JPH0622758Y2 - Base material for lightweight floor impact noise improvement - Google Patents
Base material for lightweight floor impact noise improvementInfo
- Publication number
- JPH0622758Y2 JPH0622758Y2 JP7227788U JP7227788U JPH0622758Y2 JP H0622758 Y2 JPH0622758 Y2 JP H0622758Y2 JP 7227788 U JP7227788 U JP 7227788U JP 7227788 U JP7227788 U JP 7227788U JP H0622758 Y2 JPH0622758 Y2 JP H0622758Y2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- base material
- floor impact
- lightweight floor
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】 〔技術分野〕 本考案は、軽量床において衝撃に伴って発生する音をで
きるだけ小さくするための下地材に関する。[Technical Field] The present invention relates to a base material for reducing noise generated by impact on a lightweight floor as much as possible.
従来、軽量床において、衝撃に伴って発生する音を小さ
くするための下地材としては、発泡ポリエチレン、発泡
ポリウレタン、発泡ゴムなどの発泡体シートが使用され
ていた。Conventionally, in a lightweight floor, a foam sheet such as foamed polyethylene, foamed polyurethane, or foamed rubber has been used as a base material for reducing the sound generated due to impact.
しかしながら、これら発泡シートのみでは、衝撃音を防
止するのに有効な厚みにすると、局部凹みが大きくなる
のに加えて、人に揺動感を与え、居住性を害する面があ
った。However, with these foamed sheets alone, when the thickness is effective to prevent impact noise, there is a problem that the local dent becomes large, and in addition, it gives a feeling of rocking to a person and impairs comfortability.
そこで、本考案者は鋭意研究を重ねた結果、ゴムを結合
剤としたパーム材よりなる弾力層１の上に支持体層２、
表面硬度（ショアーＤ）20〜50、厚さ0.5〜３mmの物体
が衝突した時の衝撃音の発生を防止できる層（発音防止
層）３および繊維質シート層５を順次積層した下地材を
使用することにより、従来の課題を一挙に解決すること
に成功したものである。Therefore, as a result of earnest studies by the present inventor, as a result of the research, the support layer 2, on the elastic layer 1 made of palm material with rubber as a binder,
Uses a base material in which a layer (pronunciation layer) 3 and a fibrous sheet layer 5 are sequentially laminated to prevent the generation of impulsive sound when an object having a surface hardness (Shore D) of 20 to 50 and a thickness of 0.5 to 3 mm collides. By doing so, it has succeeded in solving the conventional problems all at once.
弾力層は、パーム材を通常ゴムラテックスを用いて成形
し、厚さ約４〜12mm、重量約600〜1500ｇ／ｍ２に仕上
げたものを使用する。とくに、椰子の実繊維を巻縮加工
し、弾性接着剤をスプレーして固めたクッション材とし
て市販されているパームロックにゴムラテックスを含浸
して弾性を補強したものが好ましい結果を与える。For the elastic layer, a palm material is usually formed by using rubber latex, and is finished to have a thickness of about 4 to 12 mm and a weight of about 600 to 1500 g / m 2 . In particular, a palm-lock commercially available as a cushioning material obtained by crimping coconut fiber and spraying an elastic adhesive to solidify it and impregnating it with rubber latex gives a preferable result.
ゴムを結合剤としたパーム材は他の二層との結合によ
り、ほどよい弾力を与えて衝撃を吸収し、かつ安定感の
ある居住性を示す。The palm material, which uses rubber as a binder, gives a moderate elasticity by absorbing the impact by combining with the other two layers, and shows a stable habitability.
支持体層は、ベニヤ板、ハードボード、繊維板〔繊維板
としてはとくに中密度（ｄ＝0.5〜0.8）繊維板が好まし
い〕、無機質板、金属板などが使用でき、通常、厚みは
約2.0〜5.5mmのものが使用される。The support layer may be a plywood board, a hard board, a fiber board [particularly preferable as a fiber board is a medium density (d = 0.5 to 0.8) fiber board], an inorganic board, a metal board, or the like, and usually has a thickness of about 2.0 to 5.5mm is used.
発音防止層としては、表面硬度（ショアーＤ硬度）20〜
50、とくに30〜40、厚さ0.5〜３mm、とくに1.0〜2.0の
発泡合成樹脂シートを使用するが、これらは単層であっ
ても、複数層であってもよく、裏面に繊維層、又は非発
泡タイプの合成樹脂、ゴムなどのシートを裏打ちするこ
ともできる。発泡体の発泡倍率は３〜20倍とくに、５倍
程度が好ましい。いずれにせよ、発泡体の表面硬度（シ
ョアーＤ硬度）を測定したとき、その値が20〜50のもの
を選択することが必要である。これが小さすぎると局部
凹みを発生したり、居住性を劣化させ、又、大きすぎる
と発音防止層としての役目をはたさなくなる。発泡体を
構成する材料としてはとくに制限はないが、架橋ポリエ
チレン、ポリウレタン、ポリ塩化ビニルなどがあげられ
る。Surface hardness (Shore D hardness) of 20-
A foamed synthetic resin sheet having a thickness of 50, particularly 30 to 40, and a thickness of 0.5 to 3 mm, and particularly 1.0 to 2.0 is used, but these may be a single layer or a plurality of layers, a fiber layer on the back surface, or It is also possible to line a sheet of non-foaming type synthetic resin, rubber or the like. The expansion ratio of the foam is preferably 3 to 20 times, especially about 5 times. In any case, when the surface hardness (Shore D hardness) of the foam is measured, it is necessary to select one having a value of 20 to 50. If it is too small, a local dent is generated or the comfortability is deteriorated, and if it is too large, it does not serve as a sound-preventing layer. The material constituting the foam is not particularly limited, but examples thereof include crosslinked polyethylene, polyurethane, polyvinyl chloride and the like.
繊維質シート層としては、天然、合成繊維あるいはガラ
ス繊維のような鉱物繊維の不織布、ネット、織布およ
び、その樹脂含浸シート、あるいはこれらの繊維材料と
樹脂よりなる組成物のシート状物などを挙げることがで
きる。As the fibrous sheet layer, a nonwoven fabric of natural, synthetic fibers or mineral fibers such as glass fibers, a net, a woven fabric, and a resin-impregnated sheet thereof, or a sheet-like material of a composition composed of these fiber materials and a resin, etc. Can be mentioned.
この繊維質シート層の使用により、軽衝撃テストのさい
の高音領域の防音特性を一層向上することができると共
に、施工時あるいは表面仕上材のはりかえのさい、発音
防止層が傷付くのを防止することができる。By using this fibrous sheet layer, it is possible to further improve the soundproofing characteristics in the high-pitched sound area during a light impact test, and also to prevent the soundproof layer from being damaged during construction or when the surface finishing material is replaced. be able to.
本考案の下地材の上に施工される表面仕上材としてはポ
リ塩化ビニルなどの合成樹脂系タイル、クッションフロ
ア、リノリウムシート、ポリ塩化ビニルのような合成樹
脂シート、コルク、木材板などの軽量床仕上材である。Synthetic resin tiles such as polyvinyl chloride, cushion floors, linoleum sheets, synthetic resin sheets such as polyvinyl chloride, lightweight floors such as cork, wood boards, etc. as the surface finishing material to be applied on the base material of the present invention. It is a finishing material.
実施例 パーム繊維とゴムとの割合が６：４になるように天然ゴ
ムラテックスを用いてパーム繊維を板状に成形して得ら
れた厚さ６mmのパーム材１の上にゴム系接着材を用いて
厚さ３mmの合板２を、その上にウレタン系接着材を用い
て、表面硬度40、発泡倍率５倍の厚さ1.1mmのポリ塩化
ビニル製発泡体シート３を、さらにその上に厚さ0.4mm
ガラス繊維不織布４（35ｇ／ｍ２）を積層し、下地材を
得た。Example A rubber-based adhesive was formed on a palm material 1 having a thickness of 6 mm obtained by molding palm fiber into a plate shape using natural rubber latex so that the ratio of palm fiber to rubber was 6: 4. Using plywood 2 with a thickness of 3 mm, urethane adhesive is used on it, and a polyvinyl chloride foam sheet 3 with a surface hardness of 40 and a foaming ratio of 5 times and a thickness of 1.1 mm is further applied. 0.4 mm
A glass fiber non-woven fabric 4 (35 g / m 2 ) was laminated to obtain a base material.
JIS-A-1418の「建築物の現場における床衝撃音レベルの
測定方法」に従い、この下地材をコンクリート床面（床
下地５）に両面接着テープで固着し、下地材の上には木
質化粧板（厚さ3.5mm）（化粧板６）を貼り、テストを
行った。In accordance with JIS-A-1418 "Measurement of floor impact sound level at construction site", this base material is fixed to the concrete floor surface (floor base 5) with a double-sided adhesive tape, and a wooden makeup is applied on the base material. A plate (thickness: 3.5 mm) (decorative plate 6) was attached and tested.
テスト結果、 打撃点：３点 階下受音点：５点 床衝撃音レベル改善量(dB)：表のとおり、 〔考案の効果〕 本考案下地材は、四つの特定層の積層により、比較的薄
い構成にもかかわらず、Ｌ−55という驚くべきレベルの
防音効果が達成され、しかも、局部凹みや揺動感のない
すぐれた居住性を与えることに成功したものである。Test results, impact point: 3 points Downstairs sound receiving point: 5 points Floor impact sound level improvement (dB): As shown in the table, [Effect of the Invention] The base material of the present invention achieves a surprising level of soundproofing effect of L-55 due to the lamination of the four specific layers and has a relatively thin structure. It has succeeded in providing excellent habitability.
又、繊維質シート層の使用により繊維質シート層を使用
しない本出願人の特願昭62−285273号（特開平１−1277
60号）の発明に較べて下地材の表面が保護された状態に
あり、施工および表面仕上材の貼りかえのさい、下地材
を傷付けることがなく、あわせて、寸法安定性を向上す
るとともに音を分散させる効果を発揮する。Further, the use of the fibrous sheet layer does not use the fibrous sheet layer.
Compared with the invention of No. 60), the surface of the base material is protected, and the base material is not damaged during construction and when the surface finish material is replaced, and at the same time, the dimensional stability is improved and the sound is reduced. Exerts the effect of dispersing.
第１図は、本考案の下地材の層構成を示す断面図、第２
図は、本考案の下地材を施工した場合の例を示す断面図
である。 １……弾力層、２……支持体層 ３……発音防止層、４……繊維質シート層 ５……床下地、６……化粧板FIG. 1 is a sectional view showing a layer structure of a base material of the present invention, and FIG.
The figure is a cross-sectional view showing an example in which the base material of the present invention is applied. 1 ... Resilient layer, 2 ... Support layer, 3 ... Soundproof layer, 4 ... Fibrous sheet layer, 5 ... Floor base, 6 ... Decorative plate
Claims (1)
層、支持体層、表面硬度（ショアーＤ硬度）20〜50、厚
さ0.5〜３mmの物体が衝突した時の衝撃音の発生を防止
できる層（発音防止層）および繊維質シート層が順次積
層されていることを特徴とする軽量床衝撃音改善用下地
材。1. An impact sound is generated when an elastic layer made of palm material using a rubber as a binder, a support layer, an object having a surface hardness (Shore D hardness) of 20 to 50 and a thickness of 0.5 to 3 mm collides. A lightweight floor impact sound improving base material, in which a preventable layer (prohibition layer) and a fibrous sheet layer are sequentially laminated.