JPH08134796A - Flame-retardant paper for vinyl wall paper backing - Google Patents
Flame-retardant paper for vinyl wall paper backingInfo
- Publication number
- JPH08134796A JPH08134796A JP27517794A JP27517794A JPH08134796A JP H08134796 A JPH08134796 A JP H08134796A JP 27517794 A JP27517794 A JP 27517794A JP 27517794 A JP27517794 A JP 27517794A JP H08134796 A JPH08134796 A JP H08134796A
- Authority
- JP
- Japan
- Prior art keywords
- flame
- paper
- retardant
- calcium carbonate
- opacity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ビニル壁紙の裏打ち用
に用いられる難燃紙に関し、特に不透明度および白色度
の高いビニル壁紙裏打ち用難燃紙に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a flame-retardant paper used for backing vinyl wallpaper, and more particularly to a flame-retardant paper for backing vinyl wallpaper having high opacity and whiteness.
【０００２】[0002]
【従来の技術】難燃紙は壁装材料、建築基材、電子機器
用基材などとして広く用いられており、ビニル壁紙裏打
ち用基材としても使用されている。BACKGROUND OF THE INVENTION Flame-retardant paper is widely used as a wall covering material, a building base material, a base material for electronic devices and the like, and is also used as a base material for backing vinyl wallpaper.
【０００３】難燃紙としては、紙に難燃剤を塗布あるい
は含浸したもの、あるいはセルロースパルプに難燃性の
有機物質や無機物質を湿式抄紙により含有せしめたもの
が知られている。代表的なものとしては、難燃剤として
スルファミン酸グアニジンを紙に含浸処理した難燃紙
や、無機物質として水酸化アルミニウムをパルプと混抄
した無機質シートがある。Known flame-retardant papers are those obtained by coating or impregnating paper with a flame-retardant agent, or cellulose pulps containing a flame-retardant organic substance or inorganic substance by wet papermaking. Typical examples include flame-retardant paper obtained by impregnating paper with guanidine sulfamate as a flame-retardant, and an inorganic sheet obtained by mixing aluminum hydroxide with pulp as an inorganic substance.
【０００４】一般に壁紙裏打ち用難燃紙の不透明度が低
いと、壁面に壁紙を施工した場合に、施工した場所の裏
地の色が壁紙の表面に映り、壁紙としての風合いを損ね
るため壁装材料としては好ましくない。この理由から、
不透明度の高いビニル壁紙裏打ち用難燃紙が求められて
いる。Generally, when the flame-retardant paper for wallpaper lining has a low opacity, when the wallpaper is applied to the wall surface, the color of the lining at the applied location is reflected on the surface of the wallpaper, and the texture of the wallpaper is impaired. Is not preferable. For this reason
There is a need for flame-retardant paper for backing vinyl wallpaper with high opacity.
【０００５】従来のビニル壁紙裏打ち用難燃紙は不透明
度を付与するために、二酸化チタン、タルク等の無機質
粉体の１種または２種以上を混合抄紙してなる基材が広
く使用されている。しかしながら、特に高不透明度を付
与する必要のある場合には二酸化チタンを高配合する必
要が生じ、二酸化チタンは高価であるために紙のコスト
が高くなり、実用的でない。The conventional flame-retardant paper for backing vinyl wallpaper is widely used as a base material made of a mixture of one or more inorganic powders such as titanium dioxide and talc in order to impart opacity. There is. However, when it is necessary to impart high opacity, it is necessary to add a high amount of titanium dioxide, and since titanium dioxide is expensive, the cost of paper is high, which is not practical.
【０００６】さらに、水酸化アルミニウムをパルプと混
抄した無機質シートもビニル壁紙裏打ち用基材として従
来から使用されており、ある程度の不透明度を付与する
ことが出来る。しかしながら水酸化アルミニウムを紙中
に７０〜８０重量％と高歩留りで留めるため、１００ｇ
／ｍ2 以上の米坪量にしないと抄紙困難であり、１００
ｇ／ｍ2 以下の米坪量の裏打ち用基材が必要の場合に
は、紙に難燃剤を塗布あるいは含浸して難燃化した難燃
紙が使用されている。Further, an inorganic sheet prepared by mixing aluminum hydroxide with pulp has also been conventionally used as a base material for backing vinyl wallpaper, and can give a certain degree of opacity. However, since aluminum hydroxide is retained in the paper with a high yield of 70 to 80% by weight, 100 g of aluminum hydroxide is used.
/ M 2 or more of not the US basis weight and a paper difficult, 100
When a backing substrate having a rice basis weight of g / m 2 or less is required, flame-retardant paper which is flame-retarded by coating or impregnating a flame-retardant agent on the paper is used.
【０００７】かかる難燃紙に不透明度を付与する他の手
段としては、半晒パルプあるいはメカニカルパルプ等の
着色した繊維の配合あるいは着色顔料等の併用がある。
しかし、このような手段は紙の白色度を低下させるた
め、難燃紙の白色度を高めて壁紙としてのデザイン性を
高めようとする要請に反する。As another means for imparting opacity to such flame-retardant paper, there is a combination of colored fibers such as semi-bleached pulp or mechanical pulp, or the combined use of color pigments.
However, since such a means lowers the whiteness of the paper, it is against the demand to increase the whiteness of the flame-retardant paper to improve the design of the wallpaper.
【０００８】難燃剤を塗布あるいは含浸処理したビニル
壁紙裏打ち用難燃紙で不透明度の良好なものとしては、
特開平３−１９９５００号公報で提案されている難燃紙
がある。しかしながら、この難燃紙はメカニカルパルプ
を約３０％配合しているため必然的に白色度が低下す
る。The flame-retardant paper for backing vinyl wallpaper, which has been coated or impregnated with a flame-retardant, has good opacity.
There is a flame-retardant paper proposed in JP-A-3-199500. However, since the flame-retardant paper contains about 30% mechanical pulp, the whiteness is inevitably lowered.
【０００９】不透明度と白色度を両立させるべく考慮し
たビニル壁紙裏打ち用難燃紙としては、粒径の異なる２
種以上の水酸化アルミニウムを針葉樹晒クラフトパルプ
と混合し、湿式抄紙法で水酸化アルミニウムを紙全重量
中に４０重量％以上６０重量％以下含有せしめる方法が
提案されている（特開平４−５０４００号公報参照）。
しかしながらこの方法によると、ある程度の不透明度を
付与することは可能であるが、更なる高不透明度の要求
には応え難い。即ち水酸化アルミニウム含有量を４０重
量％から６０重量％まで増大させても不透明度は１％増
大するのみである。As a flame-retardant paper for backing vinyl wallpaper in consideration of achieving both opacity and whiteness, there are 2 different particle sizes.
A method has been proposed in which at least 40% by weight and 60% by weight or less of aluminum hydroxide is contained in the total weight of paper by a wet papermaking method by mixing at least one kind of aluminum hydroxide with softwood bleached kraft pulp (JP-A-4-50400). (See the official gazette).
However, according to this method, it is possible to give opacity to some extent, but it is difficult to meet the demand for higher opacity. That is, increasing the aluminum hydroxide content from 40% to 60% by weight only increases the opacity by 1%.
【００１０】[0010]
【発明が解決しようとする課題】本発明は、難燃剤を塗
布または含浸せしめてなる難燃紙において、白色度を維
持しつつ不透明度を向上させる新たな手段を提供するこ
とを目的としてなされたものである。白色度と不透明度
の両品質を充足した原紙はデザイン性、意匠性に富み、
極めて有用である。SUMMARY OF THE INVENTION The present invention has been made for the purpose of providing a new means for improving the opacity while maintaining the whiteness of a flame-retardant paper coated or impregnated with a flame-retardant agent. It is a thing. The base paper, which satisfies both the whiteness and opacity qualities, is rich in design and design.
Extremely useful.
【００１１】[0011]
【課題を解決するための手段】本発明者らは、繊維と無
機質粉体を混合抄紙したシートに難燃剤を塗布または含
浸せしめた難燃紙について、不透明度と白色度を向上さ
せるべく鋭意研究した結果、無機質粉体の比率を上げる
だけでは不透明度と白色度を十分なレベルまで向上させ
ることが出来ないとの結論に至り、混合抄紙する無機質
粉体として粒度分布範囲の狭い特定寸法の炭酸カルシウ
ムを使用することによって不透明度の高いビニル壁紙裏
打ち用難燃紙が得られることを見いだした。その結果、
使用するパルプを着色したり着色顔料等を併用する必要
がなくなるため、結果として白色度の向上も達成でき
た。[Means for Solving the Problems] The inventors of the present invention have earnestly studied to improve the opacity and whiteness of a flame-retardant paper obtained by coating or impregnating a sheet made by mixing fibers and inorganic powder with a flame-retardant agent. As a result, it was concluded that the opacity and whiteness could not be improved to a sufficient level simply by increasing the ratio of the inorganic powder, and as the inorganic powder for mixed papermaking, carbon dioxide of a specific size with a narrow particle size distribution range was used. It has been found that a flame-retardant paper for vinyl wallpaper with high opacity can be obtained by using calcium. as a result,
Since it is not necessary to color the pulp used or to use a coloring pigment in combination, the whiteness can be improved as a result.
【００１２】すなわち本発明によるビニル壁紙裏打ち用
難燃紙は、繊維と炭酸カルシウムからなるシートに難燃
剤を塗布または含浸せしめてなる難燃紙であって、(1)
該炭酸カルシウムが短径０．２μｍ以上０．８μｍ以下
の炭酸カルシウムであり、(2) 難燃紙全重量中に占める
該炭酸カルシウムの含有量が２０重量％から４０重量％
の範囲であることを特徴とするものである。That is, the flame-retardant paper for backing vinyl wallpaper according to the present invention is a flame-retardant paper obtained by coating or impregnating a sheet made of fibers and calcium carbonate with a flame-retardant agent.
The calcium carbonate has a minor axis of 0.2 μm or more and 0.8 μm or less, and (2) the content of the calcium carbonate in the total weight of the flame-retardant paper is 20% by weight to 40% by weight.
It is characterized by being in the range of.
【００１３】原紙の繊維原料としては、針葉樹晒クラフ
トパルプ（ＮＢＫＰ）、広葉樹晒クラフトパルプ（ＬＢ
ＫＰ）、針葉樹晒サルファイトパルプ（ＮＢＳＰ）、広
葉樹晒サルファイトパルプ（ＬＢＳＰ）、その他の木材
パルプ等があり、これら１種または２種以上のパルプを
適宜選択して用いることができる。また、ポリエステル
繊維、ガラス繊維等の合成繊維または無機繊維の１種ま
たは２種以上を上記の繊維原料中に配合することによ
り、寸法安定性向上を図ってもよい。As the fiber raw material for the base paper, bleached softwood kraft pulp (NBKP), bleached hardwood kraft pulp (LB)
KP), softwood bleached sulfite pulp (NBSP), hardwood bleached sulfite pulp (LBSP), other wood pulp, and the like, and one or more of these pulps can be appropriately selected and used. Further, dimensional stability may be improved by blending one kind or two or more kinds of synthetic fibers such as polyester fibers and glass fibers or inorganic fibers into the above fiber raw material.
【００１４】原紙の不透明度を向上させる手段として
は、繊維に混合抄紙する無機質粉体の比表面積を大きく
すること、あるいは屈折率の高い無機質粉体を用いるこ
とが考えられるが、比表面積の大きい無機質粉体を繊維
と混合して湿式抄紙すると無機質粉体の歩留まりの低下
を招くため好ましくない。また、屈折率が高いうえに高
白色度を付与することのできる二酸化チタン等の無機質
粉体は価格が高く、一方、屈折率は高いが白色度の低い
無機質粉体を用いると白色度を低下させるため好ましく
ない。As a means for improving the opacity of the base paper, it is conceivable to increase the specific surface area of the inorganic powder to be mixed with the fibers and to use the inorganic powder having a high refractive index, but the specific surface area is large. It is not preferable to mix the inorganic powder with the fiber and to perform wet papermaking because the yield of the inorganic powder is reduced. In addition, inorganic powders such as titanium dioxide, which has a high refractive index and can impart high whiteness, are expensive, while using inorganic powders with a high refractive index but low whiteness reduces whiteness. It is not preferable because it causes
【００１５】本発明においては、比較的安価な炭酸カル
シウムを用い、かつこの炭酸カルシウムの粒子の短径を
可視光線の波長領域である０．２μｍ〜０．８μｍの範
囲内とすることにより、結果として可視光線の波長領域
外の領域にある粒子径のものは殆ど存在しなくなるた
め、高不透明度の要求を解決することができる。炭酸カ
ルシウム粒子の短径が０．２μｍ未満の場合には、可視
光線の波長領域から外れるため散乱係数が低下し不透明
度が低下する。一方、炭酸カルシウム粒子の短径が０．
８μｍを超えて大きくなると、可視光線の波長領域から
外れるため比表面積が小さくなるために不透明度が低下
する。上記で規定したごとき寸法の炭酸カルシウム粒子
を用いることにより高不透明度を付与できる結果、使用
する繊維原料を着色したり着色顔料等を併用する必要が
なく、可視光線の波長領域が炭酸カルシウム粒子の短径
と一致するために、従来より高白色度を付与することが
できる。In the present invention, relatively inexpensive calcium carbonate is used, and the short diameter of the calcium carbonate particles is set within the range of 0.2 μm to 0.8 μm, which is the wavelength range of visible light. As there are almost no particles having a particle size outside the wavelength range of visible light, the requirement for high opacity can be solved. If the minor axis of the calcium carbonate particles is less than 0.2 μm, the particles fall outside the wavelength range of visible light, so that the scattering coefficient decreases and the opacity decreases. On the other hand, the short diameter of the calcium carbonate particles is 0.
When it exceeds 8 μm and becomes large, it is out of the wavelength range of visible light and the specific surface area is small, so that the opacity is lowered. As a result that high opacity can be imparted by using the calcium carbonate particles having the dimensions as defined above, it is not necessary to color the fiber raw material to be used or to use a coloring pigment in combination, and the wavelength range of visible light is calcium carbonate particles. Since it matches the short diameter, higher whiteness can be imparted than before.
【００１６】従来使用されている粉砕法によって製造さ
れた重質炭酸カルシウムにおいては粒度分布範囲が広い
ため、平均粒子径が例えば０．８μｍの製品でも、可視
光線の波長領域外の粒子径のものが９０％弱存在する。
これに対して特開昭５９−２６９２７号公報や特開平６
−５６４２２号公報に記載されている炭酸カルシウムの
合成方法、すなわち生石灰を水で消和させることによっ
て得られる水酸化カルシウム懸濁液に炭酸ガスを反応さ
せることによって製造された紡錘状炭酸カルシウムは、
粒度分布範囲を狭い範囲に押さえることができ、短径を
上記した可視光線の波長領域内の範囲に制御することが
できる。この紡錘状炭酸カルシウムは通常３〜４のアス
ペクト比を有しており、従って、上記のごとき合成法に
より製造した短径０．２μｍ〜０．８μｍでアスペクト
比３〜４の紡錘状炭酸カルシウムは、粒度分布範囲が狭
く、可視光線の波長領域外の領域にある粒子径のものは
殆ど存在しないため、本発明で用いる炭酸カルシウム粒
子として好ましく使用することができる。Since the conventional calcium carbonate produced by the pulverizing method has a wide particle size distribution range, even a product having an average particle size of 0.8 μm has a particle size outside the visible light wavelength range. Is a little less than 90%.
On the other hand, JP-A-59-26927 and JP-A-6-26927
The method for synthesizing calcium carbonate described in JP-56422, namely, the spindle-shaped calcium carbonate produced by reacting carbon dioxide with a calcium hydroxide suspension obtained by soaking quicklime with water,
The particle size distribution range can be suppressed to a narrow range, and the minor axis can be controlled to a range within the above visible light wavelength range. This spindle-shaped calcium carbonate usually has an aspect ratio of 3 to 4, and therefore, the spindle-shaped calcium carbonate having a minor axis of 0.2 μm to 0.8 μm and an aspect ratio of 3 to 4 produced by the above-mentioned synthetic method is Since the particle size distribution range is narrow and there are almost no particles having a particle diameter outside the visible light wavelength range, they can be preferably used as the calcium carbonate particles used in the present invention.
【００１７】本発明においては、炭酸カルシウムの配合
割合を全原料に対して２０重量％〜４０重量％の範囲と
する。炭酸カルシウムの配合割合が２０重量％未満では
所望の不透明度が発現され難い。一方、配合割合が４０
重量％を超えると、繊維原料分が少なくなり、必要な紙
の強度が維持できなくなるために好ましくない。In the present invention, the blending ratio of calcium carbonate is in the range of 20% by weight to 40% by weight based on the total raw materials. If the blending ratio of calcium carbonate is less than 20% by weight, the desired opacity is difficult to be exhibited. On the other hand, the compounding ratio is 40
If it exceeds 5% by weight, the amount of the fiber raw material becomes small and the required strength of the paper cannot be maintained, which is not preferable.
【００１８】本発明によるビニル壁紙裏打ち用難燃紙
は、繊維原料と炭酸カルシウムの混合スラリーに、歩留
り助剤やバインダーを適宜選択して添加し、通常の湿式
抄紙法によって容易に抄造することができる。使用する
抄紙機は円網、短網、長網、バーチフォーマー、ロトフ
ォーマー、ハイドロフォーマーなどのいずれでもよく、
乾燥機はヤンキー型、多筒型、スルー型のいずれでもよ
い。The flame-retardant paper for backing vinyl wallpaper according to the present invention can be easily produced by a conventional wet papermaking method by adding a retention aid or a binder to a mixed slurry of a fiber raw material and calcium carbonate as appropriate. it can. The paper machine used may be any of a cylinder, a short-mesh, a fourdrinier, a birch former, a rotoformer, a hydroformer, etc.,
The dryer may be a Yankee type, a multi-cylinder type, or a through type.
【００１９】歩留り助剤としては、例えばカチオン性高
分子としては、カチオン化澱粉、カチオン性ポリアクリ
ルアミド、ポリエチレンイミン、ポリアミドポリアミン
エピクロルヒドリン、カチオン変性グアーガム、カチオ
ン変性ポリビニルアルコール、その他のカチオン性高分
子などがあり、特に限定されない。アニオン性高分子と
しては、ポリアクリルアミド、ポリメタクリルアミド、
酸化澱粉、その他のアニオン性高分子等があり、特に限
定されない。また、原紙強度を保つ目的で接着剤、例え
ば溶解性ビニロン繊維、ラテックスエマルジョン等を用
いてもよい。Examples of the retention aid include cationic polymers such as cationized starch, cationic polyacrylamide, polyethyleneimine, polyamide polyamine epichlorohydrin, cation-modified guar gum, cation-modified polyvinyl alcohol and other cationic polymers. There is no particular limitation. As the anionic polymer, polyacrylamide, polymethacrylamide,
There is no particular limitation, such as oxidized starch and other anionic polymers. Further, an adhesive such as soluble vinylon fiber or latex emulsion may be used for the purpose of maintaining the strength of the base paper.
【００２０】炭酸カルシウムを含有する本発明の難燃紙
は、ビニル壁紙施工時に糊が原紙の中に浸透してしまわ
ないようにするため、抄紙時に内添および／または外添
サイズ剤を添加することが好ましい。用いるサイズ剤と
しては、アルキルケテンダイマー、スチレンアクリル
系、スチレンアミド系などの内添および／または外添サ
イズ剤を適宜選択して使用することができる。In the flame-retardant paper of the present invention containing calcium carbonate, an internal and / or external sizing agent is added at the time of papermaking in order to prevent the paste from penetrating into the base paper when the vinyl wallpaper is applied. It is preferable. As the sizing agent to be used, an internally and / or externally added sizing agent such as an alkyl ketene dimer, a styrene acrylic type, a styrene amide type can be appropriately selected and used.
【００２１】本発明のビニル壁紙裏打ち用難燃紙は、繊
維と炭酸カルシウムを混合して湿式抄紙して得られたシ
ートに、さらに難燃剤を塗布または含浸させることによ
り得られる。難燃化処理に際しては、通常用いられる難
燃剤、例えばグアニジン系難燃剤を、通常用いられる方
法、例えばサイズプレス機を用いて塗布あるいは含浸す
ればよい。The flame-retardant paper for backing vinyl wallpaper of the present invention is obtained by further mixing or impregnating a flame-retardant agent on a sheet obtained by mixing fibers and calcium carbonate and performing wet papermaking. In the flame retardation treatment, a commonly used flame retardant, for example, a guanidine flame retardant may be applied or impregnated by a commonly used method, for example, using a size press machine.
【００２２】[0022]
【実施例】以下に実施例および比較例を挙げて本発明を
具体的に説明するが、勿論本発明はこれによって限定さ
れるものではない。なお、実施例および比較例で示す％
は全て重量％を意味する。EXAMPLES The present invention will be specifically described below with reference to examples and comparative examples, but the present invention is not of course limited thereto. In addition,% shown in Examples and Comparative Examples
All mean% by weight.
【００２３】実施例１および２ ＮＢＫＰ（自製）を離解後、常法によりフリーネス５５
０ｍｌまで叩解したパルプスラリーを作製した。このパ
ルプスラリーに紡錘状炭酸カルシウム（奥多摩工業製、
「ＴＰ−１２１ＳＤＰ」、短径０．５μｍ×長径１．５
μｍ、沈降法による測定で平均粒径２．６μｍ品）を投
入し、十分に混合してパルプ繊維と紡錘状炭酸カルシウ
ムの混合スラリーを作製した。 Examples 1 and 2 After disintegrating NBKP (manufactured by itself), a freeness of 55 was obtained by a conventional method.
A pulp slurry beaten to 0 ml was prepared. Spindle-shaped calcium carbonate (made by Okutama Kogyo,
"TP-121SDP", minor axis 0.5 μm x major axis 1.5
μm, a product having an average particle size of 2.6 μm as measured by the sedimentation method) was added and sufficiently mixed to prepare a mixed slurry of pulp fibers and spindle-shaped calcium carbonate.
【００２４】この混合物に、更に有機繊維としてポリエ
ステル繊維（直径１０μｍ、繊維長３ｍｍ、クラレ製）
を全重量当り１％添加し、バインダー繊維として溶解性
ビニロン繊維（１．５ｄ、繊維長３ｍｍ、クラレ社製）
を全重量当り０．６％添加した。上記繊維スラリーに歩
留り助剤としてカチオン化剤（ディック・ハーキュレス
社製、「エピノックス」）０．６％、アニオン化剤（ア
ライドコロイド社製、「パーコール１７３」）０．０５
％をそれぞれ繊維分全重量に対して添加して紙料を調製
した後、実験室手抄きマシンを用いて坪量６０ｇ／
ｍ2 、密度０．６ｇ／ｃｍ3 のシートを作成した。この
シートに、難燃剤としてスルファミン酸グアニジンを対
パルプ２０％含浸せしめた。難燃剤含浸液の組成はポリ
ビニルアルコール（クラレ製、「ポバール１１７」）：
デンプン（王子コーンスターチ製、「王子エース
Ａ」）：スルファミン酸グアニジン系難燃剤（大日本イ
ンキ化学工業製、「ＳＧ−２」）：アクリル系サイズ剤
（ミサワセラミックケミカル製、「ハマコートＳ９００
Ｇ」）＝４．５：７．５：８０：８とした。上記の方法
により、紙全重量中に含まれる紡錘状炭酸カルシウムの
配合割合が２２％の製品（実施例１）と３８％の製品
（実施例２）の２種類を作製した。Polyester fiber (diameter 10 μm, fiber length 3 mm, made by Kuraray) as organic fiber was added to this mixture.
Soluble vinylon fiber (1.5d, fiber length 3mm, made by Kuraray Co., Ltd.) as binder fiber
Was added to the total weight of 0.6%. As a retention aid, 0.6% of a cationizing agent (manufactured by Dick Hercules, "Epinox") in the fiber slurry, 0.05 anionizing agent (manufactured by Allied Colloid, "Percoll 173") 0.05
% To the total weight of the fiber to prepare the stock, and then using a laboratory handmade machine, basis weight 60 g /
A sheet having m 2 and a density of 0.6 g / cm 3 was prepared. This sheet was impregnated with guanidine sulfamate as a flame retardant to 20% of pulp. The composition of the flame retardant impregnating liquid is polyvinyl alcohol (Kuraray, "Poval 117"):
Starch (Oji Corn Starch, "Oji Ace A"): Guanidine sulfamate flame retardant (Dainippon Ink and Chemicals, "SG-2"): Acrylic sizing agent (Misawa Ceramic Chemical, "Hamacoat S900"
G ”) = 4.5: 7.5: 80: 8. According to the above method, two types of products were produced, that is, a product containing 22% of the spindle-shaped calcium carbonate in the total weight of the paper (Example 1) and a product containing 38% (Example 2).
【００２５】これらのシートについて、不透明度、白色
度および引張強さを測定した。不透明度はＪＩＳ−Ｐ−
８１３８の紙の不透明度試験方法に準じて測定した。ま
た、白色度はＪＩＳ−Ｐ−８１２３の紙及びパルプのハ
ンター白色度試験方法に準じて測定した。引張強さはＪ
ＩＳ−Ｐ−８１１３の紙及び板紙の引張強さ試験方法に
準じて測定した結果を表１に示す。The opacity, whiteness and tensile strength of these sheets were measured. Opacity is JIS-P-
It measured according to the opacity test method of the paper of 8138. The whiteness was measured in accordance with the Hunter-Whiteness test method for paper and pulp of JIS-P-8123. Tensile strength is J
Table 1 shows the results of measurement according to the tensile strength test method for paper and paperboard of IS-P-8113.
【００２６】比較例１ 紡錘状炭酸カルシウムの紙重量当りの配合割合を１８％
に調整した以外は実施例１と同様の方法でシートを作成
し、難燃剤を対パルプ２０％含浸せしめた。このシート
について、不透明度、白色度および引張強さを測定した
結果を表１に示す。 Comparative Example 1 The blending ratio of spindle-shaped calcium carbonate was 18% per weight of paper.
A sheet was prepared in the same manner as in Example 1 except that the content of the flame retardant was impregnated with 20% of pulp. Table 1 shows the results of measuring the opacity, whiteness and tensile strength of this sheet.
【００２７】比較例２ 紡錘状炭酸カルシウムの紙重量当りの配合割合を４４％
に調整した以外は実施例１と同様の方法でシートを作成
し、難燃剤を対パルプ２０％含浸せしめた。このシート
について、不透明度、白色度および引張強さを測定した
結果を表１に示す。 Comparative Example 2 The blending ratio of spindle-shaped calcium carbonate was 44% based on the weight of paper.
A sheet was prepared in the same manner as in Example 1 except that the content of the flame retardant was impregnated with 20% of pulp. Table 1 shows the results of measuring the opacity, whiteness and tensile strength of this sheet.
【００２８】比較例３ 紡錘状炭酸カルシウムの代わりに、粉砕法により製造さ
れた重質炭酸カルシウム（白石カルシウム製、「ソフト
ン２２００」、沈降法による測定で平均粒径１μｍ品）
を用い、炭酸カルシウムの紙重量当たりの配合割合を３
０％に調整した以外は実施例１と同様の方法でシートを
作成し、難燃剤を対パルプ２０％含浸せしめた。このシ
ートについて、不透明度、白色度および引張強さを測定
した結果を表１に示す。 Comparative Example 3 Instead of spindle-shaped calcium carbonate, ground calcium carbonate produced by a pulverizing method ("Shiroishi Calcium," Softon 2200 ", product having an average particle size of 1 μm measured by a sedimentation method)"
And the blending ratio of calcium carbonate per weight of paper is 3
A sheet was prepared in the same manner as in Example 1 except that the content was adjusted to 0%, and the flame retardant was impregnated with 20% of the pulp. Table 1 shows the results of measuring the opacity, whiteness and tensile strength of this sheet.
【００２９】 [0029]
【００３０】表１からわかるように、実施例１と２のビ
ニル壁紙裏打ち用難燃紙は、いずれも不透明度９０％以
上を達成しているため壁紙施工後の壁紙としての風合い
は良好となる。また実施例１と２を比較すると、炭酸カ
ルシウムの配合割合が増えるに従って、不透明度および
白色度が高くなることがわかる。As can be seen from Table 1, the flame-retardant papers for backing vinyl wallpaper of Examples 1 and 2 have achieved an opacity of 90% or more, so that the texture as wallpaper after wallpaper construction is good. . Further, comparing Examples 1 and 2, it can be seen that the opacity and whiteness increase as the blending ratio of calcium carbonate increases.
【００３１】実施例１と２で得られた壁紙裏打ち用難燃
紙は、炭酸カルシウムを紙中に２０％未満配合した比較
例１のものに比べて、不透明度、白色度ともに優れてい
る。また、炭酸カルシウムを紙中に４０％を超えて配合
した比較例２のものは、不透明度、白色度ともに実施例
１および２のものより優れているが、引張強さが１．８
ｋｇｆ以下であるために壁紙加工適性が劣る。The flame-retardant paper for wallpaper lining obtained in Examples 1 and 2 is superior in opacity and whiteness to that of Comparative Example 1 in which less than 20% of calcium carbonate is mixed in the paper. Further, Comparative Example 2 in which calcium carbonate was mixed in the paper in an amount of more than 40% was superior to those in Examples 1 and 2 in both opacity and whiteness, but the tensile strength was 1.8.
Since it is less than or equal to kgf, wallpaper suitability is poor.
【００３２】更に、炭酸カルシウム配合割合が適性範囲
内であっても、粒度分布範囲の広い重質炭酸カルシウム
を使用した比較例３の難燃紙は、紡錘状炭酸カルシウム
を使用した難燃紙と比較して、不透明度、白色度ともに
劣っている。Further, the flame-retardant paper of Comparative Example 3 using the heavy calcium carbonate having a wide particle size distribution range is different from the flame-retardant paper using the spindle-shaped calcium carbonate even if the calcium carbonate content is within the proper range. In comparison, both opacity and whiteness are inferior.
【００３３】[0033]
【発明の効果】以上説明したところからわかるように本
発明によれば、繊維と炭酸カルシウムからなるシートに
難燃剤を塗布または含浸せしめてなる難燃紙であって、
炭酸カルシウムの短径が０．２μｍ〜０．８μｍであ
り、かつ難燃紙全重量中に占める炭酸カルシウムの含有
量が２０〜４０重量％の範囲とすることにより、不透明
度および白色度の高いビニル壁紙裏打ち用難燃紙を提供
することができる。As described above, according to the present invention, a flame-retardant paper obtained by coating or impregnating a sheet made of fibers and calcium carbonate with a flame-retardant agent,
Opacity and whiteness are high when the minor axis of calcium carbonate is 0.2 μm to 0.8 μm and the content of calcium carbonate in the total weight of the flame-retardant paper is in the range of 20 to 40% by weight. A flame-retardant paper for backing vinyl wallpaper can be provided.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ２１Ｈ 3/78 (72)発明者 山地 安之 東京都西多摩郡日の出町平井字欠下２番１ 号 日鉄鉱業株式会社内 (72)発明者 吉田 健彦 東京都西多摩郡日の出町平井字欠下２番１ 号 日鉄鉱業株式会社内─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification number Reference number within the agency FI Technical indication location D21H 3/78 (72) Inventor Yasuyuki Yamaji Hirai-cho, Nishitama-gun, Tokyo Metropolitan area No. 2 Nittetsu Mining Co., Ltd. (72) Inventor Takehiko Yoshida No. 2-1 Hirai, Hirai-cho, Nishitama-gun, Tokyo Inside Nittetsu Mining Co., Ltd.
Claims (2)
難燃剤を塗布または含浸せしめてなる難燃紙であって、 (1) 該炭酸カルシウムが短径０．２μｍ以上０．８μｍ
以下の炭酸カルシウムであり、 (2) 難燃紙全重量中に占める該炭酸カルシウムの含有量
が２０重量％から４０重量％の範囲であることを特徴と
するビニル壁紙裏打ち用難燃紙。1. A flame-retardant paper obtained by coating or impregnating a sheet of fibers and calcium carbonate with a flame-retardant, wherein (1) the calcium carbonate has a minor axis of 0.2 μm or more and 0.8 μm.
The flame retardant paper for backing vinyl wallpaper, which comprises the following calcium carbonate, and (2) the content of the calcium carbonate in the total weight of the flame retardant paper is in the range of 20% by weight to 40% by weight.
上０．８μｍ以下でかつアスペクト比が３以上４以下の
紡錘状炭酸カルシウムである請求項１記載のビニル壁紙
裏打ち用難燃紙。2. The flame-retardant paper for backing vinyl wallpaper according to claim 1, wherein the calcium carbonate is a spindle-shaped calcium carbonate having a minor axis of 0.2 μm or more and 0.8 μm or less and an aspect ratio of 3 or more and 4 or less.