JPH06247076A - Re-peelable pressure-sensitive adhesive postcard - Google Patents
Re-peelable pressure-sensitive adhesive postcardInfo
- Publication number
- JPH06247076A JPH06247076A JP5035195A JP3519593A JPH06247076A JP H06247076 A JPH06247076 A JP H06247076A JP 5035195 A JP5035195 A JP 5035195A JP 3519593 A JP3519593 A JP 3519593A JP H06247076 A JPH06247076 A JP H06247076A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- pressure
- sensitive adhesive
- postcard
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、再び剥離することによ
ってその接合面の情報を見ることができる再剥離性感圧
接着葉書に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a releasable pressure-sensitive adhesive postcard in which information on the joint surface can be seen by repeeling.
【０００２】[0002]
【従来の技術】個人情報を載せた部分に粘着ラベルを貼
り付けて、その箇所の情報を隠蔽するタイプの機密性葉
書は、葉書料金で機密情報を郵送できるメリットから需
要が増加しつつある。こうしたタイプの葉書としては、
既に数種類のものが市販されているが、いずれも性能と
コストの何れかの面でまだ充分とは言えない状況にあ
る。例えば、実開昭６３−６８７０号に記載のものは、
剥離が接合面である粘着層以外の非粘着性の樹脂層から
生じて、一度そのラベルを葉書から剥がすと容易に再接
合できないように設計されており、ラベルの剥離が極め
て安定しているという特徴を有するが、使用される粘着
ラベルが多層構造を有するために、その製造に際して多
くの工程を必要として製造コストが極めて高くなり、郵
送料金の割安からくるコスト的なメリットが小さいもの
となっている。2. Description of the Related Art Confidential postcards of a type in which an adhesive label is attached to a portion on which personal information is placed and the information at that portion is concealed are in increasing demand due to the merit that the confidential information can be mailed at a postcard fee. For this type of postcard,
Although several kinds have already been put on the market, none of them are still sufficient in terms of performance or cost. For example, the one described in Japanese Utility Model Publication No. 63-6870 is
It is designed so that peeling occurs from a non-adhesive resin layer other than the adhesive layer that is the bonding surface, and once the label is peeled from the postcard, it cannot be easily re-bonded, and the label peeling is extremely stable. Although it has features, since the adhesive label used has a multi-layered structure, many steps are required for its manufacture, resulting in extremely high manufacturing cost and a small cost merit due to the low shipping fee. There is.
【０００３】また、本発明者等は、先に特願平１−２７
０８４９号、同１−３３９９９５号において、特定のＴ
型剥離力を有する感圧接着性シートと非接着性シートを
重て加圧処理することによって接合でき、且つ接合面を
剥離することによって再び接合面の情報を読むことがで
きる再剥離性の葉書が、製造コストの面で実開昭６３−
６８７０号の葉書より優れていることを明らかにした。The inventors of the present invention previously filed Japanese Patent Application No. 1-27.
0849, 1-339995, the specific T
Releasable postcards that can be joined by pressure-treating a pressure-sensitive adhesive sheet having a mold release force and a non-adhesive sheet and by reading the joined surface again by peeling the joined surface However, in terms of manufacturing cost
It proved to be superior to the postcard of No. 6870.
【０００４】しかし、かかるタイプの葉書を詳細に検討
した結果、実用上不十分な点を有することが分かった。
即ち、葉書に個人情報を出力する際にプリンターとして
電子写真方式を用いた場合、剥離時にラベルへのトナー
の転移が発生し易く、記録像の判読できないケースが生
じる。そのため、本発明者等は、以前にこの現象を改善
する為の種々の提案をして来たが、未だ完全なものは無
く、更なる改善が望まれていた。However, as a result of detailed examination of such a type of postcard, it was found that there were some points that were insufficient for practical use.
That is, when an electrophotographic system is used as a printer when outputting personal information to a postcard, transfer of toner to a label is likely to occur at the time of peeling, and a recorded image may not be readable. Therefore, the present inventors have previously made various proposals for improving this phenomenon, but none have been perfect yet, and further improvement is desired.
【０００５】[0005]
【発明が解決しようとする課題】本発明の目的は、剥離
後における情報の判読性に優れた再剥離性感圧接着葉書
を提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide a removable pressure-sensitive adhesive postcard having excellent readability of information after peeling.
【０００６】[0006]
【課題を解決するための手段】本発明者等は検討した結
果、感圧接着性シートの支持体として特定の材料を用い
ることによって上記問題を解決できることを見出し、本
発明を完成するに至った。As a result of studies, the present inventors have found that the above problems can be solved by using a specific material as a support of a pressure-sensitive adhesive sheet, and have completed the present invention. .
【０００７】本発明は、支持体上に接着剤層を設けてな
るラベル用感圧接着性シートを、非接着性葉書用シート
上に強圧下で接合して得られる再剥離性感圧接着葉書に
おいて、該感圧接着性シートの支持体が、中空粒子層を
有する基材からなることを特徴とする再剥離性感圧接着
葉書である。The present invention relates to a removable pressure-sensitive adhesive postcard obtained by bonding a pressure-sensitive adhesive sheet for labels having an adhesive layer on a support to a non-adhesive postcard sheet under high pressure. The pressure-sensitive adhesive postcard is characterized in that the support of the pressure-sensitive adhesive sheet is composed of a base material having a hollow particle layer.
【０００８】[0008]
【作用】本発明は中空粒子層を有する基材を感圧接着性
シートの支持体として使用することを特徴とするもので
あるが、この効果については、使用した中空粒子のクッ
ション性に起因するものと思われる。The present invention is characterized by using a substrate having a hollow particle layer as a support for a pressure-sensitive adhesive sheet. This effect is due to the cushioning property of the hollow particles used. It seems to be.
【０００９】かかる支持体としては、例えば上質紙或
いは含浸紙或いは合成紙等の基材（以下基材と称す）の
表面に中空粒子層を設けたもの、基材の表面に中空粒
子層と有色コート層を順次積層したもの、基材の表面
に有色コート層と中空粒子層を順次積層したもの、基
材の表面に中空粒子層を設け、又その裏面に顔料コート
層を設けたもの、基材の表面に有色コート層と中空粒
子層を順次積層し、又その裏面に顔料コート層を設けた
もの、基材の表面に中空粒子層と有色コート層を順次
積層し、又その裏面に顔料コート層を設けたもの、基
材の表面に中空粒子層を設け、更にその中空粒子層上に
顔料コート層を設けたもの、基材の表面に中空粒子層
と顔料コート層を順次積層し、又その裏面に有色コート
層を設けたものが挙げられる。又、中空粒子層を複数層
有するもの、或いは特殊なケースとして、抄紙の際に中
空粒子を抄込んだものなども使用できる。しかし、コス
ト面と性能面で最もバランスの取れたものは、の
ケースである。As such a support, for example, a base material (hereinafter referred to as a base material) such as high-quality paper, impregnated paper or synthetic paper, provided with a hollow particle layer on the surface, a hollow particle layer and a colored layer on the surface of the base material One in which a coat layer is sequentially laminated, one in which a colored coat layer and a hollow particle layer are sequentially laminated on the surface of a base material, one in which a hollow particle layer is provided on the surface of a base material, and a pigment coat layer is provided on the back surface thereof, A material in which a colored coat layer and a hollow particle layer are sequentially laminated on the surface of the material, and a pigment coat layer is provided on the back surface thereof, a hollow particle layer and a colored coat layer are sequentially laminated on the surface of the base material, and a pigment is formed on the back surface thereof. The one provided with a coat layer, the hollow particle layer provided on the surface of the substrate, the one further provided with a pigment coat layer on the hollow particle layer, the hollow particle layer and the pigment coat layer are sequentially laminated on the surface of the substrate, Further, there may be mentioned one having a colored coat layer provided on the back surface thereof. Further, it is also possible to use one having a plurality of hollow particle layers, or as a special case, one in which hollow particles are incorporated during papermaking. However, the most balanced case in terms of cost and performance is the case of.
【００１０】中空粒子層の形成に用いられる塗液は、中
空粒子とバインダーを基本成分として含有させたもので
ある。中空粒子として最も好ましいものは、芯物質とし
てｎ−ブタン，ｉ−ブタン，ペンタン、ネオペンタンの
様な低沸点化合物を内包し、壁膜剤として塩化ビニリデ
ン，アクリロニトリル，メチルメタクリレート，スチレ
ン等の熱可塑性樹脂を使用した発泡性マイクロカプセル
であり、具体的には、松本マイクロスフェアＦ−３０，
Ｆ−５０，Ｆ−８０（松本油脂社製）、エクスパンセル
ＷＵ−６４２，ＷＵ−５５１，ＷＵ−４６２（エクスパ
ンセル社製）等が挙げられる。The coating liquid used for forming the hollow particle layer contains hollow particles and a binder as basic components. The most preferable hollow particles include a low boiling point compound such as n-butane, i-butane, pentane or neopentane as a core substance, and a thermoplastic resin such as vinylidene chloride, acrylonitrile, methyl methacrylate or styrene as a wall film agent. Is a foamable microcapsule using, specifically, Matsumoto Microsphere F-30,
F-50, F-80 (made by Matsumoto Yushi Co., Ltd.), Expancel WU-642, WU-551, WU-462 (made by Expancel), etc. are mentioned.
【００１１】バインダーとしては、水性系として塗布す
る場合にはスチレン・ブタジエン系ラテックス，アクリ
ル酸エステル系ラテックス，酢酸ビニル系ラテックス，
塩化ビニル系ラテックス等のラテックス系バインダー、
糊化澱粉，カルボキシメチルセルロース，ヒドロキシエ
チルセルロース，アルギン酸ソーダ，ポリビニルアルコ
ール，ポリアクリル酸等の水溶性バインダー、非水性と
して塗布する場合にはポリビニルメチルエーテル，ポリ
ビニルエチルエーテル，エチルセルロース，ポリウレタ
ン樹脂，アルキド樹脂等の油溶性バインダーが使用され
る。又電子線或いは紫外線で硬化する場合にはアクリル
酸エステル類等のエチレン性不飽和結合を有するモノマ
ー，オリゴマー，プレポリマーが使用される。As the binder, when applied as an aqueous system, styrene / butadiene latex, acrylic ester latex, vinyl acetate latex,
Latex binder such as vinyl chloride latex,
Water-soluble binders such as gelatinized starch, carboxymethyl cellulose, hydroxyethyl cellulose, sodium alginate, polyvinyl alcohol, polyacrylic acid, etc. When applied non-aqueous, polyvinyl methyl ether, polyvinyl ethyl ether, ethyl cellulose, polyurethane resin, alkyd resin, etc. An oil soluble binder is used. Further, in the case of curing with electron beams or ultraviolet rays, monomers, oligomers and prepolymers having an ethylenically unsaturated bond such as acrylic acid esters are used.
【００１２】バインダーは、通常中空粒子１重量部に対
して１〜１００重量部の範囲で配合される。必要に応じ
て更にシリカ，カオリン，水酸化アルミニウム，酸化亜
鉛，酸化チタン，メラミン樹脂粒子，ベンゾグアナミン
樹脂粒子，澱粉粒子，パルプパウダー等の顔料、有色顔
料或いは有色染料、アルミニウム等の金属粉末、帯電防
止剤、増粘剤、分散剤、界面活性剤、防腐剤、酸化防止
剤、消泡剤、光重合開始剤等を適宜選択して添加でき
る。The binder is usually blended in the range of 1 to 100 parts by weight with respect to 1 part by weight of the hollow particles. If necessary, silica, kaolin, aluminum hydroxide, zinc oxide, titanium oxide, melamine resin particles, benzoguanamine resin particles, starch particles, pigments such as pulp powder, colored pigments or colored dyes, metal powders such as aluminum, antistatic Agents, thickeners, dispersants, surfactants, preservatives, antioxidants, defoamers, photopolymerization initiators and the like can be appropriately selected and added.
【００１３】中空粒子層は、上記成分を含有する塗液を
エアーナイフコーター、グラビアコーター、ロールコー
ター、カーテンコーター、ブレードコーター、バーコー
ター等の塗工機或いはグラビア印刷、スクリーン印刷、
フレキソ印刷、活版印刷、オフセット印刷等の印刷機を
用い、通常乾燥重量が３〜３０ｇ／ｍ2 となるように塗
布形成される。発泡性マイクロカプセルとしては既に発
泡処理済のものも使用できるが、発泡を塗抹後に行う場
合には、熱風、熱ロール、赤外線ヒーター、マイクロ波
等従来公知の加熱方法が使われる。The hollow particle layer is formed by coating a coating solution containing the above components with a coating machine such as an air knife coater, a gravure coater, a roll coater, a curtain coater, a blade coater or a bar coater, or gravure printing, screen printing,
Using a printing machine such as flexographic printing, letterpress printing, offset printing, etc., it is usually applied and formed so as to have a dry weight of 3 to 30 g / m 2 . As the expandable microcapsules, those that have already undergone foaming can be used, but when foaming is performed after smearing, a conventionally known heating method such as hot air, a heat roll, an infrared heater, or a microwave is used.
【００１４】顔料コート層の形成に用いられる塗液は、
白色顔料とバインダーを基本成分として含有させたもの
であり、該白色顔料として好ましいものとしては、シリ
カ，カオリン，水酸化アルミニウム，酸化亜鉛，酸化チ
タン，メラミン樹脂粒子，ベンゾグアナミン樹脂粒子，
尿素樹脂等が挙げられる。また、バインダーとしては、
上記のバインダーが挙げられる。The coating liquid used for forming the pigment coat layer is
A white pigment and a binder are contained as basic components. Preferred white pigments include silica, kaolin, aluminum hydroxide, zinc oxide, titanium oxide, melamine resin particles, benzoguanamine resin particles,
Examples include urea resins. Also, as a binder,
The binders mentioned above may be mentioned.
【００１５】上記塗液には、必要に応じて有色顔料或い
は有色染料、アルミニウム等の金属粉末、帯電防止剤、
増粘剤、分散剤、界面活性剤、防腐剤、酸化防止剤、消
泡剤、光重合開始剤等を適宜選択して添加できる。顔料
コート層は、上記成分を含有する塗液をエアーナイフコ
ーター、グラビアコーター、ロールコーター、カーテン
コーター、ブレードコーター、バーコーター等の塗工機
或いはグラビア印刷、スクリーン印刷、フレキソ印刷、
活版印刷、オフセット印刷等の印刷機を用い、通常乾燥
重量が２〜３０ｇ／ｍ2 となるように塗布形成される。If necessary, the above coating liquid may include a colored pigment or colored dye, a metal powder such as aluminum, an antistatic agent,
A thickener, a dispersant, a surfactant, a preservative, an antioxidant, a defoaming agent, a photopolymerization initiator and the like can be appropriately selected and added. The pigment coat layer is a coating liquid containing the above components, such as an air knife coater, a gravure coater, a roll coater, a curtain coater, a blade coater, a bar coater, or a gravure printing, screen printing, flexographic printing,
Using a printing machine such as letterpress printing or offset printing, coating is usually applied to form a dry weight of 2 to 30 g / m 2 .
【００１６】本発明において有色コート層の形成に用い
られる塗液は、有色染料或いは有色顔料とバインダーを
基本成分として含有させたものであり、該有色染料或い
は有色顔料には従来公知の材料が使用できる。又、バイ
ンダーとしては、上記のバインダーが挙げられる。上記
塗液には、必要に応じて上記白色顔料、アルミニウム等
の金属粉末、帯電防止剤、増粘剤、分散剤、界面活性
剤、防腐剤、酸化防止剤、消泡剤、光重合開始剤等を適
宜選択して添加できる。The coating liquid used for forming the colored coat layer in the present invention contains a colored dye or colored pigment and a binder as basic components, and conventionally known materials are used for the colored dye or colored pigment. it can. Further, examples of the binder include the above binders. In the coating liquid, if necessary, the white pigment, metal powder such as aluminum, antistatic agent, thickener, dispersant, surfactant, preservative, antioxidant, defoaming agent, photopolymerization initiator Etc. can be appropriately selected and added.
【００１７】有色コート層は、上記成分を含有する塗液
をエアーナイフコーター、グラビアコーター、ロールコ
ーター、カーテンコーター、ブレードコーター、バーコ
ーター等の塗工機或いはグラビア印刷、スクリーン印
刷、フレキソ印刷、活版印刷、オフセット印刷等の印刷
機を用い、通常乾燥重量が２〜２０ｇ／ｍ2 となるよう
に塗布形成される。The colored coat layer is formed by coating a coating solution containing the above components with an air knife coater, a gravure coater, a roll coater, a curtain coater, a blade coater, a bar coater or the like, or gravure printing, screen printing, flexographic printing, letterpress printing. Using a printing machine such as printing or offset printing, it is usually applied and formed to have a dry weight of 2 to 20 g / m 2 .
【００１８】上記各塗液が塗抹される上質紙紙或いは含
浸紙或いは合成紙には、通常２０〜１５０ｇ／ｍ2 の範
囲のものが使用される。因みに、上質紙或いは含浸紙の
原紙の抄紙方法は特に限定されず、古紙再生パルプを含
んでいても構わない。又、合成紙としては、ポリエチレ
ン、ポリプロピレン、ポリスチレン、ポリエステル等従
来公知の材料のものが使用できる。尚、本発明の効果
は、上質紙を使用した場合に最も顕著である。The fine paper, impregnated paper or synthetic paper to which the above coating liquids are smeared is usually used in the range of 20 to 150 g / m 2 . Incidentally, the method for making a base paper of high-quality paper or impregnated paper is not particularly limited, and recycled paper recycled pulp may be contained. Further, as the synthetic paper, conventionally known materials such as polyethylene, polypropylene, polystyrene and polyester can be used. The effect of the present invention is most remarkable when using high-quality paper.
【００１９】本発明においては、顔料コート層、有色コ
ート層、中空粒子層の形成後、必要に応じてスーパーキ
ャレンダー掛けすることができる。In the present invention, after the formation of the pigment coat layer, the colored coat layer and the hollow particle layer, super calendering can be carried out if necessary.
【００２０】本発明において接着剤層の形成に用いられ
る接着剤としては、例えばエチレン−酢酸ビニル系樹
脂、アクリル系樹脂、塩化ビニル系樹脂、塩化ビニリデ
ン系樹脂、合成ゴム系樹脂、天然ゴム系樹脂等が挙げら
れ、中でもガラス転移点が−１００〜０℃のものが好ま
しい。Examples of the adhesive used for forming the adhesive layer in the present invention include ethylene-vinyl acetate resin, acrylic resin, vinyl chloride resin, vinylidene chloride resin, synthetic rubber resin and natural rubber resin. And the like. Among them, those having a glass transition point of −100 to 0 ° C. are preferable.
【００２１】接着剤層には、更にシリカ，カオリン，ク
レー，炭酸カルシウム，水酸化アルミニウム，酸化亜
鉛，酸化チタン，メラミン樹脂粒子，ベンゾグアナミン
樹脂粒子，澱粉粒子，パルプパウダー等の顔料、カゼイ
ン，寒天，アラビアゴム，アルギン酸ソーダ，澱粉，酸
化澱粉，エステル化澱粉，カルボキシメチルセルロー
ス，ヒドロキシエチルセルロース，ポリビニルアルコー
ル，ポリビニルピロリドン，ポリアクリル酸等の水溶性
高分子、スチレン−ブタジエンラテックス，アクリロニ
トリル−ブタジエンラテックス等のラテックス、ロジン
系樹脂及びその誘導体，テルペン系樹脂，クマロンイン
デン樹脂，キシレン樹脂，アルキルフェノール樹脂，Ｃ
5 乃至Ｃ9 系石油樹脂等の粘着付与剤、各種パラフィン
ワックス，脂肪酸，脂肪酸金属塩或いは脂肪酸アミド等
の脂肪酸誘導体，高級アルコール類，金属石鹸類，シリ
コーン類等の離型剤、接着性を高めるための接着剤含有
カプセルやオイルカプセル、有色顔料或いは有色染料、
アルミニウム等の金属粉末、帯電防止剤、増粘剤、分散
剤、防腐剤、酸化防止剤、消泡剤等を適宜選択して添加
できる。中でも、離型剤とパルプパウダーの１０重量％
以上の添加系は、耐ブロッキング性と耐トナー転移性に
優れた効果を有し、特に好ましい。The adhesive layer further includes silica, kaolin, clay, calcium carbonate, aluminum hydroxide, zinc oxide, titanium oxide, melamine resin particles, benzoguanamine resin particles, starch particles, pigments such as pulp powder, casein, agar, Gum Arabic, Sodium Alginate, Starch, Oxidized Starch, Esterified Starch, Carboxymethyl Cellulose, Hydroxyethyl Cellulose, Polyvinyl Alcohol, Polyvinylpyrrolidone, Polyacrylic Acid and Other Water-Soluble Polymers, Styrene-Butadiene Latex, Acrylonitrile-Butadiene Latex and Other Latex, Rosin resin and its derivatives, terpene resin, coumarone indene resin, xylene resin, alkylphenol resin, C
5 to C 9 petroleum resin tackifiers, various paraffin waxes, fatty acids, fatty acid metal salts or fatty acid derivatives such as fatty acid amides, release agents such as higher alcohols, metal soaps, silicones, etc. Adhesive-containing capsules or oil capsules, colored pigments or dyes,
A metal powder such as aluminum, an antistatic agent, a thickener, a dispersant, a preservative, an antioxidant, an antifoaming agent, etc. can be appropriately selected and added. Above all, 10% by weight of release agent and pulp powder
The above addition system is particularly preferable because it has excellent blocking resistance and toner transfer resistance.
【００２２】接着剤層形成に用いられる塗液としては、
水性系又は有機溶剤系又は無溶剤系（ホットメルト，電
離放射線）のいずれでも使用可能であるが、通常上記接
着剤をエマルジョンとした水性系の塗液が用いられる。
接着剤層は、上記成分を含有する塗液をエアーナイフコ
ーター、グラビアコーター、ロールコーター、カーテン
コーター、ブレードコーター、バーコーター等の塗工機
或いはグラビア印刷、スクリーン印刷、フレキソ印刷、
活版印刷、オフセット印刷等の印刷機を用い、通常乾燥
重量が２〜３０ｇ／ｍ2 となるように上記支持体に塗布
形成される。The coating liquid used for forming the adhesive layer is
Although any of an aqueous system, an organic solvent system and a solventless system (hot melt, ionizing radiation) can be used, an aqueous coating solution obtained by using the above adhesive as an emulsion is usually used.
The adhesive layer is a coating liquid containing the above components such as an air knife coater, a gravure coater, a roll coater, a curtain coater, a blade coater, a bar coater, or a gravure printing, screen printing, flexographic printing,
Using a printing machine such as letterpress printing or offset printing, it is usually applied and formed on the support so that the dry weight is 2 to 30 g / m 2 .
【００２３】本発明の感圧接着性シートとして最も好ま
しいものは、上質紙或いは含浸紙或いは合成紙の表面
に中空粒子層と接着剤層を順次積層したもの、上質紙
或いは含浸紙或いは合成紙の表面に顔料コート層を設
け、又その裏面に中空粒子層と接着剤層を順次積層した
もの、上質紙或いは含浸紙或いは合成紙の表面に中空
粒子層と顔料コート層を順次積層し、又その裏面に接着
剤層を設けたものである。The most preferable pressure-sensitive adhesive sheet of the present invention is a high-quality paper or impregnated paper or synthetic paper in which a hollow particle layer and an adhesive layer are sequentially laminated, or high-quality paper or impregnated paper or synthetic paper. A pigment coating layer is provided on the surface, and a hollow particle layer and an adhesive layer are sequentially laminated on the back surface thereof. A hollow particle layer and a pigment coating layer are sequentially laminated on the surface of high-quality paper or impregnated paper or synthetic paper, or An adhesive layer is provided on the back surface.
【００２４】この感圧接着性シートは、更に必要に応じ
てシートの表面及び／又は裏面への印刷（一般情報の印
刷，地紋印刷），ミシン目とマージナルと打ち抜き等の
加工を適宜選択して施されてラベルとした後に、通常Ｚ
折り或いは巻取りにされる。This pressure-sensitive adhesive sheet is further appropriately selected by printing on the front surface and / or the back surface of the sheet (printing of general information, tint block printing), perforation, marginal and punching. After the label is applied, it is usually Z
It is folded or rolled up.
【００２５】本発明に用いられる葉書用シートとしては
通常上質紙が用いられるが、他に合成紙、含浸紙、ラミ
ネート紙、金属蒸着紙、印刷用塗工紙（微塗工紙，コー
ト紙，アート紙，キャストコート等）、記録用塗工紙
（感熱記録紙，感圧複写紙，静電記録紙，熱転写記録用
受像紙，印画紙，インキジェット記録紙等）等を用いる
こともできる。尚、これらに用いる紙の抄紙方法は特に
限定されず、勿論古紙再生パルプを含んでいても構わな
い。As the postcard sheet used in the present invention, high-quality paper is usually used. In addition, synthetic paper, impregnated paper, laminated paper, metal vapor-deposited paper, coated paper for printing (slightly coated paper, coated paper, Art paper, cast coat, etc.), recording coated paper (heat-sensitive recording paper, pressure-sensitive copying paper, electrostatic recording paper, thermal transfer recording image-receiving paper, printing paper, ink jet recording paper, etc.) can also be used. The paper making method used for these is not particularly limited, and it may of course contain recycled pulp of used paper.
【００２６】この葉書用シートは、必要に応じて宛先
欄、金額欄、宣伝等の下地印刷、剥離安定化インキの印
刷、ミシン目とマージナル等の加工が適宜選択して施さ
れ、通常Ｚ折り或いは巻取りにされる。続いて、ライン
プリンター等の記録装置にかけられ個人情報が記録され
る。This postcard sheet is appropriately subjected to a base printing such as an address column, an amount column, advertisement and the like, printing of a peeling stabilizing ink, processing such as perforation and marginal, as required, and is usually Z-folded. Or it is rolled up. Subsequently, the personal information is recorded on a recording device such as a line printer.
【００２７】続いて、該葉書用シートと上記ラベル用シ
ートは、葉書用シートの記録面とラベル用シートの接着
剤面を重ねながら加圧シール装置内に誘導され処理され
る。加圧シール装置としては、通常マージナル穴でシー
トを誘導するタイプで、シートのスリット、カット、折
り及び加圧等の処理を行うことができる箇所を適宜具備
した機械が用いられる。尚、葉書用シート及びラベル用
シートは、必ずしも連続シートとして扱われるものに限
定されず、枚葉のシートとして扱うことも可能である。Subsequently, the postcard sheet and the label sheet are guided and processed in the pressure sealing device while the recording surface of the postcard sheet and the adhesive surface of the label sheet are overlapped. As the pressure-sealing device, a machine that is usually of a type that guides a sheet through a marginal hole, and is equipped with a machine capable of appropriately performing processing such as slitting, cutting, folding and pressing the sheet is used. Note that the postcard sheet and the label sheet are not necessarily limited to those handled as continuous sheets, and may be handled as individual sheets.
【００２８】加圧処理は、通常加圧ロールを用いて５０
〜１０００kg／cm2 の圧力下で行われる。その際、シー
トを予め３０〜６０℃に加温すると接着力が安定するた
め加温装置を具備したものがより好ましい。The pressure treatment is usually performed by using a pressure roll.
It is carried out under a pressure of ˜1000 kg / cm 2 . In that case, if the sheet is preheated to 30 to 60 ° C., the adhesive force becomes stable, so that a sheet equipped with a heating device is more preferable.
【００２９】本発明の効果は、記録装置として湿式或い
は乾式の電子写真法を用いた場合に現れるものである
が、熱転写記録法、感熱記録法、静電記録法、電解記録
法、インパクト法、インキジェット法、銀塩写真法等の
装置で出力した葉書にも、本発明のラベル用シートを用
いることができる。The effects of the present invention appear when a wet or dry electrophotographic method is used as a recording apparatus, but the thermal transfer recording method, thermal recording method, electrostatic recording method, electrolytic recording method, impact method, The label sheet of the present invention can also be used for postcards output by devices such as the ink jet method and the silver salt photography method.
【００３０】[0030]
【実施例】以下、本発明の実施例を記載するが、本発明
がこれらの実施例のみに限定されないことは勿論であ
る。尚、実施例の中で特に断らない限り部とあるのは重
量部、％とあるのは重量％を意味する。EXAMPLES Examples of the present invention will be described below, but it goes without saying that the present invention is not limited to these examples. In the examples, "parts" means "parts by weight" and "%" means "% by weight" unless otherwise specified.
【００３１】実施例１ 「中空粒子層を設けたシートの作成」アクリル酸エステ
ル系エマルジョン（ＡＥ−３３７，日本合成ゴム社製）
７０重量部（乾燥重量）と中空粒子（商品名：エクスパ
ンセルＷＵ−６４２、エクスパンセル社製）１０重量部
（乾燥重量）と水酸化アルミニウム（商品名：Ｈ−４
２、昭和電工製）２０重量部と微量の助剤（分散剤，泡
消剤，増粘剤）を混合して固形分濃度を３０％に調整し
て得た塗液を、８０ｇ／ｍ2 の上質紙の片面に乾燥重量
が２０ｇ／ｍ2 となるようにエアーナイフコーターで塗
抹し、１５０℃のオーブンで発泡させて中空粒子層を設
けたシートを得た。Example 1 "Preparation of Sheet Having Hollow Particle Layer" Acrylic ester emulsion (AE-337, manufactured by Japan Synthetic Rubber Co., Ltd.)
70 parts by weight (dry weight) and hollow particles (trade name: Expancel WU-642, manufactured by Expancel) 10 parts by weight (dry weight) and aluminum hydroxide (trade name: H-4)
80 g / m 2 of a coating liquid obtained by mixing 20 parts by weight of Showa Denko) and a small amount of an auxiliary agent (dispersant, defoaming agent, thickener) to adjust the solid content concentration to 30%. A sheet having a hollow particle layer was obtained by smearing one surface of the wood free paper with an air knife coater so that the dry weight was 20 g / m 2 and foaming in an oven at 150 ° C.
【００３２】「ラベル用連続シートの作成」アクリル酸
エステル系エマルジョン（商品名：AE-923、日本合成ゴ
ム製) １００重量部（乾燥重量）とステアリン酸亜鉛
（ハイドリンＺ−７，中京油脂社製）５０重量部（乾燥
重量）とパルプパウダー（アボセルＢＥ６００／３０，
リッテンマイヤー製）５０重量部と微量の助剤（分散
剤，泡消剤，増粘剤）を混合して固形分濃度を３０％に
調整して得た接着剤塗液を、上記シートの中空粒子層上
に乾燥重量が９ｇ／ｍ2 となるようにエアーナイフコー
ターで全面塗抹して感圧接着性シートを得た。[Preparation of continuous sheet for label] 100 parts by weight (dry weight) of acrylic acid ester emulsion (trade name: AE-923, made by Japan Synthetic Rubber) and zinc stearate (Hydrin Z-7, made by Chukyo Yushi-Seiyaku Co., Ltd.) ) 50 parts by weight (dry weight) and pulp powder (Avocell BE600 / 30,
An adhesive coating solution obtained by mixing 50 parts by weight of Rittenmeyer) with a small amount of an auxiliary agent (dispersant, defoaming agent, thickener) to adjust the solid content concentration to 30% is used. The entire surface of the hollow particle layer was smeared with an air knife coater so that the dry weight was 9 g / m 2 , to obtain a pressure-sensitive adhesive sheet.
【００３３】続いて、シートの両面に下地印刷した後に
ミシン目とマージナルを入れてラベル用連続シート（図
２のシートをＺ折りしたもの）を得た。Subsequently, a base sheet was printed on both sides of the sheet, and then perforations and margins were inserted to obtain a continuous label sheet (a sheet of FIG. 2 folded in Z).
【００３４】「葉書用連続シートの作成」１４５ｇ／ｍ
2 の上質紙の表裏面に下地印刷し、続いてミシン目とマ
ージナルを入れ、更に電子写真方式のラインプリンター
で住所、氏名、データ等の個人情報を出力して葉書用連
続シート（図１のシートをＺ折りしたもの）を得た。"Creating a continuous sheet for postcards" 145 g / m
2 Underprint on the front and back of high-quality paper, then insert perforations and marginals, and further output personal information such as address, name, data, etc. with an electrophotographic line printer and print a continuous sheet for postcards (see Figure 1 The sheet was Z-folded).
【００３５】「再剥離性感圧接着葉書の作成」葉書用連
続シートのデータを印字した上に上記ラベル用連続シー
トを図３の如く重合わせながら加圧シール装置内に導入
した後、先ず予備接着し、続いてマージナルとミシン目
を切断し、更に５００kg／cm2 の圧力で加圧して再剥離
性感圧接着葉書（図４及び図５）を得た。 〔評価〕ラベルの剥がされた箇所の葉書上の文字を観察
したところ、トナーの脱落は殆ど認められなかった。"Preparation of Removable Pressure-Sensitive Adhesive Postcard" After printing the data of the continuous sheet for postcards and introducing the continuous sheet for labels as shown in FIG. Then, the marginal and perforated lines were cut, and further pressed at a pressure of 500 kg / cm 2 to obtain a removable pressure-sensitive adhesive postcard (FIGS. 4 and 5). [Evaluation] When the letters on the postcard were observed where the label was peeled off, almost no toner was removed.
【００３６】実施例２ 「顔料コート層を設けたシートの作成」スチレン−ブタ
ジエン系エマルジョン（Ｔ−０３８，日本合成ゴム社
製）１０重量部（乾燥重量）と糊化澱粉５重量部とカオ
リン（商品名：ＵＷ−９０，エンゲルハルト・ミネラル
社製）５０重量部（乾燥重量）と水酸化アルミニウム
（商品名：Ｈ−４２、昭和電工製）５０重量部と微量の
助剤（分散剤，泡消剤，増粘剤）を混合して固形分濃度
を３０％に調整して得た塗液を、８０ｇ／ｍ2 の上質紙
の片面に乾燥重量が２０ｇ／ｍ2 となるようにエアーナ
イフコーターで塗抹した後に、スーパーキャレンダー掛
けして顔料コート層を設けたシートを得た。 「ラベル用連続シートの作成」実施例１と同様にして得
た中空粒子塗料を、上記シートの原紙面に乾燥重量が２
０ｇ／ｍ2 となるようにエアーナイフコーターで塗抹
し、１５０℃のオーブンで発泡させて中空粒子層を設け
たシートを得た。Example 2 "Preparation of Sheet Having Pigment Coat Layer" Styrene-butadiene emulsion (T-038, manufactured by Nippon Synthetic Rubber Co., Ltd.) 10 parts by weight (dry weight), gelatinized starch 5 parts by weight and kaolin ( Product name: UW-90, Engelhard Mineral Co., Ltd. 50 parts by weight (dry weight) and aluminum hydroxide (Product name: H-42, Showa Denko) 50 parts by weight and a small amount of auxiliary agent (dispersant, foam) A coating solution obtained by adjusting the solid content concentration to 30% by mixing an eraser and a thickener) with an air knife so that the dry weight becomes 20 g / m 2 on one side of 80 g / m 2 of fine paper. After smearing with a coater, it was supercalendered to obtain a sheet having a pigment coat layer. "Preparation of continuous sheet for label" The hollow particle coating material obtained in the same manner as in Example 1 was applied to the base paper surface of the above-mentioned sheet in a dry weight of 2
The sheet was smeared with an air knife coater so as to have a weight of 0 g / m 2 and foamed in an oven at 150 ° C. to obtain a sheet having a hollow particle layer.
【００３７】続いて、実施例１と同様にして得た接着剤
塗液を、上記シートの中空粒子層上に乾燥重量が９ｇ／
ｍ2 となるようにエアーナイフコーターで全面塗抹して
感圧接着性シートを得た。続いて、シートの両面に下地
印刷した後にミシン目とマージナルを入れてラベル用連
続シート（図２のシートをＺ折りしたもの）を得た。Subsequently, the adhesive coating solution obtained in the same manner as in Example 1 was dried on the hollow particle layer of the above sheet to give a dry weight of 9 g /
The entire surface was smeared with an air knife coater to obtain m 2 to obtain a pressure-sensitive adhesive sheet. Then, a base sheet was printed on both sides of the sheet, and then perforations and margins were added to obtain a continuous label sheet (a sheet of FIG. 2 folded in Z).
【００３８】「再剥離性感圧接着葉書の作成」実施例１
と同様にして得た葉書用連続シート上に上記ラベル用連
続シートを図３の如く重合わせながら加圧シール装置内
に導入した後、先ず予備接着し、続いてマージナルとミ
シン目を切断し、更に５００kg／cm2 の圧力で加圧して
再剥離性感圧接着葉書（図４及び図６）を得た。 〔評価〕ラベルの剥がされた箇所の葉書上の文字を観察
したところ、トナーの脱落は殆ど認められなかった。[Preparation of Removable Pressure-sensitive Adhesive Postcard] Example 1
After introducing the above label continuous sheet onto the postcard continuous sheet obtained in the same manner as above in the pressure sealing device while superposing as shown in FIG. 3, first prebonding is performed, and then marginal and perforation are cut, The pressure was further applied at a pressure of 500 kg / cm 2 to obtain a removable pressure-sensitive adhesive postcard (FIGS. 4 and 6). [Evaluation] When the letters on the postcard were observed where the label was peeled off, almost no toner was removed.
【００３９】実施例３ 「ラベル用連続シートの作成」実施例１と同様にして得
た中空粒子層を設けたシートの中空粒子層上に、実施例
１と同様にして得た顔料コート層用塗料を乾燥重量が２
０ｇ／ｍ2 となるようにエアーナイフコーターで塗抹し
た後に、スーパーキャレンダー掛けした。Example 3 "Preparation of continuous label sheet" For the pigment coat layer obtained in the same manner as in Example 1 on the hollow particle layer of the sheet provided with the hollow particle layer obtained in the same manner as in Example 1 Dry weight of paint is 2
After smearing with an air knife coater so as to be 0 g / m 2 , it was supercalendered.
【００４０】続いて、実施例１と同様にして得た接着剤
塗液を、上記シートの原紙面に乾燥重量が９ｇ／ｍ2 と
なるようにエアーナイフコーターで全面塗抹して感圧接
着性シートを得た。続いて、シートの両面に下地印刷し
た後にミシン目とマージナルを入れてラベル用連続シー
ト（図２のシートをＺ折りしたもの）を得た。Subsequently, the adhesive coating solution obtained in the same manner as in Example 1 was coated on the entire surface of the above-mentioned sheet with an air knife coater so that the dry weight was 9 g / m 2, and the pressure-sensitive adhesive property was obtained. Got the sheet. Then, a base sheet was printed on both sides of the sheet, and then perforations and margins were added to obtain a continuous label sheet (a sheet of FIG. 2 folded in Z).
【００４１】「再剥離性感圧接着葉書の作成」実施例１
と同様にして得た葉書用連続シート上に上記ラベル用連
続シートを図３の如く重合わせながら加圧シール装置内
に導入した後、先ず予備接着し、続いてマージナルとミ
シン目を切断し、更に５００kg／cm2 の圧力で加圧して
再剥離性感圧接着葉書（図４及び図７）を得た。 〔評価〕ラベルの剥がされた箇所の葉書上の文字を観察
したところ、トナーの脱落は殆ど認められなかった。た
だし、実施例１及び２よりやや劣っていた。"Preparation of Removable Pressure-sensitive Adhesive Postcard" Example 1
After introducing the above label continuous sheet onto the postcard continuous sheet obtained in the same manner as above in the pressure sealing device while superposing as shown in FIG. 3, first prebonding is performed, and then marginal and perforation are cut, The pressure was further applied at a pressure of 500 kg / cm 2 to obtain a removable pressure-sensitive adhesive postcard (FIGS. 4 and 7). [Evaluation] When the letters on the postcard were observed where the label was peeled off, almost no toner was removed. However, it was slightly inferior to Examples 1 and 2.
【００４２】比較例１ 「ラベル用連続シートの作成」中空粒子層を設けなかっ
た以外は、実施例１と同様にして感圧接着性シートを得
た。続いて、シートの両面に下地印刷した後にミシン目
とマージナルを入れてラベル用連続シート（図２のシー
トをＺ折りしたもの）を得た。Comparative Example 1 "Preparation of continuous label sheet" A pressure-sensitive adhesive sheet was obtained in the same manner as in Example 1 except that the hollow particle layer was not provided. Then, a base sheet was printed on both sides of the sheet, and then perforations and margins were added to obtain a continuous label sheet (a sheet of FIG. 2 folded in Z).
【００４３】「再剥離性感圧接着葉書の作成」実施例１
と同様にして得た葉書用連続シート上に上記ラベル用連
続シートを図３の如く重合わせながら加圧シール装置内
に導入した後、先ず予備接着し、続いてマージナルとミ
シン目を切断し、更に５００kg／cm2 の圧力で加圧して
再剥離性感圧接着葉書（図４及び図８）を得た。 〔評価〕ラベルの剥がされた箇所の葉書上の文字を観察
したところ、トナーの脱落が激しく、情報の判読ができ
なかった。[Preparation of Removable Pressure-sensitive Adhesive Postcard] Example 1
After introducing the above label continuous sheet onto the postcard continuous sheet obtained in the same manner as above in the pressure sealing device while superposing as shown in FIG. 3, first prebonding is performed, and then marginal and perforation are cut, The pressure was further applied at a pressure of 500 kg / cm 2 to obtain a removable pressure-sensitive adhesive postcard (FIGS. 4 and 8). [Evaluation] When the letters on the postcard where the label was peeled off were observed, the toner fell off so much that the information could not be read.
【００４４】[0044]
【発明の効果】このように、本発明の再剥離性感圧接着
葉書は、剥離後における情報の判読性が極めて優れたも
のである。As described above, the removable pressure-sensitive adhesive postcard of the present invention has extremely excellent readability of information after peeling.
【図１】非接着性の葉書用連続シートの一例を示す平面
図である。FIG. 1 is a plan view showing an example of a non-adhesive continuous sheet for postcards.
【図２】感圧接着性シートであるラベル用連続シートの
一例を示す平面図である。FIG. 2 is a plan view showing an example of a label continuous sheet which is a pressure-sensitive adhesive sheet.
【図３】図１の葉書用シート上に、図２のラベル用シー
トを重ねた状態を示したものである。3 shows a state in which the label sheet of FIG. 2 is superposed on the postcard sheet of FIG.
【図４】本発明の再剥離性感圧接着葉書の一例で、図３
の重ねたシートを汎用の加圧シール装置内に誘導し、マ
ージナルとミシン目の切断を行った後に加圧処理して得
られる。FIG. 4 is an example of a removable pressure-sensitive adhesive postcard of the present invention.
It is obtained by guiding the stacked sheets of (1) into a general-purpose pressure sealing device, cutting marginal and perforated lines, and then applying pressure.
【図５】図４の再剥離性感圧接着葉書のＡ−Ａ線におけ
る断面図である。5 is a cross-sectional view taken along the line AA of the removable pressure-sensitive adhesive postcard of FIG.
【図６】本発明の別の態様を示す断面図である。FIG. 6 is a sectional view showing another embodiment of the present invention.
【図７】本発明の別の態様を示す断面図である。FIG. 7 is a sectional view showing another embodiment of the present invention.
【図８】従来の再剥離性感圧接着葉書の断面図である。FIG. 8 is a cross-sectional view of a conventional removable pressure-sensitive adhesive postcard.
１：葉書用連続シート ２：ミシン目 ３：マージナル穴 ４：個人情報（住所・氏名） ５：個人情報（データ） ６：ラベル用連続シート ７：再剥離性感圧接着葉書 ８：葉書 ９：ラベル １０：上質紙（含浸紙、合成紙） １１：中空粒子層 １２：接着剤層 １３：顔料コート層 1: Continuous sheet for postcards 2: Perforation 3: Marginal hole 4: Personal information (address / name) 5: Personal information (data) 6: Continuous sheet for labels 7: Removable pressure-sensitive adhesive postcard 8: Postcard 9: Label 10: Fine paper (impregnated paper, synthetic paper) 11: Hollow particle layer 12: Adhesive layer 13: Pigment coat layer
Claims (2)
感圧接着性シートを、非接着性葉書用シート上に強圧下
で接合して得られる再剥離性感圧接着葉書において、該
感圧接着性シートの支持体が、中空粒子層を有する基材
からなることを特徴とする再剥離性感圧接着葉書。1. A repeelable pressure-sensitive adhesive postcard obtained by bonding a pressure-sensitive adhesive sheet for labels, which comprises an adhesive layer on a support, onto a non-adhesive postcard sheet under high pressure. A removable pressure-sensitive adhesive postcard, wherein the support of the pressure-sensitive adhesive sheet is composed of a base material having a hollow particle layer.
る請求項１記載の再剥離性感圧接着葉書。2. The removable pressure-sensitive adhesive postcard according to claim 1, wherein the hollow particles are expandable microcapsules.