JPH07126454A - Polypropylene-based resin composition and film and sheet having excellent transparency and surface gloss obtained from the same - Google Patents
Polypropylene-based resin composition and film and sheet having excellent transparency and surface gloss obtained from the sameInfo
- Publication number
- JPH07126454A JPH07126454A JP5274073A JP27407393A JPH07126454A JP H07126454 A JPH07126454 A JP H07126454A JP 5274073 A JP5274073 A JP 5274073A JP 27407393 A JP27407393 A JP 27407393A JP H07126454 A JPH07126454 A JP H07126454A
- Authority
- JP
- Japan
- Prior art keywords
- film
- polypropylene
- sheet
- resin composition
- syndiotactic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は透明性、表面光沢、およ
び成形加工性に優れたポリプロピレン系樹脂組成物、お
よびこれから得られるフィルムおよびシートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polypropylene resin composition which is excellent in transparency, surface gloss and moldability, and a film and a sheet obtained therefrom.
【0002】[0002]
【従来の技術】現在、アイソタクチックポリプロピレン
フィルムは、安価で透明性、剛性、耐湿性および耐熱性
に優れていることから各種の包装材料に広く使用されて
いる。しかしながら、その透明性や光沢が十分でなく、
その改良が望まれている。2. Description of the Related Art At present, isotactic polypropylene films are widely used for various packaging materials because they are inexpensive and have excellent transparency, rigidity, moisture resistance and heat resistance. However, its transparency and gloss are not sufficient,
The improvement is desired.
【0003】一方近年、J.A.Ewenらにより非対称な配位
子を有する遷移金属触媒とアルミノキサンからなる触媒
によって、シンジオタクチックペンタッド分率が0.7
を越えるようなタクティシティの高いポリプロピレンを
得られることが発見された。(J.Am.Chem.Soc.,1988,11
0,6255-6256 )。このシンジオタクチックポリプロピレ
ンは従来のアイソタクチックポリプロピレンに比べ極め
て透明性および表面光沢が高く、また柔軟性にも優れる
ため、透明・軟質なフィルムとしての用途が期待されて
おり、その成形方法としては従来のアイソタクチックポ
リプロピレンフィルムの成形方法、例えばT−ダイ押出
成形法や水冷インフレーション成形法(特開平3−81
130)が適用できるがその加工が非常に困難であっ
た。On the other hand, in recent years, a syndiotactic pentad fraction of 0.7 was obtained by a catalyst composed of a transition metal catalyst having an asymmetric ligand and aluminoxane according to JA Ewen et al.
It was discovered that a polypropylene having a high tacticity that exceeds the above can be obtained. (J.Am.Chem.Soc., 1988,11
0,6255-6256). This syndiotactic polypropylene has much higher transparency and surface gloss than conventional isotactic polypropylene, and also has excellent flexibility, so it is expected to be used as a transparent and soft film. Conventional isotactic polypropylene film molding methods such as T-die extrusion molding method and water-cooled inflation molding method (JP-A-3-81).
130) can be applied, but its processing was very difficult.
【0004】[0004]
【発明が解決しようとする課題】アイソタクチックポリ
プロピレンフィルムのうち、特にエチレン−プロピレン
ランダム共重合体のフィルムは透明性に優れるが、フィ
ルムの厚さが増すとともに透明性は低下するので、例え
ば包装材料として内容物の外観を損なわないような十分
な透明性を得ようとする場合、フィルムの厚さは60μ
m程度が限界だった。そのため、これまで透明性の高い
ポリプロピレンの厚物フィルムまたはシートの製造が困
難であるとされていた。Among the isotactic polypropylene films, the ethylene-propylene random copolymer film is particularly excellent in transparency, but the transparency decreases as the film thickness increases. In order to obtain sufficient transparency that does not impair the appearance of the contents as a material, the film thickness is 60μ.
The limit was about m. Therefore, it has been considered difficult to manufacture a thick polypropylene film or sheet having high transparency.
【0005】また、その表面は比較的光沢感があるが、
近年、商品の高級化指向に伴ってさらなる高光沢性が求
められており、その点で十分であるとは言い難かった。Further, although its surface has a relatively glossy feeling,
In recent years, higher glossiness has been demanded along with the trend toward higher grade products, and it is difficult to say that this point is sufficient.
【0006】一方、シンジオタクチックポリプロピレン
を例えばT−ダイ押出成形法により成形加工して得られ
るフィルムは、アイソタクチックポリプロピレンから得
られるフィルムに比べ透明性や表面光沢などの性質が良
好であり、その用途が期待される。しかしながら、シン
ジオタクチックポリプロピレンはアイソタクチックポリ
プロピレンに比べて結晶化速度が遅く、また結晶化度も
低いため、T−ダイ押出成形においてはフィルムが冷却
ロールに巻きつきやすく、アイソタクチックポリプロピ
レンに比べ加工性が劣っていた。本発明の目的は上記問
題点を解決した、透明性、表面光沢に優れたポリプロピ
レンフィルムおよびシートを得るために用いられる成形
加工性に優れたポリプロピレン系樹脂組成物およびこれ
から得られたフィルムまたはシートを提供することにあ
る。On the other hand, a film obtained by molding syndiotactic polypropylene by, for example, a T-die extrusion molding method has excellent properties such as transparency and surface gloss as compared with a film obtained from isotactic polypropylene. Its use is expected. However, since syndiotactic polypropylene has a slower crystallization rate and lower crystallinity than isotactic polypropylene, in T-die extrusion molding, the film is easily wound around a cooling roll, and thus, compared to isotactic polypropylene. The workability was poor. The object of the present invention is to solve the above problems, transparency, polypropylene resin composition excellent in molding processability used to obtain a polypropylene film and sheet having excellent surface gloss, and a film or sheet obtained therefrom. To provide.
【0007】[0007]
【課題を解決するための手段】本発明者はアイソタクチ
ックポリプロピレンよりも透明性が格段に優れ、しかも
柔軟で、表面光沢の良好なフィルム、さらには特に厚さ
60μm以上のシートを加工性良く得ることを目的とし
て研究を行い本発明に到達した。DISCLOSURE OF THE INVENTION The present inventors have found that the transparency of the film is far superior to that of isotactic polypropylene, and the film is flexible and has a good surface gloss, and particularly a sheet having a thickness of 60 μm or more is processed easily. Research was conducted for the purpose of obtaining the present invention, and the present invention was reached.
【0008】すなわち、本発明は、13C−NMRによっ
て測定されるシンジオタクチックペンタッド分率が0.
5〜0.9の範囲にあるシンジオタクチックポリプロピ
レン5〜95重量部、およびアイソタクチック構造を有
するプロピレン単独重合体95〜5重量部とからなるポ
リプロピレン系樹脂組成物およびこれを成形して得られ
るシートまたはフィルムであり、その厚さが0.001
〜5mmのフィルムおよびシートであり、特に100μ
m〜5mmのシートでる。また、入射角60°で測定し
たグロス値が95以上であるフィルムおよびシートであ
る。That is, according to the present invention, the syndiotactic pentad fraction measured by 13 C-NMR is 0.
A polypropylene resin composition comprising 5 to 95 parts by weight of syndiotactic polypropylene in the range of 5 to 0.9 and 95 to 5 parts by weight of a propylene homopolymer having an isotactic structure, and a polypropylene resin composition obtained by molding the same. Sheet or film having a thickness of 0.001
~ 5mm film and sheet, especially 100μ
It is a sheet of m to 5 mm. Further, the film and the sheet have a gloss value of 95 or more measured at an incident angle of 60 °.
【0009】すなわち、以下本発明を詳細に説明する。That is, the present invention will be described in detail below.
【0010】本発明においてシンジオタクチックポリプ
ロピレンを製造する触媒としては、例えば特開平2−4
1303号公報、特開平2−41305号公報、特開平
2−274703号公報、特開平2−274704号公
報、特開平3−179005号、特開平3−17900
6号公報、特開平4−69394号公報に記載されてい
るような互いに非対称な配位子を有する架橋型遷移金属
化合物および助触媒からなるような触媒を挙げることが
できるが、異なる構造の触媒であっても13C−NMRに
よって測定されるシンジオタクチックペンタッド分率が
0.7以上のポリプロピレンを製造できるものであれば
利用でき、その重合方法としてはスラリー重合法、塊状
重合法、気相重合法のいずれも利用できる。The catalyst for producing syndiotactic polypropylene in the present invention is, for example, Japanese Patent Application Laid-Open No. 2-4.
No. 1303, No. 2-41305, No. 2-274703, No. 2-274704, No. 3-179005, No. 3-17900.
Examples of the catalyst include a bridged transition metal compound having mutually asymmetric ligands and a cocatalyst as described in JP-A-6-69394 and JP-A-4-69394, but catalysts having different structures. However, any polymer can be used as long as it can produce polypropylene having a syndiotactic pentad fraction of 0.7 or more measured by 13 C-NMR, and its polymerization method includes a slurry polymerization method, a bulk polymerization method, and a gas polymerization method. Any of the phase polymerization methods can be used.
【0011】本発明において用いられるシンジオタクチ
ックポリプロピレンは本発明のフィルムとしての透明
性、表面光沢、および機械物性を損なわない限り、プロ
ピレン以外のコモノマー、例えばエチレン、1−ブテ
ン、1−ヘキセン、1−デセン、1−ヘキサデセン、シ
クロペンテン、ノルボルネン等のオレフィン類や、ヘキ
サジエン、オクタジエン、デカジエン、ジシクロペンタ
ジエン、5−エチリデン2−ノルボルネンなどのジエン
類を少量含有する共重合体であっても差し支えない。そ
のような共重合体は、前記のシンジオタクティシティの
良好なポリ−α−オレフィンを与える公知の触媒の存在
下にプロピレンと少量のコモノマーを共重合することに
よって得ることができる。The syndiotactic polypropylene used in the present invention is a comonomer other than propylene, such as ethylene, 1-butene, 1-hexene, 1 as long as it does not impair the transparency, surface gloss and mechanical properties of the film of the present invention. A copolymer containing a small amount of olefins such as decene, 1-hexadecene, cyclopentene and norbornene, and diene such as hexadiene, octadiene, decadiene, dicyclopentadiene and 5-ethylidene-2-norbornene may be used. Such a copolymer can be obtained by copolymerizing propylene with a small amount of a comonomer in the presence of a known catalyst which gives the poly-α-olefin having good syndiotacticity.
【0012】本発明で使用されるシンジオタクチックホ
モポリプロピレンは、その13C−NMRにより求められ
るシンジオタクチックペンタッド分率が好ましくは0.
7〜0.9のものが使用され上、特に好ましくは0.7
5以上の値をもつ。The syndiotactic homopolypropylene used in the present invention preferably has a syndiotactic pentad fraction determined by 13 C-NMR, which is preferably 0.
7 to 0.9 is used, and particularly preferably 0.7
It has a value of 5 or more.
【0013】シンジオタクチックポリプロピレンの分子
量は、135℃のテトラリン溶液中で測定される極限粘
度として0.1〜10dl/g、好ましくは0.5〜
5.0dl/gの範囲である。The molecular weight of syndiotactic polypropylene is 0.1 to 10 dl / g, preferably 0.5 to 10 as an intrinsic viscosity measured in a tetralin solution at 135 ° C.
It is in the range of 5.0 dl / g.
【0014】本発明においてアイソタクチック構造を有
するプロピレン単独重合体としては、市場で入手できる
ような公知のアイソタクチックホモポリプロピレンが使
用できる。また、その他に例えば特開昭61−1303
14号公報、特開平3−12406号公報等に記載され
ているような、いわゆるメタロセン化合物を主成分とす
る触媒を用いて製造されるアイソタクチックホモポリプ
ロピレンも利用できる。 シンジオタクチックポリプロ
ピレン単独重合体とアイソタクチック構造を有するプロ
ピレン単独重合体の混合割合は、シンジオタクチックポ
リプロピレン単独重合体5〜95重量部およびアイソタ
クチック構造を有するプロピレン単独重合体5〜95重
量部からなるものがポリプロピレン系樹脂組成物として
使用できる。この割合は目的によって適宜選択すること
ができ、例えばシンジオタクチックポリプロピレンの加
工性を改良することを目的とする場合は、シンジオタク
チックポリプロピレン95〜50重量部、好ましくは9
0〜60重量部、さらに好ましくは85〜65重量部で
あり、一方、アイソタクチック構造を有するプロピレン
単独重合体の透明性や光沢を改良する場合はアイソタク
チックポリプロピレン95〜50重量部、好ましくは9
0〜60重量部、さらに好ましくは85〜65重量部の
組成で使用することができる。In the present invention, as the propylene homopolymer having an isotactic structure, known isotactic homopolypropylene which is commercially available can be used. In addition, in addition, for example, JP-A-61-1303
Isotactic homopolypropylene produced using a catalyst containing a so-called metallocene compound as a main component, such as those described in JP-A No. 14 and JP-A No. 3-12406, can also be used. The mixing ratio of syndiotactic polypropylene homopolymer and propylene homopolymer having isotactic structure is 5 to 95 parts by weight of syndiotactic polypropylene homopolymer and 5 to 95 parts by weight of propylene homopolymer having isotactic structure. The polypropylene resin composition can be used as a polypropylene resin composition. This ratio can be appropriately selected depending on the purpose. For example, in the case of improving the processability of syndiotactic polypropylene, the syndiotactic polypropylene is 95 to 50 parts by weight, preferably 9 parts by weight.
0 to 60 parts by weight, more preferably 85 to 65 parts by weight. On the other hand, in the case of improving the transparency and gloss of a propylene homopolymer having an isotactic structure, 95 to 50 parts by weight of isotactic polypropylene, preferably Is 9
It can be used in a composition of 0 to 60 parts by weight, more preferably 85 to 65 parts by weight.
【0015】本発明の樹脂組成物には必要に応じてブロ
ッキング防止剤、滑剤、結晶核剤、紫外線吸収剤、熱安
定剤、耐候安定剤、耐放射線剤、顔料、染料等の添加剤
を添加してもよい。If necessary, additives such as antiblocking agents, lubricants, crystal nucleating agents, UV absorbers, heat stabilizers, weather resistance stabilizers, radiation resistance agents, pigments and dyes are added to the resin composition of the present invention. You may.
【0016】本発明の樹脂組成物は、シンジオタクチッ
クポリプロピレン、アイソタクチックホモポリプロピレ
ンおよび必要に応じて公知の安定剤、添加剤をヘンシェ
ルミキサー等の混合機により混合した後、押出機にて溶
融混練、造粒する方法、あるいはロール、バンバリーミ
キサー、加圧ニーダー、ブラベンダー等により溶融混練
する方法などにより製造できる。また、シンジオタクチ
ックポリプロピレンおよびアイソタクチックホモポリプ
ロピレンをそれぞれ個別に押出機等により造粒し、成形
加工する際にそれらのペレットをブレンドして用いても
良い。The resin composition of the present invention is prepared by mixing syndiotactic polypropylene, isotactic homopolypropylene and, if necessary, known stabilizers and additives with a mixer such as a Henschel mixer and then melting the mixture with an extruder. It can be produced by a method of kneading and granulating, or a method of melt-kneading with a roll, a Banbury mixer, a pressure kneader, a Brabender or the like. Further, the syndiotactic polypropylene and the isotactic homopolypropylene may be individually granulated by an extruder or the like, and the pellets may be blended and used at the time of molding.
【0017】本発明のごとくシンジオタクチックポリプ
ロピレンとアイソタクチックホモポリプロピレンとをブ
レンドすることによりシンジオタクチックポリプロピレ
ンの成形加工性が改善されるので、T−ダイ押出成形法
あるいはインフレーション成形法等の公知のアイソタク
チックポリプロピレンの加工方法がそのまま適用でき
る。本発明のフィルムおよびシートは、本発明の樹脂組
成物のペレットを製造した後、そのような加工方法を用
いて容易に製造することができる。By blending syndiotactic polypropylene and isotactic homopolypropylene as in the present invention, the molding processability of syndiotactic polypropylene is improved. Therefore, known methods such as T-die extrusion molding and inflation molding are known. The processing method of isotactic polypropylene can be applied as it is. The film and sheet of the present invention can be easily produced by using such a processing method after producing pellets of the resin composition of the present invention.
【0018】また、その組成比を変えることによって所
望の透明性、表面光沢、および機械物性を有するフィル
ム、シートが得られるばかりでなく、シンジオタクチッ
クポリプロピレンを主体としたフィルム、シートは、従
来の結晶性アイソタクチックエチレン−プロピレンラン
ダム共重合体のフィルム、シートに比べ極めて透明性お
よび表面光沢が高く、特にその厚さが60μmを越えて
も非常に高い透明性を有する。Further, by changing the composition ratio, not only a film or sheet having desired transparency, surface gloss and mechanical properties can be obtained, but a film or sheet mainly composed of syndiotactic polypropylene is not Compared with a crystalline isotactic ethylene-propylene random copolymer film or sheet, it has extremely high transparency and surface gloss, and in particular, has extremely high transparency even when its thickness exceeds 60 μm.
【0019】さらに、本発明のフィルムおよびシートは
通常のアイソタクチックポリプロピレンのフィルム、シ
ートに比べて白みがなくスッキリとした透明感があり、
包装材料としては極めて商品価値の高いものである。Furthermore, the film and sheet of the present invention have a clear and clear feeling without whiteness as compared with a normal isotactic polypropylene film and sheet.
It has extremely high commercial value as a packaging material.
【0020】[0020]
【実施例】本発明をさらに詳細に説明するために以下に
実施例を述べるが、本発明はこれらに限定されるもので
はない。なお、実施例における測定方法は下記の通りで
あり、ヘイズおよびグロスの測定値は第1表に示す。 (1)メルトフローインデックス:ASTM D−12
38 (2)ヘイズ:ASTM−D−1003 (3)グロス:ASTM D−523(入射角60°で
測定した) (4)内部ヘイズ:三井東圧化学法(フィルムあるいは
シートの両面に流動パラフィンとトルエンの1:1(重
量)の割合の混合した溶液を塗布後、ASTM−D−1
003の方法に準じてヘイズを測定した。EXAMPLES The following examples are provided for illustrating the present invention further in detail, but the present invention is not limited thereto. The measuring methods in the examples are as follows, and the measured values of haze and gloss are shown in Table 1. (1) Melt flow index: ASTM D-12
38 (2) Haze: ASTM-D-1003 (3) Gloss: ASTM D-523 (measured at an incident angle of 60 °) (4) Internal haze: Mitsui Toatsu Chemical Method (with liquid paraffin on both surfaces of the film or sheet) After applying a mixed solution of toluene at a ratio of 1: 1 (weight), ASTM-D-1
Haze was measured according to the method of 003.
【0021】実施例1 特開平2ー274763号公報に従い、ジフェニルメチ
レン(シクロペンタジエニル)フルオレニルジルコニウ
ムジクロライドおよびメチルアルミノキサンからなる触
媒を用いて、水素の存在下でプロピレンの塊状重合法に
よって得られたシンジオタクチックポリプロピレン(1
35℃のテトラリン溶液中で測定した極限粘度(以下
〔η〕と略記する)が1.39dl/g、メルトフロー
インデックス(以下MFIと略記する)が3.2g/1
0min、示差走査熱量分析で測定した結晶化温度のピ
ーク温度が74.6℃、13C−NMRによって測定され
たシンジオタクチックペンタッド分率が0.787)
(H−SPP)80重量部、およびアイソタクチックホ
モポリプロピレン(三井東圧化学(株)製、JHH−
G:MFI 8g/10min)20重量部とをブレン
ドし、40φmm下向きT−ダイ付き押出機により押出
機温度210℃、冷却ロール温度30℃で製膜して厚さ
が100μmのシートを得た。Example 1 Obtained by bulk polymerization of propylene in the presence of hydrogen using a catalyst consisting of diphenylmethylene (cyclopentadienyl) fluorenyl zirconium dichloride and methylaluminoxane according to JP-A-2-274763. Syndiotactic polypropylene (1
The intrinsic viscosity (hereinafter abbreviated as [η]) measured in a tetralin solution at 35 ° C. is 1.39 dl / g, and the melt flow index (hereinafter abbreviated as MFI) is 3.2 g / 1.
0 min, peak temperature of crystallization temperature measured by differential scanning calorimetry is 74.6 ° C., syndiotactic pentad fraction measured by 13 C-NMR is 0.787)
(H-SPP) 80 parts by weight, and isotactic homopolypropylene (Mitsui Toatsu Chemical Co., Ltd., JHH-
G: MFI (8 g / 10 min) (20 parts by weight) was blended, and a film having a thickness of 100 μm was obtained by forming a film with an extruder with a φ-down T-die at an extruder temperature of 210 ° C. and a cooling roll temperature of 30 ° C.
【0022】比較例1 アイソタクチックホモポリプロピレン(三井東圧化学
(株)製、JHH−G:MFI 8g/10min)を
実施例1と同様に製膜して厚さ100μmのシートを得
た。Comparative Example 1 Isotactic homopolypropylene (manufactured by Mitsui Toatsu Chemicals, Inc., JHH-G: MFI 8 g / 10 min) was formed in the same manner as in Example 1 to obtain a sheet having a thickness of 100 μm.
【0023】比較例2 アイソタクチックエチレン−プロピレンランダム共重合
体(三井東圧化学(株)製、EFL−200:MFI
9g/10min、エチレン含有率4.9重量%)を実
施例1と同様に製膜して厚さ100μmのシートを得
た。Comparative Example 2 Isotactic ethylene-propylene random copolymer (manufactured by Mitsui Toatsu Chemicals, Inc., EFL-200: MFI)
9 g / 10 min, ethylene content 4.9% by weight) was formed in the same manner as in Example 1 to obtain a sheet having a thickness of 100 μm.
【0024】実施例2 シンジオタクチックポリプロピレンH−SPP 80重
量部およびアイソタクチックポリプロピレン JHH−
G20 重量部とから実施例1と同様に製膜して厚さ5
00μmのシートを得た。Example 2 80 parts by weight of syndiotactic polypropylene H-SPP and isotactic polypropylene JHH-
A film having a thickness of 5 was formed from G20 by weight in the same manner as in Example 1.
A sheet of 00 μm was obtained.
【0025】比較例3 アイソタクチックプロピレンーエチレンランダム共重合
体(三井東圧化学(株)製、GFL−G:MFI 9g
/10min、エチレン含有率3.1重量%)を実施例
1と同様に製膜して厚さ500μmのシートを得た。Comparative Example 3 Isotactic propylene-ethylene random copolymer (manufactured by Mitsui Toatsu Chemicals, Inc., GFL-G: MFI 9 g)
/ 10 min, ethylene content 3.1% by weight) was formed into a film in the same manner as in Example 1 to obtain a sheet having a thickness of 500 μm.
【0026】実施例3 実施例1の組成で、同様な方法で製膜して厚さ50μm
のフィルムを得た。Example 3 The composition of Example 1 was used to form a film in a similar manner to a thickness of 50 μm.
I got a film of.
【0027】比較例4 実施例1で用いたシンジオタクチックポリプロピレンH
−SPPのみを用いて実施例1の方法に準じて製膜して
厚さ500μmのシートを得た。Comparative Example 4 Syndiotactic polypropylene H used in Example 1
A film having a thickness of 500 μm was obtained by forming a film using only —SPP according to the method of Example 1.
【0028】この製膜は樹脂が固化しにくく、実施例1
の方法よりも製膜速度を半分程度に下げたがシートの厚
みにかなり不均一な部分が生じた。In this film formation, the resin is hard to solidify,
The film-forming speed was reduced to about half that of the above method, but a part where the thickness of the sheet was uneven was generated.
【0029】[0029]
【表1】 [Table 1]
【0030】[0030]
【発明の効果】本発明のポリプロピレン系樹脂組成物
は、シンジオタクチックポリプロピレン単体に比べ成形
加工性が非常に良好で、公知の成形方法により容易にフ
ィルム、シートに加工できる。また、本発明のフィルム
およびシートは、従来のアイソタクチックポリプロピレ
ンから得られるフィルム、シートに比べ極めて透明性に
優れるため内容物の外観を損なうことがなく、かつ非常
に表面光沢が高いため製品に高級感を付与することがで
きるので、例えば包装材料として有用である。The polypropylene resin composition of the present invention has much better moldability than syndiotactic polypropylene alone and can be easily processed into a film or sheet by a known molding method. In addition, the film and sheet of the present invention are excellent in transparency as compared with the film and sheet obtained from conventional isotactic polypropylene, so that the appearance of the contents is not impaired, and the surface gloss is very high. Since it can impart a high-grade feeling, it is useful, for example, as a packaging material.
フロントページの続き (72)発明者 井上 則英 神奈川県横浜市栄区笠間町1190番地 三井 東圧化学株式会社内Front Page Continuation (72) Inventor Norihide Inoue 1190 Kasama-cho, Sakae-ku, Yokohama-shi, Kanagawa Mitsui Toatsu Chemical Co., Ltd.
Claims (5)
オタクチックペンタッド分率が0.5〜0.9の範囲に
あるシンジオタクチックポリプロピレン5〜95重量
部、およびアイソタクチック構造を有するプロピレン単
独重合体95〜5重量部とからなるポリプロピレン系樹
脂組成物。1. A syndiotactic polypropylene having a syndiotactic pentad fraction measured by 13 C-NMR in the range of 0.5 to 0.9 and 5 to 95 parts by weight, and propylene having an isotactic structure. A polypropylene resin composition comprising 95 to 5 parts by weight of a homopolymer.
オタクチックペンタッド分率が0.5〜0.9の範囲に
あるシンジオタクチックポリプロピレン5〜95重量
部、およびアイソタクチック構造を有するプロピレン単
独重合体95〜5重量部とからなるポリプロピレン系樹
脂組成物を押出し成形して得られるシートまたはフィル
ム。2. 5 to 95 parts by weight of syndiotactic polypropylene having a syndiotactic pentad fraction measured by 13 C-NMR in the range of 0.5 to 0.9, and propylene having an isotactic structure. A sheet or film obtained by extruding a polypropylene resin composition comprising 95 to 5 parts by weight of a homopolymer.
厚さが0.001〜5mmのフィルムおよびシート。3. A film or sheet having a thickness of 0.001 to 5 mm obtained from the resin composition according to claim 1.
厚さが0.1mm〜5mmのシート。4. A sheet having a thickness of 0.1 mm to 5 mm obtained from the resin composition according to claim 1.
以上である請求項1記載のフィルムおよびシート。5. The gloss value measured at an incident angle of 60 ° is 95.
The film and sheet according to claim 1, which are the above.