JPH07102390A - Method for cleaning metallic strip - Google Patents
Method for cleaning metallic stripInfo
- Publication number
- JPH07102390A JPH07102390A JP5249448A JP24944893A JPH07102390A JP H07102390 A JPH07102390 A JP H07102390A JP 5249448 A JP5249448 A JP 5249448A JP 24944893 A JP24944893 A JP 24944893A JP H07102390 A JPH07102390 A JP H07102390A
- Authority
- JP
- Japan
- Prior art keywords
- cleaning
- metal strip
- cleaning liquid
- sprayed
- metallic strip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、金属帯の洗浄方法に関
する。FIELD OF THE INVENTION The present invention relates to a method for cleaning a metal strip.
【0002】[0002]
【従来の技術】例えば、圧延して得た金属帯を二次加工
したり或いはそのまま製品化する際には、圧延工程で付
着した油脂類等の汚れを除去する必要がある。こうした
金属帯を洗浄する方法として、走行する金属帯の表面に
洗浄液を順次吹き付けて汚れを除去する方法が行われて
いる。即ち、この方法によれば、洗浄室をほぼ水平方向
に走行する金属帯は、該洗浄室の上部及び下部に各設置
された洗浄液噴射ノズルからその上面及び下面に洗浄液
が吹き付けられ、表面に付着した油脂類等の汚れが洗い
落とされる。また、洗浄された金属帯は、通常、続いて
乾燥室に搬入されその表面に付着した洗浄液が乾燥され
る。ここで、こうした洗浄方法に用いられる洗浄液とし
ては、油脂類等の溶解力の高さから、多くの場合におい
て、トリクロロエタン、パークロルエチレン、メチレン
クロライド等の塩素化炭化水素系溶剤が用いられてい
る。2. Description of the Related Art For example, when a metal strip obtained by rolling is subjected to secondary processing or is directly produced as a product, it is necessary to remove stains such as fats and oils attached in the rolling process. As a method of cleaning such a metal strip, a method of sequentially spraying a cleaning liquid on the surface of the running metal strip to remove dirt is performed. That is, according to this method, the metal strip running in the cleaning chamber in a substantially horizontal direction is sprayed with the cleaning liquid on the upper and lower surfaces of the cleaning liquid from the cleaning liquid injection nozzles installed at the upper and lower parts of the cleaning chamber, and adheres to the surface. Dirt such as oils and fats that have been washed off is washed off. Further, the cleaned metal strip is usually carried into a drying chamber and the cleaning liquid attached to the surface thereof is dried. Here, as a cleaning liquid used in such a cleaning method, a chlorinated hydrocarbon solvent such as trichloroethane, perchlorethylene, methylene chloride or the like is often used because of its high dissolving power for fats and oils. .
【0003】[0003]
【発明が解決しようとする課題】以上のような金属帯の
洗浄方法において、前記洗浄室の上部及び下部に各設置
される洗浄液噴射ノズルは、通常、ほぼ水平方向に走行
する金属帯に対して洗浄液がほとんど垂直に吹き付けら
れるように設けられている。しかして、このように洗浄
液が走行する金属帯に対して垂直に吹き付けられた場
合、金属帯の上面では、この吹き付けられた洗浄液は、
走行する金属帯上を流動し該金属帯の側縁から落下する
までの間に、金属帯上面に付着した汚れをくまなく洗い
落とす。In the method of cleaning a metal strip as described above, the cleaning liquid injection nozzles installed at the upper and lower portions of the cleaning chamber are usually installed on the metal strip traveling in a substantially horizontal direction. The cleaning liquid is provided so as to be sprayed almost vertically. Then, when the cleaning liquid is sprayed perpendicularly to the traveling metal strip in this way, on the upper surface of the metal strip, the sprayed cleaning liquid is
The dirt adhered to the upper surface of the metal strip is thoroughly washed off while flowing on the running metal strip and falling from the side edge of the metal strip.
【0004】ところが、上記金属帯の下面では、前記の
如く洗浄液が走行する金属帯に対して垂直に吹き付けら
れても、該洗浄液は、金属帯下面と接触後自重によりす
ぐに該金属帯面から落下する。従って、この金属帯の下
面では、一つの洗浄液噴射ノズルから噴出される洗浄液
は、該金属帯下面との接触面積及び接触時間とも十分な
洗浄には不足しがちになり易い。特に、近年こうした金
属帯の洗浄液は、地球環境保護の面から、前記した油脂
類等の溶解力の高い塩素化炭化水素系溶剤の使用が次第
に規制されつつあり、これに代えてナフテン系、パラフ
ィン系、芳香族系等の炭化水素系溶剤や水等が使用され
始めている。しかして、こうした炭化水素系溶剤や水等
の油脂の溶解力は、上記塩素化炭化水素系溶剤に比べる
とかなり劣るため、かかる溶剤や水を金属帯の洗浄液と
して適用した場合には、前記金属帯の下面において汚れ
の洗い残しが多々生じる。However, on the lower surface of the metal strip, even if the cleaning liquid is sprayed perpendicularly to the traveling metal strip as described above, the cleaning liquid immediately comes out of contact with the lower surface of the metal strip from the surface of the metal strip by its own weight. To fall. Therefore, on the lower surface of the metal band, the cleaning liquid ejected from one cleaning liquid injection nozzle tends to be insufficient for sufficient cleaning in terms of contact area and contact time with the lower surface of the metal band. In particular, in recent years, the use of chlorinated hydrocarbon-based solvents having a high dissolving power for the above-mentioned oils and fats is gradually being regulated in the cleaning solution for such metal strips from the viewpoint of protecting the global environment. Hydrocarbon-based solvents such as organic and aromatic solvents, water, etc. have begun to be used. However, the solubility of such hydrocarbon solvents and fats and oils such as water is considerably inferior to that of the above chlorinated hydrocarbon solvents, and therefore when such a solvent or water is applied as a cleaning solution for a metal strip, Many stains are left unwashed on the lower surface of the belt.
【0005】これを防止するためには、金属帯の下部に
設置される洗浄液噴射ノズルの数を過度に増やすことも
考えられるが、洗浄装置の複雑化や大型化につながり効
率的でない。In order to prevent this, it is conceivable to excessively increase the number of cleaning liquid injection nozzles installed in the lower part of the metal strip, but this is not efficient because the cleaning device becomes complicated and large.
【0006】こうした背景から本発明は、水平方向に走
行する金属帯の下面に付着した汚れの洗浄が、簡単な手
段で良好に行える方法を開発することを目的とする。From this background, the present invention has an object of developing a method capable of satisfactorily cleaning dirt adhering to the lower surface of a horizontally running metal strip by a simple means.
【0007】[0007]
【課題を解決するための手段】上記した問題点に鑑み、
本発明者らは鋭意研究を続けてきた。その結果、ほぼ水
平方向に走行する金属帯の下面に洗浄液を吹き付けるに
際し、該洗浄液を、上記金属帯の走行方向に対して特定
の向きと角度で吹き付けることにより、上記の問題点が
解決できることを見いだし本発明を提案するに至った。[Means for Solving the Problems] In view of the above problems,
The present inventors have continued to earnestly research. As a result, when the cleaning liquid is sprayed on the lower surface of the metal strip that travels in a substantially horizontal direction, by spraying the cleaning liquid at a specific direction and angle with respect to the traveling direction of the metal strip, it is possible to solve the above problems. They have found the present invention and have proposed the present invention.
【0008】即ち、本発明は、ほぼ水平方向に走行する
金属帯の下面に洗浄液を吹き付けて該金属帯の下面を洗
浄するに際し、上記金属帯の走行方向に対して1〜45
゜の角度で、該走行方向の下流に向かって洗浄液を吹き
付けることを特徴とする金属帯の洗浄方法である。That is, according to the present invention, when the cleaning liquid is sprayed on the lower surface of the metal strip that travels in a substantially horizontal direction to clean the lower surface of the metal strip, 1 to 45 with respect to the traveling direction of the metal strip.
A method for cleaning a metal strip is characterized in that a cleaning liquid is sprayed toward the downstream side in the traveling direction at an angle of °.
【0009】本発明の洗浄方法は、ほぼ水平方向、好適
には該水平方向に対し±10°内の走行角度で走行する
金属帯の下面に洗浄液を吹き付けて該金属帯の下面を洗
浄する場合であれば、何等制限されることなく採用する
ことができる。通常は、図1に示す如くの一般的な金属
帯の洗浄装置において、金属帯の下面を洗浄する方法と
して採用するのが好ましい。According to the cleaning method of the present invention, a cleaning liquid is sprayed onto the lower surface of a metal strip that travels in a substantially horizontal direction, preferably a traveling angle within ± 10 ° with respect to the horizontal direction, to clean the lower surface of the metal strip. If so, it can be adopted without any limitation. Usually, it is preferable to adopt it as a method for cleaning the lower surface of the metal strip in a general metal strip cleaning apparatus as shown in FIG.
【0010】即ち、図1の洗浄装置において1は洗浄室
であり、該洗浄室1では、金属帯搬入口2より搬入され
た金属帯3は室内をほぼ水平に走行し、金属帯排出口4
より排出される。そして、この洗浄室1では、かかる室
内をほぼ水平に走行する金属帯3の上方及び下方にそれ
ぞれ洗浄液噴射ノズル5a、5bが設けられており、該
走行する金属帯3はこの洗浄液噴射ノズル5a、5bよ
り洗浄液6が吹き付けられ、その上面及び下面が洗浄さ
れる。また、こうして洗浄された金属帯3は、通常、絞
りロール7を通過することによりその表面に付着してい
る洗浄液の大部分が排除された後、該洗浄室1より、隣
接される乾燥室8移送され、加熱または熱風を吹きかけ
る等の手段により乾燥される。なお、こうした洗浄装置
において、洗浄室は連結して複数設けられても良い。That is, in the cleaning apparatus of FIG. 1, 1 is a cleaning chamber, in which the metal band 3 carried in through the metal band carry-in port 2 travels substantially horizontally in the room and the metal band discharge port 4 is provided.
More discharged. In the cleaning chamber 1, cleaning liquid jet nozzles 5a and 5b are provided above and below the metal strip 3 that travels substantially horizontally in the cleaning chamber 1. The traveling metal strip 3 has the cleaning liquid jet nozzle 5a. The cleaning liquid 6 is sprayed from 5b, and the upper and lower surfaces thereof are cleaned. Further, the metal strip 3 thus cleaned is usually passed through the squeeze roll 7 to remove most of the cleaning liquid adhering to the surface thereof, and then the drying chamber 8 adjacent to the cleaning chamber 1 is removed. It is transferred and dried by means such as heating or blowing hot air. In such a cleaning device, a plurality of cleaning chambers may be connected and provided.
【0011】しかして、この図1の洗浄装置では、上記
洗浄室1に設置される金属帯3に洗浄液を吹き付ける洗
浄液噴射ノズルのうち、金属帯の下面を洗浄するノズル
5bが、上記金属帯の走行方向に対して1〜45゜の角
度で、該走行方向の下流に向かって傾斜して設けられて
いる。このようにして本発明では、ほぼ水平方向に走行
する金属帯を洗浄するに際し、その下面の洗浄を、洗浄
液が上記特定の角度と向きで金属帯下面に吹き付けられ
るようにした点に最大の特徴を有するものである。前記
した通り水平方向に走行する金属帯の下面に垂直または
それに近い角度で洗浄液が吹き付けられた場合、該洗浄
液は、金属帯下面と接触後自重によりすぐに該金属帯面
から落下する。これに対して、上記の如くの角度と向き
で洗浄液が金属帯下面に吹き付けられた場合、この洗浄
液の噴射流は該金属帯の走行方向と同方向の強い速度ベ
クトルを有しているため、吹き付けられた洗浄液の大部
分は、かなりの間該金属帯と同伴してこの金属帯下面を
流れていく。その結果、本発明の洗浄方法によれば、走
行する金属帯の下面は、洗浄液との接触面積及び接触時
間とも著しく向上し、良好なる洗浄が施される。In the cleaning apparatus shown in FIG. 1, however, among the cleaning liquid jet nozzles for spraying the cleaning liquid onto the metal strip 3 installed in the cleaning chamber 1, the nozzle 5b for cleaning the lower surface of the metal strip is the metal strip It is provided at an angle of 1 to 45 with respect to the traveling direction and is inclined toward the downstream side in the traveling direction. Thus, in the present invention, when cleaning a metal strip that travels in a substantially horizontal direction, the cleaning of the lower surface of the metal strip has the greatest feature in that the cleaning liquid is sprayed onto the lower surface of the metal strip at the specific angle and direction. Is to have. As described above, when the cleaning liquid is sprayed vertically or at an angle close to the lower surface of the metal strip traveling in the horizontal direction, the cleaning liquid immediately falls from the metal strip surface by its own weight after contacting the lower surface of the metal strip. On the other hand, when the cleaning liquid is sprayed on the lower surface of the metal strip at the angle and direction as described above, the jet flow of the cleaning liquid has a strong velocity vector in the same direction as the traveling direction of the metal strip. Most of the sprayed cleaning liquid flows with the metal strip under the metal strip for a considerable period of time. As a result, according to the cleaning method of the present invention, the lower surface of the running metal strip is significantly improved in both the contact area and the contact time with the cleaning liquid, and good cleaning is performed.
【0012】本発明において、こうした金属帯下面に吹
き付けられる洗浄液は、吹き付けの向きが、金属帯の走
行方向と同じ向きであることが必要である。この向きが
金属帯の走行方向と同じでない場合、金属帯下面に吹き
付けられた洗浄液は、該金属帯と同伴してこの金属帯下
面を流れていくことが困難になる。また、この吹き付け
の向きが金属帯の走行方向と同じであっても、その吹き
付け角度が45°より大きい場合、洗浄液の噴射流に占
める該金属帯の走行方向と同方向の速度ベクトルの割合
が小さくなり、上記と同様に金属帯下面に吹き付けられ
た洗浄液は、該金属帯と同伴してこの金属帯下面を流れ
ていくことが困難になる。一方、この吹き付け角度を1
°より小さくすることは、実際上困難である。本発明に
おいて、金属帯に吹き付けられる洗浄液の該吹き付け角
度は、10〜40°であるのが最も好ましい。In the present invention, the cleaning liquid sprayed on the lower surface of the metal strip needs to be sprayed in the same direction as the traveling direction of the metal strip. If this direction is not the same as the running direction of the metal strip, it becomes difficult for the cleaning liquid sprayed on the lower surface of the metal strip to flow along the lower surface of the metal strip together with the metal strip. Further, even if the direction of spraying is the same as the traveling direction of the metal strip, if the spraying angle is larger than 45 °, the ratio of the velocity vector in the same direction as the traveling direction of the metal strip in the jet flow of the cleaning liquid is high. It becomes smaller, and it becomes difficult for the cleaning liquid sprayed on the lower surface of the metal strip to flow along the lower surface of the metal strip together with the metal strip as described above. On the other hand, this spray angle is 1
It is practically difficult to make it smaller than °. In the present invention, the spray angle of the cleaning liquid sprayed on the metal strip is most preferably 10 to 40 °.
【0013】本発明の洗浄方法において、使用する洗浄
液は、こうした金属帯の洗浄液として公知のものが何等
制限なく使用できる。具体的には、ナフテン系、パラフ
ィン系、芳香族系等の炭化水素系溶剤:トリクロロエタ
ン、パークロルエチレン、メチレンクロライド等の塩素
化炭化水素系溶剤:水等が挙げられる。これらの洗浄液
の内、上記炭化水素系溶剤や水は前記した通り油脂類等
の溶解力が比較的小さいものであるが、本発明の洗浄方
法は、該洗浄能力の小さい洗浄液を用いても、金属帯の
下面の洗浄を良好に行うことができ有用である。特に、
炭化水素系溶剤は可燃性であり、放電着火による爆発の
危険性等から、その洗浄能力を引き上げるため吹き付け
時の噴射圧力や液温等を高くすることが制限される場合
が多いが、本発明の洗浄方法はこうした場合において
も、優れた洗浄効果が発揮でき好適である。In the cleaning method of the present invention, as the cleaning liquid to be used, any known liquid for cleaning such metal bands can be used without any limitation. Specific examples thereof include hydrocarbon solvents such as naphthene-based, paraffin-based, and aromatic-based solvents: chlorinated hydrocarbon-based solvents such as trichloroethane, perchlorethylene, and methylene chloride: water. Among these cleaning liquids, the hydrocarbon solvent and water have a relatively small dissolving power for fats and oils as described above, but the cleaning method of the present invention uses a cleaning liquid having a small cleaning ability, This is useful because the lower surface of the metal strip can be cleaned well. In particular,
The hydrocarbon solvent is flammable, and from the danger of explosion due to discharge ignition, etc., it is often restricted to increase the injection pressure and the liquid temperature at the time of spraying in order to enhance the cleaning ability, but the present invention Even in such a case, the cleaning method of 1 is suitable because it can exhibit an excellent cleaning effect.
【0014】本発明において、洗浄液の噴射圧力及び液
温は、特に制限されるものではないが、通常、0.5〜
5kg/cm2及び20〜50℃のなかから採択され
る。炭化水素系溶剤等の可燃性の洗浄液を用いた場合に
は、この洗浄液の噴射圧力及び液温は、上記した理由か
ら0.5〜2kg/cm2及び20〜40℃であるのが
好ましい。In the present invention, the injection pressure and the liquid temperature of the cleaning liquid are not particularly limited, but are usually 0.5-.
5 kg / cm 2 and 20 to 50 ° C. are adopted. When a flammable cleaning liquid such as a hydrocarbon solvent is used, the injection pressure and the liquid temperature of the cleaning liquid are preferably 0.5 to 2 kg / cm 2 and 20 to 40 ° C. for the reasons described above.
【0015】次に、水平方向に走行する金属帯の走行速
度は、特に制限されるものではないが、通常、10〜8
0m/minであるのが好ましい。また、走行する金属
帯に吹き付けられる洗浄液量は、特に制限されるもので
はないが、好ましくは洗浄される金属帯下面の全面積に
対し、0.5〜1.5L/m2の洗浄液が吹き付けられ
るのが良い。こうした液量の洗浄液は、金属帯の走行方
向において1箇所に設けた洗浄液噴射ノズルのみから吹
き付けられても良いし、該走行方向において複数箇所に
設けられた洗浄液噴射ノズルから吹き付けられても良
い。Next, the traveling speed of the metal strip traveling in the horizontal direction is not particularly limited, but usually 10 to 8
It is preferably 0 m / min. The amount of the cleaning liquid sprayed on the running metal strip is not particularly limited, but preferably 0.5 to 1.5 L / m 2 of the cleaning liquid is sprayed on the entire area of the lower surface of the metal strip to be cleaned. It is good to be. The cleaning liquid having such a liquid amount may be sprayed only from the cleaning liquid injection nozzles provided at one position in the traveling direction of the metal strip, or may be sprayed from the cleaning liquid injection nozzles provided at a plurality of positions in the traveling direction.
【0016】なお、本発明において、洗浄に供される金
属帯の材質は特に制限されるものではなく、銅、鉄、
鉛、ニッケル、アルミニウム或いはそれらの合金等の
他、工業材料として使用される金属帯のあらゆる材質が
採用される。In the present invention, the material of the metal strip used for cleaning is not particularly limited, and copper, iron,
In addition to lead, nickel, aluminum or alloys thereof, any metal band used as an industrial material can be used.
【0017】[0017]
【発明の効果】本発明の洗浄方法によれば、金属帯の下
面に付着した油脂類等の汚れを簡単な手段で極めて良好
に除去することができる。従って、本発明の洗浄方法
は、油脂類等の溶解力が比較的小さい炭化水素系溶剤や
水等を洗浄液として用いた場合においても、良好に金属
帯の下面を洗浄することができる。特に、炭化水素系溶
剤等の可燃性を有する洗浄液を用いた場合においては、
噴出圧力や液温を高めなくても、上記の如く良好な洗浄
が行えるため、安全性の面からも極めて有用である。According to the cleaning method of the present invention, dirt such as fats and oils attached to the lower surface of the metal strip can be removed very well by a simple means. Therefore, according to the cleaning method of the present invention, the lower surface of the metal strip can be satisfactorily cleaned even when a hydrocarbon solvent or water having a relatively small dissolving power for oils and fats is used as the cleaning liquid. Especially when a flammable cleaning liquid such as a hydrocarbon solvent is used,
Since good cleaning can be performed as described above without increasing the ejection pressure or the liquid temperature, it is extremely useful in terms of safety.
【0018】[0018]
【実施例】以下、本発明をさらに具体的に説明するため
に実施例を示すが、本発明はこれらの実施例に何等限定
されるものではない。EXAMPLES Examples will be shown below to more specifically describe the present invention, but the present invention is not limited to these examples.
【0019】実施例1 図1に示される洗浄装置により、220mm幅で0.1
5mm厚のアルミニウム製の金属帯下面の洗浄を行っ
た。この洗浄装置において、該金属帯下面を洗浄するた
めに2箇所に設置される洗浄液噴射ノズル5bから噴射
される洗浄液の、金属帯の走行方向に対する吹き付け角
度及び金属帯の走行速度は、表1に示すような各条件と
した。また、かかる洗浄において、その他の洗浄条件
は、下記のようにした。Example 1 With the cleaning apparatus shown in FIG.
The lower surface of the metal strip made of aluminum having a thickness of 5 mm was washed. In this cleaning device, the spraying angle of the cleaning liquid sprayed from the cleaning liquid spraying nozzles 5b installed at two locations for cleaning the lower surface of the metal strip with respect to the traveling direction of the metal strip and the traveling speed of the metal strip are shown in Table 1. The conditions are as shown below. In addition, in such cleaning, other cleaning conditions were as follows.
【0020】・金属帯下面への付着油脂:圧延油、60
0mg/m2 ・洗浄液:パラフィン系炭化水素系溶剤 ・金属帯下面への洗浄液の吹き付け圧力:1.0kg/
cm2 ・洗浄液の液温:35℃ ・洗浄液の吹き付け量:30L/min 洗浄後、金属帯下面に付着する圧延油の残油量を測定し
た。その結果を表1に示した。Oils and fats attached to the lower surface of the metal strip: rolling oil, 60
0 mg / m 2・ Cleaning liquid: Paraffin hydrocarbon solvent ・ Spraying pressure of cleaning liquid on the bottom surface of metal strip: 1.0 kg /
cm 2 · Liquid temperature of cleaning liquid: 35 ° C. · Spraying amount of cleaning liquid: 30 L / min After cleaning, the residual oil amount of rolling oil adhering to the lower surface of the metal strip was measured. The results are shown in Table 1.
【0021】[0021]
【表1】 [Table 1]
【0022】比較例1 実施例1において、洗浄液噴射ノズル5bから噴射され
る洗浄液の吹き付け角度を90゜とし、また、金属帯の
走行速度を60m/minとする以外は、実施例1と同
様にして金属帯の洗浄を実施した。洗浄後、金属帯下面
に付着する圧延油の残油量を測定したところ、51mg
/m2であった。Comparative Example 1 The same as Example 1 except that the spray angle of the cleaning liquid sprayed from the cleaning liquid spray nozzle 5b was 90 ° and the traveling speed of the metal strip was 60 m / min. The metal strip was cleaned by using After cleaning, the amount of rolling oil remaining on the bottom surface of the metal strip was measured and found to be 51 mg.
/ M 2 .
【図1】図1は、本発明の金属帯の洗浄方法の代表的態
様を示す概略図である。FIG. 1 is a schematic view showing a typical embodiment of a method for cleaning a metal strip according to the present invention.
1:洗浄室 2:金属帯搬入口 3:金属帯 4:金属帯排出口 5a,5b:洗浄液噴射ノズル 6:洗浄液 7:絞りロール 8:乾燥室 9:熱風噴射ノズル 1: Washing chamber 2: Metal band carry-in port 3: Metal band 4: Metal band discharge port 5a, 5b: Cleaning liquid injection nozzle 6: Cleaning liquid 7: Squeeze roll 8: Drying chamber 9: Hot air injection nozzle
Claims (1)
浄液を吹き付けて該金属帯の下面を洗浄するに際し、上
記金属帯の走行方向に対して1〜45゜の角度で、該走
行方向の下流に向かって洗浄液を吹き付けることを特徴
とする金属帯の洗浄方法。1. When cleaning a lower surface of a metal strip by spraying a cleaning liquid on the lower surface of the metal strip traveling in a substantially horizontal direction, the traveling direction is 1 to 45 ° with respect to the traveling direction of the metal strip. A method for cleaning a metal strip, which comprises spraying a cleaning liquid toward the downstream of the metal strip.