JPH0725170A - Heat transfer medium - Google Patents

Abstract

PURPOSE:To solve low multi-transferability and dullinitial start-up sensitivity of a laminate type heat transfer medium. CONSTITUTION:A heat transfer medium comprises two or more layers which are made by dispersing heat transferable dye in organic binder and laminated on a base, wherein the layers contain at least two or more heat transferable dyes of the same color tone, and a mixing ratio of the two or more dyes is differentiated at each layer or the upper layer contains heat transferable dye which is not provided in the lower layer.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は複写機、カラープリンタ
ー等に用いる熱転写体、殊に速度差モード法による多数
回記録（マルチ記録）に適する昇華型熱転写体に関わ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a thermal transfer material for use in a copying machine, a color printer or the like, and more particularly to a sublimation type thermal transfer material suitable for recording many times (multi-recording) by a speed difference mode method.

【０００２】[0002]

【従来の技術】近年、フルカラープリンターの需要が年
々増加している。このフルカラープリンターの記録方式
として電子写真法、インクジェット法、感熱転写方式が
あるが、この中で保守が容易、騒音がない等より感熱転
写法が多く用いられている。この感熱転写法は基体上
に、熱溶融物質中に着色剤を分散したインク層、または
樹脂結着剤中に昇華染料を分散したインクを設けてなる
熱転写記録媒体（いわゆるカラーインクシート）のイン
ク層面に受像シートを重ね、記録媒体側から、レーザー
やサーマルヘッド等の電気信号により制御された熱エネ
ルギーを印加してその部分のインクを受像シート上に熱
溶融転写または昇華移行させて画像を形成する記録方法
である。2. Description of the Related Art In recent years, the demand for full-color printers has been increasing year by year. There are electrophotographic methods, ink jet methods, and thermal transfer methods as recording methods for this full-color printer. Among them, thermal transfer methods are often used because they are easy to maintain and do not generate noise. This thermal transfer method is an ink of a thermal transfer recording medium (so-called color ink sheet) in which an ink layer in which a colorant is dispersed in a hot melt substance or an ink in which a sublimation dye is dispersed in a resin binder is provided on a substrate. An image receiving sheet is overlaid on the layer surface, and thermal energy controlled by an electric signal from a laser or a thermal head is applied from the recording medium side to transfer the ink in that portion onto the image receiving sheet by thermal fusion transfer or sublimation transfer to form an image. This is the recording method.

【０００３】そしてこの感熱転写記録法は使用される記
録媒体の種類によって熱溶融型と昇華転写型とに大別さ
れるが、特に後者は原理的にサーマルヘッド等からの熱
エネルギーに対して染料が単分子状で転写するため容易
に中間調が得られる利点をフルカラープリンターに最も
適した方式と考えられる。この昇華型熱転写記録法は、
１枚のフルカラー画像を作るのに、イエロー、マゼン
タ、シアン（ブラック）のインクシートを各１枚使用し
てインクシートごとに選択的な熱印字を行い、その後、
未使用部が残っていても破棄するため、ランニングコス
トが高いという欠点を有している。This heat-sensitive transfer recording method is roughly classified into a heat-melting type and a sublimation transfer type depending on the type of recording medium used. In particular, the latter is theoretically a dye for heat energy from a thermal head or the like. However, it is considered to be the most suitable method for a full-color printer because of the advantage that halftone can be easily obtained because it is transferred as a single molecule. This sublimation thermal transfer recording method
To make one full-color image, each one of the yellow, magenta, and cyan (black) ink sheets is used to perform selective thermal printing for each ink sheet, and then
Since the unused portion remains is discarded, the running cost is high.

【０００４】そこでこの欠点を改善するために、本発明
者は、特願昭６３−６２８６６号において、積層構造の
昇華型感熱転写体を提案し、「染料供給層と染料転写寄
与層を有する昇華型感熱型転写体において、染料供給層
と染料転写寄与層の染料放出能を染料供給層＞染料転写
寄与層とすること」により多数回記録でも濃度低下を来
さない方法を提案した。すなわち、染料供給層（下層）
及び染料転写寄与層（上層）を各々の処方にて同一付着
料になるように基体上にそれぞれ単独層として形成し、
その染料供給層及び染料転写寄与層を別々の受像層と重
ねあわせ、両者に同一の熱エネルギーを印加したとき、
それぞれの受像層への染料転写量が、 染料供給層＞染料転写寄与層 の関係にすることにより記録体のマルチ能を高めること
を可能にした。In order to solve this drawback, the present inventor proposed a sublimation type thermal transfer member having a laminated structure in Japanese Patent Application No. 63-62866, and said, "Sublimation having a dye supply layer and a dye transfer contributing layer. In a heat-sensitive transfer member, a method has been proposed in which the density of the dye supply layer and the dye transfer contributing layer is set to "dye supply layer> dye transfer contributing layer" so that the density does not decrease even if the recording is performed many times. That is, the dye supply layer (lower layer)
And the dye transfer contributing layer (upper layer) is formed as a single layer on the substrate so as to have the same adhesive in each formulation,
When the dye supplying layer and the dye transfer contributing layer are overlapped with separate image receiving layers and the same thermal energy is applied to both,
By making the amount of dye transferred to each image receiving layer such that the dye supplying layer> the dye transfer contributing layer, it is possible to enhance the multi-functionality of the recording material.

【０００５】[0005]

【発明が解決しようとする課題】本発明は積層タイプ転
写体（層間に染料濃度勾配及び／または染料拡散係数勾
配を設けた）が、マルチ転写能と初期立上り感度の低い
点を解決することを目的とする。DISCLOSURE OF THE INVENTION The present invention solves the problems of a multi-transfer type and a low initial rise sensitivity in a laminate type transfer body (in which a dye concentration gradient and / or a dye diffusion coefficient gradient are provided between layers). To aim.

【０００６】[0006]

【課題を解決するための手段】上記課題は、基体上に熱
移行性染料を有機結着剤中に分散させてなる層を２種以
上に積層した熱転写体において、各層とも２種以上の同
一色調の熱移行性染料を含有し、各層ごとに上記２種以
上の染料の配合比を異ならせること、特に、熱移行性染
料のうち、有機溶媒に対する溶解度が高いものの配合比
を下層のほうで少なくすること、及び基体上に熱移行性
染料を有機結着剤中に分散させてなる層を２層以上に積
層した熱転写体において、上層は下層にない熱移行性染
料を含有させることにより解決されることを見出した。Means for Solving the Problems The above-mentioned problem is a thermal transfer member in which two or more layers each having a heat transferable dye dispersed in an organic binder are laminated on a substrate. A heat transferable dye having a color tone is contained, and the compounding ratio of the above-mentioned two or more dyes is made different for each layer. Especially, among the heat transferable dyes, the compounding ratio of the one having a high solubility in an organic solvent is lower in the layer. To solve the problem by reducing the amount and by incorporating a heat transferable dye which is not in the lower layer in the upper layer in a thermal transfer body in which two or more layers in which the heat transferable dye is dispersed in an organic binder are laminated on the substrate. I was found to be done.

【０００７】すなわち、積層した層間の初期染料濃度勾
配を繰り返し使用した状態に近づけるため溶剤に対し溶
解度の高い染料を混合させることより初期立上がりを改
善し、また、繰り返し使用する場合下層から染料が供給
されることによりマルチ能が得られる。そのため上、下
層の染料の配合比を変化させることにより、供給しやす
くなり、マルチ能が向上する。特に下層に高溶解度の染
料の配合比を少なくあるいは配合しないことにより、高
溶解度の染料が初期に出すぎることによるマルチ能低下
の発生もなく良好なマルチ能が得られる。特に、同一色
調の熱移行性染料が高溶解度、即ち少なくとも２０℃に
おけるトルエン溶剤に対し溶解度５０ｇ／ｌ以上のもの
と、低溶解度、即ち溶解度５０ｇ／ｌ未満であるものと
を有することにより初期立上がりが優れ、かつマルチ能
が優れる熱転写体が得られる。That is, in order to bring the initial dye concentration gradient between the laminated layers closer to the state of repeated use, the initial rise is improved by mixing a dye having a high solubility in the solvent, and when repeatedly used, the dye is supplied from the lower layer. By doing so, multi-skill is obtained. Therefore, by changing the compounding ratio of the dyes in the upper and lower layers, supply becomes easier and mulching ability is improved. In particular, when the compounding ratio of the highly soluble dye is reduced or not mixed in the lower layer, good mulching ability is obtained without the occurrence of deterioration of mulching ability due to too much of the highly soluble dye in the initial stage. In particular, the heat transferable dye having the same color tone has a high solubility, that is, a solubility of 50 g / l or more in a toluene solvent at least at 20 ° C. and a low solubility, that is, a solubility of less than 50 g / l. It is possible to obtain a thermal transfer member having excellent heat transfer property and multi-function.

【０００８】又、基体上にこの基体側から順にそれぞれ
熱移行性染料を有機結着剤中に分散させてなる下層、上
層を積層した熱転写体において、さらにその上に低染着
性樹脂層を有することにより尾引き、ゴーストが発生し
ない良好なマルチ画像が得られる。更に、本発明の熱転
写体においては、上層と下層の組み合わせを２つ以上用
い、２種類以上の色調を出すこと、即ち２色以上の面順
次とすることも可能である。特に、基体上に少なくとも
３色別々の転写体を設けることにより初期立上りとマル
チ能良好なフルカラーが得られる。Further, in a thermal transfer member in which a lower layer and an upper layer are laminated on a substrate, in which a heat transferable dye is dispersed in an organic binder in this order from the substrate side, a low dyeing resin layer is further formed thereon. With this, a good multi-image without tailing or ghosting can be obtained. Further, in the thermal transfer member of the present invention, it is possible to use two or more combinations of the upper layer and the lower layer to produce two or more kinds of color tones, that is, two or more colors of frame sequential. In particular, by providing at least three different color transfer bodies on the substrate, it is possible to obtain a full color with good initial start-up and good multi-functionality.

【０００９】昇華型熱転写体による熱転写はサーマルヘ
ッドによって行っても良いが、支持体層及び／またはイ
ンク層を通電によりジュール熱を発生するように調整
し、通電転写によって行っても良い。また、支持体とし
てレーザー光を吸収し発熱する材料を選択することによ
ってレーザー転写法を利用することも可能である。The thermal transfer by the sublimation type thermal transfer member may be carried out by a thermal head, but it may also be carried out by adjusting the support layer and / or the ink layer so that Joule heat is generated by energization and by energization transfer. It is also possible to use the laser transfer method by selecting a material that absorbs laser light and generates heat as a support.

【００１０】本発明者の知見によれば、インク層中にお
ける染料の拡散はフィックの法則、すなわち、断面積ｑ
をｄｔ時間に通過した染料量ｄｎは、拡散方向における
染料の濃度勾配をｄｃ／ｄｘとし、Ｄを熱印加されたと
きのインク層中の各部位の平均拡散係数としたとき、 ｄｎ／ｄｔ＝−Ｄｑ ｄｃ／ｄｘ の関係が適用される。According to the knowledge of the present inventor, the diffusion of the dye in the ink layer is Fick's law, that is, the cross-sectional area q
The amount of dye dn that has passed through in the dt time is dn / dt =, where Dc is the concentration gradient of the dye in the diffusion direction and D is the average diffusion coefficient of each part in the ink layer when heat is applied. The -Dq dc / dx relationship applies.

【００１１】そこで、下層から上層に昇華性染料が拡散
供給されやすくするための手段としては、 １）染料濃度に関して、染料供給層＞転写寄与層の関係
とさせること、及び／または ２）それぞれの層中における拡散係数に関して、染料供
給層＞転写寄与層の関係とさせる手段がある。Therefore, as means for facilitating the diffusive supply of the sublimable dye from the lower layer to the upper layer, 1) regarding the dye concentration, the relationship of dye supplying layer> transfer contributing layer and / or 2) Regarding the diffusion coefficient in the layer, there is a means for making the relationship of dye supply layer> transfer contributing layer.

【００１２】本発明の上層及び低染着性樹脂層の厚さ
は、一般には０．０５〜５μｍ、好ましくは０．１〜２
μである。また下層の厚さは一般的には０．１〜２０μ
ｍ、好ましくは０．５〜１０μｍである。本発明の上層
及び下層に使用される昇華染料、結着剤等は公知のもの
が使用できる。The thickness of the upper layer and the low-dyeing resin layer of the present invention is generally 0.05 to 5 μm, preferably 0.1 to 2
is μ. The lower layer generally has a thickness of 0.1 to 20 μm.
m, preferably 0.5 to 10 μm. Known sublimation dyes, binders and the like can be used in the upper and lower layers of the present invention.

【００１３】昇華性染料としては６０℃以上で昇華ある
いは気化する染料であり、主に分散染料、油溶性染料な
ど熱転写捺染で使用されるものであれば良く、例えば
Ｃ．Ｉ．ディスパースイエローの１，３，８，９，１
６，４１，５４，６０，７７，１１６など、Ｃ．Ｉ．デ
ィスパースレッドの１，４，６，１１，１５，１７，５
５，５９，６０，７３，８３など、Ｃ．Ｉ．ディスパー
スブルーの３，１４，１９，２６，５６，６０，６４，
７２，９９，１０８など、Ｃ．Ｉ．ソルベントイエロー
の７７，１１６など、Ｃ．Ｉ．ソルベントレッドの２
３，２５，２７など、Ｃ．Ｉ．ソルベントブルーの３
６，８３，１０５などが挙げられ、これらの染料の一種
で使用可能であるが、数種混合しても使用可能である。The sublimable dye is a dye that sublimes or vaporizes at 60 ° C. or higher, and may be any dye mainly used in thermal transfer printing such as disperse dyes and oil-soluble dyes. I. Disperse Yellow 1,3,8,9,1
6,41,54,60,77,116, etc., C.I. I. 1,4,6,11,15,17,5 of Disperse Red
5,59,60,73,83, C.I. I. Disperse Blue 3,14,19,26,56,60,64,
72, 99, 108, etc., C.I. I. Solvent Yellow 77, 116, C.I. I. Solvent Red 2
3, 25, 27, etc., C.I. I. Solvent Blue 3
6, 83, 105 and the like can be used, and one of these dyes can be used, but a mixture of several dyes can also be used.

【００１４】上層及び下層に使用される結着剤には熱可
塑性又は熱硬化性樹脂が用いられ、そのうち比較的高ガ
ラス転移点または高軟化性を有する樹脂としては、例え
ば塩化ビニル樹脂、酢酸ビニル樹脂、ポリアミド、ポリ
エチレン、ポリカーボネート、ポリスチレン、ポリプロ
ピレン、アクリル樹脂、フェノール樹脂、ポリエステ
ル、ポリウレタン、エポキシ樹脂、シリコーン樹脂、フ
ッ素樹脂、ブチラール樹脂、メラミン樹脂、天然ゴム、
合成ゴム、ポリビニルアルコール、セルロース樹脂等が
挙げられる。これらの樹脂は一種で使用できるが、数種
を混合するか、さらに共重合体を使用しても良い。A thermoplastic or thermosetting resin is used for the binder used in the upper layer and the lower layer, and as the resin having a relatively high glass transition point or a high softening property, for example, a vinyl chloride resin or vinyl acetate is used. Resin, polyamide, polyethylene, polycarbonate, polystyrene, polypropylene, acrylic resin, phenol resin, polyester, polyurethane, epoxy resin, silicone resin, fluororesin, butyral resin, melamine resin, natural rubber,
Examples thereof include synthetic rubber, polyvinyl alcohol, cellulose resin and the like. These resins can be used alone, but several kinds may be mixed or a copolymer may be used.

【００１５】さらに上層と下層との間においてガラス転
移又は軟化温度に対し差をつける場合、ガラス転移温度
０℃以下、又は軟化温度６０℃以下の樹脂又は天然、合
成ゴムが好ましく、具体的には、ポリエチレンオキサイ
ド（アルコックスＥ−３０，４５，Ｒ−１５０，４０
０，１０００明成化学工業）；カプロラクトンポリオー
ル（プラクセルＨ−１，４，７ダイセル化学工業）等が
実用上有用であり、また先に記した熱可塑性又は熱硬化
性樹脂と上記一種又は数種と混合した形で用いるのが好
ましい。When there is a difference in glass transition or softening temperature between the upper layer and the lower layer, a resin having a glass transition temperature of 0 ° C. or lower, or a softening temperature of 60 ° C. or lower, or a natural or synthetic rubber is preferable. , Polyethylene oxide (ALCOX E-30, 45, R-150, 40
0,1000 Meisei Chemical Industry Co., Ltd.); caprolactone polyol (Placcel H-1,4,7 Daicel Chemical Industry Co., Ltd.) and the like are practically useful, and the thermoplastic or thermosetting resin described above and one or more of the above It is preferably used in a mixed form.

【００１６】上層の染料濃度は通常、５〜８０％、好ま
しくは１０〜６０％程度である。また下層の染料濃度に
ついては、５〜８０％の染料濃度が好ましいが上層と下
層との間に染料濃度勾配をつける場合、上層染料濃度に
たいし、１．１〜５倍、好ましくは１．５〜３倍が望ま
しい。基体シートとしてはコンデンサーペーパー、ポリ
エステルフィルム、ポリスチレンフィルム、ポリサルフ
ォンフィルム、ポリイミドフィルム、ポリアラミドフィ
ルム等のフィルムが使用され基体シートと下層との間に
は必要に応じて従来の接着層などを設けていても良く、
又、基体シートの裏面には必要に応じて従来慣用の耐熱
性潤滑層を設けても良い。The dye concentration in the upper layer is usually 5 to 80%, preferably about 10 to 60%. Further, the dye concentration of the lower layer is preferably 5 to 80%, but when a dye concentration gradient is provided between the upper layer and the lower layer, the upper layer dye concentration is 1.1 to 5 times, preferably 1. 5 to 3 times is desirable. As the base sheet, films such as condenser paper, polyester film, polystyrene film, polysulfone film, polyimide film and polyaramid film are used, and a conventional adhesive layer or the like is provided between the base sheet and the lower layer as needed. Good,
If necessary, a conventional heat resistant lubricating layer may be provided on the back surface of the base sheet.

【００１７】今まで染料層を２層に分けた例について述
べてきたが、適切な染料転写量の差を生じさせ本発明が
意図する機能分離ができれば染料層を２層以上の多層に
することも可能である。以上の説明は感熱ヘッドを用い
ての記録方法により説明したが、本発明の転写媒体は記
録エネルギー以外の方法によって記録する記録方法、例
えば、熱印版、レーザー光、あるいは支持体等媒体中で
発生するジュール熱による方法に対しても用いることが
できる。このうち、媒体中で発生するジュール熱を用い
る通電感熱転写法が最も良く知られ、例えばＵＳＰ４，
１０３，０６６、特開昭５７−１４０６０、特開昭５７
−１１０８０あるいは特開昭５９−９０９６号公報等の
多くの文献に記載されている。Up to now, an example in which the dye layer is divided into two layers has been described. However, if an appropriate difference in the dye transfer amount is generated and the function separation intended by the present invention can be achieved, the dye layer should be made into a multilayer of two or more layers. Is also possible. Although the above description has been given of the recording method using a thermal head, the transfer medium of the present invention is a recording method of recording by a method other than recording energy, for example, in a medium such as a hot printing plate, a laser beam, or a support. It can also be used for a method using generated Joule heat. Of these, the current-carrying thermal transfer method using Joule heat generated in the medium is the most well known.
103, 066, JP-A-57-14060, JP-A-57.
It is described in many documents such as -11080 or JP-A-59-9096.

【００１８】この通電転写法に用いる場合には支持体と
して比較的耐熱性の良いポリエステル、ポリカーボネー
ト、トリアセチルセルロース、ナイロン、ポリイミド、
芳香族ポリアミド等の樹脂にアルミニウム、銅、鉄、
錫、亜鉛、ニッケル、モリブデン、銀等の金属粉及び／
又はカーボンブラック等の導電性粉末を分散させて抵抗
値を絶縁体と良導体との中間に調整した支持体、又これ
らの支持体に前述のような導電性金属を蒸着又はスパッ
タリングさせた支持体を用いれば良い。これらの支持体
の厚さはジュール熱の伝導効率を考慮すると、２〜１５
ミクロン程度であることが望ましい。When used in this electric transfer method, as a support, polyester, polycarbonate, triacetyl cellulose, nylon, polyimide, which has relatively high heat resistance,
Aluminium, copper, iron, resin, such as aromatic polyamide
Metal powder such as tin, zinc, nickel, molybdenum, silver and /
Alternatively, a support in which a conductive powder such as carbon black is dispersed to adjust the resistance value to an intermediate value between an insulator and a good conductor, or a support in which a conductive metal as described above is vapor-deposited or sputtered on the support is used. You can use it. The thickness of these supports is 2 to 15 considering the Joule heat conduction efficiency.
It is desirable that the size is about micron.

【００１９】又、レーザー光転写法に用いる場合には、
支持体としてレーザー光を吸収し発熱する材質を選べば
良い。例えば従来の熱転写用フィルムにカーボン等の光
吸収変換剤を含有させるか、又は吸収層を支持体の表、
裏面に形成したものが使用される。When used in the laser light transfer method,
A material that absorbs laser light and generates heat may be selected as the support. For example, a conventional thermal transfer film contains a light absorption conversion agent such as carbon, or the absorption layer is a surface of a support,
The one formed on the back surface is used.

【００２０】[0020]

〔中間接着層〕[Intermediate adhesive layer]

ポリビニルブチラール樹脂ＢＸ−１（積水化学社製） １０部 ジイソシアネート コロネートＬ（日本ポリウレタン社製） ５部 溶剤 トルエン ９５部 メチルエチルケトン ９５部 〔下層〕 ポリビニルブチラール樹脂ＢＸ−１ ７部 ポリエチレンオキサイド アルコックスＲ４００（明成化学製） ３部 ジイソシアネート コロネートＬ ３部 熱移行性染料 ＨＳＯ−１４４（三井東圧染料） ２１部 Ｆｒｏｎ Ｂｒｉｌｉａｎｔ Ｂｌｕｅ ＳＲ ９部 溶剤 エチルアルコール １７０部 ブチルアルコール ２０部 〔上層〕 ポリビニルブチラール樹脂ＢＸ−１ １０部 ジイソシアネート コロネートＬ ３部 熱移行性染料 ＨＳＯ−１４４ １６部 Ｆｒｏｎ Ｂｒｉｌｉａｎｔ Ｂｌｕｅ ＳＲ ４部 溶剤 トルエン ９５部 メチルエチルケトン ９５部 以上用意した液を用い、厚さ１μｍのシリコーン樹脂系
耐熱層を有する厚さ６μｍの芳香族ポリアミドフィルム
上にワイヤーバーを用い、厚さ１．０μｍの中間接着
層、次に下層を膜厚４．５μｍになるように塗布し、さ
らにその上に上層を膜厚１．０μｍになるよう塗布し、
インク層を形成し６０℃、時間熱硬化させて実施例１の
記録体を作成した。Polyvinyl butyral resin BX-1 (manufactured by Sekisui Chemical Co., Ltd.) 10 parts Diisocyanate Coronate L (manufactured by Nippon Polyurethane Company) 5 parts Solvent Toluene 95 parts Methyl ethyl ketone 95 parts [Lower layer] Polyvinyl butyral resin BX-1 7 parts Polyethylene oxide Alcox R400 (Meisei) Chemicals) 3 parts Diisocyanate Coronate L 3 parts Heat transfer dye HSO-144 (Mitsui Toatsu Dye) 21 parts Fron Brilliant Blue SR 9 parts Solvent ethyl alcohol 170 parts Butyl alcohol 20 parts [Upper layer] Polyvinyl butyral resin BX-1 10 Part Diisocyanate Coronate L 3 parts Heat transfer dye HSO-144 16 parts Fron Brilliant Blue SR 4 parts Solvent Toluene 95 parts Methyl ethyl ketone 95 parts Liquid prepared above Using a wire bar on a 6 μm-thick aromatic polyamide film having a 1 μm-thick silicone resin-based heat-resistant layer, a 1.0 μm-thick intermediate adhesive layer, and then a lower layer to a thickness of 4.5 μm , And then apply an upper layer on it to a film thickness of 1.0 μm,
An ink layer was formed and heat-cured at 60 ° C. for an hour to prepare the recording material of Example 1.

【００２１】実施例：２，３及び比較例：１，２ 実施例１において熱移行性染料の種類と部数を表１に示
すように変えて実施例２，３、比較例１，２の記録体を
作成した。Examples: 2, 3 and Comparative Examples: 1, 2 Recording of Examples 2, 3 and Comparative Examples 1 and 2 by changing the type and number of parts of the heat transferable dye in Example 1 as shown in Table 1. Created the body.

【００２２】[0022]

【表１】 [Table 1]

【００２３】以上の実施例１，２，３及び比較例１，２
の記録体と組合せるために、下記受像層液をワイヤーバ
ーを用いて厚さ約１５０μｍの合成紙（ユポＦＰＧ−１
５０；王子油化合成紙性）上に塗布し、乾燥温度７５℃
で１分間乾燥して厚さ約５μｍの染料受像層を形成させ
た後、さらに８０℃で３時間保存して硬化させ試験に用
いる受像体を作成した。The above Examples 1, 2, 3 and Comparative Examples 1, 2
In order to combine it with the recording material of No. 1, the following image receiving layer liquid was applied using a wire bar to a synthetic paper (Yupo FPG-1) having a thickness of about 150 μm.
50; Oji Okaka Synthetic paper) and dried at 75 ° C
Was dried for 1 minute to form a dye image-receiving layer having a thickness of about 5 μm, and then the dye image-receiving layer was further stored at 80 ° C. for 3 hours and cured to prepare an image receptor used in the test.

【００２４】 〔受像層液〕 塩化ビニル／酢酸ビニル／ビニルアルコール共重合体ＶＡＧＨ （ユニオンカーバイド社製） １０部 ジイソシアネート コロネートＬ（日本ポリウレタン社製） ５部 アミノ変性シリコーン ＳＦ８４１７（東レダウコーニング社 製） ０．５部 エポキシ変性シリコーン ＳＦ８４１１（東レダウコーニング 社製） ０．５部 溶剤 トルエン ４０部 メチルエチルケトン ４０部 上記組成の混合物を充分混合分散させ、染料受像層用塗
液を調整した。用意した実施例１，２，３及び比較例
１，２の記録体及び受像体を用い、下記条件で速度差モ
ード法により画像を形成させた。[Image-receiving layer liquid] Vinyl chloride / vinyl acetate / vinyl alcohol copolymer VAGH (manufactured by Union Carbide) 10 parts Diisocyanate Coronate L (manufactured by Nippon Polyurethane Co.) 5 parts Amino-modified silicone SF8417 (manufactured by Toray Dow Corning) 0.5 part Epoxy-modified silicone SF8411 (manufactured by Toray Dow Corning Co., Ltd.) 0.5 part Solvent Toluene 40 parts Methyl ethyl ketone 40 parts A mixture of the above composition was sufficiently mixed and dispersed to prepare a dye image-receiving layer coating liquid. An image was formed by the speed difference mode method under the following conditions using the prepared recording bodies and image receiving bodies of Examples 1, 2, 3 and Comparative Examples 1, 2.

【００２５】印字装置の条件 サーマルヘッド解像度；１２ドット／ｍｍ 印加エネルギー ；０．６４ｍｊ／ドット 印加電力 ；０．１６Ｗ／ドット 記録時の送り速度 ７倍速 受像体シート ８．４ｍｍ／ｓｅｃ 記録体インクシート １．２ｍｍ／ｓｅｃ １４倍速 受像体シート ８．４ｍｍ／ｓｅｃ 記録体インクシート ０．６ｍｍ／ｓｅｃ 初期立上がりは等速と７倍速の画像を比較し、マルチ能
は７倍速と１４倍速について比較した。その結果を表２
に示す。ここで、○…良好，△…やや良，×…不良を示
す。Printing device conditions Thermal head resolution: 12 dots / mm Applied energy: 0.64 mj / dot Applied power: 0.16 W / dot Feed speed during recording 7 times speed Image receptor sheet 8.4 mm / sec Recording ink sheet 1.2 mm / sec 14 × speed image receptor sheet 8.4 mm / sec Recording medium ink sheet 0.6 mm / sec Initial rising speed was compared between images at constant velocity and 7 × speed, and multi-function was compared at 7 × speed and 14 × speed. The results are shown in Table 2.
Shown in. Here, ◯ ... good, Δ ... somewhat good, × ... bad.

【００２６】[0026]

【表２】 [Table 2]

【００２７】実施例：４ 厚さ１μｍのシリコーン樹脂系耐熱層を有する厚さ６μ
ｍの芳香族ポリアミドフィルム上にワイヤーバーを用
い、厚さ１．０μｍの中間接着層、次にイエロー、マゼ
ンタ、シアンの３色面順次のインク層を形成し６０℃、
２４時間熱硬化させて記録体を作成した。なお下層はメ
ッシュ数１５０メッシュ／インチ、上層はメッシュ数３
００メッシュ／インチのスクリーン版を用いてスクリー
ン印刷塗工より作成した。Example 4: 4 μm thick having a 1 μm thick silicone resin heat-resistant layer
Using a wire bar on the aromatic polyamide film having a thickness of m, an intermediate adhesive layer having a thickness of 1.0 μm and then an ink layer having three color planes of yellow, magenta and cyan are formed at 60 ° C.
A recording body was prepared by heat curing for 24 hours. The lower layer has 150 mesh / inch, and the upper layer has 3 mesh.
It was prepared by screen printing coating using a screen plate of 00 mesh / inch.

【００２８】 〔中間接着層〕 ポリビニルブチラール樹脂ＢＸ−１（積水化学製） １０重量部 ジイソシアネート コロネートＬ（日本ポリウレタン製） ５ 溶剤 トルエン ９５ メチルエチルケトン ９５ 〔下層〕 ポリビニルブチラール樹脂ＢＸ−１ ７ ポリエチレンオキサイド樹脂Ｒ−４００（明成化学） ３ ジイソシアネート コロネートＬ ３ 熱移行性染料 ３０ 溶剤 ブチルアルコール １３３ 〔上層〕 ポリビニルブチラール樹脂ＢＸ−１ １０ ジイソシアネート コロネートＬ ５ 熱移行性染料 ２０ 滑剤 エポキシ変性シリコンオイルＳＦ８４１１（東レダ ウコーニング） １．５ アルコール変性シリコンオイルＳＦ８４２７（東レ ダウコーニング） １．５ 溶剤 シクロヘキサノン １３３[Intermediate Adhesive Layer] Polyvinyl butyral resin BX-1 (manufactured by Sekisui Chemical Co., Ltd.) 10 parts by weight diisocyanate Coronate L (manufactured by Nippon Polyurethane) 5 solvent toluene 95 methyl ethyl ketone 95 [lower layer] polyvinyl butyral resin BX-17 polyethylene oxide resin R -400 (Meisei Kagaku) 3 Diisocyanate Coronate L 3 Heat transfer dye 30 Solvent Butyl alcohol 133 [Upper layer] Polyvinyl butyral resin BX-1 10 Diisocyanate Coronate L 5 Heat transfer dye 20 Lubricant Epoxy modified silicone oil SF8411 (Toray Dow Corning) ) 1.5 Alcohol modified silicone oil SF8427 (Toray Dow Corning) 1.5 Solvent Cyclohexanone 133

【００２９】[0029]

【表３】 [Table 3]

【００３０】得られた実施例４、比較例３を実施例１〜
３、比較例１，２と同様にしてフルカラー画像を形成し
た結果、実施例４では、等速、７倍速、１４倍速で良好
なフルカラー画像が得られた。比較例３では等速で画像
濃度が低いため良好なフルカラー画像が得られなかっ
た。The obtained Example 4 and Comparative Example 3 were used in Examples 1 to 1.
3. As a result of forming a full-color image in the same manner as in Comparative Examples 1 and 2, in Example 4, a good full-color image was obtained at constant speed, 7 times speed, and 14 times speed. In Comparative Example 3, a good full-color image could not be obtained because the image density was low at a constant speed.

【００３１】[0031]

【発明の効果】以上説明したように、本発明の熱転写体
においては、各層とも２種以上の同一色調の熱移行性染
料を含有し、各層ごとに上記２種以上の染料の配合比を
異ならせることにより、マルチ性に優れ、初期立上り良
好な熱転写体が得られる。また、熱移行性染料のうち、
有機溶媒に対する溶解度が高いものの配合比を下層のほ
うで少なくすることにより、上記改善効果が顕著であ
る。更に、熱転写体を２色以上の面順次とすれば、マル
チ性に優れ、初期立上がり良好なフルカラー画像が得ら
れる。As described above, in the thermal transfer member of the present invention, each layer contains two or more kinds of heat transferable dyes having the same color tone, and if the mixing ratio of the above two or more kinds of dyes is different for each layer. By doing so, it is possible to obtain a thermal transfer member having excellent multiplicity and good initial rising. Also, among the heat transfer dyes,
Although the solubility in the organic solvent is high, the improvement effect is remarkable by decreasing the compounding ratio in the lower layer. Further, when the thermal transfer member is a frame sequential of two or more colors, a full-color image having excellent multiplicity and good initial rise can be obtained.

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】 基体上に熱移行性染料を有機結着剤中に
分散させてなる層を２種以上に積層した熱転写体におい
て、各層とも２種以上の同一色調の熱移行性染料を含有
し、各層ごとに上記２種以上の染料の配合比が異なるこ
とを特徴とする熱転写体。1. A thermal transfer member comprising two or more layers in which a heat transferable dye is dispersed in an organic binder on a substrate, and each layer contains two or more heat transferable dyes having the same color tone. A thermal transfer member, wherein the compounding ratio of the above-mentioned two or more dyes is different for each layer. 【請求項２】 熱移行性染料のうち、有機溶媒に対する
溶解度が高いものの配合比が下層のほうが少ないことを
特徴とする請求項１記載の熱転写体。2. The thermal transfer member according to claim 1, wherein among the heat transferable dyes, those having a high solubility in an organic solvent have a lower compounding ratio in the lower layer. 【請求項３】 基体上に熱移行性染料を有機結着剤中に
分散させてなる層を２層以上に積層した熱転写体におい
て、上層は下層にない熱移行性染料を有することを特徴
とする熱転写体。3. A thermal transfer member comprising two or more layers each having a heat transferable dye dispersed in an organic binder on a substrate, wherein the upper layer has a heat transferable dye not present in the lower layer. A thermal transfer material.