JPH06165771A - Fingerprint detecting liquid and method for detecting fingerprint - Google Patents
Fingerprint detecting liquid and method for detecting fingerprintInfo
- Publication number
- JPH06165771A JPH06165771A JP42A JP26799092A JPH06165771A JP H06165771 A JPH06165771 A JP H06165771A JP 42 A JP42 A JP 42A JP 26799092 A JP26799092 A JP 26799092A JP H06165771 A JPH06165771 A JP H06165771A
- Authority
- JP
- Japan
- Prior art keywords
- fingerprint
- cyanoacrylate
- detecting
- detection
- fingerprints
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、指紋を簡便かつ明瞭に
検出可能とする検出液および検出方法に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a detection liquid and a detection method capable of simply and clearly detecting a fingerprint.
【０００２】[0002]
【従来の技術】犯罪者の割り出し・検挙・訴追に必要な
証拠物件となる潜在指紋の検出は犯罪捜査上重要な手段
である。通常指紋の検出には、指紋の付着している、ま
たは指紋の付着していると思われる検体の表面をアルミ
ニウム粉末を含ませたハケで軽くはき、指紋にアルミニ
ウム粉末を付着させてゼラチン紙に写しとる、通称アル
ミ粉末によるハケ法が用いられることが多いが、検体が
拳銃、刃物などの金属製凶器、合成皮革、テープ類の粘
着面など特定の素材である場合には、当該法は鮮明な指
紋を転写することが出来ず、 これに代わってシアノアク
リル酸エステルを気化させ、指紋上に生成した白色重合
体の存在によって検出する方法が、 より明瞭な指紋痕跡
を復元させる手段として使用されてきている。2. Description of the Related Art Detection of a latent fingerprint, which is an evidence property necessary for the identification, arrest and prosecution of a criminal, is an important means for criminal investigation. Usually, to detect fingerprints, lightly scrape the surface of the specimen with fingerprints or the fingerprints that seem to have fingerprints with a brush containing aluminum powder, attach the aluminum powder to the fingerprints, and then use gelatin paper. In many cases, the brush method using aluminum powder, which is commonly referred to as a copy, is used.However, if the specimen is a specific material such as a pistol, metal weapons such as blades, synthetic leather, adhesive surface of tapes, etc. A clear fingerprint cannot be transferred, and instead, a method in which cyanoacrylate ester is vaporized and detected by the presence of the white polymer formed on the fingerprint is used as a means to restore a clearer fingerprint trace. Has been done.
【０００３】シアノアクリル酸エステルを気化させ指紋
部に白色重合体を析出させる方法（以下シアノアクリル
酸エステル気体法又は単に気体法と呼ぶ）は、アルミ粉
末によるハケ法に不適な検体から指紋を検出する方法と
して多用されているが、その操作と効果には種々の問題
があった。例えば、検出に当たっては、シアノアクリル
酸エステルのガスを検体が入ったケース中に充満させる
必要があり、低温の場合にはケース内温を上昇させ気化
した該エステルの量を増加させて気体濃度を高めたり、
重合を促進するためにケース内にお湯をいれて水蒸気濃
度を上げるなどの工夫を要するという不便さがあった。
これらの点は現場において指紋検出を行う場合において
は、検出用設備のケースがないために特に不都合なもの
である。このような操作上の問題を解決させ、効率的な
検出を行うため、シアノアクリル酸エステルを粉粒体に
滴下したり（特公平３ー８１３７８）、織布や不織布に
含浸させる（特開昭６２ー４７３４３）方法等が提案さ
れているが完全な解決には至っていないのが実状であ
る。また気体法では検出箱内にシアノアクリル酸エステ
ル気体を充満させるので箱壁にも重合体が付着するた
め、検体上の指紋が完全に検出されたかどうか外部から
把握することが出来ないという不都合さも存在する。ま
たこの方法では油成分が付着した検体では指紋を検出し
にくいという欠点も存在している。A method of vaporizing a cyanoacrylate ester to deposit a white polymer on a fingerprint portion (hereinafter referred to as a cyanoacrylate ester gas method or simply a gas method) is to detect a fingerprint from a sample unsuitable for a brush method using aluminum powder. However, there are various problems in its operation and effect. For example, in the case of detection, it is necessary to fill the case containing the sample with a cyanoacrylate ester gas, and when the temperature is low, the temperature inside the case is increased to increase the amount of the vaporized ester to increase the gas concentration. Raise or
There is an inconvenience that it is necessary to add hot water in the case to increase the water vapor concentration in order to accelerate the polymerization.
These points are particularly inconvenient when fingerprint detection is performed in the field because there is no case of detection equipment. In order to solve such an operational problem and perform efficient detection, a cyanoacrylate ester is dropped into a powder or granular material (Japanese Patent Publication No. 3-81378) or impregnated into a woven fabric or a non-woven fabric (Japanese Patent Laid-Open Publication No. Sho. 62-47343) method and the like have been proposed, but the actual situation is that they have not been completely solved. Further, in the gas method, the detection box is filled with cyanoacrylate gas, so the polymer also adheres to the box wall, and it is not possible to externally determine whether or not the fingerprint on the sample is completely detected. Exists. Further, this method has a drawback that it is difficult to detect fingerprints on a sample to which an oil component is attached.
【０００４】さらに、蛍光性色素とシアノアクリル酸エ
ステルを揮発性有機溶媒中に溶解した溶液を用いて指紋
を検出する方法が米国特許 4,882,195号明細書、特開昭
６３ー１６１９３９号公報に開示されており、また特開
昭６３ー１６１９４０号公報には、検体を有機溶媒とシ
アノアクリル酸エステルとからなる溶液で前処理した
後、さらに蛍光性色素を含む別の溶液に接触させる方法
が開示されている。これら３件の提案ではシアノアクリ
ル酸エステルを含む溶液で検体表面を処理するための方
法としてもっぱらスプレーを用いている（以下この方法
をシアノアクリル酸エステル噴霧法又は単に噴霧法とい
う）。シアノアクリル酸エステル噴霧法で検出液に使用
する溶剤として、前述の米国特許では、実質上スプレー
用プロペラントである塩素系やフッ素系溶媒が使用され
ている。また、特開昭６３ー１６１９３９および特開昭
６３ー１６１９４０ではトリクロロエタン、シクロヘキ
サン、クロロホルムおよびこれに代わる溶剤が使用され
ている。Further, a method of detecting a fingerprint using a solution in which a fluorescent dye and a cyanoacrylic acid ester are dissolved in a volatile organic solvent is disclosed in US Pat. No. 4,882,195 and JP-A-63-161939. Further, JP-A-63-161940 discloses a method of pretreating a sample with a solution consisting of an organic solvent and a cyanoacrylate, and then contacting it with another solution containing a fluorescent dye. ing. In these three proposals, a spray is exclusively used as a method for treating the sample surface with a solution containing a cyanoacrylate (hereinafter, this method is referred to as a cyanoacrylate spray method or simply a spray method). As the solvent used for the detection liquid in the cyanoacrylate ester spraying method, chlorine-based or fluorine-based solvents which are substantially propellants for spraying are used in the above-mentioned US patents. Further, in JP-A-63-161939 and JP-A-63-161940, trichloroethane, cyclohexane, chloroform and a solvent replacing them are used.
【０００５】噴霧法では、身体組織を接着するおそれの
あるシアノアクリル酸エステルを含む溶液をスプレーで
噴霧するため、目や鼻等に接着剤が付着するおそれがあ
り、該方法は安全上問題の多い方法である。さらに有機
溶剤を含む液を噴霧することによって空気中の溶剤濃度
は急激に上昇し、これらの溶剤は引火性や毒性が極めて
高いものであるため危険性が大きい方法でもある。In the spraying method, since a solution containing a cyanoacrylic acid ester that may adhere to body tissues is sprayed, the adhesive may adhere to eyes, nose, etc., which is a safety problem. There are many ways. Further, spraying a liquid containing an organic solvent causes a rapid increase in the solvent concentration in the air, and since these solvents are extremely flammable and highly toxic, it is a highly dangerous method.
【０００６】さらに油分の上に付着した指紋や逆に指紋
の上を油分が覆っているなどの検体における検出は従来
のアルミ粉末によるハケ法やシアノアクリル酸エステル
気体法では全く指紋が復元できず、シアノアクリル酸エ
ステル噴霧法でも検出液中に含まれる有機溶剤の極性が
強すぎて油分を溶解してしまうためか、明瞭な検出は不
可能であった。かかる油面状態の指紋は重大犯罪におい
て特に頻出する傾向があるという事情もあって、簡便に
使え、かつ明瞭に検出できる方法が強く望まれている。Further, in the detection of a sample such as a fingerprint adhered on the oil or conversely the oil is covered on the fingerprint, the conventional brush method using aluminum powder or the cyanoacrylate gas method cannot restore the fingerprint at all. However, even with the cyanoacrylate ester spraying method, clear detection was impossible, probably because the organic solvent contained in the detection liquid was too polar to dissolve the oil. There is a strong demand for a method that can be easily used and can be detected clearly because of the fact that such oily fingerprints tend to occur particularly frequently in serious crimes.
【０００７】[0007]
【本発明が解決しようとする課題】本発明は、従来のす
べての検出方法に存在していた、油分が付着している検
体上の指紋が確実明瞭に検出しえないという点、従来の
シアノアクリル酸エステル気体法が有していた取扱い上
不便であるという点、およびシアノアクリル酸エステル
噴霧法における危険性・毒性等の問題点を解決しようと
するものである。DISCLOSURE OF THE INVENTION The present invention has been found in all conventional detection methods, in that fingerprints on a sample to which oil is attached cannot be detected reliably and clearly. It is intended to solve the problems that the acrylic acid ester gas method has, such as inconvenience in handling, and the problems such as danger and toxicity in the cyanoacrylic acid ester spraying method.
【０００８】[0008]
【課題を解決するための手段】本発明者等は、シアノア
クリル酸エステルと脂肪族炭化水素系溶剤とからなる指
紋検出液に、指紋を検出すべき物体（検体）を浸漬し、
液中で指紋上にシアノアクリル酸エステルを重合させ、
それにより指紋を検出するという方法を採用することに
より、上記の問題点を解消し得ることを見出して本発明
を完成した。Means for Solving the Problems The present inventors have dipped an object (sample) whose fingerprint is to be detected in a fingerprint detection liquid consisting of a cyanoacrylate and an aliphatic hydrocarbon solvent,
Polymerize cyanoacrylate on fingerprint in liquid,
The present invention has been completed by finding that the above-mentioned problems can be solved by adopting a method of detecting a fingerprint thereby.
【０００９】すなわち、本発明はシアノアクリル酸エス
テルと脂肪族炭化水素系溶剤とからなることを特徴とす
る指紋検出液および該指紋検出液中に浸漬した検体表面
に生成したシアノアクリル酸エステル重合体により検出
することを特徴とする指紋検出方法に関するものであ
る。That is, the present invention is a fingerprint detection liquid characterized by comprising a cyanoacrylic acid ester and an aliphatic hydrocarbon solvent, and a cyanoacrylic acid ester polymer formed on the surface of a sample immersed in the fingerprint detection liquid. The present invention relates to a fingerprint detection method characterized by being detected by.
【００１０】本発明におけるシアノアクリル酸エステル
とは、瞬間接着剤の主成分として知られているものであ
り、例えば、シアノアクリル酸アルキルエステル、シア
ノアクリル酸アルケニルエステル、シアノアクリル酸ア
ルキニルエステル、シアノアクリル酸アルコキシアルキ
ルエステル、シアノアクリル酸ハロアルキルエステル、
シアノアクリル酸ハロアルコキシアルキルエステル、シ
アノアクリル酸シクロアルキルエステル等を挙げること
ができ、具体的な化合物としてはメチル２ーシアノアク
リレート（２−シアノアクリル酸メチルエステルに同じ
以下同様）、エチル２ーシアノアクリレート、ｎ−プロ
ピル２ーシアノアクリレート、ｉ−プロピル２ーシアノ
アクリレート、ｎ−ブチル２ーシアノアクリレート、ｉ
−ブチルシアノアクリレート、ｎ−ヘキシル２ーシアノ
アクリレート、ｎ−オクチル２ーシアノアクリレート、
２ーエチルヘキシル２ーシアノアクリレート、アリル２
ーシアノアクリレート、プロパルギル２ーシアノアクリ
レート、メトキシメチル２ーシアノアクリレート、メト
キシエチル２ーシアノアクリレート、エトキシエチル２
ーシアノアクリレート、メトキシブチル２ーシアノアク
リレート、２ークロロエチル２ーシアノアクリレート、
２ークロロエトキシエチル２ーシアノアクリレート、
２，２，２ートリフルオロエチル２ーシアノアクリレー
ト、シクロヘキシル２ーシアノアクリレート等を挙げる
ことができる。本発明においては、これらの化合物の一
種を単独で或いは二種以上を混合して使用することがで
き、さらには瞬間接着剤として販売されているそのもの
をシアノアクリル酸エステルとして用いることもでき
る。さらに、本発明の検出液には、上記からも明らかな
様に瞬間接着剤中に配合されている亜硫酸ガス、ハイド
ロキノンなどの安定剤、ポリアルキレングリコール、ク
ラウンエーテルなどの重合促進剤、ポリメチルメタクリ
レート、ポリシアノアクリレート、セルロースエステル
類、シリカなどの増粘剤、チクソトロピック性付与剤を
シアノアクリル酸エステルと共に配合することが可能で
ある。The cyanoacrylic acid ester in the present invention is known as a main component of instant adhesives, and examples thereof include alkyl cyanoacrylate, cyanoacrylic acid alkenyl ester, cyanoacrylic acid alkynyl ester, and cyanoacrylic. Acid alkoxyalkyl ester, cyanoacrylic acid haloalkyl ester,
Examples of the compound include cyanoacrylic acid haloalkoxyalkyl ester and cyanoacrylic acid cycloalkyl ester, and specific compounds include methyl 2-cyanoacrylate (the same applies to 2-cyanoacrylic acid methyl ester) and ethyl 2-cyano. Acrylate, n-propyl 2-cyanoacrylate, i-propyl 2-cyanoacrylate, n-butyl 2-cyanoacrylate, i
-Butyl cyanoacrylate, n-hexyl 2-cyanoacrylate, n-octyl 2-cyanoacrylate,
2-ethylhexyl 2-cyanoacrylate, allyl 2
-Cyanoacrylate, propargyl 2-cyanoacrylate, methoxymethyl 2-cyanoacrylate, methoxyethyl 2-cyanoacrylate, ethoxyethyl 2
-Cyanoacrylate, methoxybutyl 2-cyanoacrylate, 2-chloroethyl 2-cyanoacrylate,
2-chloroethoxyethyl 2-cyanoacrylate,
2,2,2-trifluoroethyl 2-cyanoacrylate, cyclohexyl 2-cyanoacrylate and the like can be mentioned. In the present invention, one kind of these compounds may be used alone or two or more kinds may be mixed and used, and furthermore, the one sold as an instant adhesive may be used as a cyanoacrylate ester. Further, the detection liquid of the present invention, as is apparent from the above, sulfur dioxide gas that is blended in the instant adhesive, stabilizers such as hydroquinone, polyalkylene glycol, polymerization accelerators such as crown ether, polymethyl methacrylate. , Polycyanoacrylate, cellulose esters, thickeners such as silica, and thixotropic agents can be blended with the cyanoacrylic acid ester.
【００１１】脂肪族炭化水素系溶剤とは、化学式がＣn
Ｈ2n+2で表される飽和炭化水素を主成分とする溶剤であ
り、具体的には石油ベンジン、リグロイン、ミネラルス
ピリット、灯油などの石油からの留分を主成分とする溶
剤である。本発明ではこれらの溶剤に多少の不飽和脂肪
族炭化水素、芳香族および脂環族炭化水素が混入したも
のも使用可能であるが、混合物である場合も、全量の過
半量は飽和脂肪族炭化水素であることが必要である。酢
酸エチル、酢酸ブチルなどのエステル類、メチルイソブ
チルケトン、シクロヘキサノンなどのケトン類、酢酸セ
ロソルブ、酢酸メチルセロソルブ、酢酸カルビト−ルな
どのエーテルアルコールのエステルなど極性の高い化合
物を主成分とする溶剤は、検出される成分であるシアノ
アクリル酸エステル重合体を溶解してしまうため明瞭な
復元が難しく、さらにプラスチックを基材とする検体で
は、基材そのものを溶解・膨潤・変質させてしまう可能
性が高く、その検出液の適用範囲が限定され不適当なも
のである。またシアノアクリル酸エステルと混合した場
合に、重合を開始させうる官能基であるアルコール性水
酸基、アミン基、アミド基などを有する溶剤も使用でき
ないものである。このような溶剤を用いると液中にシア
ノアクリル酸エステルの重合体が生成し、液中に沈澱し
たり、液全体がゲル状物になる。さらに塩素系溶剤やフ
ッ素系溶剤は油脂の洗浄力が強く油面上の指紋検出には
不適でもあり、毒性や環境に悪影響を与える点からも不
都合である。なお脂肪族炭化水素系溶剤であっても、ガ
ソリンや石油エーテルなどのように極度に低沸点、低引
火点であるものや、検体を検出液中に浸漬後、室温下で
検体を乾燥するに際し極端に乾燥速度が遅い、例えば沸
点が３００℃を越える高沸点溶剤等は実用上からは好ま
しくなく、好ましいものは沸点範囲が、例えば６０〜３
００℃程度のものである。従って化合物としては炭素数
６〜１０程度の直鎖状あるいは分岐状の脂肪族炭化水素
を主要な構成成分とする溶剤が本発明にとり好ましい。An aliphatic hydrocarbon solvent has a chemical formula of C n
It is a solvent whose main component is a saturated hydrocarbon represented by H 2n + 2 , and more specifically, a solvent whose main component is a fraction from petroleum such as petroleum benzine, ligroin, mineral spirits and kerosene. In the present invention, these solvents may be mixed with some unsaturated aliphatic hydrocarbons, aromatic and alicyclic hydrocarbons, but even in the case of a mixture, the majority of the total amount is saturated aliphatic hydrocarbons. It must be hydrogen. Ethyl acetate, esters such as butyl acetate, methyl isobutyl ketone, ketones such as cyclohexanone, cellosolve acetate, methyl cellosolve acetate, solvents mainly composed of highly polar compounds such as esters of ether alcohols such as carbitol acetate, It is difficult to restore clearly because it dissolves the cyanoacrylate polymer that is the component to be detected, and in the case of specimens that use plastics as the base material, there is a high possibility that the base material itself will dissolve, swell, or deteriorate. However, the applicable range of the detection liquid is limited and inappropriate. Further, a solvent having an alcoholic hydroxyl group, an amine group, an amide group or the like, which is a functional group capable of initiating polymerization when mixed with a cyanoacrylate, cannot be used. When such a solvent is used, a polymer of cyanoacrylic acid ester is produced in the liquid, which precipitates in the liquid or the entire liquid becomes a gel. Further, the chlorine-based solvent and the fluorine-based solvent have strong detergency for fats and oils and are not suitable for detecting fingerprints on the oil surface, and are also inconvenient in that they adversely affect toxicity and environment. Note that even aliphatic hydrocarbon solvents, such as gasoline and petroleum ether, that have extremely low boiling points and low flash points, or when the sample is immersed in the detection solution and then dried at room temperature An extremely slow drying rate, for example, a high-boiling point solvent having a boiling point of more than 300 ° C. is not preferable in practice, and a preferable boiling point range is, for example, 60 to 3
It is about 00 ° C. Therefore, as the compound, a solvent containing a linear or branched aliphatic hydrocarbon having about 6 to 10 carbon atoms as a main constituent is preferable for the present invention.
【００１２】シアノアクリル酸エステルと脂肪族炭化水
素系溶剤とからなる検出液中のシアノアクリル酸エステ
ルの濃度は特に限定されるものではないが、あまりにも
低濃度の場合には指紋上に生成し析出する重合体量が不
十分となって明瞭な指紋復元が不可能になったり、析出
までの時間が遅くなったりする不都合さがある。また必
要以上の高濃度溶液を用いると、指紋存在部以外への重
合物の生成が見られたり、浸漬後の乾燥作業が取扱い上
不便であり好ましくない。従って適当な液中のシアノア
クリル酸エステルの濃度は、好ましくは0.０１〜１Vol
％であり、より好ましくは0.２〜0.６Vol ％である。The concentration of the cyanoacrylate ester in the detection liquid consisting of the cyanoacrylate ester and the aliphatic hydrocarbon solvent is not particularly limited, but if it is too low, it is formed on the fingerprint. There are disadvantages that the amount of polymer to be deposited becomes insufficient and clear fingerprint restoration becomes impossible, and the time until deposition is delayed. Further, if a solution having a higher concentration than necessary is used, the formation of a polymer in a portion other than the fingerprint portion is observed, and the drying operation after immersion is inconvenient in handling, which is not preferable. Therefore, the concentration of cyanoacrylate in a suitable liquid is preferably 0.01 to 1 vol.
%, And more preferably 0.2 to 0.6 Vol%.
【００１３】本発明における検出液中には、一般に有機
溶剤に可溶な着色染料や蛍光染料を添加することができ
る。検体が白色や淡色などの場合、指紋上に生成した重
合体を着色することによってさらに明瞭となるからであ
る。着色染料としては、検出液の貯蔵安定性や指紋の鮮
明性からシアノアクリル酸エステルの重合を著しく促進
する作用を持つアミノ基、水酸基などの官能基を有しな
い化学構造である染料が好ましい。それらの官能基を有
する染料を含む検出液は貯蔵安定性に劣り、指紋の鮮明
性も低下する。具体的には着色染料としては、アゾ系染
料、アンスラキノン系染料、フタロシアニン系染料、ア
ジン系染料および塩基性染料ベースの脂肪酸塩系染料な
どであり、一方蛍光染料としては、ビス（ベンズオキサ
ゾリル）エチレン系、ビス（ベンズオキサゾリル）チオ
フェン系、ナフトール酸ーＮ置換イミド系、スチルベン
系、クマリン系などが挙げられる。着色の種類としては
特に限定されるものではなく、検体自身の色に比べ析出
するシアノアクリル酸エステルの重合体が着色され鮮明
に識別できるものが好ましい。着色染料と蛍光染料とを
混合して用いることも可能である。検出液中の染料濃度
は特に限定されるものではなく染料の溶解性、検出液の
安定性、検出指紋の鮮明性、経済性などから適当な範囲
内が選択される。A coloring dye or a fluorescent dye which is generally soluble in an organic solvent can be added to the detection liquid of the present invention. This is because when the sample is white or light-colored, it becomes clearer by coloring the polymer formed on the fingerprint. As the coloring dye, a dye having a chemical structure having no functional group such as amino group and hydroxyl group, which has a function of remarkably promoting the polymerization of cyanoacrylate ester from the storage stability of the detection liquid and the sharpness of fingerprint, is preferable. The detection liquid containing the dye having such a functional group is inferior in storage stability, and the sharpness of fingerprints is also deteriorated. Specifically, coloring dyes include azo dyes, anthraquinone dyes, phthalocyanine dyes, azine dyes and basic dye-based fatty acid salt dyes, while fluorescent dyes include bis (benzoxazolidine). Examples thereof include ethylene), bis (benzoxazolyl) thiophene, naphtholic acid-N-substituted imide, stilbene, and coumarin. The type of coloring is not particularly limited, and it is preferable that the color of the polymer of the cyanoacrylate ester to be precipitated is clearly colored and clearly distinguishable from the color of the sample itself. It is also possible to mix and use a coloring dye and a fluorescent dye. The concentration of the dye in the detection liquid is not particularly limited and is selected within an appropriate range in view of the solubility of the dye, the stability of the detection liquid, the sharpness of the detected fingerprint, the economical efficiency and the like.
【００１４】検体を染料を含まぬ検出液中に浸漬し指紋
上に白色重合体を析出後、これを染料を含む水溶液ない
し有機溶剤溶液中に浸漬し重合体を着色する二液法も使
用可能であり、この場合特に水溶性染料からなる染色液
はとくに美しく染色できる傾向がある。使用される水溶
性染料としてはアゾ染料、アントラキノン染料、インジ
ゴイド染料、フタロシアニン染料、カルボニウム染料、
キノンイミン染料、メチン染料、キノリン染料、ニトロ
染料、ニトロソ染料、ベンゾキノンおよびナフトキノン
染料、ナフタルイミド染料、ベリノン染料などである。It is also possible to use a two-component method in which a sample is immersed in a detection liquid containing no dye, a white polymer is deposited on a fingerprint, and then this is immersed in an aqueous solution containing a dye or an organic solvent solution to color the polymer. In this case, a dyeing solution containing a water-soluble dye tends to be dyed particularly beautifully. Water-soluble dyes used include azo dyes, anthraquinone dyes, indigoid dyes, phthalocyanine dyes, carbonium dyes,
Examples thereof include quinone imine dyes, methine dyes, quinoline dyes, nitro dyes, nitroso dyes, benzoquinone and naphthoquinone dyes, naphthalimide dyes, and verinone dyes.
【００１５】指紋検出の手順としては、指紋が付着して
いると予測される検体を、検体の入る適当サイズの検出
液入り容器、出来れば無色透明で指紋の検出状態が外部
から観察できる蓋付きの検出液入り容器に入れ、検体を
検出液中に室温で約１〜３６０分程度浸漬し、その後こ
れを検出液から引き上げ常温で自然乾燥するということ
で良い。浸漬時間は、あまり長時間では指紋以外の部分
にも重合体が析出し不鮮明となるので好ましくなく、短
時間すぎても析出重合体量が少ないため鮮明な検出が出
来ない傾向がある。従って透明な浸漬容器中で指紋の検
出状態を観察しながら浸漬を続け、明瞭な検出が完成し
た時点を待って、引き上げる方法が好ましい。また、火
焔瓶に付着した指紋を検出する場合など、灯油や油脂類
の上にのっている指紋の検出には、指紋上に析出した重
合体が脱落しないよう、浸漬中の液を動かさないのが望
ましい。As a procedure for detecting fingerprints, a container containing a detection liquid of an appropriate size in which a sample expected to have fingerprints is contained, preferably a colorless transparent container with a lid for observing the fingerprint detection state from the outside. It can be said that the sample is placed in the container containing the detection liquid, and the sample is immersed in the detection liquid at room temperature for about 1 to 360 minutes, then taken out of the detection liquid and naturally dried at room temperature. If the dipping time is too long, the polymer will be unclear because it will be deposited even on the part other than the fingerprint, and if it is too short, the amount of the precipitated polymer will be too small to allow clear detection. Therefore, it is preferable to continue dipping while observing the detection state of fingerprints in a transparent dipping container, and wait until the time when clear detection is completed before pulling up. In addition, when detecting fingerprints attached to the flame bottle, for detecting fingerprints on kerosene or oils, do not move the liquid during immersion so that the polymer deposited on the fingerprints does not fall off. Is desirable.
【００１６】[0016]
【作用】本発明の指紋検出液は、溶剤として、脂肪族炭
化水素系溶剤を使用しているため、油面上の指紋検出に
おいて指紋下の油分を洗浄しながら、指紋を明瞭に復元
することを可能とし、プラスチックを基材とする検体で
も基材を溶解・膨潤・変質させることも少ないという作
用を奏するのである。なお、シアノアクリル酸エステル
の重合は、指紋中に含まれる水分、アミノ酸類等の指頭
分泌物の作用によるものと推定されている。Since the fingerprint detection liquid of the present invention uses an aliphatic hydrocarbon solvent as a solvent, it can clearly restore the fingerprint while washing the oil below the fingerprint in the fingerprint detection on the oil surface. It is possible to achieve the above, and it is possible to dissolve, swell, and change the quality of a sample having a plastic base material. The polymerization of cyanoacrylic acid ester is presumed to be due to the action of fingertip secretions such as water and amino acids contained in fingerprints.
【００１７】[0017]
【実施例】以下実施例と比較例を挙げて、本発明を具体
的に説明する。EXAMPLES The present invention will be specifically described below with reference to Examples and Comparative Examples.
【００１８】実施例１〜５ リグロイン１００ｍｌにエトキシエチル２ーシアノアク
リレートを主成分とする瞬間接着剤（東亞合成化学工業
株式会社製アロンアルフア＃８０１）をそれぞれ0.０９
ｍｌ、0.１５ｍｌ、0.３ｍｌ、0.４５ｍｌ、0.６ｍｌを
加え撹拌し調製した溶液を検出液Ａ〜Ｅとした。検出液
をガラス製の角型容器中に入れ、軟質塩化ビニールシー
ト上に指を押しつけ指紋を付着させた検体を検出液に浸
漬した。検体表面に指紋状の白色ポリマーが析出するま
で浸漬し、析出を確認後検体を取り出し溶剤を乾燥させ
て指紋検出状態を確認した。これらの結果を表１に示し
た。Examples 1 to 5 0.09 of an instant adhesive (Aron Alpha # 801 manufactured by Toagosei Kagaku Kogyo Co., Ltd.) containing ethoxyethyl 2-cyanoacrylate as a main component was added to 100 ml of ligroin.
ml, 0.15 ml, 0.3 ml, 0.45 ml, and 0.6 ml were added and the solutions prepared by stirring were used as detection liquids A to E. The detection liquid was placed in a rectangular glass container, and a sample having a fingerprint attached by pressing a finger on a soft vinyl chloride sheet was immersed in the detection liquid. The sample was immersed until a fingerprint-like white polymer was deposited on the surface of the sample. After confirming the deposition, the sample was taken out and the solvent was dried to confirm the fingerprint detection state. The results are shown in Table 1.
【００１９】[0019]
【表１】 [Table 1]
【００２０】なお液調製３日後、検出液Ａ〜Ｅに同じ瞬
間接着剤各0.１５ｍｌを追加し再度同様の試験を実施し
たところ、いずれの場合も６〜７分の浸漬で鮮明な指紋
を検出できた。After 3 days from the preparation of the solution, 0.15 ml of the same instant adhesive was added to each of the detection solutions A to E and the same test was conducted again. In any case, a clear fingerprint was obtained by immersion for 6 to 7 minutes. I was able to detect it.
【００２１】実施例６〜８、比較例１〜３ 各種の有機溶剤７０ｍｌにイソブチル２ーシアノアクリ
レートを0.１５ｍｌ加えて溶解し検出液（シアノアクリ
レート濃度＝0.２Vol ％）を調製し、直ちに実施例１と
同様の方法で指紋検出試験をおこなった。検出液の性状
と指紋検出結果を表２に記載した。Examples 6 to 8 and Comparative Examples 1 to 3 0.15 ml of isobutyl 2-cyanoacrylate was added to 70 ml of various organic solvents and dissolved to prepare a detection solution (concentration of cyanoacrylate = 0.2 vol%). A fingerprint detection test was conducted in the same manner as in Example 1. Table 2 shows the properties of the detection liquid and the fingerprint detection results.
【００２２】[0022]
【表２】 表２ ┌────┬───────┬───────┬────────────┐ │ │ 溶剤の種類 │検出液の性状 │ 指紋検出状態 │ ├────┼───────┼───────┼────────────┤ │実施例６│石油ベンジン │無色透明 │６０分浸漬後極めて鮮明 │ │実施例７│リグロイン │無色透明 │６０分浸漬後極めて鮮明 │ │実施例８│白灯油 │無色透明 │６０分浸漬後鮮明 │ ├────┼───────┼───────┼────────────┤ │比較例１│酢酸エチル │無色透明 │塩ヒ゛シート自体が白化し指紋 │ │ │ │ │が不鮮明 │ │比較例２│ｎーフ゛チルアルコール │沈澱物析出 │検出せず │ │比較例３│メチルイソフ゛チルケトン │白濁液 │検出せず │ │ │ │ │ │└ ────┴───────┴───────┴────────────┘[Table 2] Table 2 ┌────┬───────┬───────┬────────────┐ │ │ Solvent type │ Detection solution Properties │ Fingerprint detection │ ├────┼───────┼───────┼────────────┤ │Example 6│Petroleum benzine │ colorless Clear │ Extremely clear after 60 minutes immersion │ Example 7 │ Ligroin │ Colorless transparent │ Extremely clear after 60 minutes immersion │ │ Example 8 │ White kerosene │ Colorless transparent │ Clear after 60 minutes immersion │ ├────┼─ ──────┼───────┼────────────┤ │ Comparative Example 1 │ Ethyl acetate │ colorless transparent │ salt salt sheet whitened fingerprint │ │ │ │ │ │ is unclear │ │ Comparative Example 2 │ n-butyl alcohol │ Precipitate deposition │ Not detected │ │ Comparative Example 3 │ Methyl isobutyl ketone │ White turbid liquid │ Not detected │ │ │ │ │ │ └ ────┴───────┴───────┴────────────┘
【００２３】実施例９ 実施例１で使用した瞬間接着剤３ｍｌ、青色油溶性染料
0.５ｇをリグロイン５００ｍｌに加えて撹拌溶解し、青
色の指紋検出液とした。てんぷら油をうすく塗布したナ
イフの側面（金属部分）に指を押しつけ指紋を付着させ
た検体を、透明容器に入れた上記検出液中に浸漬し、１
２０分静置した。検体を取り出して自然乾燥させた後、
指紋付着部分を観察したところ青色の鮮明な指紋が検出
されていた。Example 9 3 ml of the instant adhesive used in Example 1, blue oil-soluble dye
0.5 g was added to 500 ml of ligroin and dissolved by stirring to obtain a blue fingerprint detection liquid. A sample with a fingerprint attached by pressing a finger on the side surface (metal part) of a knife lightly coated with tempura oil was dipped in the above-mentioned detection liquid contained in a transparent container, and 1
Let stand for 20 minutes. After removing the sample and allowing it to air dry,
When the fingerprint adhered portion was observed, a clear blue fingerprint was detected.
【００２４】比較例４ 実施例９において、有機溶剤としてリグロインの代わり
に酢酸エチルおよびｎ−ブチルアルコールを用いて検出
液を調製し同様の指紋検出試験を行った。いずれの検出
液を用いてもナイフ上に鮮明な指紋を検出することは出
来なかった。Comparative Example 4 In Example 9, a detection liquid was prepared by using ethyl acetate and n-butyl alcohol instead of ligroin as the organic solvent, and the same fingerprint detection test was conducted. It was not possible to detect a clear fingerprint on the knife using any of the detection solutions.
【００２５】比較例５ 実施例９で使用した検体を用い、アルミニウム粉末を用
いるアルミ粉末によるハケ法で指紋を検出しようと試み
たが指紋は検出出来なかった。また、同じ検体を、瞬間
接着剤とお湯を別々に入れた皿が入っている箱の中に置
き、シアノアクリル酸エステル気体法により指紋を検出
しようと試みたが、鮮明な指紋の検出は出来なかった。Comparative Example 5 Using the sample used in Example 9, an attempt was made to detect a fingerprint by the brush method using aluminum powder, but the fingerprint could not be detected. Also, the same sample was placed in a box containing a dish containing instant adhesive and hot water, and an attempt was made to detect fingerprints by the cyanoacrylate gas method, but clear fingerprints could be detected. There wasn't.
【００２６】[0026]
【発明の効果】本発明による指紋検出液を用いる指紋検
出方法は、従来の指紋検出法では検出不能であった油脂
が付着した検体上の指紋検出を極めて鮮明な状態で可能
とする上、それ以外の多くの検体上の指紋検出をも簡便
迅速な操作により可能とするものであり、なおかつ毒
性、引火危険性など安全面にも優れていて犯罪捜査に著
しく貢献するものである。The fingerprint detection method using the fingerprint detection liquid according to the present invention enables the fingerprint detection on a specimen with oil and fat adhered thereto, which could not be detected by the conventional fingerprint detection method, in an extremely clear state. Other than the above, fingerprint detection on many specimens can be performed by a simple and quick operation, and it is also excellent in safety such as toxicity and danger of ignition, and it significantly contributes to criminal investigation.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 藤本 嘉明 愛知県名古屋市港区船見町１番地の１東亞 合成化学工業株式会社名古屋総合研究所内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Yoshiaki Fujimoto 1st Toa, Funami-cho, Minato-ku, Nagoya, Aichi Nagoya Synthetic Chemical Industry Co., Ltd.
Claims (2)
化水素系溶剤とからなることを特徴とする指紋検出液。1. A fingerprint detection liquid comprising a cyanoacrylic acid ester and an aliphatic hydrocarbon solvent.
し、検体表面の潜在指紋をこれに沿って生成したシアノ
アクリル酸エステル重合体により検出することを特徴と
する指紋検出方法。2. A fingerprint detection method, comprising immersing a sample in the fingerprint detection liquid according to claim 1, and detecting a latent fingerprint on the sample surface by a cyanoacrylate polymer formed along the latent fingerprint.