JPH06157262A - Multilayered cosmetic for protection against ultraviolet rays - Google Patents
Multilayered cosmetic for protection against ultraviolet raysInfo
- Publication number
- JPH06157262A JPH06157262A JP30413092A JP30413092A JPH06157262A JP H06157262 A JPH06157262 A JP H06157262A JP 30413092 A JP30413092 A JP 30413092A JP 30413092 A JP30413092 A JP 30413092A JP H06157262 A JPH06157262 A JP H06157262A
- Authority
- JP
- Japan
- Prior art keywords
- powder
- coated
- titanium oxide
- iron oxide
- make
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、メークアップ下地料を
第一層用とし、メークアップ仕上料を第二層用として組
合せた、紫外線カット効果を有する紫外線防護用重層化
粧料に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a multilayer cosmetic for UV protection having a UV blocking effect in which a make-up base material is used for the first layer and a make-up finish is used for the second layer.
【０００２】[0002]
【従来の技術】従来、メークアップ化粧料による紫外線
カット効果は、紫外線吸収剤の配合割合や、化粧料中に
おける紫外線吸収剤の分散性の向上（例えば、球状粉体
に紫外線吸収剤を内包、あるいは含浸させたり、界面活
性剤を併せて配合する）を図ることにより、向上を目指
すものが多い。2. Description of the Related Art Conventionally, the UV-cutting effect of makeup cosmetics has been improved by improving the mixing ratio of the UV-absorbing agent and the dispersibility of the UV-absorbing agent in the cosmetic (for example, encapsulating the UV-absorbing agent in a spherical powder, In many cases, it is aimed to improve by impregnating or mixing a surfactant together).
【０００３】また、二酸化チタンや、微粒子化した酸化
チタンなど紫外線カット効果の高い粉体を使用したり、
さらには酸化チタンを種々の顔料で表面処理し、被覆す
ることで処方系中での分散性を向上させることにより、
紫外線カット効果を高めることも行われている。Further, powders having a high UV blocking effect such as titanium dioxide and finely divided titanium oxide are used,
Furthermore, by improving the dispersibility in the formulation system by surface-treating titanium oxide with various pigments and coating it,
It is also being carried out to enhance the UV blocking effect.
【０００４】しかし、このような従来の処方系による化
粧膜では、皮膚に塗布直後の紫外線カット効果はあるも
のの、夏期使用などの実使用においては、汗、皮脂等に
よる化粧料くずれを招き、紫外線カット効果を有する化
粧膜としての耐久性は、問題となることが多かった。す
なわち、メーク後数時間経過した後の紫外線カット効果
が、塗布直後の紫外線カット効果とほぼ変化のないよう
なメークアップ料は得られていなかった。However, the cosmetic film according to such a conventional prescription system has an effect of blocking ultraviolet rays immediately after being applied to the skin, but in actual use such as summer use, it causes the cosmetics to break due to sweat, sebum, etc. Durability as a decorative film having a cutting effect was often a problem. That is, no make-up material was obtained in which the UV-cutting effect after a lapse of several hours from the make-up was almost the same as the UV-cutting effect immediately after application.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、上記問題を
克服し、紫外線カット効果が長時間にわたって持続し、
しかも物理的刺激や水、油剤等に接触してもその効果が
減少することのない紫外線防護用化粧料を提供すること
を課題とする。DISCLOSURE OF THE INVENTION The present invention overcomes the above-mentioned problems, and the ultraviolet blocking effect lasts for a long time,
Moreover, it is an object of the present invention to provide a UV-protective cosmetic that does not reduce its effect even if it is exposed to physical irritation, water, oil, etc.
【０００６】[0006]
【課題を解決するための手段】本発明者らは、上記課題
を解決するために鋭意研究を重ねた結果、粘着性物質を
含有するメークアップ下地料を肌上に塗布して第一層と
し、その上に更に紫外線カット効果を有するメークアッ
プ仕上料を第二層として塗布すると、紫外線カット効果
に優れ、なおかつ密着性、持続性及び耐物理的刺激性、
耐油性、耐水性が向上した塗膜が得られることを見出
し、本発明を完成するに至った。Means for Solving the Problems As a result of intensive studies to solve the above problems, the present inventors applied a makeup base material containing an adhesive substance onto the skin to form a first layer. , If a make-up finish having an ultraviolet ray blocking effect is further applied as a second layer thereon, the ultraviolet ray blocking effect is excellent, and the adhesion, durability and physical irritation resistance are excellent,
They have found that a coating film having improved oil resistance and water resistance can be obtained, and completed the present invention.
【０００７】すなわち本発明は、粘着性物質を含有する
第一層用メークアップ下地料と、紫外線カット効果を有
する第二層用メークアップ仕上料とを組合せた紫外線防
護用重層化粧料を提供する。That is, the present invention provides a multilayer cosmetic for UV protection in which a make-up base material for the first layer containing a sticky substance and a make-up finish for the second layer having an ultraviolet blocking effect are combined. .
【０００８】以下に本発明を詳細に説明する。 ＜１＞本発明のメークアップ下地料 まず、本発明のメークアップ下地料は、皮膚に直接塗布
される第一層用として使用される。このメークアップ下
地料は粘着性物質を含有する。粘着性物質はこの第一層
の密着性は勿論のこと、その上の第二層に使用される光
を拡散反射する粉体を含有するメークアップ仕上げ料の
固着化、密着性及び持続性を向上させると共に、対物理
的刺激性、耐油性、耐水性のある化粧膜を形成する目的
で使用される。The present invention will be described in detail below. <1> Makeup base material of the present invention First, the make-up base material of the present invention is used for the first layer directly applied to the skin. This make-up base material contains a sticky substance. The adhesive substance not only adheres to the first layer, but also fixes, adheres and lasts the makeup finish containing the powder used for the second layer that diffuses and reflects light. It is used for the purpose of improving and simultaneously forming a cosmetic film having physical irritancy, oil resistance and water resistance.
【０００９】粘着性物質としては、通常の化粧料に使用
されるものであればよく、これらは粘着テープとしてＪ
ＩＳ Ｚ−０２３７に規定される方法で試験した時、下
記性能 タック：５〜２０ 粘着力（ステンレス板）：５００〜２０００ｇ／２５ｍ
ｍ を有するものである。この粘着性試験方法について更に
詳しく説明すると、粘着性物質のサンプルを離型紙に塗
布、乾燥し、これをコート紙に貼り付けた後、離型紙を
剥して粘着テープとし、これを常温（２５℃）で下記方
法に従って試験を行う。As the adhesive substance, any substance used in ordinary cosmetics may be used.
When tested by the method specified in IS Z-0237, the following performance tack: 5-20 Adhesive force (stainless steel plate): 500-2000 g / 25 m
m. This adhesiveness test method will be described in more detail. A sample of an adhesive substance is applied to a release paper, dried, and attached to a coated paper, and then the release paper is peeled off to obtain an adhesive tape, which is kept at room temperature (25 ° C). ) And perform the test according to the following method.
【００１０】（試験方法） タック：ＪＩＳ Ｚ−０２３７に規定された試験方法に
よるタック 粘着力：ＪＩＳ Ｚ−０２３７に規定された１８０度引
きはがし法による粘着力（ｇ／２５ｍｍ）（被着体：ス
テンレス板）(Test method) Tack: Tack according to the test method specified in JIS Z-0237 Adhesive force: Adhesive force according to the 180 degree peeling method specified in JIS Z-0237 (g / 25 mm) (Adherend: Stainless plate)
【００１１】このような粘着性物質の具体例としては、
アクリル酸エステルを主成分モノマーとし、これに重合
性カルボン酸を共重合させたポリマー（以下、アクリル
系共重合体という）；三次元網状シリコーン等が挙げら
れる。As a concrete example of such an adhesive substance,
Polymers obtained by copolymerizing an acrylic acid ester as a main component monomer with a polymerizable carboxylic acid (hereinafter referred to as an acrylic copolymer); three-dimensional reticulated silicone and the like can be mentioned.
【００１２】これらの粘着性物質について更に詳しく説
明すると、まずアクリル系共重合体はアクリル酸エステ
ルに対して１〜１０重量％の重合性カルボン酸を共重合
させることにより得られ、その平均分子量は１万〜１０
０万程度である。[0012] Explaining these tacky substances in more detail, first, an acrylic copolymer is obtained by copolymerizing 1 to 10% by weight of a polymerizable carboxylic acid with an acrylic ester, and its average molecular weight is 10,000-10
It is about 0,000.
【００１３】前記アクリル酸エステルとしては、アクリ
ル酸メチル、アクリル酸エチル、アクリル酸プロピル、
アクリル酸ブチル、アクリル酸イソブチル、アクリル酸
ヘキシル、アクリル酸２エチルヘキシル等を挙げること
ができ、これらは単独であるいは２種以上の組合せで使
用することができる。Examples of the acrylic acid ester include methyl acrylate, ethyl acrylate, propyl acrylate,
Examples thereof include butyl acrylate, isobutyl acrylate, hexyl acrylate, and 2-ethylhexyl acrylate. These can be used alone or in combination of two or more.
【００１４】前記重合性カルボン酸としては、低炭素数
の不飽和カルボン酸を挙げることができ、好ましくはア
クリル酸、メタクリル酸、イタコン酸、マレイン酸等を
例示することができる。これらは単独であるいは２種以
上の組合せで使用することができる。Examples of the polymerizable carboxylic acid include unsaturated carboxylic acids having a low carbon number, preferably acrylic acid, methacrylic acid, itaconic acid, maleic acid and the like. These can be used alone or in combination of two or more.
【００１５】主成分モノマーであるアクリル酸エステル
以外に、副成分モノマーとして、酢酸ビニル、メタクリ
ル酸メチル、アクリルアミドの１種又は２種以上を使用
してもよい。前記と同様に主成分モノマー及び副成分モ
ノマーと、これらのモノマー全量に対して１〜１０重量
％の重合性カルボン酸とを共重合させた平均分子量１万
〜１００万のポリマーを使用する。この場合は、主成分
モノマーと副成分モノマーとの重量比が、９９：１〜７
０：３０であることが好ましい。In addition to the acrylic ester which is the main component monomer, one or more of vinyl acetate, methyl methacrylate, and acrylamide may be used as the sub-component monomer. Similarly to the above, a polymer having an average molecular weight of 10,000 to 1,000,000 obtained by copolymerizing a main component monomer and a subcomponent monomer with 1 to 10% by weight of a polymerizable carboxylic acid based on the total amount of these monomers is used. In this case, the weight ratio of the main component monomer and the sub-component monomer is 99: 1 to 7
It is preferably 0:30.
【００１６】アクリル系共重合体の市販品としては、例
えば大成化工（株）から販売されているＳＥ−７５３
Ａ、３ＬＸ−１７４がある。次に、三次元網状シリコー
ンは、例えば有機トリクロロシラン（ＲＳｉＣｌ3）と
有機ジクロロシラン（ＲＳｉＣｌ2）とを加水分解した
後、縮合し、架橋させることによって得られる。市販品
としては、信越化学社製シリコーンＫＦ７６１３Ｂ等が
ある。Examples of commercially available acrylic copolymers include SE-753 sold by Taisei Kako Co., Ltd.
A, 3LX-174. Next, the three-dimensional reticulated silicone is obtained, for example, by hydrolyzing organic trichlorosilane (RSiCl 3 ) and organic dichlorosilane (RSiCl 2 ), then condensing and crosslinking. Examples of commercially available products include Silicone KF7613B manufactured by Shin-Etsu Chemical Co., Ltd.
【００１７】以上のような粘着性物質の含有量は、メー
クアップ下地料全量に対し通常０．５〜７０重量％程度
である。メークアップ下地料にはその他、通常の化粧料
に使用される希釈剤、保湿剤、防腐剤、香料等を含有さ
せてもよい。The content of the adhesive substance as described above is usually about 0.5 to 70% by weight based on the total amount of the makeup base material. In addition, the make-up base material may contain a diluent, a moisturizing agent, an antiseptic, a fragrance and the like which are commonly used in cosmetics.
【００１８】＜２＞本発明のメークアップ仕上げ料 本発明のメークアップ仕上料は、上記のメークアップ下
地料からなる第一層上に塗布される第二層（ファンデー
ション）用として使用される。このメークアップ仕上料
は、紫外線をカットする成分（以下、「紫外線カット成
分」という。）を含有する。<2> Makeup Finishing Material of the Present Invention The makeup finishing material of the present invention is used for the second layer (foundation) applied on the first layer composed of the above-mentioned makeup base material. This makeup finish contains a component that blocks ultraviolet rays (hereinafter referred to as "ultraviolet blocking component").
【００１９】前記紫外線カット成分は、紫外線をカット
する目的で使用されるものである。ここで、紫外線カッ
トとは、紫外線の拡散反射あるいは吸収等により、皮膚
表面に存在した場合に皮膚に紫外線を到達させないもの
をいう。具体的には、（Ａ）酸化チタン、微粒子酸化チ
タン、酸化チタン被覆雲母、酸化チタン被覆セリサイ
ト、酸化チタン被覆タルク、酸化鉄被覆雲母、酸化鉄被
覆セリサイト、酸化鉄被覆タルク、酸化鉄、二酸化亜鉛
等の粉体、（Ｂ）パラメトキシケイ皮酸オクチル、２−
エチルヘキシルパラジメチルアミノベンゾエート、オキ
シベンゾン、ウロカニン酸、４−ｔｅｒｔ−ブチル−
４’−メトキシ−ジベンゾイルメチルから選ばれる少な
くとも１種を、ポリエチレンビーズ、ナイロンパウダ
ー、シリコーンパウダー、メタクリル酸メチルパウダ
ー、シリカパウダー、ケイ酸マグネシウム粉末、ケイ酸
カルシウム粉末から選ばれる少なくとも１種に内包ある
いは含浸させたもの、が挙げられる。これらは、単独で
も任意の２種以上の混合物としても使用できる。The UV-cutting component is used for the purpose of cutting UV rays. Here, the ultraviolet ray cut means an element that does not allow the ultraviolet ray to reach the skin when it exists on the skin surface due to the diffuse reflection or absorption of the ultraviolet ray. Specifically, (A) titanium oxide, fine particle titanium oxide, titanium oxide-coated mica, titanium oxide-coated sericite, titanium oxide-coated talc, iron oxide-coated mica, iron oxide-coated sericite, iron oxide-coated talc, iron oxide, Powder such as zinc dioxide, (B) octyl paramethoxycinnamate, 2-
Ethylhexyl paradimethylaminobenzoate, oxybenzone, urocanic acid, 4-tert-butyl-
At least one selected from 4'-methoxy-dibenzoylmethyl is included in at least one selected from polyethylene beads, nylon powder, silicone powder, methyl methacrylate powder, silica powder, magnesium silicate powder, and calcium silicate powder. Alternatively, it may be impregnated. These can be used alone or as a mixture of two or more kinds.
【００２０】第二層用メークアップ仕上料は、上記紫外
線カット成分を、メークアップ仕上料全量に対し通常１
〜９０重量％、好ましくは１〜４０重量％配合される。
第二層中の紫外線カット成分の配合量が１％未満では紫
外線カット効果が低下することがある。The make-up finish for the second layer contains the above-mentioned UV-blocking component in an amount of usually 1 with respect to the total amount of the make-up finish.
˜90% by weight, preferably 1-40% by weight.
If the blending amount of the UV blocking component in the second layer is less than 1%, the UV blocking effect may be reduced.
【００２１】メークアップ仕上料にはその他、通常のメ
ークアップ仕上料に使用される有機、無機の各種粉体；
顔料；固型、半固型又は液状油分；界面活性剤；顔料分
散剤；可塑剤；香料；防腐剤等を含有させてもよい。Other make-up finishes include various organic and inorganic powders used in ordinary make-up finishes;
Pigments; solid, semi-solid or liquid oils; surfactants; pigment dispersants; plasticizers; fragrances; preservatives and the like may be contained.
【００２２】[0022]
【作用】上記メークアップ下地料は、粘着性を有してお
り、この上にメークアップ仕上げ料を重ねて塗布するこ
とができるので、皮膚への密着性がよい。このメークア
ップ仕上げ料は、紫外線カット成分を含有しているの
で、紫外線をカットする効果、及びその効果の耐久性を
有する。The above-mentioned make-up base material has tackiness, and since the make-up finishing material can be overlaid and applied thereon, it has good adhesion to the skin. Since this make-up finishing material contains an ultraviolet ray-cutting component, it has the effect of cutting off ultraviolet rays and the durability of that effect.
【００２３】[0023]
【実施例】以下に本発明を実施例によって更に詳しく説
明する。なお、実施例中の配合量（％）は全て重量％で
ある。EXAMPLES The present invention will be described in more detail below with reference to examples. In addition, all compounding amounts (%) in the examples are% by weight.
【００２４】[0024]
【実施例１】表１に示すＡ成分を撹拌し可溶化した後、
Ｂ成分を少量ずつ撹拌しながら加え、第一層用のメーク
アップ下地料（以下、下地料１という）を製造した。な
お、表１中のアクリル系共重合体とは、アクリル酸エス
テルとして９８．５重量％のアクリル酸エチルとアクリ
ル酸ブチル（アクリル酸エチル：アクリル酸ブチル＝
４：１）を、重合性カルボン酸として１．５重量％のア
クリル酸を用い、これらを共重合させて得られた平均分
子量１０万の共重合体で、タック１７、粘着力１５００
ｇ／２５ｍｍの性能を有するものである。Example 1 After stirring and solubilizing the component A shown in Table 1,
Component B was added little by little with stirring to produce a makeup base material for the first layer (hereinafter referred to as base material 1). The acrylic copolymer in Table 1 means 98.5% by weight of ethyl acrylate and butyl acrylate (ethyl acrylate: butyl acrylate = acrylic acid ester).
4: 1) is a copolymer having an average molecular weight of 100,000 obtained by copolymerizing 1.5% by weight of acrylic acid as a polymerizable carboxylic acid, tack 17, adhesive strength 1500
It has a performance of g / 25 mm.
【００２５】[0025]
【表１】 [Table 1]
【００２６】次に、表２に示す粉体成分Ａをヘンシェル
ミキサー中で混合し、更にパルベライザーで粉砕した
後、再びヘンシェルミキサーに入れ、油剤成分Ｂを混入
し、粉体成分Ａを油剤成分Ｂでコーティングした。これ
を取り出した後、パルベライザーで仕上げ粉砕を行い、
第二層用のメークアップ仕上料（パウダーファンデーシ
ョン）（以下、仕上料１という）を製造した。なお、こ
れは中皿にプレス成形して保存した。Next, the powder component A shown in Table 2 is mixed in a Henschel mixer, further pulverized with a pulsarizer, and then put into the Henschel mixer again, and the oil agent component B is mixed therein, and the powder component A is changed to the oil agent component B. Coated with. After taking this out, finish pulverize with a pulsarizer,
A makeup finish (powder foundation) for the second layer (hereinafter referred to as finish 1) was produced. In addition, this was press-molded in a medium plate and stored.
【００２７】[0027]
【表２】 [Table 2]
【００２８】[0028]
【実施例２】第一層用メークアップ下地料として実施例
１で製造した下地料１を用意した。次に表３に示す成分
を用いた他は実施例１の第二層用メークアップ仕上げ料
の製造方法と同様にして第二層用メークアップ仕上げ料
（以下、仕上げ料２という）を製造した。これは中皿に
プレス成形して保存した。Example 2 The base material 1 produced in Example 1 was prepared as the makeup base material for the first layer. Next, except that the components shown in Table 3 were used, a make-up finish for the second layer (hereinafter referred to as finish 2) was produced in the same manner as in the method for producing the make-up finish for the second layer of Example 1. . This was press-molded in a medium plate and stored.
【００２９】[0029]
【表３】 [Table 3]
【００３０】[0030]
【実施例３】表４に示す各成分を溶解釜に入れ、常温で
混合して第一層用メークアップ下地料（以下、下地料２
という）を製造した。Example 3 The ingredients shown in Table 4 were placed in a melting pot and mixed at room temperature to prepare a first layer make-up base material (hereinafter referred to as Base Material 2).
Called) was manufactured.
【００３１】[0031]
【表４】 [Table 4]
【００３２】なお、表４中の三次元網状シリコーンと
は、例えば特開昭６１−１８７０８号公報（出願人：ポ
ーラ化成工業）に従って製造したもので、タック１０、
粘着力１０００ｇ／２５ｍｍという性能を有するもので
ある。The three-dimensional reticulated silicone in Table 4 is a product manufactured according to, for example, Japanese Patent Application Laid-Open No. 61-18708 (applicant: POLA CHEMICAL INDUSTRIES).
The adhesive strength is 1000 g / 25 mm.
【００３３】一方、第二層用のメークアップ仕上料とし
て実施例１で製造した仕上料１を用意した。On the other hand, the finishing material 1 produced in Example 1 was prepared as the makeup finishing material for the second layer.
【００３４】[0034]
【実施例４】第一層用メークアップ下地料として実施例
３で製造した下地料２を用意し、第二層用メークアップ
仕上げ料として実施例２で製造した仕上げ料２を用意し
た。Example 4 The base material 2 prepared in Example 3 was prepared as the make-up base material for the first layer, and the finish material 2 prepared in Example 2 was prepared as the make-up finish material for the second layer.
【００３５】[0035]
【比較例１】アクリル系共重合体の代わりにポリビニル
アルコールを用いた他は実施例１と同じ方法で第一層用
のメークアップ下地料（以下、下地料３という）を製造
した。Comparative Example 1 A makeup base material for the first layer (hereinafter referred to as base material 3) was produced in the same manner as in Example 1 except that polyvinyl alcohol was used instead of the acrylic copolymer.
【００３６】一方、第二層用のメークアップ仕上料とし
て実施例１で製造した仕上料１を用意した。On the other hand, the finishing material 1 produced in Example 1 was prepared as a makeup finishing material for the second layer.
【００３７】[0037]
【比較例２】第一層用のメークアップ下地料として実施
例１で製造した下地料１を用意した。Comparative Example 2 The base material 1 produced in Example 1 was prepared as a makeup base material for the first layer.
【００３８】一方、表５に示す粉体成分Ａ及び油剤成分
Ｂを用いて実施例１と同様な方法で第二層用のメークア
ップ仕上料（パウダーファンデーション）（以下、仕上
料３という）を製造した。On the other hand, by using the powder component A and the oil agent component B shown in Table 5, a make-up finish (powder foundation) for the second layer (hereinafter referred to as finish 3) was prepared in the same manner as in Example 1. Manufactured.
【００３９】[0039]
【表５】 [Table 5]
【００４０】[0040]
【比較例３】第一層用のメークアップ下地料として実施
例３で製造した下地料２を用意し、また第二層用のメー
クアップ仕上料として比較例２で製造した仕上料３を用
意した。[Comparative Example 3] The base material 2 prepared in Example 3 was prepared as the make-up base material for the first layer, and the finish material 3 prepared in Comparative Example 2 was prepared as the make-up finish material for the second layer. did.
【００４１】[0041]
【比較例４】第一層用のメークアップ下地料として比較
例１で製造した下地料３を用意し、また第二層用のメー
クアップ仕上料として比較例２で製造した仕上料３を用
意した。[Comparative Example 4] The base material 3 prepared in Comparative Example 1 was prepared as the make-up base material for the first layer, and the finish material 3 prepared in Comparative Example 2 was prepared as the make-up finish material for the second layer. did.
【００４２】＜本発明の紫外線防護用重層化粧料の評価
＞次に、以上のようにして得られたメークアップ化粧料
について紫外線をカットする効果とその持続力、耐水
性、耐物理的刺激性について評価した。<Evaluation of Multilayer Cosmetics for UV Protection of the Present Invention> Next, the effect of blocking ultraviolet rays and the durability, water resistance and physical irritation resistance of the makeup cosmetics obtained as described above. Was evaluated.
【００４３】（１）紫外線カット効果 紫外線カット効果の指標として、ＳＰＦ（サン・プロテ
クション・ファクター(Sun protection factor)：日焼
け止め指数）を測定した。ＳＰＦは、ヒトの皮膚に紫外
線カット剤を塗布して紫外線を照射し、紫外線カット成
分を使用しない場合に対して皮膚に同等の炎症を起こさ
せる照射エネルギー量（時間）の比で表すものである。
方法は、日本化粧品工業連合会ＳＰＦ測定法基準に準じ
て行った。(1) UV Protection Effect As an index of UV protection effect, SPF (Sun protection factor) was measured. SPF is a ratio of the amount of irradiation energy (time) that applies an ultraviolet ray-cutting agent to human skin and irradiates it with ultraviolet rays, and causes the skin to be inflamed to the same level as in the case where no ultraviolet ray-cutting component is used. .
The method was performed according to the Japan Cosmetic Industry Federation SPF measurement method standard.
【００４４】８％のホモサレート（３，３，５−トリメ
チルシクロヘキシルサリチレート）を含有したＯ／Ｗ型
エマルジョン（ＳＰＦ＝４．０）を標準として、２０人
以上の被験者（皮膚タイプＩ、ＩＩ、またはＩＩＩ）の
背中の５０ｃｍ2以上の部分に２ｍｇ／ｃｍ2または２μ
ｌ／ｃｍ2の割合で、実施例及び比較例の下地料及び仕
上料を重層し、ソーラーシミュレーターで、未塗布時の
最小照射量×（１．２５n）の割合で増量して照射し、
２４時間後に下記式により最小紅斑量ＭＥＤ（肉眼で見
える微かな紅斑を生じる最小のエネルギー量または照射
時間）を測定、算出した。With an O / W type emulsion (SPF = 4.0) containing 8% homosalate (3,3,5-trimethylcyclohexyl salicylate) as a standard, 20 or more test subjects (skin type I, II , Or III), 2 mg / cm 2 or 2μ on 50 cm 2 or more of the back
The base material and the finishing material of Examples and Comparative Examples were layered at a ratio of 1 / cm 2 , and a solar simulator was used to increase the irradiation amount at a minimum irradiation amount × (1.25 n ) when not applied, and irradiation was performed.
After 24 hours, the minimum erythema dose MED (minimum energy amount or irradiation time that produces a slight erythema visible to the naked eye) was measured and calculated by the following formula.
【００４５】ＳＰＦ＝（化粧料を使用した皮膚でのＭＥ
Ｄ）／（化粧料を使用しない皮膚でのＭＥＤ）SPF = (ME on skin using cosmetics
D) / (MED on skin without cosmetics)
【００４６】（２）紫外線カット効果の持続性 上記（１）の方法で下地料及び仕上げ料を塗布した後、
３０℃、湿度７０％の環境試験室に３時間入室後、同室
内にて上記と同様にＳＰＦを測定した。(2) Persistence of UV blocking effect After applying the base material and the finishing material by the method of (1) above,
After entering the environment test room at 30 ° C. and 70% humidity for 3 hours, the SPF was measured in the same room as above.
【００４７】（３）耐水性 （１）と同様の方法で下地料及び仕上げ料を塗布した
後、水道水で１０回背中を指でこすりながら洗滌した
後、水分をタオルで軽くふき取り、５分後に同様にＳＰ
Ｆを測定した。(3) Water resistance After applying a base material and a finishing material in the same manner as in (1), washing with tap water 10 times while rubbing the back with fingers, lightly wipe the water with a towel for 5 minutes. Later SP as well
F was measured.
【００４８】（４）耐物理的刺激性 （１）と同様の方法で下地料及び仕上げ料を塗布した
後、５分後に乾いたティッシュペーパーで１０回こすっ
た後、同様にＳＰＦを測定した。(4) Physical irritation resistance After applying a base material and a finishing material in the same manner as in (1), after 5 minutes, rubbing with dry tissue paper 10 times and then measuring SPF in the same manner.
【００４９】以上、評価（１）〜（４）の結果を表６に
示す。Table 6 shows the results of evaluations (1) to (4).
【００５０】[0050]
【表６】 [Table 6]
【００５１】以上の結果から、本発明の紫外線防護用重
層化粧料は、比較例に比べて、紫外線をカットする効果
及びその持続性、耐水性、耐物理的刺激性のいずれにお
いても優れていることが明らかである。From the above results, the multilayer cosmetic for ultraviolet protection of the present invention is superior to the comparative example in the effect of blocking ultraviolet rays and its durability, water resistance and physical irritation resistance. It is clear.
【００５２】[0052]
【発明の効果】本発明の紫外線防護用重層化粧料は、紫
外線をカットする効果に優れている上、その効果の持続
性、耐水性、耐物理的刺激性等においても優れている。INDUSTRIAL APPLICABILITY The multilayer cosmetic for protecting ultraviolet rays of the present invention is excellent in the effect of blocking ultraviolet rays, and is also excellent in the durability of the effect, water resistance, physical irritation resistance and the like.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ａ６１Ｋ 7/02 Ｎ 7252−4Ｃ Ｍ 7252−4Ｃ Ｐ 7252−4Ｃ 7/44 7252−4Ｃ Ｃ０９Ｋ 3/00 １０４ 8517−4Ｈ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Office reference number FI Technical display location A61K 7/02 N 7252-4C M 7252-4C P 7252-4C 7/44 7252-4C C09K 3 / 00 104 8517-4H
Claims (4)
ップ下地料と、紫外線カット効果を有する第二層用メー
クアップ仕上料とを組合せた紫外線防護用重層化粧料。1. A multilayer cosmetic for UV protection comprising a combination of a make-up base material for a first layer containing an adhesive substance and a make-up finish for a second layer having an ultraviolet blocking effect.
Ｚ−０２３７に規定される方法で試験したとき、下記
性能 タック：５〜２０ 粘着力（ステンレス板）：５００〜２０００ｇ／２５ｍ
ｍ を有することを特徴とする請求項１記載の紫外線防護用
重層化粧料。2. The adhesive material is JIS as an adhesive tape.
When tested by the method specified in Z-0237, the following performance tack: 5-20 Adhesive force (stainless steel plate): 500-2000 g / 25 m
The multilayer cosmetic for ultraviolet protection according to claim 1, which has m 2.
クアップ仕上料が、下記（Ａ）又は／及び（Ｂ）の成分
を含むことを特徴とする請求項１記載の紫外線防護用重
層化粧料。 （Ａ）酸化チタン、微粒子酸化チタン、酸化チタン被覆
雲母、酸化チタン被覆セリサイト、酸化チタン被覆タル
ク、酸化鉄被覆雲母、酸化鉄被覆セリサイト、酸化鉄被
覆タルク、酸化鉄、二酸化亜鉛から選ばれる少なくとも
１種、 （Ｂ）パラメトキシケイ皮酸オクチル、２−エチルヘキ
シルパラジメチルアミノベンゾエート、オキシベンゾ
ン、ウロカニン酸、４−ｔｅｒｔ−ブチル−４’−メト
キシ−ジベンゾイルメチルから選ばれる少なくとも１種
を、ポリエチレンビーズ、ナイロンパウダー、シリコー
ンパウダー、メタクリル酸メチルパウダー、シリカパウ
ダー、ケイ酸マグネシウム粉末、ケイ酸カルシウム粉末
から選ばれる少なくとも１種に内包あるいは含浸させた
もの。3. The multilayer cosmetic for UV protection according to claim 1, wherein the make-up finish for the second layer having the UV blocking effect contains the following components (A) and / or (B). . (A) Titanium oxide, fine particle titanium oxide, titanium oxide-coated mica, titanium oxide-coated sericite, titanium oxide-coated talc, iron oxide-coated mica, iron oxide-coated sericite, iron oxide-coated talc, iron oxide, zinc dioxide At least one selected from the group consisting of (B) octyl paramethoxycinnamate, 2-ethylhexylparadimethylaminobenzoate, oxybenzone, urocanic acid, and 4-tert-butyl-4′-methoxy-dibenzoylmethyl is polyethylene. Encapsulated or impregnated with at least one selected from beads, nylon powder, silicone powder, methyl methacrylate powder, silica powder, magnesium silicate powder, and calcium silicate powder.
び（Ｂ）の成分の含有量が、メークアップ仕上料全量に
対し１〜９０重量％であることを特徴とする紫外線防護
用重層化粧料。4. The ultraviolet protection multilayer according to claim 3, wherein the content of the component (A) or / and (B) is 1 to 90% by weight based on the total amount of the makeup finishing agent. Cosmetics.