JPH07298793A - Light-shielding net - Google Patents
Light-shielding netInfo
- Publication number
- JPH07298793A JPH07298793A JP9099294A JP9099294A JPH07298793A JP H07298793 A JPH07298793 A JP H07298793A JP 9099294 A JP9099294 A JP 9099294A JP 9099294 A JP9099294 A JP 9099294A JP H07298793 A JPH07298793 A JP H07298793A
- Authority
- JP
- Japan
- Prior art keywords
- light
- shielding net
- stitches
- woven fabric
- density polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、農業において使用され
る遮光用のネットに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a shading net used in agriculture.
【０００２】[0002]
【従来の技術】従来の遮光シートとしては、実公平５−
３３３３９号公報に示されているものがあり、これに
は、延伸ポリエチレンフィルム上にアルミニウム蒸着層
及び延伸してないポリエチレンを順次積層してなる積層
体テープを用いた編織物からなる遮光ネットが開示され
ており、また、上記の積層体テープを横糸とし、他のモ
ノフィラメントを縦糸とした織物からなる遮光ネットが
開示されている。2. Description of the Related Art As a conventional shading sheet,
Japanese Patent No. 33339 discloses a light-shielding net made of a knitted fabric using a laminated tape formed by sequentially laminating an aluminum vapor deposition layer and unstretched polyethylene on a stretched polyethylene film. In addition, a light-shielding net made of a woven fabric in which the above-mentioned laminated tape is used as a weft and another monofilament is used as a warp is disclosed.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、本来、
遮光ネットの目的は、単に光を遮断するだけではなく、
光を遮断することによって遮光される場所又はその空間
の温度を低下させることであるところ、上記のような遮
光ネットは、アルミニウム蒸着層によって光を反射させ
ることによって単純に遮光しようとするものであって、
このアルミニウム蒸着層による反射は、平均反射率で約
８５パーセントである反面、平均約１５パーセントもの
光の吸収率を有していた。即ち、照射される光をある程
度反射できるものの、残余部分を吸収してしまい、遮光
ネットそのものに熱が蓄積され、この蓄積された熱が遮
光ネットから発散されることとなって、予定する程度に
まで遮光空間の温度を下降させることができず、もって
断熱効果を減少させるものであった。[Problems to be Solved by the Invention] However, originally,
The purpose of the shading net is not only to block the light,
Whereas the temperature of a place where light is blocked or the space thereof is lowered by blocking light, the above-mentioned light-shielding net is intended to simply shield light by reflecting light with an aluminum vapor deposition layer. hand,
The reflection by this aluminum vapor-deposited layer had an average reflectance of about 85%, while having an average light absorption of about 15%. That is, although the emitted light can be reflected to some extent, the remaining portion is absorbed, heat is accumulated in the light-shielding net itself, and the accumulated heat is dissipated from the light-shielding net. However, the temperature of the light-shielded space could not be lowered, and the heat insulating effect was reduced.
【０００４】また、上記の遮光ネットはアルミニウム蒸
着層の上に延伸してないポリエチレンを積層する構成で
あるが、予め編織物に使用できる程度に細くした積層体
テープを設けておき、これにアルミニウムを蒸着したう
えでポリエチレンを積層することは、細かな作業が多く
なるために生産性が低く、遮光ネットが高価なものとな
っていた。そこで、生産性を向上させるためには、大面
積の積層体を製造した後に細く切断して積層体テープを
設けなければならず、そのため、切断した部分の切断部
端辺においては、中間層であるアルミニウム蒸着層が露
出する状態となるため、この部分のアルミニウムの酸化
が進行するという不具合もあった。Further, the above-mentioned light-shielding net is constructed by laminating unstretched polyethylene on an aluminum vapor-deposited layer. A laminated tape which is thin enough to be used for knitting and woven fabric is provided in advance, and aluminum is attached to this. When polyethylene is laminated after vapor deposition, the productivity is low and the light-shielding net is expensive because of the large number of detailed work. Therefore, in order to improve productivity, it is necessary to manufacture a large-area laminated body and then cut it into thin pieces to provide a laminated body tape. Therefore, at the cut edge of the cut portion, an intermediate layer is used. Since a certain aluminum vapor deposition layer is exposed, there is also a problem that oxidation of aluminum in this portion proceeds.
【０００５】さらに、上記の遮光ネットはアルミニウム
蒸着層を有しているため、ネット全体が柔軟性に欠ける
ものとならざるを得ず、折曲又は折畳むことなどによっ
て容易に収納することができない不便さがあった。ま
た、このような柔軟性の欠如のために、設置したネット
の残余部分を適当に折曲して放置することは許されず、
残余の部分を設置した部分から切り離さなければなら
ず、作業能率のうえで非常に不具合であり、敢えて折曲
を繰り返すことによって加工硬化による亀裂の発生もあ
った。さらに、アルミニウム蒸着層、即ち、薄膜状の金
属層を有することは、遮光ネットの重量が大きいものと
なってしまい、これまた作業能率の向上を阻害するもの
であった。Further, since the above-mentioned light-shielding net has an aluminum vapor-deposited layer, the net as a whole has to lack flexibility and cannot be easily housed by bending or folding. There was inconvenience. In addition, due to such lack of flexibility, it is not allowed to bend and leave the rest of the installed net properly.
The remaining part had to be separated from the installed part, which was extremely inconvenient in terms of work efficiency, and cracks occurred due to work hardening due to repeated bending. Furthermore, having the vapor-deposited aluminum layer, that is, the thin-film metal layer increases the weight of the light-shielding net, which also hinders improvement in work efficiency.
【０００６】本発明は、上記の諸点に鑑み、断熱効果を
向上させるとともに、軽量で柔軟な遮光ネットを提供す
ることを目的とする。In view of the above points, it is an object of the present invention to improve the heat insulation effect and to provide a lightweight and flexible light shielding net.
【０００７】[0007]
【課題を解決するための手段】本発明は、高密度ポリエ
チレンスパンボンドフラッシュ紡糸法による不織布を細
長に裁断して縦糸とし、他の合成繊維を横糸とした編織
物からなることを特徴とする遮光ネットを要旨とする。DISCLOSURE OF THE INVENTION The present invention comprises a knitted woven fabric in which a nonwoven fabric produced by a high-density polyethylene spunbond flash spinning method is cut into long and narrow yarns and other synthetic fibers as weft yarns. The net is the gist.
【０００８】前記縦糸が適度な間隔を有するようにして
なることが好ましい。It is preferable that the warp yarns have an appropriate interval.
【０００９】本発明は、高密度ポリエチレンスパンボン
ドフラッシュ紡糸法による不織布を細長に裁断して横糸
とし、他の合成繊維を縦糸とした編織物からなることを
特徴とする遮光ネットを要旨とする。The gist of the present invention is a light-shielding net characterized by comprising a knitted fabric in which a nonwoven fabric produced by a high-density polyethylene spunbond flash spinning method is cut into long and narrow wefts and other synthetic fibers as warp yarns.
【００１０】前記横糸が適度な間隔を有するようにして
なることが好ましい。It is preferable that the weft threads have an appropriate interval.
【００１１】本発明は、高密度ポリエチレンスパンボン
ドフラッシュ紡糸法による不織布を細長に裁断して縦糸
及び横糸とした編織物からなることを特徴とする遮光ネ
ットを要旨とする。The gist of the present invention is a light-shielding net comprising a knitted woven fabric obtained by cutting a nonwoven fabric produced by a high-density polyethylene spunbond flash spinning method into elongated warp yarns and weft yarns.
【００１２】前記縦糸及び横糸が適度な間隔を有するよ
うにしてなることが好ましい。It is preferable that the warp yarns and the weft yarns have an appropriate interval.
【００１３】本発明は、縦糸及び横糸を合成繊維とした
編織物からなるネット本体の編目間隔内に、高密度ポリ
エチレンスパンボンドフラッシュ紡糸法による不織布を
細長に裁断してなる繊維テープを縦方向に通してなるこ
とを特徴とする遮光ネットを要旨とする。According to the present invention, a fiber tape formed by cutting a non-woven fabric by a high-density polyethylene spun bond flash spinning method into a slender shape in the longitudinal direction within a stitch interval of a net body made of a knitted fabric having warp and weft yarns as synthetic fibers. The gist is a light-shielding net that is characterized by being passed through.
【００１４】前記編目間隔が横方向に一定間隔となって
おり、編目が縦方向に平行となることが好ましい。前記
縦方向に平行な編目によってできる間隔列のうち、前記
繊維テープを通さない間隔列を有してなることが好まし
い。It is preferable that the intervals between the stitches are constant in the lateral direction and the stitches are parallel to the longitudinal direction. Among the spacing rows formed by the stitches parallel to the longitudinal direction, it is preferable that the spacing rows do not pass the fiber tape.
【００１５】本発明は、縦糸及び横糸を合成繊維とした
編織物からなるネット本体の編目間隔内に、高密度ポリ
エチレンスパンボンドフラッシュ紡糸法による不織布を
細長に裁断してなる繊維テープを横方向に通してなるこ
とを特徴とする遮光ネットを要旨とする。According to the present invention, a fiber tape formed by cutting a non-woven fabric by a high-density polyethylene spun bond flash spinning process into slender pieces is provided in the transverse direction within a stitch interval of a net body made of a knitted fabric having warp yarns and weft yarns as synthetic fibers. The gist is a light-shielding net that is characterized by being passed through.
【００１６】前記編目間隔が縦方向に一定間隔となって
おり、編目が横方向に平行となることが好ましい。前記
横方向に平行な編目によってできる間隔列のうち、前記
繊維テープを通さない間隔列を有してなることが好まし
い。It is preferable that the intervals between the stitches are constant in the vertical direction, and the stitches are parallel in the horizontal direction. Among the spacing rows formed by the stitches parallel to the lateral direction, it is preferable that the spacing rows do not pass the fiber tape.
【００１７】本発明は、縦糸及び横糸を合成繊維とした
編織物からなるネット本体の編目間隔内に、高密度ポリ
エチレンスパンボンドフラッシュ紡糸法による不織布を
細長に裁断してなる繊維テープを縦方向及び横方向に通
してなることを特徴とする遮光ネットを要旨とする。According to the present invention, a fiber tape formed by cutting a non-woven fabric by a high-density polyethylene spun bond flash spinning method into a slender shape in a longitudinal direction in a stitch interval of a net body made of a knitted fabric having warp and weft as synthetic fibers. The gist is a light-shielding net that is characterized by being passed through in the lateral direction.
【００１８】前記編目間隔が横方向及び縦方向に一定間
隔となっており、編目が縦方向及び横方向に平行となる
ことが好ましい。前記縦方向及び横方向に平行な編目に
よってできる間隔列のうち、前記繊維テープを通さない
間隔列を有してなることが好ましい。It is preferable that the stitch intervals are constant in the horizontal and vertical directions, and the stitches are parallel to the vertical and horizontal directions. Among the spacing rows formed by the stitches parallel to the longitudinal direction and the transverse direction, it is preferable that the spacing rows do not pass the fiber tape.
【００１９】[0019]
【作用】本発明は、高密度ポリエチレンスパンボンドフ
ラッシュ紡糸法による不織布を細長に裁断して縦糸と
し、他の合成繊維を横糸とした編織物からなるように構
成したので、アルミニウム蒸着層を使用するネットに比
して軽量となり、かつ、柔軟性が向上し、収納及び作業
の際の能率がよくなる。また、高密度ポリエチレンスパ
ンボンドフラッシュ紡糸法による不織布を細長に裁断し
た縦糸を使用したことから、遮光ネットが光を吸収する
ことがなく、断熱効果が向上するものである。さらに、
縦糸及び横糸を合成繊維とした編織物からなるネット本
体の編目間隔内に、高密度ポリエチレンスパンボンドフ
ラッシュ紡糸法による不織布を細長に裁断してなる繊維
テープを縦方向に通してなるので、繊維テープにより遮
光すべき面を任意に調整でき、作物に応じた遮光率を有
するネットを構成することができる。According to the present invention, the non-woven fabric produced by the high density polyethylene spunbond flash spinning method is cut into long and narrow warp yarns, and other synthetic fibers are used as weft yarns. Compared to a net, it is lighter in weight, more flexible, and more efficient in storage and work. In addition, since the warp yarn obtained by cutting the non-woven fabric by the high density polyethylene spun bond flash spinning method into long and narrow is used, the light shielding net does not absorb light, and the heat insulating effect is improved. further,
Since a fiber tape made by cutting a non-woven fabric made of high-density polyethylene spunbond flash into a slender shape is passed in the longitudinal direction within the stitch interval of a net body made of a knitted fabric with warp and weft as synthetic fibers, the fiber tape Thus, the surface to be shielded can be arbitrarily adjusted, and a net having a shielding ratio according to the crop can be constructed.
【００２０】[0020]
【実施例】以下、本発明の実施例を図面に基づいて説明
する。本発明は、遮光用のネットに関するものであっ
て、第一実施例は図１に示すものである。本実施例は、
縦糸１と横糸２とを編織したものであって、図１（ａ）
はカラミ織によるものであり図１（ｂ）は平織によるも
のである。縦糸１は合成繊維からなるものであり、この
合成繊維としてはモノフィラメント、マルチフィラメン
ト、フラットヤーン等があるが、本実施例ではモノフィ
ラメントからなるものとした。横糸２は高密度ポリエチ
レンスパンボンドフラッシュ紡糸法による不織布を細長
に裁断したものである。横糸２は、適当な間隔を有しな
がら編織されているため、横糸２ａと横糸２ｂとの間又
は横糸２ｂと横糸２ｃとの間には適当な間隔部分が存在
するようになっている。そして、横糸２の部分によって
遮光することができるようになっており、間隔部分にお
いては光が通過できるようになっている。この間隔部分
の存在によって、照射される光の一部を通過させること
ができ、遮光すべき場所の温度を調整することができる
ようになっている。従って、間隔を狭くした遮光ネット
では、横糸２による遮光面積が大きくなり、高い率の遮
光を可能にし、また、間隔を広くした遮光ネットでは、
横糸２による遮光面積が小さくなり、通過する光を多く
することができるものである。また、このような間隔部
分のないように編織してもよく、この場合、横糸２の遮
光率と同じとなる程の高い遮光率を有するの遮光ネット
を得ることができる。一方、縦糸１は、横糸２の状態を
維持できるように設けられており、横糸１の間隔の広狭
に応じて本数等は異なるものである。縦糸１を構成する
モノフィラメントは各種の材質によって製造できるが、
本実施例ではポリエチレンからなるものを採用した。こ
れにより、横糸２とともに焼却したとしても、有害な成
分を発生させることがなくなり、不要となった遮光ネッ
ト全体を焼却によって処分することが可能となる。これ
は、金属膜層を使用する遮光ネットと大きく異なるとこ
ろである。Embodiments of the present invention will be described below with reference to the drawings. The present invention relates to a light shielding net, and the first embodiment is shown in FIG. In this example,
A warp yarn 1 and a weft yarn 2 are knitted and woven, and are shown in FIG.
Is based on Karami weave, and FIG. 1 (b) is based on plain weave. The warp yarns 1 are made of synthetic fibers, and as the synthetic fibers, there are monofilaments, multifilaments, flat yarns, etc., but in this embodiment, they are made of monofilaments. The weft yarn 2 is obtained by cutting a non-woven fabric by a high-density polyethylene spun bond flash spinning method into elongated strips. Since the weft yarns 2 are knitted and woven with an appropriate spacing, there is an appropriate spacing portion between the weft yarns 2a and 2b or between the weft yarns 2b and 2c. The weft thread 2 can block light, and the light can pass through the space. Due to the existence of this interval portion, a part of the emitted light can be passed therethrough, and the temperature of the place to be shielded can be adjusted. Therefore, in the light-shielding net with a narrow interval, the light-shielding area by the weft thread 2 is large, and it is possible to shield light at a high rate.
The light-shielding area by the weft thread 2 is reduced, and more light can pass through. Further, it may be knitted or woven so as not to have such a gap portion, and in this case, it is possible to obtain a light-shielding net having a light-shielding rate as high as that of the weft yarn 2. On the other hand, the warp yarns 1 are provided so that the state of the weft yarns 2 can be maintained, and the number of the warp yarns 1 is different depending on the width of the weft yarns 1. The monofilament that constitutes the warp yarn 1 can be manufactured by various materials,
In this embodiment, polyethylene is used. As a result, even if it is incinerated together with the weft yarn 2, no harmful components are generated, and it becomes possible to dispose of the entire unnecessary light-shielding net by incineration. This is a big difference from a light-shielding net that uses a metal film layer.
【００２１】ここで、横糸２に使用する高密度ポリエチ
レンスパンボンドフラッシュ紡糸法による不織布につい
て詳述する。高密度ポリエチレンスパンボンドフラッシ
ュ紡糸法による不織布は、フラッシュ紡糸法により、極
細ポリエチレン繊維を高熱高圧力で結合させた不織布で
あり、柔軟性に富むものである。そして、この不織布
は、光に対する関係で次のような性質を有している。即
ち、反射率が９１．３０パーセントから９４．４２パー
セント、透過率が７．７１パーセントから７．８７パー
セント、吸収率が０パーセントから０．８３パーセント
である。これに対し、アルミニウム蒸着層を有するフィ
ルムでは次のような性質である。即ち、反射率が７４．
８２パーセントから８６．４５パーセント、透過率が
０．３２パーセントから１．８１パーセント、吸収率が
１２．９１パーセントから２４．０６パーセントであ
る。このような性質の比較から、アルミニウム蒸着層を
有するものを使用した遮光ネットでは、反射できない光
をほとんど吸収することとなるのに対し、高密度ポリエ
チレンスパンボンドフラッシュ紡糸法による不織布を使
用した遮光ネットでは、反射率が向上したうえに、反射
できない光をほとんど吸収することなく透過できるもの
であるということが容易に理解できる。従って、本実施
例に示す遮光ネットは、アルミニウム蒸着層を有するも
のを使用した遮光ネットと比較すると、反射率の向上に
基づいて遮光率が向上しており、しかも光を吸収しない
ものであるので、遮光ネット自体が熱を蓄積することが
なく、もって断熱効果がはるかに良いものということが
できる。また、高密度ポリエチレンスパンボンドフラッ
シュ紡糸法による不織布は、光の透過率が良いことか
ら、反射しない光を通過させることができるので、この
通過した光によって遮光した場所であっても比較的明る
い環境にすることができる。Now, the high density polyethylene spunbond flash spinning non-woven fabric used for the weft yarn 2 will be described in detail. The non-woven fabric produced by the high-density polyethylene spunbond flash spinning method is a non-woven fabric in which ultrafine polyethylene fibers are bonded at high heat and high pressure by the flash spinning method and is highly flexible. The non-woven fabric has the following properties in relation to light. That is, the reflectance is 91.30% to 94.42%, the transmittance is 7.71% to 7.87%, and the absorption is 0% to 0.83%. On the other hand, the film having the aluminum vapor deposition layer has the following properties. That is, the reflectance is 74.
82% to 86.45%, transmission of 0.32% to 1.81%, absorption of 12.91% to 24.06%. From the comparison of such properties, the light-shielding net using one having an aluminum vapor-deposited layer absorbs almost all the light which cannot be reflected, whereas the light-shielding net using the nonwoven fabric by the high density polyethylene spunbond flash spinning method. Then, it can be easily understood that, in addition to improving the reflectance, the light that can not be reflected can be transmitted with almost no absorption. Therefore, the light-shielding net shown in the present embodiment has a higher light-shielding rate based on the improved reflectance, and does not absorb light, as compared with the light-shielding net using one having an aluminum vapor deposition layer. It can be said that the light-shielding net itself does not accumulate heat and thus has a much better heat insulating effect. In addition, since the non-woven fabric produced by the high-density polyethylene spunbond flash spinning method has good light transmittance, it can pass light that does not reflect. Can be
【００２２】本実施例では上記のように、モノフィラメ
ントからなる縦糸１と、高密度ポリエチレンスパンボン
ドフラッシュ紡糸法による不織布による横糸２とを編織
するものであることから、図２に示すように、編織物全
体Ａは、モノフィラメントの縦糸１が縦方向Ｘに連続す
る状態となっており、一方、不織布の横糸２は横方向Ｙ
に連続する状態となっている。これにより、縦方向Ｘに
おいては細糸状のモノフィラメントによって十分に柔軟
であるうえに、横方向Ｙにおいては柔軟性に優れた不織
布によって一層柔軟なものとなる。従って、幅の狭い場
所に本発明のネットを設置する際であっても、横方向Ｙ
への折曲等が容易となり、設置作業を簡素化できるもの
である。In this embodiment, as described above, the warp yarn 1 made of a monofilament and the weft yarn 2 made of a non-woven fabric by the high density polyethylene spun bond flash spinning method are knitted and weaved, as shown in FIG. The whole fabric A is in a state in which the monofilament warp yarns 1 are continuous in the longitudinal direction X, while the non-woven fabric weft yarns 2 are in the transverse direction Y.
It is in a continuous state. As a result, in the longitudinal direction X, the filaments are sufficiently flexible by the filament-like monofilament, and in the transverse direction Y, the nonwoven fabric having excellent flexibility is further softened. Therefore, even when the net of the present invention is installed in a narrow space, the horizontal direction Y
This makes it easy to bend to, and simplifies the installation work.
【００２３】また、本実施例は上記のほか、図３
（ａ），（ｂ）に示すように、高密度ポリエチレンスパ
ンボンドフラッシュ紡糸法による不織布による縦糸１
と、モノフィラメントからなる横糸２とを編織するもの
であっても良い。そして、図３（ａ）はカラミ織による
ものであり図３（ｂ）は平織によるものである。このと
きの縦糸１が高密度ポリエチレンスパンボンドフラッシ
ュ紡糸法による不織布によるものであるから、縦糸１を
前記の横糸（図１）と同様に、間隔を調整することによ
って遮光率を変化させることができる。このようにして
なる編織物全体Ｂは、図４に示すように、不織布の縦糸
１が縦方向Ｘに連続する状態となっており、一方、モノ
フィラメントの横糸２は横方向Ｙ、即ち、編織物Ｂの幅
方向に平行して存在するようになっている。これによ
り、編織物Ｂを必要な長さで切断したときの長手方向に
は、当然に柔軟性に優れた不織布の縦糸１が連続するこ
ととなるため、収納時の折曲は容易となるものであり、
また、編織物を遮光すべき範囲に設置したときにもその
残余部分を容易に折曲することができ、設置作業を簡素
化できるものである。In addition to the above, this embodiment is also shown in FIG.
As shown in (a) and (b), a warp yarn 1 made of a non-woven fabric by a high-density polyethylene spunbond flash spinning method.
Alternatively, the weft yarn 2 made of a monofilament may be knitted or woven. And, FIG. 3 (a) is based on Karami weave, and FIG. 3 (b) is based on plain weave. At this time, the warp yarn 1 is made of a nonwoven fabric produced by the high-density polyethylene spunbond flash spinning method. Therefore, the light-shielding rate can be changed by adjusting the spacing of the warp yarn 1 as in the case of the weft yarn (FIG. 1). . As shown in FIG. 4, the whole knitted and woven fabric B thus formed is in a state where the warp yarns 1 of the non-woven fabric are continuous in the longitudinal direction X, while the weft yarns 2 of the monofilament are in the transverse direction Y, that is, the knitted woven fabric. It exists so as to be parallel to the width direction of B. As a result, since the warp yarn 1 of the non-woven fabric having excellent flexibility naturally continues in the longitudinal direction when the knitted woven fabric B is cut into a required length, the folding at the time of storage becomes easy. And
Further, even when the knitted fabric is installed in the area where light should be shielded, the remaining portion can be easily bent, and the installation work can be simplified.
【００２４】なお、上記の実施例には、高密度ポリエチ
レンスパンボンドフラッシュ紡糸法による不織布の糸と
モノフィラメントの糸のうち、いずれか一方を縦糸１と
し、他方を横糸２とした遮光ネットのみを示したが、縦
糸１及び横糸２をともに高密度ポリエチレンスパンボン
ドフラッシュ紡糸法による不織布としたものであれば、
横糸２によっても遮光の効果を得ることができ、縦方向
及び横方向の両方向に対して柔軟性を良くすることがで
きる。In the above example, only the light-shielding net in which one of the non-woven yarn and the monofilament yarn produced by the high-density polyethylene spunbond flash spinning method is the warp yarn 1 and the other is the weft yarn 2 is shown. However, if both the warp yarn 1 and the weft yarn 2 are non-woven fabrics made by the high density polyethylene spunbond flash spinning method,
The weft thread 2 can also provide a light-shielding effect, and can improve flexibility in both the longitudinal direction and the transverse direction.
【００２５】次に、第二実施例を図５に基づいて説明す
る。本実施例は、まず、縦糸３をモノフィラメント、横
糸４をフラットヤーンにした編織物によってネット本体
が構成されている。そして、このネット本体の横方向に
並ぶ編目５ａ，５ｂ，５ｃによって間隔６ａ，６ｂが構
成されており、この間隔６ａ，６ｂ内に高密度ポリエチ
レンスパンボンドフラッシュ紡糸法による不織布を細長
に裁断してなる繊維テープ７，８が通されている。この
とき、縦糸３は一定の間隔を有して平行な状態となって
おり、かつ、この縦糸３と横糸４とが交差する位置にお
いて編織されていることから、編目５ａ，５ｂ，５ｃは
横方向に一定の間隔を有する状態となっており、かつ、
縦方向に平行な状態となっている。即ち、縦方向には平
行する間隔の列６ａ，６ｂが設けられた状態となってい
る。そして、前記の繊維テープ７，８は、同じ幅を有す
るように裁断されており、その両側辺は平行となってい
る。この繊維テープ７，８は、横糸４の上下を交互に通
過する状態で通されており、縦方向に連続していること
から、複数の横糸４によってその位置は固定されるよう
になっている。このようにして繊維テープ７，８を間隔
列６ａ，６ｂに通すことによって、ネット全体に繊維テ
ープ７，８による面を設けることができるようになって
いる。そして、繊維テープ７，８によってできた面は、
高密度ポリエチレンスパンボンドフラッシュ紡糸法によ
る不織布による面であることから、前記の第一実施例の
縦糸と同様な遮光率及び吸収率を有するものである。こ
こで、間隔６ａ，６ｂ内に繊維テープ７，８を通すに
は、予めモノフィラメントによる縦糸３及びフラットヤ
ーンからなる横糸４を編織したネット本体を設けてお
き、そのネット本体の間隔６ａ，６ｂに、後から挿通さ
せるても良いが、縦糸３及び横糸４を編織する際、通す
べき位置に縦糸３に繊維テープ７，８を供給することに
よって、編織と同時に繊維テープ７，８の挿通を行なっ
ても良い。なお、本実施例では、間隔列６ａ，６ｂの幅
は、繊維テープ７の３本分と同一になるように構成され
ているため、各間隔列６ａ，６ｂには繊維テープ７ａ，
７ｂ，７ｃと、繊維テープ８ａ，８ｂ，８ｃが通されて
いるが、この間隔列６ａ，６ｂの幅を変更させることに
よって、１つの間隔列６ａ，６ｂに通す繊維テープ７，
８の数が変化したものを多種作成することができること
は言うまでもない。また、上記の実施例には、縦方向に
のみ繊維テープを通したものを示したが、これを横方向
にしても同様の遮光ネットを得ることができ、縦及び横
の両方向に繊維テープを通したものであっても良い。Next, a second embodiment will be described with reference to FIG. In this embodiment, first, the net body is made of a knitted fabric in which the warp yarn 3 is a monofilament and the weft yarn 4 is a flat yarn. The spaces 6a, 6b are formed by the stitches 5a, 5b, 5c arranged in the lateral direction of the net body, and the non-woven fabric made by the high-density polyethylene spunbond flash spinning method is cut into the spaces 6a, 6b in a slender manner. The fiber tapes 7 and 8 are passed through. At this time, the warp yarns 3 are in a parallel state with a certain interval, and since the warp yarns 3 and the weft yarns 4 are knitted at the intersecting positions, the stitches 5a, 5b, 5c Is in a state with a constant interval in the direction, and
It is parallel to the vertical direction. That is, the columns 6a and 6b are arranged in parallel in the vertical direction at intervals. The fiber tapes 7 and 8 are cut so as to have the same width, and both sides thereof are parallel to each other. The fiber tapes 7 and 8 are passed in such a manner that they pass above and below the weft thread 4 alternately, and since they are continuous in the longitudinal direction, their positions are fixed by a plurality of weft threads 4. . By passing the fiber tapes 7 and 8 through the gap rows 6a and 6b in this manner, it is possible to provide the surface of the fiber tapes 7 and 8 on the entire net. And the surface formed by the fiber tapes 7 and 8 is
Since the surface is made of the non-woven fabric obtained by the high-density polyethylene spunbond flash spinning method, it has the same light-shielding rate and absorptivity as the warp threads of the first embodiment. Here, in order to pass the fiber tapes 7 and 8 into the spaces 6a and 6b, a net body in which the warp yarns 3 of monofilament and the weft yarns 4 of the flat yarn are knitted and woven is provided in advance, and the gaps 6a and 6b of the net bodies are provided. Although the fiber tapes 7 and 8 may be inserted later, when the warp yarn 3 and the weft yarn 4 are knitted and woven, the fiber tapes 7 and 8 are inserted into the warp yarns 3 at the positions to be passed so that the fiber tapes 7 and 8 are inserted at the same time as the knitting and weaving. May be. In this embodiment, since the width of the spacing rows 6a and 6b is the same as that of the three fiber tapes 7, the spacing tapes 6a and 6b have the same width.
7b, 7c and the fiber tapes 8a, 8b, 8c are passed through. By changing the width of the spacing rows 6a, 6b, the fiber tapes 7 passing through one spacing row 6a, 6b,
It goes without saying that it is possible to create various types of which the number of 8 has changed. Further, in the above embodiment, the fiber tape was passed through only in the longitudinal direction, but the same light-shielding net can be obtained even when the fiber tape is traversed in the longitudinal direction. It may be passed through.
【００２６】次に、第三実施例を図６に基づいて説明す
る。本実施例は、前記の第二実施例を変化させたもので
ある。ネット本体は第二実施例と同様に、縦糸９をモノ
フィラメント、横糸１０をフラットヤーンにした編織物
によってが構成されており、編目１１によって構成され
る間隔列１２も同様に、縦方向には平行な状態となって
いる。そして、この間隔列１２の幅は、繊維テープ１３
の１本の幅と同一になるように設けられている。これに
より、各間隔列１２のうち繊維テープ１３を通した間隔
列１２ａ，１２ｂと、通さない間隔列１２ｃとに分ける
ことができるようになっている。そして、繊維テープ１
３を通した部分によって光を遮断し、繊維テープ１３を
通さない部分によって光を通過させることができように
なっており、従って、任意に遮光率を調整できるように
なっている。繊維テープ１３を通した部分は、高密度ポ
リエチレンスパンボンドフラッシュ紡糸法による不織布
によって遮光されることとなるから、前記第一実施例及
び第二実施例と同様な遮光率及び吸収率を有するもので
ある。なお、本実施例においても、繊維テープ１３を通
した間隔列１２ａ，１２ｂと繊維テープ１３を通さない
間隔列１２ｃの割合を２対１としたもののみを示した
が、これらの数を変更することによって多種の異なる遮
光率を有するネットを得ることができることは言うまで
もない。例えば、図５に示すように、縦糸２０と横糸２
１との編目２２によってできる間隔列２３，２４，２
５，２６のうち、２列の繊維テープ２７ａ，２７ｂを通
した間隔列２３，２４と２列の繊維テープを通さない間
隔列２５，２６とによって１対１の割合として構成させ
ることもできる。また、図７に示すものは、縦糸２０と
横糸２１との編織をラッセル織にしたものであって、こ
のようなものであっても良い。上記の実施例には、縦方
向にのみ繊維テープを通したものを示したが、これを横
方向にしても同様の遮光ネットを得ることができ、縦及
び横の両方向に繊維テープを通したものであっても良
い。Next, a third embodiment will be described with reference to FIG. This embodiment is a modification of the second embodiment. Similar to the second embodiment, the net body is made of a knitted fabric in which the warp yarns 9 are monofilaments and the weft yarns 10 are flat yarns, and the spacing rows 12 formed by the stitches 11 are also parallel in the longitudinal direction. It is in a state. The width of the spacing row 12 is equal to
It is provided so as to have the same width as one of the above. As a result, the spacing rows 12 can be divided into the spacing rows 12a and 12b through which the fiber tape 13 is passed and the spacing rows 12c through which the fiber tape 13 is not passed. And fiber tape 1
The light can be blocked by the portion through which the light is passed through, and the light can be passed through by the portion through which the fiber tape 13 is not passed. Therefore, the light blocking rate can be arbitrarily adjusted. The portion passing through the fiber tape 13 is shielded from light by the non-woven fabric produced by the high density polyethylene spunbond flash spinning method. Therefore, the portion having the same light shielding ratio and absorptivity as those in the first and second embodiments is used. is there. In the present embodiment as well, only the ratio of the spacing rows 12a and 12b through which the fiber tape 13 is passed and the spacing rows 12c through which the fiber tape 13 is not passed is shown to be 2 to 1, but these numbers are changed. Needless to say, it is possible to obtain various nets having different shading rates. For example, as shown in FIG. 5, warp yarn 20 and weft yarn 2
Interval row 23, 24, 2 formed by stitch 22 with 1
It is also possible to configure the interval rows 23 and 24 of the five and 26 through which the two rows of the fiber tapes 27a and 27b are inserted and the interval rows 25 and 26 through which the two rows of the fiber tapes are not inserted as a one-to-one ratio. Moreover, what is shown in FIG. 7 is a Russell weave in which the warp yarn 20 and the weft yarn 21 are knitted, and such a weave may be used. In the above example, the fiber tape was passed through only in the longitudinal direction. However, the same light-shielding net can be obtained by using the fiber tape in the transverse direction, and the fiber tape is passed through in both the longitudinal and lateral directions. It may be one.
【００２７】なお、本発明の趣旨を逸脱しない範囲で種
々なる実施の態様を取り得ることは無論である。例え
ば、上記実施例には、縦糸又は横糸に使用する合成繊維
をモノフィラメント又はフラットヤーンによるもののみ
を示したが、これらの外にマルチフィラメント等を用い
ても良く、さらに、モノフィラメント、マルチフィラメ
ント、フラットヤーン等を適宜組み合わせて編織物を構
成させても良い。また、合成繊維（実施例中においては
モノフィラメント又はフラットヤーン）をポリエチレン
以外の材質のものを用いても良く、このときの材質とし
ては、ポリエステル、ナイロン、ビニロン、アクリル、
ポリプロピレン等が考えられる。It is needless to say that various embodiments can be taken without departing from the spirit of the present invention. For example, in the above examples, only synthetic filaments used for warp or weft are shown as monofilaments or flat yarns, but in addition to these, multifilaments may be used, and further, monofilaments, multifilaments, flat yarns may be used. A knitted fabric may be formed by appropriately combining yarns and the like. Further, synthetic fibers (monofilaments or flat yarns in the examples) made of materials other than polyethylene may be used, and the materials at this time include polyester, nylon, vinylon, acrylic,
Polypropylene or the like is considered.
【００２８】[0028]
【効果】本発明は、高密度ポリエチレンスパンボンドフ
ラッシュ紡糸法による不織布を細長に裁断して縦糸と
し、他の合成繊維を横糸とした編織物からなるので、柔
軟性に優れたものである。特に、遮光するための材質と
して、縦糸に高密度ポリエチレンスパンボンドフラッシ
ュ紡糸法による不織布を細長に裁断したものを採用した
ことから、アルミニウム蒸着層を有するものを使用した
遮光ネットよりも遮光率を向上させることができ、反射
できない光をほとんど吸収することなく透過できること
から、本発明の遮光ネット自体が熱を蓄積することがな
く、もって断熱効果がはるかに良いものということがで
きる。また、高密度ポリエチレンスパンボンドフラッシ
ュ紡糸法による不織布は、光の透過率が良いことから、
反射しない光を通過させることができるので、この通過
した光によって遮光したにもかかわらず、遮光された場
所は比較的明るいものである。さらに、合成繊維の材質
をポリエチレンにすることによって、焼却による有害成
分の発生を抑制することができるので、環境的に良好な
ものである。また、金属膜を使用しないので、酸化及び
加工硬化等の心配がないものである。[Effect] The present invention is excellent in flexibility because it is made of a knitted fabric in which a nonwoven fabric produced by a high-density polyethylene spunbond flash spinning method is cut into elongated warp yarns and other synthetic fibers are weft yarns. In particular, as a material for shielding light, we adopted a non-woven fabric obtained by cutting high-density polyethylene spunbond flash spinning method into slender warp yarns, which improves the shading rate compared to a light-shielding net using one with an aluminum deposition layer. The light-shielding net of the present invention does not accumulate heat because it can transmit light that cannot be reflected and that can be transmitted, so that it can be said that the heat insulating effect is much better. In addition, since the non-woven fabric produced by the high-density polyethylene spunbond flash spinning method has good light transmittance,
Since non-reflected light can be passed, the light-shielded place is relatively bright even though it is blocked by the light that has passed through. Furthermore, by using polyethylene as the material of the synthetic fiber, it is possible to suppress the generation of harmful components due to incineration, which is environmentally friendly. Further, since no metal film is used, there is no fear of oxidation and work hardening.
【００２９】前記縦糸が適度な間隔を有するようにして
なることから、間隔の広さを変えることによって、容易
に遮光率を変化させることができる。Since the warp yarns have an appropriate interval, it is possible to easily change the light blocking ratio by changing the width of the interval.
【００３０】本発明は、縦糸及び横糸を合成繊維とした
編織物からなるネット本体の編目間隔内に、高密度ポリ
エチレンスパンボンドフラッシュ紡糸法による不織布を
細長に裁断してなる繊維テープを縦方向に通してなるか
ら、柔軟性に優れたものである。また、ある程度の幅を
有する繊維テープによって遮光するため、容易に広い面
積を構成させることができ、高密度ポリエチレンスパン
ボンドフラッシュ紡糸法による不織布の性質を十分に発
揮させることができる。According to the present invention, a fiber tape formed by cutting a non-woven fabric by a high-density polyethylene spunbond flash spinning method into a slender shape in a longitudinal direction within a stitch interval of a net body made of a knitted fabric having warp yarns and weft yarns as synthetic fibers. Since it is passed through, it has excellent flexibility. Further, since the fiber tape having a certain width is used to shield the light, a large area can be easily formed, and the properties of the non-woven fabric obtained by the high density polyethylene spunbond flash spinning method can be sufficiently exhibited.
【００３１】前記編目間隔が横方向に一定間隔にして、
編目が縦方向に平行となるようにし、この縦方向に平行
な編目によってできる複数の間隔列のうち、繊維テープ
を通さない間隔列を有してなるから、繊維テープを通す
列と通さない列との割合によって、遮光率を容易に調整
できる。特に、繊維テープを高密度ポリエチレンスパン
ボンドフラッシュ紡糸法による不織布を細長に裁断した
ものを採用したことから、遮光ネット自体に熱が蓄積さ
れず、これにより、遮光ネットからの輻射熱がなく、予
定する遮光の効果を得ることができるものである。The stitch interval is set to a constant interval in the lateral direction,
Since the stitches are arranged so as to be parallel to the longitudinal direction, and among the plural spacing rows formed by the stitches parallel to the longitudinal direction, there are spacing rows that do not pass the fiber tape, so rows that pass the fiber tape and rows that do not pass. The light-shielding rate can be easily adjusted by the ratio. In particular, since the fiber tape is made by cutting a non-woven fabric made of high-density polyethylene spunbond flash into long and narrow strips, heat is not accumulated in the light-shielding net itself, and there is no radiant heat from the light-shielding net. The effect of shading can be obtained.
【図１】第一実施例の説明図である。FIG. 1 is an explanatory diagram of a first embodiment.
【図２】第一実施例による遮光ネットの概略を示す説明
図である。FIG. 2 is an explanatory diagram showing an outline of a light shielding net according to the first embodiment.
【図３】第一実施例の説明図である。FIG. 3 is an explanatory diagram of the first embodiment.
【図４】第一実施例による遮光ネットの概略を示す説明
図である。FIG. 4 is an explanatory diagram showing an outline of a light shielding net according to the first embodiment.
【図５】第二実施例の説明図である。FIG. 5 is an explanatory diagram of a second embodiment.
【図６】第三実施例の説明図である。FIG. 6 is an explanatory diagram of a third embodiment.
【図７】第三実施例の他の変形例を示す説明図である。FIG. 7 is an explanatory diagram showing another modification of the third embodiment.
１ 縦糸 ２ 横糸 ３ 縦糸 ４ 横糸 ５ 編目 ６ 間隔列 ７，８ 繊維テープ Ａ，Ｂ 遮光ネット 1 Warp yarn 2 Weft yarn 3 Warp yarn 4 Weft yarn 5 Stitch 6 Spacing row 7,8 Fiber tape A, B Shading net
───────────────────────────────────────────────────── フロントページの続き (72)発明者 井上 昌人 愛知県豊川市牧野町野畔54番地の19 有限 会社井上商店内 (72)発明者 河村 充雅 東京都千代田区岩本町２丁目14番２号 丸 和バイオケミカル株式会社内 (72)発明者 三尾 彰 東京都千代田区岩本町２丁目14番２号 丸 和バイオケミカル株式会社内 (72)発明者 石井 清雄 東京都中央区日本橋小舟町４番１号 伊場 仙ビル 平成ポリマー株式会社内 (72)発明者 島村 敏和 東京都中央区日本橋小舟町４番１号 伊場 仙ビル 平成ポリマー株式会社内 (72)発明者 鈴木 英司 東京都中央区日本橋小舟町４番１号 伊場 仙ビル 平成ポリマー株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Masato Inoue Inoue Shoten Co., Ltd. at 54 Noro, Makino-cho, Toyokawa-shi, Aichi (72) Inventor Mitsumasa Kawamura 2-14-2 Iwamoto-cho, Chiyoda-ku, Tokyo Maruwa Biochemical Co., Ltd. (72) Inventor Akira Mio 2-14-2 Iwamotocho, Chiyoda-ku, Tokyo Maruwa Biochemical Co., Ltd. (72) Inventor Kiyoo Ishii 4 Nihonbashi Kobunecho, Chuo-ku, Tokyo No. 1 Inaba Sen Building Heisei Polymer Co., Ltd. (72) Inventor Toshikazu Shimamura No. 4 Nihonbashi Kobunecho, Chuo-ku, Tokyo Inaba Sen Building Heisei Polymer Co., Ltd. (72) Inventor Eiji Suzuki Nihonbashi, Chuo-ku, Tokyo Kobunecho No. 4-Iba Sen Building Heisei Polymer Co., Ltd.
Claims (15)
シュ紡糸法による不織布を細長に裁断して縦糸とし、他
の合成繊維を横糸とした編織物からなることを特徴とす
る遮光ネット。1. A light-shielding net comprising a knitted woven fabric in which a nonwoven fabric produced by high-density polyethylene spunbond flash spinning is cut into warp yarns and other synthetic fibers are weft yarns.
てなる請求項１の遮光ネット。2. The light-shielding net according to claim 1, wherein the warp yarns have an appropriate interval.
シュ紡糸法による不織布を細長に裁断して横糸とし、他
の合成繊維を縦糸とした編織物からなることを特徴とす
る遮光ネット。3. A light-shielding net comprising a knitted woven fabric in which a nonwoven fabric produced by a high-density polyethylene spunbond flash spinning method is cut into long and narrow yarns and wefts made of other synthetic fibers.
てなる請求項３の遮光ネット。4. The light-shielding net according to claim 3, wherein the weft threads have an appropriate interval.
シュ紡糸法による不織布を細長に裁断して縦糸及び横糸
とした編織物からなることを特徴とする遮光ネット。5. A light-shielding net comprising a knitted woven fabric obtained by cutting a non-woven fabric produced by a high-density polyethylene spunbond flash spinning method into elongated warp yarns and weft yarns.
ようにしてなる請求項５の遮光ネット。6. The light-shielding net according to claim 5, wherein the warp yarns and the weft yarns have an appropriate interval.
らなるネット本体の編目間隔内に、高密度ポリエチレン
スパンボンドフラッシュ紡糸法による不織布を細長に裁
断してなる繊維テープを縦方向に通してなることを特徴
とする遮光ネット。7. A fiber tape formed by cutting a nonwoven fabric produced by high-density polyethylene spunbond flash spinning in a slender manner is passed in the longitudinal direction within a stitch interval of a net body made of a knitted fabric having warp yarns and weft yarns as synthetic fibers. A light-shielding net characterized by
ており、編目が縦方向に平行となる請求項７の遮光ネッ
ト。8. The light-shielding net according to claim 7, wherein the stitches are arranged at regular intervals in the lateral direction, and the stitches are parallel in the longitudinal direction.
間隔列のうち、前記繊維テープを通さない間隔列を有し
てなる請求項８の遮光ネット。9. The light-shielding net according to claim 8, wherein among the spacing rows formed by the stitches parallel to the longitudinal direction, there are spacing rows that do not pass the fiber tape.
からなるネット本体の編目間隔内に、高密度ポリエチレ
ンスパンボンドフラッシュ紡糸法による不織布を細長に
裁断してなる繊維テープを横方向に通してなることを特
徴とする遮光ネット。10. A fiber tape formed by cutting a non-woven fabric obtained by high-density polyethylene spunbond flash spinning in a slender manner is passed in the transverse direction within a stitch interval of a net body made of a knitted woven fabric including warp yarns and weft yarns as synthetic fibers. A light-shielding net characterized by
っており、編目が横方向に平行となる請求項１０の遮光
ネット。11. The light-shielding net according to claim 10, wherein the stitches are arranged at regular intervals in the vertical direction, and the stitches are parallel in the horizontal direction.
る間隔列のうち、前記繊維テープを通さない間隔列を有
してなる請求項１１の遮光ネット。12. The light-shielding net according to claim 11, wherein among the spacing rows formed by the stitches parallel to the lateral direction, there are spacing rows that do not pass the fiber tape.
からなるネット本体の編目間隔内に、高密度ポリエチレ
ンスパンボンドフラッシュ紡糸法による不織布を細長に
裁断してなる繊維テープを縦方向及び横方向に通してな
ることを特徴とする遮光ネット。13. A fiber tape obtained by cutting a non-woven fabric by a high-density polyethylene spun bond flash spinning method into slenderness in the longitudinal direction and the transverse direction within a stitch interval of a net body made of a knitted fabric having warp yarns and weft yarns as synthetic fibers. A light-shielding net characterized by being threaded through.
定間隔となっており、編目が縦方向及び横方向に平行と
なる請求項１３の遮光ネット。14. The light-shielding net according to claim 13, wherein the stitches are arranged at regular intervals in the horizontal and vertical directions, and the stitches are parallel to each other in the vertical and horizontal directions.
よってできる間隔列のうち、前記繊維テープを通さない
間隔列を有してなる請求項１４の遮光ネット。15. The light-shielding net according to claim 14, wherein among the spacing rows formed by the stitches parallel to the longitudinal direction and the transverse direction, there are spacing rows that do not pass the fiber tape.