JPH08181174A - Tape for tab which has adhesive agent, and semiconductor device - Google Patents

Abstract

PURPOSE: To obtain a tape for TAB excellent in adhesion and resistance to chemicals, by making an adhesive agent layer contain xylene resin and polyamide resin as inevitable components which layer forms a laminate together with a protective film layer, on an organic insulating film having flexibility. CONSTITUTION: A tape for TAB which has adhesive agent is constituted of a laminate having an adhesive agent layer 2 and a protective film layer on an insulating film 1 having flexibility. The adhesive agent layer 2 contains xylene resin and polyamide resin as inevitable components. The xylene resin has reactive groups which are obtained by reacting formaldehyde with ortho or meta or para xylene derivatives or mixture of them, under acid catalyst. It is preferable for the polyamid resin to contain dimer acid. As to the compound ratio of xylene resin and polyamide resin, 30-80wt.% of xylene resin to 100wt.% of polyamide resin is preferable.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は半導体集積回路の実装方
法であるテープオートメーテッドボンディング（ＴＡ
Ｂ）方式に用いられる接着剤付きテープ（以下、ＴＡＢ
用テープと称する）およびそれを用いた半導体装置に関
する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a tape automated bonding (TA) method for mounting a semiconductor integrated circuit.
B) Tape with adhesive used in the system (hereinafter, TAB
Tape) and a semiconductor device using the same.

【０００２】[0002]

【従来の技術】通常のＴＡＢ用テープは、ポリイミドフ
ィルム等の可撓性を有する有機絶縁性フィルム上に、接
着剤層および保護フィルム層として離型性を有するポリ
エステルフィルム等を積層した３層構造より構成されて
いる。2. Description of the Related Art A conventional TAB tape has a three-layer structure in which a flexible organic insulating film such as a polyimide film is laminated with an adhesive layer and a polyester film having releasability as a protective film layer. It is composed of

【０００３】ＴＡＢ用テープは、スプロケットおよび
デバイス孔の穿孔、銅箔との熱ラミネート、パター
ン形成（レジスト塗布、エッチング、レジスト除去）、
スズまたは金−メッキ処理などの加工工程を経てＴＡ
Ｂテープ（パターンテープ）に加工される。図１にパタ
ーンテープの形状を示す。図２に本発明の半導体装置の
一態様の断面図を示す。パターンテープのインナーリー
ド部６を、半導体集積回路８の金バンプ１０に熱圧着
（インナーリードボンディング）し、半導体集積回路を
搭載する。次いで、封止樹脂９による樹脂封止工程を経
て半導体装置が作成される。このような半導体装置をテ
ープキャリアパッケージ（ＴＣＰ）型半導体装置と称す
る。ＴＣＰ型半導体装置は、他の部品を搭載した回路基
板等とアウターリード７を介して接続（アウターリード
ボンディング）され、電子機器への実装がなされる。TAB tape is used for sprocket and device hole punching, thermal lamination with copper foil, pattern formation (resist coating, etching, resist removal),
TA through a tin or gold-plating process
Processed into B tape (pattern tape). FIG. 1 shows the shape of the pattern tape. FIG. 2 shows a cross-sectional view of one embodiment of the semiconductor device of the present invention. The inner lead portion 6 of the pattern tape is thermocompression bonded (inner lead bonding) to the gold bump 10 of the semiconductor integrated circuit 8 to mount the semiconductor integrated circuit. Next, a semiconductor device is created through a resin sealing process using the sealing resin 9. Such a semiconductor device is called a tape carrier package (TCP) type semiconductor device. The TCP type semiconductor device is connected (outer lead bonding) to a circuit board or the like on which other components are mounted via outer leads 7 and mounted on an electronic device.

【０００４】最終的にＴＡＢ用テープの接着剤層は、パ
ッケージ内に残留するため、絶縁性、耐熱性、接着性が
要求される。近年電子機器の小型化、高密度化が進行す
るに伴い、ＴＡＢ方式における導体幅が非常に狭くなっ
てきており、高い接着強度を有する接着剤の必要性が高
まっている。しかし、かかる多数の工程において種々の
薬品にさらされるため、初期の接着強度とともに接着剤
の耐薬品性が高いことが非常に重要である。特に、レジ
スト剥離、金メッキ時のアルカリ、あるいはエッチン
グ、スズメッキ時の酸に対して接着力の低下が少ないこ
とは必須の特性である。Finally, since the adhesive layer of the TAB tape remains in the package, it is required to have insulation, heat resistance and adhesiveness. With the recent progress in downsizing and high density of electronic devices, the conductor width in the TAB method has become extremely narrow, and the need for an adhesive having high adhesive strength is increasing. However, since it is exposed to various chemicals in such a large number of steps, it is very important that the adhesive has high chemical resistance as well as initial adhesive strength. In particular, it is an essential property that the adhesive strength is less likely to decrease with respect to resist peeling, alkali during gold plating, or acid during etching or tin plating.

【０００５】このような観点から、従来のＴＡＢ用テー
プの接着剤層にはエポキシ樹脂および／またはフェノー
ル樹脂とポリアミド樹脂の混合組成物が主として用いら
れてきた。（特開平２−１４３４４７号公報、特開平３
−２１７０３５号公報等）。From such a viewpoint, a mixed composition of an epoxy resin and / or a phenol resin and a polyamide resin has been mainly used for the adhesive layer of the conventional TAB tape. (JP-A-2-143447, JP-A-3
-217035).

【０００６】[0006]

【発明が解決しようとする課題】しかし、上述の接着性
および接着力からみた耐薬品性において、従来のＴＡＢ
用テープは必ずしも十分とはいえない。たとえば、スズ
メッキ時に導体の下にメッキ液が侵入し、接着力が大き
く低下する場合がある。その場合、ボンディング等の後
工程で導体の剥離を生じ、集積回路、回路基板と接続で
きないことがある。However, in view of the above-mentioned adhesiveness and chemical resistance in view of the adhesive force, the conventional TAB is used.
Tape is not always sufficient. For example, the plating solution may penetrate under the conductor during tin plating, resulting in a large decrease in adhesive strength. In that case, the conductor may be peeled off in a post-process such as bonding, and it may not be possible to connect to the integrated circuit or the circuit board.

【０００７】本発明はこのような問題点を解決し、接着
性および耐薬品性に優れた新規なＴＡＢ用テープおよび
それを用いた半導体装置を提供することを目的とする。An object of the present invention is to solve the above problems and to provide a novel TAB tape having excellent adhesiveness and chemical resistance and a semiconductor device using the same.

【０００８】[0008]

【課題を解決するための手段】本発明者らは、上記の目
的を達成するためにＴＡＢ用テープの接着剤成分の化学
構造と金属に対する接着性および耐薬品性との関係を鋭
意検討した結果、キシレン樹脂とポリアミド樹脂をを巧
みに組み合わせることにより、接着性および耐薬品性に
優れたＴＡＢ用テープが得られることを見い出し、本発
明に至ったものである。Means for Solving the Problems In order to achieve the above-mentioned object, the present inventors have diligently studied the relationship between the chemical structure of the adhesive component of the TAB tape and the adhesiveness and chemical resistance to metal. It was found that a TAB tape excellent in adhesiveness and chemical resistance can be obtained by skillfully combining a xylene resin and a polyamide resin, and the present invention has been completed.

【０００９】すなわち、本発明は可撓性を有する絶縁性
フィルム上に、接着剤層および保護フィルム層を有する
積層体より構成され、該接着剤層がキシレン樹脂および
ポリアミド樹脂を必須成分として含むことを特徴とする
ＴＡＢ用接着剤付きテープおよびそれを用いた半導体装
置に関する。That is, the present invention comprises a laminate having an adhesive layer and a protective film layer on a flexible insulating film, and the adhesive layer contains xylene resin and polyamide resin as essential components. And a tape with an adhesive for TAB and a semiconductor device using the same.

【００１０】本発明で使用されるキシレン樹脂は、オル
ト、メタ、パラの各キシレン誘導体またはこれらの混合
物にホルムアルデヒドを酸触媒下で反応させて得られる
反応性基を有する樹脂である。本発明において、キシレ
ン樹脂をそのまま用いることは何等発明の効果を損なう
ものではないが、キシレン樹脂を、フェノール、アルキ
ル置換フェノール、ビスフェノールＦ、ビスフェノール
Ａ、ビスフェノールＳ、等のフェノール誘導体と反応さ
せて変性した変性キシレン樹脂を用いるとさらに良好で
ある。この場合、フェノール誘導体変性キシレン樹脂の
フェノール性水酸基当量は、好ましくは１２０以上、さ
らに好ましくは１４０以上である。フェノール性水酸基
当量が１２０未満の場合、純フェノール樹脂の構造に近
づくため、従来の接着剤と同様に接着性を向上させるこ
とができない。The xylene resin used in the present invention is a resin having a reactive group obtained by reacting ortho, meta, para para xylene derivatives or a mixture thereof with formaldehyde under an acid catalyst. In the present invention, the use of the xylene resin as it is does not impair the effects of the invention, but the xylene resin is modified by reacting it with a phenol derivative such as phenol, alkyl-substituted phenol, bisphenol F, bisphenol A and bisphenol S. It is even better to use the modified xylene resin. In this case, the phenolic hydroxyl group equivalent of the phenol derivative-modified xylene resin is preferably 120 or more, more preferably 140 or more. When the phenolic hydroxyl group equivalent is less than 120, the structure is close to that of a pure phenolic resin, and thus the adhesiveness cannot be improved like the conventional adhesives.

【００１１】本発明で使用されるポリアミド樹脂は、公
知の種々のものが使用できる。特に、接着剤層に可撓性
を持たせ、かつ低吸水率のため絶縁性にすぐれる、炭素
数が３６であるジカルボン酸（いわゆるダイマー酸）を
含むものが好適である。ダイマー酸を含むポリアミド樹
脂は、常法によるダイマー酸とジアミンの重縮合により
得られるが、この際にダイマー酸以外のアジピン酸、ア
ゼライン酸、セバシン酸等のジカルボン酸を共重合成分
として含有してもよい。ジアミンはエチレンジアミン、
ヘキサメチレンジアミン、ピペラジン、等の公知のもの
が使用でき、吸湿性、溶解性の点から２種以上の混合で
もよい。As the polyamide resin used in the present invention, various known ones can be used. In particular, those containing a dicarboxylic acid having 36 carbon atoms (so-called dimer acid), which has flexibility in the adhesive layer and has excellent insulating property due to low water absorption, are preferable. Polyamide resin containing dimer acid is obtained by polycondensation of dimer acid and diamine by a conventional method, at this time adipic acid other than dimer acid, azelaic acid, containing dicarboxylic acid such as sebacic acid as a copolymerization component. Good. Diamine is ethylenediamine,
Known materials such as hexamethylenediamine and piperazine can be used, and two or more kinds may be mixed in view of hygroscopicity and solubility.

【００１２】上記のキシレン樹脂とポリアミド樹脂との
配合割合は、ポリアミド樹脂１００重量部に対してキシ
レン樹脂５〜１００重量部、好ましくは３０〜８０重量
部である。キシレン樹脂が５重量部未満では耐熱性の低
下を招く。また、１００重量部を越えると接着性が低下
するので好ましくない。The mixing ratio of the xylene resin and the polyamide resin is 5 to 100 parts by weight, preferably 30 to 80 parts by weight, based on 100 parts by weight of the polyamide resin. If the amount of the xylene resin is less than 5 parts by weight, the heat resistance will be deteriorated. Further, if it exceeds 100 parts by weight, the adhesiveness is deteriorated, which is not preferable.

【００１３】本発明において、接着剤層に公知のエポキ
シ樹脂を添加することにより、一層接着性および耐薬品
性を向上させることができる。エポキシ樹脂は１分子内
に２個以上のエポキシ基を有するものであれば特に制限
されないが、ビスフェノールＦ、ビスフェノールＡ、ビ
スフェノールＳ、ジヒドロキシナフタレン等のジグリシ
ジルエーテル、エポキシ化フェノールノボラック、エポ
キシ化クレゾールノボラック、エポキシ化トリスフェニ
ロールメタン、エポキシ化テトラフェニロールエタン、
エポキシ化メタキシレンジアミン、等が挙げられる。エ
ポキシ樹脂の添加量はポリアミド樹脂１００重量部に対
して２０〜１００重量部、好ましくは４０〜７０重量部
である。In the present invention, by adding a known epoxy resin to the adhesive layer, the adhesiveness and chemical resistance can be further improved. The epoxy resin is not particularly limited as long as it has two or more epoxy groups in one molecule, but diglycidyl ethers such as bisphenol F, bisphenol A, bisphenol S, and dihydroxynaphthalene, epoxidized phenol novolac, epoxidized cresol novolac. , Epoxidized trisphenylol methane, epoxidized tetraphenylol ethane,
Epoxidized meta-xylene diamine, etc. are mentioned. The amount of the epoxy resin added is 20 to 100 parts by weight, preferably 40 to 70 parts by weight, based on 100 parts by weight of the polyamide resin.

【００１４】さらに、接着剤層にノボラック型フェノー
ル樹脂、レゾール型フェノール樹脂等の公知のフェノー
ル樹脂を含有してもよい。この場合、キシレン樹脂との
縮合により変性キシレン樹脂と同様の効果を得ることが
できる。フェノール樹脂の添加量はポリアミド樹脂１０
０重量部に対して５〜６０重量部であると好ましく、キ
シレン樹脂とフェノール樹脂を合計した樹脂分を基準と
したフェノール性水酸基当量は、１２０以上が好まし
い。Further, the adhesive layer may contain a known phenol resin such as novolac type phenol resin or resol type phenol resin. In this case, the same effect as the modified xylene resin can be obtained by condensation with the xylene resin. The amount of phenol resin added is polyamide resin 10
The amount is preferably 5 to 60 parts by weight with respect to 0 parts by weight, and the phenolic hydroxyl group equivalent based on the total resin content of the xylene resin and the phenol resin is preferably 120 or more.

【００１５】本発明の接着剤層にエポキシ樹脂、キシレ
ン樹脂およびフェノール樹脂の硬化剤および硬化促進剤
を添加することは何等制限されない。たとえば、芳香族
ポリアミン、三フッ化ホウ素トリエチルアミン錯体等の
三フッ化ホウ素のアミン錯体、２−アルキル−４−メチ
ルイミダゾール、２−フェニル−４−アルキルイミダゾ
ール等のイミダゾール誘導体、無水フタル酸、無水トリ
メリット酸等の有機酸、ジシアンジアミド、トリフェニ
ルフォスフィン等公知のものが使用できる。添加量はポ
リアミド樹脂１００重量部に対して０．１〜１０重量部
であると好ましい。There is no limitation to add a curing agent and a curing accelerator for epoxy resin, xylene resin and phenol resin to the adhesive layer of the present invention. For example, an aromatic polyamine, an amine complex of boron trifluoride such as boron trifluoride triethylamine complex, an imidazole derivative such as 2-alkyl-4-methylimidazole, 2-phenyl-4-alkylimidazole, phthalic anhydride, and trianhydride. Known organic acids such as organic acid such as meritic acid, dicyandiamide, triphenylphosphine can be used. The addition amount is preferably 0.1 to 10 parts by weight with respect to 100 parts by weight of the polyamide resin.

【００１６】以上の成分以外に、接着剤の特性を損なわ
ない範囲で酸化防止剤、イオン捕捉剤などの有機、無機
成分を添加することは何ら制限されるものではない。In addition to the above components, addition of organic or inorganic components such as an antioxidant and an ion scavenger is not limited to the extent that the characteristics of the adhesive are not impaired.

【００１７】本発明でいう可撓性を有する絶縁性フィル
ムとはポリイミド、ポリエステル、ポリフェニレンスル
フィド、ポリエーテルスルホン、ポリエーテルエーテル
ケトン、アラミド、ポリカーボネート、ポリアリレー
ト、等のプラスチックあるいはエポキシ樹脂含浸ガラス
クロス等の複合材料からなる厚さ２５〜１２５μのフィ
ルムであり、これらから選ばれる複数のフィルムを積層
して用いても良い。また必要に応じて、加水分解、コロ
ナ放電、低温プラズマ、物理的粗面化、易接着コーティ
ング処理等の表面処理を施すことができる。The flexible insulating film referred to in the present invention is a plastic such as polyimide, polyester, polyphenylene sulfide, polyether sulfone, polyether ether ketone, aramid, polycarbonate, polyarylate, or epoxy resin-impregnated glass cloth. A film having a thickness of 25 to 125 μm, which is made of the composite material, and a plurality of films selected from these may be laminated and used. If necessary, surface treatment such as hydrolysis, corona discharge, low temperature plasma, physical surface roughening, and easy adhesion coating treatment can be applied.

【００１８】本発明でいう保護フィルム層とは、銅箔を
熱ラミネートする前に接着剤面からＴＡＢ用テープの形
態を損なうことなく剥離できれば特に限定されないが、
たとえばシリコーンあるいはフッ素化合物のコーティン
グ処理を施したポリエステルフィルム、ポリオレフィン
フィルム、およびこれらをラミネートした紙が挙げられ
る。The protective film layer referred to in the present invention is not particularly limited as long as it can be peeled from the adhesive surface without impairing the form of the TAB tape before heat-laminating the copper foil,
Examples thereof include polyester films, polyolefin films, and papers laminated with these, which are coated with silicone or a fluorine compound.

【００１９】次にＴＡＢ用接着剤付きテープの製造方法
について説明する。Next, a method of manufacturing the adhesive tape for TAB will be described.

【００２０】可撓性を有する絶縁性フィルムに、上記接
着剤組成物を溶剤に溶解した塗料を塗布、乾燥する。接
着剤層の膜厚は１０〜２５μとなるように塗布すること
が好ましい。乾燥条件は、１００〜２００℃、１〜５分
である。溶剤は特に限定されないが、トルエン、キシレ
ン、クロルベンゼン等の芳香族系とメタノール、エタノ
ール、プロパノール等のアルコール系の混合が好適であ
る。このようにして得られたフィルムに保護フィルムを
ラミネートし、最後に３５〜１５８ｍｍ程度にスリット
する。A coating material prepared by dissolving the above adhesive composition in a solvent is applied to a flexible insulating film and dried. It is preferable to apply the adhesive layer so that the thickness thereof is 10 to 25 μm. The drying conditions are 100 to 200 ° C. and 1 to 5 minutes. The solvent is not particularly limited, but a mixture of an aromatic solvent such as toluene, xylene and chlorobenzene and an alcohol solvent such as methanol, ethanol and propanol is preferable. A protective film is laminated on the film thus obtained, and finally slit to about 35 to 158 mm.

【００２１】[0021]

【実施例】以下に実施例を挙げて本発明を説明するが、
本発明はこれらの実施例に限定されるものではない。実
施例の説明に入る前に評価方法について述べる。The present invention will be described below with reference to examples.
The present invention is not limited to these examples. The evaluation method will be described before the description of the examples.

【００２２】評価方法 （１）評価用サンプル作成方法 ＴＡＢ用接着剤付きテープサンプルに１８μの電解銅箔
を、１４０℃、１ｋｇ／ｃｍ^２の条件でラミネートし
た。続いてエアオーブン中で、８０℃、３時間、１００
℃、５時間、１５０℃、５時間の順次加熱処理を行な
い、銅箔付きＴＡＢ用テープを作成した。得られた銅箔
付きＴＡＢ用テープの銅箔面に常法によりフォトレジス
ト膜形成、エッチング、レジスト剥離を行ない、所定の
導体幅のパターンを作成した。Evaluation method (1) Method for preparing evaluation sample A tape sample with an adhesive for TAB was laminated with an electrolytic copper foil of 18 μ under the conditions of 140 ° C. and 1 kg / cm ² . Then, in an air oven, 80 ° C, 3 hours, 100
C., 5 hours, 150.degree. C., 5 hours were sequentially heat-treated to prepare a TAB tape with a copper foil. Photoresist film formation, etching, and resist stripping were performed on the copper foil surface of the obtained TAB tape with copper foil by a conventional method to create a pattern having a predetermined conductor width.

【００２３】（２）スズメッキ処理 耐薬品性評価のため、上記（１）の方法で得られたパタ
ーンを、ホウフッ酸系の無電解スズメッキ液に７０℃、
５分浸漬処理し、０．５μ厚のメッキを施した。(2) Tin Plating Treatment In order to evaluate chemical resistance, the pattern obtained by the above method (1) was applied to a borofluoric acid-based electroless tin plating solution at 70 ° C.
It was immersed for 5 minutes and plated with a thickness of 0.5 μm.

【００２４】（３）剥離強度 上記（１）および（２）の方法で得たサンプルを用い
て、導体を９０°方向に５０ｍｍ／min の速度で剥離
し、その際の剥離力を測定した。導体幅５０μおよび２
００μについて行なった。(3) Peel strength Using the samples obtained by the methods (1) and (2), the conductor was peeled in the 90 ° direction at a speed of 50 mm / min, and the peeling force at that time was measured. Conductor width 50μ and 2
It carried out about 00micro.

【００２５】実施例１ ポリアミド樹脂（ヘンケル白水（株）製、“マクロメル
ト”６９００）、エポキシ樹脂（油化シェルエポキシ
（株）製、“エピコート”８２８、エポキシ当量１８
６）、フェノール変性キシレン樹脂（三菱ガス化学
（株）製、“ニカノール”ＧＲＬ、フェノール性水酸基
当量１４０）、をそれぞれ表１の組成比となるように配
合し、濃度２０重量％となるようにメタノール／モノク
ロルベンゼン混合溶媒に３０℃で撹拌、混合して接着剤
溶液を作成した。この接着剤をバーコータで、厚さ２５
μのポリエチレンテレフタレートフィルム（東レ（株）
製”ルミラー”）に約１８μの乾燥厚さとなるように塗
布し，１００℃、１分および１６０℃で５分間の乾燥を
行ない、接着剤シートを作成した。さらに、得られた接
着剤シートを厚さ７５μのポリイミドフィルム（宇部興
産（株）製“ユーピレックス”７５Ｓ）に１２０℃、１
ｋｇ／ｃｍ^２の条件でラミネートしてＴＡＢ用接着剤付
きテープを作成した。特性を表１に示す。Example 1 Polyamide resin (Henkel Hakusui Co., Ltd., "Macromelt" 6900), epoxy resin (Yukaka Shell Epoxy Co., Ltd., "Epicoat" 828, epoxy equivalent 18
6), and phenol-modified xylene resin (manufactured by Mitsubishi Gas Chemical Co., Inc., "Nikanol" GRL, phenolic hydroxyl group equivalent 140), were compounded so as to have the composition ratios shown in Table 1 so that the concentration was 20% by weight. An adhesive solution was prepared by stirring and mixing in a mixed solvent of methanol / monochlorobenzene at 30 ° C. Apply this adhesive with a bar coater to a thickness of 25
μ polyethylene terephthalate film (Toray Industries, Inc.)
"Lumirror" manufactured by the present invention was applied to a dry thickness of about 18 μm and dried at 100 ° C. for 1 minute and 160 ° C. for 5 minutes to prepare an adhesive sheet. Furthermore, the obtained adhesive sheet was applied to a polyimide film having a thickness of 75 μ (“UPILEX” 75S manufactured by Ube Industries, Ltd.) at 120 ° C.
A tape with an adhesive for TAB was prepared by laminating under the condition of kg / cm ² . The characteristics are shown in Table 1.

【００２６】上記の手順で得られたＴＡＢ用接着剤付き
テープを用いて、前述の評価方法（１）および（２）と
同一の方法で半導体集積回路接続用の導体回路を形成
し、図１に示すパターンテープを得た。Using the adhesive tape for TAB obtained by the above procedure, a conductor circuit for connecting a semiconductor integrated circuit was formed by the same method as the above-described evaluation methods (1) and (2), and FIG. The pattern tape shown in was obtained.

【００２７】さらにこのパターンテープを用いて、４５
０℃，１分の条件でインナーリードボンディングを行な
い、半導体集積回路を接続した。しかるのちに、エポキ
シ系液状封止剤（北陸塗料（株）製“チップコート”１
３２０−６１７）で樹脂封止を行ない、半導体装置を得
た。図２は得られた半導体装置の断面を示したものであ
る。Further, using this pattern tape, 45
Inner lead bonding was performed at 0 ° C. for 1 minute to connect the semiconductor integrated circuit. Then, epoxy liquid encapsulant (“Chip coat” manufactured by Hokuriku Paint Co., Ltd. 1
320-617) and resin sealing was performed to obtain a semiconductor device. FIG. 2 shows a cross section of the obtained semiconductor device.

【００２８】実施例２〜４および比較例１〜２ 実施例１と同様の方法で、それぞれ表１に示した原料お
よび組成比で調合した接着剤を用いてＴＡＢ用接着剤付
きテープを得た。特性を表１に示す。Examples 2 to 4 and Comparative Examples 1 to 2 In the same manner as in Example 1, tapes with an adhesive for TAB were obtained using the adhesives prepared with the raw materials and the composition ratios shown in Table 1, respectively. . The characteristics are shown in Table 1.

【００２９】[0029]

【表１】 [Table 1]

【００３０】表１の実施例および比較例から本発明によ
り得られるＴＡＢ用接着剤付きテープは、接着性および
耐薬品性に優れることがわかる。From the examples and comparative examples in Table 1, it is understood that the adhesive tape for TAB obtained by the present invention is excellent in adhesiveness and chemical resistance.

【００３１】[0031]

【発明の効果】本発明は接着性および耐薬品性に優れた
新規なＴＡＢ用接着剤付きテープおよびそれを用いた半
導体装置を工業的に提供するものであり、本発明のＴＡ
Ｂ用接着剤付きテープによって高密度実装用の半導体装
置の信頼性および経済性を向上させることができる。INDUSTRIAL APPLICABILITY The present invention industrially provides a novel tape with an adhesive for TAB, which has excellent adhesiveness and chemical resistance, and a semiconductor device using the same.
The adhesive tape for B can improve the reliability and economy of the semiconductor device for high-density mounting.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明のＴＡＢ用接着剤付きテープを加工して
得られた、半導体集積回路搭載前のパターンテープの斜
視図。FIG. 1 is a perspective view of a pattern tape before being mounted with a semiconductor integrated circuit, which is obtained by processing a tape with an adhesive for TAB of the present invention.

【図２】本発明のＴＡＢ用接着剤付きテープを用いた半
導体装置の断面図。FIG. 2 is a sectional view of a semiconductor device using the adhesive tape for TAB of the present invention.

【符号の説明】[Explanation of symbols]

１ 可撓性を有する絶縁性フィルム ２ 接着剤 ３ スプロケット孔 ４ デバイス孔 ５ 半導体集積回路接続用の導体 ６ インナーリード部 ７ アウターリード部 ８ 半導体集積回路 ９ 封止樹脂 １０金バンプ １１保護膜 1 Flexible Insulating Film 2 Adhesive 3 Sprocket Hole 4 Device Hole 5 Conductor for Connecting Semiconductor Integrated Circuit 6 Inner Lead Part 7 Outer Lead Part 8 Semiconductor Integrated Circuit 9 Sealing Resin 10 Gold Bump 11 Protective Film

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.⁶ 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０９Ｊ 7/02 ＪＫＣ ＪＫＤ ＪＫＥ 161/18 ＪＥＭ 177/00 ＪＧＡ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. ⁶ Identification code Internal reference number FI Technical display area C09J 7/02 JKC JKD JKE 161/18 JEM 177/00 JGA

Claims (6)

【特許請求の範囲】[Claims] 【請求項１】可撓性を有する有機絶縁性フィルム上に、
接着剤層および保護フィルム層を有する積層体より構成
され、該接着剤層がキシレン樹脂およびポリアミド樹脂
を必須成分として含むことを特徴とするＴＡＢ用接着剤
付きテープ。1. An organic insulating film having flexibility,
An adhesive tape for TAB, comprising a laminate having an adhesive layer and a protective film layer, the adhesive layer containing a xylene resin and a polyamide resin as essential components. 【請求項２】接着剤層がエポキシ樹脂を含有することを
特徴とする請求項１記載のＴＡＢ用接着剤付きテープ。2. The adhesive tape for TAB according to claim 1, wherein the adhesive layer contains an epoxy resin. 【請求項３】キシレン樹脂が、フェノール誘導体変性キ
シレン樹脂であり、かつ該変性キシレン樹脂のフェノー
ル性水酸基当量が１２０以上であることを特徴とする請
求項１記載のＴＡＢ用接着剤付きテープ。3. The adhesive tape for TAB according to claim 1, wherein the xylene resin is a phenol derivative-modified xylene resin, and the phenolic hydroxyl group equivalent of the modified xylene resin is 120 or more. 【請求項４】ポリアミド樹脂が炭素数３６のジカルボン
酸を必須成分として含むことを特徴とする請求項１記載
のＴＡＢ用接着剤付きテープ。4. The adhesive tape for TAB according to claim 1, wherein the polyamide resin contains a dicarboxylic acid having 36 carbon atoms as an essential component. 【請求項５】接着剤層がフェノール樹脂を含有すること
を特徴とする請求項１記載のＴＡＢ用接着剤付きテー
プ。5. The adhesive tape for TAB according to claim 1, wherein the adhesive layer contains a phenol resin. 【請求項６】請求項１〜５記載のＴＡＢ用接着剤付きテ
ープを用いた半導体装置。6. A semiconductor device using the tape with an adhesive for TAB according to claim 1.