形部用の金型に取付固定された状態
で、型成形部が押出成形部の端面に対し連続的に接続成
形される。2. Description of the Related Art Conventionally, when a weather strip of this type is manufactured, an extrusion-molded portion is preliminarily formed into a substantially linear shape by a known extrusion-molding method. Then, the mold forming part is continuously connected and molded to the end face of the extrusion forming part in a state where the tip end part of the extrusion forming part is attached and fixed to the mold for the mold forming part.

【０００３】上記型成形部の接続成形に使用される金型
装置としては、例えば図７に示すようなものが知られて
いる。すなわち、金型装置５１は、固定型５２、可動型
５３、それらの間に位置する中型５４及びウエザストリ
ップの中空部を形成するべく、その長手方向に延びるよ
う配設されるコア５５を備えている。可動型５３は、図
示しないエアシリンダにより図の左右方向へ、中型５４
は図の上下方向へそれぞれスライド可能に配設されてい
る。また、コア５５には、成形後において自身を取り外
すための所定の幅を有する取出し片５６がコア５５の長
手方向に沿って一体形成されている。As a mold apparatus used for connection molding of the above-mentioned molding section, for example, one shown in FIG. 7 is known. That is, the mold device 51 includes a fixed mold 52, a movable mold 53, a middle mold 54 located between them, and a core 55 arranged so as to extend in the longitudinal direction thereof so as to form a hollow portion of the weather strip. ing. The movable mold 53 is moved to the left and right in the drawing by an air cylinder (not shown),
Are arranged so as to be slidable in the vertical direction in the figure. Further, the core 55 is integrally formed with a take-out piece 56 having a predetermined width for removing itself after molding along the longitudinal direction of the core 55.

【０００４】型成形部の成形に際しては、まず、各型５
３，５４，５５を型開きした状態で、予め公知の押出成
形法により成形されてなる押出成形部の端部をセット
し、押出成形部を金型装置５１に対し取付固定する。次
に、エアシリンダを駆動させ、可動型５３、中型５４等
をスライドさせ、型締めを行う。すると、コア５５の周
りの固定型５２、可動型５３及び中型５４で囲まれた空
間によって、型成形部成形用のキャビティ５７が形成さ
れる。そして、そのキャビティ５７内に、図示しないゲ
ート等を介して未加硫ゴムを注入し、充填させる。その
後、未加硫ゴムを加硫させ、各型５３，５４を開き、コ
ア５５及び加硫ゴム（型成形部前駆体）５８Ａの一体と
なったものを取り出す。このとき、型成形部前駆体５８
Ａには、上記取出し片５６の存在により開口部５９が形
成される。When molding the mold forming section, first, each mold 5
With the molds 3, 54, 55 opened, the ends of the extruded parts formed by a known extruding method are set in advance, and the extruded parts are attached and fixed to the mold device 51. Next, the air cylinder is driven to slide the movable mold 53, the middle mold 54, and the like to perform mold clamping. Then, the space surrounded by the fixed mold 52, the movable mold 53, and the middle mold 54 around the core 55 forms a cavity 57 for molding the molding portion. Then, the unvulcanized rubber is injected into the cavity 57 through a gate or the like (not shown) and filled. After that, the unvulcanized rubber is vulcanized, the molds 53 and 54 are opened, and the core 55 and the vulcanized rubber (molding part precursor) 58A integrated with each other are taken out. At this time, the molding portion precursor 58
An opening 59 is formed in A by the presence of the extraction piece 56.

【０００５】さらに、図８に示すように、前記開口部５
９から取出し片５６を取り出すことにより、図中２点鎖
線で示すような型成形部前駆体５８Ａが得られる。その
後、開口部５９の相対向する開口面同士を接着剤で接合
することにより、基底部６１、シール部６２、リップ部
６３及び中空部６４を備えた型成形部５８が得られる。
つまり、この型成形部５８及び押出成形部の一体となっ
たウエザストリップが得られる。Further, as shown in FIG.
By taking out the take-out piece 56 from 9, a mold forming portion precursor 58A as indicated by a two-dot chain line in the figure is obtained. After that, the opposite opening surfaces of the opening 59 are joined together with an adhesive to obtain the mold forming portion 58 including the base portion 61, the seal portion 62, the lip portion 63, and the hollow portion 64.
That is, a weather strip in which the mold forming portion 58 and the extrusion forming portion are integrated is obtained.

【０００６】[0006]

【発明が解決しようとする課題】しかしながら、上記従
来技術では、型成形部５８を得るためには、予めコア５
５を取り出すための取出し片５６を一体形成しておき、
成形完了後において所定の幅を有していた開口部５９を
閉じる必要があった。このため、最終的に得られる型成
形部５８の基底部６１の幅が、当初成形時における型成
形部前駆体５８Ａのそれに対応する幅に対して、閉じら
れる開口部５９の幅の分だけ短くなってしまっていた。
従って、成形時には、つまり金型設計段階においては、
予めその短縮長さ分をみこして確保しておく必要があっ
た。このため、金型の形状設計が非常に困難なものとな
ってしまうおそれがあった。However, in the above-mentioned conventional technique, in order to obtain the mold forming portion 58, the core 5 is previously prepared.
The take-out piece 56 for taking out 5 is integrally formed,
It was necessary to close the opening 59 having a predetermined width after the completion of molding. Therefore, the width of the finally obtained base portion 61 of the mold forming portion 58 is shorter than the width of the mold forming portion precursor 58A at the time of initial molding by the width of the opening 59 to be closed. It had become.
Therefore, at the time of molding, that is, at the mold design stage,
It was necessary to secure the shortened length in advance. For this reason, there is a possibility that it becomes very difficult to design the shape of the mold.

【０００７】また、基底部６１の幅短縮により、シール
部６２の形状が当初の型成形部前駆体５８Ａの形状に比
べて変形して潰れてしまったものとなってしまうおそれ
があった。その結果、当初予想していたシール部６２形
状が得られずに、期待していたシール性を充分に確保で
きないおそれがあった。Further, due to the width reduction of the base portion 61, the shape of the seal portion 62 may be deformed and crushed as compared with the original shape of the molding portion precursor 58A. As a result, the initially expected shape of the sealing portion 62 could not be obtained, and the expected sealing performance could not be sufficiently ensured.

【０００８】本発明は上記問題点を解決するためになさ
れたものであって、その目的は、押出成形部と、その押
出成形部に対し金型装置により連続的に接続成形された
型成形部とを備えてなるウエザストリップを成形するに
際し、形状設計を容易に行うことができ、しかも、期待
どおりのシール性を確保することのできるウエザストリ
ップの製造方法を提供することにある。The present invention has been made to solve the above problems, and an object of the present invention is to provide an extrusion molding part and a molding part which is continuously connected and molded to the extrusion molding part by a mold device. It is an object of the present invention to provide a method for manufacturing a weatherstrip, in which a shape design can be easily carried out when a weatherstrip including the above is formed, and moreover the expected sealing property can be secured.

【０００９】[0009]

【課題を解決するための手段】上記目的を達成するた
め、請求項１に記載の発明においては、ほぼ直線状に形
成された押出成形部と、当該押出成形部に対し連続的に
接続成形されるとともに、少なくとも基底部、シール部
及びこれらによって囲まれた中空部を有してなる型成形
部とを備えたウエザストリップの製造方法であって、押
出成形法により前記押出成形部を成形する工程と、少な
くとも固定型、可動型及び前記中空部を形成するための
コアを備えた金型装置により前記型成形部を成形するた
めのキャビティを形成するとともに、前記コアの一部に
一体形成してなる突起を、前記キャビティのうち前記基
底部に対応する部分に突出せしめる工程と、前記押出成
形部の端面が前記キャビティに露呈するよう前記押出成
形部を前記金型装置に固定する工程と、前記キャビティ
内に可塑化状態にあるゴム材料を注入、充填する工程
と、前記ゴム材料が固化した後、前記固定型に対し、前
記可動型を離間させるとともに、前記固化により成形さ
れた型成形部を前記コアとともに前記金型装置から取り
外す工程と、前記突起に対応した薄肉部分を開口せしめ
るとともに、該開口部分から前記コアを取り出す工程
と、前記開口部分の相互に対向する面を相互に接合する
ことにより、最終的に基底部を形成して型成形部を得る
工程とを備えたことをその要旨としている。In order to achieve the above-mentioned object, in the invention described in claim 1, an extrusion-molded portion formed in a substantially linear shape and continuously connected-molded to the extrusion-molded portion. And a method for producing a weather strip having at least a base portion, a seal portion, and a molding portion having a hollow portion surrounded by these, wherein the extrusion molding portion is molded by an extrusion molding method. The step of forming a cavity for molding the mold-forming part by a mold device having at least a fixed mold, a movable mold, and a core for forming the hollow part, and integrally forming it in a part of the core. Projecting a projection formed on a portion of the cavity corresponding to the base portion, and the extrusion molding unit so that the end surface of the extrusion molding unit is exposed to the cavity. A step of fixing, a step of injecting and filling a rubber material in a plasticized state into the cavity, and a step of separating the movable die from the fixed die after the rubber material has solidified and molding by the solidification A step of removing the formed molding part together with the core from the mold device; a step of opening a thin portion corresponding to the protrusion and taking out the core from the opening; and a surface of the opening opposite to each other. The step is to finally form a base part by joining the two to each other to obtain a mold forming part.

【００１０】また、請求項２に記載の発明においては、
請求項１に記載のウエザストリップの製造方法におい
て、前記コアの一部には、前記基底部を貫通して前記コ
アの取り外しを容易ならしめるための棒状の被把持部を
設けたことをその要旨としている。According to the second aspect of the invention,
2. The method for manufacturing a weather strip according to claim 1, wherein a part of the core is provided with a rod-shaped gripped portion that penetrates the base portion and facilitates removal of the core. It is a summary.

【００１１】[0011]

【作用】上記請求項１に記載の発明によれば、押出成形
法により押出成形部がほぼ直線状に成形される。また、
少なくとも固定型、可動型及び中空部を形成するための
コアを備えた金型装置により型成形部を成形するための
キャビティが形成される。このとき、コアの一部に一体
形成された突起が、キャビティのうち前記基底部に対応
する部分に突出した状態とされる。さらに、押出成形部
の端面がキャビティに露呈するよう押出成形部が金型装
置に固定される。そして、キャビティ内に可塑化状態に
あるゴム材料が注入、充填される。ゴム材料が固化した
後、固定型に対し、可動型が離間され、固化により成形
された型成形部先駆体がコアとともに金型装置から取り
外される。このとき、押出成形部の前記キャビティに露
呈していた端面は型成形部先駆体に対し連続的に接続成
形されている。次に、型成形部先駆体のうち、突起に対
応した部分は薄肉となっており、該薄肉部分が容易に開
口されて、該開口部分からコアが取り出される。そし
て、開口部分の相互に対向する面が相互に接合されるこ
とにより、最終的に基底部が形成されて、少なくとも基
底部、シール部及びこれらによって囲まれた中空部を有
してなる型成形部が得られる。According to the first aspect of the present invention, the extrusion-molded portion is molded into a substantially linear shape by the extrusion molding method. Also,
A cavity for molding the mold molding portion is formed by a mold device including at least a fixed mold, a movable mold, and a core for forming the hollow portion. At this time, the protrusion integrally formed on a part of the core is in a state of protruding to a portion of the cavity corresponding to the base portion. Further, the extrusion molding part is fixed to the mold device so that the end surface of the extrusion molding part is exposed to the cavity. Then, the rubber material in a plasticized state is injected and filled in the cavity. After the rubber material is solidified, the movable mold is separated from the fixed mold, and the mold molding part precursor molded by solidification is removed together with the core from the mold device. At this time, the end surface exposed to the cavity of the extrusion molding portion is continuously connected and molded to the precursor of the molding portion. Next, in the molding portion precursor, the portion corresponding to the protrusion is thin, the thin portion is easily opened, and the core is taken out from the opening. Then, the surfaces of the opening portions facing each other are joined to each other to finally form the base portion, and at least the base portion, the seal portion, and the hollow portion surrounded by these are molded. Part is obtained.

【００１２】さて、本発明によれば、上記接合により基
底部が形成されるのに際し、開口部分の閉じによって基
底部の幅が成形時の幅に対して短縮されることを考慮す
る必要性がさほどない。また、かかる短縮によるシール
部の変形が回避されうる。According to the present invention, when the base is formed by the above-mentioned joining, it is necessary to consider that the width of the base is shortened by the closing of the opening portion with respect to the width at the time of molding. Not so much. Further, the deformation of the seal portion due to such shortening can be avoided.

【００１３】また、請求項２に記載の発明によれば、請
求項１に記載の発明の作用に加えて、コアの一部には、
基底部を貫通する棒状の被把持部が設けられる。このた
め、コアの取り外しに際しては、外部に突出したこの被
把持部が把持される。従って、コアの取り外しが容易に
行われうる。Further, according to the invention described in claim 2, in addition to the function of the invention described in claim 1, in a part of the core,
A rod-shaped grasped portion that penetrates the base portion is provided. Therefore, when the core is removed, the gripped portion protruding outward is gripped. Therefore, the core can be easily removed.

【００１４】[0014]

【実施例】以下、本発明を具体化した一実施例を図１〜
図６に基づいて説明する。図２に示すように、例えばド
アを有する車両本体において、当該ドアに沿った車両本
体の開口部には、ドアの外周形状に沿うようにしてＥＰ
ＤＭ（エチレン−プロピレン−ジエン共重合ゴム）より
なるウエザストリップ３が取付けられている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT An embodiment embodying the present invention will now be described with reference to FIGS.
It will be described with reference to FIG. As shown in FIG. 2, for example, in a vehicle main body having a door, an EP along the outer peripheral shape of the door is provided at an opening of the vehicle main body along the door.
A weather strip 3 made of DM (ethylene-propylene-diene copolymer rubber) is attached.

【００１５】上記ウエザストリップ３は、押出成形部
４，５と型成形部６とを備えている。すなわち、押出成
形部４，５は、図示しない押出成形機によりほぼ直線状
に（長尺状に）形成される。また、型成形部６は、隣接
する押出成形部４，５を連結するように後述する金型装
置９（図４参照）により形成されている。The weather strip 3 has extrusion molding parts 4 and 5 and a mold molding part 6. That is, the extrusion molding portions 4 and 5 are formed in a substantially linear shape (in a long shape) by an extrusion molding machine (not shown). Further, the mold forming part 6 is formed by a mold device 9 (see FIG. 4) described later so as to connect the adjacent extrusion forming parts 4 and 5.

【００１６】本実施例において、前記押出成形部４，５
は、車両本体の図示しないサッシュに取付けられる基底
部１１、当該基底部１１から延び、内部に中空部１２を
有してなるシール部１３及びシール部１３から延びるリ
ップ部１４を備えている。また、図３に示すように、型
成形部６についても、形状こそ違うものの、押出成形部
４，５の場合と同様、基底部１５、シール部１６、リッ
プ部１７及び中空部１８を有している。In this embodiment, the extruded parts 4, 5
Includes a base portion 11 attached to a sash (not shown) of the vehicle body, a seal portion 13 extending from the base portion 11 and having a hollow portion 12 therein, and a lip portion 14 extending from the seal portion 13. Further, as shown in FIG. 3, the mold forming portion 6 also has a base portion 15, a seal portion 16, a lip portion 17 and a hollow portion 18, as in the case of the extrusion forming portions 4 and 5, although the shape is different. ing.

【００１７】次に、上記ウエザストリップ３の型成形部
６を成形するための金型装置９について説明する。図４
は、型成形部６を成形するために使用される金型装置９
を示す断面図である。金型装置９は、例えば図の右側に
位置する固定型２１、図の左側に位置する可動型２２、
これら両型２１，２２の間に位置する中型２３及びこれ
ら各型２１，２２，２３で囲まれた空間の中央に設置さ
れるコア２４を備えている。前記可動型２２は、図示し
ないシリンダにより図の左右方向へ移動可能に配設さ
れ、固定型２１に対し接離可能となっている。さらに、
中型２３はシリンダにより図の上下方向にスライド可能
に配設されている。Next, a die unit 9 for forming the die forming portion 6 of the weather strip 3 will be described. FIG.
Is a mold device 9 used to mold the mold forming part 6.
FIG. The mold device 9 includes, for example, a fixed mold 21 located on the right side of the figure, a movable mold 22 located on the left side of the figure,
It is provided with a middle mold 23 located between these molds 21, 22 and a core 24 installed in the center of the space surrounded by these molds 21, 22, 23. The movable mold 22 is arranged by a cylinder (not shown) so as to be movable in the left-right direction in the drawing, and can be brought into contact with and separated from the fixed mold 21. further,
The middle die 23 is arranged by a cylinder so as to be slidable in the vertical direction in the figure.

【００１８】固定型２１、可動型２２及び中型２３に
は、前記型成形部６の外形形状に対応した成形面２１
ａ，２２ａ，２３ａがそれぞれ形成されている。また、
コア２４は前記型成形部６の中空部１８を形成するよう
になっている。そして、これら成形面２１ａ，２２ａ，
２３ａ及びコア２４の外面によって型成形部６を成形す
るためのキャビティ２５が形成されている。さらに、コ
ア２４には、先端の尖った突起２６がコア２４の長手方
向（紙面奥行方向）に延びるようにして一体的に形成さ
れており、該突起２６は前記キャビティ２５のうち、基
底部１５を形成する空間部分に突出した状態となってい
る。併せて、コア２４の一部には、前記固定型２１内ま
で延びる被把持部としての棒状の取出し部２７が一体的
に形成されている。The fixed mold 21, the movable mold 22, and the middle mold 23 have molding surfaces 21 corresponding to the outer shape of the mold molding portion 6.
a, 22a and 23a are formed respectively. Also,
The core 24 forms the hollow portion 18 of the mold forming portion 6. Then, these molding surfaces 21a, 22a,
A cavity 25 for molding the mold-molding portion 6 is formed by the outer surfaces of 23 a and the core 24. Further, a projection 26 having a sharp tip is integrally formed on the core 24 so as to extend in the longitudinal direction of the core 24 (the depth direction of the paper surface). It is in a state of protruding into the space portion forming the. In addition, a rod-shaped take-out portion 27 as a held portion extending into the fixed die 21 is integrally formed on a part of the core 24.

【００１９】次に、上記の構成を有してなるウエザスト
リップ３の製造方法及び製造時の作用効果について説明
する。まず、図示しない押出成形機を用い、公知の押出
成形法により上記押出成形部４，５を成形する。このと
きには、押出成形部４，５の前記基底部１１、シール部
１３、中空部１２及びリップ部１４が形成される。Next, a method of manufacturing the weather strip 3 having the above-mentioned structure and the function and effect at the time of manufacturing will be described. First, the extrusion molding parts 4 and 5 are molded by a known extrusion molding method using an extrusion molding machine (not shown). At this time, the base portion 11, the seal portion 13, the hollow portion 12, and the lip portion 14 of the extrusion-molded portions 4 and 5 are formed.

【００２０】次に、以下のようにして型成形部６を成形
する。すなわち、まず、各型２１，２２，２３等を相互
に型開きした状態で、上記押出成形部４，５の端部をコ
ア２４の両端部に嵌め込みセットし、可動型２２及び中
型２３を固定型２１に対し型締めする。これにより、押
出成形部４，５が金型装置９に対し取付固定されるとと
もに、図４に示すように、キャビティ２５が形成され
る。Next, the mold forming part 6 is formed as follows. That is, first, with the molds 21, 22, 23 and the like opened, the ends of the extruded parts 4, 5 are fitted into both ends of the core 24 and set to fix the movable mold 22 and the middle mold 23. The mold 21 is clamped. As a result, the extrusion-molded parts 4 and 5 are fixedly attached to the mold device 9, and the cavity 25 is formed as shown in FIG.

【００２１】そして、この状態から図１に示すように、
キャビティ２５内に、可塑化状態にあるＥＰＤＭを図示
しないゲートより注入し、充填させる。その後、ＥＰＤ
Ｍを加硫固化させるとともに、固化完了後、図５に示す
ように、可動型２２及び中型２３を型開きして、成形さ
れた型成形部前駆体６Ａをコア２４とともに金型装置９
から取り外す。From this state, as shown in FIG.
EPDM in a plasticized state is injected into the cavity 25 from a gate (not shown) and filled. After that, EPD
M is vulcanized and solidified, and after solidification is completed, as shown in FIG. 5, the movable mold 22 and the middle mold 23 are opened, and the molded mold forming portion precursor 6A is molded together with the core 24 in the mold device 9
Remove from.

【００２２】次に、型成形部前駆体６Ａを別途支持した
状態で、取り外し部２７を把持し、同図矢印方向に引っ
張る。このとき、型成形部前駆体６Ａのうちの前記基底
部１５に相応する部分のうち、前記突起２６に対応する
部分は、当該突起２６の存在により他の部分に比べて薄
肉となっている。このため、上記の引っ張り動作によ
り、該薄肉部分が容易に引き裂かれて破れ、図６に示す
ように、開口部分２８が形成されるとともに、該開口部
分２８からコア２４が容易に取り出される。この取り外
しにより、型成形部前駆体６Ａの内部は中空状態とな
る。Next, while the mold forming portion precursor 6A is separately supported, the detaching portion 27 is gripped and pulled in the direction of the arrow in the figure. At this time, of the portion corresponding to the base portion 15 of the mold forming portion precursor 6A, the portion corresponding to the protrusion 26 is thinner than the other portions due to the presence of the protrusion 26. Therefore, by the above-described pulling operation, the thin portion is easily torn and torn, and as shown in FIG. 6, the opening portion 28 is formed and the core 24 is easily taken out from the opening portion 28. By this removal, the interior of the mold forming portion precursor 6A becomes hollow.

【００２３】次に、図３に示すように、極めて幅狭な開
口部分２８の相互に対向しあう面を接合することによ
り、最終的に基底部１５が形成される。また、これとと
もに、シール部１６及び中空部１８も最終的に形成され
る。このようにして、押出成形部４，５と、同押出成形
部４，５に対し連続的に接続成形された型成形部６とを
備えたウエザストリップ３が得られるのである。なお、
コア２４の取り外しに伴い、取り外し部２７の痕跡たる
開口が形成されるが、その開口面積は微小であることか
ら、上記接合に際しては無視されうる。Next, as shown in FIG. 3, the base portions 15 are finally formed by joining the surfaces of the extremely narrow opening portions 28 facing each other. Along with this, the seal portion 16 and the hollow portion 18 are finally formed. In this way, the weather strip 3 including the extrusion-molded portions 4 and 5 and the die-molded portion 6 that is continuously connected and molded to the extrusion-molded portions 4 and 5 is obtained. In addition,
Along with the removal of the core 24, an opening that is a trace of the removal portion 27 is formed, but since the opening area is very small, it can be ignored in the above joining.

【００２４】以上説明したように、本実施例によれば、
コア２４には先端の尖った突起２６を一体形成するとと
もに、突起２６を前記キャビティ２５のうち、前記基底
部１５形成用の空間部分に突出せしめるようにした。こ
のため、薄肉部分が引き裂かれ、極めて幅狭な開口部分
２８が形成されることにより、コア２４は容易に取り出
される。従って、接合により最終的に基底部１５が形成
されるのに際し、開口部分２８の閉じによって基底部１
５の幅が成形時の幅に対して短縮されることがない。従
って、金型装置９の設計段階において、基底部１５の短
縮を考慮する必要がなく、かかる短縮分をみこして設計
が複雑困難なものとなってしまうのを防止することがで
きる。すなわち、金型装置９の設計を容易に行うことが
できる。As described above, according to this embodiment,
A protrusion 26 having a sharp tip is integrally formed on the core 24, and the protrusion 26 is made to project into the space portion of the cavity 25 for forming the base portion 15. Therefore, the thin portion is torn and the opening portion 28 having an extremely narrow width is formed, so that the core 24 can be easily taken out. Therefore, when the base 15 is finally formed by joining, the base 1 is closed by closing the opening 28.
The width of 5 is not shortened with respect to the width at the time of molding. Therefore, it is not necessary to consider the shortening of the base portion 15 in the design stage of the mold device 9, and it is possible to prevent the design from becoming complicated due to such shortening. That is, the mold device 9 can be easily designed.

【００２５】また、上記接合に際しての基底部１５の幅
短縮がないことから、接合に伴って、成形直後の型成形
部前駆体６Ａの形状に比べて型成形部６の形状が大きく
変形してしまうこともない。そのため、シール部１６等
の変形に起因するシール性の低下等の不具合の発生を確
実に防止することができる。Further, since the width of the base portion 15 is not shortened at the time of the above-mentioned joining, the shape of the die-molding portion 6 is largely deformed as compared with the shape of the die-forming portion precursor 6A immediately after the molding. It doesn't get lost. Therefore, it is possible to reliably prevent the occurrence of defects such as deterioration of the sealing property due to the deformation of the seal portion 16 and the like.

【００２６】さらに、本実施例では、コア２４の一部に
は、基底部１５を貫通せしめるべく棒状の取出し部２７
を設けるようにした。このため、コア２４の取り外しに
際しては、外部に突出したこの取出し部２７が把持さ
れ、引き抜かれることにより、コア２４を容易に取り外
すことができる。その結果、作業性の著しい向上を図る
ことができる。Further, in this embodiment, a rod-shaped take-out portion 27 is provided in a part of the core 24 so that the base portion 15 can be penetrated.
Was set up. Therefore, when the core 24 is removed, the core 24 can be easily removed by grasping and pulling out the take-out portion 27 protruding to the outside. As a result, the workability can be significantly improved.

【００２７】併せて、本実施例では、突起２６の形状を
先端が尖った形状としたので、薄肉部分を容易に引き裂
くことができる。このため、コア２６の取り外しを、必
要以上の力をかけずとも容易に行うことができ、ひいて
は作業性の向上を図ることができる。In addition, in this embodiment, since the projection 26 has a sharp tip, the thin portion can be easily torn. Therefore, the core 26 can be easily removed without applying an excessive force, and the workability can be improved.

【００２８】尚、本発明は上記実施例に限定されず、例
えば次の如く構成してもよい。 （１）前記実施例では、１つの中型２３を使用する構成
としたが、ウエザストリップ自体の形状がより複雑な場
合には複数の中型を用いる場合に具体化してもよい。The present invention is not limited to the above embodiment, but may be configured as follows, for example. (1) In the above-described embodiment, one medium mold 23 is used, but when the weather strip itself has a more complicated shape, a plurality of medium molds may be used.

【００２９】（２）型成形部６におけるリップ部１７の
本数は特に限定されるものではない。また、特にリップ
部を有しない場合に具体化してもよい。 （３）前記実施例では、ウエザストリップ３のコーナー
部分に相当する型成形部６を成形する場合に具体化した
が、例えばウエザストリップ３の端部等その他の型成形
部を得る場合にも具体化できる。(2) The number of the lip parts 17 in the mold forming part 6 is not particularly limited. Further, it may be embodied especially when it does not have a lip portion. (3) In the above-described embodiment, the case was embodied in the case of molding the mold forming portion 6 corresponding to the corner portion of the weather strip 3. Can also be embodied.

【００３０】（４）前記実施例では、ウエザストリップ
３の素材としてＥＰＤＭを用いたが、その外にもスチレ
ンブタジエンム、ブタジエンゴム、クロロプレンゴム、
ブチルゴム、ニトリルゴム、エチレンプロピレン共重合
ゴム、アクリルゴム等の各種ゴム、或いはゴム状弾性を
有する合成樹脂素材によりウエザストリップを形成して
もよい。(4) In the above embodiment, EPDM was used as the material of the weather strip 3, but in addition to this, styrene-butadiene rubber, butadiene rubber, chloroprene rubber,
The weather strip may be formed of various rubbers such as butyl rubber, nitrile rubber, ethylene-propylene copolymer rubber, acrylic rubber, or a synthetic resin material having rubber-like elasticity.

【００３１】（５）前記実施例では、車両本体のドア開
口部に取付けられるウエザストリップ３に関して具体化
したが、ルーフサイド等その他の部位に取付けられるウ
エザストリップに具体化してもよい。(5) In the above embodiment, the weather strip 3 attached to the door opening of the vehicle body is embodied, but it may be embodied as a weather strip attached to other parts such as the roof side.

【００３２】（６）前記実施例では、突起２６として、
先端が尖った、断面ほぼ三角形状を有するものに具体化
したが、接合により基底部１５の幅が短縮されにくいも
のであれば、いかなる形状のものをも採用することがで
きる。(6) In the above embodiment, the protrusion 26 is
The embodiment has been embodied in a shape with a sharp tip and a substantially triangular cross section, but any shape can be adopted as long as it is difficult to reduce the width of the base portion 15 by joining.

【００３３】特許請求の範囲の各請求項に記載されない
ものであって、上記実施例から把握できる技術的思想に
ついて以下にその効果とともに記載する。 （ａ）請求項１又は２に記載のウエザストリップの製造
方法において、前記突起の形状を先端が尖ったものとし
たことを特徴とする。かかる構成とすることにより、コ
アの取り外し作業をさらに容易に行うことができ、作業
性の向上を図ることができる。The technical idea which is not described in each claim of the claims and can be grasped from the above-mentioned embodiment will be described below together with its effect. (A) In the method of manufacturing a weather strip according to claim 1 or 2, the shape of the protrusion is a pointed tip. With such a configuration, the work of removing the core can be performed more easily, and the workability can be improved.

【００３４】[0034]

【発明の効果】以上詳述したように、本発明のウエザス
トリップの製造方法によれば、押出成形部と、その押出
成形部に対し金型装置により連続的に接続成形された型
成形部とを備えてなるウエザストリップを成形するに際
し、形状設計を容易に行うことができ、しかも、期待ど
おりのシール性を確保することができるという優れた効
果を奏する。As described above in detail, according to the method for producing a weather strip of the present invention, the extrusion molding portion and the molding portion formed by continuously connecting and molding the extrusion molding portion with the molding device. When the weather strip including the above is molded, it is possible to easily design the shape, and moreover, it is possible to ensure the desired sealing performance.

【００３５】特に、請求項２に記載の発明によれば、コ
アの取り外し作業を容易に行うことができ、作業性の向
上を図ることができるという優れた効果を奏する。In particular, according to the second aspect of the invention, there is an excellent effect that the work of removing the core can be easily performed and the workability can be improved.

【図面の簡単な説明】[Brief description of drawings]

【図１】一実施例においてキャビティにＥＰＤＭを充填
した状態を示す金型装置の断面図である。FIG. 1 is a cross-sectional view of a mold device showing a state in which a cavity is filled with EPDM in one example.

【図２】ウエザストリップを示す部分斜視図である。FIG. 2 is a partial perspective view showing a weather strip.

【図３】型成形部を示す図２のＸ−Ｘ線断面図である。FIG. 3 is a cross-sectional view taken along line XX of FIG. 2 showing a mold forming part.

【図４】型成形部を成形するための金型装置を示す断面
図である。FIG. 4 is a cross-sectional view showing a mold device for molding a mold molding portion.

【図５】コア及び型成形部前駆体を示す断面図である。FIG. 5 is a cross-sectional view showing a core and a molding part precursor.

【図６】一実施例における接合前の型成形部を示す断面
図である。FIG. 6 is a cross-sectional view showing a mold forming portion before joining in one example.

【図７】従来技術の型成形部成形用金型装置を示す断面
図である。FIG. 7 is a cross-sectional view showing a conventional mold device for molding a mold portion.

【図８】従来技術の型成形部を示す断面図である。FIG. 8 is a cross-sectional view showing a conventional die molding unit.

【符号の説明】[Explanation of symbols]

３…ウエザストリップ、４，５…押出成形部、６…型成
形部、６Ａ…型成形部前駆体、９…金型装置、１５…基
底部、１６…シール部、１８…中空部、２１…固定型、
２２…可動型、２３…中型、２４…コア、２５…キャビ
ティ、２６…突起、２７…被把持部としての取出し部、
２８…開口部分。3 ... Weather strip, 4, 5 ... Extrusion molding part, 6 ... Mold molding part, 6A ... Mold molding part precursor, 9 ... Mold device, 15 ... Base part, 16 ... Seal part, 18 ... Hollow part, 21 … Fixed type,
22 ... Movable type, 23 ... Medium type, 24 ... Core, 25 ... Cavity, 26 ... Projection, 27 ... Take-out section as grasped section,
28 ... Opening part.

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】 ほぼ直線状に形成された押出成形部
（４，５）と、当該押出成形部（４，５）に対し連続的
に接続成形されるとともに、少なくとも基底部（１
５）、シール部（１６）及びこれらによって囲まれた中
空部（１８）を有してなる型成形部（６）とを備えたウ
エザストリップの製造方法であって、 押出成形法により前記押出成形部（４，５）を成形する
工程と、 少なくとも固定型（２１）、可動型（２２）及び前記中
空部（１８）を形成するためのコア（２４）を備えた金
型装置（９）により前記型成形部（６）を成形するため
のキャビティ（２５）を形成するとともに、前記コア
（２４）の一部に一体形成してなる突起（２６）を、前
記キャビティ（２５）のうち前記基底部（１５）に対応
する部分に突出せしめる工程と、 前記押出成形部（４，５）の端面が前記キャビティ（２
５）に露呈するよう前記押出成形部（４，５）を前記金
型装置（９）に固定する工程と、 前記キャビティ（２５）内に可塑化状態にあるゴム材料
を注入、充填する工程と、 前記材料ゴムが固化した後、前記固定型（２１）に対
し、前記可動型（２２）を離間させるとともに、前記固
化により成形された型成形部前駆体（６Ａ）を前記コア
（２４）とともに前記金型装置（９）から取り外す工程
と、 前記型成形部前駆体（６Ａ）のうち、前記突起（２６）
に対応した薄肉部分を開口せしめるとともに、該開口部
分（２８）から前記コア（２４）を取り出す工程と、 前記開口部分（２８）の相互に対向する面を接合するこ
とにより、最終的に基底部（１５）を形成して型成形部
（６）を得る工程とを備えたことを特徴とするウエザス
トリップの製造方法。1. An extrusion-molded portion (4,5) formed in a substantially linear shape, and continuously connected-molded to the extrusion-molded portion (4,5), and at least a base portion (1).
5), a sealing part (16) and a molding part (6) having a hollow part (18) surrounded by the sealing part (16), the method comprising: A step of molding the molding parts (4, 5), and a mold device (9) including at least a fixed mold (21), a movable mold (22) and a core (24) for forming the hollow part (18) To form a cavity (25) for molding the die-molding part (6), and to form a protrusion (26) integrally formed on a part of the core (24) in the cavity (25). A step of projecting to a portion corresponding to the base portion (15); and an end surface of the extrusion-molded portion (4, 5) having the cavity (2).
5) fixing the extrusion molding part (4, 5) to the mold device (9) so as to be exposed to 5), and injecting and filling a rubber material in a plasticized state into the cavity (25). After the material rubber is solidified, the movable mold (22) is separated from the fixed mold (21), and the mold forming part precursor (6A) molded by the solidification is also formed together with the core (24). A step of removing from the mold device (9), and the protrusion (26) of the mold forming part precursor (6A)
By opening the thin portion corresponding to the above, and taking out the core (24) from the opening portion (28), and by joining the surfaces of the opening portion (28) facing each other, finally the base portion. (15) is formed to obtain a mold forming part (6). 【請求項２】 請求項１に記載のウエザストリップの製
造方法において、 前記コア（２４）の一部には、前記基底部（１５）を貫
通して前記コア（２４）の取り外しを容易ならしめるた
めの棒状の被把持部（２７）を設けたことを特徴とする
ウエザストリップの製造方法。2. The method of manufacturing a weather strip according to claim 1, wherein a part of the core (24) penetrates the base portion (15) to facilitate removal of the core (24). A method for manufacturing a weather strip, characterized in that a bar-shaped gripped portion (27) for tightening is provided.