JPH06158559A - Woven and knit fabric having excellent light resistance - Google Patents
Woven and knit fabric having excellent light resistanceInfo
- Publication number
- JPH06158559A JPH06158559A JP4308750A JP30875092A JPH06158559A JP H06158559 A JPH06158559 A JP H06158559A JP 4308750 A JP4308750 A JP 4308750A JP 30875092 A JP30875092 A JP 30875092A JP H06158559 A JPH06158559 A JP H06158559A
- Authority
- JP
- Japan
- Prior art keywords
- spandex
- light resistance
- polyester
- producing
- soft segment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、耐光性に優れたスパン
デックス交編織物の製法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a spandex interwoven fabric having excellent light resistance.
【０００２】[0002]
【従来の技術】従来、スパンデックス交編織物の耐光性
は不良であり、特に分散染料による染色物の耐光性は不
良であった。又、スパンデックスの中で、現在実質的に
世界市場の略１００％を占める、ソフトセグメントとし
てポリエーテル（ポリテトラメチレングリコール又は若
干の改質されたものを含む）を用いたものは、エーテル
の光劣化が激しいことに起因して、特に耐光性が不良で
あった。この為、スパンデックスの化学構造を問わず、
染色処理後にスパンデックスより染料を抜く処理、例え
ば強烈な還元洗浄等を実施し、スパンデックスより染料
を脱色してしまう等の処理を実施しているが、その処理
が不十分であったり、その処理によりスパンデックスが
劣化損傷したりして、好ましくない状態であった。又、
所謂後加工により耐光性を付与しようとする事も、有力
な処方であるが洗濯等に対する耐久性が当然ながら不足
しており、十分なものとは言えない状況である。2. Description of the Related Art Conventionally, spandex interwoven fabrics have a poor light resistance, and in particular, a dyed product with a disperse dye has a poor light resistance. In addition, among spandex, the one that uses polyether (including polytetramethylene glycol or a slightly modified one) as the soft segment, which currently occupies substantially 100% of the world market, is the light of ether. Due to the severe deterioration, the light resistance was particularly poor. Therefore, regardless of the chemical structure of spandex,
After the dyeing process, the dye is removed from the spandex, for example, intense reduction washing is performed, and the dye is decolorized from the spandex, but the treatment is insufficient or The spandex was deteriorated and damaged, which was not preferable. or,
Attempting to impart light resistance by so-called post-processing is a powerful prescription, but the durability against washing and the like is naturally insufficient, and it cannot be said to be sufficient.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、ポエステル
をソフトセグメントとするスパンデックス交編織物の消
費性能上の耐久性の高い耐光性を、スパンデックスを損
傷する等、性能を害なう事無く、向上しようとするもの
である。DISCLOSURE OF THE INVENTION The present invention provides highly durable light resistance of spandex interwoven fabrics having a polyester as a soft segment, without damaging the spandex, without impairing the performance. It is an attempt to improve.
【０００４】[0004]
【課題を解決するための手段】本発明者らは、ポリエス
テルをソフトセグメントとするスパンデックスの交編織
物を染色加工するに当たり、ベンゾトリアゾール系耐光
性向上剤（紫外線吸収剤）を併用する事により、スパン
デックスよりの強烈な脱色加工等を施す事無く、良好な
耐光性が得られることを見出したものである。もちろ
ん、染色後、一般的な布に対して通常実施される還元洗
浄処理等の処理は実施するべきである。Means for Solving the Problems The present inventors have used a benzotriazole type light resistance improver (ultraviolet absorber) in combination in dyeing a spandex interwoven fabric having polyester as a soft segment, It has been found that good light resistance can be obtained without performing a strong decolorization process or the like that of spandex. Needless to say, after dyeing, treatment such as reduction cleaning treatment that is usually performed on a general cloth should be performed.
【０００５】耐光性向上剤として、ベンゾフェノン系耐
光性向上剤も効果が無いわけではないが、一般的に紫外
領域の吸収波長幅が狭く、効果不十分な場合があり、ベ
ンゾトリアゾール系のものが好ましく用いられる。ベン
ゾトリアゾール系耐光性向上剤の使用量としては、布帛
に対して０．１〜５．０重量％（ｏｗｆ）が好ましく用
いられ、更に好ましくは０．５〜２．５％ｏｗｆであ
る。ベンゾトリアゾール系耐光性向上剤の使用料が少な
いと必要な効果が得られず、多すぎるとコストアップす
るばかりか、ブリードアウトして汚染の原因となるなど
し、逆効果となってしまう。As the light resistance improver, a benzophenone type light resistance improver is not ineffective, but in general, the absorption wavelength width in the ultraviolet region is narrow and the effect may be insufficient. It is preferably used. The amount of the benzotriazole-based light resistance improver used is preferably 0.1 to 5.0% by weight (owf) with respect to the cloth, and more preferably 0.5 to 2.5% owf. If the amount of the benzotriazole-based light resistance improver used is small, the required effect cannot be obtained, and if it is too large, not only the cost increases, but also bleeding out causes contamination, which is an adverse effect.
【０００６】本発明に好ましく用いられるベンゾトリア
ゾール系耐光性向上剤（紫外線吸収剤）は染色加工工程
に適応可能なものである。例えば、染色液中に分散して
用い得るもの、プリント加工ではプリント用の糊剤に添
加して用い得るもの、が好ましい。別途、該向上剤を含
有させる工程も取り得るが、余分な加工履歴を与えるこ
ととなり、布帛性能の低下や加工コストの上昇を招くの
で、出来るかぎり避けるべきである。The benzotriazole-based light resistance improver (ultraviolet absorber) preferably used in the present invention is applicable to the dyeing process. For example, those which can be used by being dispersed in a dyeing solution and those which can be used by being added to a sizing agent for printing in printing processing are preferable. Although it is possible to separately take a step of incorporating the improving agent, an extra processing history is given, which causes deterioration in fabric performance and an increase in processing cost. Therefore, it should be avoided as much as possible.
【０００７】本発明に言うスパンデックスと交編織した
編織物とは、スパンデックスを所謂生糸の状態で他の繊
維、例えばポリエステル、ナイロン、綿、アクリル、レ
ーヨン、アセテートなどと編織したものや、これらの糸
を巻き付けたカバリングヤーンやエア交絡したものを交
編織したもの等を例示することが出来る。The knitted woven fabric in which the spandex and the knitted fabric are referred to in the present invention means the one obtained by knitting the spandex in the state of so-called raw yarn with other fibers such as polyester, nylon, cotton, acrylic, rayon and acetate, and these yarns. Examples of the covering yarn include wound yarns, and air-entangled yarns that are interwoven and woven.
【０００８】更に本発明者等は、ポリエステル系スパン
デックスとポリエステル系繊維とを交編織し、染色時に
ベンゾトリアゾール系耐光性向上剤を併用した場合、よ
り有効である事を見出だした。これは解明されたわけで
は無いが、同じポリエステル系であることにより耐光性
向上剤の効果がより大きく発揮されたためと推定され
る。本発明に言うポリエステル繊維とは、ポリエチレン
テレフタレート、ポリブチレンテレフタレート及びこれ
らの２０モル％以内の範囲で改質された樹脂より製造さ
れたもの、及びこれらと他の樹脂（例えばナイロン）と
の複合紡糸によるものやそれら単独の繊維と混繊された
もので、ポリエステルが３０％以上含まれるものを言
う。Further, the present inventors have found that it is more effective when a polyester type spandex and a polyester type fiber are interwoven and knitted and a benzotriazole type light fastness improving agent is used together during dyeing. Although this has not been clarified, it is presumed that the effect of the light resistance improver was exerted more greatly by using the same polyester system. The polyester fibers referred to in the present invention include those produced from polyethylene terephthalate, polybutylene terephthalate and resins modified within the range of 20 mol% thereof, and composite spinning of these with other resins (for example, nylon). Or a mixture of these fibers with a single fiber and containing 30% or more of polyester.
【０００９】更に本発明者等は、ポリエステル系スパン
デックスとして下記（１）式で示されるスパンデックス
に本発明を適用した場合、更に耐光性が向上するばかり
でなく、その他の消費性能、例えば、ポリエステルの染
色に用いる分散染料の移行昇華性なども向上することを
見出だした。Further, when the present invention is applied to a spandex represented by the following formula (1) as a polyester-based spandex, not only the light resistance is further improved, but also other consumption performance, for example, polyester It has been found that the transfer sublimability of the disperse dye used for dyeing is also improved.
【化２】 （ここで、Ｒ1は２価の有機基で、その５０モル％以上
は−ＣＨ2−ＣＨ2−ＣＨ（ＣＨ3）−ＣＨ2−ＣＨ2−で
あり、ｎは４〜１０の整数であって、且つ、下記
（２）、（３）の関係を満足する平均分子量１０００〜
３５００のポリエステル。） ６≦（全炭素数／エステル結合数）≦９ （２） ０．０３≦（メチン基数／全炭素数）≦０．１ （３） （ここで、全炭素数とは高分子ジオール中のエステル結
合に含まれる炭素を除いた残りの炭素の合計数。）[Chemical 2] (Here, R 1 is a divalent organic group, 50 mol% or more of which is —CH 2 —CH 2 —CH (CH 3 ) —CH 2 —CH 2 —, and n is an integer of 4 to 10. And an average molecular weight of 1000 to satisfy the following relationships (2) and (3):
3500 polyester. ) 6 ≤ (total carbon number / ester bond number) ≤ 9 (2) 0.03 ≤ (methine group number / total carbon number) ≤ 0.1 (3) (where, the total carbon number means The total number of remaining carbons excluding the carbons contained in the ester bond.)
【００１０】この理由は解明されているわけでは無い
が、染料やベンゾトリアゾール系耐光性向上剤の吸着座
席のバランスが取れ、よりその効果を発現するためと推
定される。即ち、エステル結合の極性とメチン基の疏水
性のバランスが重要な要素を形成しており、−ＣＨ2−
ＣＨ2−ＣＨ（ＣＨ3）−ＣＨ2−ＣＨ2−基の含有率は、
ソフトセグメントの非晶性を保証するものと推定され
る。Although the reason for this has not been clarified, it is presumed that the adsorption seat of the dye or the benzotriazole-based light resistance improver is balanced and the effect thereof is further exhibited. That is, hydrophobic balance of polar and methine groups of the ester bonds forms a key element, -CH 2 -
The content rate of the CH 2 —CH (CH 3 ) —CH 2 —CH 2 — group is
It is presumed to guarantee the amorphousness of the soft segment.
【００１１】さらに本発明者等は、本発明に用いられる
ポリエステル系スパンデックス中に、ヒンダードアミン
系光安定剤Ａとヒンダードフェノール系酸化防止剤Ｂを
（４）〜（６）式の範囲で添加すると更に耐光性が向上
することを見出だした。 ０．１wt％≦ Ａ ≦２．０wt％ （４） ０．１wt％≦ Ｂ ≦２．０wt％ （５） ０．２ ≦Ａ／Ｂ≦５ （６） ヒンダードアミン系光安定剤のみあるいはヒンダードフ
ェノール系酸化防止剤のみを添加した場合には、十分な
耐光性向上効果が得られず、これらを（４）〜（６）式
を満足する範囲で併用することにより相乗的に耐光性が
向上する。Further, the inventors of the present invention add the hindered amine light stabilizer A and the hindered phenolic antioxidant B in the range of the formulas (4) to (6) in the polyester spandex used in the present invention. It has been found that the light resistance is further improved. 0.1 wt% ≤ A ≤ 2.0 wt% (4) 0.1 wt% ≤ B ≤ 2.0 wt% (5) 0.2 ≤ A / B ≤ 5 (6) Hindered amine light stabilizer only or hindered phenol When only a system antioxidant is added, a sufficient light resistance improving effect cannot be obtained, and when these are used together in a range satisfying the expressions (4) to (6), the light resistance is synergistically improved. .
【００１２】本発明に用いられるヒンダードアミン系光
安定剤（HALS）は、種々の物が用い得るがスパンデック
スの紡糸や編織、染色等の工程中にブリードアウトや昇
華分解を生じない出来るだけ分子量の大きいもの、スパ
ンデックスを形成するポリウレタンの分子中に組み込ま
れるものが好ましく、特に後者のタイプが好ましく用い
られる。The hindered amine light stabilizer (HALS) used in the present invention may be various ones, but it has a molecular weight as large as possible without causing bleed-out or sublimation decomposition during the steps of spinning, knitting, dyeing, etc. of spandex. Those incorporated into the molecule of polyurethane forming spandex are preferable, and the latter type is particularly preferably used.
【００１３】本発明に用いられるヒンダードフェノール
系酸化防止剤としては、スパンデックスの紡糸や編織、
染色等の工程中にブリードアウトや昇華分解の生じない
出来るだけ分子量の大きいものが好ましく用いられる。
ヒンダードのタイプとしては、片ヒンダードでも両ヒン
ダードでも良いが、フェノール基がイソシアネート基と
反応しないタイプの物が良く、この反応に触媒作用を有
する金属類の存在に十分な注意が必要である。例えば、
ヒンダードアミン系光安定剤やヒンダードフェノール系
酸化防止剤の合成に用いられるリチウム等の存在に留意
する必要がある。The hindered phenolic antioxidant used in the present invention includes spandex spinning, knitting and weaving,
Those having a molecular weight as large as possible without causing bleed-out or sublimation decomposition during the steps such as dyeing are preferably used.
The hindered type may be one-sided hindered type or both-sided hindered type, but a type in which a phenol group does not react with an isocyanate group is preferable, and it is necessary to pay sufficient attention to the presence of a metal having a catalytic action for this reaction. For example,
It is necessary to pay attention to the presence of lithium and the like used in the synthesis of hindered amine light stabilizers and hindered phenol antioxidants.
【００１４】本発明に於いて用いられるヒンダードアミ
ン系光安定剤のポリエステル系スパンデックスへの添加
時期は、用いるポリウレタンの合成からスパンデックス
としての製糸時迄のどの時点でも良いが、酸化劣化によ
る効果の低下を考慮すると、製糸直前の添加が最も好ま
しい。しかし、ポリウレタンに組み込まれるタイプの光
安定剤の場合には、ポリウレタンの合成時に添加するの
が好ましい。本発明に於いて用いられるヒンダードフェ
ノール系酸化防止剤のポリエステル系スパンデックスへ
の添加時期は、耐光性の観点から言えば、スパンデック
スとしての製糸時に添加するのが最も良いが、その工程
上の最適な時点を選択することが可能である。The hindered amine light stabilizer used in the present invention may be added to the polyester spandex at any time from the synthesis of the polyurethane used to the spinning of the spandex, but the effect is deteriorated due to oxidative deterioration. Considering this, the addition immediately before spinning is most preferable. However, in the case of a light stabilizer of the type incorporated in polyurethane, it is preferably added during the synthesis of the polyurethane. From the viewpoint of light resistance, it is best to add the hindered phenolic antioxidant used in the present invention to the polyester spandex at the time of spinning as a spandex, but it is optimal in the process. It is possible to select any time point.
【００１５】本発明に言うポリエステルをソフトセグメ
ントとするスパンデックスには、乾式紡糸や湿式紡糸に
より主に生産されるポリウレタンウレア系スパンデック
スや、溶融紡糸により主に生産されるポリウレタン系ス
パンデックスがある。本発明に言うポリエステルには、
炭酸エステル系ポリエステル、即ち、ポリカーボネート
も含まれる。The spandex containing polyester as the soft segment in the present invention includes polyurethane urea-based spandex mainly produced by dry spinning and wet spinning, and polyurethane-based spandex mainly produced by melt spinning. The polyester referred to in the present invention includes
Carbonate ester type polyester, that is, polycarbonate is also included.
【００１６】[0016]
【実施例】以下、実施例により説明する。なお、本発明
における耐光性評価方法は、ＪＩＳ Ｌ０８４２−１９
７１に従い、カーボンア−ク灯法（６３℃）により実施
した。EXAMPLES Examples will be described below. The light resistance evaluation method in the present invention is based on JIS L0842-19.
No. 71, the carbon arc lamp method (63 ° C.).
【００１７】（実施例−１、比較例−１）分子量１５０
０のポリ−３−メチルペンタンアゼレートをソフトセグ
メントとするポリウレタンよりなる４０デニールのスパ
ンデックスと、５０デニール／３６フィラメントのポリ
エステル繊維よりなるツーウェイトリコットを、Ｓｍｉ
ｋａｌｏｎ Ｒｅｄ Ｅ−ＲＰＤ ０．１％ｏｗｆにて
１２５℃で染色した。染め上がった布を１６０℃でファ
イナルセットし、耐光性を評価した所、染色時にベンゾ
トリアゾール系耐光性向上剤であるＳｕｍｉｐｏｎ−Ｕ
Ｌを１％ｏｗｆとなるように染色液に添加したものは４
−５級であるのに対し、添加しなかったものは３級以下
であった。(Example-1, Comparative Example-1) Molecular weight 150
A 40-denier spandex made of polyurethane having 0 of poly-3-methylpentane azelate as a soft segment and a two-weight ricott made of polyester fiber of 50-denier / 36 filaments are used as Smi
Stained with kalon Red E-RPD 0.1% owf at 125 ° C. The dyed cloth was finally set at 160 ° C. and evaluated for light resistance. As a result, Sumipon-U, which is a benzotriazole-based light resistance improver at the time of dyeing
It was 4 when L was added to the dyeing solution so that it became 1% owf.
While the grade was −5, those not added were grade 3 or lower.
【００１８】（実施例−２、比較例−２）実施例−１で
用いたスパンデックスと４０デニール／２０フィラメン
トのナイロン糸によるツーウェイトリコットを、９５℃
で熱水処理したものの耐光性を評価したところ、熱水に
ベンゾトリアゾール系耐光性向上剤Ｓｕｍｉｐｏｎ−Ｕ
Ｌを１％ｏｗｆとなるように添加したものは３−４級で
あったが、添加しなかったものはフェード１０時間でグ
レースケール１号と激しく黄変し、極めて耐光性が不良
であった。(Example-2, Comparative Example-2) A two-weight cot with the spandex and the nylon yarn of 40 denier / 20 filaments used in Example-1 was heated to 95 ° C.
When the light resistance of the product treated with hot water was evaluated, the benzotriazole-based light resistance improver Sumipon-U
The one to which L was added so as to be 1% owf was grade 3-4, but the one to which L was not added was severely yellowed to gray scale No. 1 within 10 hours of fading and had extremely poor light resistance. .
【００１９】（実施例−３、比較例−３）ポリ−エチレ
ンプロピレンアジペート（分子量１５００）をソフトセ
グメントとするポリウレタンよりなるスパンデックス
（２１０デニール）と５０デニール／３６フィラメント
のポリエステル繊維とのラッセル生地を、１２０℃で染
色処理する以外実施例−１、比較例−１と同様に染色処
理した所、ポリウレタンのヘタリを生じた。これらの耐
光性を評価したところ、Ｓｕｍｉｐｏｎ−ＵＬを添加し
たものは３−４級であり、添加しないものは激しく黄変
し３級以下であった。(Example-3, Comparative Example-3) A Russell fabric composed of spandex (210 denier) made of polyurethane having poly-ethylene propylene adipate (molecular weight 1500) as a soft segment and polyester fiber of 50 denier / 36 filaments was prepared. When the dyeing treatment was carried out in the same manner as in Example-1 and Comparative Example-1 except that the dyeing treatment was carried out at 120 ° C., the settling of polyurethane was generated. When the light resistance of these was evaluated, those with Sumipon-UL added were grade 3-4, and those without addition were severely yellowed and grade 3 or lower.
【００２０】（実施例−４、５）分子量２０００のポリ
−３−メチル−ペンタンアゼレートをソフトセグメント
とするポリウレタンを合成する際に、ヒンダードアミン
系光安定剤Ａとしてコハク酸ジメチル−１−（２−ヒド
ロキシエチル）−４−ヒドロキシ−２，２，６，６，−
テトラメチルピペリジン重縮合物（分子量３０００以
上）を５０００ｐｐｍ添加し、これを２８０デニールの
スパンデックスとして製糸する際に、ヒンダードフェノ
ール系酸化防止剤Ｂとして、３，９−ビス［２−｛３−
（３−ｔ−ブチル−４−ヒドロキシ−５−メチルフェニ
ル）プロピオニルオキシ｝−１，１−ジメチルエチル］
−２，４，８、１０−テトラオキサスピロ［５，５］ウ
ンデカン、およびペンタエリスリチル−テトラキス［３
−（３，５−ジ−ｔ−ブチル−４−ヒドロキシフェニ
ル）プロピオネート］を其々４０００ｐｐｍ添加し、２
種のスパンデックスを得た。これと５０デニール／４８
フィラメントのポリエステル糸でラッセル生地を編成し
生地−１、生地−２を得た。この生地を１３０℃で染色
する以外実施例−１と同様にして耐光性を評価したとこ
ろ、両者とも５級であり良好な耐光性を示した。(Examples-4 and 5) Dimethyl succinate-1- (2) was used as a hindered amine light stabilizer A when synthesizing a polyurethane having poly-3-methyl-pentane azelate having a molecular weight of 2000 as a soft segment. -Hydroxyethyl) -4-hydroxy-2,2,6,6,-
When 5000 ppm of tetramethylpiperidine polycondensate (molecular weight of 3,000 or more) was added, and when this was spun into 280 denier spandex, 3,9-bis [2- {3-
(3-t-Butyl-4-hydroxy-5-methylphenyl) propionyloxy} -1,1-dimethylethyl]
-2,4,8,10-Tetraoxaspiro [5,5] undecane, and pentaerythrityl-tetrakis [3
-(3,5-di-t-butyl-4-hydroxyphenyl) propionate] was added at 4000 ppm each, and 2
Obtained the seed spandex. This and 50 denier / 48
Russell cloth was knitted with filament polyester threads to obtain cloth-1 and cloth-2. When the light fastness was evaluated in the same manner as in Example 1 except that this fabric was dyed at 130 ° C., both of them were of the 5th grade and showed good light fastness.
【００２１】[0021]
【発明の効果】本発明の方法により、ポエステルをソフ
トセグメントとするスパンデックス交編織物の耐久性の
高い耐光性を、消費性能を損なうことなく向上すること
ができる。特に、ポリエステル繊維との交編織物におい
てはポリエステル繊維とスパンデックスとが同一の色調
となるため、いわゆる目剥き状態となってもスパンデッ
クスが目立たず、交編織物の付加価値が高まり、用途分
野も拡大される。Industrial Applicability According to the method of the present invention, the durable light resistance of spandex interwoven fabrics having a soft segment of polyester can be improved without impairing the consumption performance. In particular, in a knitted fabric with polyester fibers, since the polyester fiber and spandex have the same color tone, the spandex is not conspicuous even in a so-called blinding state, the added value of the knitted fabric is increased, and the field of application is expanded. To be done.
Claims (5)
スパンデックスと交編織した編織物を染色するにあた
り、ベンゾトリアゾール系耐光性向上剤を併用すること
を特徴とする耐光性に優れた編織物の製法。1. A method for producing a knitted woven fabric having excellent light resistance, which comprises using a benzotriazole-based light resistance improver together in dyeing a knitted woven fabric that is interwoven with spandex having polyester as a soft segment.
用量が編織物の０．１〜５．０重量％である請求項１に
記載の耐光性に優れた編織物の製法。2. The method for producing a knitted fabric having excellent light resistance according to claim 1, wherein the amount of the benzotriazole-based light resistance improver used in combination is 0.1 to 5.0% by weight of the knitted fabric.
エステルである請求項１または２に記載の耐光性に優れ
た編織物の製法。3. The method for producing a knitted fabric excellent in light resistance according to claim 1, wherein the fiber interwoven with the spandex is polyester.
る繰り返し単位で構成されるポリエステルポリオールを
ソフトセグメントとするスパンデックスである請求項１
〜３のいずれかに記載の耐光性に優れた編織物の製法。 【化１】 （ここで、Ｒ1は２価の有機基で、その５０モル％以上
は−ＣＨ2−ＣＨ2−ＣＨ（ＣＨ3）−ＣＨ2−ＣＨ2−で
あり、ｎは４〜１０の整数であって、且つ、下記
（２）、（３）の関係を満足する平均分子量１０００〜
３５００のポリエステル。） ６≦（全炭素数／エステル結合数）≦９ （２） ０．０３≦（メチン基数／全炭素数）≦０．１ （３） （ここで、全炭素数とは高分子ジオール中のエステル結
合に含まれる炭素を除いた残りの炭素の合計数。）4. The spandex is a spandex having a soft segment of a polyester polyol composed of a repeating unit represented by the following formula (1).
4. The method for producing a knitted fabric excellent in light resistance according to any one of 3 to 3. [Chemical 1] (Here, R 1 is a divalent organic group, 50 mol% or more of which is —CH 2 —CH 2 —CH (CH 3 ) —CH 2 —CH 2 —, and n is an integer of 4 to 10. And an average molecular weight of 1000 to satisfy the following relationships (2) and (3):
3500 polyester. ) 6 ≤ (total carbon number / ester bond number) ≤ 9 (2) 0.03 ≤ (methine group number / total carbon number) ≤ 0.1 (3) (where, the total carbon number means The total number of remaining carbons excluding the carbons contained in the ester bond.)
スパンデックス中に、ヒンダードアミン系光安定剤（酸
化防止剤）Ａとヒンダードフェノール系酸化防止剤Ｂ
が、（４）〜（６）式の範囲で含有されている、請求項
１〜４のいずれかに記載の耐光性に優れた編織物の製
法。 ０．１wt％≦ Ａ ≦２．０wt％ （４） ０．１wt％≦ Ｂ ≦２．０wt％ （５） ０．２ ≦Ａ／Ｂ≦５ （６）5. A hindered amine light stabilizer (antioxidant) A and a hindered phenolic antioxidant B in spandex containing polyester as a soft segment.
Is contained in the range of the formulas (4) to (6), and the method for producing a knitted fabric excellent in light resistance according to any one of claims 1 to 4. 0.1 wt% ≤ A ≤ 2.0 wt% (4) 0.1 wt% ≤ B ≤ 2.0 wt% (5) 0.2 ≤ A / B ≤ 5 (6)