JPH08102041A - Polyester film for magnetic recording medium - Google Patents
Polyester film for magnetic recording mediumInfo
- Publication number
- JPH08102041A JPH08102041A JP23350394A JP23350394A JPH08102041A JP H08102041 A JPH08102041 A JP H08102041A JP 23350394 A JP23350394 A JP 23350394A JP 23350394 A JP23350394 A JP 23350394A JP H08102041 A JPH08102041 A JP H08102041A
- Authority
- JP
- Japan
- Prior art keywords
- polyester film
- film
- magnetic recording
- particles
- recording medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、磁気記録媒体用ポリエ
ステルフィルムに関する。FIELD OF THE INVENTION The present invention relates to a polyester film for a magnetic recording medium.
【0002】[0002]
【従来の技術】磁気記録媒体用ポリエステルフィルムと
しては、幅方向の強度を特定したフィルムが知られてい
る(例えば特開平4−292933号公報)。2. Description of the Related Art As a polyester film for a magnetic recording medium, a film having a specified strength in the width direction is known (for example, Japanese Patent Laid-Open No. 4-292933).
【0003】[0003]
【発明が解決しようとする課題】しかしながら、上記従
来の磁気記録媒体用ポリエステルフィルムでは、単に横
方向の強度を大きくし、磁気テ−プとして良好な電磁変
換特性を得る改良がなされてきたが、絶対値としての縦
強度が不足するという問題点があった。また、フィルム
の加工性について、たとえば適正幅にスリットする際
に、縦強度と横強度のバランスをはかりながら、縦方向
と横方向の破断伸度に異方性を持たせることが求められ
るようになってきている。本発明はかかる課題を解決
し、縦横の強度が大きく伸度に異方性を有しその結果、
特に出力特性に優れる磁気記録媒体用ポリエステルフィ
ルムを提供することを目的とする。However, the conventional polyester film for magnetic recording medium has been improved by simply increasing the strength in the lateral direction to obtain good electromagnetic conversion characteristics as a magnetic tape. There is a problem that the vertical strength as an absolute value is insufficient. Further, regarding the workability of the film, for example, when slitting to an appropriate width, it is required to give anisotropy to the breaking elongation in the longitudinal direction and the transverse direction while balancing the longitudinal strength and the lateral strength. It has become to. The present invention solves such a problem, the strength in the vertical and horizontal directions is large, and the elongation has anisotropy, as a result,
It is an object of the present invention to provide a polyester film for magnetic recording media, which is particularly excellent in output characteristics.
【0004】[0004]
【課題を解決するための手段】この目的に沿う本発明の
磁気記録媒体用ポリエステルフィルムは、ポリエチレン
−2,6−ナフタレンジカルボキシレートからなるフィ
ルムであって、縦方向のヤング率が700kg/mm2 以
上、縦方向の破断伸度が50%以上、横方向のヤング率
が700kg/mm2 以上、横方向の破断伸度が50%未満
であることを特徴とする。A polyester film for a magnetic recording medium according to the present invention for this purpose is a film made of polyethylene-2,6-naphthalene dicarboxylate and has a Young's modulus in the longitudinal direction of 700 kg / mm. 2 or more, the breaking elongation in the longitudinal direction is 50% or more, the Young's modulus in the lateral direction is 700 kg / mm 2 or more, and the breaking elongation in the lateral direction is less than 50%.
【0005】本発明の磁気記録媒体用ポリエステルフィ
ルムはポリエチレン−2,6−ナフタレンジカルボキシ
レート(以下PENと記載する場合がある)を構成成分
とするのが好ましい。なお、本発明の目的を阻害しない
範囲内で、2種以上のポリマを混合してもよいし、共重
合ポリマを用いてもよい。また、本発明の目的を阻害し
ない範囲内で酸化防止剤、熱安定剤、滑剤、紫外線吸収
剤などの添加剤が通常添加される程度添加されていても
よい。The polyester film for magnetic recording media of the present invention preferably contains polyethylene-2,6-naphthalenedicarboxylate (hereinafter sometimes referred to as PEN) as a constituent component. Two or more kinds of polymers may be mixed, or a copolymerized polymer may be used, as long as the object of the present invention is not impaired. Further, additives such as antioxidants, heat stabilizers, lubricants, and ultraviolet absorbers may be added to the extent that they are usually added within a range that does not impair the object of the present invention.
【0006】本発明の磁気記録媒体用ポリエステルフィ
ルムは特に限定されないが、出力特性の点からA層/B
層の少なくとも2層構造からなるのが好ましい。A層厚
みは特に限定されないが、出力特性の点から0.01〜
3.0μm、好ましくは0.02〜2.0μm、さらに
好ましくは0.03〜1.0μmである。積層構成の場
合、少なくとも1層の主たる成分がPENであればよ
く、他の層は特に限定されないが、ポリエステルが好ま
しく例示される。ポリエステルとしては特に限定されな
いが、ポリエチレンテレフタレ−トを主たる成分とする
ポリマ(以下PETと記載)またはPENが好ましい。The polyester film for magnetic recording media of the present invention is not particularly limited, but from the viewpoint of output characteristics, A layer / B
It preferably comprises at least a two-layer structure of layers. The thickness of the A layer is not particularly limited, but from the viewpoint of output characteristics, it is 0.01 to
The thickness is 3.0 μm, preferably 0.02 to 2.0 μm, and more preferably 0.03 to 1.0 μm. In the case of the laminated structure, the main component of at least one layer may be PEN, and the other layers are not particularly limited, but polyester is preferably exemplified. The polyester is not particularly limited, but a polymer containing polyethylene terephthalate as a main component (hereinafter referred to as PET) or PEN is preferable.
【0007】本発明の磁気記録媒体用ポリエステルフィ
ルムが積層構成の場合、A層/B層はそれぞれPEN/
PET、PEN/PEN、PET/PENのいずれでも
とり得る。When the polyester film for a magnetic recording medium of the present invention has a laminated structure, the A layer / B layer are PEN /
It may be PET, PEN / PEN or PET / PEN.
【0008】本発明の磁気記録媒体用ポリエステルフィ
ルムのA層には特に限定されないが、出力特性の点から
0.01〜1.0μm、好ましくは0.02〜0.5μ
m、さらに好ましくは0.03〜0.3μmの粒径の粒
子を、0.01〜3.0重量%、好ましくは0.02〜
2.0重量%含有するのが好ましい。粒子としては特に
限定されないが、出力特性の点から有機粒子、なかでも
架橋型有機粒子、特にポリジビニルベンゼン粒子が好ま
しい。ポリジビニルベンゼン粒子とは、架橋成分として
ジビニルベンゼンを主体とするものをいう。なかでもジ
ビニルベンゼンが粒子成分の51%以上、好ましくは6
0%以上、さらに好ましくは75%以上のものが好まし
い。他の成分としては、特に限定されないが、例えばエ
チルビニルベンゼン、ジエチルベンゼン等の架橋しない
成分があげられる。また、シリコーン粒子も好ましく例
示される。シリコーン粒子とは架橋型オルガノポリシロ
キサン(CH3 Si O3/2 )を主たる成分とするものが
好ましい。その他粒子として、結晶形がα型、γ型、δ
型、θ型、η型のアルミナ、ジルコニア、シリカ、酸化
チタン等の凝集粒子、または、炭酸カルシウム、コロイ
ダルシリカ、酸化チタン等の単分散粒子もポリマ中での
適切な粒子分散により用いることも可能である。これら
の粒子を複数併用して用いてもよい。The layer A of the polyester film for a magnetic recording medium of the present invention is not particularly limited, but from the viewpoint of output characteristics, it is 0.01 to 1.0 μm, preferably 0.02 to 0.5 μm.
m, more preferably 0.01 to 3.0% by weight, preferably 0.02 to 0.02% by weight of particles having a particle size of 0.03 to 0.3 μm.
It is preferable to contain 2.0% by weight. The particles are not particularly limited, but organic particles, particularly crosslinked organic particles, and particularly polydivinylbenzene particles are preferable from the viewpoint of output characteristics. The polydivinylbenzene particles are mainly composed of divinylbenzene as a crosslinking component. Among them, divinylbenzene is 51% or more of the particle component, preferably 6
It is preferably 0% or more, more preferably 75% or more. Other components are not particularly limited, and examples thereof include non-crosslinking components such as ethylvinylbenzene and diethylbenzene. Further, silicone particles are also preferably exemplified. From that of the silicone particles to the crosslinkable organopolysiloxane (CH 3 Si O 3/2) a main component. As other particles, the crystal form is α type, γ type, δ type
-Type, θ-type, η-type alumina, zirconia, silica, titanium oxide, and other agglomerated particles, or calcium carbonate, colloidal silica, titanium oxide, and other monodispersed particles can also be used by appropriate particle dispersion in a polymer. Is. A plurality of these particles may be used in combination.
【0009】A層厚みtとA層に含有する粒子粒径dの
関係は特に限定されないが、0.2≦t/d≦10、好
ましくは0.3≦t/d≦5、さらに好ましくは0.3
≦t/d≦3の場合に、特に出力特性が良好となる。The relation between the thickness A of the layer A and the particle diameter d of the particles contained in the layer A is not particularly limited, but 0.2≤t / d≤10, preferably 0.3≤t / d≤5, and more preferably. 0.3
When ≦ t / d ≦ 3, the output characteristics are particularly good.
【0010】A層以外のフィルム層、つまりB層等を構
成するポリマ中に粒子を含有していてもかまわない。こ
の場合、粒径は0.05〜1.0μm、好ましくは0.
1〜0.5μm、含有量は0.05〜1.0重量%であ
る炭酸カルシウム、アルミナ、シリカ、酸化チタン、有
機粒子、カーボンブラック等から選ばれる粒子を含有す
るのが好ましい。Particles may be contained in the polymer constituting the film layers other than the A layer, that is, the B layer and the like. In this case, the particle size is 0.05 to 1.0 μm, preferably 0.1.
It is preferable to contain particles selected from calcium carbonate, alumina, silica, titanium oxide, organic particles, carbon black and the like having a content of 1 to 0.5 μm and a content of 0.05 to 1.0% by weight.
【0011】本発明の磁気記録媒体用ポリエステルフィ
ルムは、上記組成物を二軸配向したフィルムである。一
軸あるいは無配向フィルムでは幅方向強度が不足するの
で好ましくない。フィルムの厚さ方向の一部分、例えば
表層付近のポリマ分子の配向が無配向、あるいは一軸配
向になっていない、すなわち厚さ方向の全部分の分子配
向が二軸配向である場合に出力特性がより一層良好とな
る。特にアッベ屈折率計、レーザーを用いた屈折率計、
全反射レーザーラマン法などによって測定される分子配
向が、表面、裏面ともに二軸配向である場合に出力特性
がより一層良好となる。The polyester film for magnetic recording media of the present invention is a film in which the above composition is biaxially oriented. A uniaxial or non-oriented film is not preferable because it lacks strength in the width direction. A part of the film in the thickness direction, for example, the orientation of polymer molecules near the surface layer is non-oriented, or not uniaxially oriented, that is, when the molecular orientation of the entire portion in the thickness direction is biaxially oriented, the output characteristics are better. It will be even better. Abbe refractometer, laser refractometer,
When the molecular orientation measured by the total reflection laser Raman method or the like is biaxial orientation on both the front surface and the back surface, the output characteristics are further improved.
【0012】本発明の磁気記録媒体用ポリエステルフィ
ルムの縦方向、横方向のヤング率は出力特性の点から、
それぞれ700kg/mm2 以上、好ましくは800kg/mm
2 以上、さらに好ましくは1000kg/mm2 以上であ
る。The Young's modulus in the machine direction and the transverse direction of the polyester film for a magnetic recording medium of the present invention is in terms of output characteristics.
700 kg / mm 2 or more, preferably 800 kg / mm
2 or more, more preferably 1000 kg / mm 2 or more.
【0013】また、本発明の磁気記録媒体用ポリエステ
ルフィルムの縦方向、横方向の破断伸度は出力特性の点
から、それぞれ50%以上、50%未満、好ましくは6
0%以上、40%以下である。The breaking elongations in the machine direction and the transverse direction of the polyester film for a magnetic recording medium of the present invention are 50% or more and less than 50%, preferably 6 from the viewpoint of output characteristics.
It is 0% or more and 40% or less.
【0014】本発明の磁気記録媒体用ポリエステルフィ
ルムのフィルム厚みは特に限定されないが、出力特性の
点から7μm以下、好ましくは6μm以下、さらに5μ
m以下が好ましい。The film thickness of the polyester film for a magnetic recording medium of the present invention is not particularly limited, but from the viewpoint of output characteristics, it is 7 μm or less, preferably 6 μm or less, and further 5 μm.
m or less is preferable.
【0015】本発明の磁気記録媒体用ポリエステルフィ
ルムには、磁性層を設ける面と反対面に必要に応じてバ
ックコート層を設けてもよい。In the polyester film for a magnetic recording medium of the present invention, a back coat layer may be provided on the surface opposite to the surface on which the magnetic layer is provided, if necessary.
【0016】本発明の磁気記録媒体用ポリエステルフィ
ルムはデジタル磁気記録媒体用ポリエステルフィルムと
して好ましく用いられる。さらに特に高出力が要求され
るHDTV(ハイディフィニションテレビジョン、例え
ばNHKのハイビジョン等)用磁気記録媒体用ポリエス
テルフィルムとしても好ましく用いられる。The polyester film for magnetic recording media of the present invention is preferably used as a polyester film for digital magnetic recording media. Further, it is also preferably used as a polyester film for a magnetic recording medium for HDTV (high definition television, for example, NHK's high vision) in which particularly high output is required.
【0017】また、本発明の磁気記録媒体用ポリエステ
ルフィルムはコンピュータ用等のデータストレージ用に
も好ましく用いられる。The polyester film for magnetic recording media of the present invention is also preferably used for data storage such as computers.
【0018】次に本発明の磁気記録媒体用ポリエステル
フィルムの好ましい製造方法を示し説明するが、これに
限定されるものではない。Next, a preferable method for producing the polyester film for a magnetic recording medium of the present invention will be shown and described, but the present invention is not limited thereto.
【0019】まずフィルムを構成するPENに粒子を含
有せしめる方法としては、ジオ−ル成分であるエチレン
グリコールにスラリーの形で分散させ、このエチレング
リコールを所定のジカルボン酸成分と重合するのが好ま
しい。また粒子の水スラリーを直接所定のPENペレッ
トと混合し、ベント式2軸混練押出機を用いてPENに
練り込む方法は、本発明の効果をより一層良好とするの
に有効である。First, as a method of incorporating particles into PEN constituting the film, it is preferable to disperse ethylene glycol as a diol component in the form of a slurry and polymerize the ethylene glycol with a predetermined dicarboxylic acid component. Further, a method of directly mixing an aqueous slurry of particles with a predetermined PEN pellet and kneading the mixture into PEN using a vent type twin-screw kneading extruder is effective for further improving the effect of the present invention.
【0020】粒子の含有量を調節する方法としては、上
記方法で高濃度マスターを作っておき、それを製膜時に
粒子を実質的に含有しないポリマで希釈して粒子の含有
量を調節する方法が有効である。As a method for controlling the content of particles, a high-concentration master is prepared by the above-mentioned method, and it is diluted with a polymer containing substantially no particles at the time of film formation to control the content of particles. Is effective.
【0021】次に、粒子を所定量含有するペレットを必
要に応じて乾燥したのち、公知の溶融積層用押出機に供
給し、スリット状のダイからシ−ト状に押出し、キャス
ティングロ−ル上で冷却固化せしめて未延伸フィルムを
作る。すなわち複数の押出し機、複数のマニホ−ルドま
たは合流ブロックを用いて溶融状態のポリエステルを積
層する。この場合、粒子を含有するポリマ流路に高精度
フィルタ−、スタティックミキサー、ギヤポンプを設置
する方法は本発明の効果をより一層良好とするのに有効
である。特に高精度フィルタ−は95%濾過が10μ
m、好ましくは5μm、さらに好ましくは3μmである
と本発明の効果に特に有効である。Next, pellets containing a predetermined amount of particles are dried, if necessary, and then fed to a known extruder for melt lamination, extruded in a sheet form from a slit die, and cast on a casting roll. It is cooled and solidified with to make an unstretched film. That is, the polyester in a molten state is laminated using a plurality of extruders, a plurality of manifolds or a merging block. In this case, a method of installing a high-precision filter, a static mixer, and a gear pump in the polymer channel containing particles is effective for further improving the effect of the present invention. Especially high-precision filter 95% filtration is 10μ
m, preferably 5 μm, more preferably 3 μm is particularly effective for the effect of the present invention.
【0022】次にこの未延伸フィルムを二軸延伸し、二
軸配向させる。延伸方法としては、逐次二軸延伸法また
は同時二軸延伸法を用いることができる。ただし、最初
に長手方向、次に幅方向の延伸を行なう逐次二軸延伸法
を用い、縦延伸温度120〜150℃、好ましくは12
0〜140℃、総縦延伸倍率3.0〜5.0倍、縦延伸
速度10,000〜50,000%/分の範囲で行なうのが好まし
い。幅方向の延伸方法としてはテンタ−を用いる方法が
好ましく、延伸温度140〜180℃、好ましくは15
0〜180℃と縦延伸温度より高めに設定を行ない、幅
方向延伸倍率は縦倍率より大きく4.0〜7.0倍、好
ましくは5.0〜6.5倍、幅方向の延伸速度1,000 〜
20,000%/分の範囲で行なうのが好ましい。さらに必要
に応じて、再縦延伸、再横延伸を行なう。その場合の延
伸条件としては長手方向の延伸は130〜180℃、延
伸倍率1.1〜2.0倍、幅方向の延伸方法としてはテ
ンタ−を用いる方法が好ましく、延伸温度130〜18
0℃、幅方向延伸倍率は1.1〜2.0で行なうのが好
ましい。Next, this unstretched film is biaxially stretched and biaxially oriented. As a stretching method, a sequential biaxial stretching method or a simultaneous biaxial stretching method can be used. However, a sequential biaxial stretching method of first stretching in the longitudinal direction and then in the width direction is used, and the longitudinal stretching temperature is 120 to 150 ° C., preferably 12
It is preferable to carry out at 0 to 140 ° C., a total longitudinal stretching ratio of 3.0 to 5.0 times, and a longitudinal stretching speed of 10,000 to 50,000% / min. As a stretching method in the width direction, a method using a tenter is preferable, and a stretching temperature is 140 to 180 ° C., preferably 15
The stretching ratio is set to 0 to 180 ° C., which is higher than the longitudinal stretching temperature, and the transverse stretching ratio is 4.0 to 7.0 times, preferably 5.0 to 6.5 times larger than the longitudinal stretching ratio, and the transverse stretching speed is 1,000. ~
It is preferably performed in the range of 20,000% / min. Further, if necessary, longitudinal re-stretching and lateral re-stretching are performed. In that case, the stretching conditions are preferably 130 to 180 ° C. in the longitudinal direction, 1.1 to 2.0 times the stretching ratio, and a tenter is used as the stretching method in the width direction, and the stretching temperature is 130 to 18
It is preferable to carry out at 0 ° C. and a draw ratio in the width direction of 1.1 to 2.0.
【0023】次にこの二軸配向フィルムを熱処理する。
この場合の熱処理温度は170〜220℃、特に170
〜210℃で時間は0.5〜60秒の範囲が好適であ
る。Next, the biaxially oriented film is heat treated.
The heat treatment temperature in this case is 170 to 220 ° C., especially 170
The range of 0.5 to 60 seconds is suitable at ˜210 ° C.
【0024】[物性の測定方法ならびに効果の評価方
法]本発明の特性値の測定方法並びに効果の評価方法は
次のとおりである。[Physical property measuring method and effect evaluating method] The characteristic value measuring method and effect evaluating method of the present invention are as follows.
【0025】(1)粒子の平均粒径 フィルム断面を透過型電子顕微鏡(TEM)を用い、1
0万倍以上の倍率で観察する。TEMの切片厚さは約1
00nmとし、場所を変えて100視野以上測定する。
粒子の平均径は重量平均径(等価円相当径)から求め
る。(1) Average Particle Size of Particles The cross section of the film was measured by using a transmission electron microscope (TEM).
Observe at a magnification of 0,000 times or more. Section thickness of TEM is about 1
It is set to 00 nm, and the location is changed to measure 100 fields or more.
The average diameter of the particles is calculated from the weight average diameter (equivalent circle diameter).
【0026】(2)粒子の含有量 ポリマは溶解し粒子は溶解させない溶媒を選択し、粒子
をポリマから遠心分離し、粒子の全体重量に対する比率
(重量%)をもって粒子含有量とする。場合によっては
赤外分光法の併用も有効である。(2) Content of particles A solvent in which the polymer is dissolved but not the particles is selected is selected, the particles are centrifuged from the polymer, and the ratio (% by weight) to the total weight of the particles is taken as the particle content. In some cases, the combined use of infrared spectroscopy is also effective.
【0027】(3)フィルム積層厚み 2次イオン質量分析装置(SIMS)を用いて、表層か
ら深さ3000nmの範囲のフイルム中の粒子の内もっ
とも高濃度の粒子に起因する元素とポリエステルの炭素
元素の濃度比(M+ /C+ )を粒子濃度とし、表面から
深さ3000nmまで厚さ方向の分析を行なう。表層で
は表面という界面のために粒子濃度は低く表面から遠ざ
かるにつれて粒子濃度は高くなる。本発明フイルムの場
合はいったん極大値となった粒子濃度がまた減少し始め
る。この濃度分布曲線をもとに表層粒子濃度がの極大値
の1/2となる深さ(この深さは極大値となる深さより
も深い)を求め、これを積層厚さとした。条件は次の通
り。(3) Film Lamination Thickness Using a secondary ion mass spectrometer (SIMS), the element derived from the highest concentration of particles in the film in the depth range of 3000 nm from the surface layer and the carbon element of polyester The concentration ratio (M + / C + ) is defined as the particle concentration, and analysis is performed in the thickness direction from the surface to a depth of 3000 nm. In the surface layer, the particle concentration is low due to the interface of the surface, and the particle concentration increases as the distance from the surface increases. In the case of the film of the present invention, the particle concentration, which has once reached the maximum value, starts to decrease again. Based on this concentration distribution curve, the depth at which the surface layer particle concentration becomes 1/2 of the maximum value of (the depth is deeper than the maximum value) was determined, and this was taken as the laminated thickness. The conditions are as follows.
【0028】(1) 測定装置 2次イオン質量分析装置(SIMS) ***、ATOMIKA 社製 A-DIDA3000 (2) 測定条件 1次イオン種 :O2 + 1次イオン加速電圧:12KV 1次イオン電流:200nA ラスター領域:400μm□ 分析領域:ゲ−ト30% 測定真空度:5.0×10-9Torr E−GUN:0.5KV−3.0A なお、表層から深さ3000nmの範囲に最も多く含有
する粒子が有機高分子粒子の場合はSIMSでは測定が
難しいので、表面からエッチングしながらXPS(X線
光電子分光法)、IR(赤外分光法)などで上記同様の
デプスプロファイルを測定し積層厚さを求めても良い
し、電子顕微鏡等による断面観察で、粒子濃度の変化状
態やポリマの違いによるコントラストの差から界面を認
識し積層厚さを求めることもできる。さらには積層ポリ
マを剥離後、薄膜段差測定機を用いて積層厚さを求める
こともできる。(1) Measuring device Secondary ion mass spectrometer (SIMS) A-DIDA3000 manufactured by ATOMIKA, West Germany (2) Measuring conditions Primary ion species: O 2 + primary ion accelerating voltage: 12 KV Primary ion current: 200nA Raster area: 400μm □ Analysis area: Gate 30% Measuring vacuum degree: 5.0 × 10 -9 Torr E-GUN: 0.5KV-3.0A In addition, most contained in the range of surface depth from 3000nm If the particles to be used are organic polymer particles, it is difficult to measure with SIMS. Therefore, while etching from the surface, measure the same depth profile as above with XPS (X-ray photoelectron spectroscopy), IR (infrared spectroscopy), etc. The thickness can be obtained, or the layer thickness can be obtained by recognizing the interface from the difference in contrast due to the change state of particle concentration and the difference in polymer by observing the cross section with an electron microscope or the like. Furthermore, after peeling the laminated polymer, the laminated thickness can be obtained using a thin film step measuring machine.
【0029】(4)フィルム表面の配向 ナトリウムD線(589nm)を光源として、アッベ屈
折率計を用いて測定した。マウント液にはヨウ化メチレ
ンを用い、25℃、65%RHにて測定した。(4) Orientation of film surface It was measured using an Abbe refractometer with sodium D line (589 nm) as a light source. Methylene iodide was used as the mount solution, and measurement was performed at 25 ° C. and 65% RH.
【0030】フィルムの二軸配向性は長手方向、幅方
向、厚さ方向の屈折率をN1 、N2 、N3 とした時、
(N1 −N2 )の絶対値が0. 07以下、かつ、N3 /
[(N1+N2 )/2]が0. 95以下であることをひ
とつの基準とできる。また、レーザー型屈折率計を用い
て屈折率を測定してもよい。さらに、この方法では測定
が難しい場合は全反射レーザーラマン法を用いることも
できる。The biaxial orientation of the film is such that when the refractive indices in the longitudinal direction, width direction and thickness direction are N1, N2 and N3,
The absolute value of (N1-N2) is 0.07 or less, and N3 /
One of the criteria is that [(N1 + N2) / 2] is 0.95 or less. Further, the refractive index may be measured using a laser type refractometer. Further, when the measurement is difficult by this method, the total reflection laser Raman method can be used.
【0031】(5)ヤング率 JIS−Z−1702に規定された方法にしたがって、
インストロンタイプの引張り試験機を用いて、25℃、
65%RHにて測定した。(5) Young's modulus According to the method specified in JIS-Z-1702,
Using an Instron type tensile tester,
It was measured at 65% RH.
【0032】(6)破断伸度 JIS K−7127に規定された方法に従って、イン
ストロンタイプの引張試験機を用いて、25℃、65%
RHにて測定した時の、(伸張した長さ/元の試料長)
×100を破断伸度(%)とした。(6) Elongation at break According to the method specified in JIS K-7127, using an Instron type tensile tester, 25 ° C., 65%
(Extended length / original sample length) when measured by RH
× 100 was defined as the elongation at break (%).
【0033】(7)出力特性 フィルムに磁性塗料をグラビヤロールを用いて塗布す
る。磁性塗料は次のようにして調製した。(7) Output characteristics A magnetic paint is applied to the film using a gravure roll. The magnetic paint was prepared as follows.
【0034】 ・Fe 100部 平均粒子サイズ 長さ :0. 3μm 針状比:10/1 抗磁力 :2000Oe ・ポリウレタン樹脂 15部 ・塩化ビニル・酢酸ビニル共重合体 5部 ・ニトロセルロース樹脂 5部 ・酸化アルミ粉末 3部 (平均粒径:0.3μm) ・カーボンブラック 1部 ・レシチン 2部 ・メチルエチルケトン 100部 ・メチルイソブチルケトン 100部 ・トルエン 100部 ・ステアリン酸 2部 上記組成物をボールミルで48時間混合分散した後、硬
化剤6部を添加して得られた混練物をフィルターでろ過
して磁性塗布液を準備し、フィルム上に塗布、磁場配向
させ、110℃で乾燥し、さらに小型テストカレンダー
装置(スチールロール/ナイロンロール、5段)で、温
度70℃、線圧200kg/cm でカレンダー処理した後、
70℃、48時間でキュアリングし塗布型磁気記録媒体
を得た。このテープ原反をVTRカセットに組み込みV
TRテープとした。このテープに市販のHi8用VTR
(SONY社製EV−BS3000)を用いて、7MH
z±1MHzのC/N測定を行なった。Fe 100 parts Average particle size Length: 0.3 μm Needle ratio: 10/1 Coercive force: 2000 Oe ・ Polyurethane resin 15 parts ・ Vinyl chloride / vinyl acetate copolymer 5 parts ・ Nitrocellulose resin 5 parts ・Aluminum oxide powder 3 parts (average particle size: 0.3 μm) ・ Carbon black 1 part ・ Lecithin 2 parts ・ Methyl ethyl ketone 100 parts ・ Methyl isobutyl ketone 100 parts ・ Toluene 100 parts ・ Stearic acid 2 parts The above composition was ball milled for 48 hours. After mixing and dispersing, a kneaded product obtained by adding 6 parts of a curing agent is filtered with a filter to prepare a magnetic coating liquid, which is coated on a film, magnetically oriented, dried at 110 ° C., and further a small test calendar. After calendering with a device (steel roll / nylon roll, 5 steps) at a temperature of 70 ° C and a linear pressure of 200 kg / cm,
The coating type magnetic recording medium was obtained by curing at 70 ° C. for 48 hours. This tape roll is incorporated into a VTR cassette
TR tape was used. Commercially available Hi8 VTR on this tape
(EV-BS3000 manufactured by Sony), 7MH
C / N measurement at z ± 1 MHz was performed.
【0035】このC/Nを市販されているHi8MEビ
デオテープと比較して同等のもの(差が+0dB以下の
もの)を出力特性:不良、差が+3dB以下のものを出
力特性:良、差が+3dBを超えるものを出力特性:優
とした。Comparing this C / N with a commercially available Hi8ME video tape, an equivalent one (a difference of +0 dB or less) is output characteristic: defective, and a difference of +3 dB or less is an output characteristic: good, difference is Output characteristics exceeding +3 dB were evaluated as excellent.
【0036】[0036]
【実施例】次に実施例に基づき、本発明をさらに詳細に
説明する。The present invention will be described in more detail based on the following examples.
【0037】実施例1(表1) 粒子組成がジビニルベンゼン81%であるポリジビニル
ベンゼン粒子の水スラリーをベント式の2軸混練押出機
を用いて直接PENに練り込み、PENの粒子ペレット
を得た。Example 1 (Table 1) An aqueous slurry of polydivinylbenzene particles having a particle composition of 81% divinylbenzene was directly kneaded into PEN using a vent type twin-screw kneading extruder to obtain PEN particle pellets. It was
【0038】この粒子ペレットと実質的に粒子を含有し
ないPENポリマペレットを適当量混合し、180℃で
8時間減圧乾燥(3Torr)した後、ポリマA:0.2μ
m径ポリジビニルベンゼン粒子1.0重量%含有ポリ
マ、ポリマB:粒子を含有しないポリマをそれぞれ押出
機1、押出機2に供給し290℃、295℃で溶融し
た。これらのポリマをそれぞれ95%濾過が3μmであ
る高精度フィルタ−を用いて瀘過した後、矩形合流部に
て3層積層とした(A/B/A)。This particle pellet and a PEN polymer pellet containing substantially no particles are mixed in an appropriate amount, dried under reduced pressure (3 Torr) at 180 ° C. for 8 hours, and then polymer A: 0.2 μm.
Polymer containing 1.0% by weight of m-diameter polydivinylbenzene particles and polymer B: a polymer containing no particles were supplied to extruder 1 and extruder 2, respectively, and melted at 290 ° C and 295 ° C. Each of these polymers was filtered through a high-precision filter having 95 μm filtration of 3 μm, and then three layers were laminated at the rectangular confluence (A / B / A).
【0039】これを静電印加キャスト法を用いて表面温
度25℃のキャスティング・ドラムに巻きつけて冷却固
化し、未延伸フィルムを作った。この時、口金スリット
間隙/未延伸フィルム厚さの比を10とした。また、そ
れぞれの押出機の吐出量を調節し総厚さ、およびA層の
厚さを調節した。This was wound around a casting drum having a surface temperature of 25 ° C. by an electrostatically applied cast method and cooled and solidified to prepare an unstretched film. At this time, the ratio of the die slit gap / unstretched film thickness was set to 10. Further, the total thickness and the thickness of the A layer were adjusted by adjusting the discharge amount of each extruder.
【0040】この未延伸フィルムを温度140℃にて長
手方向に5.0倍延伸した。この延伸は2組ずつのロ−
ルの周速差で、4段階で行なった。この一軸延伸フィル
ムをテンターを用いて140℃で幅方向に4.5倍延伸
した。さらに、テンターを用いて165℃で幅方向に
1.15倍延伸した。このフィルムを定長下で2010
℃にて3秒間熱処理し、総厚さ4.5μm、A層厚さ
0.4μmの二軸配向フィルムを得た。This unstretched film was stretched 5.0 times in the longitudinal direction at a temperature of 140 ° C. This stretching is done with two pairs of rolls.
It was carried out in four stages with the peripheral speed difference of Le. This uniaxially stretched film was stretched 4.5 times in the width direction at 140 ° C. using a tenter. Furthermore, it stretched 1.15 times in the width direction at 165 ° C. using a tenter. 2010 this film under fixed length
The film was heat-treated at ℃ for 3 seconds to obtain a biaxially oriented film having a total thickness of 4.5 μm and an A layer thickness of 0.4 μm.
【0041】この磁気記録媒体用ポリエステルフィルム
の特性は第1表に示したとおりであり、出力特性が良好
であった。The characteristics of this polyester film for a magnetic recording medium are as shown in Table 1, and the output characteristics were good.
【0042】実施例2〜4、比較例1〜4(表1) 実施例1と同様にして、粒子の種類、粒径、含有量、積
層厚み、延伸倍率等を変更した磁気記録媒体用ポリエス
テルフィルムを得た。表1に示すように本発明範囲の磁
気記録媒体用ポリエステルフィルムは出力特性が良好で
あるが、そうでないものは出力特性が良好でないことが
わかる。Examples 2 to 4 and Comparative Examples 1 to 4 (Table 1) In the same manner as in Example 1, polyesters for magnetic recording media in which the kind of particles, particle size, content, laminated thickness, draw ratio, etc. were changed. I got a film. As shown in Table 1, the polyester film for a magnetic recording medium within the scope of the present invention has good output characteristics, but those without it have poor output characteristics.
【0043】[0043]
【表1】 [Table 1]
【0044】[0044]
【発明の効果】本発明の磁気記録媒体用ポリエステルフ
ィルムは縦および横方向の強度を大きくし、かつ縦およ
び横方向の伸度に異方性を持たせたので、フィルム加工
特性に起因する優れた出力特性を得ることができた。ま
た、強度が大きいので将来のテ−プ薄膜化にも対応する
ことができる。The polyester film for a magnetic recording medium of the present invention has high strength in the machine direction and the transverse direction and has anisotropy in the elongation in the machine direction and the transverse direction. It was possible to obtain excellent output characteristics. Further, since it has high strength, it can be applied to future tape thinning.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 FI 技術表示箇所 // B29K 67:00 B29L 9:00 C08L 67:00 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification number Office reference number FI technical display location // B29K 67:00 B29L 9:00 C08L 67:00
Claims (3)
ルボキシレートからなるフィルムであって、縦方向のヤ
ング率が700kg/mm2 以上、縦方向の破断伸度が50
%以上、横方向のヤング率が700kg/mm2 以上、横方
向の破断伸度が50%未満であることを特徴とする磁気
記録媒体用ポリエステルフィルム。1. A film made of polyethylene-2,6-naphthalenedicarboxylate, having a Young's modulus in the machine direction of 700 kg / mm 2 or more and a breaking elongation in the machine direction of 50.
%, The Young's modulus in the lateral direction is 700 kg / mm 2 or more, and the breaking elongation in the lateral direction is less than 50%, which is a polyester film for a magnetic recording medium.
層構造からなり、A層厚みが0.01〜3.0μmであ
る請求項1記載の磁気記録媒体用ポリエステルフィル
ム。2. The film comprises at least two layers A and B.
The polyester film for a magnetic recording medium according to claim 1, which has a layered structure and has an A layer thickness of 0.01 to 3.0 µm.
−2,6−ナフタレンジカルボキシレートである請求項
2記載の磁気記録媒体用ポリエステルフィルム。3. The polyester film for a magnetic recording medium according to claim 2, wherein the A layer and / or the B layer is polyethylene-2,6-naphthalene dicarboxylate.