JP3268122B2 - Metal strip cleaning method - Google Patents
Metal strip cleaning methodInfo
- Publication number
- JP3268122B2 JP3268122B2 JP13981394A JP13981394A JP3268122B2 JP 3268122 B2 JP3268122 B2 JP 3268122B2 JP 13981394 A JP13981394 A JP 13981394A JP 13981394 A JP13981394 A JP 13981394A JP 3268122 B2 JP3268122 B2 JP 3268122B2
- Authority
- JP
- Japan
- Prior art keywords
- cleaning liquid
- cleaning
- metal strip
- metal band
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、金属帯の洗浄方法に関
する。The present invention relates to a method for cleaning metal strips.
【０００２】[0002]
【従来の技術】例えば、圧延して得た金属帯を二次加工
したり或いはそのまま製品化する際には、圧延工程で付
着した油脂類等の汚れを除去する必要がある。こうした
金属帯を洗浄する方法として、走行する金属帯の表面に
洗浄液を順次吹き付けて汚れを除去する方法が行われて
いる。即ち、この方法によれば、洗浄室をほぼ水平方向
に走行する金属帯は、該洗浄室の上部及び下部に、上記
金属帯の走行方向において各複数設置された洗浄液噴射
ノズルから、その上面及び下面に洗浄液が順次吹き付け
られ、表面に付着した油脂類等の汚れが洗い落とされ
る。また、洗浄された金属帯は、通常、続いて乾燥室に
搬入され乾燥される。2. Description of the Related Art For example, when a metal strip obtained by rolling is subjected to secondary processing or is directly produced as a product, it is necessary to remove stains such as oils and fats adhered in a rolling step. As a method of cleaning such a metal band, a method of sequentially spraying a cleaning liquid on the surface of a running metal band to remove dirt is used. That is, according to this method, the metal band traveling substantially horizontally in the cleaning chamber has upper and lower portions of the cleaning liquid spray nozzles provided in the upper and lower portions of the cleaning chamber in the traveling direction of the metal band. A cleaning liquid is sequentially sprayed on the lower surface, and dirt such as oils and fats attached to the surface is washed away. Further, the washed metal strip is usually subsequently carried into a drying chamber and dried.
【０００３】[0003]
【発明が解決しようとする課題】以上のような金属帯の
洗浄方法において、前記洗浄室の上部及び下部に各複数
設置される洗浄液噴射ノズルは、通常いずれも、ほぼ水
平方向に走行する金属帯に対して洗浄液がほとんど垂直
に吹き付けられるように設けられている。そして、この
ようにして金属帯に吹き付けられた洗浄液は、走行する
金属帯の各面を流れる過程において、金属帯に付着した
汚れをくまなく洗い落としていく。In the above-described method of cleaning a metal band, a plurality of cleaning liquid jet nozzles respectively installed in the upper and lower portions of the cleaning chamber usually have a metal band running substantially horizontally. The cleaning liquid is provided so as to be sprayed almost vertically. Then, the cleaning liquid sprayed on the metal band in this manner, in a process of flowing on each surface of the traveling metal band, thoroughly removes dirt attached to the metal band.
【０００４】ところが、かかる金属帯に吹き付けられた
洗浄液が、このように金属帯上を流れ、該金属帯に随伴
して、洗浄液の吹き付け箇所よりもずっと下流に移動し
ていった場合、洗浄室より持ち出される洗浄液の量が増
大する。特に、金属帯の上面では、前記の如くその上方
から垂直に吹き付けられた洗浄液は、金属帯の側縁部に
流れつくまでは該金属帯上から落下しないため、この洗
浄室より持ち出される洗浄液の量は相当な量となる。な
お、こうした金属帯の洗浄方法では、かかる洗浄室より
の洗浄液の持ち出しを防止するため、通常、走行する金
属帯は洗浄室から搬出される前に一対の絞りロールの間
を通過する構造になっていることが多い。しかし、こう
した場合でも、前記金属帯の上面等の該金属帯面に随伴
する洗浄液量が多い金属帯面では、かかる多量の洗浄液
のために上記シールロールが液面上に浮き上がって回転
するようになり、思うような洗浄液排出効果があがらな
くなり易い。しかして、このように、洗浄室からの洗浄
液の持ち出し量が多くなると、洗浄後の金属帯の乾燥時
間が長くなったり、洗浄液に含有される汚染物質が金属
帯に再付着して洗浄が不十分になったりする。However, when the cleaning liquid sprayed onto the metal band flows over the metal band and moves along the metal band to a position far downstream from the cleaning liquid spraying position, the cleaning chamber is not cleaned. The amount of cleaning liquid taken out increases. In particular, on the upper surface of the metal band, as described above, the cleaning liquid sprayed vertically from above does not fall from above the metal band until it flows to the side edge of the metal band. The amount will be a considerable amount. In addition, in such a method of cleaning a metal band, in order to prevent the cleaning liquid from being taken out of the cleaning chamber, the traveling metal band usually has a structure passing between a pair of squeezing rolls before being carried out of the cleaning chamber. Often have. However, even in such a case, on a metal band surface having a large amount of cleaning liquid accompanying the metal band surface such as the upper surface of the metal band, the seal roll floats above the liquid surface and rotates because of such a large amount of cleaning liquid. It is easy to lose the desired cleaning liquid discharge effect. As described above, when the amount of the cleaning liquid taken out of the cleaning chamber is increased, the drying time of the metal band after the cleaning is prolonged, or the contaminants contained in the cleaning liquid re-adhere to the metal band and cleaning becomes impossible. Or enough.
【０００５】以上の背景から、上記した如くに水平方向
に走行する金属帯に洗浄液を吹き付けて該金属帯を洗浄
するに際し、この金属帯に随伴して洗浄液が下流に移動
することを抑制する方法の開発が望まれていた。[0005] In view of the above background, as described above, when a cleaning solution is sprayed on a metal strip traveling in the horizontal direction to wash the metal strip, a method of suppressing the movement of the cleaning liquid downstream accompanying the metal strip. The development of was desired.
【０００６】[0006]
【課題を解決するための手段】上記した問題点に鑑み、
本発明者らは鋭意研究を続けてきた。その結果、ほぼ水
平方向に走行する金属帯の同一面に、該金属帯の走行方
向における複数箇所から洗浄液を吹き付けて該金属帯を
洗浄するに際し、走行する金属帯の最下流に吹き付ける
洗浄液を、特定の向きと角度で吹き付けることにより、
上記の問題点が解決できることを見いだし本発明を提案
するに至った。SUMMARY OF THE INVENTION In view of the above problems,
The present inventors have been working diligently. As a result, on the same surface of the metal band traveling in a substantially horizontal direction, when cleaning the metal band by spraying the cleaning liquid from a plurality of locations in the traveling direction of the metal band, the cleaning liquid sprayed to the most downstream of the traveling metal band, By spraying at a specific direction and angle,
The present inventors have found that the above problems can be solved, and have proposed the present invention.
【０００７】即ち、本発明は、油脂類の汚れが付着した
金属帯がほぼ水平方向に走行する、該金属帯の同一面
に、該金属帯の走行方向における複数箇所から洗浄液を
吹き付けて金属帯を洗浄する方法において、走行する金
属帯の最下流に吹き付ける洗浄液を、上記金属帯の走行
方向に対して４０〜６５゜の角度で、該走行方向の上流
に向かって吹き付けることを特徴とする金属帯の洗浄方
法である。That is, in the present invention, dirt of oils and fats adheres.
Metal strip travels substantially horizontally, on the same surface of the metal strip, a method of cleaning a metallic strip by blowing a cleaning liquid from a plurality of locations in the traveling direction of the metal strip, blown onto the most downstream metal strip traveling A method for cleaning a metal band, comprising spraying a cleaning liquid at an angle of 40 to 65 ° with respect to the running direction of the metal band toward an upstream side of the running direction.
【０００８】本発明の洗浄方法は、ほぼ水平方向、好適
には該水平方向に対し±１０°内の走行角度で走行する
金属帯の同一面に、該金属帯の走行方向における複数箇
所から洗浄液を吹き付けて該金属帯を洗浄する場合であ
れば、何等制限されることなく採用することができる。
通常は、図１に示す如くの一般的な金属帯の洗浄装置に
おいて、金属帯の上面及び／または下面を洗浄する方法
として採用するのが好ましい。[0008] The cleaning method of the present invention comprises the steps of: cleaning a cleaning liquid from a plurality of locations in the running direction of the metal band on the same surface of the metal band running in a substantially horizontal direction, preferably at a running angle within ± 10 ° from the horizontal direction; Can be adopted without any limitation as long as the metal band is washed by spraying.
Normally, it is preferable to adopt a general metal band cleaning apparatus as shown in FIG. 1 as a method for cleaning the upper surface and / or lower surface of the metal band.
【０００９】即ち、図１の洗浄装置において１は洗浄室
であり、該洗浄室１では、金属帯搬入口２より搬入され
た金属帯３は室内をほぼ水平に走行し、金属帯排出口４
より排出される。そして、この洗浄室１では、かかる室
内をほぼ水平に走行する金属帯３の上方及び下方にそれ
ぞれ複数の洗浄液噴射ノズル５ａ、５ｂ、５ｃ、５
ａ’、５ｂ’、５ｃ’が設けられており、該走行する金
属帯３はこの洗浄液噴射ノズルにより洗浄液６が吹き付
けられ、その上面及び下面が洗浄される。ここで、上記
洗浄液噴射ノズルは、金属帯の上面及び下面の各面にお
いて、通常、金属帯の長さ５〜１０ｃｍごとに設けられ
るのが一般的である。また、こうして洗浄された金属帯
３は、通常、絞りロール７を通過することによりその表
面に付着している洗浄液の大部分が排除された後、該洗
浄室１より、隣接される乾燥室８に移送され、加熱また
は熱風を吹きかける等の手段により乾燥される。なお、
こうした洗浄装置において、洗浄室は連結して複数設け
られても良い。That is, in the cleaning apparatus shown in FIG. 1, reference numeral 1 denotes a cleaning room. In the cleaning room 1, a metal band 3 carried in from a metal band carrying port 2 travels substantially horizontally in the room, and a metal band discharge port 4 is provided.
Is more exhausted. In the cleaning chamber 1, a plurality of cleaning liquid spray nozzles 5a, 5b, 5c, 5c are provided above and below the metal strip 3 traveling substantially horizontally in the chamber.
a ′, 5b ′ and 5c ′ are provided, and the cleaning liquid 6 is sprayed on the traveling metal band 3 by the cleaning liquid injection nozzle, and the upper and lower surfaces thereof are cleaned. Here, the cleaning liquid injection nozzle is generally provided at every 5 to 10 cm length of the metal band on each of the upper surface and the lower surface of the metal band. Further, the metal strip 3 thus washed is usually passed through the squeezing roll 7 to remove most of the cleaning liquid adhering to the surface thereof. And dried by means such as heating or blowing hot air. In addition,
In such a cleaning apparatus, a plurality of cleaning chambers may be connected and provided.
【００１０】そうして、この図１の洗浄装置では、上記
洗浄室１に設置される金属帯３の上面及び下面にそれぞ
れ洗浄液を吹き付ける洗浄液噴射ノズルのうち、走行す
る金属帯に対して最下流に位置するノズル５ｃ、５ｃ’
が、上記金属帯の走行方向に対して４０〜６５゜の角度
で、該走行方向の上流に向かって傾斜して設けられてい
る。このようにして本発明では、ほぼ水平方向に走行す
る金属帯の同一面に、該金属帯の走行方向における複数
箇所から洗浄液を吹き付けて該金属帯を洗浄するに際
し、走行する金属帯の最下流に吹き付ける洗浄液が上記
特定の角度と向きで吹き付けられるようにした点に最大
の特徴を有するものである。前記した通り水平方向に走
行する金属帯の面、特に上面に、垂直またはそれに近い
角度で洗浄液が吹き付けられた場合、該洗浄液の多くの
量は、金属帯に随伴して、洗浄液の吹き付け箇所よりも
ずっと下流に移動していく。ところが、上記の如く吹き
付けられる洗浄液のうち、走行する金属帯の最下流に吹
き付けるものが上記特定の角度と向きで噴射された場
合、この洗浄液の流れは、前記金属帯に随伴して流れる
洗浄液の流れと逆行するため、結果として、かかる金属
帯に随伴する洗浄液の流れは遮断される。In the cleaning apparatus shown in FIG. 1, among the cleaning liquid jet nozzles for spraying the cleaning liquid onto the upper and lower surfaces of the metal strip 3 installed in the cleaning chamber 1, the cleaning liquid jet nozzle is located at the most downstream position with respect to the traveling metal strip. Nozzles 5c, 5c 'located at
Are provided at an angle of 40 to 65 ° with respect to the traveling direction of the metal strip and inclined toward the upstream in the traveling direction. In this manner, in the present invention, the cleaning liquid is sprayed onto the same surface of the metal band traveling in a substantially horizontal direction from a plurality of locations in the traveling direction of the metal band to wash the metal band. The most characteristic feature is that the cleaning liquid is sprayed at the above specific angle and direction. As described above, when the cleaning liquid is sprayed on the surface of the metal strip traveling in the horizontal direction, particularly on the upper surface, at a vertical angle or an angle close thereto, a large amount of the cleaning liquid accompanies the metal strip, and is discharged from the point where the cleaning liquid is sprayed. Also move far downstream. However, among the cleaning liquids sprayed as described above, when the one sprayed at the most downstream of the traveling metal band is jetted at the specific angle and direction, the flow of the cleaning liquid is caused by the cleaning liquid flowing accompanying the metal band. As a result, the flow of the cleaning liquid associated with such a metal strip is interrupted.
【００１１】本発明において、走行する金属帯の最下流
に吹き付ける洗浄液は、吹き付けの向きが、金属帯の走
行方向を上流に向かう向きであることが必要である。こ
の向きが上記向きでない場合、金属帯面に吹き付けられ
た洗浄液は、前記金属帯に随伴する洗浄液の流れを遮断
することができなくなる。また、この吹き付けの向きが
該向きであっても、その吹き付け角度が４０〜６５°に
ないと、上記金属帯に随伴する洗浄液の流れを遮断する
効果が充分でなくなる。即ち、該角度が６５°より大き
いと、吹き付けられた洗浄液の金属帯上の流れに、該金
属帯上を下流に向かう向きが強く生じるようになる。一
方、該角度が４０°より小さいと、洗浄液噴射ノズルか
ら噴射された洗浄液の、実際に金属帯面に接するまでの
距離が長くなり、洗浄液の噴射流の威力が十分でなくな
ったり、或いは金属帯面に接触しても該金属帯に随伴し
て下流に流れる洗浄液流を遮断せず、該洗浄液流上を単
に逆方向に上滑りして流れるようになる。なお、本発明
において、金属帯の同一面に吹き付ける複数の洗浄液の
うち、上記走行する金属帯に対して最下流に位置するも
の以外の洗浄液の吹き付けの向きと角度は、特に制限さ
れるものでなく如何なる向きと角度としても良い。通常
は、金属帯の面に対して、垂直またはそれに近い角度で
吹き付けらるのが一般的である。In the present invention, it is necessary that the direction of spraying of the cleaning liquid sprayed to the lowermost stream of the traveling metal strip is the direction in which the traveling direction of the metal strip is directed to the upstream. If the direction is not the above direction, the cleaning liquid sprayed on the metal band surface cannot block the flow of the cleaning liquid accompanying the metal band. Even if the spray direction is the same, if the spray angle is not in the range of 40 to 65 °, the effect of blocking the flow of the cleaning liquid accompanying the metal band becomes insufficient. That is, if the angle is greater than 65 °, the flow of the sprayed cleaning liquid on the metal band will be strongly directed downstream on the metal band. On the other hand, if the angle is smaller than 40 °, the distance of the cleaning liquid injected from the cleaning liquid injection nozzle until it actually contacts the metal band surface becomes longer, and the power of the cleaning liquid jet flow becomes insufficient, or The contact with the surface does not block the flow of the cleaning liquid flowing downstream along with the metal band, but simply slides upward on the flow of the cleaning liquid in the opposite direction. In the present invention, among the plurality of cleaning liquids sprayed on the same surface of the metal band, the direction and angle of spraying of the cleaning liquid other than the one located at the most downstream position with respect to the traveling metal band are particularly limited. Instead, any orientation and angle may be used. Usually, it is common to spray at an angle perpendicular or close to the plane of the metal strip.
【００１２】本発明の洗浄方法において、使用する洗浄
液は、金属帯の洗浄液として公知のものが何等制限なく
使用できる。具体的には、ナフテン系、パラフィン系、
芳香族系等の炭化水素系溶剤：トリクロロエタン、パー
クロルエチレン、メチレンクロライド等の塩素化炭化水
素系溶剤：水等が挙げられる。In the cleaning method of the present invention, any known cleaning liquid for cleaning metal strips can be used without any limitation. Specifically, naphthenic, paraffinic,
Hydrocarbon solvents such as aromatic solvents: chlorinated hydrocarbon solvents such as trichloroethane, perchlorethylene, and methylene chloride: water.
【００１３】本発明において、洗浄液の噴射圧力及び液
温は、特に制限されるものではないが、通常、０．５〜
５ｋｇ／ｃｍ2及び２０〜５０℃のなかから採択され
る。炭化水素系溶剤等の可燃性の洗浄液を用いた場合に
は、この洗浄液の噴射圧力及び液温は、０．５〜２ｋｇ
／ｃｍ2及び２０〜４０℃であるのが好ましい。In the present invention, the jet pressure and temperature of the cleaning liquid are not particularly limited, but are usually 0.5 to 0.5.
Adopted from 5 kg / cm 2 and 20-50 ° C. When a flammable cleaning liquid such as a hydrocarbon solvent is used, the injection pressure and the liquid temperature of the cleaning liquid are 0.5 to 2 kg.
/ Cm 2 and 20 to 40 ° C. are preferred.
【００１４】次に、水平方向に走行する金属帯の走行速
度は、特に制限されるものではないが、通常、１０〜８
０ｍ／ｍｉｎであるのが好ましい。また、走行する金属
帯に吹き付けられる洗浄液量は、特に制限されるもので
はないが、好ましくは洗浄される金属帯の全面積に対
し、０．５〜１．５Ｌ／ｍ2の洗浄液が吹き付けられる
のが良い。Next, the traveling speed of the metal strip traveling in the horizontal direction is not particularly limited, but is usually 10-8.
It is preferably 0 m / min. The amount of the cleaning liquid sprayed on the traveling metal strip is not particularly limited, but preferably, 0.5 to 1.5 L / m 2 of the cleaning liquid is sprayed on the entire area of the metal strip to be cleaned. Is good.
【００１５】なお、本発明において、洗浄に供される金
属帯の材質は特に制限されるものではなく、銅、鉄、
鉛、ニッケル、アルミニウム或いはそれらの合金等の
他、工業材料として使用される金属帯のあらゆる材質が
採用される。In the present invention, the material of the metal strip to be cleaned is not particularly limited, and copper, iron,
In addition to lead, nickel, aluminum or alloys thereof, any material of a metal band used as an industrial material is employed.
【００１６】[0016]
【発明の効果】本発明の洗浄方法によれば、水平方向に
走行する金属帯に洗浄液を吹き付けて該金属帯を洗浄す
るに際し、この金属帯の洗浄液の吹き付け箇所より下流
に、洗浄液が流れることが抑制される。従って、本発明
の洗浄方法によれば、金属帯に随伴して洗浄室より持ち
出される洗浄液の量を低下させることができ、引いては
洗浄後の金属帯の乾燥時間を短縮化させたり、洗浄液に
含有される汚染物質の金属帯への再付着等を防止するこ
とができる。According to the cleaning method of the present invention, when the cleaning liquid is sprayed on the metal strip traveling in the horizontal direction to clean the metal strip, the cleaning liquid flows downstream from the cleaning liquid spraying position of the metal strip. Is suppressed. Therefore, according to the cleaning method of the present invention, the amount of the cleaning liquid taken out of the cleaning chamber accompanying the metal band can be reduced, and thus the drying time of the metal band after cleaning can be shortened, or the cleaning liquid can be reduced. Of the contaminants contained in the metal strip can be prevented.
【００１７】[0017]
【実施例】以下、本発明をさらに具体的に説明するため
に実施例を示すが、本発明はこれらの実施例に何等限定
されるものではない。EXAMPLES Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples.
【００１８】実施例１ 図１に示される洗浄装置により、２２０ｍｍ幅で０．１
５ｍｍ厚のアルミニウム製の金属帯の洗浄を行った。こ
の洗浄装置において、該金属帯の上面及び下面を洗浄す
るために設置される洗浄液噴射ノズルのうち、最下流に
位置する５ｃ、５ｃ’から噴射される洗浄液の、金属帯
の走行方向に対する吹き付け角度及び金属帯の走行速度
は、表１に示すような各条件とした。なお、該洗浄装置
において、上記最下流に位置する洗浄液噴射ノズル以外
のノズルから噴射される洗浄液は、金属帯の上面及び下
面に対して垂直に吹き付けられるようにした。また、か
かる洗浄において、その他の洗浄条件は、下記のように
した。Example 1 The cleaning apparatus shown in FIG.
A 5 mm thick aluminum metal strip was cleaned. In this cleaning device, of the cleaning liquid jet nozzles installed for cleaning the upper and lower surfaces of the metal strip, the spray angle of the cleaning liquid jetted from the lowermost stream 5c, 5c 'with respect to the traveling direction of the metal strip. The running speed of the metal strip was set to each condition as shown in Table 1. In the cleaning device, the cleaning liquid jetted from the nozzles other than the cleaning liquid jet nozzle located at the most downstream position is sprayed perpendicular to the upper and lower surfaces of the metal strip. In this cleaning, other cleaning conditions were as follows.
【００１９】・洗浄液：パラフィン系炭化水素系溶剤 ・各洗浄液噴射ノズルからの洗浄液の吹き付け圧力：
１．０ｋｇ／ｃｍ2 ・洗浄液の液温：３５℃ ・洗浄液の吹き付け量：１５Ｌ／ｍｉｎ 洗浄時において、金属帯に随伴して洗浄室から持ち出さ
れる洗浄液量を測定して表１に示した。・ Cleaning liquid: paraffinic hydrocarbon solvent ・ Blowing pressure of cleaning liquid from each cleaning liquid spray nozzle:
1.0 kg / cm 2 · Cleaning liquid temperature: 35 ° C · Spraying rate of cleaning liquid: 15 L / min During cleaning, the amount of cleaning liquid taken out of the cleaning chamber along with the metal band was measured and shown in Table 1.
【００２０】[0020]
【表１】 [Table 1]
【００２１】比較例１ 実施例１において、洗浄液噴射ノズル５ｃ、５ｃ’から
噴射される洗浄液の吹き付け角度を９０゜とする以外
は、実施例１と同様にして金属帯の洗浄を実施した。な
お、金属帯の走行速度は６０ｍ／ｍｉｎとした。洗浄
後、金属帯に随伴して洗浄室から持ち出される洗浄液量
を測定したところ、１．３５Ｌ／ｈｒであった。Comparative Example 1 A metal strip was cleaned in the same manner as in Example 1, except that the spray angle of the cleaning liquid jetted from the cleaning liquid jet nozzles 5c and 5c 'was 90 °. The running speed of the metal strip was 60 m / min. After the washing, the amount of the washing liquid taken out of the washing chamber accompanying the metal band was measured and found to be 1.35 L / hr.
【００２２】比較例２ 実施例１において、洗浄液噴射ノズル５ｃ、５ｃ’から
噴射される洗浄液の吹き付け角度を３０゜とする以外
は、実施例１と同様にして金属帯の洗浄を実施した。な
お、金属帯の走行速度は６０ｍ／ｍｉｎとした。洗浄
後、金属帯に随伴して洗浄室から持ち出される洗浄液量
を測定したところ、１．６１Ｌ／ｈｒであった。Comparative Example 2 A metal strip was cleaned in the same manner as in Example 1 except that the spray angle of the cleaning liquid jetted from the cleaning liquid jet nozzles 5c and 5c 'was 30 °. The running speed of the metal strip was 60 m / min. After the washing, the amount of the washing liquid taken out of the washing chamber accompanying the metal band was measured and found to be 1.61 L / hr.
【図１】図１は、本発明の金属帯の洗浄方法の代表的態
様を示す概略図である。FIG. 1 is a schematic view showing a typical embodiment of the metal strip cleaning method of the present invention.
１：洗浄室 ２：金属帯搬入口 ３：金属帯 ４：金属帯排出口 ５ａ、５ｂ、５ｃ、５ａ’、５ｂ’、５ｃ’：洗浄液噴
射ノズル ６：洗浄液 ７：絞りロール ８：乾燥室 ９：熱風噴射ノズル1: Cleaning room 2: Metal band carry-in port 3: Metal band 4: Metal band discharge port 5a, 5b, 5c, 5a ', 5b', 5c ': Cleaning liquid injection nozzle 6: Cleaning liquid 7: Squeezing roll 8: Drying room 9 ： Hot air spray nozzle
Claims (1)
方向に走行する、該金属帯の同一面に、該金属帯の走行
方向における複数箇所から洗浄液を吹き付けて金属帯を
洗浄する方法において、走行する金属帯の最下流に吹き
付ける洗浄液を、上記金属帯の走行方向に対して４０〜
６５゜の角度で、該走行方向の上流に向かって吹き付け
ることを特徴とする金属帯の洗浄方法。1. A metal strip dirty oils and fats is attached travels substantially horizontally, on the same surface of the metal strip, by spraying the cleaning liquid from the plurality of positions in the running direction of the metal strip to clean the metallic strip In the method, the cleaning liquid sprayed to the most downstream of the traveling metal strip is applied to the cleaning liquid in a direction of 40 to 100 with respect to the traveling direction of the metal strip.
A method for cleaning a metal strip, characterized by spraying at an angle of 65 ° toward the upstream in the running direction.