JPH0788887A - Resin molded form with transparent part and manufacture thereof - Google Patents
Resin molded form with transparent part and manufacture thereofInfo
- Publication number
- JPH0788887A JPH0788887A JP26171993A JP26171993A JPH0788887A JP H0788887 A JPH0788887 A JP H0788887A JP 26171993 A JP26171993 A JP 26171993A JP 26171993 A JP26171993 A JP 26171993A JP H0788887 A JPH0788887 A JP H0788887A
- Authority
- JP
- Japan
- Prior art keywords
- molded product
- transparent
- resin molded
- insert sheet
- transparent portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】この発明は、しわ、位置ずれおよ
びたるみのないインサートシートがきれいに固着された
透明部を有する樹脂成形品とその製造方法に関するもの
である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a resin molded product having a transparent portion to which an insert sheet having no wrinkles, misalignment and slack is fixed firmly and a method for producing the same.
【０００２】[0002]
【従来の技術】インサートシートを射出成形により成形
品に一体化して作製する方法がある。成形品を通して内
部の液晶文字などが見えるようにするためには、成形品
に表示窓となる透明部分を設けることが必要である。2. Description of the Related Art There is a method in which an insert sheet is manufactured by being integrated with a molded product by injection molding. In order for the liquid crystal characters and the like to be visible through the molded product, it is necessary to provide the molded product with a transparent portion serving as a display window.
【０００３】透明部分を設ける方法として、透明部と隠
蔽部とを有するインサートシートを用い、インサートシ
ートの背面全部に透明性樹脂成形品を一体化して形成す
る方法がある（図５参照）。透明部の背面にも透明性樹
脂成形品が一体化して形成されるため、透明部は透明性
にすぐれ、樹脂成形品の表面は金型形状が忠実に再現さ
れた美しいものになる。As a method of providing a transparent portion, there is a method of using an insert sheet having a transparent portion and a concealing portion and integrally forming a transparent resin molded product on the entire back surface of the insert sheet (see FIG. 5). Since the transparent resin molded product is integrally formed on the back surface of the transparent part, the transparent part has excellent transparency, and the surface of the resin molded product becomes a beautiful one in which the mold shape is faithfully reproduced.
【０００４】また、透明部と隠蔽部とを有するインサー
トシートを用い、隠蔽部の背面にのみ不透明樹脂成形品
を一体化して形成し、透明部の背面には樹脂成形品が形
成されないようにする方法がある（図６参照）。An insert sheet having a transparent portion and a concealing portion is used, and an opaque resin molded product is integrally formed only on the back surface of the concealing portion so that the resin molded product is not formed on the rear surface of the transparent portion. There is a method (see FIG. 6).
【０００５】[0005]
【発明が解決しようとする課題】しかし、前者の場合、
インサートシートが射出成形された透明樹脂成形品部分
をすべて覆うように構成されることに起因して、側面の
立上がりが大きい成形品を得るときには、インサートシ
ートの伸びが樹脂成形品の形状に追従できないので、イ
ンサートシートにしわが生じたり、位置ずれなどが生じ
るという欠点があった。However, in the case of the former,
When the insert sheet is configured to cover all the injection-molded transparent resin molded product parts, the elongation of the insert sheet cannot follow the shape of the resin molded product when obtaining a molded product with a large side rise. Therefore, there is a defect that the insert sheet is wrinkled or displaced.
【０００６】また、後者の場合、インサートシートの透
明部の背面には不透明樹脂成形品が形成されないように
する結果、不透明樹脂成形品には穴あき部が形成され
る。ところが、成形と同時にインサートシートを一体化
すると、成形用樹脂を成形して金型から取り出して大気
中で放冷したとき、成形品には樹脂収縮が起こるがイン
サートシートには収縮が生じない。このため、インサー
トシートの透明部がたるんでしまい、液晶表示などがゆ
がんで見えるという問題点が生じた。また、立ち上がり
が大きい成形品を得るときには、前者の方法と同様に、
インサートシートの伸びが不充分であるため、インサー
トシートにしわが生じたり、位置ずれなどが生じるとい
う欠点があった。In the latter case, since the opaque resin molded product is not formed on the back surface of the transparent portion of the insert sheet, the opaque resin molded product has a hole. However, if the insert sheet is integrated at the same time as the molding, when the molding resin is molded, taken out from the mold and allowed to cool in the air, the molded product shrinks but the insert sheet does not shrink. As a result, the transparent portion of the insert sheet sags, and the liquid crystal display appears distorted. Also, when obtaining a molded product with a large rise, similar to the former method,
Since the insert sheet is insufficiently stretched, there are drawbacks such that the insert sheet is wrinkled or displaced.
【０００７】したがって、この発明は、上記のような欠
点を解消した透明部を有する樹脂成形品とその製造方法
を提供することを目的とする。Therefore, it is an object of the present invention to provide a resin molded article having a transparent portion which eliminates the above-mentioned drawbacks and a method for producing the same.
【０００８】[0008]
【課題を解決するための手段】この発明は、以上の目的
を達成するために、透明部を有する樹脂成形品を、透明
部と隠蔽部を有するインサートシートが一体成形された
成形品において、透明部に対応して透明樹脂成形品が形
成され、隠蔽部に対応する部分を含む部分に不透明樹脂
成形品が形成され、インサートシートが不透明樹脂成形
品を部分的に覆うように一体成形されるように構成し
た。In order to achieve the above object, the present invention provides a resin molded article having a transparent portion, which is a molded article in which an insert sheet having a transparent portion and a concealing portion is integrally molded. A transparent resin molded product is formed corresponding to the part, an opaque resin molded product is formed in a portion including a portion corresponding to the concealed portion, and the insert sheet is integrally molded so as to partially cover the opaque resin molded product. Configured to.
【０００９】また、この発明は、以上の目的を達成する
ために、透明部を有する樹脂成形品の製造方法を、透明
部と隠蔽部を有するインサートシートの透明部に対応し
て透明樹脂成形品を接着させ、次にインサートシートを
金型内に装着し隠蔽部に対応する部分を含む部分に不透
明樹脂を射出して不透明樹脂成形品の一部分にインサー
トシートを一体的に形成するように構成した。Further, in order to achieve the above object, the present invention provides a method for producing a resin molded product having a transparent portion, in which a transparent resin molded product corresponding to a transparent portion of an insert sheet having a transparent portion and a concealing portion is provided. Then, the insert sheet is mounted in a mold, and an opaque resin is injected to a portion including a portion corresponding to the concealing portion to integrally form the insert sheet on a part of the opaque resin molded product. .
【００１０】また、この発明は、上記の透明部を有する
樹脂成形品の製造方法において、インサートシートが、
透明樹脂成形品を接着する前に予備成形されたものであ
るように構成してもよい。Further, in the present invention, in the method for producing a resin molded product having the above-mentioned transparent portion, the insert sheet is
The transparent resin molded article may be preformed before being bonded.
【００１１】図面を参照しながらこの発明をさらに詳し
く説明する。The present invention will be described in more detail with reference to the drawings.
【００１２】図１は、この発明の透明部を有する樹脂成
形品の一実施例を示す断面図である。図２は、この発明
の透明部を有する樹脂成形品の製造方法に用いるインサ
ートシートの一実施例を示す断面図である。図３は、こ
の発明の透明部を有する樹脂成形品の製造方法の一実施
例を示す断面図である。図４は、この発明の透明部を有
する樹脂成形品の他の実施例を示す断面図である。１は
インサートシート、２は基体シート、３は隠蔽部、４は
透明部、５は透明樹脂成形品、６は不透明樹脂成形品、
７はエンボスをそれぞれ示す。FIG. 1 is a sectional view showing an embodiment of a resin molded product having a transparent portion of the present invention. FIG. 2 is a sectional view showing an embodiment of an insert sheet used in the method for producing a resin molded product having a transparent portion according to the present invention. FIG. 3 is a sectional view showing an embodiment of a method for manufacturing a resin molded product having a transparent portion of the present invention. FIG. 4 is a sectional view showing another embodiment of a resin molded product having a transparent portion of the present invention. 1 is an insert sheet, 2 is a base sheet, 3 is a concealing part, 4 is a transparent part, 5 is a transparent resin molded product, 6 is an opaque resin molded product,
7 shows embossing, respectively.
【００１３】インサートシート１の基体シート２として
は、ポリエチレンテレフタレート、ポリカーボネート、
ポリブチレンテレフタレートなどの透明性を有するフィ
ルムを使用するとよい。As the base sheet 2 of the insert sheet 1, polyethylene terephthalate, polycarbonate,
It is preferable to use a transparent film such as polybutylene terephthalate.
【００１４】隠蔽部３は、背面の樹脂成形品が見えない
ようにする部分であり、単に背面を遮蔽するだけでな
く、文字・記号などが形成された図柄であってもよい。
隠蔽部３は、ウレタン系樹脂、ポリエステル系樹脂など
の基体シート２に固着性のよい隠蔽性インキで印刷して
形成するとよい。また、真空蒸着法、イオンプレーティ
ング法、スパッタリング法などにより、部分的に金属蒸
着層を設けてもよい。The concealing portion 3 is a portion for preventing the resin molded product on the back surface from being seen, and may not only shield the back surface but also a pattern in which characters and symbols are formed.
The concealing portion 3 may be formed by printing the concealing ink having good adhesiveness on the base sheet 2 such as urethane resin or polyester resin. Further, the metal vapor deposition layer may be partially provided by a vacuum vapor deposition method, an ion plating method, a sputtering method, or the like.
【００１５】透明部４は、成形品の背面に配置された液
晶表示などが見えるようにする透明な部分である。透明
部４は、隠蔽部３を印刷しないことにより形成される。
また、透明部４を、透過性染料インキ、透過性顔料イン
キなどを印刷して着色することも可能である。隠蔽部３
と透明部４を印刷するのは、フィルムの表面、裏面のい
ずれでも、また両面でもよい。The transparent portion 4 is a transparent portion which allows a liquid crystal display or the like arranged on the back surface of the molded product to be seen. The transparent portion 4 is formed by not printing the concealing portion 3.
Further, the transparent portion 4 can be colored by printing a transparent dye ink or a transparent pigment ink. Concealing section 3
The transparent portion 4 may be printed on either the front surface or the back surface of the film, or on both surfaces.
【００１６】また、必要に応じて、インサートシート１
の背面に接着層を設けてもよい。If necessary, the insert sheet 1
An adhesive layer may be provided on the back surface of the.
【００１７】また、必要に応じて、インサートシート１
を予備成形し、射出成形用金型に追随しやすい形状にし
てもよい。Further, if necessary, the insert sheet 1
May be preformed to have a shape that easily follows the injection molding die.
【００１８】次に、インサートシート１の透明部４に透
明樹脂成形品５を接着する。接着するには、インサート
シート１の透明部４または透明樹脂成形品５に接着剤を
塗布し、貼り合わせればよい。透明樹脂成形品５として
は、先に射出成形して最終の金型形状に沿わせた透明成
形品や板状の透明成形品を用いることができる。透明樹
脂成形品５の大きさは、透明部４と同一とする。また、
透明部４よりも若干大きめとし、隠蔽部３に若干かかる
程度としてもよい。透明部４より小さい透明樹脂成形品
５は、成形した時に不透明樹脂成形品６が透明部４の背
面にまで成形され、透明部４から不透明樹脂成形品６が
見えるので不適当である。Next, the transparent resin molded product 5 is bonded to the transparent portion 4 of the insert sheet 1. For adhesion, an adhesive may be applied to the transparent portion 4 of the insert sheet 1 or the transparent resin molded product 5 and then bonded. As the transparent resin molded product 5, it is possible to use a transparent molded product that is injection-molded first and conforms to the final mold shape, or a plate-shaped transparent molded product. The size of the transparent resin molded product 5 is the same as that of the transparent portion 4. Also,
It may be slightly larger than the transparent portion 4 and may be slightly covered by the concealing portion 3. A transparent resin molded product 5 smaller than the transparent portion 4 is unsuitable because the opaque resin molded product 6 is molded up to the back surface of the transparent portion 4 and the opaque resin molded product 6 can be seen from the transparent portion 4 when molded.
【００１９】次に、透明樹脂成形品５を貼り付けたイン
サートシート１を射出成形用金型内に装着し、透明部４
背面以外のキャビティに不透明樹脂成形品６を射出する
ことにより、不透明樹脂成形品６の一部分とインサート
シート１とを一体化させ、透明部４を有する樹脂成形品
を得ることができる。金型は、金型を閉じた際に透明部
４の背面に不透明樹脂成形品６が充填されないようにす
るため、キャビティのコアを押し当ててすきまが生じな
いようにする必要がある。Next, the insert sheet 1 to which the transparent resin molded product 5 is attached is mounted in the injection molding die, and the transparent portion 4
By injecting the opaque resin molded product 6 into the cavity other than the back surface, a part of the opaque resin molded product 6 and the insert sheet 1 can be integrated, and a resin molded product having the transparent portion 4 can be obtained. In order to prevent the opaque resin molded product 6 from being filled in the back surface of the transparent portion 4 when the mold is closed, it is necessary to press the core of the cavity so that no gap is generated.
【００２０】また、上記したように、インサートシート
１に透明樹脂成形品５を貼り付けたのち不透明樹脂成形
品６を射出成形するのではなく、透明樹脂成形品５と不
透明樹脂成形品６とを続けて射出成形して成形品を形成
するために、２色成形専用の射出成形機を用いてもよ
い。As described above, the transparent resin molded product 5 and the opaque resin molded product 6 are not injection-molded after the transparent resin molded product 5 is pasted on the insert sheet 1. An injection molding machine dedicated to two-color molding may be used to subsequently perform injection molding to form a molded product.
【００２１】また、透明部４を有する樹脂成形品には、
メンブレンスイッチ用の押しボタン部となるエンボス７
があわせて形成されたものであってもよい（図４参
照）。金型の一方に凸部を、他方に凹部を設け、凸部と
凹部との間にはインサートシート１のみが挟まれるよう
にすることにより、インサートシート１の一部分をエン
ボス７に形成することができる。インサートシート１の
エンボス７の裏側には、不透明樹脂成形品６が形成され
ないが、インサートシート１のエンボス７はふくらんだ
状態となっているので、樹脂収縮が生じてもたるみが問
題となることはない。Further, in the resin molded product having the transparent portion 4,
Embossing 7 to be the push button for the membrane switch
May be formed together (see FIG. 4). By forming a convex portion on one side of the mold and a concave portion on the other side so that only the insert sheet 1 is sandwiched between the convex portion and the concave portion, a part of the insert sheet 1 can be formed on the embossment 7. it can. The opaque resin molded product 6 is not formed on the back side of the emboss 7 of the insert sheet 1, but since the emboss 7 of the insert sheet 1 is in a bulged state, sagging does not cause a problem even if resin shrinkage occurs. Absent.
【００２２】[0022]
【作用】この発明は、以上の構成よりなるから、次の作
用が奏される。Since the present invention has the above-mentioned structure, the following effects are achieved.
【００２３】この発明の透明部を有する樹脂成形品の製
造方法は、インサートシートを樹脂成形品の表面に全面
的に一体成形するのではなく、樹脂成形品の一部分のみ
一体成形する。したがって、インサートシートは無理に
伸ばされない。In the method of manufacturing a resin molded product having a transparent portion of the present invention, the insert sheet is not integrally molded on the entire surface of the resin molded product but only a part of the resin molded product is integrally molded. Therefore, the insert sheet is not stretched forcibly.
【００２４】また、この発明の透明部を有する樹脂成形
品は、インサートシートの透明部にも透明樹脂成形品が
存在する。Further, in the resin molded product having the transparent portion of the present invention, the transparent resin molded product also exists in the transparent portion of the insert sheet.
【００２５】[0025]
【実施例】厚さ188μｍのポリエチレンテレフタレート
フィルムを基体シートとし、家電製品のスイッチパネル
となるように、ウレタンインキで隠蔽部をスクリーン印
刷して形成した。インキが印刷されず窓として残したい
部分を透明部とした。さらに、インキの固着を高めるた
め、40℃、24時間の乾燥を行ってインサートシートを得
た。EXAMPLE A polyethylene terephthalate film having a thickness of 188 μm was used as a base sheet, and a concealing portion was screen-printed with urethane ink so as to form a switch panel for home electric appliances. The area where the ink was not printed and was left as a window was made transparent. Further, in order to enhance the fixation of the ink, it was dried at 40 ° C. for 24 hours to obtain an insert sheet.
【００２６】次に、インサートシートの裏面全面にポリ
エステル系樹脂からなるホットメルト接着剤をコーティ
ングし、ホットメルト接着剤が活性なうちに、あらかじ
め切断しておいた透明部より面積がやや大きい透明樹脂
板を貼り付けた。Next, the entire back surface of the insert sheet is coated with a hot-melt adhesive made of polyester resin, and while the hot-melt adhesive is active, the transparent resin has a slightly larger area than the transparent portion cut in advance. I stuck the board.
【００２７】ホットメルト接着剤を冷却固化した後、透
明樹脂板が貼り付けられたインサートシートを射出成形
用金型内に装着し、金型を閉じ、ベージュ色に着色され
たＡＢＳ樹脂を射出した。金型には、インサートシート
の透明部の背面にＡＢＳ樹脂が充填されないようにする
ため、透明樹脂板を挟み込むように作動するコアを設
け、また金型を閉じるのと同時にインサートシートの隠
蔽部の一部に押しボタンとなるエンボスを形成すること
ができる凹凸を設けた。After the hot melt adhesive was cooled and solidified, an insert sheet having a transparent resin plate attached thereto was mounted in a mold for injection molding, the mold was closed, and a beige-colored ABS resin was injected. . In order to prevent the ABS resin from being filled on the back surface of the transparent part of the insert sheet, the mold is provided with a core that operates so as to sandwich the transparent resin plate, and at the same time when the mold is closed, the concealed part of the insert sheet is hidden. The unevenness that can form the embossing that becomes the push button was provided in part.
【００２８】金型を開け、取り出した透明部を有する樹
脂成形品は、インサートシートがしわや位置ずれなく一
体成形され、美しい透明部を有するものであった。In the resin molded product having the transparent portion taken out of the mold, the insert sheet was integrally molded without wrinkles or displacement and had a beautiful transparent portion.
【００２９】[0029]
【発明の効果】この発明の透明部を有する樹脂成形品と
その製造方法は、以上の作用および構成からなるので、
次の効果が奏される。The resin molded product having a transparent portion and the method for producing the same according to the present invention have the above-described actions and configurations.
The following effects are exhibited.
【００３０】この発明は、しわ、位置ずれおよびたるみ
のないインサートシートがきれいに固着された透明部を
有する樹脂成形品を得ることができる。According to the present invention, it is possible to obtain a resin molded product having a transparent portion to which an insert sheet having a wrinkle, a positional deviation and a slack is fixed firmly.
【００３１】また、この発明の透明部を有する樹脂成形
品の製造方法によると、上記の透明部を有する樹脂成形
品を容易に得ることができる。Further, according to the method for producing a resin molded product having a transparent portion of the present invention, the resin molded product having a transparent portion can be easily obtained.
【図１】この発明の透明部を有する樹脂成形品の一実施
例を示す断面図である。FIG. 1 is a sectional view showing an embodiment of a resin molded product having a transparent portion of the present invention.
【図２】この発明の透明部を有する樹脂成形品の製造方
法に用いるインサートシートの一実施例を示す断面図で
ある。FIG. 2 is a sectional view showing an embodiment of an insert sheet used in the method for producing a resin molded product having a transparent portion according to the present invention.
【図３】この発明の透明部を有する樹脂成形品の製造方
法の一実施例を示す断面図である。FIG. 3 is a cross-sectional view showing an embodiment of a method for producing a resin molded product having a transparent portion according to the present invention.
【図４】この発明の透明部を有する樹脂成形品の他の実
施例を示す断面図である。FIG. 4 is a sectional view showing another embodiment of a resin molded product having a transparent portion of the present invention.
【図５】従来の透明部を有する樹脂成形品の一実施例を
示す断面図である。FIG. 5 is a cross-sectional view showing an example of a conventional resin molded product having a transparent portion.
【図６】従来の透明部を有する樹脂成形品の一実施例を
示す断面図である。FIG. 6 is a cross-sectional view showing an example of a conventional resin molded product having a transparent portion.
１ インサートシート ２ 基体シート ３ 隠蔽部 ４ 透明部 ５ 透明樹脂成形品 ６ 不透明樹脂成形品 ７ エンボス 1 Insert Sheet 2 Base Sheet 3 Concealed Part 4 Transparent Part 5 Transparent Resin Molded Product 6 Opaque Resin Molded Product 7 Embossing
Claims (3)
トが一体成形された成形品において、透明部に対応して
透明樹脂成形品が形成され、隠蔽部に対応する部分を含
む部分に不透明樹脂成形品が形成され、インサートシー
トが不透明樹脂成形品を部分的に覆うように一体成形さ
れたことを特徴とする透明部を有する樹脂成形品。1. A molded product integrally formed with an insert sheet having a transparent portion and a concealing portion, wherein a transparent resin molded product is formed corresponding to the transparent portion, and an opaque resin molding is performed on a portion including a portion corresponding to the concealing portion. A molded resin product having a transparent portion, wherein the molded product is formed and an insert sheet is integrally molded so as to partially cover the opaque molded resin product.
トの透明部に対応して透明樹脂成形品を接着させ、次に
インサートシートを金型内に装着し隠蔽部に対応する部
分を含む部分に不透明樹脂を射出して不透明樹脂成形品
の一部分にインサートシートを一体的に形成することを
特徴とする透明部を有する樹脂成形品の製造方法。2. A transparent resin molded product is adhered to a transparent portion of an insert sheet having a transparent portion and a concealing portion, and then the insert sheet is mounted in a mold to a portion including a portion corresponding to the concealing portion. A method for manufacturing a resin molded product having a transparent portion, which comprises injecting an opaque resin to integrally form an insert sheet on a part of the opaque resin molded product.
接着する前に予備成形されたものである請求項２記載の
透明部を有する樹脂成形品の製造方法。3. The method for producing a resin molded product having a transparent portion according to claim 2, wherein the insert sheet is preformed before adhering the transparent resin molded product.