JPH0643097B2 - Method for producing biaxially oriented polyester film - Google Patents
Method for producing biaxially oriented polyester filmInfo
- Publication number
- JPH0643097B2 JPH0643097B2 JP2077360A JP7736090A JPH0643097B2 JP H0643097 B2 JPH0643097 B2 JP H0643097B2 JP 2077360 A JP2077360 A JP 2077360A JP 7736090 A JP7736090 A JP 7736090A JP H0643097 B2 JPH0643097 B2 JP H0643097B2
- Authority
- JP
- Japan
- Prior art keywords
- tenter
- film
- polyester film
- biaxially oriented
- oriented polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、二軸配向ポリエステルフィルムの製造方法に
関するものであり、詳しくは、テンター法による二軸配
向ポリエステルフィルムの製造において、特定の態様の
弛緩処理を採用することにより、平面性が良好で且つ長
手方向の破断時強度が大きく、特に、１００℃を超える
高温加熱時の収縮率が小さくて高度な寸法安定性を有す
る二軸配向ポリエステルフィルムの工業的有利な製造方
法に関するものである。TECHNICAL FIELD The present invention relates to a method for producing a biaxially oriented polyester film, and more specifically, in the production of a biaxially oriented polyester film by a tenter method, By adopting the relaxation treatment, the biaxially oriented polyester film has good flatness and high strength at break in the longitudinal direction, and particularly has a small shrinkage factor at high temperature heating exceeding 100 ° C. and has high dimensional stability. And an industrially advantageous production method thereof.
本発明方法による二軸配向ポリエステルフィルムは、そ
の高度な寸法安定性故に、磁気記録用途は勿論のこと、
特に、光学的用途、電気的用途に好適である。The biaxially oriented polyester film produced by the method of the present invention is not limited to magnetic recording applications because of its high dimensional stability.
In particular, it is suitable for optical applications and electrical applications.
二軸配向ポリエステルフィルムは、機械的性質、耐熱性
および耐薬品性に優れているため、広範囲の用途に利用
されている。The biaxially oriented polyester film has excellent mechanical properties, heat resistance and chemical resistance, and is therefore used in a wide range of applications.
そして、磁気記録用途などにおいては、良好な寸法安定
性が要求され、特に、透明導電性フィルム等の光学的用
途や電気絶縁性フィルム等の電気的用途においては、１
５０℃に調節された空気中に３０分放置後の収縮率が
０．５％以下という一層高度な寸法安定性が要求され
る。In magnetic recording applications, good dimensional stability is required, and particularly in optical applications such as transparent conductive films and electrical applications such as electrically insulating films, 1
A higher degree of dimensional stability is required, such that the shrinkage rate after standing for 30 minutes in air adjusted to 50 ° C. is 0.5% or less.
二軸配向ポリエステルフィルムは、一般的には、テンタ
ー法により製造され、フィルムの寸法安定性は、熱固定
後の二軸配向ポリエステルフィルムに弛緩処理を行うこ
とにより付与することができる。The biaxially oriented polyester film is generally produced by a tenter method, and the dimensional stability of the film can be imparted by subjecting the biaxially oriented polyester film after heat setting to a relaxation treatment.
テンター法においては、二軸配向ポリエステルフィルム
の速度はテンターレールを走行するテンタークリップの
速度（以下、「テンター速度」という）でコントロール
されるが、フィルムの両端部がクリップから開放された
後は、後続の引取りロールの速度でコントロールされ
る。In the tenter method, the speed of the biaxially oriented polyester film is controlled by the speed of the tenter clip traveling on the tenter rail (hereinafter, referred to as "tenter speed"), but after both ends of the film are released from the clip, It is controlled by the speed of the subsequent take-up roll.
従って、テンター速度に比して引取りロールの速度を小
さくすることにより、二軸配向ポリエステルフィルム
は、長手方向（縦方向）において必要な弛緩状態に保た
れ、この状態でフィルムは熱処理を受けることになる。Therefore, by decreasing the speed of the take-up roll in comparison with the tenter speed, the biaxially oriented polyester film is kept in the necessary relaxed state in the longitudinal direction (longitudinal direction), and the film is subjected to heat treatment in this state. become.
そして、弛緩処理は、肉厚部の両端耳部を除去して行う
のが有効であり好ましい。Then, it is effective and preferable to perform the relaxation treatment by removing both end ears of the thick portion.
上記のような方法として、例えば、特公昭５７−５４２
９０号公報には、テンタークリップに把持されている二
軸配向ポリエステルフィルムの左右の両端耳部を切断
し、この両端耳部以外の中央部のみをテンタークリップ
の拘束から開放することにより、テンター内において弛
緩処理を行う方法が開示されている。Examples of the method as described above include Japanese Patent Publication No. 57-542.
No. 90 discloses that the biaxially oriented polyester film gripped by the tenter clip is cut at both left and right end ears, and only the central portion other than the both end ears is released from the restraint of the tenter clip. Discloses a method of performing a relaxation treatment.
また、特開平１−３１０９３５号公報には、二軸配向ポ
リエステルフィルムの両端耳部の切断をテンターレール
の出口付近で行うことにより、比較的低温で弛緩処理を
行う方法が開示されている。Further, JP-A-1-310935 discloses a method of performing relaxation treatment at a relatively low temperature by cutting both ends of the biaxially oriented polyester film near the exit of the tenter rail.
しかしながら、特公昭５７−５４２９０号公報に記載さ
れた方法では、高温部において耳部の切断を行うことか
ら、次の問題がある。However, the method disclosed in Japanese Examined Patent Publication No. 57-54290 has the following problems because the ear portion is cut at the high temperature portion.
すなわち、切断部に急激な幅収縮が生じてフィルムが破
断し易くなると共に幅方向の熱収縮応力が小さくなる。
また、切断刃の取付位置が高温であるため、切断刃の交
換性が悪く保全が困難である。That is, abrupt width shrinkage occurs at the cut portion, the film is easily broken, and the heat shrinkage stress in the width direction becomes small.
Further, since the mounting position of the cutting blade is high, the replaceability of the cutting blade is poor and maintenance is difficult.
また、上記方法では、両端耳部の切断された被弛緩処理
フィルムは何等の支持もなされずに自由状態となってい
ることから、特に弛緩率を大きくし、高度な寸法安定性
の二軸配向ポリエステルフィルムを製造せんとする場合
には、次のような重大な問題がある。Further, in the above method, the film to be relaxed whose both ears have been cut is in a free state without any support, so that the relaxation rate is particularly increased, and the biaxial orientation has a high degree of dimensional stability. When manufacturing a polyester film, there are the following serious problems.
すなわち、被弛緩処理フィルムが自重弛みを起こし、こ
れがフィルムの収縮応力よりも大きい場合は、中央部に
シワが入って平面性が悪化し、最悪の場合には、テンタ
ー内のノズルの各部に接触してフィルムに傷が入る。従
って、斯かる問題を回避するために、弛緩率を制限せざ
る得ない。また、同時に起こる幅方向の弛緩をコントロ
ールし得ないために、これが過大となり、高温加熱使用
の用途においては、二軸配向ポリエステルフィルムが膨
張して使用し得ないという問題がある。更に、生産性を
高めるたるに走行速度を大きくした場合は、被弛緩処理
フィルムがバタついて切断部から破断する。この傾向
は、フィルム厚みが小さくなるほど顕著となる。In other words, if the film to be relaxed sags due to its own weight, and if it is larger than the shrinkage stress of the film, wrinkles will form in the center and the flatness will deteriorate, and in the worst case, it will contact each part of the nozzle in the tenter. Then the film gets scratched. Therefore, in order to avoid such a problem, there is no choice but to limit the relaxation rate. Moreover, since the simultaneous relaxation in the width direction cannot be controlled, this becomes excessive, and there is a problem that the biaxially oriented polyester film expands and cannot be used in applications where high temperature heating is used. Furthermore, when the running speed is increased to increase productivity, the film to be relaxed flaps and breaks from the cut portion. This tendency becomes more remarkable as the film thickness becomes smaller.
そして、被弛緩処理フィルムの自由状態による上記の問
題は、例えば、１００℃以上の高い弛緩温度を採用し、
高度な寸法安定性の二軸配向ポリエステルフィルムを製
造せんとする場合に助長される。And the above-mentioned problem due to the free state of the film to be relaxed, for example, adopts a high relaxation temperature of 100 ° C. or higher,
This is facilitated when manufacturing a biaxially oriented polyester film having a high dimensional stability.
一方、特開平１−３１０９３５号公報に記載された方法
は、前記の高温部における耳部切断による問題を解消し
た方法ではあるが、特公昭５７−４２９０号公報に記載
された方法と同様に、被弛緩処理フィルムの支持につい
ての手当てが何等なされていないために、比較的低温で
弛緩処理を行うにせよ、被弛緩処理フィルムの自由状態
による前記問題は解消できない。On the other hand, the method described in Japanese Patent Application Laid-Open No. 1-310935 is a method that solves the problem due to the cutting of the ears in the high temperature portion, but like the method described in Japanese Patent Publication No. 57-4290, Since no measures have been taken to support the relaxed film, the above-mentioned problems due to the free state of the relaxed film cannot be solved even if the relaxation process is performed at a relatively low temperature.
そして、被弛緩処理フィルムの自由状態による前記問題
を解決する方法としては、幅出しロール（クロスガイダ
ーロール）の利用が考えられる。Then, as a method of solving the above-mentioned problem due to the free state of the film to be relaxed, use of a tenter roll (cross guider roll) can be considered.
しかしながら、特公昭５７−５４２９０号公報に記載さ
れた方法の場合には、テンター内が高温であるために、
テンター内に配置された幅出しロールの保全が困難であ
るばかりか、幅出しロールがテンター内の空気流を乱し
てフィルム温度の均一性が損われるという問題がある。
仮に、このような問題に対処できたとしても、テンター
レールとの関係において幅出しロールの取付けが極めて
複雑となり、設備的な不利益は免れ得ない。However, in the case of the method described in JP-B-57-54290, the temperature inside the tenter is high,
Not only is it difficult to maintain the tenter rolls arranged in the tenter, but also the tenter rolls disturb the air flow in the tenter to impair the uniformity of the film temperature.
Even if such a problem could be dealt with, installation of the tenter roll would be extremely complicated in relation to the tenter rail, and there would be inevitable equipment disadvantages.
一方、特開平１−３１０９３５号公報に記載された方法
の場合には、上記ほどの問題はないにせよ、同公報に示
されたように、テンターレール上で耳部フィルムの切断
を行って弛緩処理を行う以上、幅出しロールの取付け
は、依然前記と同様に複雑であり、設備的には不利であ
る。On the other hand, in the case of the method described in Japanese Patent Application Laid-Open No. 1-310935, even if there is no problem as described above, as shown in the same publication, the ear film is cut on the tenter rail to relax the film. As long as the processing is performed, the mounting of the tenter roll is still complicated as described above, which is disadvantageous in terms of equipment.
本発明の目的は、特開平１−３１０９３５号公報に記載
された方法と同様に、特公昭５７−５４２９０号公報に
記載された方法の高温部における耳部切断による問題を
解消しつつ、特開平１−３１０９３５号公報に記載され
た方法とは異なって特公昭５７−５４２９０号公報に記
載された方法と同様の高温弛緩処理を可能とし、しか
も、耳部の切断された被弛緩処理フィルムの自由状態に
よる前記の種々の問題を一挙に解決し、特に、高度な寸
法安定性を有する二軸延伸ポリエステルフィルムの工業
的有利な製造方法を提供することにある。An object of the present invention is to solve the problem caused by cutting the ears in the high temperature part of the method described in Japanese Patent Publication No. 57-54290, as in the method described in Japanese Patent Application Laid-Open No. 1-310935, and Unlike the method described in Japanese Patent Publication No. 1-310935, the same high-temperature relaxation treatment as the method described in Japanese Patent Publication No. 57-54290 is possible, and, moreover, the freeness of the processed film to be relaxed with the ears cut off. SUMMARY OF THE INVENTION It is an object of the present invention to solve the above-mentioned various problems depending on the conditions at once, and particularly to provide an industrially advantageous method for producing a biaxially stretched polyester film having a high degree of dimensional stability.
本発明の上記目的は、テンター法で二軸配向されたポリ
エステルフィルムをテンターの熱固定ゾーンで熱固定し
た後、テンタークリップから開放し、テンター速度より
遅い速度の引取りロールにより弛緩状態で引取る二軸配
向ポリエステルフィルムの製造方法において、熱固定温
度を１３０〜２５０℃となし、熱固定温度よりも低いが
１００℃以上の弛緩温度に冷却された二軸配向ポリエス
テルフィルムの両端耳部をテンターレールの外側で切断
し、次いで、両端耳部を切断除去された二軸配向ポリエ
ステルフィルムの両端部をフィルムの走行方向の両側に
配置された幅出しロールで直ちに把持して引取ることを
特徴とする二軸配向ポリエステルフィルムの製造方法に
より容易に達成される。The above object of the present invention is to fix a biaxially oriented polyester film by a tenter method in a heat setting zone of a tenter, then release from the tenter clip, and take it in a relaxed state by a take-up roll having a speed slower than the tenter speed. In the method for producing a biaxially oriented polyester film, the heat setting temperature is 130 to 250 ° C., and both ends of the biaxially oriented polyester film cooled to a relaxation temperature lower than the heat setting temperature but 100 ° C. or more are tenter rails. The outer edge of the biaxially oriented polyester film is cut off at both ends, and then both ends of the biaxially oriented polyester film having both edges cut off are immediately grasped and taken off by tenter rolls arranged on both sides in the running direction of the film. It is easily achieved by the method for producing a biaxially oriented polyester film.
以下、本発明を詳細に説明する。Hereinafter, the present invention will be described in detail.
本発明において、原料のポリエステルは、結晶性芳香族
ポリエステルであり、芳香族ジカルボン酸とグリコール
とを直接重縮合させる方法の他、芳香族ジカルボン酸の
ジアルキルエステルとグリコールとをエステル交換させ
た後、重縮合させる方法あるいは芳香族ジカルボン酸の
ジグリコールエステルを重縮合させる方法等によっても
得ることができる。そして、芳香族ジカルボン酸として
は、代表的には、テレフタル酸、イソフタル酸、ナフタ
レン−２，６−ジカルボン酸等が挙げられ、また、グリ
コールとしては、代表的には、エチレングリコール、ジ
エチレングリコール、テトラメチレングリコール、ネオ
ペンチルグリコール等が挙げられる。In the present invention, the raw material polyester is a crystalline aromatic polyester, other than the method of directly polycondensing the aromatic dicarboxylic acid and glycol, after transesterifying the dialkyl ester of the aromatic dicarboxylic acid and glycol, It can also be obtained by a method such as polycondensation or a method of polycondensing a diglycol ester of an aromatic dicarboxylic acid. The aromatic dicarboxylic acid typically includes terephthalic acid, isophthalic acid, naphthalene-2,6-dicarboxylic acid and the like, and the glycol typically includes ethylene glycol, diethylene glycol and tetracarboxylic acid. Examples thereof include methylene glycol and neopentyl glycol.
また、原料のポリエステルは、共重合ポリエステルであ
っても、ブレンド物であってもよく、そして、ブレンド
物は、ポリオレフィン等の他のポリマーとのブレンド物
であってもよい。Further, the raw material polyester may be a copolyester or a blended product, and the blended product may be a blended product with another polymer such as a polyolefin.
本発明において、特に好ましい原料ポリエステルは、繰
り返し構造単位の８０％以上がエチレンテレフタレート
単位またはエチレン−２，６−ナフタレン単位を有する
ポリエステルである。In the present invention, a particularly preferable raw material polyester is a polyester in which 80% or more of repeating structural units have ethylene terephthalate units or ethylene-2,6-naphthalene units.
上記の原料ポリエステル中には、微粒子を存在させ、得
られるポリエステルフィルムに易滑性を付与することも
できる。微粒子としては、ポリエステル合成時に使用す
る金属化合物触媒による所謂析出粒子であっても、カオ
リン、クレー、炭酸カルシウム、シリカ、アルミナ等の
添加粒子であってもよい。Fine particles may be present in the above raw material polyester to impart slipperiness to the obtained polyester film. The fine particles may be so-called precipitated particles due to a metal compound catalyst used in polyester synthesis, or may be particles added with kaolin, clay, calcium carbonate, silica, alumina or the like.
また上記の原料ポリエステル中には、必要に応じて、帯
電防止剤、潤滑剤、酸化防止剤、着色剤などを配合する
こともできる。In addition, an antistatic agent, a lubricant, an antioxidant, a colorant and the like may be blended in the above raw material polyester, if necessary.
本発明において、テンター法で二軸配向されたポリエス
テルフィルムは、従来公知の方法に従い、実質的に非晶
質のポリエステルシート（未延伸シート）を縦・横二軸
方向に延伸したものである。In the present invention, the biaxially oriented polyester film by the tenter method is a substantially amorphous polyester sheet (unstretched sheet) stretched in the longitudinal and transverse biaxial directions according to a conventionally known method.
未延伸シートは、溶融押出機のダイから押し出された溶
融シートを冷却回転ドラムに直ちに接触させて冷却固化
する方法により得ることができる。そして、この場合、
通常、溶融温度は２７０〜３００℃、冷却温度は４０〜
７０℃の範囲とされる。The unstretched sheet can be obtained by a method in which a molten sheet extruded from a die of a melt extruder is immediately brought into contact with a cooling rotary drum to be cooled and solidified. And in this case,
Usually, the melting temperature is 270 to 300 ° C, and the cooling temperature is 40 to
The range is 70 ° C.
縦延伸は、周速の異なるロール群によって行うことがで
き、横延伸は、テンターを用いて行われる。The longitudinal stretching can be performed by rolls having different peripheral speeds, and the transverse stretching is performed using a tenter.
本発明は、斯かるテンター法による二軸配向ポリエステ
ルの製造において、特定の弛緩処理を採用した点に特徴
を有する。The present invention is characterized in that a specific relaxation treatment is adopted in the production of the biaxially oriented polyester by the tenter method.
第１図は、本発明方法を実施するためのテンターの一例
を示す概略平面図である。FIG. 1 is a schematic plan view showing an example of a tenter for carrying out the method of the present invention.
縦延伸後のポリエステルフィルム(a)は、テンター
（１）に連続的に供給され、横延伸されて二軸配向フィ
ルム(b)となり、引取りロール（２）にて引取られる。The longitudinally stretched polyester film (a) is continuously supplied to the tenter (1) and transversely stretched to form a biaxially oriented film (b), which is taken up by a take-up roll (2).
テンター（１）は、予熱ゾーン（３）、横延伸ゾーン
（４）、熱固定ゾーン（５）、幅方向弛緩ゾーン
（６）、冷却ゾーン（７）に区分されており、ポリエス
テルフィルム(a)は、テンターレール（８），（８′）
上を走行する図示しないテンタークリップにその両端部
を把持されて連続的に走行される。The tenter (1) is divided into a preheating zone (3), a transverse stretching zone (4), a heat setting zone (5), a width direction relaxation zone (6) and a cooling zone (7), and a polyester film (a). Are tenter rails (8), (8 ')
Both ends are gripped by a tenter clip (not shown) that travels above, and the tenter clip travels continuously.
ポリエステルフィルム(a)は、通常、７０〜１５０℃の
範囲にされた予熱ゾーン（３）にて予熱された後、横延
伸ゾーン（４）において、通常、７０〜２２０℃で２〜
６倍延伸され、二軸配向ポリエステルフィルム(b)とな
る。The polyester film (a) is usually preheated in the preheating zone (3) in the range of 70 to 150 ° C., and then usually 2 to 70 to 220 ° C. in the transverse stretching zone (4).
The film is stretched 6 times to obtain a biaxially oriented polyester film (b).
次いで、二軸配向ポリエステルフィルム(b)は、熱固定
ゾーン（５）において、熱固定処理と共に熱弛緩処理が
行われ、これら処理により、ポリエステルフィルム(b)
には、寸法安定性が付与される。そして、この場合、熱
固定ゾーン（５）の温度は、二軸配向ポリエステルフィ
ルムの寸法安定性を高度なものとするために、１３０〜
２５０℃の範囲とする必要がある。Next, the biaxially oriented polyester film (b) is subjected to heat relaxation treatment and heat relaxation treatment in the heat fixation zone (5), and by these treatments, the polyester film (b)
Has dimensional stability. And, in this case, the temperature of the heat setting zone (5) is set to 130 to 130 ° C. in order to enhance the dimensional stability of the biaxially oriented polyester film.
It must be in the range of 250 ° C.
なお、上記の熱固定処理に先立ち、再縦延伸を行うこと
もできる。Note that re-longitudinal stretching can be performed prior to the above heat setting treatment.
幅方向弛緩ゾーン（６）は、フィルムの幅方向の収縮率
を調節するために、必要に応じて設けられるゾーンであ
る。このゾーンは、第１図では、熱固定ゾーン（５）の
後に設けられているが、熱固定ゾーン（５）のテンター
レールの幅を漸次狭めることにより、熱固定と同時に幅
方向の弛緩処理を行うこともできる。また、フィルムの
幅方向の収縮率の調節は、上記の弛緩処理の他、テンタ
ーレールの幅を漸次広げ、フィルムを伸長熱処理するこ
とによっても行い得る。The width direction relaxation zone (6) is a zone provided as necessary in order to adjust the shrinkage rate in the width direction of the film. In FIG. 1, this zone is provided after the heat setting zone (5), but by gradually narrowing the width of the tenter rail of the heat setting zone (5), heat treatment and relaxation treatment in the width direction are performed. You can also do it. In addition, the shrinkage ratio of the film in the width direction can be adjusted not only by the relaxation treatment described above but also by gradually widening the width of the tenter rail and subjecting the film to elongation heat treatment.
次いで、二軸配向ポリエステルフィルム(b)は、冷却ゾ
ーン（７）において、熱固定温度以下の所定温度まで冷
却されるが、このゾーンの温度は、後述するフィルムの
弛緩温度を決定するために重要である。Next, the biaxially oriented polyester film (b) is cooled to a predetermined temperature below the heat setting temperature in the cooling zone (7), and the temperature of this zone is important for determining the relaxation temperature of the film described later. Is.
一般に、弛緩温度は、二軸配向ポリエステルフィルムの
目的とする用途において、寸法安定性を問題とする温度
（以下、Ｔｃという）に依存するが、Ｔｃ−５０℃〜Ｔ
ｃ＋５０℃（但し、Ｔｃ＋５０℃＜熱固定温度）の範囲
が好ましい。特に、１５０℃に調節された空気中で３０
分間放置後の収縮率が０．５％以下の二軸配向ポリエス
テルを製造するため、本発明においては、熱固定温度以
下、１００℃以上、好ましくは、１５０℃以上の弛緩温
度が必要である。In general, the relaxation temperature depends on the temperature (hereinafter, referred to as Tc) in which dimensional stability is a problem in the intended use of the biaxially oriented polyester film, but Tc-50 ° C to T
The range of c + 50 ° C. (however, Tc + 50 ° C. <heat setting temperature) is preferable. In particular, 30 in air adjusted to 150 ° C
In order to produce a biaxially oriented polyester having a shrinkage ratio of 0.5% or less after being left for a minute, a relaxation temperature of 100 ° C. or higher, preferably 150 ° C. or higher is required in the present invention.
従って、冷却ゾーン（７）の温度は、その出口における
フィルムが上記弛緩温度を達成するように決定される。Therefore, the temperature of the cooling zone (7) is determined so that the film at its outlet achieves the relaxation temperature.
冷却ゾーン（７）を経た二軸配向ポリエステルフィルム
(b)は、切断刃（９），（９′）（第１図中、切断刃は
切断位置によって表現されている）により、その両端耳
部を切断除去され、引取りロール（２）にて引取られ
る。Biaxially oriented polyester film that has passed through the cooling zone (7)
(b) is cut and removed at both ends by cutting blades (9) and (9 ') (in FIG. 1, the cutting blade is represented by a cutting position), and is removed to a take-up roll (2). Will be taken over.
そして、引取りロール（２）の速度はテンター速度より
遅くなされており、肉厚の耳部を切断除去された二軸配
向ポリエステルフィルム(b)（被弛緩処理フィルム）
は、縦弛緩処理される。And the speed of the take-up roll (2) is slower than the tenter speed, and the biaxially oriented polyester film (b) with the thick ears cut and removed (relaxation-treated film)
Is subjected to vertical relaxation processing.
弛緩率は、これが大きいほど、寸法安定性の大きな二軸
配向ポリエステルフィルムが得られるが、余りにも大き
な弛緩率は、後述の幅出しロール（クロスガイダーロー
ル）の採用によっても、フィルムの自重弛みが生じ易い
ので２％以下とするのがよい。The larger the relaxation rate, the more dimensional stability the biaxially oriented polyester film can be obtained. However, the too large relaxation rate is due to the adoption of a tentering roll (cross guider roll) described later, which causes the film to lose its own weight. Since it easily occurs, it is preferable to set it to 2% or less.
前述の収縮率０．５％以下のフィルムを製造する場合に
は、弛緩温度にもよるが、弛緩率は０．２％以上とする
必要があり、好ましい弛緩率は０．５〜１．５％の範囲
である。In the case of producing a film having a shrinkage ratio of 0.5% or less, the relaxation ratio needs to be 0.2% or more, though it depends on the relaxation temperature, and the preferable relaxation ratio is 0.5 to 1.5. % Range.
そして、本発明においては、上記の両端耳部の切断をテ
ンターレール（８），（８′）の外側で行い、そして、
被弛緩処理フィルムの両端部を幅出しロール（１０），
（１０′）及び（１１），（１１′）で把持することが
重要である。Then, in the present invention, the cutting of the both ends is performed outside the tenter rails (8) and (8 '), and
Both ends of the relaxation treated film are tentered rolls (10),
It is important to grip with (10 ') and (11), (11').
両端耳部の切断は、前述の弛緩温度を満足し且つテンタ
ーレール（８），（８′）の外側であれば、特にその位
置は制限されないが、テンターレール（８），（８′）
の直後が好ましい。The cutting of the both ends is not particularly limited as long as it satisfies the above-mentioned relaxation temperature and is outside the tenter rails (8) and (8 '), but the tenter rails (8) and (8') are not limited.
Immediately after is preferable.
そして、被弛緩処理フィルムの幅出しロール（１０），
（１０′）及び（１１），（１１′）による把持は、耳
部切断後、直ちに行う必要がある。従って、幅出しロー
ル（１０），（１０′）及び（１１），（１１′）は、
フィルムの走行方向の両側において切断刃（９），
（９′）の直後に配置する必要がある。Then, the tenter roll (10) of the film to be relaxed,
Grasping by (10 '), (11), and (11') must be performed immediately after cutting the ears. Therefore, the tenter rolls (10), (10 ') and (11), (11') are
Cutting blades (9) on both sides of the film running direction,
It must be placed immediately after (9 ').
幅出しロールは、ニップロールで構成され、フィルムの
幅方向のみに張力を付与し、縦方向の速度変動には影響
しないものであり、従って、これにより、被弛緩処理フ
ィルムの自重弛みは有効に防止される。The tenter roll is composed of a nip roll, which imparts tension only in the width direction of the film and does not affect the speed fluctuation in the longitudinal direction. Therefore, it is possible to effectively prevent the loosened film from loosening due to its own weight. To be done.
なお、幅出しロールの材質は、フィルムが滑って外れる
ことのないものであれば、いずれの材質でもよく、従っ
て、幅出しロールとしては、金属ロール、ゴムロール、
樹脂ロール、セラミックロール等を適宜使用することが
できる。The material of the tenter roll may be any material as long as the film does not slip off, and therefore, as the tenter roll, a metal roll, a rubber roll,
A resin roll, a ceramic roll, or the like can be used as appropriate.
本発明においては、二軸配向ポリエステルフィルム(b)
の両端耳部の切断はテンターレール（８）の外側で行う
こととしたが、これにより、テンター（１）内やテンタ
ーレール（８）上で耳部切断を行う場合に比し、幅出し
ロール（１０），（１０′）及び（１１），（１１′）
の取付けが容易なものとなり、その取付けが実現され
る。In the present invention, a biaxially oriented polyester film (b)
It was decided to cut both ends of the ears on the outside of the tenter rail (8), but this allows the tentering roll to be cut compared to the case where the ears are cut inside the tenter (1) or on the tenter rail (8). (10), (10 ') and (11), (11')
Can be easily mounted and the mounting is realized.
なお、幅出しロールは、上記の理由により、複数組配置
することができ、特に、その数は制限されないが、２組
以上の配置が好ましい。For the above reason, a plurality of sets of tenter rolls can be arranged, and the number thereof is not particularly limited, but two or more sets are preferable.
本発明方法は、以上のような特定態様の縦弛緩処理の採
用により、高度な寸法安定性を有する二軸配向ポリエス
テルフィルムを製造することができるが、本発明方法に
より得られるフィルムは、磁気記録用途の他、特に、光
学的用途や電気絶縁用途に有用である。The method of the present invention can produce a biaxially oriented polyester film having a high degree of dimensional stability by adopting the longitudinal relaxation treatment of the above-described specific embodiment. However, the film obtained by the method of the present invention is a magnetic recording medium. Besides the application, it is particularly useful for optical applications and electrical insulation applications.
以下、本発明を実施例により更に詳細に説明するが、本
発明はその要旨を超えない限り、以下の実施例に限定さ
れるものではない。Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited to the following Examples as long as the gist thereof is not exceeded.
なお、以下の例において、各物性値の測定は、次の方法
に従って行い、各例で得られたフィルムの物性測定の結
果を表−１に示した。In the following examples, the physical property values were measured according to the following methods, and the results of the physical property measurements of the films obtained in each example are shown in Table-1.
(1)長手方向の破断時強度（ＦＢ値） 温度２５℃、湿度５０％ＲＨに調製された室内におい
て、長さ５０mm、幅１５mmの試料フィルムを５０mm／mi
nの速度で引っ張って破断させ、その時の強度を測定す
る。(1) Strength at break in longitudinal direction (FB value) In a room prepared at a temperature of 25 ° C and a humidity of 50% RH, a sample film having a length of 50 mm and a width of 15 mm is 50 mm / mi.
It is pulled at a speed of n to break and the strength at that time is measured.
フィルムの測定場所は、製品となる有効幅の中央部と両
端部の３カ所とし、その平均値をＦＢ値とした。The film was measured at three points, the central part and both ends of the effective width of the product, and the average value was used as the FB value.
(2)収縮率 試料フィルムを１５０℃に調節された空気中で３０分間
または１８０℃に調節された空気中で５分間放置し、そ
れぞれについて収縮率を測定する。(2) Shrinkage rate The sample film is left in the air adjusted to 150 ° C for 30 minutes or in the air adjusted to 180 ° C for 5 minutes, and the shrinkage rate is measured for each.
フィルムの測定場所は、製品となる有効幅の中央部と両
端部の３カ所とし、その平均値を収縮率とした。The film was measured at three points in the center and both ends of the effective width of the product, and the average value thereof was taken as the shrinkage rate.
(3)平面性 幅２ｍ、長さ２ｍの大きさにフィルムを切り出し、平ら
なテーブル面の上に広げ、フィルムの波打ちの状態から
評価した。品質上問題のないレベルを○、問題のあるレ
ベルを×とした。(3) Flatness The film was cut into a size of 2 m in width and 2 m in length, spread on a flat table surface, and evaluated from the wavy state of the film. The level with no quality problem was marked with ○, and the problematic level was marked with ×.
実施例１ 第１図に示すテンターにより二軸配向ポリエチレンテレ
フタレートフィルムの製造を行った。Example 1 A biaxially oriented polyethylene terephthalate film was produced using the tenter shown in FIG.
先ず、公知の方法に従い、原料溶融樹脂を急冷固化して
厚さ８００μの未延伸シートを得、該未延伸シートをロ
ールの周速差を利用して８５℃で３．５倍縦延伸した。First, according to a known method, the raw material molten resin was rapidly solidified to obtain an unstretched sheet having a thickness of 800 μ, and the unstretched sheet was longitudinally stretched 3.5 times at 85 ° C. by utilizing the peripheral speed difference of rolls.
次いで、延伸されたフィルムを１００℃の予熱ゾーン
（３）で予熱した後、１１５℃の横延伸ゾーン（４）で
３．６倍に延伸し、２２０℃の熱固定ゾーン（５）で熱
固定した。Next, the stretched film is preheated in a preheating zone (3) at 100 ° C., then stretched 3.6 times in a transverse stretching zone (4) at 115 ° C., and heat set in a heat setting zone (5) at 220 ° C. did.
次いで、熱固定したフィルムを冷却ゾーン（７）で冷却
してその出口におけるフィルム温度を１５０℃とし、テ
ンターレール（８），（８′）の直後において切断刃
（９），（９′）により両端耳部を切断除去し、直ち
に、幅出しロール（１０），（１０′）及び（１１），
（１１′）で把持し、１％の弛緩率に調節された引取り
ロール（２）で引取って二軸配向ポリエステルフィルム
を得た。Then, the heat-fixed film is cooled in the cooling zone (7) so that the film temperature at the outlet thereof is 150 ° C., and immediately after the tenter rails (8) and (8 ′), the cutting blades (9) and (9 ′) are used. Cut and remove the ears at both ends, and immediately, the tenter rolls (10), (10 ') and (11),
The film was gripped with (11 ') and taken with a take-up roll (2) adjusted to a relaxation rate of 1% to obtain a biaxially oriented polyester film.
実施例２ 実施例１において、冷却ゾーン（７）出口におけるフィ
ルム温度を１８０℃とした以外は、実施例１と同様にし
て二軸配向ポリエステルフィルムを得た。Example 2 A biaxially oriented polyester film was obtained in the same manner as in Example 1 except that the film temperature at the exit of the cooling zone (7) was 180 ° C.
比較例１ 実施例１において、両端耳部の切断を行わなかった以外
は、実施例１と同様にして二軸配向ポリエステルフィル
ムを得た。Comparative Example 1 A biaxially oriented polyester film was obtained in the same manner as in Example 1 except that the cutting of both ends was not performed.
比較例２ 実施例１において、幅出しロールを使用しなかった以外
は実施例１と同様にして二軸配向ポリエステルフィルム
を得た。Comparative Example 2 A biaxially oriented polyester film was obtained in the same manner as in Example 1 except that the tenter roll was not used.
〔発明の効果〕 以上説明した本発明によれば、特定態様の縦弛緩処理の
採用により、平面性が良好で且つ長手方向の破断強度が
大きく、特に、高度な寸法安定性を有する二軸配向ポリ
エステルフィルムの工業的有利な製造方法が提供され、
本発明は、ポリエステルフィルムの製造分野に寄与する
ところ大である。 [Effects of the Invention] According to the present invention described above, by adopting the longitudinal relaxation treatment of the specific mode, the flatness is good and the breaking strength in the longitudinal direction is large, and in particular, the biaxial orientation having a high dimensional stability. An industrially advantageous method for producing a polyester film is provided,
The present invention largely contributes to the field of manufacturing polyester films.
第１図は、本発明方法を実施するためのテンターの一例
を示す概略平面図である。 図中、（１）はテンター、（２）は引取りロール、
（３）予熱ゾーン、（４）は横延伸ゾーン、（５）は熱
固定ゾーン、（６）は幅方向弛緩ゾーン、（７）は冷却
ゾーン、（８），（８′）はテンターレール、（９），
（９′）は切断刃、（１０），（１０′），（１１），
（１１′）は幅出しロールである。FIG. 1 is a schematic plan view showing an example of a tenter for carrying out the method of the present invention. In the figure, (1) is a tenter, (2) is a take-up roll,
(3) preheating zone, (4) transverse stretching zone, (5) heat setting zone, (6) width direction relaxation zone, (7) cooling zone, (8), (8 ') tenter rail, (9),
(9 ') is a cutting blade, (10), (10'), (11),
(11 ') is a tenter roll.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 鈴木 忍 神奈川県横浜市緑区鴨志田町1000番地 ダ イアホイル株式会社中央研究所内 (56)参考文献 特開 昭62−268629（ＪＰ，Ａ) ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Shinobu Suzuki 1000, Kamoshida-cho, Midori-ku, Yokohama-shi, Kanagawa Daifoil Co., Ltd. Central Research Laboratory (56) Reference JP-A-62-268629 (JP, A)
Claims (3)
フィルムをテンターの熱固定ゾーンで熱固定した後、テ
ンタークリップから開放し、テンター速度より遅い速度
の引取りロールにより弛緩状態で引取る二軸配向ポリエ
ステルフィルムの製造方法において、熱固定温度を１３
０〜２５０℃となし、熱固定温度よりも低いが１００℃
以上の弛緩温度に冷却された二軸配向ポリエステルフィ
ルムの両端耳部をテンターレールの外側で切断し、次い
で、両端耳部を切断除去された二軸配向ポリエステルフ
ィルムの両端部をフィルムの走行方向の両側に配置され
た幅出しロールで直ちに把持して引取ることを特徴とす
る二軸配向ポリエステルフィルムの製造方法。1. A biaxially stretched polyester film biaxially oriented by a tenter method, after being heat-set in a heat-setting zone of the tenter, released from a tenter clip and drawn in a relaxed state by a take-up roll having a speed slower than the tenter speed. In the method for producing an oriented polyester film, the heat setting temperature is set to 13
0-250 ℃, lower than heat setting temperature but 100 ℃
Both ends of the biaxially oriented polyester film cooled to the above relaxation temperature are cut outside the tenter rail, and then both ends of the biaxially oriented polyester film are removed by cutting the both ends of the film in the running direction of the film. A method for producing a biaxially oriented polyester film, which is characterized in that the tenter rolls arranged on both sides are immediately gripped and taken off.
特徴とする請求項１に記載の製造方法。2. The manufacturing method according to claim 1, wherein the relaxation rate is in the range of 0.2 to 2%.
に調節された空気中で３０分間放置後の測定値として
０．５％以下であることを特徴とする請求項１又は２に
記載の製造方法。3. The shrinkage rate of the film after the relaxation treatment is 150 ° C.
The method according to claim 1 or 2, wherein the measured value after standing for 30 minutes in the air adjusted to 0.5 is 0.5% or less.