JPH06289328A - Method for processing lens, manufacture of lens, and lens - Google Patents

Abstract

PURPOSE:To easily obtain the lens which have both its surfaces processed differently. CONSTITUTION:The plane or concave surface side of the lens is shielded by a shield member which can contact the peripheral edge part of the lens, the part contacting the lens is sealed with a removable sealing means, and the lens is coated with a hard coat, etc. The shield member which contact with the peripheral edge part of the lens and has the surface, facing the lens, formed into a plane or concave surface is usable as the shield member. After the coating process, the seal part is removed to obtain the lens which has both its surfaces processed differently. After the seal part is removed, at least the internal surface can be coated differently from the external surface. The lens which has its external surface coated with the hard coat and its internal surface coated for fog protection is suitably used for a spectacle lens with high practicality.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、レンズの片面のみを被
覆処理するレンズの処理方法、両面の表面処理態様が互
いに異なるレンズの製造方法、および、両面に異なる被
覆処理が施された新規なレンズに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for treating a lens in which only one side of a lens is coated, a method for producing a lens in which surface treatment modes of both sides are different from each other, and a novel coating treatment in which both sides are different. Regarding the lens.

【０００２】[0002]

【従来の技術】レンズを製造する際には、レンズの表面
特性を改善したり、新たな特性を付与するため、種々の
被覆処理がレンズ表面に施される。例えば、発汗や吐息
等によりレンズ表面が曇るのを防止するため防曇コート
が施されたり、可視光の反射を防止するため反射防止コ
ートが施される。また、有害光線から目を保護するた
め、赤外線反射被膜、紫外線や近赤外線吸収被膜などが
レンズ表面に施されたりする。さらに、プラスチックレ
ンズはガラスレンズと比較して硬度が低く耐擦傷性に劣
るため、シリコン系樹脂、アクリル系樹脂などの被膜を
レンズ表面に形成するハードコーティングが行われる。
そして、このような被覆処理は、通常、浸漬法、スプレ
ー法、フローコート法、カーテンコート法、スピンコー
ト法などによって行われる。2. Description of the Related Art When manufacturing a lens, various coating treatments are applied to the lens surface in order to improve the surface characteristics of the lens or impart new characteristics. For example, an anti-fog coating is applied to prevent the lens surface from fogging due to sweating, breathing, or the like, or an antireflection coating is applied to prevent reflection of visible light. Further, in order to protect the eyes from harmful light rays, an infrared reflective coating, an ultraviolet or near infrared absorbing coating may be applied to the lens surface. Further, since the plastic lens has a lower hardness and a lower scratch resistance than the glass lens, a hard coating for forming a coating film of a silicone resin, an acrylic resin or the like on the lens surface is performed.
Then, such coating treatment is usually performed by a dipping method, a spray method, a flow coating method, a curtain coating method, a spin coating method, or the like.

【０００３】しかし、上記のような被覆処理は必ずしも
レンズの両面に必要であるわけではなく、また、レンズ
の両面のそれぞれに異なる表面特性が要求される場合が
ある。例えば、メガネレンズにおいては、前記紫外線吸
収被膜などはレンズの何れか一方の面に形成すれば十分
である。また、メガネレンズの外側の面は、外界の物体
と接触し易く、風塵に当りやすいためハードコーティン
グする必要性が高いが、レンズの内側の面は、ハードコ
ートの必要性は低い。逆に、前記防曇コートは、メガネ
レンズの内側の面には必要性が高いが、外側の面にはあ
えて施す必要がない。However, the coating treatment as described above is not always necessary on both surfaces of the lens, and different surface characteristics may be required on both surfaces of the lens in some cases. For example, in a spectacle lens, it is sufficient to form the ultraviolet absorbing film or the like on either surface of the lens. Further, the outer surface of the spectacle lens is likely to come into contact with an external object and is easily hit by dust, so that it is highly necessary to perform hard coating, but the inner surface of the lens is not required to be hard coated. On the contrary, the anti-fog coating is highly necessary on the inner surface of the spectacle lens, but it is not necessary to dare to apply it to the outer surface.

【０００４】上記のように両面の被覆処理態様が互いに
異なるレンズを製造しようとする場合、処理すべきレン
ズをそのまま前記浸漬法で処理すると、レンズの両面に
同一の被覆処理が施されるため、両面の被覆処理態様が
互いに異なるレンズを製造することができない。例え
ば、特公昭５３−１４２７４号公報および特公昭６０−
３０７１２号公報には、レンズなどを処理する上で有用
なシロキサン加水分解縮合物を含むコーティング組成物
が開示されているものの、浸漬法によりレンズの両面を
表面処理している。また、前記スプレー法等の他の方法
によっても、レンズをそのまま処理に供する場合には、
処理面とは反対側の非処理面にまでも処理液の液滴が付
着するため、一方の面のみを効率かつ精度よく被覆処理
することは困難である。When it is desired to manufacture lenses having different coating treatments on both sides as described above, if the lenses to be treated are directly treated by the dipping method, the same coating treatment is applied to both sides of the lens. It is not possible to manufacture lenses with different coating treatments on both sides. For example, Japanese Patent Publication No. 53-14274 and Japanese Patent Publication No. 60-
Although Japanese Patent No. 30712 discloses a coating composition containing a siloxane hydrolyzed condensate which is useful for treating a lens or the like, both surfaces of the lens are surface-treated by a dipping method. Also, when the lens is directly subjected to the treatment by another method such as the spray method,
Since the droplets of the treatment liquid adhere to the non-treatment surface opposite to the treatment surface, it is difficult to coat only one surface efficiently and accurately.

【０００５】このように、従来より、両面ハードコート
されたレンズ及び両面防曇コートされたレンズは知られ
ているが、例えば、レンズの外側の面がハードコートさ
れ、内側の面が防曇コートされたレンズなどを製造する
のは困難である。Thus, conventionally, a lens having both sides hard-coated and a lens having both sides anti-fog coated are known. For example, the outer surface of the lens is hard-coated and the inner surface is anti-fog coated. It is difficult to manufacture such lenses.

【０００６】[0006]

【発明が解決しようとする課題】従って、本発明の目的
は、両面の被覆処理態様が互いに異なるレンズを、簡易
に製造する方法を提供することにある。SUMMARY OF THE INVENTION It is, therefore, an object of the present invention to provide a method for easily manufacturing lenses having different coating treatment modes on both surfaces.

【０００７】本発明の他の目的は、外側の面がハードコ
ートされ、内側の面が防曇コートされた新規なレンズを
提供することにある。Another object of the present invention is to provide a novel lens having an outer surface hard-coated and an inner surface anti-fog coated.

【０００８】[0008]

【発明の構成】本発明者は上記目的を達成するため鋭意
検討した結果、レンズの平面又は凹面側を少なくともレ
ンズの周縁部と接触可能な遮蔽部材で遮蔽し、レンズと
遮蔽部材との接触部を除去可能なシール手段でシール
し、前記レンズを被覆処理すると、片面のみが簡易に被
覆処理されること、次いで前記シール部を除去すること
により両面の表面処理態様が互いに異なるレンズが効率
的に得られることを見出し本発明を完成した。As a result of intensive studies to achieve the above-mentioned object, the inventor of the present invention shields the flat or concave side of the lens with a shielding member which is capable of contacting at least the peripheral edge of the lens, and the contact portion between the lens and the shielding member. If the lens is covered with a removable sealing means and the lens is covered, only one surface can be covered easily, and by removing the sealing portion, lenses with different surface treatment modes on both surfaces can be efficiently used. The inventors have found that they can be obtained and completed the present invention.

【０００９】すなわち、本発明は、少なくとも一方の面
が平面又は凹面であるレンズを処理する方法であって、
レンズの平面又は凹面側を少なくともレンズの周縁部と
接触可能な遮蔽部材で遮蔽し、レンズと遮蔽部材との接
触部を除去可能なシール手段でシールし、前記レンズを
被覆処理するレンズの処理方法を提供する。That is, the present invention provides a method for treating a lens, at least one surface of which is a flat surface or a concave surface,
A method for treating a lens, in which a flat surface or a concave surface side of a lens is shielded by a shielding member capable of contacting at least a peripheral portion of the lens, and a contact portion between the lens and the shielding member is sealed by a removable sealing means, and the lens is covered. I will provide a.

【００１０】本発明は、また、少なくとも一方の面が平
面又は凹面であり、且つ両面の表面処理態様が互いに異
なるレンズの製造方法であって、レンズの平面又は凹面
側を少なくともレンズの周縁部と接触可能な遮蔽部材で
遮蔽し、レンズとの接触部を除去可能なシール手段でシ
ールし、前記レンズを被覆処理し、次いで前記シール部
を除去するレンズの製造方法を提供する。The present invention is also a method of manufacturing a lens in which at least one surface is a flat surface or a concave surface, and the surface treatment modes on both surfaces are different from each other, and the flat surface or the concave surface side of the lens is at least the peripheral portion of the lens. Provided is a method for manufacturing a lens, which is shielded by a contacting shield member, a contact portion with a lens is sealed by a removable sealing means, the lens is coated, and then the seal portion is removed.

【００１１】本発明は、さらに、外側の面がハードコー
トされ、内側の面が防曇コートされているレンズを提供
する。The present invention further provides a lens having an outer surface hard-coated and an inner surface anti-fog coated.

【００１２】本発明において、被覆処理に供するレンズ
として、少なくとも一方の面が平面又は凹面であるレン
ズを用いる。このようなレンズには、メニスカスレン
ズ、フラットレンズ、両凹面のダブルレンズ、平面又は
凹面を有するサングラスレンズなどが含まれる。前記レ
ンズは、球面レンズであってもよく、また非球面レンズ
であってもよい。In the present invention, a lens having at least one surface that is a flat surface or a concave surface is used as the lens that is subjected to the coating treatment. Such lenses include meniscus lenses, flat lenses, biconcave double lenses, sunglass lenses having a flat or concave surface, and the like. The lens may be a spherical lens or an aspherical lens.

【００１３】前記レンズは、ガラスレンズ又はプラスチ
ックレンズの何れであってもよい。プラスチックレンズ
の材料としては、光線透過率が高く、成形可能なポリマ
ーであればよく、例えば、ポリメチルメタクリレート等
のメタクリル樹脂、ポリカーボネート、ポリジエチレン
グリコールビスアリルカーボネート等のポリジアリルグ
リコールカーボネート類、ポリスチレン、アクリロニト
リル−スチレン共重合体、メチルメタクリレート−スチ
レン共重合体、ゴム強化メタクリル樹脂、セルロースア
セテート等のセルロースエステル類、ポリ塩化ビニル、
ＡＢＳ樹脂などが例示できる。これらのうち、透明性、
成形性に優れ、機械的強度の高いポリカーボネートなど
が好ましい。The lens may be either a glass lens or a plastic lens. As the material of the plastic lens, a polymer having a high light transmittance and a moldability may be used, and examples thereof include methacrylic resins such as polymethyl methacrylate, polycarbonate, polydiallyl glycol carbonates such as polydiethylene glycol bisallyl carbonate, polystyrene and acrylonitrile. -Styrene copolymer, methyl methacrylate-styrene copolymer, rubber-reinforced methacrylic resin, cellulose esters such as cellulose acetate, polyvinyl chloride,
ABS resin etc. can be illustrated. Of these, transparency,
Polycarbonate having excellent moldability and high mechanical strength is preferable.

【００１４】本発明では、レンズの平面又は凹面側を少
なくともレンズの周縁部と接触可能な遮蔽部材で遮蔽
し、レンズと遮蔽部材との接触部を除去可能なシール手
段でシールする。前記遮蔽部材としては、レンズの周縁
部で封止するため、少なくともレンズの周縁部と接触可
能であれば特に限定されない。例えば、プラスチック
製、ガラス製、金属製等のシートなどを用いることがで
き、シートは凹面状などに湾曲していてもよい。また、
前記遮蔽部材として、レンズの周縁部と接触可能であっ
て、且つレンズとの対向面が平面又は凹面に形成されて
いるレンズを用いてもよい。後者の場合、例えば、２枚
の同種又は異種のレンズの平面又は凹面側を対向させ周
縁部で封止させることにより、それぞれのレンズの平面
又は凹面側を互いに遮蔽することができる。In the present invention, the flat surface or concave surface side of the lens is shielded by at least the shielding member that can contact the peripheral portion of the lens, and the contact portion between the lens and the shielding member is sealed by the removable sealing means. The shielding member is not particularly limited as long as it can be brought into contact with at least the peripheral edge of the lens because it is sealed at the peripheral edge of the lens. For example, a sheet made of plastic, glass, metal, or the like can be used, and the sheet may be curved in a concave shape or the like. Also,
As the shielding member, a lens that can be brought into contact with the peripheral portion of the lens and whose surface facing the lens is a flat surface or a concave surface may be used. In the latter case, for example, the flat or concave sides of two lenses of the same type or different types may be made to face each other and sealed at the peripheral edge portion to shield the flat or concave sides of the respective lenses from each other.

【００１５】前記遮蔽部材によるレンズ周縁部の遮蔽に
際しては、レンズの平面又は凹面側と遮蔽部材との間に
空間を形成するのが好ましい。このような空間を形成す
ると、レンズ及び遮蔽部材の少なくとも一方の部材とし
て、弾性又は可撓性を有する部材を用いると、レンズと
遮蔽部材との周縁部をシール手段で封止しても、前記周
縁部などを押圧することにより、両者を容易に分離でき
る。特に凹面を互いに対向させた一対のプラスチックレ
ンズの周縁部をシールする場合には、周縁部の押圧に伴
なって、プラスチックレンズの弾性により、両者を外方
方向に引離す力が作用するので、レンズを損傷させるこ
となく効率よく分離できる。しかも、この場合には、外
面に同一の被覆処理が施されたレンズを一度に２枚得る
ことができるという利点をも有する。When the peripheral edge of the lens is shielded by the shield member, it is preferable to form a space between the flat or concave side of the lens and the shield member. When such a space is formed, if a member having elasticity or flexibility is used as at least one of the lens and the shielding member, even if the peripheral portions of the lens and the shielding member are sealed by the sealing means, Both can be easily separated by pressing the peripheral portion. In particular, when sealing the peripheral edges of a pair of plastic lenses whose concave surfaces are opposed to each other, the elasticity of the plastic lenses accompanies the pressing of the peripheral edges, so that a force that separates the two outwardly acts. Can be efficiently separated without damaging the lens. Moreover, in this case, there is an advantage that two lenses having the same coating treatment on the outer surface can be obtained at one time.

【００１６】前記シール手段としては、除去可能であっ
て、レンズ表面を損傷させることなく、表面処理がレン
ズの外面にのみ施され得るような手段であればよい。例
えば、レンズと遮蔽部材との接触部を溶着でき、溶着の
程度も振動数、強度、時間などを調整することにより制
御できる超音波や高周波による周縁部の溶着；適当な接
着剤等による周縁部の接着等を行うことができる。The sealing means may be any means that is removable and that can be surface-treated only on the outer surface of the lens without damaging the lens surface. For example, the contact portion between the lens and the shielding member can be welded, and the degree of welding can be controlled by adjusting the frequency, strength, time, etc. Welding of the peripheral portion by ultrasonic waves or high frequencies; peripheral portion by an appropriate adhesive or the like Can be adhered.

【００１７】前記接着剤としては、レンズの材質に応じ
て、プラスチック用として通常用いられる接着剤、例え
ば、エチレン、酢酸ビニル、（メタ）アクリル酸エステ
ル等のビニル化合物の重合体であるビニル重合体接着
剤；クロロプレンゴム、ニトリルゴムなどのゴム系接着
剤；ポリエステル、ポリアミド、エポキシ樹脂、ポリウ
レタン、フェノール樹脂、ユリア樹脂などの重縮合、重
付加物接着剤等が挙げられる。As the adhesive, an adhesive usually used for plastics depending on the material of the lens, for example, a vinyl polymer which is a polymer of vinyl compounds such as ethylene, vinyl acetate, and (meth) acrylic acid ester. Adhesives: rubber-based adhesives such as chloroprene rubber and nitrile rubber; polycondensation of polyester, polyamide, epoxy resin, polyurethane, phenol resin, urea resin, and polyaddition adhesives.

【００１８】前記シール手段によるシール強度は、被覆
処理後に除去可能な程度であり、例えば、テンサイルテ
スターによる引張り試験法で３０〜１０００ｇ／ｃｍ、
好ましくは５０〜２００ｇ／ｃｍ程度である。The sealing strength of the sealing means is such that it can be removed after the coating treatment, for example, 30 to 1000 g / cm by a tensile test method using a tensil tester,
It is preferably about 50 to 200 g / cm.

【００１９】前記シール後、レンズを被覆処理する。前
記被覆処理としては、レンズの表面特性を改善するため
に行われる種々の被覆処理、例えば、塗膜形成処理、無
機質膜形成処理等が挙げられる。After the sealing, the lens is covered. Examples of the coating treatment include various coating treatments performed to improve the surface characteristics of the lens, such as a coating film forming treatment and an inorganic film forming treatment.

【００２０】塗膜形成処理には、ハードコート、防曇コ
ート、紫外線吸収コート、近赤外線吸収コート、青色光
吸収コート、染料溶出防止コート、帯電防止コート等が
含まれる。The coating film forming treatment includes a hard coat, an antifogging coat, an ultraviolet absorption coat, a near infrared absorption coat, a blue light absorption coat, a dye elution prevention coat, an antistatic coat and the like.

【００２１】塗膜形成処理は、例えば、ハードコート
剤、防曇処理剤、紫外線吸収剤等の処理剤をレンズに塗
布した後、必要に応じて乾燥、硬化させることによって
行うことができる。前記処理剤は、適当な溶媒に溶解又
は懸濁させた溶液である場合が多い。The coating film-forming treatment can be carried out, for example, by applying a treatment agent such as a hard coat agent, an antifogging treatment agent, an ultraviolet absorber or the like to the lens, and then drying and curing it, if necessary. The treatment agent is often a solution dissolved or suspended in a suitable solvent.

【００２２】前記溶媒は、形成させる塗膜の種類によっ
て異なるが、レンズを浸蝕しない種々の溶媒、例えば、
水；メタノール、エタノール、イソプロパノール、ブタ
ノール、ジアセトンアルコール等のアルコール類；アセ
トン、メチルエチルケトンなどのケトン類；酢酸エチ
ル、酢酸ブチル、酢酸アミルなどのエステル類；メチル
セロソルブ、エチルセロソルブ、ブチルセロソルブ、酢
酸セロソルブ等のセロソルブ類；ベンゼン、トルエン、
キシレンなどの芳香族炭化水素；塩化メチレン、クロロ
ホルムなどのハロゲン化炭化水素等が例示できる。これ
らの溶媒は混合して用いてもよい。The solvent varies depending on the type of coating film to be formed, but various solvents which do not corrode the lens, for example,
Water; alcohols such as methanol, ethanol, isopropanol, butanol, diacetone alcohol; ketones such as acetone and methyl ethyl ketone; esters such as ethyl acetate, butyl acetate, amyl acetate; methyl cellosolve, ethyl cellosolve, butyl cellosolve, cellosolve acetate, etc. Cellosolves; benzene, toluene,
Examples thereof include aromatic hydrocarbons such as xylene; halogenated hydrocarbons such as methylene chloride and chloroform. These solvents may be used as a mixture.

【００２３】処理剤は一種又は二種以上混合して用いて
もよく、また、必要に応じて、硬化触媒；シリカ、チタ
ニア、酸化セリウム等の無機微粒子、着色剤、界面活性
剤などの添加剤を併用してもよい。The treating agents may be used alone or in admixture of two or more, and if necessary, a curing catalyst; inorganic fine particles such as silica, titania and cerium oxide, additives such as colorants and surfactants. You may use together.

【００２４】前記処理剤の塗布方法としては、例えば、
浸漬法、スプレー法、フローコート法、カーテンコート
法、スピンコート法等の慣用の塗布方法を採用すること
ができる。本発明の方法では、レンズと遮蔽部材との周
縁部がシール手段により封止されているので、浸漬法や
スプレー法などを採用しても、レンズの一方の面だけを
処理できるという利点がある。これらの方法のうち、特
に、コーティング剤のロスが少なく、良好な作業環境で
処理でき、しかも優れた平滑精度が得られる浸漬法が好
適に用いられる。As a method of applying the treatment agent, for example,
A conventional coating method such as a dipping method, a spray method, a flow coating method, a curtain coating method or a spin coating method can be adopted. In the method of the present invention, since the peripheral portions of the lens and the shielding member are sealed by the sealing means, there is an advantage that only one surface of the lens can be processed even if the dipping method or the spray method is adopted. . Of these methods, the dipping method is particularly preferably used because it causes less loss of the coating agent, can be processed in a good working environment, and has excellent smoothing accuracy.

【００２５】なお、レンズと塗膜との密着性を向上させ
るため、前記処理剤による処理に先立って、レンズ表面
を、プライマー、例えば、（メタ）アクリル系重合体等
からなるプライマーで処理してもよい。In order to improve the adhesion between the lens and the coating film, the lens surface is treated with a primer, for example, a primer made of a (meth) acrylic polymer, prior to the treatment with the treatment agent. Good.

【００２６】前記ハードコート剤としては、特に限定さ
れず、例えば、有機ケイ素化合物の一種又は二種以上の
部分加水分解物等のシリコン系ハードコート剤などが挙
げられる。前記有機ケイ素化合物には、テトラメトキシ
シラン、テトラエトキシシラン、テトラブトキシシラン
などのテトラアルコキシシラン類；メチルトリメトキシ
シラン、メチルトリエトキシシランなどのトリアルコキ
シシラン類；メチルトリアセトキシシラン、エチルトリ
アセトキシシランなどのトリアセトキシシラン類；ジメ
チルジメトキシシラン、ジフェニルジメトキシシランな
どのジアルコキシシラン類等が含まれる。これらの有機
ケイ素化合物は、エポキシ基などを含んでいてもよい。The hard coating agent is not particularly limited, and examples thereof include silicon-based hard coating agents such as one or more partial hydrolysates of organic silicon compounds. The organosilicon compound includes tetraalkoxysilanes such as tetramethoxysilane, tetraethoxysilane and tetrabutoxysilane; trialkoxysilanes such as methyltrimethoxysilane and methyltriethoxysilane; methyltriacetoxysilane and ethyltriacetoxysilane. Such as triacetoxysilanes; dialkoxysilanes such as dimethyldimethoxysilane and diphenyldimethoxysilane. These organosilicon compounds may contain an epoxy group or the like.

【００２７】ハードコート剤をレンズ表面に塗布した
後、通常硬化工程に供される。硬化条件は、ハードコー
ト剤や硬化触媒の種類等によって異なるが、硬化温度は
レンズの熱変形温度未満の温度、例えば４０〜２５０℃
程度、硬化時間は０．０５〜２４時間程度である。After the hard coat agent is applied to the lens surface, it is usually subjected to a curing step. The curing conditions vary depending on the type of hard coating agent or curing catalyst, but the curing temperature is lower than the heat distortion temperature of the lens, for example, 40 to 250 ° C.
The curing time is about 0.05 to 24 hours.

【００２８】前記防曇処理剤には、ヒドロキシル基、エ
ーテル結合等の親水性基を有する種々の樹脂組成物、例
えば、熱可塑性樹脂組成物、熱硬化性樹脂組成物、光硬
化性樹脂組成物等が含まれる。好ましい防曇処理剤に
は、塗膜の特性に優れる熱硬化性樹脂組成物、光硬化性
樹脂組成物が含まれる。光硬化性樹脂組成物を用いる
と、熱による悪影響を抑制しつつ、効率よく防曇性被膜
を形成できるという利点がある。As the antifogging agent, various resin compositions having a hydrophilic group such as a hydroxyl group and an ether bond, for example, a thermoplastic resin composition, a thermosetting resin composition and a photocurable resin composition are used. Etc. are included. The preferred antifogging treatment agent includes a thermosetting resin composition and a photocurable resin composition having excellent coating film properties. Use of the photocurable resin composition has an advantage that an antifogging film can be efficiently formed while suppressing an adverse effect due to heat.

【００２９】前記熱可塑性樹脂組成物としては、ポリビ
ニルアルコール、エチレン−ビニルアルコール共重合
体、水溶性アクリル樹脂などの親水性ポリマーを含む組
成物が挙げられ、熱硬化性樹脂組成物としては、例え
ば、ポリエチレングリコールなどのポリアルキレングリ
コール単位を有する不飽和ポリエステルやポリウレタ
ン、ヒドロキシル基やカルボキシル基などの硬化に利用
可能な官能基を有する水溶性アクリル樹脂のポリマー
と、重合開始剤やメラミン樹脂などの硬化剤とを含む組
成物などが例示できる。Examples of the thermoplastic resin composition include compositions containing hydrophilic polymers such as polyvinyl alcohol, ethylene-vinyl alcohol copolymer, and water-soluble acrylic resin. Examples of the thermosetting resin composition include: , Polyesters such as polyethylene glycol, unsaturated polyesters and polyurethanes, water-soluble acrylic resin polymers with functional groups that can be used for curing hydroxyl groups and carboxyl groups, and curing of polymerization initiators and melamine resins Examples thereof include a composition containing an agent.

【００３０】光硬化性樹脂組成物としては、例えば、
（メタ）アクリル酸２−ヒドロキシエチル、（メタ）ア
クリル酸２−ヒドロキシプロピル、ペンタエリスリトー
ルジ（メタ）アクリレート、ペンタエリスリトールトリ
（メタ）アクリレート、トリメチロールプロパンジ（メ
タ）アクリレート、グリセリン１モルと（メタ）アクリ
ル酸グリシジル１〜２モルとの付加物などのヒドロキシ
ル基を有する重合性モノマー、エチレングリコールジ
（メタ）アクリレート、ジエチレングリコールジ（メ
タ）アクリレート、プロピレングリコールジ（メタ）ア
クリレート、ジプロピレングリコールジ（メタ）アクリ
レート、ポリエチレングリコールジ（メタ）アクリレー
ト、ポリプロピレングリコールジ（メタ）アクリレート
などのエーテル結合を有する重合性モノマーなどの親水
性光重合性モノマーと、光重合開始剤とを含む組成物が
含まれる。Examples of the photocurable resin composition include:
2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, pentaerythritol di (meth) acrylate, pentaerythritol tri (meth) acrylate, trimethylolpropane di (meth) acrylate, 1 mol of glycerin ( Polymerizable monomer having a hydroxyl group such as an adduct with 1 to 2 mol of glycidyl (meth) acrylate, ethylene glycol di (meth) acrylate, diethylene glycol di (meth) acrylate, propylene glycol di (meth) acrylate, dipropylene glycol di A hydrophilic photopolymerizable monomer such as a polymerizable monomer having an ether bond such as (meth) acrylate, polyethylene glycol di (meth) acrylate, polypropylene glycol di (meth) acrylate It includes compositions comprising a photopolymerization initiator.

【００３１】光硬化性樹脂組成物は、被膜形成成分とし
て、例えば、（メタ）アクリル酸エステル類、スチレン
などの重合性単量体の単独重合体又は共重合体などの熱
可塑性樹脂；エポキシ（メタ）アクリレート、ポリウレ
タン（メタ）アクリレート、ポリエステル（メタ）アク
リレートなどの光硬化性樹脂などを含んでいてもよい。
さらに、光硬化性樹脂組成物は、重合性モノマー、例え
ば、（メタ）アクリル酸エチル、（メタ）アクリル酸ブ
チル、（メタ）アクリル酸２−エチルヘキシル、グリセ
リントリ（メタ）アクリレート、トリメチロールプロパ
ントリ（メタ）アクリレート、ペンタエリスリトールテ
トラ（メタ）アクリレート、（メタ）アクリル酸グリシ
ジル、（メタ）アクリル酸ジメチルアミノエチル、（メ
タ）アクリル酸ジエチルアミノエチルなどの（メタ）ア
クリル酸エステル類；（メタ）アクリルアミド、Ｎ−メ
チロール（メタ）アクリルアミド、ジアセトン（メタ）
アクリルアミドなどの（メタ）アクリルアミド類などの
他、着色剤、界面活性剤などを含んでいてもよい。The photocurable resin composition is used as a film-forming component, for example, a thermoplastic resin such as a homopolymer or copolymer of (meth) acrylic acid esters, a polymerizable monomer such as styrene; an epoxy ( A photocurable resin such as (meth) acrylate, polyurethane (meth) acrylate or polyester (meth) acrylate may be contained.
Further, the photocurable resin composition is a polymerizable monomer such as ethyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, glycerin tri (meth) acrylate, trimethylolpropane trichloride. (Meth) acrylic acid esters such as (meth) acrylate, pentaerythritol tetra (meth) acrylate, glycidyl (meth) acrylate, dimethylaminoethyl (meth) acrylate, diethylaminoethyl (meth) acrylate; (meth) acrylamide , N-methylol (meth) acrylamide, diacetone (meth)
In addition to (meth) acrylamides such as acrylamide, a colorant, a surfactant and the like may be contained.

【００３２】このような防曇処理剤をレンズ表面に塗布
した後、乾燥、加熱、紫外線照射等により硬化させるこ
とにより、レンズ表面に防曇被膜を形成できる。An anti-fog coating can be formed on the lens surface by applying such an anti-fog treatment agent on the lens surface and then curing it by drying, heating, ultraviolet irradiation or the like.

【００３３】前記無機質膜形成処理には、無機強化コー
ト、反射防止コート、赤外線反射コートなどが含まれ
る。The inorganic film forming treatment includes an inorganic reinforcing coat, an antireflection coat, an infrared reflection coat and the like.

【００３４】無機質膜形成処理は、慣用の方法、例え
ば、真空蒸着法、イオンスパッタリング法などにより行
うことができる。被膜は、例えば無機強化コートの場合
は特殊ガラス、反射防止コートの場合はＳｉＯ、ＳｉＯ
₂ 、ＺｒＯ₂ 、Ａｌ₂ Ｏ₃ 、ＴｉＯ₂ 、Ｔｉ₂ Ｏ₃ 、Ｍ
ｇＯ、ＭｇＦ₂ 、ＣｅＯ₂ 、ＴｈＯ₂ など、赤外線反射
コートの場合はアルミニウム、金などで形成される。被
膜は単層であっても多層であってもよい。The inorganic film forming treatment can be carried out by a conventional method such as a vacuum vapor deposition method or an ion sputtering method. The coating is, for example, special glass in the case of an inorganic reinforced coating, or SiO, SiO in the case of an antireflection coating
₂ , ZrO ₂ , Al ₂ O ₃ , TiO ₂ , Ti ₂ O ₃ , M
In the case of infrared reflection coating, gO, MgF ₂ , CeO ₂ , ThO ₂ or the like is formed of aluminum, gold or the like. The coating may be a single layer or multiple layers.

【００３５】前記被覆処理により形成される各被膜の厚
みは、被覆処理の種類により異なり、例えばハードコー
ト、防曇コートなどの塗膜形成処理によって形成される
被膜の場合には、通常１〜２０μｍ、好ましくは３〜１
０μｍ程度である。The thickness of each coating formed by the above coating treatment varies depending on the type of coating treatment, and in the case of a coating formed by a coating forming treatment such as hard coating or anti-fog coating, it is usually 1 to 20 μm. , Preferably 3 to 1
It is about 0 μm.

【００３６】本発明において好ましい被覆処理には、ハ
ードコートおよび防曇コートなどが含まれる。特に、ハ
ードコートに際してシリコン系ハードコート剤を用いる
と、表面張力の小さなシリコン系被膜が形成される。そ
のため、シリコン系被膜をマスキング剤でマスキングし
て、レンズの外面とは異なる被膜形成処理をレンズの両
面に施した後、前記マスキング層を容易に剥離でき、マ
スキング層の剥離に伴なってレンズの内面に外面とは異
なる被膜を形成できるという利点を有する。Preferred coating treatments in the present invention include hard coats and anti-fog coats. In particular, when a silicon-based hard coating agent is used for hard coating, a silicon-based coating having a small surface tension is formed. Therefore, after masking the silicon-based film with a masking agent and applying a film forming treatment different from the outer surface of the lens to both surfaces of the lens, the masking layer can be easily peeled off. This has the advantage that a coating different from the outer surface can be formed on the inner surface.

【００３７】上記のように被覆処理した後、前記シール
部を除去することにより、両面の表面処理態様が互いに
異なるレンズを製造することができる。After the coating treatment as described above, the sealing portion is removed, whereby lenses having different surface treatment modes on both sides can be manufactured.

【００３８】シール部を除去する手段としては、レンズ
や被膜を損傷しない限りいかなる手段を用いてもよい。
例えば、手又は適当な道具を用いることによりシール部
を除去できる。なお、前記のように、レンズ及び遮蔽部
材の少なくとも一方の部材として、弾性又は可撓性を有
する部材を用い、レンズと遮蔽部材との間に空間を形成
すると、レンズと遮蔽部材との周縁部などを押圧するこ
とにより、両者を容易に分離できる。As means for removing the seal portion, any means may be used as long as it does not damage the lens or the coating.
For example, the seal can be removed by hand or by using a suitable tool. As described above, when a member having elasticity or flexibility is used as at least one of the lens and the shielding member, and a space is formed between the lens and the shielding member, the peripheral portion of the lens and the shielding member is formed. Both can be easily separated by pressing.

【００３９】このようして、レンズ表面が未処理のレン
ズを本発明の被覆処理に供する場合には、一方の面が未
処理で他方の面が被覆処理されたレンズが得られる。ま
た、例えば、前記被覆処理等、既に何等かの表面処理が
なされたレンズを本発明の方法に供する場合には、レン
ズの両面に互いに異なった表面処理が施されたレンズが
得られる。Thus, when a lens whose lens surface is untreated is subjected to the coating treatment of the present invention, a lens having one surface untreated and the other surface coated is obtained. Further, for example, when a lens which has already been subjected to some surface treatment such as the above-mentioned coating treatment is subjected to the method of the present invention, a lens having different surface treatments on both surfaces of the lens is obtained.

【００４０】本発明においては、シール部を除去した
後、さらに、外面とは異なる被覆処理を、少なくとも内
面に施すことができる。前記内面に施す処理は、外面に
施した被覆処理とは異なる処理であるのが有用であり、
前記の種々の被覆処理が挙げられる。各被覆処理は、前
記した方法によって行うことができる。また、この処理
は、内面のみに施してもよく、両面に施してもよい。In the present invention, after removing the seal portion, at least the inner surface can be subjected to a coating treatment different from the outer surface. It is useful that the treatment applied to the inner surface is a treatment different from the coating treatment applied to the outer surface,
The various coating treatments mentioned above may be mentioned. Each coating treatment can be performed by the method described above. Further, this treatment may be applied only to the inner surface or both surfaces.

【００４１】前記処理を内面のみに施す場合には、例え
ば、シール部を除去する前に外面をマスキングし、次い
でシールを除去して、両面に前記被覆処理を行い、しか
る後に外面のマスキング層を除去すればよい。When the above treatment is applied only to the inner surface, for example, the outer surface is masked before removing the seal portion, then the seal is removed, and the both surfaces are subjected to the coating treatment, and then the outer masking layer is applied. Just remove it.

【００４２】マスキングの方法としては、外面に施した
被膜が損傷せず、シール除去後の両面の被覆処理工程で
マスキング層が剥離しないような方法であればよい。マ
スキングは、剥離可能な被膜を形成させたり、フィルム
等を張付けることによって行うことができる。例えば、
レンズの外面がシリコン系ハードコート剤によりハード
コートされている場合には、適当なマスキング剤又は塗
料によるコーティング、あるいはマスキングシートやマ
スキングフィルムの張付け等によりマスキングを行うこ
とができる。この場合には、前記のように、レンズの外
面が表面張力の小さなシリコン系被膜が形成されている
ため、レンズ両面の被覆処理後、外面に形成されたマス
キング層を前記被覆処理により形成された外面の被膜と
共に容易に剥離することができ、マスキング層の剥離に
伴なってレンズの内面に外面とは異なる被膜を形成する
ことができる。また、マスキングは、レンズの外面に離
型剤を塗布した後、塗料等を塗布したり、フィルム等を
張付けることによって行うこともできる。As a masking method, any method may be used as long as the coating applied to the outer surface is not damaged and the masking layer is not peeled off in the coating treatment step on both surfaces after the seal is removed. The masking can be performed by forming a peelable coating or applying a film or the like. For example,
When the outer surface of the lens is hard-coated with a silicon-based hard coating agent, masking can be performed by coating with a suitable masking agent or paint, or by attaching a masking sheet or masking film. In this case, as described above, since the outer surface of the lens is formed with the silicon-based coating having a small surface tension, the masking layer formed on the outer surface is formed by the coating treatment after the coating treatment on both surfaces of the lens. It can be easily peeled off together with the coating on the outer surface, and a coating different from the outer surface can be formed on the inner surface of the lens as the masking layer is peeled off. The masking can also be performed by applying a release agent on the outer surface of the lens and then applying a paint or the like, or applying a film or the like.

【００４３】前記マスキング剤としては、例えば、サン
ノプコ（株）製のＴＣ−５３０−ＳＮ、ＴＣ−５３３−
ＳＮ、ＴＣ−５３９−ＳＮ、ノプコマスク４０５６、ノ
プコマスクＵＶ−３０等が挙げられる。また、前記塗料
には、ポリエステル樹脂、アクリル樹脂、アミノ樹脂、
エポキシ樹脂、ウレタン樹脂、水性樹脂等が含まれる。
前記塗料として、例えば、ストリップペイント［田辺化
学工業（株）製、関西ペイント（株）製など］として市
販されている塗料等を用いることができる。塗料等によ
るコーティングは、例えば浸漬法等によって行うことが
できる。Examples of the masking agent include TC-530-SN and TC-533-made by San Nopco Ltd.
SN, TC-539-SN, Nopco mask 4056, Nopco mask UV-30, etc. are mentioned. In addition, the paint includes polyester resin, acrylic resin, amino resin,
Epoxy resin, urethane resin, water-based resin, etc. are included.
As the paint, for example, a paint commercially available as strip paint [manufactured by Tanabe Chemical Industry Co., Ltd., Kansai Paint Co., Ltd., etc.] can be used. The coating with a paint or the like can be performed by, for example, a dipping method.

【００４４】マスキング層の除去法としては、例えば、
形成された被膜又はシートを剥がしたり、適当な溶媒に
より塗料等を溶解させる方法等が例示できる。マスキン
グ層の剥離強度は、テンサイルテスターによる引張り試
験法で、例えば、幅１５ｍｍ当り５〜１００ｇ程度であ
る。As a method of removing the masking layer, for example,
Examples include a method of peeling off the formed coating film or sheet, and a method of dissolving the paint or the like with an appropriate solvent. The peel strength of the masking layer is, for example, about 5 to 100 g per 15 mm width by a tensile test method using a tensil tester.

【００４５】本発明の方法において、レンズの外面にハ
ードコートを施した後、外面をマスキングし、次いでシ
ールを除去し、両面に防曇処理を施し、しかる後にマス
キング層を除去する場合には、外側の面がハードコート
され、内側の面が防曇コートされたレンズを得ることが
できる。このレンズは、外側の面にハードコート層が形
成されているため外界の物体や風塵等による傷に強く、
しかも内側の面に防曇被膜が形成されているため発汗や
吐息等によるレンズの表面の曇りを防止できるという優
れた特性を有する。従って、このレンズは、実用的なメ
ガネレンズとして極めて有用である。In the method of the present invention, when a hard coat is applied to the outer surface of the lens, the outer surface is masked, then the seal is removed, both surfaces are subjected to antifogging treatment, and then the masking layer is removed, It is possible to obtain a lens whose outer surface is hard-coated and whose inner surface is anti-fog coated. This lens has a hard coat layer on the outer surface, so it is resistant to scratches from external objects and dust,
Moreover, since the antifogging film is formed on the inner surface, it has an excellent property that it is possible to prevent the surface of the lens from being fogged due to sweating or breathing. Therefore, this lens is extremely useful as a practical spectacle lens.

【００４６】本発明の方法により製造されたレンズは、
サングラスレンズ、度付きメガネレンズ、光学器械用レ
ンズ等として好適に用いることができる。The lens produced by the method of the present invention comprises:
It can be preferably used as a sunglasses lens, a prescription eyeglass lens, a lens for optical instruments, and the like.

【００４７】[0047]

【発明の効果】本発明の方法によれば、簡易な手段によ
り、レンズの片面のみが被覆処理されるため、両面の表
面処理態様が互いに異なるレンズを効率的に製造でき
る。According to the method of the present invention, since only one surface of the lens is coated by a simple means, it is possible to efficiently manufacture lenses having different surface treatment modes on both surfaces.

【００４８】また、本発明のレンズは、外界の物体や風
塵等による傷に強く、しかも発汗や吐息等によるレンズ
表面の曇りを防止できる。Further, the lens of the present invention is resistant to scratches caused by external objects, dust and the like, and can prevent the lens surface from being fogged due to sweating or breathing.

【００４９】[0049]

【実施例】以下、本発明を実施例によって具体的に説明
するが、これらの実施例により限定されるものではな
い。なお、実施例中において、部は重量部を表す。EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples. In addition, in an Example, a part represents a weight part.

【００５０】実施例 ポリカーボネート製のレンズ（外径７５ｍｍ、中心厚２
ｍｍ）２枚を、凹面同士を向かい合わせ、周縁部を超音
波によりシールした。Example Polycarbonate lens (outer diameter 75 mm, center thickness 2)
2 mm), the concave surfaces were made to face each other, and the peripheral edge was sealed by ultrasonic waves.

【００５１】シールした２枚のレンズを、下記の組成か
らなるハードコート液に浸漬し、１０ｃｍ／分の速度で
引き上げ、１００℃、３時間で硬化させて、レンズの外
面をハードコートした。被膜の厚みは８μｍであった。The two sealed lenses were dipped in a hard coating solution having the following composition, pulled up at a speed of 10 cm / min, and cured at 100 ° C. for 3 hours to hard coat the outer surfaces of the lenses. The coating thickness was 8 μm.

【００５２】 メチルトリエトキシシラン部分加水分解縮合物 ２５部 エタノール ５０部 酢酸 ９部 イソプロパノール １５部 界面活性剤［信越化学（株）製、Ｓ−１１３］ １部 次いで、ハードコートしたレンズを、ストリップペイン
ト［田辺化学工業（株）製］に浸漬し、１５ｃｍ／分の
速度で引上げ、３０℃で１時間乾燥して外面をマスキン
グした。Methyltriethoxysilane partial hydrolysis condensate 25 parts Ethanol 50 parts Acetic acid 9 parts Isopropanol 15 parts Surfactant [Shin-Etsu Chemical Co., Ltd., S-113] 1 part Then, the hard-coated lens was strip-painted. It was immersed in [Tanabe Chemical Co., Ltd.], pulled up at a speed of 15 cm / min, and dried at 30 ° C. for 1 hour to mask the outer surface.

【００５３】外面をマスキングしたレンズのシール部を
除き、２枚のレンズに分離した。分離した各レンズを、
下記の組成からなる防曇コート液に浸漬し、８ｃｍ／分
の速度で引き上げ、乾燥し、紫外線照射により硬化させ
て、レンズの両面を防曇処理した。防曇被膜の厚みは１
０μｍであった。なお、アクリル系防曇処理剤溶液とし
て、光硬化性樹脂組成物（２−ヒドロキシエチルメタク
リレートとジエチルアミノエチルメタクリレートの共重
合体、ポリエチレングリコールジアクリレート、２−ヒ
ドロキシエチルメタクリレート、光重合開始剤を含む）
のイソプロパノール溶液を用いた。The outer surface of the lens, which was masked, was removed, and the lens was separated into two lenses. Each separated lens,
The both surfaces of the lens were subjected to antifogging treatment by immersing in an antifogging coating solution having the following composition, pulling up at a rate of 8 cm / min, drying, and curing by ultraviolet irradiation. Thickness of anti-fog coating is 1
It was 0 μm. As the acrylic anti-fog treatment solution, a photocurable resin composition (including a copolymer of 2-hydroxyethyl methacrylate and diethylaminoethyl methacrylate, polyethylene glycol diacrylate, 2-hydroxyethyl methacrylate, a photopolymerization initiator)
Was used.

【００５４】 アクリル系防曇処理剤溶液 ４０部 ｎ−プロパノール ２０部 イソプロパノール １０部 セロソルブ ３０部 前記マスキングによって形成された被膜を剥がすことに
より、外側の面がハードコートされ、内側の面が防曇コ
ートされたレンズが得られた。Acrylic anti-fogging agent solution 40 parts n-propanol 20 parts Isopropanol 10 parts Cellosolve 30 parts By peeling off the film formed by the masking, the outer surface is hard-coated and the inner surface is anti-fog coated. The obtained lens was obtained.

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 少なくとも一方の面が平面又は凹面であ
るレンズを処理する方法であって、レンズの平面又は凹
面側を、少なくともレンズの周縁部と接触可能な遮蔽部
材で遮蔽し、前記レンズと遮蔽部材との接触部を除去可
能なシール手段でシールし、前記レンズを被覆処理する
レンズの処理方法。1. A method for treating a lens, at least one surface of which is a flat surface or a concave surface, wherein the flat surface or the concave surface side of the lens is shielded by at least a shielding member which can be in contact with a peripheral portion of the lens, A method of treating a lens, wherein a contact portion with a shielding member is sealed with a removable sealing means, and the lens is covered. 【請求項２】 遮蔽部材が、レンズの周縁部と接触可能
であって、且つレンズとの対向面が平面又は凹面に形成
されているレンズである請求項１記載のレンズの処理方
法。2. The lens processing method according to claim 1, wherein the shielding member is a lens that is capable of contacting the peripheral edge of the lens and has a surface facing the lens formed into a flat surface or a concave surface. 【請求項３】 少なくとも一方の面が平面又は凹面であ
り、且つ両面の表面処理態様が互いに異なるレンズの製
造方法であって、レンズの平面又は凹面側を少なくとも
レンズの周縁部と接触可能な遮蔽部材で遮蔽し、前記レ
ンズと遮蔽部材との接触部を除去可能なシール手段でシ
ールし、前記レンズを被覆処理し、次いで前記シール部
を除去するレンズの製造方法。3. A method of manufacturing a lens in which at least one surface is a flat surface or a concave surface, and the surface treatment modes of the both surfaces are different from each other, and the flat surface or the concave surface side of the lens is capable of contacting at least the peripheral portion of the lens. A method of manufacturing a lens, which comprises shielding with a member, sealing a contact portion between the lens and the shielding member with a removable sealing means, coating the lens, and then removing the sealing portion. 【請求項４】 ２枚のレンズの凹面側を対向させ、その
周縁部を除去可能なシール手段でシールし、前記レンズ
を被覆処理し、次いでシール部を除き２枚のレンズを分
離する請求項３記載のレンズの製造方法。4. The two lenses are made to face each other with their concave surfaces facing each other, the peripheral portions thereof are sealed with removable sealing means, the lenses are covered, and then the two lenses are separated except for the sealing portion. 3. The method for manufacturing a lens according to item 3. 【請求項５】 シール部を除去した後、外面とは異なる
被覆処理を、少なくとも内面に施す請求項３記載のレン
ズの製造方法。5. The method of manufacturing a lens according to claim 3, wherein after the seal portion is removed, a coating treatment different from the outer surface is applied to at least the inner surface. 【請求項６】 外面にハードコートを施し、内面に防曇
コートを施す請求項５記載のレンズの製造方法。6. The method for producing a lens according to claim 5, wherein the outer surface is hard-coated and the inner surface is anti-fog coated. 【請求項７】 外側の面がハードコートされ、内側の面
が防曇コートされているレンズ。7. A lens having an outer surface hard-coated and an inner surface anti-fog coated.