JPH0625330Y2 - Translucent decorative sheet - Google Patents
Translucent decorative sheetInfo
- Publication number
- JPH0625330Y2 JPH0625330Y2 JP1989075585U JP7558589U JPH0625330Y2 JP H0625330 Y2 JPH0625330 Y2 JP H0625330Y2 JP 1989075585 U JP1989075585 U JP 1989075585U JP 7558589 U JP7558589 U JP 7558589U JP H0625330 Y2 JPH0625330 Y2 JP H0625330Y2
- Authority
- JP
- Japan
- Prior art keywords
- translucent
- plate
- sheet
- decorative sheet
- metal plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本考案は、金属薄板に形成した孔部を介して背面側を透
かし見ることができ、窓材，透し板材等として使用され
る透光性装飾シートに関する。The present invention relates to a translucent decorative sheet used as a window material, a see-through plate material, etc., through which a back side can be seen through a hole formed in a thin metal plate.
二枚のガラス板の間に透光性中間膜を挟み込んだ複合ガ
ラスは、ガラスの欠点である破壊時の貫通や破片の脱
落，飛散がない安全ガラスとして使用されている。透光
性中間膜で弾力性を付与し、外力を撓み変形によって吸
収することができるため、強度の向上も図られる。 挟み込む中間膜として半透明の着色シートや孔の開いた
金属薄板を使用するとき、透光量を調節できることは勿
論、透過した光によって審美性のある空間が形成され
る。この特徴を活用し、種々の中間膜を挟み込んだ複合
ガラスが内装材，外装材等として使用され始めている。 たとえば、パンチングメタルの両面に柔軟性のあるシー
トを張り合せ、中間膜として使用することが知られてい
る。パンチングメタルは、金属板に機械的な打抜き加工
を施すことにより直径３〜３０mmの貫通孔を設けたもの
である。このパンチングメタルを柔軟性シートに張り合
せた中間膜は、金属板本来の強度によって補強されてい
るため、耐破損性や飛散防止機能が一層向上する。Composite glass in which a translucent interlayer film is sandwiched between two glass plates is used as a safety glass that is free from penetration, breakage, and shattering at the time of breaking, which is a drawback of glass. Elasticity can be imparted by the translucent intermediate film, and external force can be absorbed by bending deformation, so that the strength can be improved. When a translucent colored sheet or a thin metal plate with holes is used as an intermediate film to be sandwiched, the amount of light transmitted can be adjusted, and of course, an aesthetic space is formed by the light transmitted. Taking advantage of this feature, composite glass sandwiching various kinds of interlayer films has begun to be used as an interior material, an exterior material, or the like. For example, it is known to bond a flexible sheet to both sides of a punching metal and use it as an intermediate film. The punching metal is one in which a through hole having a diameter of 3 to 30 mm is provided by mechanically punching a metal plate. Since the interlayer film obtained by sticking the punching metal to the flexible sheet is reinforced by the original strength of the metal plate, the breakage resistance and the scattering prevention function are further improved.
柔軟性シートの間に挟み込むものとしてパンチングメタ
ルを使用するとき、打抜き加工の作業面から使用可能な
金属薄板の下限板厚，形成される貫通孔のサイズ，分布
状態等に制約を受ける。たとえば、数十ミクロン程度の
金属薄板からパンチングメタルを得ようとすると、打抜
き加工時のポンチとダイス間とのクリアランスを狭くす
ることが必要になる。その結果、高精度に仕上げられた
ポンチ，ダイス等を備えた精密プレスの使用を余儀なく
され、製造コストが上昇する。 この点、通常の打抜き加工機でステンレス鋼等を加工す
るとき、パンチングされる原板の板厚は０．３mmが下限
とされている。板厚に対する制約は、金属薄板を挟み込
んだ中間膜を軽量化するときのネックになることは勿
論、中間膜を組み込んだ複合ガラスの見栄えも悪くす
る。すなわち、複合ガラスを観察するとき、貫通孔の内
壁面（板厚部）が視覚に与える印象が強く、貫通孔を透
かしてみた景色等が内壁面（板厚部）の陰影によって縁
どられたものになる。 本考案は、このような問題を解消すべく案出されたもの
であり、穿孔パターンをエッチングで形成することによ
って非常に薄い箔等の金属薄板の使用を可能にすると共
に、見栄えの良い透光性装飾シートを提供することを目
的とする。When punching metal is used as a material to be sandwiched between flexible sheets, there are restrictions on the lower limit thickness of the metal sheet that can be used, the size of the through holes to be formed, the distribution state, etc. from the working surface of punching. For example, in order to obtain punching metal from a thin metal plate of about several tens of microns, it is necessary to narrow the clearance between the punch and the die during punching. As a result, it is necessary to use a precision press equipped with punches, dies, etc. that are finished with high precision, which increases the manufacturing cost. In this respect, when processing stainless steel or the like with a normal punching machine, the lower limit of the thickness of the punched original plate is 0.3 mm. The restriction on the plate thickness not only becomes a bottleneck for reducing the weight of the interlayer film sandwiching the metal thin plates, but also makes the composite glass incorporating the interlayer film unattractive. That is, when observing the composite glass, the inner wall surface (thickness portion) of the through hole has a strong visual impression, and the view through the through hole is framed by the shadow of the inner wall surface (thickness portion). It becomes a thing. The present invention has been devised to solve such a problem, and by forming a perforation pattern by etching, it is possible to use a metal thin plate such as a very thin foil, and at the same time, it has a good-looking light transmission. It is intended to provide a sex decorative sheet.
本発明の透光性装飾シートは、その目的を達成するた
め、エッチングによって所定の穿孔パターンが形成され
た金属薄板と、該金属薄板の両面に張り合わされた透光
性シートとを備え、該透光性シートは、前記金属薄板に
の貫通孔に充填された接着剤により直接接合されている
ことを特徴とする。 透光性シートとしては、柔軟性のある合成樹脂シートを
使用することが好ましい。金属薄板を挟み込んだ透光性
シートの片面又は両面に、更にガラス板，硬質プラスチ
ックス等の透光性板材を張り合わされることもできる。In order to achieve the object, the translucent decorative sheet of the present invention comprises a metal thin plate having a predetermined perforation pattern formed by etching, and a translucent sheet laminated on both sides of the metal thin plate. The light-sensitive sheet is characterized in that it is directly bonded to the thin metal plate with an adhesive filled in a through hole. A flexible synthetic resin sheet is preferably used as the translucent sheet. A transparent plate material such as a glass plate or hard plastics may be attached to one side or both sides of the transparent sheet sandwiching the metal thin plate.
本考案の透光性装飾シートを窓材として組み込むとき、
金属薄板に形成した穿孔パターンを介して背面側の景色
を観察することができる。この透かし見た景色は、遮光
部である金属薄板の表面光沢とコントラストを形成し、
強い印象を与える。挟み込まれている金属薄板は、薄肉
であるため、視覚に悪影響を及ぼすことがない。 透光性シートに挟み込まれる金属薄板の穿孔パターン
は、パンチングメタルと異なり、高い自由度で図形，模
様等の一定パターンを再現性良く形成することができ
る。また、従来の打抜き加工では不可能であった微小で
平坦度に優れた貫通孔も容易に形成される。特に、板厚
が小さくなるほど短時間でパターン形成することができ
ることに、エッチングの有意性がある。そして、たとえ
ば微小な貫通孔を多数形成することによって、レースの
カーテンと同様な遮光性を備えた装飾シートになる。 エッチングで形成された貫通孔の端面は、平滑度の高い
表面になっている。そのため、気泡を残留させることな
く、貫通孔が接着剤で完全に充填される。その結果、金
属薄板と透光性シートとの間の接着性が長期間にわたっ
て良好に維持されると共に、透かし見た景色が残留気
泡，層間剥離等で濁ったり歪んだりすることがない。 透光性シートに挟み込まれる金属薄板には、ステンレス
鋼，普通鋼，アルミ板等があり、厚さ数ミクロンの箔を
使用することもできる。金属薄板は、板厚が０．５mm以
下で可能な限り薄いものであることが好ましい。板厚が
薄くなるほど、エッチングを短時間で完了させることが
できると共に、芯材の平滑化も図られる。 金属薄板をエッチングすることにより、第１図の（ａ）
又は（ｂ）に示すような所定パターンで貫通孔が形成さ
れる。エッチング方法としては、フォトエッチングによ
る穿孔処理を採用することが好ましい。この場合、金属
薄板にレジストを塗布した後、基準パターンを密着さ
せ、露光，バーニング，エッチング等の処理を順次施
す。 貫通孔が形成された金属薄板１の両面に、第２図に示す
ように透光性シート２，２が張り合わされる。透光性シ
ート２，２には、複合ガラスとするとき外側に張り合わ
されるガラス板３，３よりも軟質で、無色透明或いは適
宜の着色を施した透明又は半透明の樹脂，合成樹脂等が
使用される。柔軟性のある透光性シート２，２の使用に
より、金属薄板１を間に挟み込んだ後でもコイル状に巻
き取ることが可能となり、取扱いや運搬，施工等が容易
になる。 透光性シート２，２は、金属薄板１に張り合わされると
共に、金属薄板１に形成した貫通孔に充填される接着剤
４を介し互いに直接接合される。そのため、接着強度が
一層向上し、耐層間剥離性が優れたものとなる。接着剤
４としては、透光性のある熱硬化型接着剤が好ましい。
たとえば、酢酸ビニル系，ポリブチラール系，ホットメ
ルト系等の接着剤が使用される。 接着剤４は、ロールコータ，ブラシ，スプレー等の適宜
の方法により金属薄板１の両面に塗布される。このと
き、金属薄板１の一面或いは両面にやや過剰に接着剤４
を塗布することが好ましい。接着剤４が塗布された金属
薄板４は、透光性シート２，２の間に挟み込まれ、上下
２段の複数のゴム被覆ロール間に通板される。ゴム被覆
ロールによる加圧により、透光性シート２，２に金属薄
板１が接着されると共に、接着剤４の過剰量が金属薄板
１の貫通孔に流動し、貫通孔を充填する。 透光性シート２，２が張り合わされた金属薄板１は、そ
のままで装飾シートとして使用することができる。この
場合、建築等の施工現場で、二枚のガラス板の間に装飾
シートを挟み込み、複合ガラスを構築する。或いは、既
設のガラス板に内側又は外側から装飾シートを張り付け
ることによっても、装飾性に富んだ窓にすることができ
る。このとき、シャー等によって適宜のサイズに裁断す
ることができるため、現場での施工性は優れたものとな
る。 装飾シートをガラス板，硬質プラスチックス等の透明板
材３，３に挟み込み、工場出荷段階で透光性装飾シート
材にすることも可能である。ガラス板，硬質プラスチッ
クス等に対する装飾シートの接着は、市販の接着テープ
を使用して行うことができる。或いは、ポリブチラール
樹脂膜を貼着した後、オートクレーブ中で加圧接着する
ことによっても、装飾シートをガラス板，硬質プラスチ
ックス等に張り合せることができる。When incorporating the translucent decorative sheet of the present invention as a window material,
The view on the back side can be observed through the perforation pattern formed on the thin metal plate. The scenery seen through this watermark creates contrast with the surface gloss of the thin metal plate that is the light-shielding part,
Make a strong impression. Since the thin metal plates sandwiched are thin, they do not adversely affect the vision. Unlike the punching metal, the perforation pattern of the metal thin plate sandwiched between the translucent sheets can form a fixed pattern such as a figure or a pattern with high reproducibility with a high degree of freedom. Further, minute through holes having excellent flatness, which cannot be obtained by the conventional punching process, can be easily formed. In particular, it is significant in etching that the pattern can be formed in a shorter time as the plate thickness becomes smaller. Then, for example, by forming a large number of minute through holes, a decorative sheet having a light shielding property similar to that of a lace curtain is obtained. The end surface of the through hole formed by etching has a high smoothness. Therefore, the through holes are completely filled with the adhesive without leaving bubbles. As a result, the adhesiveness between the metal thin plate and the translucent sheet is maintained good for a long period of time, and the view through the watermark does not become turbid or distorted due to residual bubbles, delamination or the like. The metal thin plates sandwiched between the translucent sheets include stainless steel, ordinary steel, aluminum plates and the like, and a foil with a thickness of several microns can also be used. The metal thin plate is preferably as thin as possible with a plate thickness of 0.5 mm or less. As the plate thickness becomes thinner, the etching can be completed in a shorter time and the core material can be smoothed. By etching the thin metal plate, (a) of FIG.
Alternatively, the through holes are formed in a predetermined pattern as shown in (b). As the etching method, it is preferable to adopt a perforation process by photoetching. In this case, after applying a resist to a thin metal plate, a reference pattern is brought into close contact therewith, and treatments such as exposure, burning, and etching are sequentially performed. As shown in FIG. 2, translucent sheets 2 and 2 are attached to both surfaces of the metal thin plate 1 having the through holes formed therein. The translucent sheets 2 and 2 are made of a composite resin such as a transparent or translucent resin which is softer than the glass plates 3 and 3 which are laminated to the outside and is colorless and transparent or appropriately colored. used. By using the flexible light-transmitting sheets 2 and 2, it is possible to wind the thin metal plate 1 into a coil even after sandwiching the thin metal plate 1 between them, which facilitates handling, transportation, and construction. The translucent sheets 2 and 2 are bonded to the thin metal plate 1 and are directly bonded to each other via an adhesive 4 filled in a through hole formed in the thin metal plate 1. Therefore, the adhesive strength is further improved and the delamination resistance is excellent. As the adhesive 4, a translucent thermosetting adhesive is preferable.
For example, a vinyl acetate-based, polybutyral-based, hot-melt-based adhesive or the like is used. The adhesive 4 is applied to both sides of the thin metal plate 1 by an appropriate method such as a roll coater, a brush, or a spray. At this time, the adhesive 4 may be slightly overlaid on one or both surfaces of the thin metal plate 1.
Is preferably applied. The metal thin plate 4 to which the adhesive 4 is applied is sandwiched between the translucent sheets 2 and 2, and is passed between a plurality of upper and lower rubber-coated rolls. The metal thin plate 1 is bonded to the translucent sheets 2 and 2 by the pressure applied by the rubber-coated roll, and an excessive amount of the adhesive 4 flows into the through holes of the metal thin plate 1 to fill the through holes. The metal thin plate 1 to which the translucent sheets 2 and 2 are attached can be used as it is as a decorative sheet. In this case, at a construction site such as a building, a decorative sheet is sandwiched between two glass plates to construct a composite glass. Alternatively, a window with high decorativeness can be obtained by attaching a decorative sheet to an existing glass plate from inside or outside. At this time, since it can be cut into an appropriate size by a shear or the like, workability at the site becomes excellent. It is also possible to sandwich the decorative sheet between the transparent plates 3 and 3 such as glass plates and hard plastics, and use it as a translucent decorative sheet material at the factory shipment stage. Adhesion of the decorative sheet to the glass plate, hard plastics or the like can be performed using a commercially available adhesive tape. Alternatively, the decorative sheet can be attached to a glass plate, hard plastics or the like by sticking a polybutyral resin film and then pressure-bonding it in an autoclave.
金属薄板１として、板厚０．１０mmのステンレス鋼板Ｓ
ＵＳ３０４を使用した。金属薄板１をフォトエッチング
し、穿孔面積率５０％で直径３mmの円形貫通孔が複数設
けられた図１（ａ）の穿孔パターンを形成した。エッチ
ング後の金属薄板１から、３０cm×３０cmの試験片を切
り出した。 エッチングされた金属薄板１の両面に、図２に示すよう
に膜厚０．７mmのポリウレタン樹脂製透光性シート２，
２を張り合せた。このとき、接着剤４として、酢酸ビニ
ル系接着剤を予め金属薄板１の両面に塗布した。全体を
赤外線加熱によって６０℃に加熱保持した状態でロール
圧延し、金属薄板１を挟み込んだ装飾シートを得た。得
られた装飾シートを観察したところ、金属薄板１に形成
されている貫通孔は、残留気泡がみられず接着剤４で完
全に充填されていた。 更に装飾シートの両面に、酢酸ビニル系接着剤を使用
し、板厚２mmの透明珪酸ガラス３，３を張り合せた。こ
れにより、合計厚み５．５mmの複合ガラスを得た。 得られた複合ガラスをヒートサイクル試験に供した後、
強度試験を行った。ヒートサイクル試験としては、１０
０℃に３時間加熱した後で３時間放冷することを１サイ
クルとする加熱・冷却を５０サイクル繰り返した。強度
試験では、試験片の周囲を２５cm平方の木枠で固定した
状態で、約１Kgの錘を２ｍの高さから落下させ、飛散し
たガラス破片の大きさを調べた。発生したガラス破片
は、小片であり、量的にも少なくないものであった。こ
れは、外側のガラス板３，３だけが小片となって飛散し
たことに由来するものであり、極めて耐飛散性能に優れ
ていることが判る。 これに対し、板厚０．３mmのパンチングメタルを使用し
た複合ガラスでは、貫通孔を介して透かし見た背面側の
景色の周辺に貫通孔の内壁面に起因する陰影が生じてい
た。また、破壊テストでは、中間膜と外側のガラス板が
接着したままの大きな破片が発生した。これは、ヒート
サイクル試験で金属薄板と透光性シート２，２との間に
熱剥離が発生したことに起因するものと推察され、太陽
光線の照射に繰り返し曝される窓材等として使用したと
きに安全性に問題があることを示している。As the thin metal plate 1, a stainless steel plate S having a plate thickness of 0.10 mm
US304 was used. The thin metal plate 1 was photo-etched to form a perforation pattern of FIG. 1 (a) in which a plurality of circular through holes having a perforation area ratio of 50% and a diameter of 3 mm were provided. A 30 cm × 30 cm test piece was cut out from the metal thin plate 1 after etching. As shown in FIG. 2, a polyurethane resin translucent sheet 2 having a thickness of 0.7 mm is formed on both sides of the etched metal thin plate 1, as shown in FIG.
Pasted two. At this time, as the adhesive 4, a vinyl acetate-based adhesive was previously applied to both surfaces of the thin metal plate 1. The whole was heated and kept at 60 ° C. by infrared heating and rolled to obtain a decorative sheet in which the thin metal plate 1 was sandwiched. Observation of the obtained decorative sheet revealed that the through-holes formed in the metal thin plate 1 were completely filled with the adhesive 4 without residual bubbles. Further, a vinyl acetate adhesive was used on both sides of the decorative sheet, and transparent silicate glasses 3 and 3 having a plate thickness of 2 mm were attached to each other. Thereby, a composite glass having a total thickness of 5.5 mm was obtained. After subjecting the obtained composite glass to a heat cycle test,
A strength test was conducted. 10 as a heat cycle test
50 cycles of heating and cooling, which consisted of heating to 0 ° C. for 3 hours and then allowing to cool for 3 hours, were repeated. In the strength test, a weight of about 1 kg was dropped from a height of 2 m while the periphery of the test piece was fixed with a wooden frame of 25 cm square, and the size of the scattered glass fragments was examined. The generated glass fragments were small pieces and were not a few in quantity. This results from the fact that only the outer glass plates 3 and 3 were scattered as small pieces, and it can be seen that the anti-scattering performance is extremely excellent. On the other hand, in the composite glass using a punching metal having a plate thickness of 0.3 mm, a shadow due to the inner wall surface of the through hole was formed around the back side scenery seen through the through hole. Also, in the destructive test, large fragments were generated with the interlayer film and the outer glass plate being adhered. It is presumed that this is due to the occurrence of thermal delamination between the thin metal plate and the translucent sheets 2 and 2 in the heat cycle test, and it was used as a window material that is repeatedly exposed to the irradiation of sunlight. Sometimes it indicates a safety issue.
以上に説明したように、本考案の透光性装飾シートは、
エッチングにより所定の穿孔パターンが形成された金属
薄板を透光性シートの間に挟み込んでいるため、残留気
泡等に起因した層間剥離等を生じることなく、経時的に
も劣化しない優れた接着性で金属薄板と透光性シートを
一体化している。この装飾シートは、従来のパンチング
メタルに比較して大幅に薄肉の板材を使用することがで
きる。その結果、装飾シート或いは装飾シートを組み込
んだ複合ガラスを軽量化できることは勿論、貫通孔の内
壁面（板厚部）が視覚に与える影響が少なく、意匠性に
優れた建材が得られる。As described above, the translucent decorative sheet of the present invention is
Since a thin metal plate with a predetermined perforation pattern formed by etching is sandwiched between translucent sheets, it does not cause delamination due to residual bubbles, etc., and has excellent adhesiveness that does not deteriorate over time. The thin metal plate and the translucent sheet are integrated. This decorative sheet can use a plate material that is significantly thinner than conventional punching metal. As a result, it is possible to reduce the weight of the decorative sheet or the composite glass incorporating the decorative sheet, and it is also possible to obtain a building material excellent in design, since the inner wall surface (thickness portion) of the through hole has little visual effect.
図１は金属薄板に形成される穿孔パターンの例を示し、
図２は本考案実施例における複合ガラスの層構成を示
し、図３は複合ガラス板の断面斜視図を示す。 １：穿孔された金属薄板、２：透光性シート ３：透明板材、４：接着剤FIG. 1 shows an example of a perforation pattern formed on a thin metal plate,
FIG. 2 shows the layer structure of the composite glass in the embodiment of the present invention, and FIG. 3 is a sectional perspective view of the composite glass plate. 1: Perforated metal thin plate 2: Translucent sheet 3: Transparent plate material 4: Adhesive
Claims (3)
形成された金属薄板と、該金属薄板の両面に張り合わさ
れた透光性シートとを備え、該透光性シートは、前記金
属薄板にの貫通孔に充填された接着剤によって直接接合
されていることを特徴とする透光性装飾シート。1. A thin metal plate having a predetermined perforation pattern formed by etching, and a translucent sheet attached to both sides of the thin metal plate, the translucent sheet having through holes in the thin metal plate. A translucent decorative sheet, characterized in that it is directly bonded by an adhesive filled in.
ある合成樹脂シートであることを特徴とする透光性装飾
シート。2. The translucent decorative sheet according to claim 1, wherein the translucent sheet is a flexible synthetic resin sheet.
に透光性板材が接着されていることを特徴とする透光性
装飾シート。3. A translucent decorative sheet, characterized in that a translucent plate material is further adhered to the translucent sheet according to claim 1 or 2.