JPH0748250A - Tape for preventing sleepiness - Google Patents
Tape for preventing sleepinessInfo
- Publication number
- JPH0748250A JPH0748250A JP6121123A JP12112394A JPH0748250A JP H0748250 A JPH0748250 A JP H0748250A JP 6121123 A JP6121123 A JP 6121123A JP 12112394 A JP12112394 A JP 12112394A JP H0748250 A JPH0748250 A JP H0748250A
- Authority
- JP
- Japan
- Prior art keywords
- styrene
- menthol
- adhesive layer
- preventing
- tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、眠気防止用テープに関
する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a drowsiness prevention tape.
【０００２】[0002]
【従来の技術】眠気を防止するために種々の方法が試み
られており、例えばｌ−メントール入りのチューイング
ガムを噛んだり、ｌ−メントール等の香料を放出させる
方法等が挙げられる。上記ｌ−メントールは、その匂い
だけでなく皮膚に対して冷涼感を与えることから、多く
の消炎鎮痛用の外用貼付剤に用いられている。Various methods have been attempted to prevent drowsiness, such as a method of chewing chewing gum containing 1-menthol or a method of releasing a flavoring agent such as 1-menthol. The l-menthol gives a cool sensation to the skin as well as its odor, and is therefore used in many patches for external use for inflammation and analgesia.
【０００３】しかしながら、ｌ−メントールは揮発性が
あり、常温で結晶状態であることから、貼付剤に大量に
配合すると包材中で気化し、結晶が析出することがあ
る。特にゴム系粘着剤がスチレン−イソプレン−スチレ
ンブロック共重合体を主成分とする場合は、ｌ−メント
ール自体が可塑剤として働き、ｌ−メントールがスチレ
ン層を膨潤させて粘着剤層の凝集力を低下させ、凝集破
壊を起こす原因となっていた。従って、ｌ−メントール
をゴム系粘着剤に添加する場合、一定水準の粘着性を維
持しながら大量に配合することが難しいという問題点が
あった。However, since l-menthol is volatile and is in a crystalline state at room temperature, if it is mixed in a large amount in a patch, it may be vaporized in the packaging material to precipitate crystals. In particular, when the rubber-based pressure-sensitive adhesive contains a styrene-isoprene-styrene block copolymer as a main component, l-menthol itself acts as a plasticizer, and l-menthol swells the styrene layer to increase the cohesive force of the pressure-sensitive adhesive layer. It was a cause of cohesive failure. Therefore, when 1-menthol is added to a rubber-based pressure-sensitive adhesive, it is difficult to add a large amount of it while maintaining a certain level of tackiness.
【０００４】この対策として、Ａ−Ｂ−Ａ型熱可塑性エ
ラストマーに、メタケイ酸マグネシウムを配合すること
により、メタケイ酸マグネシウムにサリチル酸メチル等
の薬効成分を吸収させ、粘着剤層の可塑化や軟化を防止
する方法が開示されている（特公平３−１７４０４号公
報）。As a countermeasure against this, by mixing magnesium metasilicate with the ABA type thermoplastic elastomer, the medicinal components such as methyl salicylate are absorbed in magnesium metasilicate to plasticize or soften the pressure-sensitive adhesive layer. A method of preventing is disclosed (Japanese Patent Publication No. 3-17404).
【０００５】また、Ａ−Ｂ−Ａ型ブロック共重合体、脂
環族系石油樹脂、軟化剤及び吸水性高分子からなる粘着
剤組成物に、ｌ−メントール等の薬剤を配合する方法が
開示されている（特公平１−２９７０６９号公報）。さ
らに、スチレン−イソプレン−スチレンブロック共重合
体、流動パラフィン、粘着付与樹脂及び充填剤からなる
粘着剤組成物に、ｌ−メントール等の薬剤を配合する方
法が開示されている（特公昭５６−２０５１６号公
報）。Also disclosed is a method in which a pressure sensitive adhesive composition comprising an ABA type block copolymer, an alicyclic petroleum resin, a softening agent and a water-absorbing polymer is mixed with a drug such as 1-menthol. (Japanese Patent Publication No. 1-297069). Further, there is disclosed a method of blending a drug such as 1-menthol with an adhesive composition comprising a styrene-isoprene-styrene block copolymer, liquid paraffin, a tackifying resin and a filler (Japanese Patent Publication No. 56-20516). Issue).
【０００６】しかしながら、上記のいずれの方法も眠気
を防止するのに十分な比較的大量のｌ−メントールを配
合する場合には、粘着剤層の凝集力が低下し、糸引き、
糊残り等が生じるという問題点があった。However, in any of the above methods, when a relatively large amount of 1-menthol sufficient to prevent drowsiness is blended, the cohesive force of the pressure-sensitive adhesive layer decreases, and the stringiness,
There is a problem that adhesive residue and the like occur.
【０００７】[0007]
【発明が解決しようとする課題】本発明は、上記問題点
に鑑みてなされたものであり、その目的は、スチレン−
イソプレン−スチレンブロック共重合体を主成分とする
粘着剤層に、眠気を防止するのに十分な量のｌ−メント
ールを含有させながらも、粘着性を阻害することなく、
長時間にわたって眠気防止効果が持続可能な眠気防止用
テープを提供することにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above problems, and an object thereof is styrene-
The isoprene-styrene block copolymer-based pressure-sensitive adhesive layer, while containing l-menthol in an amount sufficient to prevent drowsiness, without impairing the adhesiveness,
The purpose of the present invention is to provide a drowsiness prevention tape that has a long-lasting drowsiness prevention effect.
【０００８】[0008]
【課題を解決するための手段】本発明の眠気防止用テー
プは、支持体上にｌ−メントールを含有する粘着剤層が
形成されたものである。The tape for preventing drowsiness of the present invention comprises a support and a pressure-sensitive adhesive layer containing 1-menthol formed on the support.
【０００９】本発明で用いられる支持体としては、貼付
剤に通常用いられているような支持体を用いることがで
き、柔軟なものが好ましく、例えば、樹脂フィルム、織
布、不織布等が好適に用いられる。As the support used in the present invention, a support which is usually used for patches can be used, and a flexible one is preferable, and for example, a resin film, a woven fabric, a non-woven fabric or the like is preferable. Used.
【００１０】上記樹脂フィルムとしては、例えば、ポリ
エチレン、ポリプロピレン、ポリエチレンテレフタレー
ト、ナイロン、ポリアミド、ポリウレタン、ポリビニル
アルコール、ポリブタジエン、ポリブテン、ポリイソプ
レン、シリコン樹脂、可塑化ポリ塩化ビニル、ポリ塩化
ビニリデン、ポリウレタン系可塑化ポリ塩化ビニル、可
塑化酢酸ビニル−塩化ビニル共重合体、エチレン−酢酸
ビニル共重合体、エチレン−塩化ビニル共重合体、エチ
レン−メタクリル酸メチル共重合体、（メタ）アクリル
酸アルキルエステル、スチレン−イソプレン−スチレン
ブロック共重合体、スチレン−ブタジエン−スチレンブ
ロック共重合体、スチレン−ブタジエンゴム、酢酸セル
ロース、エチルセルロース等をベースポリマーとして用
いるものが挙げられ、これらは単独で使用されてもよ
く、２種以上が併用されてもよい。Examples of the resin film include polyethylene, polypropylene, polyethylene terephthalate, nylon, polyamide, polyurethane, polyvinyl alcohol, polybutadiene, polybutene, polyisoprene, silicone resin, plasticized polyvinyl chloride, polyvinylidene chloride, polyurethane plastics. Polyvinyl chloride, plasticized vinyl acetate-vinyl chloride copolymer, ethylene-vinyl acetate copolymer, ethylene-vinyl chloride copolymer, ethylene-methyl methacrylate copolymer, (meth) acrylic acid alkyl ester, styrene -Isoprene-styrene block copolymers, styrene-butadiene-styrene block copolymers, those using styrene-butadiene rubber, cellulose acetate, ethyl cellulose and the like as the base polymer are mentioned. These may be used alone, or two or more kinds may be used in combination.
【００１１】上記織布及び不織布としては、例えば、
綿、麻、絹等の天然繊維；上記樹脂フィルムに用いられ
るベースポリマーの合成繊維を基材とするものが挙げら
れる。Examples of the woven and non-woven fabrics include
Examples include natural fibers such as cotton, hemp, and silk; those based on synthetic fibers of the base polymer used for the resin film.
【００１２】上記支持体として、織布、不織布又は通気
性のある樹脂フィルムを用いると、ｌ−メントールの経
皮吸収以外に、支持体を通して揮散するｌ−メントール
の爽快な匂いにより、眠気防止効果が一層向上する。When a woven fabric, a non-woven fabric, or a breathable resin film is used as the support, the refreshing odor of l-menthol that evaporates through the support is effective in preventing drowsiness in addition to the transdermal absorption of l-menthol. Is further improved.
【００１３】本発明の眠気防止用テープの粘着剤層は、
スチレン−イソプレン−スチレンブロック共重合体、流
動パラフィン及び脂環族系炭化水素樹脂を含有する粘着
剤組成物からなる。The adhesive layer of the tape for drowsiness prevention of the present invention comprises
A pressure-sensitive adhesive composition containing a styrene-isoprene-styrene block copolymer, liquid paraffin and an alicyclic hydrocarbon resin.
【００１４】上記スチレン−イソプレン−スチレンブロ
ック共重合体のスチレン含有量は、少なくなるとｌ−メ
ントールを高濃度で含有させた時に粘着剤層の凝集力が
低下して、貼付時に凝集破壊が起こり、多くなると後述
の脂環族系炭化水素樹脂が溶解しにくくなり、粘着力が
低下するので、１２〜２０重量％に限定される。When the styrene content of the styrene-isoprene-styrene block copolymer is low, the cohesive force of the pressure-sensitive adhesive layer decreases when 1-menthol is contained in a high concentration, and cohesive failure occurs during application. If the amount is too large, the alicyclic hydrocarbon resin, which will be described later, becomes difficult to dissolve, and the adhesive strength is reduced.
【００１５】また、上記スチレン−イソプレン−スチレ
ンブロック共重合体の平均分子量は８０，０００〜１８
０，０００が好ましい。The average molecular weight of the styrene-isoprene-styrene block copolymer is 80,000-18.
10,000 is preferable.
【００１６】上記流動パラフィンは、粘着力を調整する
ための軟化剤として用いられ、沸点３００℃以上、比重
ｄ20 20：０．８６０〜０．８９０、粘度３７センチスト
ークス（３７．８℃）以上のものが好ましい。The liquid paraffin is used as a softening agent for adjusting the adhesive strength, has a boiling point of 300 ° C. or more, a specific gravity d 20 20 : 0.860 to 0.890, and a viscosity of 37 centistokes (37.8 ° C.) or more. Are preferred.
【００１７】上記流動パラフィンは、粘着剤層と皮膚と
の間に油性の膜を形成して、剥離時の粘着力を調節する
効果も有し、その量は、少なくなると粘着力が強くなっ
て皮膚から剥離する際に角質層を剥離する恐れがあり、
多くなると粘着力が低下するので、スチレン−イソプレ
ン−スチレンブロック共重合体１００重量部に対して８
０〜２００重量部に限定される。The liquid paraffin forms an oily film between the pressure-sensitive adhesive layer and the skin, and also has the effect of adjusting the adhesive force at the time of peeling. The smaller the amount, the stronger the adhesive force. There is a risk of peeling the stratum corneum when peeling from the skin,
If the amount is too large, the adhesive strength will be reduced, so that it is 8 per 100 parts by weight of the styrene-isoprene-styrene block copolymer.
It is limited to 0 to 200 parts by weight.
【００１８】上記脂環族系炭化水素樹脂は、粘着付与剤
として用いられ、平均分子量６００〜８００、軟化点８
０〜１２０℃のものが好ましい。上記脂環族系炭化水素
樹脂の量は、少なくなると十分な粘着付与効果がなく、
多くなると粘着力が強くなり角質層を剥離して皮膚刺激
を起こす恐れがあり、さらに粘着剤層の凝集力が低下し
て凝集破壊や糊残りが起こるので、スチレン−イソプレ
ン−スチレンブロック共重合体１００重量部に対して６
０〜１８０重量部に限定される。The above alicyclic hydrocarbon resin is used as a tackifier and has an average molecular weight of 600 to 800 and a softening point of 8
It is preferably 0 to 120 ° C. When the amount of the alicyclic hydrocarbon resin is small, there is no sufficient tackifying effect,
If the amount is too large, there is a risk of peeling the stratum corneum and causing skin irritation, and further, the cohesive force of the adhesive layer is reduced, causing cohesive failure and adhesive residue, so a styrene-isoprene-styrene block copolymer is produced. 6 for 100 parts by weight
It is limited to 0 to 180 parts by weight.
【００１９】上記粘着剤組成物には、さらにポリブテン
を添加してもよい。上記ポリブテンは、粘着付与剤及び
軟化剤として粘着力を調節する働きがあり、平均分子量
は９００〜３，０００のものが好ましい。上記ポリブテ
ンの量は、少なくなると粘着力が低下し、多くなると粘
着力が強くなりすぎるので、スチレン−イソプレン−ス
チレンブロック共重合体１００重量部に対して３〜２０
重量部が好ましい。上記粘着剤組成物には、必要に応じ
て他の粘着付与樹脂、軟化剤、液状ゴム、さらにジブチ
ルヒドロキシトルエン等の老化防止剤等が添加されても
よい。Polybutene may be further added to the pressure-sensitive adhesive composition. The polybutene functions as a tackifier and a softening agent to control the adhesive strength, and preferably has an average molecular weight of 900 to 3,000. When the amount of the polybutene is small, the adhesive strength is low, and when it is large, the adhesive strength is too strong. Therefore, the amount of the polybutene is 3 to 20 relative to 100 parts by weight of the styrene-isoprene-styrene block copolymer.
Parts by weight are preferred. If necessary, other tackifying resins, softening agents, liquid rubbers, and antioxidants such as dibutylhydroxytoluene may be added to the pressure-sensitive adhesive composition.
【００２０】上記粘着付与樹脂としては、例えば、ロジ
ン及び水添、不均化、重合あるいはエステル化されたロ
ジン誘導体等のロジン系樹脂；α−ピネン、β−ピネン
等のフェノール樹脂；テルペンフェノール樹脂；脂肪族
系、芳香族系、脂環族系あるいは共重合系等の石油樹
脂；アルキル−フェノール樹脂；キシレン樹脂等が挙げ
られる。Examples of the tackifying resin include rosin and rosin-based resins such as hydrogenated, disproportionated, polymerized or esterified rosin derivatives; phenolic resins such as α-pinene and β-pinene; terpene phenolic resins. An aliphatic, aromatic, alicyclic or copolymer petroleum resin; an alkyl-phenol resin; a xylene resin and the like.
【００２１】上記軟化剤としては、例えば、プロセスオ
イル、液状イソブチレン、液状ポリアクリレート、ひま
し油、綿実油、パーム油、椰子油、ミツロウ、カルナバ
ロウ、ラノリン等が挙げられ、上記液状ゴムとしてはポ
リイソブチレン、液状ポリイソプレン等が挙げられる。Examples of the softening agent include process oil, liquid isobutylene, liquid polyacrylate, castor oil, cottonseed oil, palm oil, coconut oil, beeswax, carnauba wax, lanolin, and the like, and the liquid rubber includes polyisobutylene and liquid. Examples thereof include polyisoprene.
【００２２】本発明の眠気防止用テープにおいて、上記
ｌ−メントールの量は、少なくなると十分な眠気防止効
果が得られず、多くなると発赤等の皮膚刺激を引き起こ
すので、上記粘着剤組成物１００重量部に対して９〜３
０重量部に限定される。In the drowsiness-preventing tape of the present invention, when the amount of l-menthol is small, a sufficient drowsiness-preventing effect cannot be obtained, and when it is too large, it causes skin irritation such as redness. 9 to 3 for division
Limited to 0 parts by weight.
【００２３】本発明の眠気防止用テープを調製する方法
としては、従来公知の粘着テープの調製方法が採用可能
であり、例えば、ホットメルト塗工法、溶剤塗工法、カ
レンダー塗工法、エマルジョン塗工法等が挙げられる。
上記溶剤塗工法としては、粘着剤組成物及びｌ−メント
ールからなる薬剤含有粘着剤組成物を適当な溶剤に溶解
し、これを支持体上に塗工、乾燥する方法が挙げられ
る。As a method for preparing the drowsiness prevention tape of the present invention, a conventionally known method for preparing a pressure-sensitive adhesive tape can be adopted, for example, hot melt coating method, solvent coating method, calendar coating method, emulsion coating method and the like. Is mentioned.
Examples of the solvent coating method include a method in which the pressure-sensitive adhesive composition and the drug-containing pressure-sensitive adhesive composition containing 1-menthol are dissolved in a suitable solvent, and the solution is coated on a support and dried.
【００２４】上記ホットメルト塗工法としては、粘着剤
組成物及びｌ−メントールからなる薬剤含有粘着剤組成
物を加熱溶融し、これを支持体上に展延、塗工する方法
が挙げられる。またホットメルト塗工法では、薬剤含有
粘着剤組成物を加熱溶融して剥離紙上に塗工した後、支
持体に密着、転写する方法も使用可能である。ホットメ
ルト塗工法で得られた眠気防止用テープは、ｌ−メント
ールの揮散が抑えられるので好ましい。Examples of the hot-melt coating method include a method of heating and melting a pressure-sensitive adhesive composition and a drug-containing pressure-sensitive adhesive composition comprising 1-menthol, and spreading and coating the composition on a support. In the hot melt coating method, a method in which the drug-containing pressure-sensitive adhesive composition is heated and melted to be applied on release paper, and then adhered and transferred to a support can be used. The drowsiness-preventing tape obtained by the hot melt coating method is preferable because the volatilization of 1-menthol can be suppressed.
【００２５】上記剥離紙は粘着剤層の保護を目的として
用いられ、例えば、ポリエチレンコート上質紙、ポリオ
レフィンコートグラシン紙、ポリエチレンテレフタレー
ト（以下ＰＥＴという）フィルム、ポリプロピレンフィ
ルム等の片面あるいは両面をシリコン処理したものが使
用可能である。The above-mentioned release paper is used for the purpose of protecting the pressure-sensitive adhesive layer. For example, polyethylene-coated high-quality paper, polyolefin-coated glassine paper, polyethylene terephthalate (hereinafter referred to as PET) film, polypropylene film or the like is treated on one or both sides with silicon. Things can be used.
【００２６】本発明の眠気防止用テープの形状は、シー
ト状、帯状、円形、楕円形、三日月形、菱形等自由に選
択できる。The shape of the drowsiness prevention tape of the present invention can be freely selected from a sheet shape, a band shape, a circle shape, an elliptical shape, a crescent shape, a rhombus shape and the like.
【００２７】上記眠気防止用テープを、額や眼の周囲、
こめかみ等に貼付することにより、粘着剤層中のｌ−メ
ントールが経皮吸収されるとともに、支持体や粘着剤層
の縁から徐々に揮散したｌ−メントールが、眼、鼻腔、
皮膚等を適度に刺激して眠気を防止する。The above drowsiness preventive tape is applied to the forehead and around the eyes,
By attaching to the temples or the like, l-menthol in the adhesive layer is percutaneously absorbed, and 1-menthol gradually volatilized from the edges of the support and the adhesive layer becomes
Prevents drowsiness by moderately stimulating the skin.
【００２８】[0028]
（実施例１〜５及び比較例１〜７）表１に示した量のス
チレン−イソプレン−スチレンブロック共重合体、流動
パラフィン、脂環族系炭化水素樹脂、ポリブテン及びジ
ブチルヒドロキシトルエン（老化防止剤）を加えて、１
１０〜１３０℃で５時間加熱溶融して粘着剤組成物を調
製した後、さらに表１に示した量のｌ−メントールを加
えて均一に混合し、薬剤含有粘着剤組成物を得た。上記
薬剤含有粘着剤組成物をシリコン離型処理したＰＥＴフ
ィルム（厚さ５０μｍ）上に、厚さ７０μｍとなるよう
に展延、塗工し、室温に冷却した後、厚さ１００μｍの
可塑化塩化ビニルフィルム上に転写し眠気防止用テープ
を得た。(Examples 1 to 5 and Comparative Examples 1 to 7) The amounts of styrene-isoprene-styrene block copolymer, liquid paraffin, alicyclic hydrocarbon resin, polybutene and dibutylhydroxytoluene (anti-aging agent) shown in Table 1 were used. ) And add 1
After heat-melting at 10 to 130 ° C. for 5 hours to prepare a pressure-sensitive adhesive composition, 1-menthol in an amount shown in Table 1 was further added and uniformly mixed to obtain a drug-containing pressure-sensitive adhesive composition. The above drug-containing pressure-sensitive adhesive composition was spread and coated on a PET film (thickness: 50 μm) that had been subjected to a silicone release treatment so as to have a thickness of 70 μm, cooled to room temperature, and then plasticized chloride having a thickness of 100 μm. The tape was transferred onto a vinyl film to obtain a drowsiness prevention tape.
【００２９】[0029]
【表１】 [Table 1]
【００３０】なお、表１で使用した各成分は次の通りで
ある。 スチレン−イソプレン−スチレンブロック共重合体（表
中、ＳＩＳで示した） Ａ：「カリフレクッスＴＲ１１０７」（シェル化学社
製） スチレン含有量１４重量％、平均分子量１２５，０００ Ｂ：「カリフレクッスＴＲ１１１１」（シェル化学社
製） スチレン含有量２１重量％、平均分子量１２５，０００ 流動パラフィン 「局方 流動パラフィン」（日興製薬社製） 脂環族系炭化水素樹脂（表中、炭化水素樹脂で示した） 「アルコンＰ９０」（荒川化学社製） 平均分子量６３０、軟化点９０℃ ポリブテン 「ポリブテン ＨＶ３００」（日本石油化学社製） 老化防止剤 「ジブチルヒドロキシトルエン」（オリエント化学社
製） ｌ−メントール 「食添 ｌ−メントール」（小城製薬社製）The components used in Table 1 are as follows. Styrene-isoprene-styrene block copolymer (indicated by SIS in the table) A: "Califlex TR1107" (manufactured by Shell Chemical Co.) Styrene content 14% by weight, average molecular weight 125,000 B: "Califlex TR1111" (shell Chemical company) Styrene content 21% by weight, average molecular weight 125,000 Liquid paraffin "Pharmaceutical liquid paraffin" (manufactured by Nikko Pharmaceutical Co., Ltd.) Alicyclic hydrocarbon resin (indicated by hydrocarbon resin in the table) "Alcon P90 "(manufactured by Arakawa Chemical Co., Ltd.) average molecular weight 630, softening point 90 ° C Polybutene" Polybutene HV300 "(manufactured by Nippon Petrochemical Co., Ltd.) Anti-aging agent" Dibutylhydroxytoluene "(manufactured by Orient Chemical Co.) 1-Menthol" Food additive l- Menthol "(Ogi Pharmaceutical Co., Ltd.)
【００３１】〔眠気防止用テープの評価〕上記実施例１
〜５及び比較例１〜７で得られた眠気防止用テープにつ
き下記の評価を行い、その結果を表２に示した。 （１）１８０度剥離強度 ＪＩＳ Ｚ０２３７に準拠して測定した。 （２）官能試験 半径１ｃｍの円形に打ち抜いた眠気防止用テープを成人
５名の評価者の額またはこめかみに貼付し、貼付後０．
５時間、１時間、１．５時間、２時間、２．５時間及び
３時間に、次の評価基準に従って眠気防止効果を判定し
た。 〈評価基準〉 ＋：メントール臭及び皮膚に対する適度な刺激感があ
り、眠気を防止する。 ±：メントール臭はほとんどないが、皮膚に対する適度
な刺激感がある。 −：メントール臭及び皮膚に対する刺激感がない。 また官能試験終了後、眠気防止用テープを剥離する際の
糸引き及び皮膚への糊残りの有無、角質剥離の有無を次
の評価基準に従って判定した。 〈評価基準〉 （糸引き及び皮膚への糊残りの有無） ○：糸引き及び皮膚への糊残りなし ×：糸引き又は皮膚への糊残りあり （角質剥離の有無） ○：角質剥離ほとんどなし ×：角質剥離多い[Evaluation of Drowsiness Prevention Tape] Example 1 above
~ 5 and the tape for preventing drowsiness obtained in Comparative Examples 1 to 7 were evaluated as follows, and the results are shown in Table 2. (1) 180 degree peeling strength Measured in accordance with JIS Z0237. (2) Sensory test A drowsiness prevention tape punched out in a circular shape with a radius of 1 cm was attached to the forehead or temple of 5 adult evaluators, and after the attachment, 0.
At 5 hours, 1 hour, 1.5 hours, 2 hours, 2.5 hours and 3 hours, the drowsiness preventive effect was evaluated according to the following evaluation criteria. <Evaluation Criteria> +: There is a menthol odor and an appropriate feeling of irritation to the skin, which prevents drowsiness. ±: Almost no menthol odor, but moderately irritating to the skin. -: No menthol odor or irritation to the skin. After the sensory test, the presence or absence of stringing and adhesive residue on the skin when peeling the drowsiness prevention tape and the presence or absence of keratin peeling were determined according to the following evaluation criteria. <Evaluation Criteria> (Existence of stringing and adhesive residue on skin) ○: No stringing and adhesive residue on skin ×: Presence of stringing or adhesive residue on skin (presence or absence of exfoliation) ○: Almost no exfoliation of exfoliation X: Exfoliation is large
【００３２】[0032]
【表２】 [Table 2]
【００３３】[0033]
【発明の効果】本発明の眠気防止用テープは上述の通り
であり、粘着性を損ねることなく眠気を防止するのに十
分な量のｌ−メントールを含有させることができるの
で、長時間にわたって眠気防止効果を持続できる。The tape for preventing drowsiness of the present invention is as described above, and since it can contain l-menthol in an amount sufficient to prevent drowsiness without impairing the adhesiveness, it can be used for a long time. The prevention effect can be sustained.
Claims (1)
された眠気防止用テープで、上記粘着剤層は、スチレン
含有量が１２〜２０重量％であるスチレン−イソプレン
−スチレンブロック共重合体１００重量部、流動パラフ
ィン８０〜２００重量部及び脂環族系炭化水素樹脂６０
〜１８０重量部からなる粘着剤組成物１００重量部と、
薬剤としてｌ−メントール９〜３０重量部よりなること
を特徴とする眠気防止用テープ。1. A drowsiness preventive tape having a pressure-sensitive adhesive layer containing a drug formed on a support, wherein the pressure-sensitive adhesive layer comprises a styrene-isoprene-styrene block copolymer having a styrene content of 12 to 20% by weight. 100 parts by weight of polymer, 80 to 200 parts by weight of liquid paraffin, and alicyclic hydrocarbon resin 60
100 parts by weight of an adhesive composition consisting of ˜180 parts by weight,
A tape for preventing drowsiness, which comprises 9 to 30 parts by weight of l-menthol as a drug.