JPH0718578A - Article for treating fiber product - Google Patents

Abstract

PURPOSE:To obtain an article for treating fiber product capable of imparting excellent softness and antistatic properties to fiber products, especially chemical fibers by uniformly transferring a softening component into clothes, etc. CONSTITUTION:This article for fiber product treatment used in drying process of washing is obtained by carrying a softening agent composition containing 10-60wt.% of (A) a cationic surfactant having two long-chain hydrocarbon groups and at least whose one group among these two groups is interrupted with an ester group and (B) a cationic surfactant having one long-chain hydrocarbon group in a weight ratio of the components A/B of (95/5) to (50/50) and 40-90wt.% of (C) a sorbitan fatty acid ester and (D) a fatty acid in a weight ratio of the components C/D of (10/90) to (90/10), and having <50wt.% sorbitan fatty acid ester content therein on a substrate such as nonwoven fabric or sponge.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、乾燥機中で衣料、タオ
ル等の繊維製品と接触した場合に、基体上に担持された
柔軟剤組成物をこれらに移し、繊維製品、特に化学繊維
に優れた柔軟性と帯電防止効果を付与できる繊維製品処
理用物品に関するものである。FIELD OF THE INVENTION The present invention transfers a softening agent composition carried on a substrate to a textile product, especially a chemical fiber, when the softening agent composition is contacted with the textile product such as clothes and towels in a dryer. The present invention relates to an article for treating a textile product, which can impart excellent flexibility and antistatic effect.

【０００２】[0002]

【従来の技術】洗濯物を衣類乾燥機を用いて乾燥する際
に、洗濯物に柔軟性と帯電防止性を付与するいわゆる乾
燥機用柔軟剤としては、種々のものが提案されている。
例えば特開昭５８−１７４６７９号公報にはカチオン性
界面活性剤、脂肪酸アミド及び脂肪酸エステルを吸収性
材料に含浸させたものが開示され、特開昭５９−４７４
７７号公報にはカチオン性界面活性剤、脂肪酸アミド及
び脂肪酸を吸収性材料に含浸させたものが開示されてい
る。さらに特開昭５２−１２４９９７号公報にはカチオ
ン性界面活性剤、ソルビタンエステルを基剤に含浸させ
たものが、特開昭６２−４５７８０号公報にはカチオン
性界面活性剤、ソルビタン脂肪酸エステル等を基剤に含
浸させたものが開示され、特公平０１−２９９０７号公
報には、ジアルキル／モノアルキルの混合４級塩を含む
固体共融粒状布類柔軟化組成物が、また、特開昭５９−
１１２０６９号公報にはジアルキル／モノアルキルの混
合４級塩、ノニオン性界面活性剤（５０〜９０％）を不
織布に担持させたものが開示されている。2. Description of the Related Art There have been proposed various so-called dryer softeners which impart flexibility and antistatic properties to laundry when it is dried using a clothes dryer.
For example, JP-A-58-174679 discloses an absorbent material impregnated with a cationic surfactant, a fatty acid amide and a fatty acid ester, and JP-A-59-474.
Japanese Patent Publication No. 77 discloses an absorbent material impregnated with a cationic surfactant, a fatty acid amide and a fatty acid. Further, JP-A-52-124997 discloses a base material impregnated with a cationic surfactant and sorbitan ester, and JP-A-62-45780 discloses a cationic surfactant, sorbitan fatty acid ester and the like. Japanese Patent Publication No. 01-29907 discloses a solid eutectic granular fabric softening composition containing a mixed quaternary salt of dialkyl / monoalkyl, and JP-A-59-29907. −
Japanese Patent No. 112069 discloses a non-woven fabric on which a mixed quaternary salt of dialkyl / monoalkyl and a nonionic surfactant (50 to 90%) are supported.

【０００３】しかしながら、これらの乾燥機用柔軟剤で
は、ジアルキルカチオン型柔軟剤の配合量が多いにもか
かわらず、液体柔軟剤といわれるリンスサイクルで使用
するものと比較すると、ジアルキルカチオン型柔軟剤の
衣料への付着が不均一である。従つて、ジアルキルカチ
オン型柔軟剤の均一付着を目的とする衣料へのシミ防止
が十分達成されているとはいえないのが現状である。そ
こで、特開平０３−２９４５７５号公報のようにジアル
キルカチオン型柔軟剤を更に有効かつ均一に付着させる
方法が開示されている。しかしながら、これらの乾燥機
用柔軟剤に用いられているカチオン界面活性剤は主とし
てジ長鎖アルキルジ短鎖アルキル第４級アンモニウム塩
を主成分としており、このものは生分解性に劣るために
河川の汚染の原因の一つとされている。そのため、長鎖
アルキルエステル基を有する第４級アンモニウム塩を用
いて生分解性が良好な乾燥機用柔軟剤の開発が望まれて
いる。However, in these softeners for dryers, although the amount of the dialkyl cation type softener is large, compared with the liquid softener used in the rinse cycle, it is Non-uniform adherence to clothing. Therefore, at present, it cannot be said that the prevention of stains on clothes for the purpose of uniformly attaching the dialkyl cation type softener is sufficiently achieved. Therefore, a method of more effectively and uniformly adhering a dialkyl cation type softening agent as disclosed in JP-A 03-294575 is disclosed. However, the cationic surfactants used in these dryer softeners are mainly composed of di-long-chain alkyldi-short-chain alkyl quaternary ammonium salts, which are inferior in biodegradability. It is one of the causes of pollution. Therefore, it has been desired to develop a softener for a dryer having good biodegradability using a quaternary ammonium salt having a long-chain alkyl ester group.

【０００４】[0004]

【発明が解決しようとする課題】本発明は、生分解性が
良好な長鎖アルキルエステル基を有する第４級アンモニ
ウム塩を用いた乾燥機用柔軟剤に関し、繊維製品、特に
化学繊維に優れた柔軟性と帯電防止効果を付与できる繊
維製品処理用物品を提供することを目的とする。DISCLOSURE OF THE INVENTION The present invention relates to a dryer softener using a quaternary ammonium salt having a long-chain alkyl ester group having good biodegradability, and is excellent in textile products, particularly in chemical fibers. An object is to provide an article for treating a textile product, which can impart flexibility and an antistatic effect.

【０００５】[0005]

【課題を解決するための手段】本発明の繊維製品処理用
物品は、（Ａ）２つの長鎖炭化水素基を有し、そのうち
少なくとも１つはエステル基で中断されているカチオン
性界面活性剤と（Ｂ）１つの長鎖炭化水素基を有するカ
チオン性界面活性剤を（Ａ）／（Ｂ）の重量比が９５／
５〜５０／５０で１０〜６０重量％；（Ｃ）ソルビタン
脂肪酸エステル及び（Ｄ）脂肪酸を（Ｃ）／（Ｄ）の重
量比が１０／９０〜９０／１０で４０〜９０重量％含有
し；かつ柔軟剤組成物中のソルビタン脂肪酸エステルの
含有量が５０重量％を越えない柔軟剤組成物を、基体に
担持させたことを特徴とするものであり、洗濯の乾燥工
程で使用される。The article for treating textile products of the present invention comprises (A) a cationic surfactant having two long-chain hydrocarbon groups, at least one of which is interrupted by an ester group. And (B) a cationic surfactant having one long-chain hydrocarbon group (A) / (B) in a weight ratio of 95 /
5 to 50/50 10 to 60% by weight; (C) sorbitan fatty acid ester and (D) fatty acid (C) / (D) in a weight ratio of 10/90 to 90/10 and 40 to 90% by weight. And a softener composition having a sorbitan fatty acid ester content of not more than 50% by weight supported on a substrate, which is used in a laundry drying step.

【０００６】[0006]

【発明の実施態様】本発明の（Ａ）成分としては、２つ
の長鎖炭化水素基を有し、そのうち少なくとも１つはエ
ステル基で中断されているカチオン性界面活性剤が用い
られる。（Ａ）成分のカチオン性界面活性剤の具体例と
しては、以下の化１、化２、化３の一般式（Ｉ〜VII）
に示したものを例示できる。BEST MODE FOR CARRYING OUT THE INVENTION As the component (A) of the present invention, a cationic surfactant having two long-chain hydrocarbon groups, at least one of which is interrupted by an ester group, is used. Specific examples of the cationic surfactant as the component (A) include the following general formulas (I to VII) of the following chemical formulas 1, 2 and 3.
The examples shown in can be exemplified.

【０００７】[0007]

【化１】 [Chemical 1]

【０００８】[0008]

【化２】 [Chemical 2]

【０００９】[0009]

【化３】 [Chemical 3]

【００１０】式中、Ｒ₁、Ｒ₂は、それぞれ炭素数１１〜
２３、好ましくは１５〜２１のアルキル基又はアルケニ
ル基であり、例えばＲ₁−ＣＯ、Ｒ₂−ＣＯで示される基
は通常ステアリン酸、パルミチン酸等の飽和高級脂肪
酸、オレイン酸、エライジン酸、リノール酸、リノレイ
ン酸等の不飽和高級脂肪酸、牛脂、豚脂、パーム油、パ
ーム核油、大豆油、サフラワー油、ヒマワリ油、オリー
ブ油等の天然油脂を分解、精製して得られる脂肪酸から
由来するものであるが、この中でも特にオレイン酸、ス
テアリン酸、牛脂脂肪酸、硬化牛脂脂肪酸、パーム油脂
脂肪酸、硬化パーム油脂肪酸、パーム核油脂肪酸、硬化
パーム核油脂肪酸が好適である。尚、不飽和高級脂肪酸
としては、立体異性体がシス体又はトランス体であつて
も、あるいは両者の混合物であつてもよいが、特にシス
体／トランス体の比率が２５／７５〜１００／０（重量
％）であることが好ましい。またＲ₁及びＲ₂は、同一で
も異なつていてもよい。In the formula, R ₁ and R ₂ each have 11 to 11 carbon atoms.
23, preferably 15 to 21 alkyl or alkenyl groups, for example, the groups represented by R ₁ —CO and R ₂ —CO are usually saturated higher fatty acids such as stearic acid and palmitic acid, oleic acid, elaidic acid and linole. Acids, unsaturated higher fatty acids such as linoleic acid, beef tallow, lard, palm oil, palm kernel oil, soybean oil, safflower oil, sunflower oil, olive oil and other natural fats and oils are derived from fatty acids obtained by decomposition and purification Of these, oleic acid, stearic acid, tallow fatty acid, hardened beef tallow fatty acid, palm fat and oil fatty acid, hardened palm oil fatty acid, palm kernel oil fatty acid, and hardened palm kernel oil fatty acid are particularly preferred. Incidentally, as the unsaturated higher fatty acid, the stereoisomer may be a cis isomer or a trans isomer, or a mixture of the two, and in particular, the cis isomer / trans isomer ratio is 25/75 to 100/0. (% By weight) is preferable. R ₁ and R ₂ may be the same or different.

【００１１】Ｒ₃、Ｒ₄、Ｒ₅ は、それぞれ炭素数１〜４
のアルキル基又はヒドロキシアルキル基であり、具体的
にはメチル基、エチル基、プロピル基、ブチル基、ヒド
ロキシメチル基、ヒドロキシエチル基、ヒドロキシピロ
ピル基、ヒドロキシブチル基が挙げられるが、特にメチ
ル基、エチル基、ヒドロキシエチル基が好ましく用いら
れる。Ｒ₆、Ｒ₇は、それぞれＣｑＨ₂ｑ （但しｑ＝１〜
４）で示されるアルキレン基であり、具体的にはエチレ
ン基、プロピレン基、ブチレン基が挙げられ、直鎖状で
も分岐鎖状でもよい。Ｒ₈ は、炭素数１２〜２４、好ま
しくは１５〜２１のアルキル基又はアルケニル基であ
り、それぞれが−ＣＯ−Ｏ−基、−Ｏ−ＣＯ−基、−Ｃ
Ｏ−ＮＨ−基又は−ＮＨ−ＣＯ−基で中断されているも
のでも良い。また、一般式（Ｉ）〜（VII） 中のエステ
ル基は通常Ｒ−ＣＯ−Ｏ−の形であるが、Ｒ−Ｏ−ＣＯ
−の形であつても良い。ｍ，ｎ，ｐは、１〜４の数、Ｘ
は、陰イオンであり、具体的には塩素、臭素、ヨウ素等
のハロゲン原子アニオン、Ｒ₉ＳＯ₄（Ｒ₉ は炭素数１〜
３のアルキル基であり、具体的にはメチル基、エチル基
が挙げられが、特にメチル基が好適である。）で示され
る基のアニオン等が例示される。R ₃ , R ₄ and R ₅ each have 1 to 4 carbon atoms.
Is an alkyl group or a hydroxyalkyl group, and specific examples thereof include a methyl group, an ethyl group, a propyl group, a butyl group, a hydroxymethyl group, a hydroxyethyl group, a hydroxypropyl group, and a hydroxybutyl group. , Ethyl group and hydroxyethyl group are preferably used. R ₆ and R ₇ are each CqH ₂ q (where q = 1 to
It is an alkylene group represented by 4), and specific examples thereof include an ethylene group, a propylene group, and a butylene group, which may be linear or branched. R ₈ is an alkyl group or an alkenyl group having 12 to 24 carbon atoms, preferably 15 to 21 carbon atoms, and each is —CO—O— group, —O—CO— group, or —C.
It may be interrupted by an O-NH- group or a -NH-CO- group. The ester group in the general formulas (I) to (VII) is usually in the form of R-CO-O-, but R-O-CO
It may be in the form of-. m, n, p are numbers 1 to 4, X
Is an anion, specifically, a halogen atom anion such as chlorine, bromine, or iodine, R ₉ SO ₄ (R ₉ is 1 to 1 carbon atoms.
The alkyl group of 3 includes a methyl group and an ethyl group, and a methyl group is particularly preferable. And an anion of the group represented by

【００１２】一般式（Ｉ）の具体例としては、ジ（ステ
アロイルオキシエチル）ジメチル第４級アンモニウムク
ロライド、ステアロイルオキシエチル（オレオイルオキ
シエチル）ジメチル第４級アンモニウムクロライド、ジ
（パルミトイルオキシブチル）ジメチル第４級アンモニ
ウムメチルサルフェート、ジ（オレオイルオキシイソプ
ロピル）ジメチル第４級アンモニウムクロライド等が挙
げられる。Specific examples of the general formula (I) include di (stearoyloxyethyl) dimethyl quaternary ammonium chloride, stearoyloxyethyl (oleoyloxyethyl) dimethyl quaternary ammonium chloride and di (palmitoyloxybutyl) dimethyl. Examples thereof include quaternary ammonium methyl sulfate, di (oleoyloxyisopropyl) dimethyl quaternary ammonium chloride and the like.

【００１３】一般式（II）の具体例としては、ステアリ
ル（オレオイルオキシエチル）ジメチル第４級アンモニ
ウムクロライド、ステアリル（ステアロイルオキシエチ
ル）ジメチル第４級アンモニウムクロライド、オレイル
（ステアロイルオキシイソプロピル）ジメチル第４級ア
ンモニウムメチルサルフェート、パルミチル（オレオイ
ルオキシブチル）ジメチル第４級アンモニウムクロライ
ド、ステアロイルアミノエチル（ステアロイルオキシエ
チル）ジメチル第４級アンモニウムクロライド、硬化牛
脂アミノメチル（オレオイルオキシメチル）ジメチル第
４級アンモニウムクロライド等が挙げられる。Specific examples of the general formula (II) include stearyl (oleoyloxyethyl) dimethyl quaternary ammonium chloride, stearyl (stearoyloxyethyl) dimethyl quaternary ammonium chloride, and oleyl (stearoyloxyisopropyl) dimethyl quaternary. Quaternary ammonium methyl sulfate, palmityl (oleoyloxybutyl) dimethyl quaternary ammonium chloride, stearoylaminoethyl (stearoyloxyethyl) dimethyl quaternary ammonium chloride, hardened tallow aminomethyl (oleoyloxymethyl) dimethyl quaternary ammonium chloride Etc.

【００１４】一般式（III） の具体例としては、１−メ
チル−１−ステアロイルオキシエチル−２−オレオイル
オキシエチル−４，５−ジヒドロイミダゾリニウムクロ
ライド、１−エチル−１−リノレノイルオキシエチル−
２−エライジルオキシエチル−４，５−ジヒドロイミダ
ゾリニウムクロライド等が挙げられる。Specific examples of the general formula (III) include 1-methyl-1-stearoyloxyethyl-2-oleoyloxyethyl-4,5-dihydroimidazolinium chloride and 1-ethyl-1-linolenoyl. Oxyethyl-
Examples thereof include 2-elaidyloxyethyl-4,5-dihydroimidazolinium chloride.

【００１５】一般式（IV）の具体例としては、１−メチ
ル−１−ステアロイルオキシエチル−２−オレイル−
４，５−ジヒドロイミダゾリニウムクロライド、１−メ
チル−１−エライジルオキシプロピル−２−オレイル−
４，５−ジヒドロイミダゾリニウムクロライド等が挙げ
られる。Specific examples of the general formula (IV) include 1-methyl-1-stearoyloxyethyl-2-oleyl-
4,5-dihydroimidazolinium chloride, 1-methyl-1-elaidyloxypropyl-2-oleyl-
Examples include 4,5-dihydroimidazolinium chloride and the like.

【００１６】一般式（Ｖ）の具体例としては、１−メチ
ル−１−牛脂エチル−２−オレオイルオキシエチル−
４，５−ジヒドロイミダゾリニウムクロライド、１−メ
チル−１−牛脂エチル−２−パルミトイルオキシイソプ
ロピル−４，５−ジヒドロイミダゾリニウムクロライド
等が挙げられる。Specific examples of the general formula (V) include 1-methyl-1-beef tallow-2-oleoyloxyethyl-
Examples include 4,5-dihydroimidazolinium chloride, 1-methyl-1-beef ethyl-2-palmitoyloxyisopropyl-4,5-dihydroimidazolinium chloride, and the like.

【００１７】一般式（VI）の具体例としては、１，１−
ジステアロイルオキシエチル−３−トリメチルアンモニ
ウムプロパンクロライド、１−オレオイルオキシエチル
−１−ステアロイルオキシイソプロピル−３−トリメチ
ルアンモニウムプロパンクロライド等が挙げられる。Specific examples of the general formula (VI) include 1,1-
Examples thereof include distearoyloxyethyl-3-trimethylammonium propane chloride, 1-oleoyloxyethyl-1-stearoyloxyisopropyl-3-trimethylammonium propane chloride and the like.

【００１８】一般式（VII） の具体例としては、１−ス
テアリル−１−ステアロイルオキシエチル−３−トリメ
チルアンモニウムプロパンメチルサルフェート、１−オ
レイル−１−オレオイルオキシエチル−３−トリメチル
アンモニウムプロパンクロライド等が挙げられる。Specific examples of the general formula (VII) include 1-stearyl-1-stearoyloxyethyl-3-trimethylammoniumpropanemethylsulfate, 1-oleyl-1-oleoyloxyethyl-3-trimethylammoniumpropane chloride and the like. Is mentioned.

【００１９】本発明の（Ｂ）成分としては、１つの長鎖
炭化水素基を有するカチオン性界面活性剤が用いられ
る。（Ｂ）成分のカチオン性界面活性剤の具体例として
は、以下の化４の一般式（VIII）に示したものを例示で
きる。As the component (B) of the present invention, a cationic surfactant having one long chain hydrocarbon group is used. Specific examples of the cationic surfactant as the component (B) include those represented by the following general formula (VIII).

【００２０】[0020]

【化４】 [Chemical 4]

【００２１】式中、Ｒ₉ は、炭素数８〜２０、好ましく
は１２〜１８のアルキル基又はアルケニル基であり、そ
れぞれが−ＣＯ−基、−ＣＯ−Ｏ−基、−Ｏ−ＣＯ−
基、−ＣＯ−ＮＨ−基又は−ＮＨ−ＣＯ−基で中断され
ているものでも良い。Ｒ₁₀，Ｒ₁₁，Ｒ₁₂はそれぞれ炭素
数１〜４のアルキル基又はヒドロキシアルキル基であ
り、具体的にはメチル基、エチル基、プロピル基、ブチ
ル基、ヒドロキシメチル基、ヒドロキシエチル基、ヒド
ロキシピロピル基、ヒドロキシブチル基が挙げられる
が、特にメチル基、エチル基、ヒドロキシエチル基が好
ましく用いられる。また、Ｘは陰イオンであり、具体的
には塩素、臭素、ヨウ素等のハロゲン原子アニオン、Ｒ
₁₃ＳＯ₄ （Ｒ₁₃は炭素数１〜３のアルキル基であり、具
体的にはメチル基、エチル基、プロピル基が挙げられる
が、特にメチル基が好適である。）で示される基のアニ
オン等が例示される。In the formula, R ₉ is an alkyl group or an alkenyl group having 8 to 20 carbon atoms, preferably 12 to 18 carbon atoms, each of which is —CO— group, —CO—O— group, —O—CO—.
It may be interrupted by a group, a -CO-NH- group or a -NH-CO- group. R ₁₀ , R ₁₁ and R ₁₂ are each an alkyl group having 1 to 4 carbon atoms or a hydroxyalkyl group, and specifically, methyl group, ethyl group, propyl group, butyl group, hydroxymethyl group, hydroxyethyl group, hydroxy group. Examples thereof include a propyl group and a hydroxybutyl group, with a methyl group, an ethyl group and a hydroxyethyl group being particularly preferred. X is an anion, specifically, a halogen atom anion such as chlorine, bromine or iodine, R
An anion of a group represented by ₁₃ SO ₄ (R ₁₃ is an alkyl group having 1 to 3 carbon atoms, and specific examples thereof include a methyl group, an ethyl group and a propyl group, and a methyl group is particularly preferable.). Etc. are illustrated.

【００２２】一般式（VIII）で表されるカチオン性界面
活性剤の具体例としては、例えばラウリルトリメチルア
ンモニウムメチルサルフェート、ラウロイルオキシエチ
ルトリメチルアンモニウムメチルサルフェート、ミリス
チルトリメチルクロライド、ステアロイルアミノエチル
トリメチルアンモニウムクロライド、水素添加牛脂アル
キルトリメチルアンモニウムサルフェート、テトラデシ
ルトリメチルアンモニウムメチルサルフェートなどの１
種又は２種以上の混合物が挙げられる。Specific examples of the cationic surfactant represented by the general formula (VIII) include lauryl trimethyl ammonium methyl sulfate, lauroyl oxyethyl trimethyl ammonium methyl sulfate, myristyl trimethyl chloride, stearoyl aminoethyl trimethyl ammonium chloride, hydrogen. Addition of tallow alkyl trimethyl ammonium sulphate, tetradecyl trimethyl ammonium methyl sulphate, etc. 1
Examples include species or a mixture of two or more species.

【００２３】（Ａ）、（Ｂ）成分のカチオン性界面活性
剤は、（Ａ）／（Ｂ）重量比が９５／５〜５０／５０、
好ましくは９０／１０〜７０／３０の範囲で用いられ、
両者の合計量として１０〜６０重量％、好ましくは１５
〜５０重量％の量で柔軟剤組成物中に配合される。
（Ａ）／（Ｂ）の重量比が９５／５を越えると乾燥機中
の使用条件で柔軟剤が布に均一に付着せず、柔軟効果お
よび帯電防止効果が不充分となる。一方、（Ａ）／
（Ｂ）の重量比が５０／５０未満では、柔軟基剤の高温
での保存安定性が劣化する。また、（Ａ）および（Ｂ）
の合計配合量が１０重量％未満では、柔軟付与成分の絶
対量が不足し、柔軟効果および帯電防止効果が不充分で
ある。一方、（Ａ）および（Ｂ）の合計配合量が６０重
量％を越えると、乾燥機中の使用条件で柔軟剤が布に均
一に付着せず、柔軟効果および帯電防止効果が不充分と
なる。The cationic surfactants of the components (A) and (B) have a (A) / (B) weight ratio of 95/5 to 50/50,
Preferably used in the range of 90/10 to 70/30,
The total amount of both is 10 to 60% by weight, preferably 15
-50% by weight in the softener composition.
If the weight ratio of (A) / (B) exceeds 95/5, the softening agent does not uniformly adhere to the cloth under the conditions of use in the dryer, and the softening effect and antistatic effect become insufficient. On the other hand, (A) /
When the weight ratio of (B) is less than 50/50, the storage stability of the soft base material at high temperature deteriorates. Also, (A) and (B)
If the total blending amount is less than 10% by weight, the absolute amount of the softening component is insufficient and the softening effect and antistatic effect are insufficient. On the other hand, if the total content of (A) and (B) exceeds 60% by weight, the softening agent does not uniformly adhere to the cloth under the conditions of use in the dryer, resulting in insufficient softening effect and antistatic effect. .

【００２４】（Ｃ）成分のソルビタン脂肪酸エステルと
しては、ソルビタンと炭素数１２〜２４、好ましくは１
４〜１８の脂肪酸とのモノ、ジ、トリエステル及びこれ
らの混合物があげられる。ここで脂肪酸としては直鎖又
は分岐の飽和、不飽和脂肪酸があげられるが飽和脂肪酸
が好ましく、具体的には、ドデカン酸、テトラデカン
酸、ペンタデカン酸、ヘキサデカン酸、オクタデカン
酸、エイコサン酸、ドコサン酸などの１種又は２種以上
の混合物が例示できる。（Ｃ）成分の脂肪酸のとして
は、炭素数１２〜２４、好ましくは１４〜１８の直鎖又
は分岐状の飽和、不飽和の脂肪酸が用いられる。このう
ち飽和脂肪酸が好ましい。具体的には、ドデカン酸、テ
トラデカン酸、ペンタデカン酸、ヘキサデカン酸、オク
タデカン酸、エイコサン酸、ドコサン酸などの１種又は
２種以上の混合物が例示できる。As the sorbitan fatty acid ester as the component (C), sorbitan and a carbon number of 12 to 24, preferably 1
Mention may be made of mono-, di-, triesters with 4 to 18 fatty acids and mixtures thereof. Examples of the fatty acid include linear or branched saturated and unsaturated fatty acids, but saturated fatty acids are preferable, and specifically, dodecanoic acid, tetradecanoic acid, pentadecanoic acid, hexadecanoic acid, octadecanoic acid, eicosanoic acid, docosanoic acid, etc. Examples thereof include one kind or a mixture of two or more kinds. As the fatty acid as the component (C), a linear or branched, saturated or unsaturated fatty acid having 12 to 24 carbon atoms, preferably 14 to 18 carbon atoms is used. Of these, saturated fatty acids are preferred. Specifically, one or a mixture of two or more of dodecanoic acid, tetradecanoic acid, pentadecanoic acid, hexadecanoic acid, octadecanoic acid, eicosanoic acid and docosanoic acid can be exemplified.

【００２５】本発明において、（Ｃ）ソルビタン脂肪酸
エステル／（Ｄ）脂肪酸の配合重量比は、１０／９０〜
９０／１０であるが、好ましくは１５／８５〜６０／４
０であり、また、（Ｃ）および（Ｄ）の合計配合量は４
０〜９０重量％、好ましくは５０〜７５重量％である。
（Ｃ）／（Ｄ）の重量比が、１０／９０未満では、柔軟
基剤の高温での安定性が劣化し、柔軟付与効果も低下す
る。一方、（Ｃ）／（Ｄ）の重量比が、９０／１０を越
えると、帯電防止能が劣化する。また、（Ｃ）および
（Ｄ）の合計配合量が４０重量％未満では、乾燥機の使
用条件で柔軟基剤の流動性が不良となるため、柔軟基剤
が布に不均一に吸着し、柔軟性、帯電防止性能が劣化す
るとともに、保存安定性が低下し、布にしみを生じる。
一方、（Ｃ）および（Ｄ）成分の合計配合量が９０重量
％を越えると、柔軟基剤中の柔軟主成分である（Ａ）お
よび（Ｂ）成分の絶対量が不足し、充分な柔軟性を発現
しない。さらに、柔軟剤組成物中の（Ｃ）成分であるソ
ルビタン脂肪酸エステルの配合量は、柔軟剤組成物中の
５０重量％を越えない量とすることが重要であり、好ま
しくは２０〜４０重量％の範囲である。この配合量が５
０重量％を越えると、帯電防止能が著しく劣化し、ま
た、柔軟性も低下する。In the present invention, the blending weight ratio of (C) sorbitan fatty acid ester / (D) fatty acid is from 10/90 to
90/10, but preferably 15 / 85-60 / 4
0, and the total compounding amount of (C) and (D) is 4
It is 0 to 90% by weight, preferably 50 to 75% by weight.
When the weight ratio of (C) / (D) is less than 10/90, the stability of the soft base material at high temperature deteriorates, and the softening effect also decreases. On the other hand, if the weight ratio of (C) / (D) exceeds 90/10, the antistatic ability deteriorates. If the total content of (C) and (D) is less than 40% by weight, the fluidity of the soft base material becomes poor under the conditions of use of the dryer, so that the soft base material is non-uniformly adsorbed on the cloth, The flexibility and antistatic performance are deteriorated, the storage stability is deteriorated, and the cloth is stained.
On the other hand, if the total content of the components (C) and (D) exceeds 90% by weight, the absolute amount of the components (A) and (B), which are the soft main components in the soft base, becomes insufficient, resulting in sufficient softness. Does not develop sex. Further, it is important that the blending amount of the sorbitan fatty acid ester which is the component (C) in the softener composition is not more than 50% by weight in the softener composition, and preferably 20 to 40% by weight. Is the range. This blend amount is 5
If it exceeds 0% by weight, the antistatic ability is significantly deteriorated and the flexibility is also lowered.

【００２６】本発明の柔軟剤組成物には、柔軟性及び帯
電防止性を一層向上させるために、上記（Ａ）〜（Ｄ）
成分以外に、脂肪酸アミド、高級アルコールのエチレン
オキシド付加物、アルキルフェノールのエチレンオキシ
ド付加物、油脂のエチレンオキシド付加物の群から選ば
れる一種又は二種以上の混合物を添加することができ
る。また更に蛍光増白剤、染料、顔料、香料、シリコー
ン、抗菌剤、酸化防止剤などを配合することができる。
本発明の（Ａ）〜（Ｄ）成分を含有する柔軟剤組成物
を、担持させる基体としては、材料自身の内に上記柔軟
剤組成物を保持しうる空間を有する吸収性材料が好まし
い。例えば、紙、織物、不織布、スポンジなどであり、
このうち使用性から不織布、スポンジが好ましい。不織
布としては、セルロース、レーヨン、ポリエステル繊維
等をバインダーで処理したものや、これらにポリオレフ
ィン繊維を混入させバインダーを用いないもの、スパン
ボンド布などが使用可能である。スポンジとしては、連
続気泡を有するポリウレタンホーム、ポリエステルホー
ムなどのプラスチツクホームが好ましい。また製造上及
び使用性上から可撓性シート状物が好ましく、特に見か
け比重０．０１〜０．０３、空隙率９５〜９９％、厚さ
１〜５ｍｍの範囲内にあるシート状ポリウレタンホーム
等のプラスチツクフォームや坪量１０〜５０ｇ／ｍ² 、
空隙率７０〜９０％の不織布などが好ましい。The softening agent composition of the present invention contains the above-mentioned (A) to (D) in order to further improve flexibility and antistatic property.
In addition to the components, one or a mixture of two or more selected from the group of fatty acid amides, ethylene oxide adducts of higher alcohols, ethylene oxide adducts of alkylphenols, and ethylene oxide adducts of oils and fats can be added. Further, a fluorescent whitening agent, a dye, a pigment, a fragrance, a silicone, an antibacterial agent, an antioxidant and the like can be added.
As the substrate on which the softener composition containing the components (A) to (D) of the present invention is carried, an absorbent material having a space capable of holding the softener composition in the material itself is preferable. For example, paper, woven fabric, non-woven fabric, sponge, etc.,
Of these, non-woven fabrics and sponges are preferable in terms of usability. As the non-woven fabric, cellulose, rayon, polyester fibers and the like treated with a binder, those in which polyolefin fibers are mixed without using a binder, spun-bonded cloth and the like can be used. As the sponge, a plastic home such as a polyurethane home or a polyester home having open cells is preferable. A flexible sheet-like material is preferable from the viewpoint of production and usability, and particularly, a sheet-like polyurethane home having an apparent specific gravity of 0.01 to 0.03, a porosity of 95 to 99%, and a thickness of 1 to 5 mm. Plastic foam and basis weight 10 to 50 g / m ² ,
Nonwoven fabrics having a porosity of 70 to 90% are preferable.

【００２７】上記柔軟剤組成物を基体に担持させる量は
任意に選ぶことができるが、吸収性材料が有する空隙の
うち柔軟剤組成物が占める割合（以下、空隙占有率とい
う）が１〜５０容量％となるようにするのが好ましい。
吸収性材料が不織布の場合には空隙占有率が５〜５０容
量％、シート状プラスチツクフォームの場合には２〜３
０容量％となるようにするのが特に好ましい。尚、吸収
性材料の空隙率は、吸収性材料の真比重と見かけ比重と
の差から求め、これに常法により室温で比重を測定した
柔軟剤組成物を所定の空隙占有率となるように含浸させ
る。The amount of the softening agent composition supported on the substrate can be arbitrarily selected, but the proportion of the softening agent composition in the voids of the absorbent material (hereinafter referred to as void occupancy) is 1 to 50. It is preferable to set it to the volume%.
When the absorbent material is a non-woven fabric, the void occupancy is 5 to 50% by volume, and when it is a sheet-like plastic foam, it is 2 to 3%.
It is particularly preferable that the content be 0% by volume. The porosity of the absorbent material is determined from the difference between the true specific gravity and the apparent specific gravity of the absorbent material, and the softening agent composition whose specific gravity is measured at room temperature by a conventional method has a predetermined void occupancy rate. Impregnate.

【００２８】[0028]

【発明の効果】本発明によれば、所定の量比で（Ａ）２
つの長鎖炭化水素基を有し、そのうち少なくとも１つは
エステル基で中断されているカチオン性界面活性剤と
（Ｂ）１つの長鎖炭化水素基を有するカチオン性界面活
性剤を組み合わせて配合し、さらに所定の量比で（Ｃ）
ソルビタン脂肪酸エステル及び（Ｄ）脂肪酸を組み合わ
せて配合した柔軟剤組成物を、基体に担持させて洗濯の
乾燥工程で使用される繊維製品処理用物品とすることに
より、衣料等に均一に柔軟化成分を移行させ繊維製品、
特に化学繊維に対して優れた柔軟性と帯電防止性とを付
与することができる。次に実施例により本発明を説明す
るが、本発明はこれらに限定されるものではない。EFFECTS OF THE INVENTION According to the present invention, (A) 2 is used at a predetermined amount ratio.
A cationic surfactant having one long-chain hydrocarbon group, at least one of which is interrupted by an ester group, and (B) a cationic surfactant having one long-chain hydrocarbon group, are blended in combination. , And at a predetermined amount ratio (C)
A softening agent composition in which sorbitan fatty acid ester and (D) fatty acid are combined and blended is carried on a substrate to be a textile product-treating article used in a drying step of washing, thereby uniformly softening components such as clothing. Transition to textile products,
Particularly, excellent flexibility and antistatic property can be imparted to the chemical fiber. Next, the present invention will be described with reference to examples, but the present invention is not limited thereto.

【００２９】[0029]

【実施例】実施例で用いた繊維製品処理用物品は、次の
ようにして製造した。先ず、柔軟剤組成物の配合成分を
加熱溶融混合し、この溶融液を２３×２８ｃｍに裁断し
た空隙率７５％の不織布に絞りローラーを用い、含浸量
を２ｇ、不織布の空隙占有率が４０％になるように担持
せしめて、繊維製品処理用物品を調製した。繊維製品処
理用物品の性能は次のようにして評価した。繊維製品と
して綿タオル及び化学繊維（アクリルジャージ／ポリエ
ステルジャージ／ナイロントリコツト＝１／１／１）を
市販洗剤で洗浄後十分すすぎ、乾燥させたものを使用し
た。性能評価はこの処理を行つた布を乾燥重量が１／１
（綿タオル／化学繊維）の割合で合計１Ｋｇになるよう
に縦型回転式の家庭用衣料乾燥機に入れた。繊維製品処
理用物品を１枚加えた後、約５０〜７０℃で４５分間乾
燥処理をした。 （１） 柔軟性：処理前と処理後の試験布の手触りを比
較して次の基準で評価した。 ◎：非常に柔らかい。 ○：柔らかい。 △：わずかに柔らかい。 ×：処理前と変わらない。 （２） 帯電防止性：（株）宍戸商会製のスタティック
オネストメータにより、布に印加電圧１０ｋＶ、ターゲ
ツト距離２０ｍｍで帯電させ、電圧除去後の帯電圧の半
減期（秒）を測定した。試験布としてアクリル布を用い
た。 （３） 付着の均一性：処理後の試験布をブロムフェノ
ールブルー０．０４％水溶液に約３０秒間浸漬した後、
純水で十分すすぎ、風乾後青色に染着した状態を下記の
基準により評価した。 ◎：染着むらが認められない。 ○：やや染着むらが認められる。 △：染着むらが認められる。 ×：染着むらが非常に多い。 （４） 保存安定性：繊維製品処理物品１枚を３２枚に
切り、うち１６枚を重ね、下に紙を敷き、４５℃に１５
ｈｒ以上放置後の配合成分のしみだし及び吸収性材料同
志の融着を評価した。 ５点：しみだし、融着が認められない。 ３点：しみだし、融着が僅かに認められる。 １点：しみだし、融着が激しい。EXAMPLES The textile product-treating articles used in the examples were produced as follows. First, the blending components of the softening agent composition are heated and melt mixed, and the melt is cut into 23 × 28 cm, and a non-woven fabric having a porosity of 75% is used with a squeezing roller. The impregnation amount is 2 g and the void occupancy of the non-woven fabric is 40%. Was carried out to prepare an article for treating a textile product. The performance of the article for treating a textile product was evaluated as follows. As the textile products, cotton towels and chemical fibers (acrylic jersey / polyester jersey / nylon tricot = 1/1/1) washed with a commercial detergent, thoroughly rinsed, and dried were used. The performance evaluation is that the cloth that has been subjected to this treatment has a dry weight of 1/1
A total of 1 kg of (cotton towel / chemical fiber) was put in a vertical rotary type domestic clothes dryer. After adding one article for treating a textile product, it was dried at about 50 to 70 ° C. for 45 minutes. (1) Flexibility: The touches of the test cloths before and after the treatment were compared and evaluated according to the following criteria. A: Very soft ○: Soft Δ: Slightly soft X: Same as before treatment (2) Antistatic property: A static Honest meter manufactured by Shishido Shokai Co., Ltd. was used to charge the cloth at an applied voltage of 10 kV and a target distance of 20 mm, and the half-life (second) of the charged voltage after voltage removal was measured. An acrylic cloth was used as a test cloth. (3) Uniformity of adhesion: After immersing the treated test cloth in a 0.04% aqueous solution of bromphenol blue for about 30 seconds,
The state of being sufficiently rinsed with pure water, air-dried and then dyed in blue was evaluated according to the following criteria. A: No uneven dyeing is observed. ◯: Some uneven dyeing is observed. Δ: Uneven dyeing is observed. X: Very uneven dyeing. (4) Storage stability: One textile product treated article is cut into 32 pieces, 16 pieces of which are piled up, paper is laid under the pieces, and the temperature is kept at 45 ° C. for 15 minutes.
The exudation of the blended components and the fusion bonding of the absorbent materials after standing for at least hr were evaluated. 5 points: Seepage and no fusion is observed. 3 points: Exudation and slight fusion are observed. 1 point: Exudation and severe fusion.

【００３０】実施例１ ジ（ステアロイルオキシエチル）ジメチルアンモニウム
メチルサルフェートとジ（オレオイルオキシエチル）ジ
メチルアンモニウムメチルサルフェートの１：１混合物
（重量比）を（Ａ）成分として用い、これにラウリルト
リメチルアンモニウムメチルサルフェート（（Ｂ）成
分）、ソルビタンモノステアレート（（Ｃ）成分）およ
びステアリン酸（（Ｄ）成分）を表１に示した配合量で
添加し、さらにやし脂肪酸ジエタノールアミド１０重量
％を添加して加熱溶融せしめ、均一混合して柔軟剤組成
物とした。疎水性繊維で構成され坪量が２３ｇ／ｍ² で
ある熱融着型不織布を吸収性基体として用い、不織布２
３×２８ｃｍ当たり２ｇの含浸量となるように上記柔軟
剤組成物を含浸させて繊維製品処理用物品を作成してそ
の性能を評価し、結果を表２に示した。Example 1 A 1: 1 mixture (weight ratio) of di (stearoyloxyethyl) dimethylammonium methylsulfate and di (oleoyloxyethyl) dimethylammonium methylsulfate was used as component (A), to which lauryltrimethylammonium was added. Methyl sulfate ((B) component), sorbitan monostearate ((C) component) and stearic acid ((D) component) were added in the amounts shown in Table 1, and 10% by weight of palm fatty acid diethanolamide was added. The mixture was added, heated and melted, and uniformly mixed to obtain a softener composition. A non-woven fabric prepared by using a heat-bondable non-woven fabric composed of hydrophobic fibers and having a basis weight of 23 g / m ² as an absorbent substrate.
The above softener composition was impregnated so that the impregnation amount was 2 g per 3 × 28 cm to prepare an article for treating a textile product, and its performance was evaluated. The results are shown in Table 2.

【００３１】[0031]

【表１】表１：柔軟剤組成物の組成 配合量(wt％) 配合比 (A) (B) (C) (D) (A)＋(B) (C)＋(D) (A)／(B) (C)／(D) 実施例１ 13 2 35 40 15 75 87／13 47／53 実施例２ 25 5 35 25 30 60 83／17 58／42 実施例３ 35 10 15 30 45 45 78／22 33／67 比較例１ 10 5 75 0 15 75 67／33 100／0 比較例２ 25 0 40 25 25 65 100／0 62／38 比較例３ 22 28 10 30 50 40 44／56 25／75 比較例４ 25 5 55 5 30 60 83／17 92／8 [Table 1] Table 1: Composition ratio of the softener composition (wt%) Mixing ratio (A) (B) (C) (D) (A) + (B) (C) + (D) (A) / (B) (C) / (D) Example 1 13 2 35 40 15 75 87/13 47/53 Example 2 25 5 35 25 30 60 83/17 58/42 Example 3 35 10 15 30 45 45 78/22 33/67 Comparative Example 1 10 5 75 0 15 75 67/33 100/0 Comparative Example 2 25 0 40 25 25 65 100/0 62/38 Comparative Example 3 22 28 10 30 50 40 44/56 25 / 75 Comparative Example 4 25 5 55 5 30 60 83/17 92/8

【００３２】[0032]

【表２】 [Table 2]

【００３３】実施例２ （Ａ）成分（詳細は表３に記載） ２５重量％ （Ｂ）成分（詳細は表３に記載） ５重量％ （Ｃ）成分（詳細は表３に記載） ３０重量％ （Ｄ）成分（詳細は表３に記載） ３０重量％ （Ａ）＋（Ｂ）＝３０重量％ （Ａ）／（Ｂ）＝８３／１７ （Ｃ）＋（Ｄ）＝６０重量％ （Ｃ）／（Ｄ）＝５０／５０ 上記組成からなる柔軟剤組成物を加熱、溶融し、実施例
１と同じ不織布に不織布２３×２８ｃｍ当たり２ｇの量
で含浸させて繊維製品処理用物品を作成してその性能を
評価し、その結果を表４に示した。なお、比較例７で
は、本発明の（Ｃ）および（Ｄ）成分に替えて、ステア
リルアルコールを６０重量％配合した。Example 2 Component (A) (Details are shown in Table 3) 25% by weight Component (B) (Details are shown in Table 3) 5% by weight (C) Component (Details are shown in Table 3) 30% by weight % Component (D) (details are shown in Table 3) 30% by weight (A) + (B) = 30% by weight (A) / (B) = 83/17 (C) + (D) = 60% by weight ( C) / (D) = 50/50 The softening agent composition having the above composition is heated and melted, and the same non-woven fabric as in Example 1 is impregnated with the non-woven fabric in an amount of 2 g per 23 × 28 cm to prepare an article for treating textile products. The performance was evaluated and the results are shown in Table 4. In Comparative Example 7, 60% by weight of stearyl alcohol was added instead of the components (C) and (D) of the present invention.

【００３４】[0034]

【表３】 [Table 3]

【００３５】[0035]

【表４】 （Ａ）成分： ジＳＯ−４級塩：ジ（ステアロイルオキシ）ジメチル第
４級アンモニウムメチルサルフェート Ｓ／ＯＯ−４級塩：ステアリル（オレオイルオキシエチ
ル）ジメチル第４級アンモニウムメチルサルフェート ジＯＯ／−４級塩：ジオレオイルオキシエチルジメチル
第４級アンモニウムメチルサルフェート ＯＯ／Ｓ−Ｉｍｄ：１−メチル−１−オレオイルオキシ
エチル−２−ステアリル−４，５−ジヒドロイミダゾリ
ニウムメチルサルフェート （Ｂ）成分： Ｌ₁−４級塩：ラウリルメチル第４級アンモニウムメチ
ルサルフェート Ｌ₂−４級塩：ラウリルトリメチル第４級アンモニウム
クロライド Ｍ−４級塩：ミリスチルトリメチル第４級アンモニウム
クロライド Ｐ−４級塩：パルミチルトリメチル第４級アンモニウム
メチルサルフェート （Ｃ）成分： ＳＳ：ソルビタンモノステアレート ＳＰ：ソルビタンモノパルミテート ＰＯＥＳ：ポリオキシエチレン（平均付加モル数＝４）
モノステアレート（比較品） ＳＡｌｃ：ステアリルアルコール（比較品） （Ｄ）成分： ＳＡｃ：ステアリン酸 ＰＡｃ：パルミチン酸 ＤＧＳ：ジグリセリンモノステアレート（比較品）[Table 4] Component (A): DiSO-quaternary salt: di (stearoyloxy) dimethyl
Quaternary ammonium methyl sulfate S / OO-quaternary salt: stearyl (oleoyloxyethyl ester)
Le) dimethyl quaternary ammonium methyl sulfate diOO / -quaternary salt: dioleoyloxyethyl dimethyl
Quaternary ammonium methylsulfate OO / S-Imd: 1-methyl-1-oleoyloxy
Ethyl-2-stearyl-4,5-dihydroimidazoli
Nium methyl sulfate (B) component: L₁Quaternary salt: laurylmethyl quaternary ammonium methyl
Lusulfate L₂Quaternary salt: lauryl trimethyl quaternary ammonium
Chloride M-quaternary salt: myristyl trimethyl quaternary ammonium
Chloride P-quaternary salt: palmityl trimethyl quaternary ammonium
Methyl sulfate (C) component: SS: sorbitan monostearate SP: sorbitan monopalmitate POES: polyoxyethylene (average number of moles added = 4)
Monostearate (Comparative product) SAlc: Stearyl alcohol (Comparative product) (D) Component: SAc: Stearic acid PAc: Palmitic acid DGS: Diglycerin monostearate (Comparative product)

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.⁶ 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ０６Ｍ 15/07 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. ⁶ Identification code Internal reference number FI technical display location D06M 15/07

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 （Ａ）２つの長鎖炭化水素基を有し、そ
のうち少なくとも１つはエステル基で中断されているカ
チオン性界面活性剤と（Ｂ）１つの長鎖炭化水素基を有
するカチオン性界面活性剤を（Ａ）／（Ｂ）の重量比が
９５／５〜５０／５０で１０〜６０重量％；（Ｃ）ソル
ビタン脂肪酸エステル及び（Ｄ）脂肪酸を（Ｃ）／
（Ｄ）の重量比が１０／９０〜９０／１０で４０〜９０
重量％含有し；かつ柔軟剤組成物中のソルビタン脂肪酸
エステルの含有量が５０重量％を越えない柔軟剤組成物
を、基体に担持させたことを特徴とする洗濯の乾燥工程
で使用される繊維製品処理用物品。1. A cationic surfactant having (A) two long-chain hydrocarbon groups, at least one of which is interrupted by an ester group, and (B) a cation having one long-chain hydrocarbon group. (A) / (B) in a weight ratio of 95/5 to 50/50 in an amount of 10 to 60% by weight; (C) sorbitan fatty acid ester and (D) fatty acid in (C) /
The weight ratio of (D) is 40/90 at 10/90 to 90/10.
A fiber used in a drying process for washing, characterized in that a base material is loaded with a softening agent composition containing 50% by weight of sorbitan fatty acid ester in the softening agent composition and not exceeding 50% by weight. Articles for product processing.