JPH07318704A - Window reflection preventive optical filter for vehicle - Google Patents
Window reflection preventive optical filter for vehicleInfo
- Publication number
- JPH07318704A JPH07318704A JP6112771A JP11277194A JPH07318704A JP H07318704 A JPH07318704 A JP H07318704A JP 6112771 A JP6112771 A JP 6112771A JP 11277194 A JP11277194 A JP 11277194A JP H07318704 A JPH07318704 A JP H07318704A
- Authority
- JP
- Japan
- Prior art keywords
- optical filter
- saw blade
- angles
- window
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、車両用窓映り防止光学
フィルターに関し、特に自動車などの車両室内に存在す
る表示機器及び表示パネル用の車両用窓映り防止光学フ
ィルターに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a vehicle window anti-glare optical filter, and more particularly to a vehicle window anti-glare optical filter for a display device and a display panel existing in a vehicle compartment such as an automobile.
【０００２】[0002]
【従来技術】従来、自動車などの車両の室内には、スピ
ードメーター、時計及び各種警告灯などの多くの表示機
器が使用されている。近年では、これらの表示機器に加
えて、室内空調、オーディオの集中制御、テレビ及びナ
ビゲーションシステムの一部として自動車の現在位置や
目的地などの地図情報表示のために、ＣＲＴや液晶ディ
スプレイなどの表示パネルが導入されるようになってき
ている。2. Description of the Related Art Conventionally, many display devices such as a speedometer, a clock and various warning lights are used in the interior of a vehicle such as an automobile. In recent years, in addition to these display devices, displays such as CRTs and liquid crystal displays for indoor air conditioning, centralized control of audio, and display of map information such as the current position of automobiles and destinations as part of television and navigation systems. Panels are being introduced.
【０００３】上記表示機器は夜間に点灯状態となり、ま
た表示パネルはその機能上の特徴から昼夜を問わず点灯
状態となる場合が多い。一方、点灯状態となった表示機
器や表示パネルから発せられた光は、フロントウインド
などの窓ガラスの表面で反射した後にドライバーの視点
に直接入り、いわゆる窓映りとなって認識され、運転の
際の大きな障害となるという欠点があった。In many cases, the display device is turned on at night and the display panel is turned on regardless of day or night due to its functional characteristics. On the other hand, the light emitted from the display device or display panel that has been turned on enters the driver's viewpoint directly after being reflected on the surface of the window glass such as the front window, and is recognized as what is called a window reflection. It had the drawback that it would be a major obstacle.
【０００４】このような欠点を解決するために、通常は
窓ガラスの内側に反射防止膜を設けて、ガラス表面の反
射率を落としたり、遮光フィルムを挟み込んだ透明樹脂
製カバーを表示機器や表示パネル前面に設けてウインド
ウ方向へ発せられる光の角度を制御することにより対応
している。In order to solve such drawbacks, an antireflection film is usually provided on the inside of a window glass to reduce the reflectance of the glass surface, or a transparent resin cover having a light-shielding film sandwiched therein is used as a display device or display. This is done by controlling the angle of the light provided in the front of the panel and emitted in the window direction.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、表面に
反射防止膜を設けて反射防止を行う方法では、膜界面で
の反射光と透過光との光の打ち消し合いにより反射光強
度を低減する原理を利用しているため、可視領域の特定
波長の反射率は０％にすることができるが、それ以外の
波長領域では必ずしも低反射率とはならず全体の波長領
域で反射率を十分に低くすることができないという欠点
があった。However, in the method of providing antireflection by providing an antireflection film on the surface, the principle of reducing the intensity of the reflected light by canceling the reflected light and the transmitted light at the film interface is proposed. Since it is used, the reflectance at a specific wavelength in the visible region can be set to 0%, but the reflectance is not necessarily low in other wavelength regions, and the reflectance is sufficiently low in the entire wavelength region. It had the drawback of not being able to.
【０００６】また、膜構成は最低でも３層必要となるの
で、高コストになってしまうという欠点があった。更
に、ガラスの裏面からの反射光も防止するためには、裏
面、即ち車室外面にも反射防止膜を設けなければならな
いが、耐久性の面から実用は困難であるという欠点があ
った。Further, since the film structure requires at least three layers, there is a drawback that the cost becomes high. Further, in order to prevent the reflected light from the back surface of the glass, it is necessary to provide an antireflection film on the back surface, that is, the outer surface of the passenger compartment, but there is a drawback that practical use is difficult from the viewpoint of durability.
【０００７】また、遮光フィルムを挟み込んだ透明樹脂
製カバーを表示機器や表示パネル前面に設ける方法で
は、遮光フィルムを黒く着色した樹脂と透明樹脂とを交
互に積層させ、最後に積層方向と垂直にある厚さで切断
するという工法で製造しているので、極めて高いコスト
であり自動車用途には適さず、更に遮光フィルムの透過
率が６０〜７０％と低いこと、ルーバーの間隔が２００
〜３００μｍと比較的大きいので、ルーバーの縞の状態
が肉眼でも認識することができること、液晶ディスプレ
ーなどに適用した場合には液晶の各セルとの干渉により
モアレ縞が現れることなどにより時計の文字自体が極め
て見づらくなるという欠点があった。In the method of providing a transparent resin cover with a light-shielding film sandwiched on the front of a display device or display panel, the light-shielding film is alternately laminated with black-colored resin and transparent resin, and finally in a direction perpendicular to the lamination direction. Since it is manufactured by a method of cutting it at a certain thickness, it is extremely expensive and not suitable for automobile applications. Furthermore, the transmittance of the light-shielding film is low at 60 to 70%, and the interval between louvers is 200.
Since it is relatively large at ~ 300 μm, the state of the louver stripes can be recognized with the naked eye, and when applied to a liquid crystal display etc., moire fringes appear due to interference with each cell of the liquid crystal, etc. Has the drawback that it becomes very hard to see.
【０００８】従って本発明の目的は、窓映り防止性能が
極めて優れ、かつ低コストで製造可能な車両用窓映り防
止光学フィルターを提供することにある。SUMMARY OF THE INVENTION Therefore, an object of the present invention is to provide a vehicle window antiglare optical filter which is extremely excellent in window antiglare performance and can be manufactured at low cost.
【０００９】[0009]
【課題を解決するための手段】本発明の上記の目的は、
透明基板の表面上に断面が鋸刃形状の微細な三角柱突起
が同一方向に連続して配置された車両用窓映り防止光学
フィルターにおいて、隣接する三角柱突起の間隔が１０
〜１００μｍの範囲にあり、かつ鋸刃の頂角を除く２つ
の角度がそれぞれ２０〜４０°又は９０〜１２０°の範
囲にあることを特徴とする車両用窓映り防止光学フィル
ターにより達成された。以下、本発明を更に詳細に説明
する。The above objects of the present invention are as follows.
In a vehicle window anti-glare optical filter in which fine triangular prismatic protrusions having a saw-tooth-shaped cross section are continuously arranged in the same direction on the surface of a transparent substrate, the distance between adjacent triangular prismatic protrusions is 10
It was achieved by a vehicle window anti-glare optical filter characterized by being in the range of .about.100 .mu.m and the two angles excluding the apex angle of the saw blade being in the range of 20 to 40.degree. Or 90 to 120.degree., Respectively. Hereinafter, the present invention will be described in more detail.
【００１０】図１はセンターコンソール部分の断面拡大
図及びドライバーが表示機器のひとつである時計から発
せられる光により窓映り像を視認することを説明する図
である。センターコンソール中央部分に設置されている
時計１から出た光はフロントウインドウ２へ向かい、ウ
インドウの表面で反射した後にドライバーの視点３にや
ってきて、時計の窓映り像としてドライバーに視認され
ることになる。FIG. 1 is an enlarged cross-sectional view of a center console part and a view for explaining that a driver visually recognizes a window image by light emitted from a timepiece which is one of display devices. The light emitted from the clock 1 installed in the central part of the center console travels to the front window 2, is reflected by the surface of the window, then comes to the driver's viewpoint 3, and is seen by the driver as a window image of the clock. Become.
【００１１】昼間は太陽光などの外光強度が極めて強力
なので、これらの光に対する窓映り光の強度比、即ちコ
ントラスト比が相対的に低くなるため、ドライバーの視
認性が大きく低下することはない。一方、夜間において
は外光強度が低下すると共に表示機器を点灯状態とする
ことにより窓映り光強度が増加し、結果としてコントラ
スト比が高くなるので外部視認上大きな障害となる。な
お、外光強度の比較的高い都心部又はその周辺より、夜
間外光強度が極端に低下する郊外や地方で特に問題とな
る。Since the intensity of outside light such as sunlight is extremely strong in the daytime, the intensity ratio of the window reflection light to these lights, that is, the contrast ratio is relatively low, so that the visibility of the driver is not significantly reduced. . On the other hand, at night, the intensity of outside light is reduced and the intensity of light reflected on the window is increased by turning on the display device, resulting in a high contrast ratio, which is a great obstacle to external visual recognition. It is a particular problem in the suburbs and rural areas where the nighttime external light intensity is extremely lower than that in the central area where the external light intensity is relatively high or its surroundings.
【００１２】図２はフロントウインドウの室内表面側に
反射防止膜４を設けることにより、窓映り防止を施して
いる方法を説明する図である。フロントウインドウの室
内側表面に反射した窓映り光の方向はそのままである
が、反射防止膜により光強度を低くすることによりコン
トラスト比を下げてドライバーから視認しにくくなるよ
うにしている。FIG. 2 is a view for explaining a method for preventing window reflection by providing an antireflection film 4 on the indoor surface side of the front window. Although the direction of the window reflection light reflected on the indoor side surface of the front window remains the same, the light intensity is reduced by the antireflection film to lower the contrast ratio and make it difficult for the driver to see.
【００１３】図３は時計の前面に遮光フィルターを挟み
込んだ透明樹脂製カバー５を設けてウインドウ方向へ発
される光の角度を制御することにより窓映り防止を施し
ている方法を説明する図である。時計から出た光が遮光
フィルターを挟み込んだ透明樹脂製カバーを通過する
と、透過光は透明樹脂製カバーの法線に対して一定の角
度範囲内に制限されるので、この透過光がフロントウイ
ンドウの表面で反射する位置はより上方となり、結果と
して反射光は視点上方へ逃げることになり、窓映り像と
してはドライバーに視認されないことになる。透過光が
出現する角度範囲は遮光フィルターの厚さとルーバーの
間隔により決定される。このような遮光フィルターとし
ては信越ポリマー株式会社製のものや住友スリーエム株
式会社製のものなどが知られている。FIG. 3 is a diagram for explaining a method of preventing window reflection by providing a transparent resin cover 5 with a light-shielding filter sandwiched in front of the watch to control the angle of light emitted toward the window. is there. When the light emitted from the watch passes through the transparent resin cover with the light blocking filter sandwiched, the transmitted light is limited within a certain angle range with respect to the normal line of the transparent resin cover. The position of reflection on the surface is higher, and as a result, the reflected light escapes above the viewpoint, and is not visible to the driver as a window image. The angle range in which the transmitted light appears is determined by the thickness of the shading filter and the distance between the louvers. As such a light-shielding filter, those manufactured by Shin-Etsu Polymer Co., Ltd., Sumitomo 3M Co., Ltd., and the like are known.
【００１４】図４は本発明の車両用窓映り防止光学フィ
ルター６の断面部分拡大図である。図４において、(d)
(e)(f) は表面に鋸刃形状三角柱を連続に配置した透明
フィルム(a)(b)(c) を透明基板７上に接着剤層８を挟ん
で積層したものであり、(a′)(b ′)(c ′)(d ′)(e
′)(f ′) はそれぞれ(a)(b)(c)(d)(e)(f)の表面に必
要に応じてハードコート層９を設けたものである。FIG. 4 is an enlarged cross-sectional partial view of the vehicle window reflection preventing optical filter 6 of the present invention. In Figure 4, (d)
(e) and (f) are transparent films (a), (b) and (c) each having a saw-toothed triangular prism continuously arranged on the surface, and are laminated on a transparent substrate 7 with an adhesive layer 8 interposed therebetween. ′) (B ′) (c ′) (d ′) (e
′) (F ′) is provided with a hard coat layer 9 on the surface of (a) (b) (c) (d) (e) (f) as required.
【００１５】図５は本発明の車両用窓映り防止光学フィ
ルター６をセンターコンソール中央部分の時計前面に透
明樹脂製カバーとして設置した場合の効果を説明する図
であり、図６は本発明の車両用窓映り防止光学フィルタ
ーを通過する光の屈折状況を説明するための断面部分拡
大図である。FIG. 5 is a diagram for explaining the effect of the case where the vehicle window reflection preventing optical filter 6 of the present invention is installed as a transparent resin cover on the front face of the watch in the center portion of the center console. FIG. 6 shows the vehicle of the present invention. It is a cross-sectional partial enlarged view for explaining the refraction situation of the light which passes through the window reflection preventing optical filter.
【００１６】時計から出た光が本発明の車両用窓映り防
止光学フィルターへ入射するとその表面形状に従って下
方へ屈折するので、透過光はある角度より上には現れな
くなる。この屈折角は鋸刃傾斜面の傾斜角度と材料の屈
折率の増加に伴い大きくなる。図６(a) は鋸刃傾斜面の
傾斜角度が小さい場合、図６(b) は大きい場合の光の屈
折状況を示す図である。図６(a) に示すように鋸刃傾斜
面の傾斜角度が小さく屈折角が小さければ、図５(a) に
示すように透過光がフロントウインドウの表面で反射す
る位置はより上方となって反射光は視点上方へ逃げ、逆
に図６(b) に示すように鋸刃傾斜面の傾斜角度が大きく
屈折角が大きい場合には、図５(b) に示すようにフロン
トウインドウの表面には反射しないので、いずれの場合
も窓映りには問題がないことが判る。When the light emitted from the timepiece is incident on the vehicle window anti-glare optical filter of the present invention, it is refracted downward according to its surface shape, so that the transmitted light does not appear above a certain angle. This refraction angle increases as the inclination angle of the saw blade inclined surface and the refractive index of the material increase. FIG. 6A is a diagram showing a refraction state of light when the inclination angle of the saw blade inclined surface is small, and FIG. As shown in Fig. 6 (a), if the angle of inclination of the saw blade inclined surface is small and the refraction angle is small, the position where the transmitted light is reflected on the surface of the windshield is higher as shown in Fig. 5 (a). The reflected light escapes above the viewpoint, and conversely, as shown in Fig. 6 (b), when the angle of inclination of the saw blade inclined surface is large and the refraction angle is large, as shown in Fig. 5 (b), it is reflected on the surface of the windshield. Since it does not reflect, it can be seen that there is no problem in window reflection in any case.
【００１７】鋸刃形状三角柱を連続に配置した側はドラ
イバー側にあっても、又は時計側にあっても同等な光学
特性が得られるので、必要に応じてどちらかを選択して
も良い。用いる材料自体は透明なので、透過率が低下し
時計の文字盤が視認しにくくなるといった問題点も生じ
ない。また、図６中で示す破線は透過光が多重に反射す
る状態を示すものであり、これが存在すると透過像のボ
ケなどが発生する。Since the same optical characteristics can be obtained whether the sawtooth-shaped triangular prisms are continuously arranged on the driver side or on the timepiece side, either one may be selected as necessary. Since the material itself used is transparent, there is no problem that the transmittance is lowered and the timepiece dial becomes difficult to see. Further, the broken line shown in FIG. 6 shows a state in which the transmitted light is reflected in multiple layers, and when this is present, blurring of the transmitted image occurs.
【００１８】図７は多重に反射する透過光を防止するた
めに形状工夫を施したことを説明する図である。鋸刃の
頂角を除く２つの角のうち角度範囲が９０〜１２０°の
範囲にある角に接している面を粗面化することにより、
この部分を通過する光を散乱させて光強度を低下させる
ことが可能となるのである。FIG. 7 is a view for explaining that a shape is devised in order to prevent multiple-reflected transmitted light. By roughening the surface that is in contact with the angle within the range of 90 to 120 ° of the two angles excluding the apex angle of the saw blade,
It is possible to scatter the light passing through this portion and reduce the light intensity.
【００１９】断面が鋸刃形状の微細な三角柱突起の間隔
が１０μｍより小さいと、透過像の品質低下を招き、逆
に１００μｍより大きいと鋸刃の頂角部分が欠けやす
く、かつ透き間にゴミが混入すると容易に除去すること
ができない。鋸刃の頂角を除く２つの角のうち、一方の
角は２０°未満だと透過光がほとんど屈折せず効果が現
れず、逆に４０°より大きいと屈折しすぎて表示像の視
認性が低下する。他方の角は９０°未満だと透過像が２
重となってしまい、逆に１２０°より大きいと鋸刃の頂
角部分の機械的強度が低下する。If the distance between the fine triangular protrusions having a saw blade-shaped cross section is smaller than 10 μm, the quality of the transmitted image is deteriorated. On the other hand, if it is larger than 100 μm, the apex angle portion of the saw blade is liable to be chipped and dust is left in the gap. If mixed, it cannot be easily removed. Of the two angles excluding the apex angle of the saw blade, if one of the angles is less than 20 °, the transmitted light is hardly refracted and the effect does not appear. Is reduced. If the other angle is less than 90 °, the transmission image is 2
If it is larger than 120 °, the mechanical strength of the apex angle portion of the saw blade is reduced.
【００２０】鋸刃の頂角を除く２つの角のうち、角度範
囲が９０〜１２０°となる角側に接している面の粗面化
の程度は、１０点平均粗さＲｚが１０μｍ未満になると
透過像が多重となってしまい、逆に１０μｍより大きい
と光の散乱が激しく起こってしまい表面全体が白色化し
てしまう。Of the two angles other than the apex angle of the saw blade, the degree of roughening of the surface in contact with the angle side having an angle range of 90 to 120 ° is such that the 10-point average roughness Rz is less than 10 μm. If so, the transmission images will be multiplexed, and conversely, if it is larger than 10 μm, the light will be scattered greatly, and the entire surface will be whitened.
【００２１】本発明において用いられる透明基板として
は、ポリカーボネート(PC)、ポリメチルメタクリレート
(PMMA)、ポリスチレンなどの透明樹脂やガラスなどから
任意に選択することができる。また、フィルムを用いる
場合のフィルムとしては、ポリエチレンテレフタレート
(PET) 、ポリイミド(PI)を始めとして、ポリプロピレン
(PP)、ポリスチレン(PS)、塩化ビニル、ナイロン、トリ
アセテート、セロハンなどが好適に用いられるが、機械
的性質、熱的性質及び電気特性のすべてにバランスが取
れていることから、特にＰＥＴが好ましい。The transparent substrate used in the present invention includes polycarbonate (PC) and polymethylmethacrylate.
(PMMA), polystyrene, or another transparent resin, glass, or the like can be arbitrarily selected. When a film is used, the film is polyethylene terephthalate.
(PET), polyimide (PI), polypropylene
(PP), polystyrene (PS), vinyl chloride, nylon, triacetate, cellophane, etc. are preferably used, but PET is particularly preferable because it has a good balance of mechanical properties, thermal properties, and electrical properties. .
【００２２】透明基板の表面に直接鋸刃形状三角柱の突
起は、機械加工、ワイヤーカット放電加工などにより予
め表面に所望の鋸刃形状三角柱連続突起を形成した金型
を用い、射出成形や加圧成形法などにより金型表面の形
状を直接転写することにより連続的に設けることができ
る。The projection of the sawtooth-shaped triangular prism is directly formed on the surface of the transparent substrate by injection molding or pressing using a mold in which a desired sawtooth-shaped triangular prism continuous projection is previously formed on the surface by machining, wire cut electric discharge machining or the like. It can be continuously provided by directly transferring the shape of the mold surface by a molding method or the like.
【００２３】鋸刃の頂角を除く２つの角のうち角度範囲
が９０〜１２０°となる角側に接している面を粗面化す
る方法としては、金型表面へ鋸刃形状三角柱連続突起を
機械加工した後に鋸刃垂直面も機械加工、サンドブラス
トなどにより粗面化することにより成形と同時に転写し
てしまう方法と、表面へ鋸刃形状三角柱連続突起を機械
加工した金型を用いて成形、転写した鋸刃垂直面をサン
ドブラスト処理などにより粗面化する方法とがある。As a method for roughening the surface of the two angles excluding the apex angle of the saw blade, which is in contact with the angle side having an angle range of 90 to 120 °, a saw blade-shaped triangular prism continuous projection is formed on the die surface. After machining, the vertical surface of the saw blade is also machined and roughened by sandblasting, etc. to transfer at the same time as molding, and using a die machined with sawtooth-shaped triangular prism continuous projections on the surface , There is a method of roughening the transferred saw blade vertical surface by sandblasting or the like.
【００２４】また、フィルム表面に鋸刃形状三角柱の突
起は、機械加工、放電加工及びフォトリソグラフィによ
る異方性エッチングなどにより予め表面に鋸刃形状三角
柱連続突起を形成したロールを用いて、ロール間にフィ
ルムを連続的に通過、プレスして転写することにより連
続的に設けることができる。The sawtooth-shaped triangular prism protrusions on the surface of the film are formed by using a roll in which sawtooth-shaped triangular prism continuous protrusions are previously formed on the surface by machining, electric discharge machining, anisotropic etching by photolithography, or the like. The film can be continuously provided by continuously passing the film through, pressing and transferring.
【００２５】この際、フィルムを直接プレスして鋸刃形
状を転写したり、又は予め紫外線や電子線などの活性光
線や熱により硬化可能な硬化性組成物を塗布したフィル
ムにプレスして鋸刃形状を転写した後に、硬化性樹脂組
成物に活性光線や熱をさらして硬化したりする方法があ
る。At this time, the film is directly pressed to transfer the shape of the saw blade, or the film is preliminarily coated with a curable composition which is curable by actinic rays such as ultraviolet rays and electron beams or heat. After transferring the shape, there is a method of exposing the curable resin composition to actinic rays or heat to cure the composition.
【００２６】紫外線硬化樹脂としては、光重合性プレポ
リマー、光重合性モノマー及び光開始剤を主成分として
成る「ソーラプレン」（三井東圧化学株式会社の商標
名）や「アデカオプト２」（旭電化株式会社の商標名）
などがある。これらの硬化性樹脂組成物の膜厚は５００
μｍ以下であることが好ましいが、転写精度を考慮する
と１００μｍ程度であることが好ましい。Examples of the UV curable resin include "Solarprene" (trade name of Mitsui Toatsu Chemicals, Inc.) and "Adekaopt 2" (Asahi Denka Co., Ltd.), which are mainly composed of a photopolymerizable prepolymer, a photopolymerizable monomer and a photoinitiator. (Trademark name of corporation)
and so on. The film thickness of these curable resin compositions is 500.
The thickness is preferably less than or equal to μm, but is preferably about 100 μm in consideration of transfer accuracy.
【００２７】鋸刃の頂角を除く２つの角のうち角度範囲
が９０〜１２０°となる角側に接している面の粗面化
は、透明基板表面に直接鋸刃形状三角柱の突起を連続的
に設ける方法と同様にして行うことができる。Roughening of the surface of the two angles excluding the apex angle of the saw blade, which is in contact with the angle side of which the angle range is 90 to 120 °, is achieved by continuously forming the sawtooth-shaped triangular prism projections directly on the transparent substrate surface. It can be performed in the same manner as the method for providing the same.
【００２８】表面に鋸刃形状三角柱の連続突起を設けた
フィルムと透明基板とを接着するに際しては、透明基板
の表面に接着剤を塗布してフィルムを貼り合わせること
が一般的である。この際、用いられる接着剤としては、
一般的な熱可塑性接着剤、エラストマー接着剤及び熱硬
化性接着剤などを単独で使用しても良く、また必要に応
じて２種以上を混合して使用しても良い。When a film having a saw-toothed triangular prism continuous projection on its surface is bonded to a transparent substrate, it is common to apply an adhesive to the surface of the transparent substrate and bond the films together. At this time, as the adhesive used,
Common thermoplastic adhesives, elastomer adhesives, thermosetting adhesives, etc. may be used alone, or if necessary, two or more kinds may be mixed and used.
【００２９】例えば、主剤である液状エポキシ樹脂と硬
化剤である芳香族アミンを主成分として成る熱硬化性の
エポキシ系接着剤（市販品としては「セメダインＣＳ−
２３４０−５」：セメダイン株式会社の商品番号）など
を用いれば良い。接着剤の膜厚は１μｍ以下であること
が好ましい。For example, a thermosetting epoxy adhesive mainly composed of a liquid epoxy resin as a main component and an aromatic amine as a curing agent (commercially available as "Cemedine CS-
2340-5 ”: a product number of Cemedine Co., Ltd.) or the like may be used. The film thickness of the adhesive is preferably 1 μm or less.
【００３０】一般に自動車用表示機器や表示パネルに使
用されるフィルターは、運転者及び同乗者の手に直接触
れる場所にあるため、表面はある程度の機械的強度を有
することが必要とされる。表面の強度が要求される場合
には、鋸刃形状の表面にハードコート層を設けても差し
支えない。このハードコート層は鋸刃傾斜面のみ設けて
も良く、又は全面に設けても差し支えない。ハードコー
ト層としては熱硬化性樹脂などがあり、例えばシリコー
ン系コーティング液を塗布、硬化したものなどが好適に
用いられる。Generally, a filter used for a display device or a display panel for an automobile is in a place where it directly comes into contact with the hands of a driver and a passenger, and therefore the surface is required to have some mechanical strength. If surface strength is required, a hard coat layer may be provided on the saw-toothed surface. This hard coat layer may be provided only on the inclined surface of the saw blade, or may be provided on the entire surface. The hard coat layer may be a thermosetting resin or the like, and for example, one obtained by applying and curing a silicone-based coating liquid is preferably used.
【００３１】シリコーン系コーティング液としては、従
来よりプラスチックの表面硬化層として使用されている
シロキサン結合を有するものが好適に使用することがで
きる。このようなシリコーン系コーティング層は、一般
式ＲｎＳｉ（ＯＲ1 ）4-n （式中、ｎは１〜３の整数、
Ｒは炭素数１〜６の炭化水素基、Ｒ1 は炭素数１〜４の
アルキル基を示す。）で示される化合物と、四アルコキ
シ珪素の共部分加水分解物、又はこれらの分解物との混
合物を主成分として成るコーティング剤（特開昭５７−
１７７０２８号公報、「スミユニ」：住友化学工業株式
会社の商標名）、又はメチルシルセスキシロキサン及び
コロイダル状シリカの混合物を主成分として成るコーテ
ィング剤（「トスガード」：東芝シリコーン株式会社の
商標名）などを塗布することにより形成される。塗布の
方法としては、流し塗り法、スプレー法、ディッピング
法及びスピンコート法などを使用することができる。As the silicone-based coating liquid, a liquid having a siloxane bond, which has been conventionally used as a surface-hardening layer for plastics, can be preferably used. Such a silicone-based coating layer has a general formula RnSi (OR 1 ) 4-n (wherein n is an integer of 1 to 3,
R represents a hydrocarbon group having 1 to 6 carbon atoms, and R 1 represents an alkyl group having 1 to 4 carbon atoms. ) And a co-partial hydrolyzate of tetraalkoxysilicon or a mixture of these decomposed products as a main component (JP-A-57-
No. 177028, "Sumiuni": trade name of Sumitomo Chemical Co., Ltd.), or a coating agent containing a mixture of methylsilsesquisiloxane and colloidal silica as a main component ("Tosguard": trade name of Toshiba Silicone Co., Ltd.), etc. It is formed by applying. As a coating method, a flow coating method, a spray method, a dipping method, a spin coating method, or the like can be used.
【００３２】次に、本発明の車両用窓映り防止光学フィ
ルターの製造方法について説明する。鋸刃形状三角柱の
突起を連続的に透明基板の表面に直接形成する場合に
は、まず射出成形や加圧成形法で用いる金型表面を機械
加工やワイヤーカット放電加工により精密加工し、所望
の鋸刃形状三角柱連続突起を形成する。Next, a method of manufacturing the vehicle window reflection preventing optical filter of the present invention will be described. When continuously forming protrusions of a saw-toothed triangular prism directly on the surface of a transparent substrate, first the mold surface used in injection molding or pressure molding is precisely processed by machining or wire cut electrical discharge machining, and then the desired Saw blade-shaped triangular prism continuous protrusions are formed.
【００３３】射出成形法では、透明基板の原料となる樹
脂又はガラスを加熱して溶融させたものをこの金型中へ
圧力を加えて導入した後に溶融温度以下で所定時間維持
して成形し、表面に鋸刃形状三角柱連続突起を転写す
る。加圧成形法では透明基板を予め軟化温度以上に加熱
した後に金型にセットし、次いで圧力を加えながら所定
時間維持し、表面に鋸刃形状三角柱連続突起を転写す
る。In the injection molding method, a resin or glass which is a raw material of a transparent substrate is heated and melted, and then a material is introduced into the mold by applying pressure, and then molded while maintaining the temperature below the melting temperature for a predetermined time. Saw blade-shaped triangular prism continuous protrusions are transferred to the surface. In the pressure molding method, a transparent substrate is heated to a softening temperature or higher in advance and then set in a mold, and then pressure is maintained for a predetermined time to transfer sawtooth-shaped triangular prism continuous protrusions to the surface.
【００３４】鋸刃の頂角を除く２つの角のうち角度範囲
が９０〜１２０°となる角側に接している面を粗面化す
る方法としてサンドブラスト処理を用いる場合には、平
均粒径約２０μｍのガラスビース、圧力２Ｋｇｆ／の圧
縮空気で約６０秒間処理を行う。表面に形成した鋸刃形
状三角柱連続突起の機械的強度が十分でない場合にハー
ドコート層を設ける場合には、射出成形や加圧成形によ
り表面に鋸刃形状三角柱連続突起を転写した後にシリコ
ーン系コーティング液を表面に塗布する。膜厚は５〜１
０μｍの範囲であることが好ましい。塗布した後、２０
分間放置して風乾させ、続いて１２０℃で６０分間保持
してハードコート層を形成する。When sandblasting is used as a method of roughening the surface of the two angles excluding the apex angle of the saw blade, which is in contact with the angle side having an angle range of 90 to 120 °, the average particle size is about Treatment is carried out for about 60 seconds with 20 μm glass beads and compressed air with a pressure of 2 Kgf /. When the hard coat layer is provided when the mechanical strength of the saw blade-shaped triangular prism continuous protrusions is not sufficient, silicone coating is applied after the saw blade-shaped triangular prism continuous protrusions are transferred to the surface by injection molding or pressure molding. Apply the liquid to the surface. Film thickness is 5 to 1
It is preferably in the range of 0 μm. 20 after applying
It is left to stand for air drying, and then kept at 120 ° C. for 60 minutes to form a hard coat layer.
【００３５】フィルム表面に鋸刃形状三角柱の突起を連
続的に形成し、透明基板と接着するに際しては、まずフ
ィルムをイソプロピルアルコールによる脱脂処理をした
後、純水リンス及び窒素ブロー乾燥して洗浄する。直接
フィルム表面に加工する場合にはフィルム又はロールを
所定温度まで加熱しておく。また、硬化性樹脂組成物を
用いる場合には、まず硬化性樹脂組成物を所定の厚さに
塗布した後に紫外線、電子線又は熱を僅かに加えて、硬
化性樹脂組成物を半硬化させた状態にする。When continuously forming a saw-toothed triangular prism on the film surface and adhering it to a transparent substrate, the film is first degreased with isopropyl alcohol, and then rinsed with pure water and dried with nitrogen blow to clean. . When directly processing the film surface, the film or roll is heated to a predetermined temperature. When the curable resin composition is used, first, the curable resin composition is applied to a predetermined thickness, and then ultraviolet rays, electron beams or heat is slightly added to semi-cure the curable resin composition. Put in a state.
【００３６】紫外線硬化樹脂の場合には紫外線露光装置
にて紫外線を１０秒間、電子線硬化性樹脂の場合には電
子線照射装置にて電子線を約２０秒間、熱硬化性樹脂の
場合には８０℃で１分間処理する。次に、鋸刃形状三角
柱の連続突起が表面に加工されたロールの間にこのフィ
ルムを通過させてプレスし、鋸刃形状三角柱連続突起を
フィルム上の半硬化させた硬化性樹脂組成物へ転写す
る。そして再び所定の方法により硬化性樹脂組成物を完
全に硬化させて、鋸刃形状三角柱連続突起を固定化す
る。紫外線及び電子線硬化性樹脂の場合には照射時間３
分間以上、熱硬化性樹脂の場合には１００℃で１０分間
以上処理すれば完全に硬化する。In the case of an ultraviolet curable resin, ultraviolet rays are irradiated for 10 seconds by an ultraviolet exposure device, in the case of an electron beam curable resin, an electron beam is irradiated for about 20 seconds in an electron beam irradiation device, and in the case of a thermosetting resin. Treat at 80 ° C for 1 minute. Next, this film is passed through a roll between rolls having saw blade-shaped triangular prism continuous protrusions processed on the surface, and the saw blade-shaped triangular prism continuous protrusions are transferred to a semi-cured curable resin composition on the film. To do. Then, the curable resin composition is completely cured again by a predetermined method to fix the sawtooth-shaped triangular prism continuous protrusions. Irradiation time 3 for UV and electron beam curable resins
If the thermosetting resin is treated for at least 10 minutes and at 100 ° C. for 10 minutes or more, it is completely cured.
【００３７】鋸刃の頂角を除く２つの角のうち角度範囲
が９０〜１２０°の範囲となる角側に接している面を粗
面化する方法としてサンドブラスト処理を用いる場合に
は、平均粒径約２０μｍのガラスビース、圧力２Ｋｇｆ
／ｃｍ2 の圧縮空気で約６０秒間処理を行う。次に、透
明基板の表面へ接着剤を所定厚さに塗布した後に、接着
剤が乾燥しないうちにフィルムを端から皺にならないよ
うに順に貼り付ける。When sandblasting is used as a method for roughening the surface in contact with the corner side of the two angles other than the apex angle of the saw blade, the angle range being in the range of 90 to 120 °, the average grain is used. Glass bead with a diameter of about 20 μm, pressure 2 kgf
The treatment is performed with compressed air of / cm 2 for about 60 seconds. Next, after the adhesive is applied to the surface of the transparent substrate to a predetermined thickness, the films are attached in order so that the film does not become wrinkled from the edges before the adhesive dries.
【００３８】表面に形成した鋸刃形状三角柱連続突起の
機械的強度が十分でない場合にハードコート層を設ける
場合には、フィルムと透明基体とを接着したフィルター
の鋸刃形状表面へシリコン系コーティング液を塗布す
る。膜厚は５〜１０μｍの範囲にあることが好ましい。
塗布した後、２０分間放置して風乾させ、続いて１２０
℃で６０分間保持してハードコート層を形成する。When the hard coat layer is provided when the mechanical strength of the saw-tooth-shaped triangular prism continuous protrusions formed on the surface is not sufficient, the surface of the saw-tooth-shaped surface of the filter to which the film and the transparent substrate are adhered is coated with a silicon-based coating liquid. Apply. The film thickness is preferably in the range of 5 to 10 μm.
After application, leave it for 20 minutes to air dry, then 120
Hold at 60 ° C. for 60 minutes to form a hard coat layer.
【００３９】以上のようにして成形した、表面に鋸刃形
状三角柱の連続突起が形成された車両用窓映り防止光学
フィルターの、窓映り防止性能を以下のようにして評価
した。実際に走行可能な自動車の時計の透明樹脂製カバ
ーを本発明の車両用窓映り防止光学フィルターと交換し
た後に昼夜を問わず様々な環境下で走行し、時計からの
光がフロントウインドの室内側表面で反射してドライバ
ーの視点に入って窓映りを起こすことにより運転に支障
が生じるか、また時計の文字盤が見にくいかについて調
べた。The window reflection preventing performance of the vehicle window reflection preventing optical filter formed as described above and having saw blade-shaped triangular prism continuous projections formed on the surface was evaluated as follows. After exchanging the transparent resin cover of the vehicle clock that can be actually driven with the vehicle window reflection preventing optical filter of the present invention, the vehicle travels in various environments day and night, and the light from the clock is emitted from the inside of the front window. I investigated whether driving would be hindered by reflection on the surface and entering the driver's point of view to cause window reflections, and whether the clock face was difficult to see.
【００４０】どの条件下でも窓映りが認識されず運転に
支障が無く、また時計の文字盤にも問題無く視認するこ
とができれば、本発明の車両用窓映り防止光学フィルタ
ーの窓映り防止効果はあると判断された。If the window reflection is not recognized under any condition, the driving is not hindered, and the clock dial can be visually recognized without any problem, the window reflection prevention optical filter of the present invention has the effect of preventing the window reflection. It was decided that there was.
【００４１】[0041]
【実施例】以下、本発明を実施例によって更に詳述する
が、本発明はこれによって限定されるものではない。EXAMPLES The present invention will be described in more detail below with reference to examples, but the present invention is not limited thereto.
【００４２】実施例１ 頂角を除く２つ角の角度がそれぞれ３０°、１００°で
あり、かつ間隔２０μｍの鋸刃形状三角柱連続突起を縦
型ＮＣフライス加工盤により表面に形成した金型を用い
て、射出成形法により厚さ２ｍｍのアクリル製透明基板
を形成した。このようにして作製した、表面に断面が鋸
刃形状の三角柱連続突起を有する車両用窓映り防止光学
フィルターの窓映り防止性能を評価した結果、いかなる
走行条件下でも窓映り光は認識されず、また運転にも全
く支障がなかった。Example 1 A mold having saw blade-shaped triangular prism continuous projections having angles of 30 ° and 100 ° excluding the apex angle and intervals of 20 μm formed on the surface by a vertical NC milling machine was used. Then, an acrylic transparent substrate having a thickness of 2 mm was formed by an injection molding method. As a result of evaluating the window anti-glare performance of the vehicle window anti-glare optical filter having a triangular prism continuous protrusion having a sawtooth-shaped cross section on the surface produced in this manner, no window glint is recognized under any running condition, There was no problem in driving.
【００４３】実施例２ 頂角を除く２つの角の角度がそれぞれ４０°、１２０°
であり、かつ間隔８０μｍの鋸刃形状三角柱連続突起を
ワイヤーカット放電加工盤により表面に形成した金型を
用いて、射出成形法により厚さ２ｍｍのポリカーボネー
ト製透明基板を形成した。このようにして作製した、表
面に鋸刃形状の三角柱連続突起を有する車両用窓映り防
止光学フィルターの窓映り防止性能を評価した結果、い
かなる走行条件下でも窓映り光は認識されず、また運転
にも全く支障がなかった。Example 2 The angles of the two angles excluding the apex angle are 40 ° and 120 °, respectively.
A transparent substrate made of polycarbonate having a thickness of 2 mm was formed by an injection molding method using a mold in which saw blade-shaped triangular prism continuous protrusions having an interval of 80 μm were formed on the surface by a wire cut electric discharge machine. As a result of evaluating the anti-windowing performance of the vehicle anti-glare optical filter having the sawtooth-shaped triangular prism continuous protrusions produced in this way, no windowing light was recognized under any driving conditions, There was no problem at all.
【００４４】実施例３ 厚さ１５０μｍのＰＥＴフィルム上へ紫外線硬化性樹脂
組成物「ソーラプレン」（三井東圧化学株式会社の商標
名）を約１００μｍ塗布した後、頂角を除く２つ角の角
度がそれぞれ２２°、１１０°であり、かつ間隔６０μ
ｍの鋸刃形状三角柱連続突起を転写し、紫外線照射装置
により紫外線を２分間照射して紫外線硬化性樹脂組成物
を硬化させた。続いて大きさ１５０ｍｍ×４５０ｍｍ×
２ｍｍｔのアクリル製透明基板とフィルムとを接着剤と
して熱硬化性エポキシ系接着剤「セメダインＣＳ−２３
４０−５」（セメダイン株式会社の商品番号）を用いて
接着した。このようにして作製した、表面に鋸刃形状の
三角柱連続突起を有する車両用窓映り防止光学フィルタ
ーの窓映り性能を評価した結果、いかなる走行条件下で
も窓映り光は認識されず、また運転にも全く支障が無か
った。Example 3 After coating the ultraviolet curable resin composition "Solarprene" (trade name of Mitsui Toatsu Chemicals, Inc.) on a PET film having a thickness of 150 μm by about 100 μm, two corner angles excluding the apex angle are applied. Are 22 ° and 110 °, respectively, and the spacing is 60μ.
m saw blade-shaped triangular prism continuous protrusions were transferred and irradiated with ultraviolet rays for 2 minutes by an ultraviolet irradiation device to cure the ultraviolet curable resin composition. Then size 150 mm × 450 mm ×
A thermosetting epoxy adhesive "Cemedine CS-23" using a 2 mmt acrylic transparent substrate and a film as an adhesive.
40-5 "(product number of Cemedine Co., Ltd.). As a result of evaluating the window reflection performance of the vehicle window reflection prevention optical filter having the sawtooth-shaped triangular prism continuous protrusions produced in this way, the window reflection light was not recognized under any running condition, and There was no problem at all.
【００４５】実施例４ 頂角を除く２つの角度をそれぞれ２７°、１００°とし
た他は、実施例３と全く同様にして車両用窓映り防止光
学フィルターを作製した。このようにして作製した、表
面に鋸刃形状の三角柱連続突起を有する車両用窓映り防
止光学フィルターの窓映り防止性能を評価した結果、い
かなる走行条件下でも窓映り光は認識されず、また運転
にも全く支障が無かった。Example 4 A vehicle window anti-glare optical filter was produced in exactly the same manner as in Example 3 except that the two angles except the apex angle were 27 ° and 100 °, respectively. As a result of evaluating the anti-windowing performance of the vehicle anti-glare optical filter having the sawtooth-shaped triangular prism continuous protrusions produced in this way, no windowing light was recognized under any driving conditions, There was no problem at all.
【００４６】実施例５ 頂角を除く２つの角度がそれぞれ３５°、１２０°とし
た他は、実施例３と全く同様にして車両用窓映り防止光
学フィルターを作製した。このようにして作製した、表
面に鋸刃形状の三角柱連続突起を有する車両用窓映り防
止光学フィルターの窓映り防止性能を評価した結果、い
かなる走行条件下でも窓映り光は認識されず、また運転
にも全く支障が無かった。Example 5 A vehicle window anti-glare optical filter was manufactured in exactly the same manner as in Example 3 except that the two angles except the vertical angle were 35 ° and 120 °, respectively. As a result of evaluating the anti-windowing performance of the vehicle anti-glare optical filter having the sawtooth-shaped triangular prism continuous protrusions produced in this way, no windowing light was recognized under any driving conditions, There was no problem at all.
【００４７】実施例６ 表面に更にハードコート層として「トスガード」（東芝
シリコーン株式会社の商標名）を１μｍになるように塗
布した他は、実施例３と全く同様な方法により車両用窓
映り防止光学フィルターを作製した。このようにして作
製した、表面に鋸刃形状の三角柱連続突起を有する車両
用窓映り防止光学フィルターの窓映り防止性能を評価し
た結果、いかなる走行条件下でも窓映り光は認識され
ず、また運転にも全く支障が無かった。Example 6 In the same manner as in Example 3, except that "Tosguard" (trade name of Toshiba Silicone Co., Ltd.) was further applied as a hard coat layer on the surface to prevent window reflection for vehicles. An optical filter was produced. As a result of evaluating the anti-windowing performance of the vehicle anti-glare optical filter having the sawtooth-shaped triangular prism continuous protrusions produced in this way, no windowing light was recognized under any driving conditions, There was no problem at all.
【００４８】実施例７ 縦型ＮＣフライス加工盤により、頂角を除く２つの角度
がそれぞれ３２°、９０°であり、かつ９０°となる角
側に接している面の１０点平均粗さが ０．２μｍであ
る鋸刃形状三角柱連続突起を形成した金型を用いて、射
出成形法により厚さ２ｍｍのアクリル製透明基板を形成
した。このようにして作製した、表面に鋸刃形状の三角
柱連続突起を有する車両用窓映り防止光学フィルターの
窓映り防止性能を評価した結果、いかなる走行条件下で
も窓映り光は認識されず、また運転にも全く支障が無か
った。Example 7 Using a vertical NC milling machine, the two angles except the apex angle were 32 ° and 90 °, respectively, and the 10-point average roughness of the faces in contact with the corner side of 90 ° was obtained. A 2 mm thick acrylic transparent substrate was formed by an injection molding method using a mold having saw blade-shaped triangular prism continuous protrusions of 0.2 μm. As a result of evaluating the anti-windowing performance of the vehicle anti-glare optical filter having the sawtooth-shaped triangular prism continuous protrusions produced in this way, no windowing light was recognized under any driving conditions, There was no problem at all.
【００４９】実施例８ ワイヤーカット放電加工盤により、頂角を除く２つの角
度がそれぞれ２５°、９０°であり、かつ９０°となる
角度に接している面の１０点平均粗さが０．６μｍの鋸
刃形状三角柱連続突起を形成した金型を用いて、射出成
形法により厚さ２ｍｍのポリカーボネート製透明基板を
形成した。このようにして作製した、表面に鋸刃形状三
角柱連続突起を有する車両用窓映り防止光学フィルター
の窓映り防止性能を評価した結果、いかなる走行条件下
でも窓映り光は認識されず、また運転にも全く支障が無
かった。Example 8 Using a wire-cut electric discharge machine, the two angles excluding the apex angle were 25 ° and 90 °, and the 10-point average roughness of the surfaces in contact with the angles of 90 ° was 0. A polycarbonate transparent substrate having a thickness of 2 mm was formed by an injection molding method using a mold in which a saw blade-shaped triangular prism continuous protrusion having a size of 6 μm was formed. As a result of evaluating the window anti-glare performance of the vehicle window anti-glare optical filter having the saw blade-shaped triangular prism continuous projections produced in this way, the window anti-glare was not recognized under any running conditions, and There was no problem at all.
【００５０】実施例９ 頂角を除く２つの角度がそれぞれ２２°、１１０°であ
り、かつ間隔６０μｍの鋸刃形状三角柱連続突起に代え
て、頂角を除く２つの角度がそれぞれ３８°、９０°で
あり、かつ９０°となる角側に接している面の１０点平
均粗さが面の１０点平均粗さ１．５μｍの鋸刃形状三角
柱連続突起を用いた他は、実施例３と全く同様な方法に
より車両用窓映り防止光学フィルターを作製した。この
ようにして作製した、表面に鋸刃形状三角柱連続突起を
有する車両用窓映り防止光学フィルターの窓映り防止性
能を評価した結果、いかなる走行条件下でも窓映り光は
認識されず、また運転にも全く支障が無かった。Example 9 The two angles excluding the apex angle were 22 ° and 110 °, respectively, and the two angles excluding the apex angle were 38 ° and 90 °, respectively, in place of the saw-tooth-shaped triangular prism continuous protrusions having an interval of 60 μm. Example 3 and Example 3 except that a saw-toothed triangular prism continuous protrusion having a 10-point average roughness of the surface in contact with the angle side of 90 ° and a 10-point average roughness of the surface of 1.5 μm is used. A vehicle window anti-glare optical filter was manufactured by a completely similar method. As a result of evaluating the window anti-glare performance of the vehicle window anti-glare optical filter having the saw blade-shaped triangular prism continuous projections produced in this way, the window anti-glare was not recognized under any running conditions, and There was no problem at all.
【００５１】実施例１０ 頂角を除く２つの角度がそれぞれ３８°、９０°であ
り、かつ９０°となる角側に接している面の１０点平均
粗さが面の１０点平均粗さ１．５μｍの鋸刃形状三角柱
連続突起に代えて、頂角を除く２つの角度がそれぞれ３
０°、９０°であり、かつ９０°となる角側に接してい
る面の１０点平均粗さが面の１０点平均粗さ５μｍの鋸
刃形状三角柱連続突起を用いた他は、実施例９と全く同
様な方法により車両用窓映り防止光学フィルターを作製
した。このようにして作製した、表面に鋸刃形状三角柱
連続突起を有する車両用窓映り防止光学フィルターの窓
映り防止性能を評価した結果、いかなる走行条件下でも
窓映り光は認識されず、また運転にも全く支障が無かっ
た。Example 10 Two angles other than the apex angle are 38 ° and 90 °, respectively, and the 10-point average roughness of the surface in contact with the angle side where the angle is 90 ° is the 10-point average roughness of the surface 1 Instead of the saw-tooth shaped triangular prism continuous protrusion of 0.5 μm, each of the two angles except the apex angle is 3
Examples except that a saw-blade-shaped triangular prism continuous protrusion having a 10-point average roughness of the surface of 0 °, 90 ° and in contact with the angle side of 90 ° and a 10-point average roughness of the surface of 5 μm was used. A vehicle window reflection preventing optical filter was produced in the same manner as in No. 9. As a result of evaluating the window anti-glare performance of the vehicle window anti-glare optical filter having the saw blade-shaped triangular prism continuous projections produced in this way, the window anti-glare was not recognized under any running conditions, and There was no problem at all.
【００５２】実施例１１ 頂角を除く２つの角度がそれぞれ３８°、９０°であ
り、かつ９０°となる角側に接している面の１０点平均
粗さが面の１０点平均粗さ１．５μｍの鋸刃形状三角柱
連続突起に代えて、頂角を除く２つの角度がそれぞれ４
０°、９０°であり、かつ９０°となる角側に接してい
る面の１０点平均粗さが面の１０点平均粗さ９μｍの鋸
刃形状三角柱連続突起を用いた他は、実施例９と全く同
様な方法により車両用窓映り防止光学フィルターを作製
した。このようにして作製した、表面に鋸刃形状三角柱
連続突起を有する車両用窓映り防止光学フィルターの窓
映り防止性能を評価した結果、いかなる走行条件下でも
窓映り光は認識されず、また運転にも全く支障が無かっ
た。Example 11 Two angles excluding the apex angle are 38 ° and 90 °, respectively, and the 10-point average roughness of the surface in contact with the corner side where the angle is 90 ° is the 10-point average roughness of the surface 1 Instead of the sawtooth-shaped triangular prism continuous protrusions of 0.5 μm, each of the two angles excluding the apex angle is 4
Example except that a saw blade-shaped triangular prism continuous protrusion having a 10-point average roughness of the surface which is 0 ° and 90 ° and is in contact with the angle side of 90 ° is 10-point average roughness of 9 μm is used. A vehicle window reflection preventing optical filter was produced in the same manner as in No. 9. As a result of evaluating the window anti-glare performance of the vehicle window anti-glare optical filter having the saw blade-shaped triangular prism continuous projections produced in this way, the window anti-glare was not recognized under any running conditions, and There was no problem at all.
【００５３】実施例１２ 表面に更にハードコート層として「トスガード」（東芝
シリコーン株式会社の商標名）を１μｍになるように塗
布した他は、実施例９と全く同様な方法により車両用窓
映り防止光学フィルターを作製した。このようにして作
製した、表面に鋸刃形状三角柱連続突起を有する車両用
窓映り防止光学フィルターの窓映り防止性能を評価した
結果、いかなる走行条件下でも窓映り光は認識されず、
また運転にも全く支障が無かった。Example 12 In the same manner as in Example 9 except that "Tosguard" (trade name of Toshiba Silicone Co., Ltd.) was further applied as a hard coat layer to the surface to prevent window reflection for vehicles. An optical filter was produced. As a result of evaluating the window reflection prevention performance of the vehicle window reflection prevention optical filter having the saw blade-shaped triangular prism continuous protrusions produced in this manner, the window reflection light was not recognized under any running condition,
In addition, there was no problem in driving.
【００５４】比較例１ センターコンソール中央部に設置されている時計の前面
に、ルーバー間隔２００μｍ、厚さ５００μｍの信越シ
リコン製遮光フィルターを挟み込んだ透明樹脂製カバー
を設けて窓映り防止性能を評価した結果、いかなる走行
条件下でも窓映り光は認識されなかったが、時計文字盤
部分が全体的に暗く見づらかった。Comparative Example 1 A transparent resin cover having a louver spacing of 200 μm and a thickness of 500 μm of a Shin-Etsu silicon light-shielding filter sandwiched was provided on the front surface of a timepiece installed in the center of the center console to evaluate window reflection preventing performance. As a result, the window light was not recognized under any driving condition, but the clock face part was totally dark and difficult to see.
【００５５】[0055]
【発明の効果】本発明の車両用窓映り防止光学フィルタ
ーは、隣接する三角柱突起の間隔が１０〜１００μｍの
範囲にあり、かつ鋸刃の頂角以外の角度がそれぞれ２０
〜４０°又は９０〜１２０°の範囲にあるので、いかな
る走行条件下でも窓映り光は認識されず、また運転にも
全く支障がない。According to the vehicle window anti-glare optical filter of the present invention, the distance between adjacent triangular prism projections is in the range of 10 to 100 μm, and the angles other than the vertical angle of the saw blade are each 20.
Since it is in the range of -40 ° or 90-120 °, no window reflection light is recognized under any driving condition and there is no problem in driving.
【図１】センターコンソール部分の断面拡大図及びドラ
イバーが時計から発せられる光により窓映り像を視認す
ることを説明する図である。FIG. 1 is an enlarged cross-sectional view of a center console portion and a view for explaining that a driver visually recognizes a window reflection image by light emitted from a timepiece.
【図２】フロントウインドウの室内表面側に反射防止膜
を設けることにより窓映り防止を施している方法を説明
する図である。FIG. 2 is a diagram illustrating a method for preventing window reflection by providing an antireflection film on the indoor surface side of the front window.
【図３】時計の前面に遮光フィルターを挟み込んだ透明
樹脂製カバーを設けてウインドウ方向へ発される光の角
度を制御することにより窓映り防止を施している方法を
説明する図である。FIG. 3 is a diagram for explaining a method for preventing window reflection by providing a transparent resin cover with a light blocking filter sandwiched on the front surface of the timepiece to control the angle of light emitted in the window direction.
【図４】本発明の車両用窓映り防止光学フィルターの断
面部分拡大図である。FIG. 4 is an enlarged cross-sectional partial view of a vehicle window reflection preventing optical filter of the present invention.
【図５】本発明の車両用窓映り防止光学フィルターをセ
ンターコンソール中央部分の時計前面に透明樹脂製カバ
ーとして設置した場合の効果を説明する図である。FIG. 5 is a diagram for explaining the effect when the vehicle window reflection preventing optical filter of the present invention is installed as a transparent resin cover on the front of the watch in the center of the center console.
【図６】本発明の車両用窓映り防止光学フィルターを通
過する光の屈折状況を説明するための断面部分拡大図で
ある。FIG. 6 is an enlarged cross-sectional partial view for explaining a refraction state of light passing through the vehicle window anti-glare optical filter of the present invention.
【図７】多重に反射する透過光を防止するために形状工
夫を施したことを説明する図である。FIG. 7 is a diagram illustrating that a shape is devised to prevent transmitted light that is reflected in multiple layers.
１ 時計 ２ フロントウインド ３ 視点 ４ 反射防止膜 ５ 透明樹脂製カバー ６ 車両用窓映り防止光学フィルター ７ 透明基板 ８ 接着剤層 ９ ハードコート層 1 Clock 2 Front window 3 Viewpoint 4 Antireflection film 5 Transparent resin cover 6 Vehicle window anti-glare optical filter 7 Transparent substrate 8 Adhesive layer 9 Hard coat layer
Claims (4)
細な三角柱突起が同一方向に連続して配置された車両用
窓映り防止光学フィルターにおいて、隣接する三角柱突
起の間隔が１０〜１００μｍの範囲にあり、かつ鋸刃の
頂角を除く２つの角度がそれぞれ２０〜４０°又は９０
〜１２０°の範囲にあることを特徴とする車両用窓映り
防止光学フィルター。1. In a vehicle window anti-glare optical filter in which fine triangular protrusions having a saw-tooth-shaped cross section are continuously arranged in the same direction on a surface of a transparent substrate, an interval between adjacent triangular protrusions is 10 to 100 μm. And the two angles excluding the vertical angle of the saw blade are 20 to 40 ° or 90, respectively.
A window reflection preventing optical filter for a vehicle, which is in the range of 120 °.
囲が９０〜１２０°の範囲となる角側に接している面が
粗面化されていて、１０点平均粗さＲｚで０．１〜１０
μｍの範囲にあることを特徴とする請求項１記載の車両
用窓映り防止光学フィルター。2. Of the two angles excluding the apex angle of the saw blade, the surface in contact with the corner side having an angle range of 90 to 120 ° is roughened and has a 10-point average roughness Rz. 0.1-10
The vehicle window antiglare optical filter according to claim 1, wherein the optical filter is in the range of μm.
形状を維持したままで、その表面にハードコート層が設
けられていることを特徴とする請求項１又は２に記載の
車両用反射防止光学フィルター。3. The vehicle according to claim 1 or 2, wherein a hard coat layer is provided on the surface of the protrusion while maintaining the shape of a fine triangular prism-shaped protrusion having a saw blade-shaped cross section. Anti-reflection optical filter.
同一方向に連続して透明フィルム表面に形成され、かつ
この透明フィルムが透明基板上に接着されていることを
特徴とする請求項１、２又は３記載の車両用窓映り防止
光学フィルター。4. A fine triangular columnar protrusion having a saw-toothed cross section is continuously formed in the same direction on the surface of the transparent film, and the transparent film is bonded onto a transparent substrate. 1. A vehicle window reflection preventing optical filter according to 1, 2 or 3.