JPH0733510B2 - Green phosphor for three-wavelength emission type fluorescent lamp and three-wavelength emission type fluorescent lamp using the same - Google Patents

Green phosphor for three-wavelength emission type fluorescent lamp and three-wavelength emission type fluorescent lamp using the same

Info

Publication number
JPH0733510B2
JPH0733510B2 JP2193497A JP19349790A JPH0733510B2 JP H0733510 B2 JPH0733510 B2 JP H0733510B2 JP 2193497 A JP2193497 A JP 2193497A JP 19349790 A JP19349790 A JP 19349790A JP H0733510 B2 JPH0733510 B2 JP H0733510B2
Authority
JP
Japan
Prior art keywords
fluorescent lamp
phosphor
emission type
type fluorescent
emitting phosphor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP2193497A
Other languages
Japanese (ja)
Other versions
JPH0480283A (en
Inventor
賢二 寺島
智治 戸村
剛 岩崎
昌彦 山川
博文 竹村
右子 林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toshiba Corp
Original Assignee
Toshiba Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toshiba Corp filed Critical Toshiba Corp
Priority to JP2193497A priority Critical patent/JPH0733510B2/en
Publication of JPH0480283A publication Critical patent/JPH0480283A/en
Publication of JPH0733510B2 publication Critical patent/JPH0733510B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】 [発明の目的] (産業上の利用分野) この発明は、緑色発光蛍光体に係り、特に三波長域発光
形蛍光ランプ用に好適な緑色発光蛍光体と、これを用い
た三波長域発光形蛍光ランプに関する。
The present invention relates to a green light emitting phosphor, and more particularly to a green light emitting phosphor suitable for a three-wavelength band emission type fluorescent lamp, and The present invention relates to a three-wavelength band emission type fluorescent lamp used.

(従来の技術) 一般照明用の蛍光ランプとして、高効率性と高演色性と
を同時に満足する三波長域発光形蛍光ランプが急速に普
及しつつあり、家庭用照明光源では主流となっている。
(Prior Art) As a fluorescent lamp for general lighting, a three-wavelength light emitting type fluorescent lamp that simultaneously satisfies high efficiency and high color rendering properties is rapidly becoming widespread, and is becoming the mainstream of a lighting source for home use. .

この種の蛍光ランプには比較的狭帯域の発光スペクトル
分布を有する青色、緑色、赤色発光蛍光体が用いられて
いる。
In this type of fluorescent lamp, blue, green and red light emitting phosphors having a relatively narrow band emission spectrum distribution are used.

従来、セリウムとテルビウムとで付活された緑色発光希
土類アルミン酸・珪酸・燐酸塩蛍光体としては、[(R
e,Tb,Ce)2O3・Al2O3・SiO2・P2O5](特公昭60−9543
号公報参照)が知られている。
Conventionally, as a green light emitting rare earth aluminate / silicic acid / phosphate phosphor activated by cerium and terbium, [(R
e, Tb, Ce) 2 O 3 · Al 2 O 3 · SiO 2 · P 2 O 5 ] (Japanese Patent Publication No. 60-9543
(See Japanese Patent Publication).

また、希土類珪酸・硼酸・燐酸塩蛍光体としては、
[(Re,Tb,Ce)2O3・SiO2・P2O5・B2O3](特公昭62−4
4792号公報参照)があり、このほか希土類正燐酸塩蛍光
体としては、[(Re,Tb,Ce)PO4](特公昭59−43508号
公報参照)が知られている。
Further, as the rare earth silicic acid / boric acid / phosphate phosphor,
[(Re, Tb, Ce) 2 O 3 · SiO 2 · P 2 O 5 · B 2 O 3 ] (Japanese Patent Publication No. 62-4
In addition, [(Re, Tb, Ce) PO 4 ] (see Japanese Patent Publication No. 59-43508) is known as a rare earth orthophosphate phosphor.

そして、水溶性の蛍光体懸濁液(スラリー)を調製する
にあたって、水溶性バインダとしてヒドロキシアルキル
セルロースを用いること(特開昭59−129286号公報参
照)が知られている。
It is known that hydroxyalkyl cellulose is used as a water-soluble binder when preparing a water-soluble phosphor suspension (slurry) (see JP-A-59-129286).

このような三波長域発光形蛍光ランプでは、その全光束
(発光出力)に対して緑色発光蛍光体の占める割合が非
常に高く、したがって、緑色発光蛍光体の特性が三波長
域発光形蛍光ランプの性能を大きく左右するのである。
In such a three-wavelength emission type fluorescent lamp, the ratio of the green light emission fluorescent material to the total luminous flux (emission output) is very high, and therefore the characteristics of the green emission emission fluorescent material are three wavelength range emission type fluorescent lamps. Performance is greatly affected.

ところで、三波長域発光形蛍光ランプの蛍光膜は、青
色、緑色、赤色の各色を混合した蛍光体懸濁液(蛍光体
スラリー)によって形成される。したがって各色の蛍光
体の物性がそれぞれスラリーの性質に影響を与えるので
あるが、たとえば各色の蛍光体の比重を比較すると、青
色発光蛍光体が通常3.8〜4.1前後、赤色発色蛍光体が5.
1前後であるのに対して、緑色発光蛍光体は5.3前後であ
り、最も大きい。
By the way, the phosphor film of the three-wavelength band emission type fluorescent lamp is formed by a phosphor suspension (phosphor slurry) in which each color of blue, green and red is mixed. Therefore, the physical properties of the phosphors of each color affect the properties of the slurry, for example, comparing the specific gravities of the phosphors of each color, the blue-emitting phosphor is usually around 3.8 to 4.1, the red-emitting phosphor is 5.
It is around 1, while that of the green-emitting phosphor is around 5.3, which is the largest.

それ故、蛍光ランプに用いられる3種類以上の混合蛍光
体の蛍光体スラリーでは、緑色発光蛍光体が他の蛍光体
よりも比較的早く沈降、落下しやすく、3色の分布が不
均一となって蛍光膜の品質低下を招くことが問題となっ
ている。
Therefore, in the phosphor slurry of three or more kinds of mixed phosphors used in the fluorescent lamp, the green light emitting phosphor is likely to settle and fall relatively faster than other phosphors, and the three color distributions become nonuniform. As a result, the quality of the fluorescent film is deteriorated.

(発明が解決しようとする課題) 上述したように、三波長域発光形蛍光ランプにおいて
は、3色混合スラリーの使用に際して、従来の緑色発光
蛍光体である希土類アルミン酸・珪酸・燐酸塩蛍光体
や、希土類珪酸・硼酸・燐酸塩蛍光体、あるいは希土類
正燐酸塩蛍光体の分散性が、他の色よりも悪いという問
題があった。
(Problems to be Solved by the Invention) As described above, in the three-wavelength band emission type fluorescent lamp, the rare earth aluminate / silicic acid / phosphate phosphor which is a conventional green light emitting phosphor is used when the three-color mixed slurry is used. Another problem is that the dispersibility of the rare earth silicic acid / boric acid / phosphate phosphor or the rare earth orthophosphate phosphor is worse than other colors.

このため緑色成分はスラリー中で凝集しやすく、他の蛍
光体よりも早く沈降して、蛍光面の3色のバランスが崩
れ、蛍光ランプの蛍光膜の品質向上を妨げている。
For this reason, the green component is likely to aggregate in the slurry and settles earlier than the other phosphors, thereby disturbing the balance of the three colors on the phosphor screen and hindering the quality improvement of the phosphor film of the fluorescent lamp.

しかも、緑色成分はランプの白色に寄与している割合が
最も大きいため、緑色成分の不安定さはそのまま蛍光ラ
ンプの品質に影響してくる。
Moreover, since the green component has the largest contribution to the white color of the lamp, the instability of the green component directly affects the quality of the fluorescent lamp.

このように、緑色成分の分散、安定性が蛍光膜(蛍光
面)の品位に大きく影響を及ぼすことから、緑色発光蛍
光体の分散性を高め、スラリー中での沈降速度を他の色
の蛍光体と同程度にコントロールすることが課題となっ
ている。
In this way, the dispersion and stability of the green component greatly affects the quality of the fluorescent film (fluorescent surface), so that the dispersibility of the green-emitting phosphor is increased, and the sedimentation speed in the slurry is reduced by the fluorescence of other colors. Controlling to the same level as the body is a challenge.

本発明はこのような課題を解決するためになされたもの
で、スラリー中での分散性が良く、均一な蛍光面を形成
することのできる三波長域発光形蛍光ランプ用緑色発光
蛍光体と、この蛍光体を用いることによって蛍光膜の品
質向上を図った三波長域発光形蛍光ランプを提供するこ
とを目的とする。
The present invention has been made in order to solve such a problem, good dispersibility in the slurry, a green light-emitting phosphor for a three-wavelength band emission type fluorescent lamp capable of forming a uniform phosphor screen, An object of the present invention is to provide a three-wavelength band emission type fluorescent lamp in which the quality of the fluorescent film is improved by using this phosphor.

[発明の構成] (課題を解決するための手段) この発明の三波長域発光形蛍光ランプ用緑色発光蛍光体
は、青色発光蛍光体および赤色発光蛍光体と共に用いら
れる三波長域発光形蛍光ランプ用緑色発光蛍光体におい
て、 一般式 (R1 1-a-bTbaCeb)2O3・eAl2O3・fSiO2・gP2O5 ……
(I) (式中、R1はY、La、Gdの中から選ばれた少なくとも一
種の元素を示し、a、bおよびe、f、gは下記の式を
満足する数である。
[Structure of the Invention] (Means for Solving the Problems) The green light-emitting phosphor for a three-wavelength band emission type fluorescent lamp of the present invention is a three-wavelength band emission type fluorescent lamp used together with a blue light emission phosphor and a red light emission phosphor Formula (R 1 1- a - bTbaCeb) 2 O 3 · eAl 2 O 3 · fSiO 2 · gP 2 O 5 ......
(I) (In the formula, R 1 represents at least one element selected from Y, La, and Gd, and a, b and e, f, and g are numbers satisfying the following formula.

a>0、b>0、0.1≦a+b≦0.7、e≧0、f≧0、
g>0、0.8≦e+f+g≦1.30。) で表されるテルビウムで付活された緑色発光蛍光体、ま
たは、 一般式 (R1 1-a-bTbaCeb)2O3・xSiO2・yP2O5・zB2O3 ……(I
I) (式中、R1はY、La、Gdの中から選ばれた少なくとも一
種の元素を示し、a、bおよびx、y、zは下記の式を
満足する数である。
a> 0, b> 0, 0.1 ≦ a + b ≦ 0.7, e ≧ 0, f ≧ 0,
g> 0, 0.8 ≦ e + f + g ≦ 1.30. ) A terbium-activated green light-emitting phosphor represented by the formula) or a general formula (R 1 1- a - bTbaCeb) 2 O 3 · xSiO 2 · yP 2 O 5 · zB 2 O 3 …… (I
I) (In the formula, R 1 represents at least one element selected from Y, La, and Gd, and a, b, and x, y, and z are numbers satisfying the following formula.

a>0、b>0、0.1≦a+b≦0.7、x≧0、y>0、
5.0×10-6≦z≦6.0×10-3、0.8≦x+y+z≦1.3
0。) で表されるテルビウムで付活された緑色発光蛍光体の粒
子100重量%に対して、水に可溶なヒドロキシアルキル
セルロースを、0.005重量%以上0.5重量%以下の範囲
で、前記蛍光体の表面に被覆したことを特徴としてい
る。
a> 0, b> 0, 0.1 ≦ a + b ≦ 0.7, x ≧ 0, y> 0,
5.0 x 10 -6 ≤ z ≤ 6.0 x 10 -3 , 0.8 ≤ x + y + z ≤ 1.3
0. ) In 100% by weight of the particles of the green light-emitting phosphor activated with terbium represented by the formula, a water-soluble hydroxyalkyl cellulose is added in an amount of 0.005% by weight or more and 0.5% by weight or less. It is characterized by being coated on the surface.

また、本発明の三波長域発光形蛍光ランプは上記三波長
域発光形蛍光ランプ用緑色発光蛍光体を含有する蛍光膜
を備えたことを特徴としている。
Further, the three-wavelength band emission type fluorescent lamp of the present invention is characterized by including a fluorescent film containing the above-mentioned green light-emitting phosphor for the three-wavelength band emission type fluorescent lamp.

本発明において、蛍光体の表面を被覆するヒドロキシア
ルキルセルロースは水に可溶なものであり、さらに水と
アルコール類との両方に可溶であることが好ましい。
In the present invention, the hydroxyalkyl cellulose that coats the surface of the phosphor is soluble in water, and preferably soluble in both water and alcohols.

これは蛍光膜と形成工程において、装置などの違いによ
って有機溶媒を使用することもあるため、水とアルコー
ル類との両方に可溶であれば、種々の蛍光膜形成システ
ムへの対応が可能となるからである。特に、ヒドロキシ
プロピルセルロースは扱いが容易で被覆層として適して
いる。
This is because the organic solvent may be used in the fluorescent film and the forming process depending on the difference in the equipment, etc. Therefore, if it is soluble in both water and alcohols, it can be applied to various fluorescent film forming systems. Because it will be. In particular, hydroxypropyl cellulose is easy to handle and suitable as a coating layer.

本発明において、上記(I)式または(II)式で表され
る緑色発光蛍光体の表面に被覆するヒドロキシアルキル
セルロースの濃度は、蛍光体粒子100重量%に対して0.0
05重量%〜0.5重量%とする。
In the present invention, the concentration of hydroxyalkyl cellulose coated on the surface of the green light-emitting phosphor represented by the above formula (I) or (II) is 0.0 with respect to 100% by weight of the phosphor particles.
05% to 0.5% by weight.

被覆量が0.005重量%未満であるとヒドロキシアルキル
セルロースの効果が充分得られず、蛍光体膜(蛍光面)
の品位は改善されない。
When the coating amount is less than 0.005% by weight, the effect of hydroxyalkyl cellulose cannot be sufficiently obtained, and the phosphor film (fluorescent surface)
The quality of is not improved.

逆に0.5重量%を超えると緑色発光蛍光体としての発光
出力が著しく低下する。
On the other hand, if it exceeds 0.5% by weight, the emission output of the green light emitting phosphor is significantly reduced.

この発明の緑色発光蛍光体の母体としては、先に述べた
ように、希土類アルミン酸・珪酸・燐酸塩、希土類珪酸
・燐酸塩・希土類アルミン酸・燐酸塩、または希土類正
燐酸塩や希土類珪酸・硼酸・燐酸塩・このほか希土類硼
酸・燐酸塩などが用いられ、母体の種類によってこの発
明の作用、効果が左右されるものではない。
As the matrix of the green light emitting phosphor of the present invention, as described above, rare earth aluminate / silicic acid / phosphate, rare earth silicic acid / phosphate / rare earth aluminate / phosphate, or rare earth orthophosphate or rare earth silicic acid / Boric acid / phosphate, other rare earth boric acid / phosphate, etc. are used, and the action and effect of the present invention are not affected by the type of the base material.

(作 用) この発明の三波長域発光形蛍光ランプ用緑色発光蛍光体
は、その表面をヒドロキシアルキルセルロースで被覆し
ているため、スラリー中での分散性が向上し、蛍光体粒
子同士の凝集を防ぐとともに、沈降の速さを抑制するこ
とができる。
(Operation) Since the surface of the green light-emitting phosphor for three-wavelength emission type fluorescent lamp of the present invention is coated with hydroxyalkyl cellulose, the dispersibility in the slurry is improved and the phosphor particles are aggregated. And the sedimentation speed can be suppressed.

このため、緑色成分だけが先に沈降して色バランスを崩
すこと(色むら)がなく、均一な蛍光膜が形成される。
Therefore, only the green component does not settle first and the color balance is not disturbed (color unevenness), and a uniform fluorescent film is formed.

これによって、発光出力が高く、かつ蛍光膜(蛍光面)
の品位の良好な三波長域発光形蛍光ランプを得ることが
できる。
Due to this, the light emission output is high and the fluorescent film (fluorescent surface)
It is possible to obtain a three-wavelength band emission type fluorescent lamp having good quality.

(実施例) 次に、この発明の実施例について説明する。(Example) Next, the Example of this invention is described.

実施例1 純水600ccにヒドロキシプロピルセルロース(日本曹達
(株)社製、HPC、M.S.3.1)を0.12g入れ、充分時間を
かけて溶液を攪拌し、完全にHPCを溶解する。
Example 1 0.12 g of hydroxypropyl cellulose (HPC, MS3.1, manufactured by Nippon Soda Co., Ltd.) was added to 600 cc of pure water, and the solution was stirred for a sufficient time to completely dissolve HPC.

次に、テルビウムで付活された希土類アルミン酸・珪酸
・燐酸塩緑色発光蛍光体[(La0.60Ce0.25Tb0.152O3
・0.003Al2O3・0.0005SiO2・1.003P2O5]を200g添加
し、充分に攪拌する。
Next, terbium activated rare earth aluminate / silicic acid / phosphate green light emitting phosphor [(La 0.60 Ce 0.25 Tb 0.15 ) 2 O 3
・ 0.003Al 2 O 3・ 0.0005SiO 2・ 1.003P 2 O 5 ], and add sufficient stirring.

その後、ヒドロキシプロピルセルロースと緑色発光蛍光
体とを混合した懸濁液を吸引濾過法により濾過し、濾過
ケーキを100℃前後の温度で乾燥する。
Thereafter, the suspension obtained by mixing hydroxypropyl cellulose and the green-emitting phosphor is filtered by a suction filtration method, and the filter cake is dried at a temperature of around 100 ° C.

こうして得た蛍光体粒子は、その表面が0.05重量%のHP
Cの被膜により均一に覆われたものである。
The phosphor particles thus obtained have a surface of 0.05 wt% HP
It is uniformly covered with the C coating.

続いて、この緑色発光蛍光体100gを、ニトロセルロース
溶液(ニトロセルロース(NC)4重量%、酢酸ブチル96
重量%)100cc、酢酸ブチル10cc、ピロ燐酸カルシウム
粉末1gを予め調合して充分攪拌した溶液中に入れ、蛍光
体の懸濁液(蛍光体スラリー)を調製する。
Subsequently, 100 g of this green-emitting phosphor was mixed with a nitrocellulose solution (nitrocellulose (NC) 4% by weight, butyl acetate 96%).
% By weight) 100 cc, butyl acetate 10 cc, and calcium pyrophosphate powder 1 g are prepared in advance and put in a well-stirred solution to prepare a phosphor suspension (phosphor slurry).

この蛍光体スラリーを用い、FL40SS/37用のガラスバル
ブ内面にスラリーを塗布して蛍光膜を形成する。
Using this phosphor slurry, the slurry is applied to the inner surface of a glass bulb for FL40SS / 37 to form a phosphor film.

乾燥後、蛍光膜を肉眼で観察し、その膜品位を評価し
た。膜品位の評価にあたっては、凝集部分(ブツ)のな
いものおよび表面が平滑であるものを10点とし、凝集部
分の程度および表面の凹凸の程度に応じて減点し、数値
化した。
After drying, the fluorescent film was visually observed and the film quality was evaluated. In the evaluation of the film quality, 10 points were those with no agglomerates (spots) and those with a smooth surface, and points were deducted according to the degree of agglomerations and the degree of surface irregularities to quantify.

さらには、蛍光膜を形成したガラスバルブを用い、常法
に従って、第1図に示すような蛍光ランプFL40SS・G/37
を作製し、初期発光出力を測定、評価した。
Furthermore, using a glass bulb having a fluorescent film formed thereon, the fluorescent lamp FL40SS / G / 37 as shown in FIG.
Was prepared, and the initial light emission output was measured and evaluated.

第1図において、蛍光ランプは、ガラスバルブ1の内面
に蛍光膜2が被着され、さらに所定圧の放電用ガスが封
入されている。
In FIG. 1, a fluorescent lamp has a glass bulb 1 coated with a fluorescent film 2, and a discharge gas having a predetermined pressure is filled therein.

そして、ガラスバルブ1の両端部に電極3が取付けら
れ、この電極3に所定電圧を印加することにより励起源
によって蛍光膜2が発光するようになっている。
Then, electrodes 3 are attached to both ends of the glass bulb 1, and by applying a predetermined voltage to the electrodes 3, the fluorescent film 2 emits light by an excitation source.

一方、比較品として、同じ緑色発光蛍光体(テルビウム
で付活された希土類アルミン酸・珪酸・燐酸塩緑色発光
蛍光体)をヒドロキシプロピルセルロースの被覆なしで
使用し、同様の蛍光ランプを作製し、実施例と同一条件
で特性を測定した。
On the other hand, as a comparative product, the same green light emitting phosphor (rare earth aluminate / silicic acid / phosphate green light emitting phosphor activated with terbium) was used without coating with hydroxypropyl cellulose to prepare a similar fluorescent lamp, The characteristics were measured under the same conditions as in the examples.

その結果、従来の蛍光体の膜品位は7.0であるのに対し
て、この実施例の蛍光体は9.5であった。
As a result, the film quality of the conventional phosphor was 7.0, while that of the phosphor of this example was 9.5.

また、初期発光出力は、従来の蛍光体の初期発光出力を
100%とした時の相対値で示しており、この実施励の蛍
光ランプは99.5%と、大きな差は認められなかった。
In addition, the initial light emission output is the initial light emission output of the conventional phosphor.
It is shown as a relative value when it is set to 100%, and the fluorescent lamp for this implementation was 99.5%, which was not a large difference.

これらの結果を第1表にまとめて示す。These results are summarized in Table 1.

実施励2 純水600ccにヒドロキシプロピル・メチルセルロース
(信越化学工業(株)社製、メトローズ60SH)を0.48g
入れ、充分時間をかけて溶液を攪拌し、完全にヒドロキ
シプロピル・メチルセルロースを溶解する。
Execution encouragement 2 0.48 g of hydroxypropyl methylcellulose (Metronose 60SH manufactured by Shin-Etsu Chemical Co., Ltd.) in 600 cc of pure water
Add the solution and stir the solution for a sufficient time to completely dissolve the hydroxypropyl methylcellulose.

次に、テルビウムで付活された希土類珪酸・硼酸・燐酸
塩緑色発光蛍光体[(La0.40Ce0.45Tb0.152O3・0.001
SiO2・0.988P2O5・0.0005B2O3]を200g添加し、充分に
攪拌する。
Next, terbium activated rare earth silicic acid / boric acid / phosphate green light emitting phosphor [(La 0.40 Ce 0.45 Tb 0.15 ) 2 O 3 0.001
SiO 2 · 0.988P 2 O 5 · 0.0005B 2 O 3 ], 200 g, and sufficiently stirred.

その後、これらを混合した懸濁液を吸引濾過法により濾
過し、濾過ケーキを100℃前後の温度で乾燥する。
Thereafter, the suspension obtained by mixing these is filtered by a suction filtration method, and the filter cake is dried at a temperature of around 100 ° C.

このようにして得られた蛍光体粒子は、その表面が0.20
重量%のヒドロキシプロピル・メチルセルロースの被膜
により均一に覆われている。
The phosphor particles thus obtained have a surface of 0.20
It is evenly covered by a coating of hydroxypropyl methylcellulose in weight percent.

この緑色発光蛍光体を用いて実施例1と同様に蛍光ラン
プを作製し、同一条件で特性を測定、評価した。
Using this green-emitting phosphor, a fluorescent lamp was produced in the same manner as in Example 1, and the characteristics were measured and evaluated under the same conditions.

これらの結果を第1表に示す。The results are shown in Table 1.

実施例3〜12 第1表に示すように、緑色発光蛍光体とこの表面を被覆
するヒドロキシアルキルセルローの被覆濃度を変化さ
せ、実施例1と同様に緑色発光蛍光体を調製した。
Examples 3 to 12 As shown in Table 1, green light emitting phosphors were prepared in the same manner as in Example 1 except that the coating concentrations of the green light emitting phosphor and the hydroxyalkyl cellulos coating the surface were changed.

また、得られた緑色発光蛍光体を用いて蛍光ランプを作
製し、特性評価を行った。
In addition, a fluorescent lamp was manufactured using the obtained green light emitting phosphor, and the characteristics were evaluated.

これらの結果をまとめて第1表に示す。The results are summarized in Table 1.

これらの結果から明らかなように、この実施例による緑
色発光蛍光体を用いた蛍光ランプは初期発光出力を従来
のものとほぼ同等に維持しつつ、かつ蛍光膜の膜品位が
著しく向上しており、大幅な品質向上を図ることができ
た。
As is clear from these results, the fluorescent lamp using the green-emitting phosphor according to this example maintains the initial emission output almost equal to that of the conventional one, and the film quality of the fluorescent film is significantly improved. , Was able to achieve a significant quality improvement.

[発明の効果] 以上説明したように、この発明によれば、高輝度、高分
散性の三波長域発光形蛍光ランプ用緑色発光蛍光体が得
られ、3色のバランスの良い均一な蛍光膜を形成するこ
とができる。したがって、三波長域発光形蛍光ランプ用
の緑色発光蛍光体として極めて有用であり、三波長域発
光形蛍光ランプの品質向上に大きく貢献するものであ
る。
[Effects of the Invention] As described above, according to the present invention, a green light-emitting phosphor for a three-wavelength band fluorescent lamp having high brightness and high dispersibility can be obtained, and a uniform fluorescent film with a good balance of three colors. Can be formed. Therefore, it is extremely useful as a green light emitting phosphor for a three-wavelength band emission type fluorescent lamp, and contributes greatly to the improvement of the quality of the three-wavelength band emission type fluorescent lamp.

【図面の簡単な説明】[Brief description of drawings]

第1図はこの発明の一実施例の蛍光ランプを一部破断し
て示す図である。 1……ガラスバルブ、2……蛍光膜、3……電極。
FIG. 1 is a partially cutaway view showing a fluorescent lamp according to an embodiment of the present invention. 1 ... glass bulb, 2 ... fluorescent film, 3 ... electrode.

フロントページの続き (72)発明者 岩崎 剛 神奈川県川崎市幸区堀川町72番地 東芝電 子デバイスエンジニアリング株式会社内 (72)発明者 山川 昌彦 神奈川県川崎市幸区堀川町72 株式会社東 芝堀川町工場内 (72)発明者 竹村 博文 神奈川県川崎市幸区堀川町72 株式会社東 芝堀川町工場内 (72)発明者 林 右子 神奈川県川崎市幸区堀川町72 株式会社東 芝堀川町工場内 (56)参考文献 特開 平2−173087(JP,A) 特開 平1−234490(JP,A)Front page continued (72) Inventor Go Iwasaki 72 Horikawa-cho, Sachi-ku, Kawasaki-shi, Kanagawa Toshiba Electronic Device Engineering Co., Ltd. (72) Inventor Masahiko Yamakawa 72 Horikawa-cho, Kawasaki-shi, Kanagawa Prefecture (72) Inventor Hirofumi Takemura 72 Horikawa-cho, Sachi-ku, Kawasaki-shi, Kanagawa Higashishiba Horikawa-cho Co., Ltd. In the factory (56) References JP-A 2-173087 (JP, A) JP-A 1-234490 (JP, A)

Claims (4)

【特許請求の範囲】[Claims] 【請求項1】青色発光蛍光体および赤色発光蛍光体と共
に用いられる三波長域発光形蛍光ランプ用緑色発光蛍光
体において、 一般式 (R1 1-a-bTbaCeb)2O3・eAl2O3・fSiO2・gP2O5 ……
(I) (式中、R1はY、La、Gdの中から選ばれた少なくとも一
種の元素を示し、a、bおよびe、f、gは下記の式を
満足する数である。 a>0、b>0、0.1≦a+b≦0.7、e≧0、f≧0、
g>0、0.8≦e+f+g≦1.30) で表されるテルビウムで付活された緑色発光蛍光体、ま
たは、 一般式 (R1 1-a-bTbaCeb)2O3・xSiO2・yP2O5・zB2O3 ……(I
I) (式中、R1はY、La、Gdの中から選ばれた少なくとも一
種の元素を示し、a、bおよびx、y、zは下記の式を
満足する数である。 a>0、b>0、0.1≦a+b≦0.7、x≧0、y>0、
5.0×10-6≦z≦6.0×10-3、0.8≦x+y+z≦1.30) で表されるテルビウムで付活された緑色発光蛍光体 の粒子100重量%に対して、 水に可溶なヒドロキシアルキルセルロースを、0.005重
量%以上0.5重量%以下の範囲で、前記蛍光体の表面に
被覆したことを特徴とする三波長域発光形蛍光ランプ用
緑色発光蛍光体。
1. A blue-emitting phosphor and red-emitting fluorescent green-emitting phosphor for three-band fluorescent lamp to be used with body, the general formula (R 1 1- a - bTbaCeb) 2 O 3 · eAl 2 O 3 · fSiO 2 · gP 2 O 5 ......
(I) (In the formula, R 1 represents at least one element selected from Y, La, and Gd, and a, b and e, f, and g are numbers satisfying the following formula. A> 0, b> 0, 0.1 ≦ a + b ≦ 0.7, e ≧ 0, f ≧ 0,
g> 0, 0.8 ≦ e + f + g ≦ 1.30), the terbium-activated green light-emitting phosphor represented by the general formula (R 1 1- a - bTbaCeb) 2 O 3 · xSiO 2 · yP 2 O 5 · zB 2 O 3 …… (I
I) (In the formula, R 1 represents at least one element selected from Y, La, and Gd, and a, b and x, y, and z are numbers satisfying the following formula. A> 0 , B> 0, 0.1 ≦ a + b ≦ 0.7, x ≧ 0, y> 0,
5.0 × 10 −6 ≦ z ≦ 6.0 × 10 −3 , 0.8 ≦ x + y + z ≦ 1.30) Terbium-activated green light-emitting phosphor 100% by weight of particles, water-soluble hydroxyalkyl A green light-emitting phosphor for a three-wavelength band emission type fluorescent lamp, characterized in that the surface of the phosphor is coated with cellulose in a range of 0.005% by weight or more and 0.5% by weight or less.
【請求項2】前記ヒドロキシアルキルセルロースは水と
アルコール類との両方に可溶である請求項1記載の三波
長域発光形蛍光ランプ用緑色発光蛍光体。
2. The green light-emitting phosphor for a three-wavelength band emission type fluorescent lamp according to claim 1, wherein the hydroxyalkyl cellulose is soluble in both water and alcohols.
【請求項3】前記ヒドロキシアルキルセルロースはヒド
ロキシプロピルセルロースである請求項1記載の三波長
域発光形蛍光ランプ用緑色発光蛍光体。
3. The green light-emitting phosphor for a three-wavelength band emission type fluorescent lamp according to claim 1, wherein the hydroxyalkyl cellulose is hydroxypropyl cellulose.
【請求項4】請求項1ないし3記載の三波長域発光形蛍
光ランプ用緑色発光蛍光体を含有する蛍光膜を備えたこ
とを特徴とする三波長域発光形蛍光ランプ。
4. A three-wavelength band emission type fluorescent lamp comprising a phosphor film containing the green light-emitting phosphor for the three-wavelength band emission type fluorescent lamp according to claim 1.
JP2193497A 1990-07-19 1990-07-19 Green phosphor for three-wavelength emission type fluorescent lamp and three-wavelength emission type fluorescent lamp using the same Expired - Lifetime JPH0733510B2 (en)