JPH0617213A - Method and device for preventing vibration of hot-dipping equipment - Google Patents
Method and device for preventing vibration of hot-dipping equipmentInfo
- Publication number
- JPH0617213A JPH0617213A JP4199289A JP19928992A JPH0617213A JP H0617213 A JPH0617213 A JP H0617213A JP 4199289 A JP4199289 A JP 4199289A JP 19928992 A JP19928992 A JP 19928992A JP H0617213 A JPH0617213 A JP H0617213A
- Authority
- JP
- Japan
- Prior art keywords
- vibration
- steel strip
- roll
- plating bath
- plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、溶融金属めっき設備に
おいて、めっき浴中ロールの振動を抑える振動防止方法
および装置に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a vibration preventing method and apparatus for suppressing vibration of a roll in a plating bath in a molten metal plating facility.
【０００２】[0002]
【従来の技術】近年、自動車用鋼板や土木、建築用ある
いは家電用鋼板として、耐食性に優れた表面処理鋼板の
需要が急増している。これらの表面処理鋼板の製造法と
しては、溶融亜鉛めっき法や溶融アルミニウムめっき法
が多用されている。2. Description of the Related Art In recent years, there has been a rapid increase in demand for surface-treated steel sheets having excellent corrosion resistance as steel sheets for automobiles, civil engineering, construction and home appliances. As a method for producing these surface-treated steel sheets, a hot dip galvanizing method and a hot dip aluminum coating method are often used.
【０００３】図１は連続溶融亜鉛めっき設備の概略構成
図である。鋼帯１は、連続炉にて機械的性質や温度を調
節された後、スナウト２を介してめっきポット３内のめ
っき浴４中に進入する。めっき浴４中に進入した鋼帯１
は、めっき浴４中に浸漬配置された非駆動のシンクロー
ル５により方向を変えられ、同じくめっき浴４中に浸漬
配置されたサポートロール６を経由してめっき浴４から
引き上げられる。めっき浴４から引き上げられた鋼帯１
は、ワイピングノズル７によりめっき金属の付着量を調
整された後、トッブロール８を通過して常温にまで冷却
される。FIG. 1 is a schematic configuration diagram of a continuous hot-dip galvanizing facility. The steel strip 1 is adjusted in its mechanical properties and temperature in a continuous furnace, and then enters the plating bath 4 in the plating pot 3 via the snout 2. Steel strip 1 that entered the plating bath 4
Is changed in direction by a non-driving sink roll 5 immersed in the plating bath 4 and pulled up from the plating bath 4 via a support roll 6 also immersed in the plating bath 4. Steel strip 1 pulled up from plating bath 4
After the amount of plated metal adhered is adjusted by the wiping nozzle 7, it passes through the tob roll 8 and is cooled to room temperature.
【０００４】ここで、めっき浴４中に浸漬配置されため
っき浴中ロールの機能は、シンクロール５について前述
したとおり鋼帯１の方向転換にある。一方、サポートロ
ール６は非駆動のシンクロール５と異なり、めっき浴４
外から駆動シャフト等により強制駆動されるのが一般的
であり、その機能は内側のスタビライジングロール６ａ
についてはワイピング時のパイスラインの確保および安
定化、外側のコレクティングロール６ｂについては主に
鋼帯１の板反り修正とされている。更に、これらのサポ
ートロール６は、鋼帯押し込み量の調節により鋼帯表面
に付着したドロス等の異物の掻き落としも行う。Here, the function of the in-plating bath roll immersed in the plating bath 4 is to change the direction of the steel strip 1 as described above for the sink roll 5. On the other hand, the support roll 6 is different from the non-driven sink roll 5 in that the plating bath 4
Generally, it is forcibly driven from the outside by a drive shaft or the like, and its function is the stabilizing roll 6a on the inside.
For the above, the pie line is secured and stabilized during wiping, and the outer collecting roll 6b is mainly used for correcting the warp of the steel strip 1. Further, these support rolls 6 also scrape off foreign matter such as dross attached to the surface of the steel strip by adjusting the pushing amount of the steel strip.
【０００５】しかしながら、めっき浴中に配設されたこ
れらの浴中ロールは、その使用環境上、軸受にすべり軸
受等のある程度クリアランスのある軸受が採用されてい
ること、ロールを支持するフレームの剛性不足、更に、
サポートロールについては、めっき浴外から駆動される
ため、その駆動シャフトがめっき浴に対して、侵入角度
を持つことによる角速度の脈動が原因となって、激しい
振動を生じる。この振動のため、鋼帯表面に付着したド
ロス等の異物がこれらの浴中ロールとの間をすり抜け、
表面欠陥の原因となる。例えば、自動車の外装用鋼板に
おいては、プレス時にプレスブツと称する表面不均一部
分が生じ、塗装後の鋼板の鮮映性が害されるだけでな
く、その不均一部分に局部電池が形成され、耐食性の低
下も引き起こす。However, in these bath rolls arranged in the plating bath, a bearing having a certain clearance such as a sliding bearing is used as the bearing in view of the environment of use, and the rigidity of the frame supporting the roll is used. Shortage, and
Since the support roll is driven from outside the plating bath, violent vibration occurs due to the pulsation of the angular velocity due to the drive shaft having an entry angle with respect to the plating bath. Due to this vibration, foreign matter such as dross adhered to the surface of the steel strip slips between these rolls in the bath,
It causes surface defects. For example, in a steel sheet for exterior of automobiles, a non-uniform surface called a press spot is generated at the time of pressing, which not only impairs the sharpness of the coated steel sheet, but also forms a local battery in the non-uniform portion to prevent corrosion resistance. It also causes a decline.
【０００６】従来、溶融金属めっき設備における振動防
止については、浴中ロールの側から振動防止を図った事
例は殆どない。一方、めっき浴から引き上げられた鋼帯
の振動を抑えるために、めっき浴中のシンクロール上方
で鋼帯の表裏面にめっき浴を吹き付ける技術は特公昭６
３−５０４１８号公報に開示され、ワイピングノズルの
近傍で鋼帯の両側端部を支持する技術は、特開昭６２−
２３８３５７号公報に開示されている。With respect to vibration prevention in hot dip galvanizing equipment, there are almost no cases in which vibration is prevented from the roll side in the bath. On the other hand, in order to suppress the vibration of the steel strip pulled up from the plating bath, the technology of spraying the plating bath on the front and back surfaces of the steel strip above the sink roll in the plating bath is disclosed in JP-B-6.
A technique disclosed in Japanese Patent Laid-Open No. 3-50418 for supporting both end portions of a steel strip in the vicinity of a wiping nozzle is disclosed in Japanese Patent Laid-Open No. 62-
It is disclosed in Japanese Patent No. 238357.
【０００７】[0007]
【発明が解決しようとする課題】めっき浴から引き上げ
られた鋼帯の振動を抑えると、めっき金属の付着量は均
一化される。しかし、めっき浴中ロールの振動が放置さ
れたままでは、鋼帯表面に付着した異物のロールすり抜
けは防止されない。従って、鋼帯の振動を抑えるための
前記開示技術は、付着異物のロールすり抜けによる表面
欠陥の防止に対しては殆ど効力を示さない。When the vibration of the steel strip pulled up from the plating bath is suppressed, the amount of plating metal deposited is made uniform. However, if the vibration of the roll is left in the plating bath, the foreign matter attached to the surface of the steel strip cannot be prevented from slipping through the roll. Therefore, the above-mentioned disclosed technique for suppressing the vibration of the steel strip shows almost no effect in preventing the surface defect due to the slip-through of the adhered foreign matter.
【０００８】本発明の目的は、めっき浴中ロールの振動
を抑えて、付着異物のロールすり抜けによる表面欠陥の
発生を防ぐ溶融金属めっき設備における振動防止方法お
よび装置を提供することにある。It is an object of the present invention to provide a vibration preventing method and apparatus in a hot dip metal plating equipment which suppresses vibration of a roll in a plating bath and prevents surface defects due to slipping of adhering foreign matter on the roll.
【０００９】[0009]
【課題を解決するための手段】本発明者は、実操業上の
経験から、サポートロールの押し込み量の調節による鋼
帯支持力の調節や鋼帯進行速度の調節、即ちライン速度
の調節が、めっき浴中ロールの振動の抑制に有効なこと
を確認している。しかし、浴中ロールの振動は、前述し
たように種々の要因が複雑に関連して発生しており、鋼
帯支持力の調節やライン速度の調節を行うにしても、管
理指標がないため、その操作はオペレータの経験と勘に
頼らざるを得ず、オペレータの個人差によるばらつきが
大きいという問題がある。Means for Solving the Problems From the experience of actual operation, the inventor has found that the adjustment of the steel strip supporting force and the adjustment of the steel strip advancing speed by adjusting the pushing amount of the support roll, that is, the adjustment of the line speed, It has been confirmed that it is effective in suppressing roll vibration in the plating bath. However, as described above, the vibration of the roll in the bath is complicatedly related to various factors, and even if the steel strip supporting force and the line speed are adjusted, there is no control index, The operation has to rely on the experience and intuition of the operator, and there is a problem that there are large variations due to individual differences among operators.
【００１０】この問題を解決するため、本発明者らは、
鋼帯支持力の調節やライン速度の調節する際の管理指標
について様々な検討を行った結果、浴中ロールを支持す
るフレームに振動検出手段を設け、その検出値を管理指
標として、該検出値を小さくするよう鋼帯支持力および
／またはライン速度を調節すれば、付着異物のロールす
り抜けによる欠陥発生が安定して防止されることを知見
した。In order to solve this problem, the present inventors have
As a result of various studies on the control index when adjusting the steel strip supporting force and the line speed, a vibration detection means is provided on the frame that supports the roll in the bath, and the detected value is used as the control index. It has been found that by adjusting the steel strip supporting force and / or the line speed so as to reduce the value, it is possible to stably prevent the occurrence of defects caused by the adhered foreign matter passing through the roll.
【００１１】本発明の溶融金属めっき設備における振動
防止方法は、溶融金属めっきポット内のめっき浴中に浸
漬され、該めっき浴中を進行する鋼帯を案内支持するめ
っき浴中ロールの支持フレームに振動検出手段を設け、
該振動検出手段により検出されるフレーム振動を抑える
べくめっきポット内における鋼帯支持力および／または
鋼帯進行速度を調節することを特徴とする。The method for preventing vibration in the hot-dip galvanizing equipment of the present invention includes a support frame of a roll in a hot-dip bath which is immersed in a hot-dip plating bath in a hot-dip galvanizing pot and guides and supports a steel strip moving through the hot-dip plating bath. Providing vibration detection means,
In order to suppress the frame vibration detected by the vibration detecting means, the steel strip supporting force and / or the steel strip moving speed in the plating pot is adjusted.
【００１２】本発明の溶融金属めっき設備における振動
防止装置は、溶融金属めっきポット内のめっき浴中に浸
漬され、該めっき浴中を進行する鋼帯を案内支持するめ
っき浴中ロールの支持フレームに設けられた振動検出手
段と、該振動検出手段により検出された振動値を入力さ
れ、鋼帯支持力および／または鋼帯進行速度を調節する
調節機構に、前記振動値が所定値より小さくなるように
動作指令を出力する制御手段とを具備することを特徴と
する。The vibration preventive device in the molten metal plating equipment of the present invention is mounted on a support frame of a roll in a plating bath which is immersed in a plating bath in a molten metal plating pot and which guides and supports a steel strip traveling in the plating bath. The provided vibration detecting means and the adjusting mechanism for inputting the vibration value detected by the vibration detecting means and adjusting the steel strip supporting force and / or the traveling speed of the steel strip are set so that the vibration value becomes smaller than a predetermined value. And a control means for outputting an operation command.
【００１３】鋼帯支持力の調節は、サーポートロール、
特に表側のコレクティングロールの押し込み量の調節に
よって行うのが良い。なぜなら、２タビライングロール
は、前述のようにパスラインの確保・安定化が主目的で
あり、これを動かすとワイピングのパスが変化し、めっ
き付着量分布のばらつきを生じ好ましくないためであ
る。Adjustment of the steel strip supporting force is performed by a support roll,
Especially, it is preferable to adjust the pushing amount of the collecting roll on the front side. This is because, as described above, the main purpose of the 2 tabline roll is to secure / stabilize the pass line, and if this is moved, the wiping pass changes, which causes variations in the plating amount distribution, which is not preferable.
【００１４】[0014]
【作用】図２は特定の条件下でコレクティングロールの
押し込み量を変化させたときのフレームの振動速度の変
化を示すグラフである。この条件下では、コレクティン
グロールの押し込み量が３０ｍｍのときに振動速度が最
小となる。FIG. 2 is a graph showing changes in the vibration speed of the frame when the pushing amount of the collecting roll is changed under specific conditions. Under this condition, the vibration speed becomes minimum when the pushing amount of the collecting roll is 30 mm.
【００１５】図３は特定の条件下でライン速度を変化さ
せたときのフレームの振動速度の変化を示すグラフであ
る。ライン速度とフレーム振動はほぼ比例しており、ラ
イン速度を遅くすることによりフレーム振動を抑えるこ
とができる。FIG. 3 is a graph showing changes in the vibration speed of the frame when the line speed is changed under specific conditions. The line speed is substantially proportional to the frame vibration, and the frame vibration can be suppressed by reducing the line speed.
【００１６】従って、めっき浴ポット内における鋼帯支
持力および／または鋼帯進行速度の調節により、フレー
ム振動が抑制され、浴中ロールの振動に伴う付着異物の
ロールすり抜けが防止されることにより、表面欠陥の発
生が防止される。Therefore, by adjusting the steel strip supporting force and / or the steel strip moving speed in the plating bath pot, the frame vibration is suppressed and the adhered foreign matter is prevented from slipping through the roll due to the vibration of the roll in the bath. The occurrence of surface defects is prevented.
【００１７】本発明の振動防止方法においては、鋼帯支
持力および／または鋼帯進行速度を手動または自動で調
節することができる。In the vibration preventing method of the present invention, the steel strip supporting force and / or the steel strip moving speed can be adjusted manually or automatically.
【００１８】本発明の振動防止装置は、この調節を自動
で行ない、操業条件等が変更されてもフレーム振動を常
に表面欠陥の発生しないレベルに抑えることができる。The vibration preventing apparatus of the present invention automatically performs this adjustment, and can suppress the frame vibration to a level at which surface defects do not always occur even if the operating conditions are changed.
【００１９】具体的な操作としては、鋼帯進行速度の低
下は生産性等に直接影響を与えるので、先ずは鋼帯支持
力の調節によりフレーム振動を最小値まで抑え、これで
表面欠陥の発生を充分に防止できないときに鋼帯進行速
度を低下させるのが良い。これにより、ライン速度の低
下を可及的に抑えて、フレーム振動を抑制できる。As a concrete operation, since the reduction of the traveling speed of the steel strip directly affects the productivity and the like, first, the frame vibration is suppressed to the minimum value by adjusting the steel strip supporting force, so that the surface defects are generated. When it is not possible to sufficiently prevent this, it is better to reduce the traveling speed of the steel strip. As a result, it is possible to suppress a decrease in line speed as much as possible and suppress frame vibration.
【００２０】[0020]
【実施例】以下に本発明の実施例を説明する。EXAMPLES Examples of the present invention will be described below.
【００２１】図４は本発明の一実施例を示す連続溶融亜
鉛めっき設備の概略構成図である。FIG. 4 is a schematic configuration diagram of a continuous hot-dip galvanizing facility showing an embodiment of the present invention.
【００２２】シンクロール５は、下部をめっき浴４中に
浸漬させたフレーム５０の下端部に回転自在に取り付け
られている。サポートロール６、即ち、スタビライジン
グロール６ａおよびコレクティングロール６ｂも、下部
をめっき浴４中に浸漬させたフレーム６０ａおよび６０
ｂの各下端部にそれぞれ回転自在に取り付けられてい
る。The sink roll 5 is rotatably attached to the lower end of the frame 50 whose lower portion is immersed in the plating bath 4. The support roll 6, that is, the stabilizing roll 6a and the collecting roll 6b are also frames 60a and 60 whose lower parts are immersed in the plating bath 4.
It is rotatably attached to each lower end of b.
【００２３】フレーム６０ａは、フレーム５０の浴外部
分に上部が連結され、フレーム５０に取り付けられた移
動機構より鋼帯に向かって前後方向に移動されて、スタ
ビライジングロール６ａの押し込み量を調節する。フレ
ーム６０ｂは、めっき浴４上に配設された固定ベース６
１に上部が連結され、固定ベース６１に取り付けられた
移動機構６２により同じく鋼帯に向かって前後方向に移
動されて、コレクティングロール６ｂの押し込み量を調
節する。The upper portion of the frame 60a is connected to the outside of the bath of the frame 50, and is moved forward and backward toward the steel strip by a moving mechanism attached to the frame 50 to adjust the pushing amount of the stabilizing roll 6a. . The frame 60b is a fixed base 6 arranged on the plating bath 4.
The upper part is connected to 1 and is moved in the front-back direction toward the steel strip by the moving mechanism 62 attached to the fixed base 61 to adjust the pushing amount of the collecting roll 6b.
【００２４】フレーム６０ａおよび６０ｂの各浴外部分
には、振動検出手段９および９がそれぞれ取り付けられ
ている。振動検出手段９および９は例えばフレーム６０
ａおよび６０ｂの振動速度を検出し、これを制御手段１
０に与える。Vibration detecting means 9 and 9 are attached to the outer portions of the frames 60a and 60b, respectively. The vibration detection means 9 and 9 are, for example, the frame 60.
The vibration speeds of a and 60b are detected, and this is controlled by the control means 1.
Give to 0.
【００２５】制御手段１０は、与えられた振動速度が最
小値となるように駆動機構６２に動作指令を与えて、コ
レクティングロール６ｂの押し込み量を調節する。コレ
クティングロール６ｂの押し込み量を調節しても振動に
よる欠陥発生を充分に防止できないときは、ライン速度
調節機構に指令信号を送って、欠陥発生を充分に防止で
きるレベルまでライン速度を低下させる。The control means 10 gives an operation command to the drive mechanism 62 so that the applied vibration speed becomes the minimum value, and adjusts the pushing amount of the collecting roll 6b. If the generation of defects due to vibration cannot be sufficiently prevented even by adjusting the pushing amount of the collecting roll 6b, a command signal is sent to the line speed adjusting mechanism to reduce the line speed to a level at which the defects can be sufficiently prevented.
【００２６】表１に示す条件の連続溶融亜鉛めっき操業
において、コレクティングロールの押し込み量を種々調
節して、フレームの振動速度の変化を調査した。調査結
果を示したのが前掲の図２である。表３に示す条件下で
ライン速度を種々調節したときのロールフレームの振動
速度の変化を示したのが前掲の図３である。In the continuous hot-dip galvanizing operation under the conditions shown in Table 1, the amount of pushing of the collecting roll was variously adjusted and changes in the vibration speed of the frame were investigated. The survey results are shown in FIG. 2 above. FIG. 3 shows changes in the vibration speed of the roll frame when various line speeds are adjusted under the conditions shown in Table 3.
【００２７】[0027]
【表１】 [Table 1]
【００２８】[0028]
【表２】 [Table 2]
【００２９】従来、表１の条件の操業においては、コレ
クティングロールの押し込み量はオペレーターの経験及
び鋼帯の振れ状況の目視チェック等により約２０ｍｍに
設定されていた。この場合、フレーム振動速度は約２ｍ
ｍ／ｓであり、ドロス格落ち発生率は1.５％、チャタマ
ーク発生率は0.５％であった。そこで、コレクティング
ロールの押し込み量を３０ｍｍにして振動速度を最小値
（約1.５ｍｍ／ｓ）にした。その結果、ドロス格落ち発
生率は1.５％から0.３％に、チャタマーク発生率は0.５
％から0.３％にそれぞれ減少した。Conventionally, in the operation under the conditions shown in Table 1, the pushing amount of the collecting roll has been set to about 20 mm based on the experience of the operator and the visual check of the running condition of the steel strip. In this case, the frame vibration speed is about 2m
m / s, the incidence of dross disqualification was 1.5%, and the incidence of chatter marks was 0.5%. Therefore, the pushing speed of the collecting roll was set to 30 mm and the vibration speed was set to the minimum value (about 1.5 mm / s). As a result, the rate of dross disqualification was changed from 1.5% to 0.3%, and the rate of chatter marks was 0.5%.
% To 0.3% respectively.
【００３０】即ち、コレクティングロールの押し込み量
の調節のみで、ライン速度を低下させることなく、表面
欠陥がほぼ完全に防止された。That is, the surface defects were almost completely prevented by only adjusting the pushing amount of the collecting roll without lowering the line speed.
【００３１】[0031]
【発明の効果】以上の説明から明らかなように、本発明
の溶融金属めっき設備における振動防止方法および装置
は、めっき浴中ロールの振動を抑制することにより、鋼
帯表面に付着する異物のロールすり抜けを阻止できるの
で、表面欠陥の発生を防止できる。従って、めっき鋼帯
の格落ち防止による歩留り向上を達成できる。また、浴
中ロール振動の管理指標としてフレーム振動を導入して
その定量化を図ったので、オペレータの個人能力に頼る
ことなく安定に振動を抑制でき、振動抑制のための作業
の平準化および完全自動化を可能にする。更に、ライン
速度を必要以上に低下させることがないので、生産性の
低下を防止できる利点もある。As is apparent from the above description, the vibration preventing method and apparatus in the molten metal plating equipment of the present invention suppress the vibration of the roll in the plating bath to prevent the roll of foreign matter from adhering to the surface of the steel strip. Since slip-through can be prevented, the occurrence of surface defects can be prevented. Therefore, it is possible to improve the yield by preventing the deterioration of the plated steel strip. In addition, since frame vibration was introduced as a control index for roll vibration in the bath to quantify it, it is possible to suppress vibration stably without relying on the operator's individual ability, and to level and complete the work for vibration suppression. Enables automation. Further, since the line speed is not reduced more than necessary, there is an advantage that productivity can be prevented from lowering.
【図１】連続溶融亜鉛めっき設備の概略構成図である。FIG. 1 is a schematic configuration diagram of a continuous hot-dip galvanizing facility.
【図２】コレクティングロールの押し込み量とフレーム
振動との関係を示すグラフである。FIG. 2 is a graph showing a relationship between a pushing amount of a collecting roll and frame vibration.
【図３】ライン速度とフレーム振動との関係を示すグラ
フである。FIG. 3 is a graph showing the relationship between line speed and frame vibration.
【図４】本発明の一実施例を示す連続溶融亜鉛めっき設
備の概略構成図である。FIG. 4 is a schematic configuration diagram of continuous hot-dip galvanizing equipment showing an embodiment of the present invention.
１ 鋼帯 ３ めっきポット ４ めっき浴 ５ シンクロール ６ サポートロール ６ａ スタビライジングロール ６ｂ コレクティングロール ７ ワイピングノズル ９ 振動検出手段 ５０，６０ａ，６０ｂ フレーム 1 Steel strip 3 Plating pot 4 Plating bath 5 Sink roll 6 Support roll 6a Stabilizing roll 6b Collecting roll 7 Wiping nozzle 9 Vibration detection means 50, 60a, 60b Frame
Claims (2)
浸漬され、該めっき浴中を進行する鋼帯を案内支持する
めっき浴中ロールの支持フレームに振動検出手段を設
け、該振動検出手段により検出されるフレーム振動を抑
えるべくめっきポット内における鋼帯支持力および／ま
たは鋼帯進行速度を調節することを特徴とする溶融金属
めっき設備における振動防止方法。1. A vibration detection means is provided on a support frame of a roll in a plating bath which is immersed in a plating bath in a molten metal plating pot and guides and supports a steel strip traveling in the plating bath. A method for preventing vibration in a molten metal plating facility, which comprises adjusting a steel strip supporting force and / or a steel strip moving speed in a plating pot in order to suppress detected frame vibration.
浸漬され、該めっき浴中を進行する鋼帯を案内支持する
めっき浴中ロールの支持フレームに設けられた振動検出
手段と、該振動検出手段により検出された振動値を入力
され、鋼帯支持力および／または鋼帯進行速度を調節す
る調節機構に、前記振動値が所定値より小さくなるよう
に動作指令を出力する制御手段とを具備することを特徴
とする溶融金属めっき設備における振動防止装置。2. Vibration detection means provided on a support frame of a roll in a plating bath for guiding and supporting a steel strip which is immersed in a plating bath in a molten metal plating pot and progresses in the plating bath, and the vibration detection. The vibration value detected by the means is input, and a control means for outputting an operation command so that the vibration value becomes smaller than a predetermined value to an adjusting mechanism for adjusting the steel strip supporting force and / or the steel strip moving speed. An anti-vibration device for use in hot dip metal plating equipment.