JPH08142492A - Production of image recording material - Google Patents
Production of image recording materialInfo
- Publication number
- JPH08142492A JPH08142492A JP6289930A JP28993094A JPH08142492A JP H08142492 A JPH08142492 A JP H08142492A JP 6289930 A JP6289930 A JP 6289930A JP 28993094 A JP28993094 A JP 28993094A JP H08142492 A JPH08142492 A JP H08142492A
- Authority
- JP
- Japan
- Prior art keywords
- image
- layer
- receiving layer
- thin film
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は画像記録体作成方法に関
し、更に詳しくは、種々の基材上に高品質の画像を形成
できる画像記録体作成方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing an image recording medium, and more particularly to a method for producing an image recording medium capable of forming high quality images on various substrates.
【０００２】[0002]
【従来の技術】従来から、ハードコピーを得る方法とし
ては、熱転写記録、電子写真、インクジェット等による
記録方法が検討されている。例えば熱転写方式では、支
持体上に熱溶融性インク層を有する転写シートを感熱ヘ
ッドにより加熱して、熱溶融性インク層からインクを受
像シート上に溶融転写させたり、支持体上に熱拡散性色
素を含有するインク層を有するインクシートを感熱ヘッ
ドにより加熱して、インク層から熱拡散性色素を受像シ
ートに熱拡散することにより画像記録体が作成されてい
る。2. Description of the Related Art Conventionally, as a method for obtaining a hard copy, a recording method by thermal transfer recording, electrophotography, ink jet or the like has been studied. For example, in the thermal transfer method, a transfer sheet having a heat-meltable ink layer on a support is heated by a thermal head to melt-transfer the ink from the heat-meltable ink layer onto an image-receiving sheet, or a heat diffusion property on the support. An image recording medium is prepared by heating an ink sheet having a dye-containing ink layer with a thermal head to thermally diffuse the heat diffusing dye from the ink layer to the image receiving sheet.
【０００３】この際、用いられる受像シートとしては、
前者では表面平滑性を良好にするための受像層、後者で
は熱拡散性色素に対して染着性のある樹脂を含有する受
像層を、それぞれ設けた専用の受像シートが用いられて
いる。At this time, as an image receiving sheet used,
In the former case, a dedicated image-receiving sheet is used which is provided with an image-receiving layer for improving the surface smoothness, and in the latter case, an image-receiving layer containing a resin having a dyeing property for a heat diffusible dye.
【０００４】又、インクジェット方式に用いられる受像
シートにおいても、インクの吸着力が有り、かつ滲みを
生じないことが必要なため、基材の上に受像層を設けた
専用紙が一般には用いられている。Further, even in the image receiving sheet used in the ink jet system, it is necessary that the sheet has an ink adsorbing power and does not cause bleeding. Therefore, a dedicated paper having an image receiving layer on a substrate is generally used. ing.
【０００５】このような記録に用いられる専用紙は、色
むら防止、ドット再現性、鮮鋭性、階調性、転写濃度な
どの特性を十分確保できる様に工夫されているが、半
面、一般にコストが高く、又、近年要求が高い、普通紙
などの基材に画像を形成させることはできなかった。The special paper used for such recording is devised so that characteristics such as color unevenness prevention, dot reproducibility, sharpness, gradation and transfer density can be sufficiently secured, but on the other hand, it is generally costly. However, it has not been possible to form an image on a base material such as plain paper, which is highly demanded in recent years.
【０００６】上記欠点を改善するために、前記熱拡散転
写方式では、特開昭59-109393号、同59-198196号、同60
-222267号、同61-83094号、同61-84281号、同61-86289
号、同61-139490号、同62-297184号、同63-56496号、同
63-17089号、同63-237994号、同64-1590号、同64-72893
号、同64-87390号、特開平1-125282号、同1-160682号、
同1-166972号、同1-225591号、同2-63892号、同2-12294
6号、同3-234592号、同4-323086号、同4-336287号等で
は、専用の受像紙を用いるのではなく、被転写体上へ受
像層転写材から受像層を転写した後、その被転写体上に
設けた受像層上に画像記録を行い画像記録体を作成して
いる。In order to improve the above-mentioned drawbacks, the above thermal diffusion transfer method is used in JP-A-59-109393, 59-198196 and 60.
-222267, 61-83094, 61-84281, 61-86289
No. 61, No. 61-139490, No. 62-297184, No. 63-56496, No.
63-17089, 63-237994, 64-1590, 64-72893
No. 64-87390, JP-A 1-125282, 1-160682,
1-141, 1-225591, 2-63892, 2-12294
No. 6, No. 3-234592, No. 4-323086, No. 4-336287, etc., instead of using a dedicated image-receiving paper, after transferring the image-receiving layer from the image-receiving layer transfer material onto the transferred material, An image is recorded on the image receiving layer provided on the transferred material to form an image recording material.
【０００７】しかしながら、受像層転写材の工夫、記録
方法の工夫などにも拘わらず、基材の表面性や基材表面
への隠蔽性が不十分であることから、専用紙を用いた画
像記録体に匹敵する画像を得ることは困難であった。However, despite the fact that the image-receiving layer transfer material is devised and the recording method is devised, since the surface property of the base material and the hiding property on the surface of the base material are insufficient, image recording using special paper is carried out. It was difficult to get an image comparable to the body.
【０００８】一方、電子写真方式では、熱転写方式やイ
ンクジェット方式のように専用受像紙ではなく、普通紙
やＯＨＰシートなど一般に用いられる基材に記録するこ
とができると言う利点を有している。On the other hand, the electrophotographic system has an advantage that it can be recorded on a commonly used base material such as plain paper or OHP sheet instead of a dedicated image receiving paper unlike the thermal transfer system or the ink jet system.
【０００９】ところで、基材として専用受像紙を用いる
熱転写方式やインクジェット方式、普通紙などの基材を
用いる電子写真方式、何れにおいても、下地が着色して
いたり、印刷が施されている基材の場合には、転写させ
る画像の種類や、インク層から転写させる、ノズルから
噴射させる、或いはトナーを静電圧着させて画像を形成
する際に用いられる顔料、染料、色素によって、十分な
コントラストが得られなかったり、隠蔽性が不十分なこ
とに起因する色濁りなどが生じる場合が多かった。By the way, in any of the thermal transfer method using a dedicated image receiving paper as a base material, the ink jet method, and the electrophotographic method using a base material such as plain paper, the base material is colored or printed. In this case, a sufficient contrast can be obtained depending on the type of image to be transferred, the transfer from the ink layer, the ejection from the nozzle, or the pigment, dye, or pigment used when electrostatically pressing the toner to form an image. In many cases, it was not obtained or color turbidity or the like was caused due to insufficient hiding property.
【００１０】[0010]
【発明が解決しようとする課題】本発明は前記の事情に
基づいて為されたものである。即ち、本発明の目的は、
表面性が劣っていたり印刷などが施されている基材上
に、画像形成される領域において画像形成部の切れがよ
く、色むらがなく、かつ隠蔽性に優れた画像記録を行う
のに好適な画像記録体作成方法を提供することにある。The present invention has been made based on the above circumstances. That is, the object of the present invention is to
It is suitable for performing image recording on a substrate with poor surface properties or printing, where the image forming area is well cut in the area where the image is formed, there is no color unevenness, and the hiding property is excellent. Another object of the present invention is to provide a method for creating an image recording material.
【００１１】[0011]
【課題を解決するための手段】本発明者らは鋭意、検討
した結果、下記構成により前記課題を解決できることを
見い出した。即ち、 (１)支持体上に顔料層、金属薄膜層の順に積層された顔
料層・金属薄膜層転写材料を用いて、基材上に金属薄膜
層付き顔料層を熱転写した後、支持体上に受像層を備え
た受像層転写材料と対面させ、熱エネルギーを与えて顔
料層上に受像層を転写し、次いで該受像層上に画像形成
を行う画像記録体作成方法。As a result of earnest studies, the present inventors have found that the above problems can be solved by the following constitution. That is, (1) a pigment layer and a metal thin film layer transfer material, in which a pigment layer and a metal thin film layer are laminated in this order on a support, are used to thermally transfer a pigment layer with a metal thin film layer onto a substrate, A method for producing an image recording body, comprising: facing an image-receiving layer transfer material having an image-receiving layer, applying heat energy to transfer the image-receiving layer onto the pigment layer, and then forming an image on the image-receiving layer.
【００１２】(２)支持体上に金属薄膜層の積層された金
属薄膜層転写材料を用いて、基材上に金属薄膜層を熱転
写した後、支持体上に受像層、顔料層の順に積層された
受像層・顔料層転写材料と対面させ、熱エネルギーを与
えて金属薄膜層上に顔料層付き受像層を転写し、次いで
該受像層上に画像形成を行う画像記録体作成方法。(2) A metal thin film layer transfer material in which a metal thin film layer is laminated on a support is used to thermally transfer the metal thin film layer on a substrate, and then an image receiving layer and a pigment layer are laminated on the support in this order. A method for producing an image recording medium, which comprises facing the image-receiving layer / pigment layer transfer material, transferring heat energy to transfer the image-receiving layer with a pigment layer onto the metal thin film layer, and then forming an image on the image-receiving layer.
【００１３】(３)支持体上に金属薄膜層の積層された金
属薄膜層転写材料、支持体上に顔料層の積層された顔料
層転写材料、支持体上に受像層の積層された受像層転写
材料を用いて、基材上に金属薄膜層、顔料層、受像層の
順に順次熱転写し、次いで該受像層上に画像形成を行う
画像記録体作成方法。(3) Metal thin film layer transfer material in which a metal thin film layer is laminated on a support, a pigment layer transfer material in which a pigment layer is laminated on a support, and an image receiving layer in which an image receiving layer is laminated on a support A method for producing an image recording body, comprising the step of thermally transferring a metal thin film layer, a pigment layer and an image receiving layer in this order on a substrate using a transfer material, and then forming an image on the image receiving layer.
【００１４】(４)支持体上に顔料層、金属薄膜層の順に
積層された顔料層・金属薄膜層転写材料を用いて、基材
上に金属薄膜層付き顔料層を熱転写した後、別途、支持
体上に受像層を備えた受像層転写材料へ画像形成を行っ
た受像層転写材料と対面させ、熱エネルギーを与えて顔
料層上に画像形成された受像層を転写する画像記録体作
成方法。(4) Using a pigment layer / metal thin film layer transfer material in which a pigment layer and a metal thin film layer are laminated in this order on a support, a pigment layer with a metal thin film layer is thermally transferred onto a substrate, and then separately. Method for producing image recording body, which comprises transferring image-receiving layer formed on a pigment layer by applying heat energy to the image-receiving layer transferring material having an image-receiving layer formed on a support so as to face the image-receiving layer transferring material .
【００１５】(５)支持体上に金属薄膜層の積層された金
属薄膜層転写材料、支持体上に顔料層の積層された顔料
層転写材料を用いて、基材上に金属薄膜層、顔料層の順
に順次熱転写し、別途、支持体上に受像層を備えた受像
層転写材料へ画像形成を行った受像層転写材料と対面さ
せ、熱エネルギーを与えて顔料層上に画像形成された受
像層を転写する画像記録体作成方法。(5) Using a metal thin film layer transfer material having a metal thin film layer laminated on a support and a pigment layer transfer material having a pigment layer laminated on a support, a metal thin film layer and a pigment are provided on a substrate. The image is formed on the pigment layer by heat transfer in order of layers and separately facing the image-receiving layer transfer material on which an image is formed on an image-receiving layer transfer material having an image-receiving layer on a support, and applying heat energy. A method for producing an image recording material in which layers are transferred.
【００１６】(６)支持体上に受像層を備えた受像層転写
材料へ画像形成を行い、支持体上に金属薄膜層、顔料層
の順に積層された金属薄膜層・顔料層転写材料を用い
て、該画像形成された受像層上へ金属薄膜層付き顔料層
を熱転写し、次いで基材と対面させ、熱エネルギーを与
えて基材上に画像形成された受像層を転写する画像記録
体作成方法。(6) An image is formed on an image receiving layer transfer material having an image receiving layer on a support, and a metal thin film layer / pigment layer transfer material in which a metal thin film layer and a pigment layer are laminated in this order on the support is used. Then, the pigment layer with the metal thin film layer is thermally transferred onto the image-formed image-receiving layer, then facing the substrate, and heat energy is applied to transfer the image-formed image-receiving layer onto the substrate. Method.
【００１７】(７)支持体上に受像層を備えた受像層転写
材料へ画像形成を行い、支持体上に顔料層の積層された
顔料層転写材料、支持体上に金属薄膜層の積層された金
属薄膜層転写材料を用いて、該画像形成された受像層上
へ顔料層、金属薄膜層の順に順次熱転写し、次いで基材
と対面させ、熱エネルギーを与えて基材上に画像形成さ
れた受像層を転写する画像記録体作成方法。(7) An image is formed on an image-receiving layer transfer material having an image-receiving layer on a support, and a pigment layer transfer material having a pigment layer laminated on the support, and a metal thin film layer laminated on the support. The metal thin film layer transfer material is used to thermally transfer the pigment layer and the metal thin film layer in this order onto the image-receiving layer on which the image has been formed, then face the substrate and apply thermal energy to form an image on the substrate. Image recording material transfer method for transferring image receiving layer.
【００１８】(８)支持体上に受像層を備えた受像層転写
材料へ画像形成を行い、支持体上に顔料層の積層された
顔料層転写材料を用いて、該画像形成された受像層上へ
顔料層を熱転写し、別途、支持体上に金属薄膜層を備え
た金属薄膜層転写材料を用いて、基材上に金属薄膜層を
熱転写した後、熱エネルギーを与えて金属薄膜層上に画
像形成された受像層を転写する画像記録体作成方法。(8) An image is formed on an image receiving layer transfer material having an image receiving layer on a support, and the image forming image receiving layer is formed by using a pigment layer transfer material having a pigment layer laminated on the support. Heat transfer the pigment layer to the top and separately transfer the metal thin film layer onto the substrate using the metal thin film layer transfer material that has the metal thin film layer on the support, and then apply heat energy to the metal thin film layer. A method for producing an image recording medium, which comprises transferring an image-receiving layer image-formed on a sheet.
【００１９】(９)前記受像層へ画像形成を行う方法が、
熱転写記録法である(１)〜(８)の何れか１項に記載の画
像記録体作成方法。(9) A method for forming an image on the image receiving layer is
The method for producing an image recording material according to any one of (1) to (8), which is a thermal transfer recording method.
【００２０】(10)前記受像層へ画像形成を行う方法が、
電子写真法である(１)〜(８)の何れか１項に記載の画像
記録体作成方法。(10) A method for forming an image on the image receiving layer is
The method for producing an image recording material according to any one of (1) to (8), which is an electrophotographic method.
【００２１】(11)前記受像層へ画像形成を行う方法が、
インクジェット記録法である(１)〜(８)の何れか１項に
記載の画像記録体作成方法。(11) A method for forming an image on the image receiving layer is
The method for producing an image recording body according to any one of (1) to (8), which is an inkjet recording method.
【００２２】以下、本発明の画像記録体作成方法、及び
該画像記録体の作成時に必要な構成要素について詳細に
説明する。The image recording material producing method of the present invention and the components necessary for producing the image recording material will be described in detail below.
【００２３】＜画像記録体作成方法＞本発明の画像記録
体は、金属薄膜層により隠蔽性が確保されていることを
特徴としており、この画像記録体の作成方法は次の三つ
に大別される。<Method of Creating Image Recording Body> The image recording body of the present invention is characterized in that the metal thin film layer secures the concealing property. The method of producing this image recording body is roughly classified into the following three. To be done.
【００２４】１．基材上の画像形成を行う位置に対して
平滑性及び／又は隠蔽性を確保した後に、最後に画像形
成を行い画像記録体を作成する方法。1. A method of forming an image recording body by finally forming an image after ensuring smoothness and / or hiding property at a position where an image is formed on a base material.
【００２５】２．平滑性及び／又は隠蔽性を確保した基
材上に、画像形成された受像層を積層することにより画
像記録体を作成する方法。2. A method for producing an image recording material by laminating an image-receiving layer on which an image is formed, on a base material that secures smoothness and / or hiding power.
【００２６】３．画像形成された受像層上に、基材に対
して平滑性及び／又は隠蔽性を確保する処理を施した後
に、該受像層を基材に積層することにより画像記録体を
作成する方法。3. A method for producing an image recording material by subjecting a base material to a treatment for ensuring smoothness and / or hiding property on the image-receiving layer having an image formed thereon, and then laminating the image receiving layer on the base material.
【００２７】作成方法−１ 本作成方法では、基材上に受像層まで積層後、受像層に
画像形成を行うことにより画像記録体を作成することを
特徴とする。以下、図を用いて説明する。 Preparation Method-1 In this preparation method, an image recording material is prepared by laminating an image receiving layer on a base material and then forming an image on the image receiving layer. Hereinafter, description will be given with reference to the drawings.
【００２８】図１(c)に示すような構成の金属薄膜層・
顔料層転写材料（以下、顔料層転写材料と記載する場合
もある）及び図２(c)に示すような受像層転写材料を用
いて、図３(b)に示すように基材８上に金属薄膜層１、
顔料層２、受像層７の順になるよう熱転写した後、受像
層７上に画像を形成することにより画像記録体を得る。
この際、各種転写材料から、基材上へ転写する方法とし
ては、図１(c)の顔料層転写材料の接着層４面と基材８
とを対面させ、画像を形成する位置に金属薄膜層１と顔
料層２の積層された層を熱転写する。又、基材への顔料
層を転写する大きさ及び位置が一定の場合は、顔料層転
写材料に切り込みを入れて一定の形状の顔料層を転写す
るようにしてもよい。A metal thin film layer having a structure as shown in FIG.
Using a pigment layer transfer material (hereinafter, also referred to as a pigment layer transfer material) and an image receiving layer transfer material as shown in FIG. 2 (c), a base material 8 is provided on the substrate 8 as shown in FIG. 3 (b). Metal thin film layer 1,
After thermally transferring the pigment layer 2 and the image receiving layer 7 in this order, an image is formed on the image receiving layer 7 to obtain an image recording material.
At this time, as a method of transferring from various transfer materials onto the base material, the adhesive layer 4 surface of the pigment layer transfer material of FIG.
And face each other, and the layer in which the metal thin film layer 1 and the pigment layer 2 are laminated is thermally transferred to a position where an image is formed. When the size and position of the pigment layer transferred to the substrate are constant, the pigment layer transfer material may be cut to transfer the pigment layer having a constant shape.
【００２９】次いで、このように基材上に形成された顔
料層２と図２(c)の受像層転写材料の接着層面とを対面
させ、受像層を形成する位置に受像層を熱転写する。こ
の場合も、大きさ及び位置が一定の場合は顔料層２の転
写同様、切り込みを入れて置いてもよい。何れの場合に
おいても、接着層４の種類により、加熱・加圧条件を選
択することにより転写したい層を積層する面上に転写す
ることができる。Next, the pigment layer 2 thus formed on the base material and the adhesive layer surface of the image receiving layer transfer material of FIG. 2 (c) are opposed to each other, and the image receiving layer is thermally transferred to the position where the image receiving layer is formed. Also in this case, when the size and the position are constant, a cut may be placed as in the transfer of the pigment layer 2. In any case, the transfer can be performed on the surface on which the layers to be transferred are laminated by selecting the heating / pressurizing conditions depending on the type of the adhesive layer 4.
【００３０】このような加熱・加圧方法としては、ヒー
トロール、ホットスタンプ等は言うまでもなく、溶融転
写や熱拡散性色素転写の画像形成時に用いるサーマルヘ
ッドなども好適に用いることができる。なお、この転写
の際にヒートロールを用いる場合の加熱温度は、通常60
〜200℃、好ましくは80〜180℃の範囲であり、圧力とし
ては、通常0.1〜50kg／cm、好ましくは0.5〜20kg／cmの
範囲であり、又、搬送速度は、通常0.1〜100mm／秒、好
ましくは0.5〜50mm／秒である。又、ホットスタンプを
用いる場合の加熱温度は、通常60〜200℃、好ましくは8
0〜150℃の範囲で、圧力としては、通常0.05〜10kg／cm
2、好ましくは0.5〜５kg／cm2、又、加熱時間は、通常
0.1〜30秒、好ましくは0.5〜10秒である。As such a heating / pressurizing method, not only a heat roll, a hot stamp, etc. but also a thermal head or the like used at the time of image formation of melt transfer or heat diffusible dye transfer can be preferably used. The heating temperature when a heat roll is used for this transfer is usually 60
To 200 ° C, preferably 80 to 180 ° C, the pressure is usually 0.1 to 50 kg / cm, preferably 0.5 to 20 kg / cm, and the conveying speed is usually 0.1 to 100 mm / sec. , Preferably 0.5 to 50 mm / sec. When using a hot stamp, the heating temperature is usually 60 to 200 ° C, preferably 8
In the range of 0-150 ℃, the pressure is usually 0.05-10kg / cm
2 , preferably 0.5 to 5 kg / cm 2 , and the heating time is usually
It is 0.1 to 30 seconds, preferably 0.5 to 10 seconds.
【００３１】受像層を転写した後の画像形成は、通常の
溶融転写、熱拡散性色素転写、インクジェット方式、電
子写真方式の各種転写法を、それぞれの記録方法に適し
た受像層を選択することにより、そのまま用いることが
できる。For image formation after transferring the image receiving layer, various image transfer methods such as ordinary melt transfer, thermal diffusible dye transfer, ink jet method and electrophotographic method are selected, and an image receiving layer suitable for each recording method is selected. Therefore, it can be used as it is.
【００３２】溶融転写、熱拡散性色素転写方式におい
て、熱エネルギーを与える熱源としては、サーマルヘッ
ドが一般的であるが、このほかに通電ヘッド、レーザー
光、赤外線フラッシュ、熱ペンなどの公知のものを使用
することができる。熱エネルギーを与える熱源として、
サーマルヘッド或いは通電ヘッドを用いる時は、印加す
る電圧或いはパルス巾を変調することにより、与える熱
エネルギーを連続的又は多段階に変化させることができ
るし、熱エネルギーを与える熱源としてレーザー光を用
いる時は、レンズ等の光学系を用いることによって、レ
ーザー光の光量や照射面積を変化させることにより与え
る熱エネルギーを変化させることができる。又、音響光
学素子を内蔵したドットジェネレーターを用いれば網点
の大小に応じた熱エネルギーを与えることもでき、更に
熱エネルギーを与える熱源として赤外線フラッシュラン
プを用いる時は、レーザー光を用いる場合と同様に、加
熱を黒色などの着色層を介して行うとよい。又、黒色な
どの、画像の濃淡を連続的に表現したパターン又は網点
パターンを介して加熱を行ってもよいし、又、一面の黒
色などの着色層と前記のパターンのネガに相当するネガ
パターンを組み合わせて加熱を行ってもよい。In the melt transfer and thermal diffusible dye transfer systems, a thermal head is generally used as a heat source for giving heat energy. In addition to this, a known head such as an energizing head, a laser beam, an infrared flash, and a heat pen. Can be used. As a heat source that gives heat energy,
When using a thermal head or energizing head, the applied heat energy can be changed continuously or in multiple steps by modulating the applied voltage or pulse width, and when using laser light as the heat source that gives the heat energy. The heat energy can be changed by changing the amount of laser light or the irradiation area by using an optical system such as a lens. Also, if a dot generator with a built-in acousto-optic element is used, it is possible to give heat energy according to the size of the halftone dot, and when using an infrared flash lamp as a heat source for giving heat energy, the same as when using laser light. In addition, heating may be performed through a colored layer such as black. Further, heating may be performed through a pattern or halftone dot pattern in which the shade of the image is continuously expressed such as black, or a negative layer corresponding to the negative of the above-mentioned pattern and a colored layer such as black on one surface. You may heat by combining a pattern.
【００３３】インクジェット方式では、ドラム走査型、
シリアル走査型、平面走査型の何れでもよく、液体のイ
ンクを小滴、液柱又は霧状にして受像層へ飛行させる方
法としては、電荷量制御型や発散型などの連続噴射型、
Kyser型、Gould型、マイクロバブル型、バブルジェット
型、Stemme型、メタルダイヤフラム型、開放型、ラミネ
ート型、スパークジェット型及び電気浸透型などのオン
デマント型、間歇噴射型、インクミスト型などの記録方
式のものを選択して使用することができる。In the ink jet system, a drum scanning type,
It may be either a serial scanning type or a plane scanning type, and as a method of making a liquid ink into droplets, liquid columns or mist, and flying to the image receiving layer, a continuous ejection type such as a charge amount control type or a divergence type,
Kyser type, Gould type, micro bubble type, bubble jet type, Stemme type, metal diaphragm type, open type, laminate type, spark jet type and electro-osmosis type on-demant type, intermittent jet type, ink mist type, etc. The system can be selected and used.
【００３４】電子写真法では、現像剤の種類によりカス
ケード法、エァーブラシ法、磁気ブラシ法、湿式法など
の２成分系、パウダークラウド法、タッチダウン法、磁
気ブラシ法などの１成分系に分けられるが、何れの場合
も磁気ブラシ現像法が好ましい。又、磁気ブラシ法を用
いた記録方式としては、特殊な受像層を選ばないＰＰＣ
が本発明においては好ましく、又、感光体は酸化亜鉛、
セレン、硫化カドミウム、アモルファスシリコーンなど
の無機系のものや、ポリビニルカルバゾールとトリニト
ロフルオレン、チアピリリウム塩とポリカーボネート及
びトリフェニルメタン誘導体などの有機系のものなどを
用いることができ、トナーの定着法としては、オーブン
やフラッシュランプなどの非接触式、ホットスタンプや
ヒートロールなどの接触式でも、熱を掛けられトナーを
受像層へ熱定着でるものであれば特に制限なく用いるこ
とができるが、操作性や均一性を確保する為には接触式
の方が好ましい。The electrophotographic method is classified into a two-component system such as a cascade method, an airbrush method, a magnetic brush method and a wet method, and a one-component system such as a powder cloud method, a touchdown method and a magnetic brush method, depending on the kind of the developer. However, in any case, the magnetic brush developing method is preferable. As a recording method using the magnetic brush method, a PPC that does not select a special image receiving layer
Is preferable in the present invention, and the photoreceptor is zinc oxide,
Inorganic compounds such as selenium, cadmium sulfide, and amorphous silicone, and organic compounds such as polyvinylcarbazole and trinitrofluorene, thiapyrylium salt and polycarbonate, and triphenylmethane derivatives can be used. A non-contact type such as an oven or a flash lamp, or a contact type such as a hot stamp or a heat roll can be used without particular limitation as long as it can apply heat to the toner to heat-fix the toner to the image-receiving layer. The contact type is preferable to ensure uniformity.
【００３５】本発明において、受像層上に画像形成を行
う際に用いることができる溶融転写、熱拡散色素転写に
用いられるインクシートは、市販されているものをその
まま用いることもできるし、従来から公知の技術を用い
て、支持体上に色材や熱拡散性色素を含有するインク
層、必要に応じて反対面にバッキング層を積層して新た
に作成してもよい。In the present invention, as the ink sheet used in the melt transfer and the thermal diffusion dye transfer which can be used when forming an image on the image receiving layer, a commercially available ink sheet can be used as it is, or a conventional ink sheet can be used. A known technique may be used to newly form an ink layer containing a coloring material or a heat diffusible dye on the support and, if necessary, a backing layer on the opposite surface.
【００３６】なお、熱拡散色素転写に用いられる色素
は、従来から用いられているシアン色素、マゼンタ色
素、イエロー色素をそのまま用いることができ、更に、
特開昭59-78893号等に記載されたキレート化された色素
で定着性等に優れる画像を形成する画像形成方法に用い
られるキレート化可能な色素、特開平3-83685号等に記
載のフェノール性水酸基を有する色素を用いて、受像層
中に含有される媒染剤と該色素との反応により形成され
る色素による画像を形成する方法に用いられる色素、更
に特開平5-26868号等に記載の含窒素有機塩基と塩を形
成してなる色素を用い、受像層中に含有される媒染剤と
該色素との塩交換反応により画像を形成する方法に用い
られる色素なども、それぞれの方法に適したものを適時
選択して用いることができる。As the dyes used for the thermal diffusion dye transfer, the cyan dyes, magenta dyes and yellow dyes which have been conventionally used can be used as they are.
Chelating dyes described in JP-A-59-78893, which can be used in an image forming method for forming an image having excellent fixability, and phenols described in JP-A-3-83685. Using a dye having a hydroxyl group, a dye used in a method for forming an image by a dye formed by the reaction of a mordant contained in the image-receiving layer with the dye, further described in JP-A-5-26868. A dye used in a method of forming an image by a salt exchange reaction between a mordant contained in the image-receiving layer and the dye, which uses a dye formed by forming a salt with a nitrogen-containing organic base, is also suitable for each method. The thing can be selected and used at any time.
【００３７】又、インクジェット方式で画像形成する場
合に用いるインクは、市販されているものをそのまま用
いることもできるし、従来から公知の技術を用いて着色
剤、溶媒、防湿剤、結着樹脂、粘度調整剤、表面張力調
整剤、伝導度調整剤、水素イオン濃度調整剤、防黴殺菌
剤、酸素吸収剤、キレート化剤などを適時選択し新たに
調製してもよい。As the ink used for forming an image by the ink jet method, a commercially available ink may be used as it is, or a colorant, a solvent, a moistureproof agent, a binder resin, a binder, A viscosity adjusting agent, a surface tension adjusting agent, a conductivity adjusting agent, a hydrogen ion concentration adjusting agent, an antifungal bactericidal agent, an oxygen absorbing agent, a chelating agent and the like may be appropriately selected and newly prepared.
【００３８】更に、電子写真法で画像形成する場合に用
いられるトナーは、磁性トナー、２成分現像剤の何れで
も、画像の種類や、画像形成される受像層の組成によっ
て市販品をそのまま用いてもよいし、新たに調製して用
いてもよい。Further, the toner used when forming an image by the electrophotographic method is either a magnetic toner or a two-component developer, and a commercially available product may be used as it is depending on the kind of the image and the composition of the image-receiving layer on which the image is formed. Alternatively, it may be newly prepared and used.
【００３９】更に、図４(c)に示すような構成の金属薄
膜層転写材料、図５(b)に示すような受像層転写材料を
用いて、図６(a)のように、基材上に、まず金属薄膜層
１を熱転写し、次いで蒸着アンカー層６上へ顔料層２と
受像層７が積層された層を熱転写することにより基材上
に受像層を形成する。後は上述と同様に画像形成するこ
とにより画像記録体が得られる。Further, by using the metal thin film layer transfer material having the structure as shown in FIG. 4C and the image receiving layer transfer material as shown in FIG. 5B, as shown in FIG. First, the metal thin film layer 1 is thermally transferred, and then the layer in which the pigment layer 2 and the image receiving layer 7 are laminated is thermally transferred onto the vapor deposition anchor layer 6 to form an image receiving layer on the substrate. After that, an image recording body is obtained by forming an image in the same manner as described above.
【００４０】一方、金属薄膜層１、顔料層２、受像層７
を順次転写させ、基材上に受像層を形成することもでき
る。例えば、基材８と図４(c)で示される金属薄膜層転
写材料の接着層４とを重ね合わせて金属薄膜層１を熱転
写することにより、図６(a)のように基材上に金属薄膜
層１を形成する。On the other hand, the metal thin film layer 1, the pigment layer 2, the image receiving layer 7
Can be sequentially transferred to form an image receiving layer on the substrate. For example, by overlaying the base material 8 and the adhesive layer 4 of the metal thin film layer transfer material shown in FIG. 4 (c) and thermally transferring the metal thin film layer 1, the metal thin film layer 1 is transferred onto the base material as shown in FIG. 6 (a). The metal thin film layer 1 is formed.
【００４１】次いで蒸着アンカー層６と図７(c)で示さ
れる顔料層転写材料の接着層４とを重ね合わせて顔料層
を熱転写することにより、図８(a)のように蒸着アンカ
ー層６上に顔料層２を積層する。更に、顔料層２と図２
(c)で示される受像層転写材料の接着層４とを重ね合わ
せて受像層を熱転写することにより、図８(b)のように
基材上に金属薄膜層１、顔料層２、受像層７と積層され
た材料を形成した後、受像層上へ画像を形成することに
より画像記録体を得る。このようにして作成した画像記
録体は、画像記録体の最外層表面に画像形成がなされて
いることから、記録された画像の耐久性が要求される場
合には、必要に応じて画像形成された受像層７を覆う形
で図11(b)のように保護層10を積層するのが好ましい。
なお、ここで言う保護層とは、図９のように保護シート
９上に接着層４を設け、シートごと画像表面を覆う保護
シート、図10(a)のように支持体３上に保護層10が積層
された保護層転写材料により保護層10のみ転写させ画像
表面を覆うものを指し、保護層を画像記録体の画像表面
へ積層させる方法としては、上述の金属薄膜層転写材
料、顔料層転写材料、受像層転写材料などと同様の方法
で設けることができる。Then, the vapor deposition anchor layer 6 and the adhesive layer 4 of the pigment layer transfer material shown in FIG. 7 (c) are superposed on each other and the pigment layer is thermally transferred, whereby the vapor deposition anchor layer 6 is formed as shown in FIG. 8 (a). The pigment layer 2 is laminated on top. Furthermore, the pigment layer 2 and FIG.
By heat-transferring the image-receiving layer by superposing it with the adhesive layer 4 of the image-receiving layer transfer material shown in (c), the metal thin film layer 1, the pigment layer 2, the image-receiving layer are formed on the substrate as shown in FIG. 8 (b). After the material laminated with No. 7 is formed, an image is formed on the image receiving layer to obtain an image recording material. The image recording material thus prepared has an image formed on the surface of the outermost layer of the image recording material. Therefore, when durability of the recorded image is required, the image is formed as necessary. It is preferable to stack a protective layer 10 as shown in FIG. 11B so as to cover the image receiving layer 7.
It should be noted that the protective layer referred to here is a protective sheet which covers the image surface together with the adhesive layer 4 on the protective sheet 9 as shown in FIG. 9, and a protective layer on the support 3 as shown in FIG. 10 (a). A protective layer transfer material in which 10 is laminated refers to one which transfers only the protective layer 10 to cover the image surface, and as a method for laminating the protective layer on the image surface of the image recording material, the above-mentioned metal thin film layer transfer material, pigment layer The transfer material, the image receiving layer transfer material and the like can be provided by the same method.
【００４２】作成方法−２ 本作成方法では、顔料層まで積層された基材と、別途作
成した受像層上に画像形成した受像層転写材料の画像形
成された受像層とを貼着させることにより画像記録体を
作成することを特徴とする。以下、図を用いて説明す
る。 Preparation Method-2 In this preparation method, the base material laminated up to the pigment layer and the image-formed image-receiving layer of the image-receiving layer transfer material image-formed on the separately prepared image-receiving layer are adhered to each other. The feature is that an image recording body is created. Hereinafter, description will be given with reference to the drawings.
【００４３】図12(b)に示すような構成の受像層転写材
料を用いて、図13のように受像層７上に画像形成を行
い、別途、図１(c)で示される顔料層転写材料を基材８
に熱転写することにより、図３(a)に示す顔料層２を積
層した基材を作成し、この顔料層２と図13の画像形成さ
れた受像層11とを対面させ、受像層11を熱転写すること
により、図14で示される画像記録体が得られる。又、図
４(c)、図７(c)で示される金属薄膜層転写材料、顔料層
転写材料を用いて、基材上に図15(a)のように基材上に
顔料層２を形成し、この顔料層２と図13の画像形成され
た受像層11とを対面させ、受像層を熱転写することによ
り、図15(b)で示される画像記録体を作成することもで
きる。なお、この方法においても、必要に応じて作成方
法−１同様、転写させる各種材料に切り込みを入れて置
いてもよい。An image is formed on the image receiving layer 7 as shown in FIG. 13 by using the image receiving layer transfer material having the structure shown in FIG. 12 (b), and the pigment layer transfer shown in FIG. 1 (c) is separately prepared. Material 8
By thermal transfer to, a base material having the pigment layer 2 shown in FIG. 3 (a) laminated is prepared, the pigment layer 2 and the image-formed image receiving layer 11 of FIG. 13 are faced to each other, and the image receiving layer 11 is thermally transferred. By doing so, the image recording body shown in FIG. 14 is obtained. Further, using the metal thin film layer transfer material and the pigment layer transfer material shown in FIGS. 4 (c) and 7 (c), the pigment layer 2 is formed on the substrate as shown in FIG. 15 (a). It is also possible to form the image recording medium shown in FIG. 15 (b) by forming the pigment layer 2 and the image-receiving layer 11 of FIG. 13 facing each other and thermally transferring the image-receiving layer. Note that, in this method as well, if necessary, various materials to be transferred may be cut and placed as in the preparation method-1.
【００４４】作成方法−３ 本作成方法では、画像形成した受像層上に少なくとも顔
料層を積層させた受像層転写材料と、基材又は基材上に
金属薄膜層を積層したものとを対面させて熱転写するこ
とにより画像記録体を作成することを特徴とする。以
下、図を用いて説明する。 Preparation Method-3 In this preparation method, the image-receiving layer transfer material in which at least a pigment layer is laminated on the image-formed image-receiving layer and the base material or the metal thin film layer laminated on the base material are faced to each other. It is characterized in that an image recording body is produced by thermal transfer by means of heat transfer. Hereinafter, description will be given with reference to the drawings.
【００４５】図16(b)に示すような構成の金属薄膜層転
写材料を用いて、図13の画像形成が行われた受像層11上
に金属薄膜層を熱転写する（図17(a)）。次いで、この
接着層兼剥離層12と基材８とを対面させ、画像形成され
た受像層11を熱転写することにより図17(b)で示される
画像記録体が得られる。又、図７(c)、図18(c)で示され
る顔料層転写材料、金属薄膜層転写材料を用いて、図13
の画像形成が行なわれた受像層11上に金属薄膜層を熱転
写し（図20(a)）、この接着層兼剥離層12と基材８とを
対面させ、受像層を熱転写することにより図19(b)で示
される画像記録体を作成することもできる。Using the metal thin film layer transfer material having the structure shown in FIG. 16 (b), the metal thin film layer is thermally transferred onto the image receiving layer 11 on which the image is formed in FIG. 13 (FIG. 17 (a)). . Next, the adhesive layer / release layer 12 and the substrate 8 are opposed to each other, and the image-receiving layer 11 on which an image has been formed is thermally transferred to obtain the image recording body shown in FIG. 17 (b). In addition, by using the pigment layer transfer material and the metal thin film layer transfer material shown in FIGS. 7 (c) and 18 (c),
By thermally transferring the metal thin film layer onto the image receiving layer 11 on which the image formation has been performed (FIG. 20 (a)), the adhesive layer / release layer 12 and the substrate 8 are faced to each other, and the image receiving layer is thermally transferred. It is also possible to prepare the image recording body shown in 19 (b).
【００４６】更に、前述の方法のように画像形成された
受像層上に金属薄膜層まで設けた後に、基材へ熱転写し
て画像記録体を作成するのではなく、基材上に金属薄膜
層を形成しておいてもよい。例えば、図13の画像形成さ
れた受像層11上に図７(c)の顔料層転写材料から顔料層
を熱転写したもの（図20(a)）と、基材上に図18(c)の金
属薄膜層転写材料から金属薄膜層１を転写したもの（図
20(b)）とを対面させ、画像形成された受像層11を熱転
写することにより図20(c)で示される画像記録体を作成
することもできる。なお、この作成方法においても、必
要に応じて作成方法−１同様、転写させる各種材料に切
り込みを入れておいてもよい。Further, the metal thin film layer is not formed on the base material by thermal transfer to the base material after the metal thin film layer is provided on the image receiving layer on which the image is formed as in the above-mentioned method, to form an image recording material. May be formed. For example, one obtained by thermally transferring a pigment layer from the pigment layer transfer material of FIG. 7 (c) onto the image-receiving image-receiving layer 11 of FIG. 13 (FIG. 20 (a)), and of FIG. Transferring the metal thin film layer 1 from the metal thin film layer transfer material (Fig.
It is also possible to prepare the image recording medium shown in FIG. 20 (c) by facing the image receiving layer 11 on which the image is formed and thermally transferring the image-receiving layer 11 on which the image is formed. Incidentally, in this producing method as well, as in the producing method-1, if necessary, various materials to be transferred may be cut.
【００４７】＜画像記録体作成の為の構成要素＞上述の
ようにして画像記録体を作成するのに必要な構成要素に
ついて以下に詳述する。<Constituent Elements for Creating Image Recording Body> The constituent elements necessary for preparing the image recording body as described above will be described in detail below.
【００４８】画像記録するための基材としては、例えば
普通紙、コート紙、ダンボール及び合成紙（例えばポリ
プロピレンを主成分とする合成紙、片面又は両面に多孔
質構造の顔料塗工層を設けた合成紙など）等の各種紙
類、ポリオレフィン系樹脂、塩化ビニル系樹脂、スチレ
ン系樹脂、アクリル系樹脂、ポリエチレンテレフタレー
ト、ポリエチレンナフタレート、ポリイミド、ポリエー
テルイミド、ポリカーボネート、ポリエーテルエーテル
ケトン、ポリアリレート、ポリスルホン、ポリエーテル
スルホン、ポリウレタン、フェノール樹脂やエポキシ樹
脂等の熱硬化性樹脂等の樹脂を１種又はそれらを２種以
上混合した各種樹脂フィルム又はシートや射出成形品、
芯材として紙やプラスチックフィルムの少なくとも片面
にポリオレフィンを押し出しラミネートしたシート、ア
ルミや鉄などの各種の金属で形成されたフィルム又はシ
ートや鋳物やプレス等の成形品、ガラスなどの各種のセ
ラミックス類で形成されたフィルム又はシートや成形
品、木材、陶磁器等を挙げることができ、更に、その基
材自体が着色していたり、顔料や色素、染料などにより
着色されていたり、表面に印刷が施されているものなど
が挙げられる。具体的には、コピー用紙、ボンド紙、プ
ラスチックフィルム、名刺やカレンダーのような印刷が
施された紙やプラスチックフィルム、画像形成された受
像層が積層される反対の面に磁気層が設けられているテ
レホンカードやクレジットカード等の各種磁気カード、
ＩＣが組み込まれたＩＣカード、印画紙やレントゲン写
真等のハロゲン化銀写真感光材料が挙げられる。As a base material for recording an image, for example, plain paper, coated paper, cardboard and synthetic paper (for example, synthetic paper containing polypropylene as a main component, a pigment coating layer having a porous structure on one or both sides thereof is provided. Synthetic paper, etc.), polyolefin resin, vinyl chloride resin, styrene resin, acrylic resin, polyethylene terephthalate, polyethylene naphthalate, polyimide, polyetherimide, polycarbonate, polyetheretherketone, polyarylate, Polysulfone, polyether sulfone, polyurethane, various resins such as thermosetting resins such as phenolic resins and epoxy resins, or various resin films or sheets or injection molded products obtained by mixing two or more of them.
Sheets made by extruding and laminating polyolefin on at least one side of paper or plastic film as core materials, films or sheets formed of various metals such as aluminum and iron, molded products such as castings and presses, various ceramics such as glass Examples include formed films or sheets, molded products, wood, ceramics, and the like, and the base material itself is colored, or is colored with a pigment, dye, dye, or the like, and the surface is printed. Some of them are listed. Specifically, a magnetic layer is provided on the opposite surface on which copy paper, bond paper, plastic film, printed paper such as business cards and calendars, plastic film, and image-receiving layer are laminated. Various magnetic cards such as telephone cards and credit cards,
Examples thereof include IC cards incorporating ICs, photographic papers, and silver halide photographic light-sensitive materials such as radiographs.
【００４９】基材の厚みは特に制限はないが、通常4.5
μm以上であり、10μm以上のものがより好ましい。The thickness of the substrate is not particularly limited, but is usually 4.5.
It is at least μm, and more preferably at least 10 μm.
【００５０】金属薄膜層転写材料、顔料層転写材料、受
像層転写材料などの転写材料に用いられる支持体として
は、シート又はフィルム状に延伸し、ヒートセットした
ものが寸法安定性の面から好ましい。支持体の厚みは特
に制限はないが、前述の作成方法の際に支持体上に積層
された層を加熱転写する必要があることから通常２〜20
0μmであり、好ましくは3.5〜100μmである。As a support used for a transfer material such as a metal thin film layer transfer material, a pigment layer transfer material and an image receiving layer transfer material, it is preferable to stretch it into a sheet or film and heat set it in terms of dimensional stability. . The thickness of the support is not particularly limited, but it is usually 2 to 20 because the layer laminated on the support needs to be transferred by heating in the above-mentioned preparation method.
It is 0 μm, preferably 3.5 to 100 μm.
【００５１】金属薄膜層としては、バインダー樹脂に各
種金属微粉末を分散して設けることができる。しかしな
がら、前述の画像記録体作成時に、基材の任意の位置に
画像形成された受像層又は画像形成されていない受像層
を転写するためには、金属薄膜層は金属のみの薄膜で形
成するのが好ましい。As the metal thin film layer, various fine metal powders can be dispersed in a binder resin. However, in order to transfer the image-receiving layer which is imaged or the image-receiving layer which is not imaged to an arbitrary position of the base material at the time of producing the above-mentioned image recording material, the metal thin film layer is formed of a thin film of only metal. Is preferred.
【００５２】このように金属から成る薄膜層を形成する
方法としては、真空蒸着法、イオンプレーティング法、
スパッタリング法などの公知の方法によって金属蒸着薄
膜として、金属の単結晶又は多結晶として設けることが
でき、蒸着する金属としては、アルミニウム、亜鉛、ア
ンチモン、インジウム、セレン、錫、タンタル、クロ
ム、鉛、金、銀、白金、ニッケル、ニオブ、ゲルマニウ
ム、珪素、モリブデン、マンガン、タングステン、パラ
ジウム等の金属を１種或いは２種以上併用などにより形
成することができる。この金属薄膜層の厚みは、通常25
〜2000Å、好ましくは50〜1000Åである。As a method for forming a thin film layer made of a metal as described above, a vacuum deposition method, an ion plating method,
As a metal vapor-deposited thin film by a known method such as a sputtering method, it can be provided as a single crystal or a polycrystal of metal, and as the metal to be vapor-deposited, aluminum, zinc, antimony, indium, selenium, tin, tantalum, chromium, lead, Metals such as gold, silver, platinum, nickel, niobium, germanium, silicon, molybdenum, manganese, tungsten, and palladium can be used alone or in combination of two or more. The thickness of this metal thin film layer is usually 25
~ 2000Å, preferably 50-1000Å.
【００５３】顔料層としては、顔料とバインダー樹脂、
及び必要に応じて各種添加剤とから構成される。As the pigment layer, a pigment and a binder resin,
And, if necessary, various additives.
【００５４】顔料としては、従来から公知のものを適時
選択して用いることができるが、これらの中で、基材が
白色で画像形成部分との差を目立たなくさせたり、複数
色で画像を受像層に形成する場合などにおいては、色濁
りを起こさず鮮明な画像が得られることから、白色顔料
を使用するのが好ましく、このような白色顔料として
は、例えば二酸化チタン、亜鉛華、鉛白、硫酸バリウ
ム、白亜等が挙げられ、中でも隠蔽力に優れる二酸化チ
タンが好ましい。As the pigment, conventionally known pigments can be appropriately selected and used. Among them, the base material is white and the difference from the image forming portion is inconspicuous, or the image is formed in a plurality of colors. When forming in the image receiving layer, it is preferable to use a white pigment because a clear image can be obtained without causing color turbidity. Examples of such white pigment include titanium dioxide, zinc white, and lead white. , Barium sulfate, chalk, and the like, and among them, titanium dioxide, which is excellent in hiding power, is preferable.
【００５５】なお、顔料層中に含有される顔料の量は、
顔料層形成組成物全量に対し、通常10〜95％、好ましく
は20〜90％である。The amount of the pigment contained in the pigment layer is
It is usually 10 to 95%, preferably 20 to 90%, based on the total amount of the pigment layer forming composition.
【００５６】バインダー樹脂としては、ポリエステル系
樹脂、ポリビニルアセタール系樹脂、ウレタン系樹脂、
アミド系樹脂、セルロース系樹脂、オレフィン系樹脂、
塩化ビニル系樹脂、アクリル系樹脂、スチレン系樹脂、
ポリカーボネート、ポリビニルアルコール、ポリビニル
ピロリドン、ポリスルホン、ポリカプロラクトン樹脂、
ポリアクリロニトリル樹脂、尿素樹脂、エポキシ樹脂、
フェノキシ樹脂等や、ロジン、水添加ロジン、ロジンマ
レイン酸、重合ロジン、ロジンフェノール、テルペン樹
脂、石油樹脂等を挙げることができ、これらの樹脂は、
１種単独でもよいし、２種以上併用してもよい。As the binder resin, polyester resin, polyvinyl acetal resin, urethane resin,
Amide resin, cellulose resin, olefin resin,
Vinyl chloride resin, acrylic resin, styrene resin,
Polycarbonate, polyvinyl alcohol, polyvinylpyrrolidone, polysulfone, polycaprolactone resin,
Polyacrylonitrile resin, urea resin, epoxy resin,
Examples include phenoxy resin and the like, rosin, water-added rosin, rosin maleic acid, polymerized rosin, rosin phenol, terpene resin, petroleum resin, and the like.
One kind may be used alone, or two or more kinds may be used in combination.
【００５７】バインダー樹脂の含有量は顔料層形成組成
物全量に対し、通常5〜90％、好ましくは10〜80％であ
る。The content of the binder resin is usually 5 to 90%, preferably 10 to 80% with respect to the total amount of the pigment layer forming composition.
【００５８】その他に、顔料分散剤、増粘剤、流動性改
良剤、消泡剤、抑泡剤、離型剤、発泡剤、浸透剤、着色
顔料、着色染料、蛍光増白剤、紫外線吸収剤、酸化防止
剤、防腐剤、防黴剤、帯電防止剤、熱溶剤等の各種添加
剤を必要に応じて適時添加することができる。In addition, pigment dispersants, thickeners, fluidity improvers, defoamers, foam suppressors, mold release agents, foaming agents, penetrants, coloring pigments, coloring dyes, fluorescent brightening agents, and ultraviolet absorbing agents. Various additives such as an agent, an antioxidant, an antiseptic, an antifungal agent, an antistatic agent, and a hot solvent can be appropriately added as needed.
【００５９】顔料層の厚みは通常0.5〜10μm、好ましく
は１〜５μmである。又、顔料層は単層で形成してもよ
く、組成が同一の多層構成、又は異なる２層以上の多層
構造としてもよい。The thickness of the pigment layer is usually 0.5 to 10 μm, preferably 1 to 5 μm. Further, the pigment layer may be formed as a single layer, or may have a multilayer structure having the same composition or a multilayer structure having two or more layers having different compositions.
【００６０】受像層は、前述した画像記録体作成の際の
記録方法、具体的には熱転写記録法（溶融転写、熱拡散
性色素転写）、インクジェット記録法、電子写真記録法
に適した受像層であれば特に制限なく用いることができ
る。具体的には、溶融転写に適した受像層としては、結
着樹脂、及び必要に応じた各種添加剤により形成するこ
とができる。The image-receiving layer is suitable for the above-mentioned recording method for producing the image recording material, specifically, the thermal transfer recording method (melt transfer, thermal diffusible dye transfer), ink jet recording method, and electrophotographic recording method. Any material can be used without particular limitation. Specifically, the image receiving layer suitable for melt transfer can be formed with a binder resin and various additives as necessary.
【００６１】結着樹脂としては、ポリビニルブチラー
ル、ポリビニルアセトアセタール、ポリビニルアルコー
ルなどのポリビニルアルコール誘導体、デンプン、コー
ンスターチ、カゼイン、ゼラチン等の天然物及びその誘
導体、メチルセルロース、ヒドロキシプロピルセルロー
ス等のセルロース系樹脂、水溶性ポリアミド、ポリアク
リル酸等の水溶性樹脂、塩化ビニル系樹脂、ブタジエン
系樹脂、アクリル系樹脂、ポリオレフィン系樹脂、ポリ
ウレタン系樹脂、エポキシ系樹脂等の合成樹脂等が挙げ
られる。なお、合成樹脂は有機溶媒に溶解したもので
も、ラテックス、エマルジョンの如く水に分散させたも
のでも用途に応じて使用することができる。溶融転写に
おける受像層としては、転写するインクとの親和性、受
像層の色調などを改善する目的で各種添加剤を添加して
もよい。インクの求油性を改善するためには多孔質顔料
を添加するのが好ましい。このような多孔質顔料として
は、天然又は合成のゼオライト、カオリン、焼成カオリ
ン、タルク、蝋石、珪藻土、シリカ、合成シリカ、クレ
ー、炭酸カルシウム、水酸化マグネシウム、炭酸マグネ
シウム、珪酸マグネシウム、酸化チタン、炭酸バリウ
ム、尿素-ホルマリンフィラー、セルロースフィラー、
水酸化アルミニウム等が挙げられる。これら多孔質顔料
は、１種単独でもよいし、２種以上併用してもよく、通
常、受像層形成組成物全量に対し５〜95重量％、更には
10〜80重量％添加するのが好ましい。As the binder resin, polyvinyl butyral, polyvinyl acetoacetal, polyvinyl alcohol and other polyvinyl alcohol derivatives, starch, corn starch, casein, gelatin and other natural products and their derivatives, methyl cellulose, hydroxypropyl cellulose and other cellulose resins, Examples thereof include water-soluble polyamides, water-soluble resins such as polyacrylic acid, vinyl chloride resins, butadiene resins, acrylic resins, polyolefin resins, polyurethane resins, epoxy resins, and other synthetic resins. The synthetic resin may be either a resin dissolved in an organic solvent or a resin dispersed in water such as a latex or emulsion, depending on the application. Various additives may be added to the image receiving layer in the melt transfer for the purpose of improving the affinity with the ink to be transferred and the color tone of the image receiving layer. In order to improve the oleophobicity of the ink, it is preferable to add a porous pigment. Examples of such porous pigments include natural or synthetic zeolite, kaolin, calcined kaolin, talc, sekiseki, diatomaceous earth, silica, synthetic silica, clay, calcium carbonate, magnesium hydroxide, magnesium carbonate, magnesium silicate, titanium oxide, carbonic acid. Barium, urea-formalin filler, cellulose filler,
Aluminum hydroxide etc. are mentioned. These porous pigments may be used alone or in combination of two or more, and usually 5 to 95% by weight based on the total amount of the image receiving layer forming composition, and further,
It is preferable to add 10 to 80% by weight.
【００６２】その他に、顔料分散剤、増粘剤、流動性改
良剤、消泡剤、抑泡剤、離型剤、発泡剤、浸透剤、着色
顔料、着色染料、蛍光増白剤、紫外線吸収剤、酸化防止
剤、防腐剤、防黴剤、帯電防止剤、熱溶剤等の各種添加
剤を必要に応じて適時添加することができる。In addition, pigment dispersants, thickeners, fluidity improvers, defoamers, foam suppressors, mold release agents, foaming agents, penetrants, coloring pigments, coloring dyes, fluorescent whitening agents, and ultraviolet absorption. Various additives such as an agent, an antioxidant, an antiseptic, an antifungal agent, an antistatic agent, and a hot solvent can be appropriately added as needed.
【００６３】溶融転写受像層の厚みは、通常0.5〜50μ
m、好ましくは１〜20μｍの範囲に選定される。又、受
像層は単層で形成してもよく、組成が同一の多層構成、
或いは異なる２層以上の多層構造としてもよい。The thickness of the melt transfer image receiving layer is usually 0.5 to 50 μm.
m, preferably 1 to 20 μm. Further, the image receiving layer may be formed of a single layer, and a multilayer structure having the same composition,
Alternatively, it may have a multilayer structure of two or more different layers.
【００６４】熱拡散性色素転写における受像層として
は、熱拡散性色素を十分受容できるものであれば特に制
限なく用いることができ、そのような熱拡散性色素転写
に適した受像層は、バインダー樹脂と必要に応じた各種
添加剤により形成することができる。The image-receiving layer in the transfer of the heat-diffusible dye can be used without particular limitation as long as it can sufficiently accept the heat-diffusible dye, and the image-receiving layer suitable for the transfer of the heat-diffusible dye is a binder. It can be formed by a resin and various additives as required.
【００６５】バインダー樹脂としては、従来から感熱転
写記録用受像シートの受像層に用いられている公知の樹
脂を使用でき、例えばポリエステル系樹脂、ポリビニル
アセタール系樹脂、ウレタン系樹脂、アミド系樹脂、セ
ルロース系樹脂、オレフィン系樹脂、塩化ビニル系樹
脂、アクリル系樹脂、スチレン系樹脂、ポリカーボネー
ト、ポリビニルアルコール、ポリビニルピロリドン、ポ
リスルホン、ポリカプロラクトン樹脂、ポリアクリロニ
トリル樹脂、尿素樹脂、エポキシ樹脂、フェノキシ樹脂
等を挙げることができ、これらの樹脂は、１種単独で使
用してもよいし、２種以上併用してもよい。As the binder resin, a known resin which has been conventionally used in an image receiving layer of a thermal transfer recording image receiving sheet can be used, and examples thereof include polyester resins, polyvinyl acetal resins, urethane resins, amide resins and cellulose. Resin, olefin resin, vinyl chloride resin, acrylic resin, styrene resin, polycarbonate, polyvinyl alcohol, polyvinylpyrrolidone, polysulfone, polycaprolactone resin, polyacrylonitrile resin, urea resin, epoxy resin, phenoxy resin, etc. These resins may be used alone or in combination of two or more.
【００６６】なお、前記のバインダー樹脂は、受像層形
成組成物全量に対し通常20〜99重量％、より好ましくは
50〜95重量％用いられる。The above-mentioned binder resin is usually contained in an amount of 20 to 99% by weight, more preferably, based on the total amount of the image-receiving layer forming composition.
Used from 50 to 95% by weight.
【００６７】熱拡散色素転写受像層には、剥離剤、酸化
防止剤、紫外線吸収剤、光安定剤、フィラー（無機微粒
子、有機樹脂粒子）、顔料、帯電防止剤を添加してもよ
い。又、増感剤として可塑剤、熱溶剤などをを添加して
もよい。A releasing agent, an antioxidant, an ultraviolet absorber, a light stabilizer, a filler (inorganic fine particles, organic resin particles), a pigment and an antistatic agent may be added to the heat diffusion dye transfer image-receiving layer. Further, a plasticizer, a hot solvent or the like may be added as a sensitizer.
【００６８】更に、特開昭59-78893号等に記載されたキ
レート化された色素で画像形成する場合には、金属含有
化合物を、特開平3-83685号等に記載のフェノール性水
酸基を有する色素、又は特開平5-26868号等に記載の含
窒素有機塩基と塩を形成して成る色素を用いて、受像層
中に含有される媒染剤と該色素との反応、又は塩交換反
応により形成される色素による画像形成する場合には、
受像層中に四級アンモニウム塩等の媒染剤を含有させて
もよい。Further, in the case of forming an image with the chelated dye described in JP-A-59-78893, a metal-containing compound is used, which has a phenolic hydroxyl group described in JP-A-3-83685. A dye or a dye formed by forming a salt with a nitrogen-containing organic base as described in JP-A-5-26868 is used to form a reaction between the mordant contained in the image-receiving layer and the dye, or a salt exchange reaction. When forming an image with the dye
A mordant such as a quaternary ammonium salt may be contained in the image receiving layer.
【００６９】熱拡散性色素転写受像層における添加剤全
体の添加量は、通常、バインダー樹脂に対して0.1〜30
重量％の範囲に選定するのが好ましく、受像層の厚み
は、通常２〜50μm、好ましくは３〜20μmの範囲に選定
される。又、受像層は単層で形成してもよく、組成が同
一の多層構成、或いは異なる２層以上の多層構造として
もよい。The total amount of the additives added to the heat diffusible dye transfer image-receiving layer is usually 0.1 to 30 with respect to the binder resin.
It is preferable to select in the range of wt%, and the thickness of the image receiving layer is usually selected in the range of 2 to 50 μm, preferably 3 to 20 μm. The image-receiving layer may be formed as a single layer, or may have a multi-layer structure having the same composition or a multi-layer structure having two or more different compositions.
【００７０】更に、インクジェット記録法における受像
層としては、インクを十分受容できるものであれば特に
制限なく用いることができ、そのようなインクジェット
方式に適した受像層は、バインダー樹脂と必要に応じた
各種添加剤により形成することができる。Further, as the image receiving layer in the ink jet recording method, any image receiving layer can be used without particular limitation as long as it can sufficiently receive ink, and the image receiving layer suitable for such an ink jet system is a binder resin and, if necessary, a binder resin. It can be formed by various additives.
【００７１】バインダー樹脂は溶融転写方式の受像層を
形成する結着剤、或いは熱拡散性色素転写方式の受像層
を形成するバインダー樹脂を適時選択して用いることが
でき、更に、インクの吸油性を改善するためには多孔質
顔料を添加するのが好ましく、このような多孔質顔料
は、溶融転写方式の受像層に添加される顔料を適時選択
して用いることができる。これらの多孔質顔料は、１種
単独で使用してもよいし、２種以上併用してもよく、通
常、受像層形成組成物全量に対し５〜95重量％、更には
10〜80重量％添加するのが好ましい。その他に、顔料分
散剤、増粘剤、流動性改良剤、消泡剤、抑泡剤、離型
剤、発泡剤、浸透剤、着色顔料、着色染料、蛍光増白
剤、紫外線吸収剤、酸化防止剤、防腐剤、防黴剤、帯電
防止剤、熱溶剤などの各種添加剤を必要に応じて適時添
加することができる。As the binder resin, a binder forming an image receiving layer of a melt transfer system or a binder resin forming an image receiving layer of a heat diffusible dye transfer system can be appropriately selected and used. In order to improve the above, it is preferable to add a porous pigment, and as such a porous pigment, a pigment added to the image-receiving layer of the melt transfer system can be appropriately selected and used. These porous pigments may be used alone or in combination of two or more, and usually 5 to 95% by weight based on the total amount of the image receiving layer forming composition, and further,
It is preferable to add 10 to 80% by weight. In addition, pigment dispersants, thickeners, fluidity improvers, defoamers, foam suppressors, mold release agents, foaming agents, penetrants, colored pigments, colored dyes, optical brighteners, ultraviolet absorbers, oxidation agents. Various additives such as an inhibitor, an antiseptic, an antifungal agent, an antistatic agent, and a heat solvent can be appropriately added as needed.
【００７２】一方、電子写真法に適した受像層として
は、トナー画像定着工程時に掛けられる温度、圧力、時
間によっても異なるが、上述の熱転写記録法の溶融熱転
写の受像層、熱拡散性色素転写の受像層、インクジェッ
ト記録法における受像層を適時選択して用いることもで
きる。On the other hand, the image-receiving layer suitable for the electrophotographic method varies depending on the temperature, pressure and time applied during the toner image fixing process, but the image-receiving layer for the thermal fusion recording in the above-mentioned thermal transfer recording method, the thermal diffusible dye transfer. The image receiving layer and the image receiving layer in the ink jet recording method can be appropriately selected and used.
【００７３】接着層は、それ自身常温で接着性を有する
物、圧力を掛けることにより接着性を発現するもの、或
いは熱を掛けることにより接着性を発現するものを含
み、例えば、軟化点の低い樹脂、接着付与剤などと、熱
溶融性物質及び／又は熱可塑性物質を混合することによ
り形成される。又、前記熱溶融性物質及び／又は熱可塑
性物質からなる樹脂層の表面に接着剤組成物を積層して
形成することもできる。或いは、接着性物質を公知の方
法でマイクロカプセルに閉じ込めた形のものを、前記熱
溶融性物質及び／又は熱可塑性物質からなる樹脂層に含
有させ形成することもできる。The adhesive layer includes a substance having adhesiveness at room temperature, a substance exhibiting adhesiveness when pressure is applied, or a substance exhibiting adhesiveness when heat is applied. For example, the adhesive layer has a low softening point. It is formed by mixing a resin, an adhesion-imparting agent and the like with a heat-meltable substance and / or a thermoplastic substance. Alternatively, the adhesive composition may be laminated on the surface of the resin layer made of the heat-meltable substance and / or the thermoplastic substance. Alternatively, it is also possible to form the adhesive material by encapsulating it in a microcapsule by a known method in the resin layer made of the heat melting material and / or the thermoplastic material.
【００７４】なお、接着層の厚みは、通常、0.1〜20μm
であり、好ましくは0.3〜10μmである。The thickness of the adhesive layer is usually 0.1 to 20 μm.
And preferably 0.3 to 10 μm.
【００７５】剥離層は、その上に積層される層との剥離
性が確保できれば特に制限はなく、又、剥離層形成樹脂
が自己支持性のあるものも本発明では好適に用いられ
る。The release layer is not particularly limited as long as the release property with the layer laminated thereon can be secured, and a release layer forming resin having a self-supporting property is also preferably used in the present invention.
【００７６】剥離層は、従来から公知の離型性を有する
化合物、及び必要に応じて各種添加剤とで構成すること
ができる。即ち、必要に応じてバインダー樹脂、及び酸
素クエンチャー、熱溶融性化合物、酸化防止剤、フィラ
ー、帯電防止剤などの各種添加剤とから構成することが
でき、剥離層の厚みは用途により適時選択されるが、自
己支持性のある場合は通常10〜50μmが好ましく、10〜2
5μmがより好ましい。又、後述する塗工法で設ける場合
は0.01〜５μmが好ましく、より好ましくは0.05〜２μm
である。The release layer can be composed of a conventionally known compound having releasability and, if necessary, various additives. That is, it can be composed of a binder resin and various additives such as an oxygen quencher, a heat-fusible compound, an antioxidant, a filler, and an antistatic agent, if necessary. However, when it is self-supporting, it is usually preferably 10 to 50 μm and 10 to 2 μm.
5 μm is more preferable. When it is provided by the coating method described later, it is preferably 0.01 to 5 μm, more preferably 0.05 to 2 μm.
Is.
【００７７】接着層兼剥離層は、上述の接着層形成成分
及び剥離層形成成分を適時選択して混合することにより
構成することができ、その厚みは通常0.05〜10μmが好
ましく、0.1〜５μmがより好ましい。The adhesive layer / release layer can be constituted by appropriately selecting and mixing the above-mentioned adhesive layer forming component and release layer forming component, and the thickness thereof is usually preferably 0.05 to 10 μm, and 0.1 to 5 μm is preferable. More preferable.
【００７８】保護層は、画像保存性、耐指紋性、耐引っ
掻き性など用途に応じて画像形成された表面を保護する
目的のものであれば特に制限なく用いることができる。
保護層とは、一般に用いられている透明支持体と接着層
とから構成されるラミネートシートや、支持体は転写せ
ずに樹脂層のみを転写させる転写箔を指し、その何れも
用途に応じて使用できる。このような、保護層として好
ましいものは、樹脂層のみを転写させる転写箔では、紫
外線吸収剤や光安定剤等を含有しているものがより好ま
しく、具体的には、特開昭58-149048号、特開平5-92670
号、同5-124362号等に記載されているものを適時選択し
て用いることができる。The protective layer may be used without particular limitation as long as it has a purpose of protecting the surface on which an image is formed, such as image storability, fingerprint resistance, scratch resistance, etc.
The protective layer refers to a laminate sheet composed of a transparent support and an adhesive layer that are generally used, or a transfer foil that transfers only the resin layer without transferring the support, any of which depends on the application. Can be used. Such a preferable protective layer is a transfer foil for transferring only the resin layer, and more preferably contains an ultraviolet absorber, a light stabilizer, or the like, and specifically, it is described in JP-A-58-149048. No. 5-92670
No. 5-124362, etc. can be selected and used as appropriate.
【００７９】保護層の厚みは、転写箔のように樹脂層の
みを転写する場合には、通常0.1〜10μmであり、好まし
くは0.3〜５μmである。又、ラミネートシートの場合
は、通常３〜200μmであり、好ましくは５〜100μmであ
る。The thickness of the protective layer is usually 0.1 to 10 μm, and preferably 0.3 to 5 μm when only the resin layer is transferred like a transfer foil. In the case of a laminated sheet, it is usually 3 to 200 μm, preferably 5 to 100 μm.
【００８０】[0080]
【実施例】以下、実施例により本発明を更に具体的に説
明するが、本発明は、これらの実施例に限定されるもの
ではない。なお、以下において「部」は、特に断りがな
い限り「有効成分としての重量部」を表す。The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples. In the following, "parts" represents "parts by weight as active ingredients" unless otherwise specified.
【００８１】本発明及び比較例としての受像層転写材料
を作成した。その構成を表１に示す。Image-receiving layer transfer materials of the present invention and comparative examples were prepared. The configuration is shown in Table 1.
【００８２】＜金属薄膜層・顔料層転写材料＞ ａ）支持体（厚み25μmのポリエチレンテレフタレート
（ＰＥＴ）フィルム：ダイアホイルヘキスト社製Ｓ）の
片面に、下記組成の剥離層形成塗工液、顔料層形成塗工
液、蒸着アンカー層形成塗工液を、ワイヤーバーコーテ
ィングにより順次塗布・乾燥し、それぞれ0.5μm、2.5
μm、0.1μmの厚さの剥離層、顔料層、蒸着アンカー層
を形成。<Metal thin film layer / pigment layer transfer material> a) A support (polyethylene terephthalate (PET) film having a thickness of 25 μm: S manufactured by DIAFOIL Hoechst Co., Ltd.) is coated on one side with a release layer-forming coating solution having the following composition, and a pigment. The layer-forming coating liquid and the vapor deposition anchor layer-forming coating liquid are applied and dried sequentially by wire bar coating, and 0.5 μm and 2.5 μm, respectively.
A peeling layer, a pigment layer, and a vapor deposition anchor layer with a thickness of 0.1 μm are formed.
【００８３】剥離層形成塗工液 シリコーン変性ポリイミド樹脂 2.5部 （住友ベークライト社製：スミレジンエクセルCRC7010） ジオキサン 97.5部顔料層形成塗工液 アクリル系樹脂 6.5部 （三菱レイヨン社製：ダイアナールBR-87） エチレン-酢酸ビニル共重合体 1.3部 （日本合成化学社製：ソアレックスR-DH） ロジンエステル（ハリマ化成社製：ハリエスターDS-90） 3.7部 酸化チタン分散物（御国色素社製：MHIホワイト＃148） 38.5部 メチルエチルケトン 50部蒸着アンカー層形成塗工液 アクリル系樹脂 20部 （三菱レイヨン社製：ダイアナールBR-83） 酢酸エチル 80部 上記蒸着アンカー層上に、金属蒸着法により厚み400Å
のアルミニウム金属薄膜層を形成した後に、下記の組成
の接着層形成塗工液を調製し、ワイヤーバーコーティン
グにより塗布・乾燥し、厚さ3.0μmの接着層を形成し、
金属薄膜層及び顔料層転写材料を作成（図１−ｃ）。 Release Layer Forming Coating Liquid Silicone Modified Polyimide Resin 2.5 parts (Sumitomo Bakelite Co., Ltd .: Sumiresin Excel CRC7010) Dioxane 97.5 parts Pigment layer forming coating liquid 6.5 parts (Mitsubishi Rayon Co., Ltd .: DIANAR BR-87) ) Ethylene-vinyl acetate copolymer 1.3 parts (Nippon Gosei Chemical Co., Ltd .: Sorex R-DH) Rosin ester (Harima Kasei Co., Ltd .: Harrier Star DS-90) 3.7 parts Titanium oxide dispersion (Mikuni Pigment Co., Ltd .: MHI White # 148) 38.5 parts Methyl ethyl ketone 50 parts Vapor deposition anchor layer forming coating liquid Acrylic resin 20 parts (Mitsubishi Rayon Co., Ltd .: Dianaal BR-83) Ethyl acetate 80 parts Thickness 400Å on the vapor deposition anchor layer by the metal vapor deposition method.
After forming the aluminum metal thin film layer of, to prepare an adhesive layer forming coating liquid of the following composition, apply and dry by wire bar coating, to form an adhesive layer of thickness 3.0μm,
A metal thin film layer and a pigment layer transfer material are prepared (Fig. 1-c).
【００８４】接着層形成塗工液 塩化ビニル-酢酸ビニル共重合体系樹脂 20部 （ユニオンカーバイト社製：VYHH） メチルエチルケトン 80部 ｂ）支持体（厚み4.5μmのＰＥＴフィルム、東レ社製：
ルミラー5AF531）の耐熱滑性層の反対面に、下記組成の
接着層兼剥離層形成塗工液を、ワイヤーバーコーティン
グにより塗布・乾燥し、厚さ0.5μmの接着層兼剥離層を
形成。 Adhesive Layer Forming Coating Liquid Vinyl Chloride-Vinyl Acetate Copolymer Resin 20 Parts (Union Carbide Co .: VYHH) Methyl Ethyl Ketone 80 Parts b) Support (PET Film of 4.5 μm Thickness, Toray Co .:
Lumirror 5AF531) is coated on the opposite side of the heat resistant slipping layer with a coating liquid for forming an adhesive layer / release layer having the following composition by wire bar coating and dried to form an adhesive layer / release layer having a thickness of 0.5 μm.
【００８５】接着層兼剥離層形成塗工液 エチレン-酢酸ビニル共重合体 10部 （三井・デュポンポリケミカル社製：エバフレックスEV210） シリコーン系樹脂 10部 （東亜合成化学工業社製：サイマックUS270） メチルエチルケトン 20部 トルエン 60部 上記接着層兼剥離層上に、スパッタリング法により厚み
300Åの亜鉛金属薄膜層を形成した後に、下記組成の顔
料層形成塗工液、接着層形成塗工液を、ワイヤーバーコ
ーティングにより順次塗布・乾燥し、それぞれ厚さ3.0
μm、2.0μmの顔料層、接着層を形成し、金属薄膜層及
び顔料層転写材料を作成（図７−ｂ）。 Adhesive layer / release layer forming coating solution 10 parts of ethylene-vinyl acetate copolymer (Mitsui DuPont Polychemical Co., Ltd .: EVAflex EV210) Silicone resin 10 parts (Toagosei Chemical Industry Co., Ltd .: Cymac US270) Methyl ethyl ketone 20 parts Toluene 60 parts Thickness on the above adhesive layer / release layer by sputtering method
After forming a 300 Å zinc metal thin film layer, a pigment layer forming coating solution and an adhesive layer forming coating solution of the following composition are sequentially applied by wire bar coating and dried, each with a thickness of 3.0
A pigment layer and an adhesive layer having a thickness of μm and 2.0 μm are formed to prepare a metal thin film layer and a pigment layer transfer material (FIG. 7-b).
【００８６】顔料層形成塗工液 ポリビニルアセタール系樹脂 5部 （積水化学工業社製：エスレックKW-1） 炭酸カルシウム 10部 （日東粉加工業社製：NITOREX ＃80） 蒸溜水 85部接着層形成塗工液 アクリル系樹脂 8部 （三菱レーヨン社製：ダイアナールBR-106） シリコーン樹脂粒子 2部 （東芝シリコーン社製：トスパース120） メチルエチルケトン 90部 ＜受像層転写材料＞ ａ）支持体（厚み25μmのＰＥＴフィルム：前出）の片
面に、下記組成の剥離層形成塗工液、顔料層形成塗工
液、蒸着アンカー層形成塗工液を、ワイヤーバーコーテ
ィングにより順次塗布・乾燥し、それぞれ厚さ0.5μm、
2.5μm、0.1μmの剥離層、受像層、接着層を形成し、受
像層転写材料を作成（図２−ｃ）。 Pigment layer forming coating solution Polyvinyl acetal resin 5 parts (Sekisui Chemical Co., Ltd .: S-REC KW-1) Calcium carbonate 10 parts (Nitto Kakoh Co., Ltd .: NITOREX # 80) Distilled water 85 parts Adhesive layer formation Coating liquid Acrylic resin 8 parts (Mitsubishi Rayon Co., Ltd .: DIANAR BR-106) Silicone resin particles 2 parts (Toshiba Silicone Co .: Tospers 120) Methyl ethyl ketone 90 parts <Image-receiving layer transfer material> a) Support (25 μm thick) On one side of the PET film: the above), a release layer forming coating solution, a pigment layer forming coating solution, and a vapor deposition anchor layer forming coating solution having the following compositions are sequentially applied by wire bar coating and dried, and each has a thickness of 0.5. μm,
An image receiving layer transfer material is prepared by forming a 2.5 μm and 0.1 μm release layer, an image receiving layer, and an adhesive layer (FIG. 2-c).
【００８７】剥離層形成塗工液 シリコーン変性ポリイミド樹脂 2.5部 （スミレジンエクセルCRC7010：前出） ジオキサン 97.5部受像層形成塗工液 ポリビニルアルコール 5.0部 （日本合成化学社製：ゴーセノールGL-05） カオリン 15部 （土屋カオリン工業社製：ASP-170） 界面活性剤（BASF社製：FT248） 0.03部 蒸溜水 80部接着層形成塗工液 ヒドロキシプロピルセルロース 10部 （信越化学工業社製：信越HPC EF-G） アクリル系樹脂 40部 （東亜合成化学工業社製：アロンタックHVC-5200） 蒸溜水 50部 ｂ）受像層形成塗工液を下記組成に変えた以外は、(ａ)
と同様に塗布・乾燥し、厚み2.0μmの受像層を有する受
像層転写材料を作成。 Release Layer Forming Coating Liquid Silicone Modified Polyimide Resin 2.5 Parts (Sumiresin Excel CRC7010: As Above) Dioxane 97.5 parts Image Receiving Layer Forming Coating Solution Polyvinyl Alcohol 5.0 parts (Nippon Gosei Kagaku GL-05) Kaolin 15 parts (Tsuchiya Kaolin Co., Ltd .: ASP-170) Surfactant (BASF: FT248) 0.03 parts Distilled water 80 parts Adhesive layer forming coating solution Hydroxypropyl cellulose 10 parts (Shin-Etsu Chemical Co., Ltd .: Shin-Etsu HPC EF) -G) Acrylic resin 40 parts (Toa Gosei Kagaku Kogyo Co., Ltd .: Arontack HVC-5200) Distilled water 50 parts b) Image receiving layer forming coating liquid was changed to the following composition (a)
Apply and dry in the same manner as above to create an image-receiving layer transfer material that has an image-receiving layer with a thickness of 2.0 μm.
【００８８】 メチルセルロース 5.0部 （信越化学工業社製：メトローズSM-15） 炭酸カルシウム（日東粉加工業社製：NS#3000） 15部 界面活性剤（FT248：前出） 0.03部 蒸溜水 80部 ｃ）受像層形成塗工液を下記組成に変えた以外は、(ａ)
と同様に塗布・乾燥し、厚み7.0μmの受像層を有する受
像層転写材料を作成。Methylcellulose 5.0 parts (Shin-Etsu Chemical Co., Ltd .: Metroz SM-15) Calcium carbonate (Nitto Powder Processing Co., Ltd .: NS # 3000) 15 parts Surfactant (FT248: above) 0.03 parts Distilled water 80 parts c ) (A) except that the composition for the image receiving layer forming coating is changed to the following composition
Apply and dry in the same manner as above to prepare an image receiving layer transfer material having an image receiving layer with a thickness of 7.0 μm.
【００８９】 ポリビニルブチラール 7.0部 （積水化学工業社製：エスレックBX-1） シリコーン樹脂粒子（トスパース120：前出） 2.0部 p-ベンジルビフェニル 0.5部 変性シリコーン樹脂（信越化学工業社製：X-24-8300） 0.5部 メチルエチルケトン 45部 トルエン 45部 ｄ）受像層形成塗工液を下記組成に変えた以外は、(ａ)
と同様に塗布・乾燥し、厚み4.0μmの受像層を有する受
像層転写材料を作成。Polyvinyl butyral 7.0 parts (Sekisui Chemical Co., Ltd .: S-REC BX-1) Silicone resin particles (Tospers 120: above) 2.0 parts p-benzylbiphenyl 0.5 parts Modified silicone resin (Shin-Etsu Chemical Co., Ltd .: X-24 -8300) 0.5 part Methyl ethyl ketone 45 parts Toluene 45 parts d) Except that the composition of the image receiving layer forming coating liquid was changed to the following composition (a)
Apply and dry in the same manner as above to prepare an image-receiving layer transfer material having an image-receiving layer with a thickness of 4.0 μm.
【００９０】 ポリビニルアセトアセタール 7.5部 （積水化学工業社製：エスレックKS-1） ビフェニル 2.0部 変性シリコーン樹脂（X-24-8300：前出） 0.5部 メチルエチルケトン 45部 トルエン 45部 ｅ）受像層形成塗工液を下記組成に変えた以外は、(ａ)
と同様に塗布・乾燥し、厚み5.0μmの受像層を形成し、
受像層転写材料を作成。Polyvinyl acetoacetal 7.5 parts (Sekisui Chemical Co., Ltd .: S-REC KS-1) Biphenyl 2.0 parts Modified silicone resin (X-24-8300: above) 0.5 parts Methyl ethyl ketone 45 parts Toluene 45 parts e) Image receiving layer forming coating (A) except that the working fluid was changed to the following composition
Apply and dry in the same manner as above to form an image receiving layer with a thickness of 5.0 μm,
Create image receiving layer transfer material.
【００９１】 ヒドロキシプロピルセルロース（信越HPC EF-G：前出） 5.0部 合成シリカ（富士シリシア化学社製：サイリシア350） 13部 界面活性剤（FT248：前出） 0.03部 蒸溜水 85部 ｆ）受像層形成塗工液を下記組成に変えた以外は、(ａ)
と同様に塗布・乾燥し、厚み5.0μmの受像層を有する受
像層転写材料を作成。Hydroxypropyl cellulose (Shin-Etsu HPC EF-G: supra) 5.0 parts Synthetic silica (Fuji Silysia Chemical Ltd .: Silysia 350) 13 parts Surfactant (FT248: supra) 0.03 parts Distilled water 85 parts f) Image reception (A) except that the layer-forming coating solution was changed to the following composition
Apply and dry in the same manner as above to prepare an image-receiving layer transfer material having an image-receiving layer with a thickness of 5.0 μm.
【００９２】 ポリビニルアセタール系樹脂（エスレックKW-1：前出） 5.0部 合成シリカ（富士シリシア化学社製：サイリシア250N） 7.0部 炭酸カルシウム（NS#3000：前出） 6.0部 界面活性剤（FT248：前出） 0.03部 蒸溜水 82部 ｇ）上記(ｂ)から接着層を省いた以外は、(ｂ)と同じ厚
みで剥離層、受像層を有する受像層転写材料を作成（図
12−ｂ）。Polyvinyl acetal resin (S-REC KW-1: supra) 5.0 parts Synthetic silica (Fuji Silysia Chemical Ltd .: Silysia 250N) 7.0 parts Calcium carbonate (NS # 3000: supra) 6.0 parts Surfactant (FT248: (Obvious) 0.03 parts Distilled water 82 parts g) An image-receiving layer transfer material having a release layer and an image-receiving layer with the same thickness as in (b) was prepared except that the adhesive layer was omitted from (b) above (Fig.
12-b).
【００９３】ｈ）上記(ｄ)から接着層を省いた以外は、
(ｄ)と同じ厚みで剥離層、受像層を形成し、受像層転写
材料を作成。H) except that the adhesive layer was omitted from (d) above.
An image receiving layer transfer material was prepared by forming a release layer and an image receiving layer with the same thickness as in (d).
【００９４】ｉ）上記(ｆ)から接着層を省いた以外は、
(ｆ)と同じ厚みで剥離層、受像層を形成し、受像層転写
材料を作成。I) except that the adhesive layer is omitted from (f) above.
A release layer and an image receiving layer are formed with the same thickness as in (f) to prepare an image receiving layer transfer material.
【００９５】＜金属薄膜層転写材料＞ ａ）支持体（厚み25μmのＰＥＴフィルム、前出）の片
面に下記の組成の蒸着アンカー層形成塗工液を、ワイヤ
ーバーコーティングにより塗布・乾燥し、厚さ0.1μmの
蒸着アンカー層を形成（図４−ａ）。<Metal thin film layer transfer material> a) A coating liquid for vapor deposition anchor layer formation having the following composition is applied to one side of a support (PET film having a thickness of 25 μm, described above) by wire bar coating and dried to give a thickness. A 0.1 μm thick vapor-deposited anchor layer is formed (Fig. 4-a).
【００９６】蒸着アンカー層形成塗工液 アクリル系樹脂（ダイアナールBR-87：前出） 10部 メチルエチルケトン 90部 上記蒸着アンカー層上に、金属蒸着法により厚み400Å
のテルル金属薄膜層を形成した後に、下記組成の接着層
形成塗工液をワイヤーバーコーティングにより塗布・乾
燥し、厚さ2.0μmの接着層を形成し、金属薄膜層転写材
料を作成（図４−ｃ）。 Vapor deposition anchor layer forming coating liquid Acrylic resin (Dianal BR-87: above) 10 parts Methyl ethyl ketone 90 parts On the above vapor deposition anchor layer, a thickness of 400 Å by metal vapor deposition method.
After forming the tellurium metal thin film layer, the adhesive layer forming coating solution having the following composition is applied by wire bar coating and dried to form an adhesive layer having a thickness of 2.0 μm to prepare a metal thin film layer transfer material (Fig. 4). -C).
【００９７】 エチレン-酢酸ビニル共重合体 3部 （三井・デュポンポリケミカル社製：エバフレックスEV410） トルエン 97部 ｂ）支持体を厚み4.5μmのＰＥＴフィルム（前出）に変
えた以外は、(ａ)と同様にして金属薄膜層転写材料を作
成。Ethylene-vinyl acetate copolymer 3 parts (Mitsui DuPont Polychemical Co .: Evaflex EV410) Toluene 97 parts b) Except that the support was changed to a PET film of 4.5 μm in thickness (described above) ( A metal thin film layer transfer material is prepared in the same manner as a).
【００９８】ｃ）支持体として厚み4.5μmのＰＥＴフィ
ルム（前出）を用い、蒸着アンカー層の代わりに下記組
成の剥離層兼接着層形成塗工液をワイヤーバーコーティ
ングにより塗布・乾燥し、厚さ2.0μmの接着層を形成し
た以外は、(ａ)と同様にして金属薄膜層転写材料を作成
（図19−ｃ）。C) A 4.5 μm-thick PET film (described above) was used as a support, and instead of the vapor deposition anchor layer, a release layer / adhesive layer forming coating solution having the following composition was applied and dried by wire bar coating to obtain a thickness. A metal thin film layer transfer material was prepared in the same manner as in (a) except that a 2.0 μm thick adhesive layer was formed (FIG. 19-c).
【００９９】剥離層兼接着層形成塗工液 エチレン-酢酸ビニル共重合体 5部 （日本合成化学社製：ソアレックスR-DH） アクリル系樹脂（ダイアナールBR-87：前出） 20部 メチルエチルケトン 75部 ｄ）支持体として厚み25μmのＰＥＴフィルム（前出）
に変えた以外は、(ｃ)と同様にして金属薄膜層転写材料
を作成。 Coating liquid for forming a peeling layer and an adhesive layer Ethylene-vinyl acetate copolymer 5 parts (Nippon Gosei Kagaku KK: Soarex R-DH) Acrylic resin (Dianal BR-87: supra) 20 parts Methyl ethyl ketone 75 Part d) PET film with a thickness of 25 μm as a support (supra)
A metal thin film layer transfer material was prepared in the same manner as in (c) except that the above was changed to.
【０１００】＜受像層・顔料層転写材料＞ ａ）支持体として厚み25μmのＰＥＴフィルム（前出）
を用い、受像層転写材料(ａ)で作成した剥離層、受像層
まで形成した受像層上に、金属薄膜層及び顔料層転写材
料(ａ)の顔料層、接着層を、該転写材料と同じ厚みにな
るよう順次塗布・乾燥し、受像層・顔料層転写材料を作
成（図５−ｂ）。<Image-Receiving Layer / Pigment Layer Transfer Material> a) PET film having a thickness of 25 μm as a support (described above)
On the release layer made of the image-receiving layer transfer material (a) and the image-receiving layer formed up to the image-receiving layer, the metal thin film layer and the pigment layer and the adhesive layer of the pigment layer transfer material (a) are the same as those of the transfer material. Coat and dry to the desired thickness to create the image-receiving layer / pigment layer transfer material (Fig. 5-b).
【０１０１】ｂ）支持体として厚み25μmのＰＥＴフィ
ルム（前出）を用い、受像層転写材料(ｃ)で作成した剥
離層、受像層まで形成した受像層上に、金属薄膜層及び
顔料層転写材料(ａ)の顔料層、接着層を、該転写材料と
同じ厚みになるよう順次塗布・乾燥し、受像層・顔料層
転写材料を作成。B) A 25 μm-thick PET film (described above) was used as a support, and a metal thin film layer and a pigment layer were transferred onto the peeling layer prepared from the image-receiving layer transfer material (c) and the image-receiving layer formed up to the image-receiving layer. The pigment layer and the adhesive layer of the material (a) are sequentially applied and dried so as to have the same thickness as the transfer material to prepare an image receiving layer / pigment layer transfer material.
【０１０２】ｃ）支持体として厚み25μmのＰＥＴフィ
ルム（前出）を用い、受像層転写材料(ｅ)で作成した剥
離層、受像層まで形成した受像層上に、金属薄膜層及び
顔料層転写材料(ａ)の顔料層、接着層を、該転写材料と
同じ厚みになるよう順次塗布・乾燥し、受像層・顔料層
転写材料を作成。C) A 25 μm-thick PET film (described above) was used as a support, and a metal thin film layer and a pigment layer were transferred onto the peeling layer prepared from the image-receiving layer transfer material (e) and the image-receiving layer formed up to the image-receiving layer. The pigment layer and the adhesive layer of the material (a) are sequentially applied and dried so as to have the same thickness as the transfer material to prepare an image receiving layer / pigment layer transfer material.
【０１０３】＜顔料層転写材料＞ ａ）支持体（厚み25μmのＰＥＴフィルム：前出）の片
面に、下記組成の剥離層形成塗工液をワイヤーバーコー
ティングにより塗布・乾燥し、厚さ0.1μmの剥離層を形
成した後、その上に金属薄膜層及び顔料層転写材料(ａ)
の顔料層、及び(ｂ)の接着層を、それぞれ同じ厚みで形
成し、顔料層転写材料を作成（図７−ｃ）。<Pigment layer transfer material> a) A release layer-forming coating solution having the following composition is applied to one side of a support (25-μm-thick PET film: described above) by wire bar coating and dried to a thickness of 0.1 μm. After forming the release layer, the metal thin film layer and the pigment layer transfer material (a)
The pigment layer of (1) and the adhesive layer of (b) are formed with the same thickness to prepare a pigment layer transfer material (Fig. 7-c).
【０１０４】剥離層形成塗工液 シリコーン変性ポリイミド樹脂 2.5部 （住友ベークライト社製：スミレジンエクセルCRC7025） ジオキサン 97.5部 ｂ）支持体として厚み4.5μmのＰＥＴレートフィルム
（前出）に変えた以外は、(ａ)と同様にして顔料層転写
材料を作成。 Release Layer Forming Coating Liquid Silicone-Modified Polyimide Resin 2.5 parts (Sumitomo Bakelite Co., Ltd .: Sumirezin Excel CRC7025) Dioxane 97.5 parts b) A PET rate film (previously described) having a thickness of 4.5 μm was used as a support. A pigment layer transfer material is prepared in the same manner as in (a).
【０１０５】ｃ）顔料層の厚みを15μmにした以外は
(ａ)と同様の方法で顔料層転写材料を作成。C) except that the thickness of the pigment layer is 15 μm
A pigment layer transfer material is prepared in the same manner as in (a).
【０１０６】＜保護層転写材料＞ ａ）厚み25μmのＰＥＴフィルム（前出）のコロナ放電
処理した面に、下記組成の剥離層形成塗工液、保護層形
成塗工液、接着層形成塗工液をワイヤーバーコーティン
グ法により順次塗布・乾燥し、それぞれ厚み0.1、2.0、
0.2μmになるように剥離層、保護層、接着層を形成し、
保護層のみを転写させる保護層転写材料を作成（図10−
ｃ）。<Protective Layer Transfer Material> a) A 25 μm-thick PET film (described above) on the surface subjected to corona discharge treatment, a release layer forming coating solution, a protective layer forming coating solution, and an adhesive layer forming coating having the following composition: Liquid is applied and dried sequentially by the wire bar coating method, and the thickness is 0.1, 2.0,
Form a release layer, a protective layer, and an adhesive layer to a thickness of 0.2 μm,
Create a protective layer transfer material that transfers only the protective layer (Fig. 10-
c).
【０１０７】剥離層形成塗工液 ニトロセルロース 4部 （旭化成工業社製：セルノバBTH1/2） 変性シリコーン樹脂 4部 （大日精化工業社製：ダイアロマーSP-712） メチルエチルケトン 92部保護層形成塗工液 ポリメチルメタクリレート 20部 （三菱レイヨン社製：ダイアナールBR-83） 酸化亜鉛 20部 （住友セメント社製：超微粒子酸化亜鉛ZnO-100） 光安定剤・酸化防止剤 2部 （チバ・ガイギー社製、イルガノックスB225） メチルエチルケトン 58部接着層形成塗工液 塩化ビニル系樹脂（ユニオンカーバイト社製：VYHH） 20部 メチルエチルケトン 80部 ＜画像記録体作成方法＞以下に述べる画像記録体作成方
法において、溶融熱転写記録には三菱ラインサーマルカ
ラープリンターG370型（三菱電機社製）とプリンター専
用のインクシート、昇華型熱転写記録には三菱フルカラ
ープリンターS3600-30形（三菱電機社製）とプリンター
専用のインクシート、電子写真による画像記録にはフル
カラー複写機U-Bix9028（コニカ社製）と複写機専用ト
ナー、インクジェット記録にはインクジェットプリンタ
ーPIXEL JET（キャノン社製）とプリンター専用のイン
クを用いた。 Release layer forming coating solution Nitrocellulose 4 parts (Casanova BTH1 / 2 manufactured by Asahi Kasei Kogyo Co., Ltd.) Modified silicone resin 4 parts (Diaichi Seika Kogyo Co., Ltd .: Dialomer SP-712) Methyl ethyl ketone 92 parts Protective layer forming coating Liquid polymethylmethacrylate 20 parts (Mitsubishi Rayon Co., Ltd .: Dianal BR-83) Zinc oxide 20 parts (Sumitomo Cement Co .: ultrafine zinc oxide ZnO-100) Light stabilizers / antioxidants 2 parts (Ciba Geigy Co.) , Irganox B225) Methyl ethyl ketone 58 parts Adhesive layer forming coating liquid Vinyl chloride resin (VYHH manufactured by Union Carbite Co., Ltd.) 20 parts Methyl ethyl ketone 80 parts <Image recording material preparation method> In the image recording material preparation method described below, melt For thermal transfer recording, Mitsubishi line thermal color printer G370 type (manufactured by Mitsubishi Electric Corp.) and printer ink sheet, for sublimation type thermal transfer recording Rishi full color printer S3600-30 type (manufactured by Mitsubishi Electric) and printer dedicated ink sheet, full color copier U-Bix9028 (manufactured by Konica) and copier toner for electrophotographic image recording, inkjet printer for inkjet recording PIXEL JET (manufactured by Canon Inc.) and printer-specific ink were used.
【０１０８】又、表１中の画像形成方法ａ、ｂ、ｃ、ｄ
は、それぞれ溶融熱転写記録、昇華型熱転写記録、電子
写真による画像記録及びインクジェット記録による画像
形成を指す。Further, the image forming methods a, b, c, d in Table 1
Indicates melt thermal transfer recording, sublimation type thermal transfer recording, image recording by electrophotography and image formation by inkjet recording, respectively.
【０１０９】１）基材として、Ａ４の印刷の施された15
7ｇ／m2のコート紙（山陽国策パルプ社製、エスプリコ
ートＣ）の印刷面と、金属薄膜層及び顔料層転写材料の
接着層面とを対面させて、10cm×10cmの面積のホットス
タンプで加熱・加圧処理（140℃、２kg／cm2、５秒）す
ることにより顔料層まで形成し、次いで該顔料層面と受
像層転写材料の接着層面とを対面させ、顔料層を形成し
た部分のみにホットスタンプで加熱・加圧処理（10cm×
10cm、120℃、３kg／cm2、10秒）することにより受像層
を基材上に形成した。1) 15 printed with A4 as a base material
The printed surface of 7 g / m 2 coated paper (Sanyo Kokusaku Pulp Co., Espricoat C) is made to face the metal thin film layer and the adhesive layer of the pigment layer transfer material, and heated with a hot stamp of 10 cm × 10 cm area.・ By applying pressure treatment (140 ° C., 2 kg / cm 2 , 5 seconds), the pigment layer is formed, and then the pigment layer surface and the adhesive layer surface of the image-receiving layer transfer material are made to face each other, and only the portion where the pigment layer is formed is formed. Heat and pressure treatment with hot stamp (10 cm x
The image receiving layer was formed on the substrate by applying 10 cm, 120 ° C., 3 kg / cm 2 , 10 seconds).
【０１１０】このようにして作成した受像層上に画像記
録し、記録画像の画像ベタ部の濃度むら、画像形成可能
な転写領域において画像形成されていない部分の濃度む
ら、顔料層部分のエッジの切れを下記の基準で評価した
結果を表１に示す。An image is recorded on the image-receiving layer thus created, and the uneven density of the solid image portion of the recorded image, the uneven density of the non-imaged portion in the transfer area where the image can be formed, and the edge of the pigment layer portion Table 1 shows the results of evaluation of breakage based on the following criteria.
【０１１１】≪画像ベタ部の濃度むら≫シアン画像部の
ベタ部（５cm×５cm）の濃度を、異なる100点で測定
し、平均値±0.100以内に入る測定点の数［Ｎ］で評
価。<< Density unevenness in solid image area >> The density of the solid image area (5 cm × 5 cm) in the cyan image area was measured at 100 different points, and evaluated by the number [N] of measurement points falling within an average value ± 0.100.
【０１１２】◎…95≦Ｎ ○…90≦Ｎ＜95 △…80≦Ｎ＜90 ×…Ｎ＜80 ≪画像形成されていない部分の濃度むら≫画像形成され
ていない部分（５cm×５cm）の濃度を、異なる100点で
測定し、平均値±0.050以内に入る測定点の数［Ｎ］で
評価。◎ ... 95 ≦ N ○ ... 90 ≦ N <95 Δ ... 80 ≦ N <90 × ... N <80 << Nonuniformity of density in non-imaged area >> of non-imaged area (5 cm × 5 cm) The density was measured at 100 different points and evaluated by the number [N] of measurement points within the average value ± 0.050.
【０１１３】◎…95≦Ｎ ○…90≦Ｎ＜95 △…80≦Ｎ＜90 ×…Ｎ＜80 ≪顔料層部分のエッジの切れ≫基材上に形成された顔料
層部分の直線性を、ある基準に対して、どれだけ離れて
いるかを測定し、「最大値−最小値」の値［Ｌ；単位μ
m］で評価。◎ ... 95 ≦ N ○ ... 90 ≦ N <95 Δ ... 80 ≦ N <90 × ... N <80 << cutting edge of pigment layer portion >> The linearity of the pigment layer portion formed on the substrate , The distance from a certain standard is measured, and the value of “maximum value-minimum value” [L; unit μ
It is evaluated by m].
【０１１４】◎…Ｌ≦100 ○…100＜Ｌ≦250 △…250＜Ｌ≦500 ×…500＜Ｌ ２）基材として、ネガ原稿を焼き付けた現像済みのハロ
ゲン化銀写真感光材料（印画紙：コニカ社製、コニカカ
ラーペーパーQA-A6）の原稿を焼き付けた面と、金属薄
膜層転写材料の接着面とを対面させて、10cm×10cmの面
積で熱転写プリンタ（日立工機社製：TL15A）で熱転写
することにより金属薄膜層を形成し、次いで蒸着アンカ
ー層面と顔料層及び受像層転写材料の接着層面とを対面
させ、金属薄膜層を形成した部分のみにホットスタンプ
で加熱・加圧処理（10cm×10cm、100℃、５kg／cm2、10
秒）することにより受像層を基材上に形成した。◎ ... L ≦ 100 ○ ... 100 <L ≦ 250 △ ... 250 <L ≦ 500 × ... 500 <L 2) A developed silver halide photographic light-sensitive material (photographic paper) on which a negative original is printed as a base material. : Konica Color Paper QA-A6 made by Konica Co., Ltd. face the printed surface of the original with the adhesive surface of the metal thin film transfer material, and a thermal transfer printer (Hitachi Koki: TL15A: TL15A) with an area of 10 cm x 10 cm. ) To form a metal thin film layer, and then the vapor deposition anchor layer surface and the adhesive layer surface of the pigment layer and the image receiving layer transfer material are faced to each other, and only the portion where the metal thin film layer is formed is heated and pressed with a hot stamp. (10cm × 10cm, 100 ℃, 5kg / cm 2 , 10
To form an image receiving layer on the substrate.
【０１１５】このようにして作成した受像層上に画像記
録し、(１)と同じ基準で評価した結果を表１に示す。Table 1 shows the results obtained by recording an image on the image-receiving layer thus prepared and evaluating the same criteria as in (1).
【０１１６】３）基材として、厚み230μmの印刷された
テレホンカードの印刷面と金属薄膜層転写材料の接着面
とを対面させて、４cm×４cmの面積のホットスタンプで
加熱・加圧処理（140℃、２kg／cm2、５秒）することに
より金属薄膜層を形成し、順次顔料層転写材料、受像層
転写材料を、金属薄膜層を転写させた同じ位置へホット
スタンプで加熱・加圧処理（４cm×４cm、120℃、３kg
／cm2、10秒）することにより受像層を基材上に形成し
た。3) As a base material, the printed surface of a printed telephone card having a thickness of 230 μm and the adhesive surface of the metal thin film layer transfer material are faced to each other, and heat / pressure treatment is carried out with a hot stamp having an area of 4 cm × 4 cm ( A metal thin film layer is formed by heating at 140 ° C., 2 kg / cm 2 , 5 seconds), and the pigment layer transfer material and the image receiving layer transfer material are sequentially heated and pressed by a hot stamp to the same position where the metal thin film layer was transferred. Treatment (4cm × 4cm, 120 ℃, 3kg
/ Cm 2 , 10 seconds) to form an image receiving layer on the substrate.
【０１１７】このようにして作成した受像層上に画像記
録し、次いで保護層転写材料をテレホンカード全面にヒ
ートロールで加熱・加圧処理（10mm／秒、150℃、８kg
／cm）して画像記録体を作成した。An image is recorded on the image-receiving layer thus prepared, and then the protective layer transfer material is heated and pressed on the entire surface of the telephone card with a heat roll (10 mm / sec, 150 ° C., 8 kg).
/ Cm) to prepare an image recording material.
【０１１８】記録画像の画像ベタ部の濃度むら、画像形
成可能な転写領域において画像形成されていない部分の
濃度むらを下記の基準で、顔料層部分のエッジの切れを
(１)と同じ基準で評価した結果を表１に示す。The unevenness of the density of the solid image portion of the recorded image and the unevenness of the density of the non-imaged portion in the transfer area where the image can be formed are determined based on the following criteria, and the edge of the pigment layer portion is cut off.
Table 1 shows the results of evaluation based on the same criteria as (1).
【０１１９】≪画像ベタ部の濃度むら≫シアン画像部の
ベタ部（２cm×２cm）の濃度を、異なる64点で測定し、
平均値±0.100以内に入る測定点の数［Ｎ］で評価。<< Density unevenness in solid image area >> The density of the solid area (2 cm × 2 cm) of the cyan image area was measured at 64 different points,
Evaluated by the number of measurement points [N] within the average value ± 0.100.
【０１２０】◎…61≦Ｎ ○…58≦Ｎ＜61 △…51≦Ｎ＜58 ×…Ｎ＜51 ≪画像形成されていない部分の濃度むら≫画像形成され
ていない部分（２cm×２cm）の濃度を、異なる64点で測
定し、平均値±0.050以内に入る測定点の数［Ｎ］で評
価。⋅ ∙ 61 ≦ N ∘∶58 ≦ N <61 Δ ... 51 ≦ N <58 × ... N <51 << Density unevenness in non-imaged area >> in non-imaged area (2 cm × 2 cm) The density was measured at 64 different points and evaluated by the number [N] of measurement points within the average value ± 0.050.
【０１２１】◎…61≦Ｎ ○…58≦Ｎ＜61 △…51≦Ｎ＜58 ×…Ｎ＜51 ４）基材として、厚み750μmの印刷された塩化ビニルカ
ードの印刷面と金属薄膜層及び顔料層転写材料の接着層
面とを対面させて、３cm×３cmの面積のホットスタンプ
で加熱・加圧処理（140℃、２kg／cm2、５秒）すること
により顔料層までを形成した。その後に、別途受像層上
に画像形成を行った受像層転写材料を顔料層を転写させ
た同じ位置へホットスタンプで加熱・加圧処理（３cm×
３cm、120℃、３kg／cm2、10秒）することにより画像記
録体を作成した。◎ ... 61 ≦ N ○ ... 58 ≦ N <61 Δ ... 51 ≦ N <58 × ... N <51 4) As a base material, a printed surface of a vinyl chloride card having a thickness of 750 μm, a metal thin film layer, and The pigment layer transfer material was made to face the adhesive layer surface and subjected to heat / pressure treatment (140 ° C., 2 kg / cm 2 , 5 seconds) with a hot stamp having an area of 3 cm × 3 cm to form the pigment layer. After that, the image-receiving layer transfer material on which the image was formed separately on the image-receiving layer was heated / pressurized (3 cm x
3 cm, 120 ° C., 3 kg / cm 2 , 10 seconds) to prepare an image recording material.
【０１２２】このようにして作成した画像記録体の記録
画像の画像ベタ部の濃度むら、画像形成可能な転写領域
において画像形成されていない部分の濃度むらを下記の
基準で評価し、顔料層部分のエッジの切れを(１)と同じ
基準で評価した結果を表１に示す。The density unevenness of the solid image portion of the recorded image of the image recording material thus prepared and the density unevenness of the portion not imaged in the transfer area where the image can be formed are evaluated according to the following criteria, and the pigment layer portion Table 1 shows the results of evaluation of the edge breakage of (1) based on the same criteria as (1).
【０１２３】≪画像ベタ部の濃度むら≫シアン画像部の
ベタ部（３cm×1.5cm）の濃度を、異なる64点で測定
し、平均値±0.100以内に入る測定点の数［Ｎ］で評
価。<< Density unevenness in solid image area >> The density of the solid area (3 cm × 1.5 cm) of the cyan image area was measured at 64 different points and evaluated by the number [N] of the measurement points within the average value ± 0.100. .
【０１２４】◎…61≦Ｎ ○…58≦Ｎ＜61 △…51≦Ｎ＜58 ×…Ｎ＜51 ≪画像形成されていない部分の濃度むら≫画像形成され
ていない部分（３cm×1.5cm）の濃度を、異なる64点で
測定し、平均値±0.050以内に入る測定点の数［Ｎ］で
評価。∙ 61 ≤ N ∘ ... 58 ≤ N <61 △ ... 51 ≤ N <58 x ... N <51 << Density unevenness in non-imaged area >> Non-imaged area (3 cm x 1.5 cm) Was measured at 64 different points and evaluated by the number [N] of measurement points within the average value ± 0.050.
【０１２５】◎…61≦Ｎ ○…58≦Ｎ＜61 △…51≦Ｎ＜58 ×…Ｎ＜51 ５）基材として、Ａ４の印刷の施された157ｇ／m2のコ
ート紙（山陽国策パルプ社製：エスプリコートＣ）の印
刷面と金属薄膜層転写材料の接着層面とを対面させて、
10cm×10cmの面積のホットスタンプで加熱・加圧処理
（140℃、２kg／cm2、５秒)することにより金属薄膜層
を形成し、次いで該金属薄膜層面と顔料層転写材料の接
着層面とを対面させ、金属薄膜層を形成した部分のみに
ホットスタンプで加熱・加圧処理（10cm×10cm、120
℃、３kg／cm2、10秒）することにより顔料層を基材上
に形成した。その後に、別途受像層上に画像形成を行っ
た受像層転写材料を、顔料層を転写させた同じ位置へホ
ットスタンプで加熱・加圧処理（10cm×10cm、120℃、
３kg／cm2、10秒）することにより画像記録体を作成し
た。◎ ... 61 ≦ N ○ ... 58 ≦ N <61 Δ ... 51 ≦ N <58 × ... N <515 5) As a base material, A4 printed 157 g / m 2 coated paper (Sanyo Kunisaku) Pulp Co., Ltd .: The printed surface of Espricoat C) and the adhesive layer surface of the metal thin film layer transfer material are faced to each other,
A metal thin film layer is formed by heating and pressurizing (140 ° C., 2 kg / cm 2 , 5 seconds) with a hot stamp having an area of 10 cm × 10 cm, and then the metal thin film layer surface and the adhesive layer surface of the pigment layer transfer material are formed. Facing each other, and heat / pressurize only the part where the metal thin film layer is formed with a hot stamp (10 cm × 10 cm, 120 cm
° C., to form a pigment layer on a substrate by 3kg / cm 2, 10 seconds). After that, the image-receiving layer transfer material on which the image was separately formed on the image-receiving layer was heated / pressurized by a hot stamp at the same position where the pigment layer was transferred (10 cm × 10 cm, 120 ° C.,
3 kg / cm 2 , 10 seconds) to prepare an image recording material.
【０１２６】このようにして作成した画像記録体の、記
録画像の画像ベタ部の濃度むら、画像形成可能な転写領
域において画像形成されていない部分の濃度むら、顔料
層部分のエッジの切れを(１)の基準で評価した結果を表
１に示す。In the thus-produced image recording material, uneven density in a solid image portion of a recorded image, uneven density in a non-image formed portion in a transfer area where an image can be formed, and edge breakage in a pigment layer portion ( Table 1 shows the results of evaluation based on the criterion 1).
【０１２７】６）受像層上に画像形成を行った受像層転
写材料の受像層面と金属薄膜層及び顔料層転写材料の接
着層面とを対面させて、10cm×10cmの面積で熱転写プリ
ンタ（日立工機社製：TL15A）で熱転写することにより
画像形成された受像層上に金属薄膜層まで形成させた。6) A thermal transfer printer (Hitachi Co., Ltd.) having an area of 10 cm × 10 cm is prepared by making the image receiving layer surface of the image receiving layer transfer material on which an image is formed on the image receiving layer face the metal thin film layer and the adhesive layer surface of the pigment layer transfer material. (Trade name: TL15A manufactured by Kiki Co., Ltd.) was used to form a metal thin film layer on the image-receiving layer on which an image was formed by thermal transfer.
【０１２８】次いで、基材として、ネガ原稿を焼き付け
た現像済みのハロゲン化銀写真感光材料（印画紙：コニ
カ社製、コニカカラーペーパーQA-A6）の原稿を焼き付
けた面と、前述の画像形成された受像層上に金属薄膜層
まで形成させた受像層転写材料の接着層兼剥離層とを対
面させ、ヒートロールで加熱・加圧処理（10mm／秒、12
0℃、４kg／cm）し金属薄膜層を形成した部分のみを転
写させることにより画像記録体を作成した。Next, as a base material, the surface of the developed original silver halide photographic light-sensitive material (printing paper: Konica Color Paper QA-A6, printed by Konica Corporation), onto which a negative original was printed, and the above-mentioned image formation The image receiving layer transfer material having the metal thin film layer formed on the formed image receiving layer faces the adhesive layer / release layer of the transfer material, and is heated / pressurized by a heat roll (10 mm / sec, 12 mm
At 0 ° C., 4 kg / cm), an image recording material was prepared by transferring only the portion where the metal thin film layer was formed.
【０１２９】このようにして作成した画像記録体の、記
録画像の画像ベタ部の濃度むら、画像形成可能な転写領
域において画像形成されていない部分の濃度むら、顔料
層部分のエッジの切れを(１)の基準で評価した結果を表
１に示す。In the thus-produced image recording material, uneven density in the solid image portion of the recorded image, uneven density in the non-imaged portion in the transfer area where the image can be formed, and edge breakage in the pigment layer portion ( Table 1 shows the results of evaluation based on the criterion 1).
【０１３０】７）受像層上に画像形成を行った受像層転
写材料の受像層面と顔料層転写材料の接着層面とを対面
させて、４cm×４cmの面積で熱転写プリンタ（日立工機
社製：TL15A）で熱転写することにより画像形成された
受像層上に顔料層を転写させ、次いで、金属薄膜層転写
材料の接着層面とを対面させ、顔料層を形成した部分の
みに４cm×４cmの面積で熱転写プリンタで金属薄膜層を
熱転写させた。7) A thermal transfer printer (manufactured by Hitachi Koki Co., Ltd.) having an area of 4 cm × 4 cm with the image receiving layer surface of the image receiving layer transfer material on which the image is formed and the adhesive layer surface of the pigment layer transfer material facing each other. TL15A) to transfer the pigment layer on the image-receiving layer image-formed by thermal transfer, and then face the adhesive layer surface of the metal thin film layer transfer material, with an area of 4 cm x 4 cm only in the portion where the pigment layer is formed. The metal thin film layer was thermally transferred with a thermal transfer printer.
【０１３１】次いで、基材として、印刷の施された葉書
の印刷面と、前述の画像形成された受像層上に金属薄膜
層まで形成させた受像層転写材料の接着層兼剥離層とを
対面させ、ヒートロールで加熱・加圧処理（７mm／秒、
100℃、10kg／cm）し金属薄膜層を形成した部分のみを
転写させることにより画像記録体を作成した。Then, as a base material, the printed surface of the printed postcard and the adhesive layer / release layer of the image-receiving layer transfer material formed up to the metal thin film layer on the above-mentioned image-formed image-receiving layer face each other. And heat and pressure treatment with a heat roll (7 mm / sec,
An image recording material was prepared by transferring only the portion on which the metal thin film layer was formed at 100 ° C. and 10 kg / cm).
【０１３２】このようにして作成した画像記録体の、記
録画像の画像ベタ部の濃度むら、画像形成可能な転写領
域において画像形成されていない部分の濃度むらを
(３)、顔料層部分のエッジの切れを(１)の基準で評価し
た結果を表１に示す。The density unevenness of the solid image portion of the recorded image and the density unevenness of the non-image formed portion of the image-formed transfer area of the image recording medium thus formed
(3), Table 1 shows the results of evaluating the edge breakage of the pigment layer portion based on the criterion (1).
【０１３３】８）受像層上に画像形成を行った受像層転
写材料の受像層面と顔料層転写材料の接着層面とを対面
させて、ホットスタンプで加熱・加圧処理（４cm×4c
m、120℃、５kg／cm2、10秒）することにより画像形成
された受像層上に顔料層を転写させた。又、別途、印刷
が施されＩＣを片側に埋め込んだICカードを基材に用
い、ＩＣを埋め込んでいない部分へ３cm×３cmの面積の
ホットスタンプで加熱・加圧処理（130℃、２kg／cm2、
５秒）することにより金属薄膜層を転写させた。上述の
ように作成した画像形成された受像層上に顔料層まで形
成させた受像層転写材料の顔料層と、基材上に設けた金
属薄膜層の接着層兼剥離層とを対面させ、金属薄膜層を
形成したのと同じ位置へホットスタンプで加熱・加圧処
理（３cm×３cm、140℃、５kg／cm2、10秒）することに
より画像記録体を作成した。8) The image receiving layer surface of the image receiving layer transfer material on which the image is formed and the adhesive layer surface of the pigment layer transfer material are made to face each other, and heated and pressed by a hot stamp (4 cm × 4 c).
m, 120 ° C., 5 kg / cm 2 , 10 seconds) to transfer the pigment layer onto the image-receiving image-receiving layer. Separately, an IC card with a printed IC embedded on one side is used as the base material, and the area where the IC is not embedded is heated and pressed with a hot stamp of 3 cm x 3 cm (130 ° C, 2 kg / cm). 2 ,
5 seconds) to transfer the metal thin film layer. The pigment layer of the image-receiving layer transfer material formed up to the pigment layer on the image-formed image-receiving layer formed as described above is faced with the adhesive layer / release layer of the metal thin film layer provided on the substrate, An image recording medium was prepared by heating and pressurizing (3 cm × 3 cm, 140 ° C., 5 kg / cm 2 , 10 seconds) with a hot stamp at the same position where the thin film layer was formed.
【０１３４】このようにして作成した画像記録体の、記
録画像の画像ベタ部の濃度むら、画像形成可能な転写領
域において画像形成されていない部分の濃度むらを
(４)、顔料層部分のエッジの切れを(１)の基準で評価し
た結果を表１に示す。The density unevenness of the solid image portion of the recorded image and the density unevenness of the non-imaged portion of the image-formed transfer area of the image recording medium thus created
(4), Table 1 shows the result of evaluation of the edge breakage of the pigment layer portion based on the criterion (1).
【０１３５】又、比較例として金属薄膜層を設けていな
い画像記録体を、上述の方法を用いて作成し、それぞれ
の評価項目に応じて評価した。評価した結果を表１に併
せて示す。As a comparative example, an image recording body not provided with a metal thin film layer was prepared by the above-mentioned method and evaluated according to each evaluation item. The evaluation results are also shown in Table 1.
【０１３６】[0136]
【表１】 [Table 1]
【０１３７】本発明の実施例が画像部エッジの切れが良
く、画像部及び未画像部の濃度ムラもないことが明らか
である。It is apparent that in the embodiment of the present invention, the edge of the image area is well cut, and there is no density unevenness in the image area and the non-image area.
【０１３８】[0138]
【発明の効果】本発明によれば、表面性が劣っていた
り、印刷等が施された基材上にも、切れが良く、濃度ム
ラがなく、かつ隠蔽性に優れた画像記録体が作成でき
る。EFFECTS OF THE INVENTION According to the present invention, an image recording material having excellent surface property, excellent cutting performance, no uneven density, and excellent hiding property can be prepared even on a printed substrate. it can.
【図面の簡単な説明】[Brief description of drawings]
【図１】本発明の画像記録体作成に用いる金属薄膜層・
顔料層転写材料の構成断面図。(a)は必須の基本形、
(b)、(c)はバリエーションを示す。FIG. 1 is a metal thin film layer used for producing the image recording material of the present invention.
FIG. 3 is a cross-sectional view of the configuration of a pigment layer transfer material. (a) is a required basic form,
(b) and (c) show variations.
【図２】本発明の画像記録体作成に用いる受像層転写材
料の構成断面図。(a)は必須の基本形、(b)、(c)はバリ
エーションを示す。FIG. 2 is a sectional view showing the structure of an image-receiving layer transfer material used for producing the image recording material of the present invention. (a) shows an essential basic form, and (b) and (c) show variations.
【図３】本発明の画像記録体の作成方法−１の一形態の
時系列的変化を示す構成断面図。FIG. 3 is a structural cross-sectional view showing a time-sequential change of one mode of the method for producing an image recording body of the invention-1.
【図４】本発明の画像記録体作成に用いる金属薄膜層の
構成断面図。(a)は必須の基本形、(b)、(c)はバリエー
ションを示す。FIG. 4 is a sectional view showing the configuration of a metal thin film layer used for producing the image recording body of the present invention. (a) shows an essential basic form, and (b) and (c) show variations.
【図５】本発明の画像記録体作成に用いる受像層・顔料
層転写材料の構成断面図。(a)は必須の基本形、(b)、
(c)はバリエーションを示す。FIG. 5 is a cross-sectional view of the constitution of an image receiving layer / pigment layer transfer material used for producing the image recording material of the present invention. (a) is a required basic form, (b),
(c) shows variations.
【図６】本発明の画像記録体の作成方法−１の一形態の
時系列的変化を示す構成断面図。FIG. 6 is a structural cross-sectional view showing a time-sequential change of one mode of the image recording medium producing method-1 of the invention.
【図７】本発明の画像記録体作成に用いる顔料層転写材
料の構成断面図。(a)は必須の基本形、(b)、(c)はバリ
エーションを示す。FIG. 7 is a cross-sectional view showing the structure of a pigment layer transfer material used for producing the image recording material of the present invention. (a) shows an essential basic form, and (b) and (c) show variations.
【図８】本発明の画像記録体の作成方法−１の一形態の
時系列的変化を示す構成断面図。FIG. 8 is a structural cross-sectional view showing a time-sequential change of one mode of the image recording medium producing method-1 of the invention.
【図９】本発明の画像記録体作成に用いる保護シートの
構成断面図。FIG. 9 is a structural cross-sectional view of a protective sheet used for producing the image recording material of the present invention.
【図１０】本発明の画像記録体作成に用いる保護層転写
材料の構成断面図。(a)は必須の基本形、(b)、(c)はバ
リエーションを示す。FIG. 10 is a cross-sectional view of the constitution of a protective layer transfer material used for producing the image recording material of the present invention. (a) shows an essential basic form, and (b) and (c) show variations.
【図１１】保護シート又は保護層で被覆された本発明の
画像記録体の構成断面図。FIG. 11 is a sectional view showing the configuration of the image recording material of the present invention covered with a protective sheet or a protective layer.
【図１２】本発明の画像記録体作成に用いる受像層転写
材料の構成断面図。(a)は必須の基本形、(b)はバリエー
ションを示す。FIG. 12 is a sectional view showing the structure of an image-receiving layer transfer material used for producing the image recording material of the present invention. (a) shows an essential basic form, and (b) shows variations.
【図１３】本発明の画像記録体作成の過程において、画
像形成された受像層の構成断面図。FIG. 13 is a sectional view showing the configuration of an image receiving layer on which an image is formed in the process of producing the image recording material of the present invention.
【図１４】本発明の画像記録体の作成方法−２で得られ
た画像記録体の一例の構成断面図。FIG. 14 is a structural cross-sectional view of an example of an image recording body obtained by the image recording body producing method-2 of the invention.
【図１５】本発明の画像記録体の作成方法−２の一形態
の時系列的変化を示す構成断面図。FIG. 15 is a structural cross-sectional view showing a time-sequential change of one mode of the image recording medium producing method-2 of the invention.
【図１６】本発明の画像記録体作成に用いる金属薄膜層
・顔料層転写材料の構成断面図。(a)は必須の基本形、
(b)はバリエーションを示す。FIG. 16 is a sectional view showing the construction of a metal thin film layer / pigment layer transfer material used for producing the image recording material of the present invention. (a) is a required basic form,
(b) shows variations.
【図１７】本発明の画像記録体の作成方法−３の一形態
の時系列的変化を示す構成断面図。FIG. 17 is a structural cross-sectional view showing a time-series change in one form of the image recording medium producing method-3 of the invention.
【図１８】本発明の画像記録体作成に用いる金属薄膜層
の構成断面図。(a)は必須の基本形、(b)、(c)はバリエ
ーションを示す。FIG. 18 is a structural cross-sectional view of a metal thin film layer used for producing the image recording body of the present invention. (a) shows an essential basic form, and (b) and (c) show variations.
【図１９】本発明の画像記録体の作成方法−３の別の一
形態の時系列的変化を示す構成断面図。FIG. 19 is a structural cross-sectional view showing a time-sequential change of another mode of the method for creating the image recording body-3 of the invention.
【図２０】本発明の画像記録体の作成方法−３の別の一
形態の時系列的変化を示す構成断面図。FIG. 20 is a structural cross-sectional view showing a time-series change of another mode of the method for creating an image recording medium-3 of the invention.
１ 金属薄膜層 ２ 顔料層 ３ 支持体 ４ 接着層 ５ 剥離層 ６ 蒸着アンカー層 ７ 受像層 ８ 基材 ９ 保護シート 10 保護層 11 画像形成された受像層 12 接着層兼剥離層 1 Metal Thin Film Layer 2 Pigment Layer 3 Support 4 Adhesive Layer 5 Release Layer 6 Vapor Deposition Anchor Layer 7 Image Receiving Layer 8 Base Material 9 Protective Sheet 10 Protective Layer 11 Image Formed Image Receiving Layer 12 Adhesive Layer / Peeling Layer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ４１Ｍ 5/40 Ｇ０３Ｇ 7/00 Ｈ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI technical display location B41M 5/40 G03G 7/00 H
Claims (11)
層された顔料層・金属薄膜層転写材料を用いて、基材上
に金属薄膜層付き顔料層を熱転写した後、支持体上に受
像層を備えた受像層転写材料と対面させ、熱エネルギー
を与えて顔料層上に受像層を転写し、次いで該受像層上
に画像形成を行うことを特徴とする画像記録体作成方
法。1. A pigment layer and a metal thin film layer transfer material, in which a pigment layer and a metal thin film layer are laminated in this order on a support, are used to thermally transfer a pigment layer with a metal thin film layer onto a substrate, and then, onto the support. A method for producing an image recording material, comprising: facing an image-receiving layer transfer material having an image-receiving layer, applying heat energy to transfer the image-receiving layer onto the pigment layer, and then forming an image on the image-receiving layer.
薄膜層転写材料を用いて、基材上に金属薄膜層を熱転写
した後、支持体上に受像層、顔料層の順に積層された受
像層・顔料層転写材料と対面させ、熱エネルギーを与え
て金属薄膜層上に顔料層付き受像層を転写し、次いで該
受像層上に画像形成を行うことを特徴とする画像記録体
作成方法。2. A metal thin film layer transfer material in which a metal thin film layer is laminated on a support is used to thermally transfer the metal thin film layer on a substrate, and then an image receiving layer and a pigment layer are laminated on the support in this order. Image-receiving layer / pigment layer, which is made to face the transfer material, is given heat energy to transfer the image-receiving layer with the pigment layer onto the metal thin film layer, and then forms an image on the image-receiving layer. Method.
薄膜層転写材料、支持体上に顔料層の積層された顔料層
転写材料、支持体上に受像層の積層された受像層転写材
料を用いて、基材上に金属薄膜層、顔料層、受像層の順
に順次熱転写し、次いで該受像層上に画像形成を行うこ
とを特徴とする画像記録体作成方法。3. A metal thin film layer transfer material in which a metal thin film layer is laminated on a support, a pigment layer transfer material in which a pigment layer is laminated on a support, and an image receiving layer transfer in which an image receiving layer is laminated on a support. A method for producing an image recording material, comprising: using a material, thermally transferring a metal thin film layer, a pigment layer, and an image receiving layer in this order on a substrate, and then forming an image on the image receiving layer.
層された顔料層・金属薄膜層転写材料を用いて、基材上
に金属薄膜層付き顔料層を熱転写した後、別途、支持体
上に受像層を備えた受像層転写材料へ画像形成を行った
受像層転写材料と対面させ、熱エネルギーを与えて顔料
層上に画像形成された受像層を転写することを特徴とす
る画像記録体作成方法。4. A pigment layer and a metal thin film layer transfer material, in which a pigment layer and a metal thin film layer are laminated in this order on a support, are used to thermally transfer a pigment layer with a metal thin film layer onto a substrate, and then separately supported. An image characterized in that the image-receiving layer transfer material having an image-receiving layer on the body is faced with the image-receiving layer transfer material on which an image is formed, and thermal energy is applied to transfer the image-formed image-receiving layer onto the pigment layer. How to make a recording.
薄膜層転写材料、支持体上に顔料層の積層された顔料層
転写材料を用いて、基材上に金属薄膜層、顔料層の順に
順次熱転写し、別途、支持体上に受像層を備えた受像層
転写材料へ画像形成を行った受像層転写材料と対面さ
せ、熱エネルギーを与えて顔料層上に画像形成された受
像層を転写することを特徴とする画像記録体作成方法。5. A metal thin film layer and a pigment layer formed on a substrate by using a metal thin film layer transfer material having a metal thin film layer laminated on a support and a pigment layer transfer material having a pigment layer laminated on a support. The image-receiving layer on which the image is formed on the pigment layer by thermally transferring the image in order of the image-receiving layer transfer material having the image-receiving layer on the support A method for producing an image recording material, which comprises transferring
料へ画像形成を行い、支持体上に金属薄膜層、顔料層の
順に積層された金属薄膜層・顔料層転写材料を用いて、
該画像形成された受像層上へ金属薄膜層付き顔料層を熱
転写し、次いで基材と対面させ、熱エネルギーを与えて
基材上に画像形成された受像層を転写することを特徴と
する画像記録体作成方法。6. An image-receiving layer transfer material having an image-receiving layer on a support is subjected to image formation, and a metal thin film layer / pigment layer transfer material in which a metal thin film layer and a pigment layer are laminated in this order on the support is used. ,
An image characterized by thermally transferring a pigment layer with a metal thin film layer onto the image-formed image-receiving layer, then facing the substrate, and applying heat energy to transfer the image-formed image-receiving layer onto the substrate. How to make a recording.
料へ画像形成を行い、支持体上に顔料層の積層された顔
料層転写材料、支持体上に金属薄膜層の積層された金属
薄膜層転写材料を用いて、該画像形成された受像層上へ
顔料層、金属薄膜層の順に順次熱転写し、次いで基材と
対面させ、熱エネルギーを与えて基材上に画像形成され
た受像層を転写することを特徴とする画像記録体作成方
法。7. An image-receiving layer transfer material having an image-receiving layer on a support is subjected to image formation, and a pigment layer transfer material having a pigment layer laminated on the support, and a metal thin film layer laminated on the support. Using a metal thin film layer transfer material, a pigment layer and a metal thin film layer were sequentially heat-transferred onto the image-formed image-receiving layer in this order, and then faced with a substrate, and heat energy was applied to form an image on the substrate. A method for producing an image recording medium, which comprises transferring an image receiving layer.
料へ画像形成を行い、支持体上に顔料層の積層された顔
料層転写材料を用いて、該画像形成された受像層上へ顔
料層を熱転写し、別途、支持体上に金属薄膜層を備えた
金属薄膜層転写材料を用いて、基材上に金属薄膜層を熱
転写した後、熱エネルギーを与えて金属薄膜層上に画像
形成された受像層を転写することを特徴とする画像記録
体作成方法。8. An image is formed on an image-receiving layer transfer material having an image-receiving layer on a support, and a pigment layer transfer material having a pigment layer laminated on the support is used to form an image on the image-receiving layer. Heat transfer the pigment layer to a metal thin film layer transfer material with a metal thin film layer on a support, and then transfer the metal thin film layer onto the base material, and then apply heat energy to the metal thin film layer. A method for producing an image recording medium, which comprises transferring the image-receiving layer on which an image is formed.
転写記録法であることを特徴とする請求項１〜８の何れ
か１項に記載の画像記録体作成方法。9. The method for producing an image recording material according to claim 1, wherein a method for forming an image on the image receiving layer is a thermal transfer recording method.
電子写真法であることを特徴とする請求項１〜８の何れ
か１項に記載の画像記録体作成方法。10. A method of forming an image on the image-receiving layer comprises:
The method for producing an image recording body according to claim 1, wherein the image recording body is an electrophotographic method.
インクジェット記録法であることを特徴とする請求項１
〜８の何れか１項に記載の画像記録体作成方法。11. A method for forming an image on the image receiving layer comprises:
The inkjet recording method is used, wherein
9. The method for producing an image recording body according to any one of items 8 to 8.