JPH08190735A - Optical information recording medium - Google Patents
Optical information recording mediumInfo
- Publication number
- JPH08190735A JPH08190735A JP7002104A JP210495A JPH08190735A JP H08190735 A JPH08190735 A JP H08190735A JP 7002104 A JP7002104 A JP 7002104A JP 210495 A JP210495 A JP 210495A JP H08190735 A JPH08190735 A JP H08190735A
- Authority
- JP
- Japan
- Prior art keywords
- dye
- recording medium
- information recording
- optical information
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、光磁気ディスクのよう
な反射率の低い媒体を対象とする記録再生装置によって
信号再生することが可能な光情報記録媒体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an optical information recording medium capable of signal reproduction by a recording / reproducing apparatus for a medium having a low reflectance such as a magneto-optical disk.
【０００２】[0002]
【従来技術】光情報記録媒体としては、オーディオ用の
コンパクトディスク（ＣＤ）、ビデオ用のレーザディス
ク（ＬＤ）等が既に広く普及している。これらコンパク
トディスク、レーザディスクは、情報信号に対応するピ
ットが凹凸形状として予め形成された基板上に反射層
と、必要に応じて保護層が設けられてなるものであり、
記録された情報信号の再生のみが行われる再生専用型の
光ディスクである。上記反射層には、Ａｌ、Ａｕ等の高
反射率、すなわち低吸収率の材料が用いられている。2. Description of the Related Art As optical information recording media, audio compact discs (CD), video laser discs (LD), and the like have already become widespread. These compact discs and laser discs are those in which a reflective layer is provided on a substrate on which pits corresponding to information signals are formed in advance as an uneven shape, and a protective layer is provided if necessary.
This is a read-only type optical disc that only reproduces the recorded information signal. The reflective layer is made of a material having a high reflectance, that is, a low absorptivity, such as Al or Au.
【０００３】一方、近年、上記再生専用型の光ディスク
と異なり、情報の書き込み、消去が可能な光情報記録媒
体として光磁気ディスクの開発が進められている。この
光磁気ディスクは、基板上に、膜面と垂直方向に磁化容
易軸を有し且つ磁気光学効果の大きな記録磁性層（例え
ばＴｂＦｅＣｏ等の希土類一遷移金属合金非晶質薄膜）
や反射層、誘電体層を積層することにより記録部を形成
してなるものである。このような光磁気ディスクとして
は、直径６４ｍｍの小径の光磁気ディスク（いわゆるミ
ニディスク）がカートリッジ内に収容された形で普及し
始めている。On the other hand, in recent years, unlike the above-mentioned read-only type optical disc, a magneto-optical disc is being developed as an optical information recording medium capable of writing and erasing information. This magneto-optical disk has a recording magnetic layer (for example, a rare earth-transition metal alloy amorphous thin film such as TbFeCo) which has an easy axis of magnetization in the direction perpendicular to the film surface and has a large magneto-optical effect on a substrate.
The recording portion is formed by laminating a reflective layer and a dielectric layer. As such a magneto-optical disk, a small-diameter magneto-optical disk (so-called mini disk) having a diameter of 64 mm has begun to be popularized in a form housed in a cartridge.
【０００４】ところで、上記再生専用型の光ディスクが
光磁気ディスク用記録再生装置によっても再生が行えれ
ば、再生専用型光ディスク、光磁気ディスクシステムの
双方の普及性、実用性を高める上で好ましいと言える。
しかし、Ａｌ膜、Ａｕ膜等を反射層とする再生専用型光
ディスクでは、レーザ光に対する反射率が７０％以上と
光磁気ディスクの反射率が１５〜２５％であるのに比べ
て格段に高く、光磁気ディスクを対象とする記録再生装
置によって信号再生することができない。By the way, it is preferable that the read-only optical disk can be played back by a magneto-optical disk recording / playback apparatus as well in order to enhance the spread and practicality of both the read-only optical disk and the magneto-optical disk system. I can say.
However, in a read-only type optical disc having an Al film, an Au film or the like as a reflective layer, the reflectance for laser light is 70% or more, which is significantly higher than the reflectance of a magneto-optical disc of 15 to 25%. A signal cannot be reproduced by a recording / reproducing device for a magneto-optical disk.
【０００５】そこで、再生専用型の光ディスクでは、Ａ
ｌ膜やＡｕ膜の代わりに、色素材料と高分子材料よりな
る色素含有層を反射層として用いる試みがなされてい
る。例えば上記色素材料としてシアニン色素を用いた光
ディスクは反射率が１５〜２５％と光磁気ディスクの反
射率と同程度であり、光磁気ディスク用記録再生装置に
適応可能な再生専用型光ディスクとして期待される。Therefore, in a read-only type optical disc, A
Attempts have been made to use a dye-containing layer made of a dye material and a polymer material as a reflective layer instead of the l film or Au film. For example, an optical disc using a cyanine dye as the dye material has a reflectance of 15 to 25%, which is about the same as the reflectance of a magneto-optical disc, and is expected as a read-only optical disc applicable to a recording / reproducing device for a magneto-optical disc. It
【０００６】[0006]
【本発明が解決しようとする課題】ところで、上述の色
素含有層を反射層として用いた光ディスクでは、読み出
し光が基板／色素含有層界面、色素含有層／空気界面で
それぞれ反射し、多重干渉することを利用して信号再生
が行われるため、色素含有層上に屈折率の高い粉塵等が
付着すると、光の多重干渉に乱れが生じ、信号再生に支
障をきたす結果となる。By the way, in an optical disc using the above-mentioned dye-containing layer as a reflective layer, read light is reflected at the substrate / dye-containing layer interface and the dye-containing layer / air interface, respectively, and causes multiple interference. Since signal reproduction is performed by utilizing this, if dust or the like having a high refractive index adheres to the dye-containing layer, the multiple interference of light is disturbed, resulting in a problem in signal reproduction.
【０００７】そこで、本発明はこのような従来の実情に
鑑みて提案されたものであり、光磁気ディスク等の反射
率の低い媒体を対象とする記録再生装置によって信号再
生することが可能であるとともに、信号再生時に粉塵等
の付着物の影響を受けないような光情報記録媒体を提供
することを目的とする。Therefore, the present invention has been proposed in view of such a conventional situation, and it is possible to reproduce a signal by a recording / reproducing apparatus for a medium having a low reflectance such as a magneto-optical disk. At the same time, it is an object to provide an optical information recording medium that is not affected by adhered substances such as dust during signal reproduction.
【０００８】[0008]
【課題を解決するための手段】本発明に係る光情報記録
媒体は、上述の目的を達成するために提案されたもので
あり、情報信号に対応する凹凸が形成された透明基板上
に、色素材料が含有され、且つ反射率が１５〜２５％で
ある反射層が形成されてなるものであり、前記反射層の
光透過率が１６％以下のものである。An optical information recording medium according to the present invention has been proposed in order to achieve the above-mentioned object, and a dye is formed on a transparent substrate on which irregularities corresponding to information signals are formed. A reflective layer containing a material and having a reflectance of 15 to 25% is formed, and the light transmittance of the reflective layer is 16% or less.
【０００９】本発明が適用される光情報記録媒体は、図
１に示すように、情報信号や案内溝、番地符号ピットに
対応する凹状のピット部２ａと凸状のランド部２ｂが形
成された透明基板１上に、反射率が１５〜２５％の色素
含有層３が反射層として形成されてなるものである。The optical information recording medium to which the present invention is applied has, as shown in FIG. 1, a concave pit portion 2a and a convex land portion 2b corresponding to information signals, guide grooves, and address code pits. The dye-containing layer 3 having a reflectance of 15 to 25% is formed as a reflective layer on the transparent substrate 1.
【００１０】本発明では、このような光情報記録媒体に
おいて、色素含有層の光等か率を１６％以下に規制す
る。色素含有層３の光透過率が１６％より大きい光情報
記録媒体は、色素含有層３上への粉塵等の付着により、
信号再生に支障をきたすものとなってしまう。In the present invention, in such an optical information recording medium, the rate of light or the like of the dye-containing layer is regulated to 16% or less. The optical information recording medium in which the light transmittance of the dye-containing layer 3 is larger than 16%, due to the adhesion of dust or the like on the dye-containing layer 3,
This will hinder the signal reproduction.
【００１１】色素含有層３の光透過率を１６％以下とす
るためには、再生光波長付近に吸収のある色素材料を用
い、これと光安定化剤とを溶媒に溶解させた色素含有層
用塗料を透明基板１上に塗布し、その後、溶媒を乾燥除
去すればよい。なお、色素含有層用塗料に、高分子材料
を混ぜると光透過率が上昇してしまうため、高分子材料
は使用しないか、使用しても少量とすることが好まし
い。In order to control the light transmittance of the dye-containing layer 3 to 16% or less, a dye material having absorption near the reproduction light wavelength is used, and this and a light stabilizer are dissolved in a solvent. The coating material for coating is applied on the transparent substrate 1, and then the solvent is dried and removed. In addition, since the light transmittance increases when a polymer material is mixed with the dye-containing layer coating material, it is preferable not to use the polymer material or to use a small amount even if it is used.
【００１２】また、色素含有層３の複素屈折率の実数部
ｎは、１．８４以上である好適である。このような色素
含有層３は、実用的な範囲での膜厚調整のみで反射率を
１５〜２５％とすることができ、製膜条件の設定が容易
となるからである。The real part n of the complex refractive index of the dye-containing layer 3 is preferably 1.84 or more. This is because such a dye-containing layer 3 can have a reflectance of 15 to 25% only by adjusting the film thickness within a practical range, and the film forming conditions can be easily set.
【００１３】上述のような色素含有層３を形成できる色
素材料としては、再生光として７８０ｎｍなる波長の光
を用いるならば、化１に示すＮＫ２４２１（日本感光色
素社製 商品名）、化２に示すＮＫ１２５（日本感光色
素社製 商品名）等のシアニン色素が挙げられる。As the dye material capable of forming the dye-containing layer 3 as described above, if light having a wavelength of 780 nm is used as the reproduction light, then NK2421 (trade name of Nippon Sensitive Dye Co., Ltd.) shown in Chemical formula 1 and Chemical formula 2 are shown in Chemical formula 2. Examples include cyanine dyes such as NK125 (trade name, manufactured by Nippon Senshoku Co., Ltd.).
【００１４】[0014]
【化１】 Embedded image
【００１５】[0015]
【化２】 Embedded image
【００１６】さらに、色素材料の光退色を防止する目的
で添加される光安定化剤としては、アミン類等の電子供
与性のあるもの、ニッケル錯体等の色素材料の励起状態
のエネルギー準位より低いエネルギー準位を有する材料
等が使用される。例えば、化３に示すＩＲＧ００３（日
本化薬社製 商品名）が挙げられる。Further, as the light stabilizer added for the purpose of preventing the photobleaching of the dye material, those having an electron donating property such as amines and the energy level of the excited state of the dye material such as nickel complex are used. A material having a low energy level is used. For example, IRG003 (trade name, manufactured by Nippon Kayaku Co., Ltd.) shown in Chemical formula 3 can be mentioned.
【００１７】[0017]
【化３】 Embedded image
【００１８】そして、前記色素含有層３上には、耐傷特
性を高める目的で、高分子材料を主体とする保護層４が
設けられてもよい。この保護層４を形成するには、高分
子材料を溶媒に溶解して保護層用塗料を調製し、前記色
素含有層３上に塗布し、その後、溶媒を乾燥除去すると
よい。A protective layer 4 mainly composed of a polymer material may be provided on the dye-containing layer 3 for the purpose of enhancing scratch resistance. In order to form the protective layer 4, it is preferable that a polymeric material is dissolved in a solvent to prepare a coating material for the protective layer, the coating material is applied onto the dye-containing layer 3, and then the solvent is dried and removed.
【００１９】この高分子材料としては、従来公知の材料
がいずれも使用可能であり、シリコンワニス、チタンポ
リマ、ニトロセルロース等が使用できる。中でも、化４
に示すＫＲ３１１（信越シリコーン社製 商品名）のご
ときシリコンワニスを用いると、溶媒が乾燥除去される
際に、水酸基の縮合反応が起こるため、硬度の高い保護
層３が得られる。As the polymer material, any conventionally known material can be used, and silicon varnish, titanium polymer, nitrocellulose or the like can be used. Above all,
When a silicon varnish such as KR311 (trade name, manufactured by Shin-Etsu Silicone Co., Ltd.) is used, a protective layer 3 having high hardness is obtained because a condensation reaction of hydroxyl groups occurs when the solvent is dried and removed.
【００２０】[0020]
【化４】 [Chemical 4]
【００２１】そして、上述の保護層用塗料には、チタン
アルコキシドあるいはその重合体を添加してもよい。こ
こで、チタンアルコキシドとは、Ｔｉ（ＯＲ）4 または
Ｔｉ（ＯＲ）3 の化学式で表されるものである。また、
チタンアルコキシドの重合体は、下式（１），（２），
（３）のようなヒドロキシ化反応、脱アルコール反応、
脱水反応を経て生成するものである。Titanium alkoxide or its polymer may be added to the above-mentioned coating material for protective layer. Here, the titanium alkoxide is represented by the chemical formula of Ti (OR) 4 or Ti (OR) 3 . Also,
Polymers of titanium alkoxide are represented by the following formulas (1), (2),
Hydroxylation reaction, dealcoholation reaction such as (3),
It is produced through a dehydration reaction.
【００２２】 Ｔｉ（ＯＲ）4 ＋ Ｈ2 Ｏ → Ｔｉ（ＯＲ）3 ＯＨ ＋ ＲＯＨ ・・・（１） Ｔｉ（ＯＲ）4 ＋Ｔｉ（ＯＲ）3 ＯＨ → Ｔｉ（ＯＲ）3 ＯＴｉ（ＯＲ）3 ＋ ＲＯＨ ・・・（２） ２Ｔｉ（ＯＲ）3 ＯＨ → Ｔｉ（ＯＲ）3 ＯＴｉ（ＯＲ）3 ＋ Ｈ2 Ｏ ・・・（３） そして、さらに重合が進むと、化５にて示されるような
ポリマーとなる。Ti (OR) 4 + H 2 O → Ti (OR) 3 OH + ROH (1) Ti (OR) 4 + Ti (OR) 3 OH → Ti (OR) 3 OTi (OR) 3 + ROH ... (2) 2Ti (OR) 3 OH → Ti (OR) 3 OTi (OR) 3 + H 2 O ... (3) Then, as the polymerization further proceeds, as shown in Chemical formula 5 Become a polymer.
【００２３】[0023]
【化５】 Embedded image
【００２４】なお、本発明においては、従来公知のチタ
ンアルコキシドまたはその重合体がいずれも使用可能で
ある。即ち、化５において、ＲはＣＨ3 ，Ｃ2 Ｈ5 ，Ｃ
3 Ｈ7 ，Ｃ4 Ｈ9 のいずれかを表し、直鎖状であっても
分岐状であってもよく、ｎは１以上の自然数であればよ
い。中でも、ＲがＣ3 Ｈ7 ，Ｃ4 Ｈ9 のいずれかであ
り、ｎが１〜１０の自然数であって好適である。In the present invention, any conventionally known titanium alkoxide or its polymer can be used. That is, in Chemical formula 5, R is CH 3 , C 2 H 5 , C
It represents either 3 H 7 or C 4 H 9 , may be linear or branched, and n may be a natural number of 1 or more. Among them, R is either C 3 H 7 or C 4 H 9 , and n is a natural number of 1 to 10, which is preferable.
【００２５】上述のようなチタンアルコキシドやその重
合体は、通常、ｎ−ブタノールやｉ−プロパノールのよ
うな溶媒に溶解された状態で入手される。The above-mentioned titanium alkoxide and its polymer are usually obtained in a state of being dissolved in a solvent such as n-butanol or i-propanol.
【００２６】そして、このようなチタンアルコキシドあ
るいはその重合体は、高分子材料と溶媒と共に色素含有
層３上に塗布された後、溶媒が除去される際に、加水分
解によりＴｉＯ2 となり、保護層４の表面に撥水性を有
する膜を形成する。Then, such a titanium alkoxide or a polymer thereof is applied onto the dye-containing layer 3 together with the polymer material and the solvent, and when the solvent is removed, it becomes TiO 2 by hydrolysis and becomes a protective layer. A film having water repellency is formed on the surface of No. 4.
【００２７】前記チタンアルコキシドあるいはその重合
体の添加量としては、保護層用塗料中の高分子材料に対
して５〜１０重量％とされて好適である。チタンアルコ
キシドあるいはその重合体の添加量が少なすぎると、十
分な撥水効果が得られない。また、多すぎても、チタン
アルコキシドあるいはその重合体の加水分解反応が十分
に進行しないために、かえって撥水効果が劣化してしま
う。The addition amount of the titanium alkoxide or its polymer is preferably 5 to 10% by weight based on the polymer material in the protective layer coating material. If the addition amount of titanium alkoxide or its polymer is too small, a sufficient water repellency effect cannot be obtained. Further, if the amount is too large, the hydrolysis reaction of the titanium alkoxide or its polymer does not proceed sufficiently, so that the water repellent effect is rather deteriorated.
【００２８】なお、以上のような色素含有層３および保
護層４が形成される透明基板１は、通常の光情報記録媒
体に用いられているものが使用可能であり、例えば、ガ
ラス、ポリカーボネート（ＰＣ）、ポリエチレンテレフ
タレート（ＰＥＴ）等が挙げられる。As the transparent substrate 1 on which the dye-containing layer 3 and the protective layer 4 as described above are formed, those used in ordinary optical information recording media can be used, such as glass and polycarbonate ( PC), polyethylene terephthalate (PET) and the like.
【００２９】以上のような構成の光情報記録媒体では、
透明基板１側から照射された読み出し光ＬＢが透明基板
１／色素含有層３界面、色素含有層３／保護層４界面、
保護層／空気界面でそれぞれ反射し、多重干渉すること
を利用して信号再生が行われることとなる。In the optical information recording medium having the above structure,
Readout light LB emitted from the transparent substrate 1 side is transparent substrate 1 / dye-containing layer 3 interface, dye-containing layer 3 / protective layer 4 interface,
Signal reproduction is performed by utilizing multiple interferences that are reflected at the protective layer / air interface.
【００３０】[0030]
【作用】情報信号に対応する凹凸が形成された透明基板
上に、反射層が形成されてなる光情報記録媒体におい
て、反射層として色素材料が含有され、且つ反射率が１
５〜２５％の色素含有層を用いると、光磁気ディスク等
の反射率が１５〜２５％の媒体を対象とする記録再生装
置によって信号再生がなされるようになる。In an optical information recording medium in which a reflective layer is formed on a transparent substrate having irregularities corresponding to information signals, a dye material is contained as the reflective layer and the reflectance is 1
If a dye-containing layer of 5 to 25% is used, signal reproduction will be performed by a recording / reproducing apparatus for a medium having a reflectance of 15 to 25% such as a magneto-optical disk.
【００３１】そして、色素含有層の光透過率が１６％以
下とされると、信号再生時に粉塵等の付着物の影響を受
けない光情報記録媒体となる。これは、色素含有層の光
透過率が低いと、色素含有層／空気界面あるいは保護層
／空気界面からの反射が小さくなるため、該色素含有層
あるいは保護層表面に屈折率の高い粉塵等が付着しても
光の多重干渉自体に大きな乱れを生じさせないからであ
る。When the light transmittance of the dye-containing layer is 16% or less, the optical information recording medium is free from the influence of dust or other adhering substances during signal reproduction. This is because when the light transmittance of the dye-containing layer is low, the reflection from the dye-containing layer / air interface or the protective layer / air interface becomes small, so that dust or the like having a high refractive index is formed on the dye-containing layer or the protective layer surface. This is because even if they are attached, no large disturbance is caused in the multiple interference of light itself.
【００３２】また、色素含有層上に、シリコンワニスと
チタンアルコキシドあるいはその重合体とを含む保護層
用塗料を塗布して保護層を形成すると、シリコンワニス
の縮合反応により、耐傷性に優れた保護層となる。ま
た、チタンアルコキシドあるいはその重合体の加水分解
によってＴｉＯ2 が生成され、表面に撥水性を有する保
護層となる。Further, when a protective layer coating material containing a silicon varnish and a titanium alkoxide or a polymer thereof is applied onto the dye-containing layer to form a protective layer, the condensation reaction of the silicon varnish causes a protective layer with excellent scratch resistance. Become a layer. Further, TiO 2 is produced by hydrolysis of titanium alkoxide or its polymer, and it becomes a protective layer having water repellency on the surface.
【００３３】このような色素含有層および保護層を有す
る光情報記録媒体は、異物との多少の接触があっても傷
がついたり、摩耗したりせず、また、高湿環境下で操作
することがあっても、水滴による色素含有層の変質や劣
化が生じることがなく、さらに、粉塵の付着にも影響を
受けることなく、良好な再生特性が維持できる光情報記
録媒体となる。An optical information recording medium having such a dye-containing layer and a protective layer does not get scratched or abraded even if there is some contact with foreign matter, and is operated in a high humidity environment. In this case, the optical information recording medium can maintain good reproduction characteristics without being altered or deteriorated in the dye-containing layer due to water droplets and without being affected by dust adhesion.
【００３４】[0034]
【実施例】本発明の好適な実施例について実験結果に基
づいて説明する。EXAMPLES Preferred examples of the present invention will be described based on experimental results.
【００３５】先ず、光透過率がそれぞれ異なる実施例
１，２、比較例１〜３のサンプルディスクを作製し、こ
の光透過率と再生特性との関係を調べた。First, sample disks of Examples 1 and 2 and Comparative Examples 1 to 3 having different light transmittances were produced, and the relationship between the light transmittances and the reproducing characteristics was examined.
【００３６】実施例１ 本実施例においては、色素材料と光安定化剤を、色素材
料：光安定化剤＝１：０．２なる重量比で溶媒に溶解し
（重量比で１００）、色素含有層用塗料を調製した。な
お、色素材料、光安定化剤、溶媒としては以下のものを
用いた。 Example 1 In this example, a dye material and a light stabilizer were dissolved in a solvent at a weight ratio of dye material: light stabilizer = 1: 0.2 (100 by weight ratio) to obtain a dye. A coating material for the containing layer was prepared. The following materials were used as the dye material, the light stabilizer and the solvent.
【００３７】色素材料 ：化１に示したシアニン色素
（日本感光色素社製，商品名ＮＫ２４２１） 光安定化剤：化３に示した１重項酸素失活剤（日本化薬
社製，商品名ＩＲＧ−００３） 溶媒 ：３−ヒドロキシ−３−メチル−２−ブタノ
ン（東京化成工業社製） このようにして調製された色素含有層用塗料を予めピッ
ト部とランド部が形成された透明基板上にスピンコート
法にて塗布した後、乾燥して色素含有層を形成し、光デ
ィスクを作製した。これを実施例１のサンプルディスク
とする。Dye material: Cyanine dye shown in Chemical formula 1 (manufactured by Nippon Senshoku Co., Ltd., trade name NK2421) Light stabilizer: Singlet oxygen quencher shown in Chemical formula 3 (manufactured by Nippon Kayaku Co., trade name IRG-003) Solvent: 3-hydroxy-3-methyl-2-butanone (manufactured by Tokyo Kasei Kogyo Co., Ltd.) The pigment-containing layer coating material thus prepared is applied on a transparent substrate on which pits and lands have been formed in advance. Then, the dye-containing layer was formed by applying a spin coat method to the above and then dried to form an optical disc. This is a sample disk of Example 1.
【００３８】実施例２ 本実施例では、色素材料を異ならせた以外は実施例１と
同様にして、色素含有層用塗料を調製した。なお、色素
材料としては以下のものを用いた。 Example 2 In this example, a coating material for a dye-containing layer was prepared in the same manner as in Example 1 except that the dye material was changed. The following were used as the dye material.
【００３９】色素材料 ：化２に示したシアニン色素
（日本感光色素社製，商品名ＮＫ１２５） そして、これを実施例１と同様にして透明基板上に塗布
した後、乾燥して光ディスクを作製し、実施例２のサン
プルディスクを得た。Dye material: Cyanine dye shown in Chemical formula 2 (manufactured by Nippon Senshoku Co., Ltd., trade name NK125) and applied on a transparent substrate in the same manner as in Example 1 and dried to prepare an optical disk. A sample disk of Example 2 was obtained.
【００４０】比較例１ ここでは、高分子材料を添加して色素含有層用塗料を調
製した。 Comparative Example 1 Here, a polymer material was added to prepare a coating material for a dye-containing layer.
【００４１】具体的には、色素材料：高分子材料：光安
定化剤＝１：１：０．２なる重量比で溶媒に溶解し（重
量比で１００）、色素含有層用塗料を調製した。なお、
色素材料および光安定化剤としては、実施例２と同様の
ものを用い、高分子材料としては以下のものを用いた。Specifically, a pigment-containing layer coating material was prepared by dissolving in a solvent at a weight ratio of pigment material: polymer material: light stabilizer = 1: 1: 0.2 (100 by weight ratio). . In addition,
The same dye material and light stabilizer as in Example 2 were used, and the following polymer materials were used.
【００４２】高分子材料：化４に示したシリコンワニス
（信越シリコーン社製，商品名ＫＲ３１１） そして、これを実施例１と同様にして透明基板上に塗布
した後、乾燥して光ディスクを作製し、比較例１のサン
プルディスクを得た。Polymer material: Silicon varnish shown in Chemical formula 4 (manufactured by Shin-Etsu Silicone Co., Ltd., trade name KR311), and applied on a transparent substrate in the same manner as in Example 1 and dried to prepare an optical disk. A sample disk of Comparative Example 1 was obtained.
【００４３】比較例２ 本比較例では、色素材料を異ならせた以外は比較例１と
同様にして、高分子材料を添加して色素含有層用塗料を
調製した。なお、色素材料としては以下のものを用い
た。 Comparative Example 2 In this Comparative Example, a polymer material was added to prepare a dye-containing layer coating material in the same manner as in Comparative Example 1 except that the dye material was changed. The following were used as the dye material.
【００４４】色素材料 ：化６に示すシアニン色素（ソ
ニー社製，商品名ＳＲＣ８）Dye material: Cyanine dye shown in Chemical formula 6 (manufactured by Sony Corporation, trade name SRC8)
【００４５】[0045]
【化６】 [Chemical 6]
【００４６】そして、これを実施例１と同様にして透明
基板上に塗布した後、乾燥して光ディスクを作製し、比
較例２のサンプルディスクを得た。Then, this was applied on a transparent substrate in the same manner as in Example 1 and dried to prepare an optical disk, and a sample disk of Comparative Example 2 was obtained.
【００４７】比較例３ 本比較例では、色素材料を異ならせた以外は比較例１と
同様にして、高分子材料を添加して色素含有層用塗料を
調製した。なお、色素材料としては以下のものを用い
た。 Comparative Example 3 In this Comparative Example, a polymer material was added to prepare a coating material for a dye-containing layer in the same manner as in Comparative Example 1 except that the dye material was changed. The following were used as the dye material.
【００４８】色素材料 ：化７に示したシアニン色素
（日本感光色素社製，商品名ＮＫ２６７０）Dye material: Cyanine dye shown in Chemical formula 7 (product name NK2670, manufactured by Nippon Senshoku Co., Ltd.)
【００４９】[0049]
【化７】 [Chemical 7]
【００５０】そして、これを実施例１と同様にして透明
基板上に塗布した後、乾燥して光ディスクを作製し、比
較例３のサンプルディスクを得た。Then, this was coated on a transparent substrate in the same manner as in Example 1 and then dried to prepare an optical disc, and a sample disc of Comparative Example 3 was obtained.
【００５１】特性の評価 ここで、以上のようにして作製した実施例１，２、比較
例１〜３のサンプルディスクについて、光透過率を測定
した。具体的には、７８０ｎｍなる波長の光を用い、各
サンプルディスクの透明基板側から色素含有層側へ透過
する光の割合を、分光光度計（日立社製，商品名Ｕ−３
２１０）にて測定した。この結果を、各サンプルディス
クにおける色素含有層の構成材料と共に表１に示す。 Evaluation of Characteristics Here, the light transmittances of the sample disks of Examples 1 and 2 and Comparative Examples 1 to 3 produced as described above were measured. Specifically, using a light having a wavelength of 780 nm, the ratio of light transmitted from the transparent substrate side of each sample disk to the dye-containing layer side was measured by a spectrophotometer (Hitachi, trade name U-3).
210). The results are shown in Table 1 together with the constituent material of the dye-containing layer in each sample disk.
【００５２】[0052]
【表１】 [Table 1]
【００５３】次に、このように光透過率の異なる各サン
プルディスクについて、粉塵による再生特性の変化を調
べた。具体的には、各サンプルディスクの色素含有層上
に二酸化チタンの微粒子を散りばめ、この前後にＣ１，
Ｃ２エラーの値を調べた。なお、Ｃ１エラーとは、エラ
ー訂正回路におけるＣ１コードが、補正可能なランダム
エラーを訂正した回数を１秒間の平均値として示すもの
である。一方、Ｃ２エラーとは、エラー訂正回路におけ
るＣ２コードが、比較的大きな欠陥で補間が必要なエラ
ー（バーストエラー）を訂正した個数を示すものであ
る。ここでは、ＭＤアナライザー（ソニー・ディスク・
テクノロジ社製）を用いて、ＣＩＲＣ（クロス・インタ
ーリーブ・リードソロモン・コード）デコーダから出力
されるＣ１フラグ、Ｃ２フラグの回数を計測することに
より、Ｃ１，Ｃ２エラーを調べた。Next, with respect to each of the sample disks having different light transmittances as described above, the change of the reproduction characteristic due to the dust was examined. Specifically, fine particles of titanium dioxide are scattered on the dye-containing layer of each sample disk, and C1,
The value of C2 error was examined. The C1 error indicates the number of times the C1 code in the error correction circuit has corrected a correctable random error as an average value for 1 second. On the other hand, the C2 error indicates the number of C2 codes in the error correction circuit that have corrected an error (burst error) that requires interpolation due to a relatively large defect. Here, MD analyzer (Sony Disc
C1 and C2 errors were investigated by measuring the number of times of C1 flag and C2 flag output from a CIRC (Cross Interleave Reed-Solomon Code) decoder using Technology.
【００５４】各サンプルディスクについての測定結果を
表２に示す。Table 2 shows the measurement results for each sample disk.
【００５５】[0055]
【表２】 [Table 2]
【００５６】表２より、光透過率の高いサンプルディス
クほど、粉塵によってＣ１エラーレートが増加し、ま
た、回復不能を示すＣ２エラーも発生することがわか
る。これに対して、光透過率の低い実施例１，２のサン
プルディスクにおいては、粉塵によってＣ１エラーレー
トが上昇することも、Ｃ２エラーが発生することもなか
ったことがわかる。From Table 2, it can be seen that the higher the light transmittance of the sample disk, the higher the C1 error rate due to the dust, and the more the C2 error indicating that the recovery is impossible. On the other hand, in the sample disks of Examples 1 and 2 having a low light transmittance, it was found that the C1 error rate did not increase and the C2 error did not occur due to the dust.
【００５７】これより、光透過率を１６％以下とするこ
とにより、粉塵による再生特性の劣化を防止できること
がわかった。From this, it was found that the deterioration of the reproduction characteristic due to dust can be prevented by setting the light transmittance to 16% or less.
【００５８】次に、色素含有層上に保護膜を形成し、光
透過率のみならず、保護層の構成をも異ならせた実施例
３〜６、比較例４，５のサンプルディスクを作製し、そ
の特性を調べた。Next, a protective film was formed on the dye-containing layer to prepare sample disks of Examples 3 to 6 and Comparative Examples 4 and 5 in which not only the light transmittance but also the constitution of the protective layer was changed. , Its characteristics were investigated.
【００５９】実施例３ 本実施例においては、色素材料と光安定化剤を、色素材
料：光安定化剤＝１：０．２なる重量比で溶媒に溶解し
（重量比で１００）、色素含有層用塗料を調製した。な
お、色素材料、光安定化剤、溶媒としては以下のものを
用いた。 Example 3 In this example, a dye material and a light stabilizer were dissolved in a solvent at a weight ratio of dye material: light stabilizer = 1: 0.2 (100 by weight ratio) to obtain a dye. A coating material for the containing layer was prepared. The following materials were used as the dye material, the light stabilizer and the solvent.
【００６０】色素材料 ：化１に示したシアニン色素
（日本感光色素社製，商品名ＮＫ２４２１） 光安定化剤：化３に示した１重項酸素失活剤（日本化薬
社製，商品名ＩＲＧ−００３） 溶媒 ：３−ヒドロキシ−３−メチル−２−ブタノ
ン（東京化成工業社製） このようにして調製された色素含有層用塗料を予めピッ
ト部とランド部が形成された透明基板上にスピンコート
法にて塗布した後、乾燥して色素含有層を形成し、保護
層を設けることなく、光ディスクを作製した。これを実
施例３のサンプルディスクとする。Dye material: Cyanine dye shown in Chemical formula 1 (manufactured by Nippon Senshoku Co., Ltd., trade name NK2421) Light stabilizer: Singlet oxygen quencher shown in Chemical formula 3 (manufactured by Nippon Kayaku Co., trade name IRG-003) Solvent: 3-hydroxy-3-methyl-2-butanone (manufactured by Tokyo Kasei Kogyo Co., Ltd.) The pigment-containing layer coating material thus prepared is applied on a transparent substrate on which pits and lands have been formed in advance. Then, the dye-containing layer was formed by applying a spin coat method to the above, and the dye-containing layer was formed. This will be referred to as a sample disk of Example 3.
【００６１】実施例４ 本実施例では、実施例３と同様にして形成された色素含
有層上に高分子材料よりなる保護層を形成した。 Example 4 In this example, a protective layer made of a polymer material was formed on the dye-containing layer formed in the same manner as in Example 3.
【００６２】具体的には、高分子材料を溶媒に溶解し
（重量比で１００）、保護層用塗料を調製した。なお、
高分子材料および溶媒としては以下のものを用いた。Specifically, a polymeric material was dissolved in a solvent (100 by weight ratio) to prepare a coating material for a protective layer. In addition,
The following materials were used as the polymer material and the solvent.
【００６３】高分子材料：化４に示したシリコンワニス
（信越シリコーン社製，商品名ＫＲ３１１） 溶媒 ：キシレン（和光純薬社製） そして、色素含有層上に上記保護層用塗料を塗布した
後、乾燥させることによって保護層を形成して、実施例
４のサンプルディスクを得た。Polymer material: Silicon varnish shown in Chemical formula 4 (manufactured by Shin-Etsu Silicone Co., Ltd., trade name KR311) Solvent: Xylene (manufactured by Wako Pure Chemical Industries, Ltd.) Then, after coating the protective layer coating material on the dye-containing layer Then, a protective layer was formed by drying to obtain a sample disk of Example 4.
【００６４】実施例５ 本実施例では、実施例４にて示された保護層用塗料に添
加剤としてチタンアルコキシドを添加した。 Example 5 In this example, titanium alkoxide was added as an additive to the coating material for protective layer shown in Example 4.
【００６５】具体的には、チタンアルコキシドを、高分
子材料：添加剤＝１：０．０５なる重量比で添加した以
外は、実施例４と同様にして保護層用塗料を調製した。
なお、添加剤としては以下のものを用いた。Specifically, a protective layer coating material was prepared in the same manner as in Example 4 except that the titanium alkoxide was added in a weight ratio of polymeric material: additive = 1: 0.05.
The following additives were used.
【００６６】添加剤 ：化５にてＲ＝Ｃ3 Ｈ7 ，ｎ＝
１で示されるチタンアルコキシド（日本曹達社製，商品
名Ａｌ） そして、色素含有層上に上記保護層用塗料を塗布した
後、乾燥させることによって保護層を形成して、実施例
５のサンプルディスクを得た。Additive: R = C 3 H 7 , n =
1. Titanium alkoxide represented by 1 (manufactured by Nippon Soda Co., Ltd., trade name Al), and after coating the above-mentioned coating material for the protective layer on the dye-containing layer, the protective layer is formed by drying, and the sample disk of Example 5 is obtained. Got
【００６７】実施例６ 本実施例では、色素含有層に含有させる色素材料を異な
らせた以外は実施例５と同様にして光ディスクを作製し
た。 Example 6 In this example, an optical disc was prepared in the same manner as in Example 5 except that the dye material contained in the dye-containing layer was changed.
【００６８】具体的には、以下の色素材料を用いた以外
は実施例３と同様にして色素含有層用塗料を調製した。Specifically, a coating material for a dye-containing layer was prepared in the same manner as in Example 3 except that the following dye materials were used.
【００６９】色素材料 ：化２に示したシアニン色素
（日本感光色素社製，商品名ＮＫ１２５） そして、これを実施例３と同様にして透明基板上に塗布
し、乾燥させて色素含有層を形成した。さらに、この上
に実施例５と同様の保護層用塗料を塗布し、乾燥させる
ことによって保護層を形成して、実施例６のサンプルデ
ィスクを得た。Dye material: Cyanine dye shown in Chemical formula 2 (manufactured by Japan Photosensitive Dye Company, trade name NK125) and applied on a transparent substrate in the same manner as in Example 3 and dried to form a dye-containing layer. did. Further, the same protective layer coating material as in Example 5 was applied onto this and dried to form a protective layer, and a sample disk of Example 6 was obtained.
【００７０】比較例４ 本比較例では、色素含有層に含有させる色素材料を異な
らせた以外は実施例５と同様にして光ディスクを作製し
た。 Comparative Example 4 In this comparative example, an optical disk was produced in the same manner as in Example 5 except that the dye material contained in the dye-containing layer was changed.
【００７１】具体的には、以下の色素材料を用いた以外
は実施例３と同様にして色素含有層用塗料を調製した。Specifically, a coating material for a dye-containing layer was prepared in the same manner as in Example 3 except that the following dye materials were used.
【００７２】色素材料 ：化６に示したシアニン色素
（ソニー社製，商品名ＳＲＣ８） そして、これを実施例３と同様にして透明基板上に塗布
し、乾燥させて色素含有層を形成した。さらに、この上
に実施例５と同様の保護層用塗料を塗布し、乾燥させる
ことによって保護層を形成し、比較例４のサンプルディ
スクを得た。Dye material: The cyanine dye shown in Chemical formula 6 (manufactured by Sony Corporation, trade name SRC8) was applied on a transparent substrate in the same manner as in Example 3 and dried to form a dye-containing layer. Further, the same protective layer coating material as in Example 5 was applied onto this and dried to form a protective layer, and a sample disk of Comparative Example 4 was obtained.
【００７３】比較例５ 本比較例では、色素含有層に含有させる色素材料を異な
らせた以外は実施例５と同様にして光ディスクを作製し
た。 Comparative Example 5 In this comparative example, an optical disk was manufactured in the same manner as in Example 5 except that the dye material contained in the dye-containing layer was changed.
【００７４】具体的には、以下の色素材料を用いた以外
は実施例３と同様にして色素含有層用塗料を調製した。Specifically, a coating material for a dye-containing layer was prepared in the same manner as in Example 3 except that the following dye materials were used.
【００７５】色素材料 ：化７に示したシアニン色素
（日本感光色素社製，商品名ＮＫ２６７０） そして、これを実施例３と同様にして透明基板上に塗布
し、乾燥させて色素含有層を形成した。さらに、この上
に実施例５と同様の保護層用塗料を塗布し、乾燥させる
ことによって保護層を形成し、比較例４のサンプルディ
スクを得た。Dye material: Cyanine dye shown in Chemical formula 7 (manufactured by Nippon Senshoku Co., Ltd., trade name NK2670) and applied on a transparent substrate in the same manner as in Example 3 and dried to form a dye-containing layer. did. Further, the same protective layer coating material as in Example 5 was applied onto this and dried to form a protective layer, and a sample disk of Comparative Example 4 was obtained.
【００７６】特性の評価 ここで、以上のようにして作製した実施例３〜６、比較
例４，５のサンプルディスクについて、前述したと同様
な方法にて光透過率を測定した。この結果を、実施例３
〜６、比較例４，５のサンプルディスクの色素含有層お
よび保護層の構成材料と共に表３に示す。 Evaluation of Characteristics Here, the light transmittances of the sample disks of Examples 3 to 6 and Comparative Examples 4 and 5 produced as described above were measured by the same method as described above. The results are shown in Example 3.
.About.6 and the constituent materials of the dye-containing layer and the protective layer of the sample disks of Comparative Examples 4 and 5 are shown in Table 3.
【００７７】[0077]
【表３】 [Table 3]
【００７８】次に、このような各サンプルディスクにつ
いて、粉塵による再生特性の変化を調べた。具体的に
は、前述したと同様の方法にて、各サンプルディスクの
色素含有層上に二酸化チタンの微粒子を散りばめ、この
前後にＣ１，Ｃ２エラーの値を調べた。この測定結果を
表４に示す。Next, with respect to each of the above sample disks, changes in the reproduction characteristics due to dust were examined. Specifically, titanium dioxide fine particles were scattered on the dye-containing layer of each sample disk in the same manner as described above, and the C1 and C2 error values were examined before and after this. The measurement results are shown in Table 4.
【００７９】[0079]
【表４】 [Table 4]
【００８０】表４より、光透過率の高いサンプルディス
クほど、粉塵によってＣ１エラーレートが増加し、ま
た、回復不能を示すＣ２エラーも発生することがわか
る。これに対して、光透過率の低い実施例３〜６のサン
プルディスクにおいては、粉塵によってＣ１エラーレー
トが上昇することも、Ｃ２エラーが発生することもなか
ったことがわかる。It can be seen from Table 4 that the higher the light transmittance of the sample disk, the higher the C1 error rate due to the dust, and the more the C2 error indicating that the recovery is impossible. On the other hand, in the sample disks of Examples 3 to 6 having a low light transmittance, it was found that neither the C1 error rate increased nor the C2 error occurred due to the dust.
【００８１】次いで、各サンプルディスクに対して、傷
付試験と環境試験とを行った。なお、傷付試験として
は、振とう器によって傷が発生するか否かを調べ、環境
試験としては、６５℃９５％の高温高湿環境下に４日保
存し、その前後のエラーレートの変化を調べた。この結
果を表５に示す。Next, a scratch test and an environmental test were performed on each sample disk. In addition, as a scratch test, it is checked whether a shaker causes scratches, and as an environmental test, it is stored in a high temperature and high humidity environment of 65 ° C and 95% for 4 days, and the error rate changes before and after that. I checked. The results are shown in Table 5.
【００８２】[0082]
【表５】 [Table 5]
【００８３】表５より、保護層が形成されていない実施
例３のサンプルディスクにおいては、傷が発生してしま
っていることがわかる。また、チタンアルコキシドを添
加していない実施例３，４のサンプルディスクにおいて
は、保存によりＣ１エラーレートが大幅に増加するとと
もに、回復不能を示すＣ２エラーが発生していることが
わかる。From Table 5, it can be seen that the sample disc of Example 3 in which the protective layer was not formed had scratches. Further, in the sample disks of Examples 3 and 4 to which the titanium alkoxide was not added, it was found that the C1 error rate was significantly increased by the storage and the C2 error indicating the unrecoverability was generated.
【００８４】これより、光透過率を１６％以下とするの
みならず、保護層を設け、該保護層を形成時にチタンア
ルコキシドを添加することにより、耐傷性、耐湿性にも
優れた光ディスクとなることがわかった。From this, it is possible to obtain an optical disk excellent not only in light transmittance of 16% or less, but also in providing a protective layer and adding a titanium alkoxide at the time of forming the protective layer, which is excellent in scratch resistance and moisture resistance. I understand.
【００８５】なお、チタンアルコキシドあるいはその重
合体よりなる添加剤の添加量とＣ２エラーの発生個数と
の関係についても調べた。The relationship between the amount of the additive made of titanium alkoxide or its polymer and the number of C2 errors generated was also investigated.
【００８６】具体的には、保護層用塗料中の各添加剤の
量を、高分子材料に対して０〜２０重量％の範囲で変化
させた以外は、実施例５と同様にして光ディスクを作製
し、６５℃／９５％の恒温恒湿槽に４日間に保存後、Ｃ
２エラーの発生状況を調査した。この結果を図２に示
す。Specifically, an optical disk was prepared in the same manner as in Example 5 except that the amount of each additive in the protective layer coating material was changed within the range of 0 to 20% by weight with respect to the polymer material. It was prepared and stored in a constant temperature / humidity bath at 65 ° C / 95% for 4 days.
2 We investigated the occurrence of errors. The result is shown in FIG.
【００８７】また、図３には、添加剤としてＡ１０（化
５にてＲ＝Ｃ3 Ｈ7 ，ｎ＝１０で示される日本曹達社製
チタンアルコキシド重合体）を用いた場合、図４には、
添加剤としてＢ１（化５にてＲ＝Ｃ4 Ｈ9 ，ｎ＝１で示
される日本曹達社製チタンアルコキシド）を用いた場
合、図５には、添加剤としてＢ４（化５にてＲ＝Ｃ4 Ｈ
9 ，ｎ＝４で示される日本曹達社製チタンアルコキシド
重合体）を用いた場合、図６には、添加剤としてＢ１０
（化５にてＲ＝Ｃ4 Ｈ9 ，ｎ＝１０で示される日本曹達
社製チタンアルコキシド重合体）を用いた場合につい
て、各添加剤の添加量とＣ２エラーの発生率との関係を
示す。Further, in FIG. 3, when A10 (R = C 3 H 7 in Chemical formula 5, N = 10 titanium alkoxide polymer manufactured by Nippon Soda Co., Ltd.) was used as an additive, ,
When B1 (R = C 4 H 9 in Chemical Formula 5, titanium alkoxide manufactured by Nippon Soda Co., Ltd., represented by n = 1 in Chemical Formula 5) was used as an additive, FIG. C 4 H
9 , a titanium alkoxide polymer manufactured by Nippon Soda Co., Ltd. represented by n = 4) is used. In FIG.
The relationship between the addition amount of each additive and the occurrence rate of C2 error in the case of using (a titanium alkoxide polymer manufactured by Nippon Soda Co., Ltd. represented by R = C 4 H 9 and n = 10 in Chemical Formula 5) is shown. .
【００８８】図２〜図６より、Ｃ２エラーの発生率は、
チタンアルコキシドまたはその重合体よりなる添加剤の
添加量に依存しており、該添加量を５〜１０重量％の範
囲とすることでＣ２エラーの発生を抑えることができる
ことがわかる。From FIGS. 2 to 6, the rate of occurrence of C2 error is
It depends on the addition amount of the additive made of titanium alkoxide or its polymer, and it is understood that the C2 error can be suppressed by setting the addition amount in the range of 5 to 10% by weight.
【００８９】これより、チタンアルコキシドまたはその
重合体よりなる添加剤の添加量を調整することにより、
光ディスクの耐湿特性を改善できることがわかった。From this, by adjusting the addition amount of the titanium alkoxide or its polymer,
It was found that the humidity resistance of the optical disk can be improved.
【００９０】[0090]
【発明の効果】以上の説明からも明らかなように、本発
明を適用すると、光磁気ディスク等の低反射率媒体を対
象とする記録再生装置によって信号再生を行うことが可
能となり、且つ、粉塵等が付着しても良好な再生特性が
維持可能な光情報記録媒体が提供できる。As is apparent from the above description, when the present invention is applied, it becomes possible to perform signal reproduction by a recording / reproducing apparatus for a low-reflectance medium such as a magneto-optical disk, and dust. It is possible to provide an optical information recording medium capable of maintaining good reproduction characteristics even when the like adheres.
【００９１】また、色素含有層上に保護層を設けること
により、耐傷性を向上させることができ、チタンアルコ
キシドまたはその重合体を添加することにより、耐湿特
性を向上させることも可能となる。By providing a protective layer on the dye-containing layer, scratch resistance can be improved, and by adding a titanium alkoxide or a polymer thereof, it is also possible to improve moisture resistance.
【図１】本発明を適応した光情報記録媒体の一構成例を
示す要部概略断面図である。FIG. 1 is a schematic cross-sectional view of an essential part showing a configuration example of an optical information recording medium to which the present invention is applied.
【図２】添加剤Ａ１の添加量とＣ２エラーの発生回数の
関係を示す特性図である。FIG. 2 is a characteristic diagram showing the relationship between the amount of additive A1 added and the number of times a C2 error occurs.
【図３】添加剤Ａ１０の添加量とＣ２エラーの発生回数
の関係を示す特性図である。FIG. 3 is a characteristic diagram showing the relationship between the amount of additive A10 added and the number of times a C2 error occurs.
【図４】添加剤Ｂ１の添加量とＣ２エラーの発生回数の
関係を示す特性図である。FIG. 4 is a characteristic diagram showing the relationship between the amount of additive B1 added and the number of times a C2 error occurs.
【図５】添加剤Ｂ４の添加量とＣ２エラーの発生回数の
関係を示す特性図である。FIG. 5 is a characteristic diagram showing the relationship between the amount of additive B4 added and the number of occurrences of C2 error.
【図６】添加剤Ｂ１０の添加量とＣ２エラーの発生回数
の関係を示す特性図である。FIG. 6 is a characteristic diagram showing the relationship between the amount of additive B10 added and the number of occurrences of C2 errors.
１ 透明基板 ２ａ ピット部 ２ｂ ランド部 ３ 色素含有層 ４ 保護層 1 Transparent Substrate 2a Pit Part 2b Land Part 3 Dye-Containing Layer 4 Protective Layer
Claims (6)
明基板上に、色素材料が含有され、且つ反射率が１５〜
２５％である反射層が形成されてなる光情報記録媒体に
おいて、 前記反射層の光透過率が１６％以下であることを特徴と
する光情報記録媒体。1. A dye material is contained on a transparent substrate on which unevenness corresponding to an information signal is formed, and the reflectance is 15 to.
An optical information recording medium having a reflective layer of 25% formed thereon, wherein the reflective layer has a light transmittance of 16% or less.
１．８４以上であることを特徴とする請求項１記載の光
情報記録媒体。2. The optical information recording medium according to claim 1, wherein the real part n of the complex refractive index of the reflective layer is 1.84 or more.
する保護層が設けられてなることを特徴とする請求項１
または請求項２に記載の光情報記録媒体。3. The protective layer mainly comprising a polymer material is provided on the reflective layer.
Alternatively, the optical information recording medium according to claim 2.
ることを特徴とする請求項３記載の光情報記録媒体。4. The optical information recording medium according to claim 3, wherein the polymer material is a silicon varnish.
アルコキシドあるいはその重合体が添加されてなる塗料
が塗布されて形成されたものであることを特徴とする請
求項３または請求項４に記載の光情報記録媒体。5. The protective layer according to claim 3, wherein the protective layer is formed by applying a coating material obtained by adding titanium alkoxide or a polymer thereof to the polymer material. The optical information recording medium described.
合体の添加量は、前記塗料中の高分子材料に対して５〜
１０重量％であることを特徴とする請求項５記載の光情
報記録媒体。6. The titanium alkoxide or its polymer is added in an amount of 5 to 5 with respect to the polymer material in the paint.
The optical information recording medium according to claim 5, wherein the optical information recording medium is 10% by weight.