JPH0816792B2 - Image forming method - Google Patents
Image forming methodInfo
- Publication number
- JPH0816792B2 JPH0816792B2 JP2277617A JP27761790A JPH0816792B2 JP H0816792 B2 JPH0816792 B2 JP H0816792B2 JP 2277617 A JP2277617 A JP 2277617A JP 27761790 A JP27761790 A JP 27761790A JP H0816792 B2 JPH0816792 B2 JP H0816792B2
- Authority
- JP
- Japan
- Prior art keywords
- toner
- image forming
- forming method
- magnetic powder
- photoconductor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 [産業上の利用分野] 本発明は磁気ブラシクリーニング機構を有する新規な
画像形成方法に関する。The present invention relates to a novel image forming method having a magnetic brush cleaning mechanism.
[従来の技術] 電子写真複写方法の一つとして、感光体上に帯電、露
光により静電潜像を形成し、この静電潜像を磁気ブラシ
法により現像し、現像トナー像を普通紙等の転写シート
上に転写し、ついで定着して最終画像を得るいわゆるPP
C方式がよく知られている。前記感光体としては、一般
にSe、ZnO、マイラーで被覆されたCdS等の感光体や、ポ
リビニルカルバゾール、ポリ−N−ビニルカルバゾール
等の有機光導電体等が使用されている。[Prior Art] As one of electrophotographic copying methods, an electrostatic latent image is formed on a photoreceptor by charging and exposure, and the electrostatic latent image is developed by a magnetic brush method, and a developed toner image is formed on a plain paper or the like. The so-called PP that transfers the image to the transfer sheet of and then fixes it to obtain the final image
The C method is well known. As the photoconductor, a photoconductor such as Se, ZnO, CdS coated with Mylar, or an organic photoconductor such as polyvinylcarbazole or poly-N-vinylcarbazole is generally used.
上記の複写方式においては、従来から現像剤として鉄
粉、フェライト粉末などの磁性キャリアとトナーと称す
る着色樹脂粉末からなる二成分系の現像剤が使用されて
おり、この様な現像剤を構成するトナーには、流動性を
高めるため表面にシリカを添加することが一般的であ
る。しかしながら、シリカは空気中の水分を吸収しやす
く、湿度が高い環境下にあってはシリカを付着させたト
ナーの摩擦帯電量を低下させトナー飛散、画像品質の低
下、地カブリの増大およびトナー消費量の増大等の問題
を発生させていた。また、湿度が低い環境下にあって
は、トナー中の電荷を蓄積させ摩擦帯電量の上昇による
画像濃度の低下という問題があった。In the copying system described above, a two-component type developer consisting of a magnetic carrier such as iron powder or ferrite powder and a colored resin powder called toner has been used as a developer, which constitutes such a developer. It is common to add silica to the surface of the toner to improve the fluidity. However, silica easily absorbs moisture in the air, and in an environment with high humidity, the amount of triboelectricity of the toner to which silica is attached decreases, resulting in toner scattering, image quality deterioration, increased background fog, and toner consumption. This caused problems such as an increase in quantity. Further, in an environment where the humidity is low, there is a problem that the electric charge is accumulated in the toner and the image density is lowered due to the increase of the triboelectric charge amount.
そこで、シリカの他に酸化チタンのような導電性の表
面処理剤をトナーの表面に付着させトナー中の電荷の蓄
積を防止し、環境変化による画像濃度の変化をおさえる
ことが提案されている。Therefore, it has been proposed that, in addition to silica, a conductive surface treatment agent such as titanium oxide be attached to the surface of the toner to prevent the accumulation of electric charges in the toner and suppress the change in image density due to environmental changes.
しかしながら、酸化チタンをトナー表面に付着させる
とトナーが感光体表面に融着しやすくなり、感光体表面
にトナーが付着するいわゆるフィルミング現象の問題が
あった。However, when titanium oxide is attached to the surface of the toner, the toner is likely to be fused to the surface of the photoconductor, and there is a problem of so-called filming phenomenon in which the toner is attached to the surface of the photoconductor.
特に、同一の磁気ブラシで現像とクリーニングをおこ
ない、感光体ドラムが2回転する間に1回のコピーが得
られる複写方式(以下単に2回転1コピー方式という)
や特開昭64-84280号等に記載の現像とクリーニングを同
時におこなう画像形成装置においては、クリーニングブ
レードがないために転写不良のトナーが感光体上に残
り、感光体表面にフィルミングが発生しやすいという問
題を有していた。In particular, a copying method in which development and cleaning are performed with the same magnetic brush, and one copy can be obtained while the photosensitive drum makes two rotations (hereinafter simply referred to as two-rotation one-copy method).
In the image forming apparatus described in Japanese Patent Application Laid-Open No. 64-84280, which simultaneously performs development and cleaning, toner having transfer failure remains on the photoconductor due to lack of a cleaning blade, and filming occurs on the photoconductor surface. It had the problem of being easy.
[発明が解決しようとする課題] 本発明の目的は上述の従来技術の問題点を解消し、感
光体表面のトナーフィルミングのない磁気ブラシクリー
ニング機構を有する新規な画像形成方法を提供すること
にある。[Problems to be Solved by the Invention] An object of the present invention is to solve the above-mentioned problems of the prior art and to provide a novel image forming method having a magnetic brush cleaning mechanism without toner filming on the surface of a photoconductor. is there.
[課題を解決するための手段] 本発明の画像形成方法は、表面に静電潜像を有する感
光体に対向して、トナーとキヤリアからなる現像剤を磁
力により付着させ磁気ブラシを形成させた現像ロールを
配置し、該磁気ブラシで前記感光体表面を摺擦して前記
静電潜像を顕像化し、かつ感光体上の残存トナーをクリ
ーニングする方法において、前記トナーとして磁性粉、
シリカ及び酸化チタンからなる複合外添剤を表面に付着
させたトナーを用いたことを特徴とする画像形成方法で
ある。[Means for Solving the Problems] In the image forming method of the present invention, a magnetic brush is formed by magnetically adhering a developer consisting of toner and carrier to a photoconductor having an electrostatic latent image on its surface. In the method of disposing a developing roller, rubbing the surface of the photoconductor with the magnetic brush to visualize the electrostatic latent image, and cleaning the residual toner on the photoconductor, magnetic powder as the toner,
An image forming method is characterized in that a toner having a surface on which a composite external additive composed of silica and titanium oxide is adhered is used.
以下本発明の詳細を図面により説明する。 Hereinafter, details of the present invention will be described with reference to the drawings.
第1図は磁気ブラシクリーニング機構を有する画像形
成方法の1例である2回転1コピー方式の複写システム
を説明するための概略図である。FIG. 1 is a schematic diagram for explaining a two-rotation, one-copy type copying system which is an example of an image forming method having a magnetic brush cleaning mechanism.
第1図において、感光体ドラム1は図示矢印方向に回
転しており、その周囲にはコロナ帯電器2、光学系3、
現像装置4、コロナ転写器5および除電手段9が配置さ
れている。まず感光体ドラム1の表面をコロナ帯電器2
により一様に帯電しついで光学系3により露光して静電
潜像(図示せず)が形成される。次に現像装置4により
静電潜像を顕像化して現像トナー像6を得る。得られた
トナー像6の上に転写シート7を重ね、その裏面からコ
ロナ転写器5により転写電界を印加して、トナー像6を
転写シート7上に転写し、ついで定着装置8により定着
して最終画像が得られる。転写後の感光体ドラム1の表
面は2回目の回転の時に現像装置4により形成された磁
気ブラシで摺擦されてクリーニングされる。なお、通常
の複写機では、クリーニング性を向上させるためにコロ
ナ転写器5とコロナ帯電器2の間に交流コロナ帯電器お
よび/又はランプなどの除電手段9を設けている。In FIG. 1, the photosensitive drum 1 is rotating in the direction of the arrow in the figure, and the corona charger 2, the optical system 3, and the
A developing device 4, a corona transfer device 5, and a charge eliminating means 9 are arranged. First, the surface of the photoconductor drum 1 is corona charger 2
Are uniformly charged and then exposed by the optical system 3 to form an electrostatic latent image (not shown). Next, the electrostatic latent image is visualized by the developing device 4 to obtain a developed toner image 6. The transfer sheet 7 is superposed on the obtained toner image 6, and a transfer electric field is applied from the back surface of the transfer sheet 7 by the corona transfer device 5 to transfer the toner image 6 onto the transfer sheet 7, and then is fixed by the fixing device 8. The final image is obtained. After the transfer, the surface of the photosensitive drum 1 is rubbed and cleaned by the magnetic brush formed by the developing device 4 during the second rotation. In an ordinary copying machine, an AC corona charger and / or a discharging means 9 such as a lamp is provided between the corona transfer device 5 and the corona charger 2 in order to improve the cleaning property.
上記の複写システムにおいて、本発明者等が種々検討
した結果、トナー表面に磁性粉と共にシリカと酸化チタ
ンとを付着させることにより感光体上にトナーフィルミ
ングがなく良好なクリーニング性が得られ、かつ環境依
存性が解消された。この結果は、酸化チタンがトナーの
摩擦帯電量を安定させ、酸化チタンによるフィルミング
の問題に対しては、磁性粉がドラム上に付着したトナー
を削り落とすためと考える。In the above copying system, as a result of various studies by the present inventors, by adhering silica and titanium oxide together with magnetic powder on the toner surface, toner filming on the photosensitive member can be obtained and good cleaning property can be obtained, and Environmental dependence has been eliminated. This result is considered to be because titanium oxide stabilizes the triboelectric charge amount of the toner, and the filming problem due to titanium oxide is caused by the magnetic powder scraping off the toner adhering to the drum.
次に本発明を構成するトナーについて説明する。 Next, the toner constituting the present invention will be described.
本発明のトナーは結着樹脂、着色剤、電荷制御剤等を
混合し、溶融混練後、粉砕分級してトナーを作製した
後、該トナーと後述する磁性粉、シリカ、および酸化チ
タンからなる複合外添剤とをタービン型攪拌機、ヘンシ
ェルミキサー、スーパーミキサーなどの一般的な攪拌機
によって攪拌し、トナーの表面に磁性粉、シリカおよび
酸化チタンを付着せしめるものである。The toner of the present invention is prepared by mixing a binder resin, a colorant, a charge control agent, etc., melt-kneading, and pulverizing and classifying the toner to prepare a toner, which is a composite of the magnetic powder, silica, and titanium oxide described below. The external additive is agitated by a general agitator such as a turbine type agitator, a Henschel mixer, a super mixer and the like, so that the magnetic powder, silica and titanium oxide are attached to the surface of the toner.
結着樹脂としてはスチレン系樹脂、スチレン−アクリ
ル系樹脂、スチレン−ブタジエン系樹脂、エポキシ樹
脂、ポリエステル樹脂等が使用できる。着色剤としては
カーボンブラック、アニリンブルー、クロームイエロ
ー、ウルトラマリンブルー、マラカイトグリーンオキザ
レート等が使用できる。電荷制御剤としては、例えば正
荷電性のニグロシン系染料や負荷電性の含金属染料が使
用できる。また、定着助剤の低分子量ポリプロピレン等
を含有させてもよい。As the binder resin, styrene resin, styrene-acrylic resin, styrene-butadiene resin, epoxy resin, polyester resin and the like can be used. Carbon black, aniline blue, chrome yellow, ultramarine blue, malachite green oxalate and the like can be used as the colorant. As the charge control agent, for example, a positively charged nigrosine dye or a negatively charged metal-containing dye can be used. Further, a low molecular weight polypropylene or the like as a fixing aid may be contained.
本発明の磁性粉としては、鉄、コバルト、ニッケル、
マンガン、亜鉛等の化合物であるマグネタイト、マグヘ
マイト、フェライト等であって、具体的にはEPT-500
(戸田工業社製)、KBN-400(関東電化工業社製)等が
ある。また、磁性粉の形状は、磁性粉がトナーから離脱
した場合に感光体を傷つけないため、8面体のものが好
ましい。トナーの表面に付着させる磁性粉の添加量は、
感光体上のフィルミングを効果的に削り落とすため、及
びトナーの表面から磁性粉を離脱させないためにトナー
100重量部に対して磁性粉0.01〜3重量部が好ましい。
シリカとしては、疎水性シリカ微粉末が好適であり、具
体的にはアエロジルR-972(日本アエロジル社製)、タ
ラノックス500(デグサ社製)等がある。また、酸化チ
タンとしてはMT-600BS(テイカ社製)等の疎水性酸化チ
タンが好ましい。The magnetic powder of the present invention includes iron, cobalt, nickel,
Compounds such as manganese and zinc such as magnetite, maghemite, ferrite, etc., specifically EPT-500
(Made by Toda Kogyo), KBN-400 (made by Kanto Denka Kogyo), etc. Further, the shape of the magnetic powder is preferably an octahedron so that the photosensitive member is not damaged when the magnetic powder is separated from the toner. The amount of magnetic powder added to the surface of the toner is
To effectively remove the filming on the photoconductor and to prevent the magnetic powder from separating from the surface of the toner, the toner
The magnetic powder is preferably 0.01 to 3 parts by weight per 100 parts by weight.
Hydrophobic silica fine powder is suitable as the silica, and specific examples thereof include Aerosil R-972 (manufactured by Nippon Aerosil Co., Ltd.) and Taranox 500 (manufactured by Degussa). As the titanium oxide, hydrophobic titanium oxide such as MT-600BS (manufactured by Teika) is preferable.
本発明を構成するキャリアは、一般にトナー用キャリ
アとして使用されるものが使用可能であって、具体的に
は鉄粉系キャリア、フェライト系キャリアがいずれも使
用でき、またこれらを芯物質としてポリエステル系樹
脂、フッ素系樹脂、アクリル系樹脂、シリコーン系樹脂
等をその表面に被覆した樹脂コートキャリアまたは鉄粉
やフェライトを結着樹脂に混練して造粒したいわゆる樹
脂キャリアも使用可能である。As the carrier constituting the present invention, those generally used as a carrier for toner can be used, and specifically, an iron powder type carrier and a ferrite type carrier can both be used, and a polyester type carrier using these as a core substance. It is also possible to use a resin-coated carrier whose surface is coated with a resin, a fluorine-based resin, an acrylic resin, a silicone-based resin or the like, or a so-called resin carrier in which iron powder or ferrite is kneaded into a binder resin and granulated.
[実施例] 以下、本発明の実施例について説明する。[Examples] Examples of the present invention will be described below.
スチレン−アクリル共重合体樹脂 85重量部 (三洋化成工業社製TB-1000) カーボンブラック 10重量部 (デグサ社製PRINTEX-L) クロム含金属染料 2重量部 (オリエント化学社製ボントロンS-34) ポリプロピレンワックス 3重量部 (三洋化成工業社製ビスコール330P) 上記の材料を溶融混練した後、粉砕分級し、平均粒子
10μmのトナーを得た。このトナー100重量部に対して
第1表のような磁性粉、シリカ及び酸化チタンからなる
複合外添剤をヘンシェルミキサーを用いて混合し、トナ
ー表面に付着させた。なお、第1表中のEPT-500(戸田
工業社製)は8面体構造を有し、KBN-400(関東電化工
業社製)は針状構造を有するものである。Styrene-acrylic copolymer resin 85 parts by weight (SANYO Kasei Co., Ltd. TB-1000) Carbon black 10 parts by weight (Degussa PRINTEX-L) Chromium metal dye 2 parts by weight (Orient Chemical Co., Ltd. Bontron S-34) Polypropylene wax 3 parts by weight (Viscole 330P, manufactured by Sanyo Kasei Co., Ltd.) The above materials were melt-kneaded and then pulverized and classified to obtain an average particle size.
A toner of 10 μm was obtained. To 100 parts by weight of this toner, a composite external additive composed of magnetic powder, silica and titanium oxide as shown in Table 1 was mixed using a Henschel mixer and made to adhere to the toner surface. EPT-500 (made by Toda Kogyo Co., Ltd.) in Table 1 has an octahedral structure, and KBN-400 (made by Kanto Denka Kogyo Co., Ltd.) has a needle-shaped structure.
次に前記各トナー3部とノンコートフェライトキャリ
ア97部とを混合して現像剤を作製し、2回転1コピー方
式の複写システムをもつ複写機に設置して、低温低湿
(10℃,10%RH)及び高温高湿(30℃,85%RH)の各環境
下において1万枚までの複写評価をおこなった。1万枚
後の評価結果を第2表に示した。第2表中の画像濃度は
マクベス反射濃度計で測定し、フィルミングは低温低湿
1万枚と高温高湿1万枚合わせて2万枚複写後の感光体
を目視にて評価した。また、画像濃度、フィルミングの
評価結果から総合的に評価した項目を第2表に付した。 Next, 3 parts of each of the toners and 97 parts of non-coated ferrite carrier are mixed to prepare a developer, which is installed in a copying machine having a two-rotation, one-copy type copying system, and the temperature and humidity are low (10 ° C, 10% RH). ) And high temperature and high humidity (30 ° C., 85% RH) environment, copying evaluation was performed up to 10,000 sheets. The evaluation results after 10,000 sheets are shown in Table 2. The image densities shown in Table 2 were measured with a Macbeth reflection densitometer, and filming was performed by visually observing the photoconductor after copying 20,000 low-temperature low-humidity 10,000 sheets and high-temperature high-humidity 10,000 sheets. In addition, Table 2 shows the items comprehensively evaluated from the evaluation results of the image density and the filming.
第2の評価結果から明らかなように本発明の画像形成
方法に基づく実施例1〜6は低温低湿環境及び高温高湿
環境において安定した画像濃度を有しており、感光体へ
のフィルミングも発生していなかった。一方、比較例
1、比較例2及び比較例6については低温低湿環境での
画像濃度が著しく低下した。また比較例3〜5について
は感光体へのフィルミングが発生し、実用上支障をきた
すものであった。 As is clear from the second evaluation result, Examples 1 to 6 based on the image forming method of the present invention have a stable image density in a low temperature and low humidity environment and a high temperature and high humidity environment, and filming on the photoconductor is also possible. It did not occur. On the other hand, in Comparative Example 1, Comparative Example 2 and Comparative Example 6, the image density in the low temperature and low humidity environment was significantly reduced. Further, in Comparative Examples 3 to 5, filming on the photoconductor occurred, which was a problem in practical use.
[発明の効果] 以上説明したように本発明は、磁性粉、シリカおよび
酸化チタンからなる複合外添剤を表面に付着させたトナ
ーを磁気ブラシクリーニング機構を有する複写システム
に用いたため、温度、湿度に関係がなく安定した画像濃
度とフィルミングの問題がない画像形成方法を提供する
ことができる。EFFECTS OF THE INVENTION As described above, according to the present invention, the toner having the composite external additive composed of magnetic powder, silica and titanium oxide adhered to the surface thereof is used in the copying system having the magnetic brush cleaning mechanism. It is possible to provide a stable image density and an image forming method free from the problem of filming regardless of the above.
第1図は2回転1コピー方式の複写システムを説明する
ための概略図である。 1……感光体ドラム、4……現像装置、7……転写シー
ト、8……定着装置。FIG. 1 is a schematic diagram for explaining a two-rotation one-copy type copying system. 1 ... Photosensitive drum, 4 ... Developing device, 7 ... Transfer sheet, 8 ... Fixing device.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 FI 技術表示箇所 G03G 15/09 Z 21/10 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 6 Identification code Office reference number FI technical display location G03G 15/09 Z 21/10
Claims (3)
て、トナーとキャリアからなる現像剤を磁力により付着
させ磁気ブラシを形成させた現像ロールを配置し、該磁
気ブラシで前記感光体表面を摺擦して前記静電潜像を顕
像化し、かつ感光体上の残存トナーをクリーニングする
方法において、前記トナーとして磁性粉、シリカ及び酸
化チタンからなる複合外添剤を表面に付着させたトナー
を用いたことを特徴とする画像形成方法。1. A developing roll having a magnetic brush formed by magnetically adhering a developer consisting of toner and a carrier is arranged facing a photoconductor having an electrostatic latent image on the surface thereof, and the magnetic brush is used for the photosensitization. In the method of rubbing the body surface to visualize the electrostatic latent image and cleaning the residual toner on the photoreceptor, a composite external additive composed of magnetic powder, silica and titanium oxide is attached to the surface as the toner. An image forming method, characterized in that the used toner is used.
を特徴とする請求項1記載の画像形成方法。2. The image forming method according to claim 1, wherein the magnetic powder has an octahedral structure.
対して0.01〜3重量部であることを特徴とする請求項1
記載の画像形成方法。3. The amount of the magnetic powder added is 0.01 to 3 parts by weight with respect to 100 parts by weight of the toner.
The image forming method described.