JPH06127968A - Glass fiber spinning furnace - Google Patents
Glass fiber spinning furnaceInfo
- Publication number
- JPH06127968A JPH06127968A JP30459692A JP30459692A JPH06127968A JP H06127968 A JPH06127968 A JP H06127968A JP 30459692 A JP30459692 A JP 30459692A JP 30459692 A JP30459692 A JP 30459692A JP H06127968 A JPH06127968 A JP H06127968A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- glass fiber
- fiber spinning
- spinning furnace
- basket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ガラス繊維紡糸炉に関
し、特に失透し易いガラスを繊維化するのに好適なガラ
ス繊維紡糸炉に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a glass fiber spinning furnace, and more particularly to a glass fiber spinning furnace suitable for fiberizing glass that is easily devitrified.
【０００２】[0002]
【従来の技術】一般に少量多品種のガラス長繊維を生産
する場合、まずガラス原料を溶融炉内で溶融し、マーブ
ルや水砕物等となるように成形した後、このガラス成形
体を紡糸炉に投入して再溶融してから紡糸する方式、す
なわち間接溶融法と呼ばれる方式が採られる。2. Description of the Related Art Generally, in the case of producing a large amount of various kinds of glass long fibers, first, a glass raw material is melted in a melting furnace and molded into a marble or a water granulated product, and then this glass molded body is put into a spinning furnace. A method in which the material is charged, remelted, and then spun, that is, a method called an indirect melting method is adopted.
【０００３】この間接溶融法に用いられる紡糸炉は、上
方にガラス成形体を投入する投入口が形成された溶融漕
と、この溶融漕の底部に取り付けられ、再溶融されたガ
ラスを紡糸するためのブッシングから主に構成されてい
る。The spinning furnace used in this indirect melting method is for spinning a remelted glass attached to the bottom of the melting tank and the melting tank in which a charging port for charging the glass molding is formed above. It is mainly composed of bushings.
【０００４】このような溶融漕やブッシングは、高温に
耐える必要があるため、耐蝕性に優れた白金合金から主
に作製され、それらの側部には通電加熱するためのター
ミナルが取り付けられており、これによって投入された
ガラス成形体が再溶融されるようになっている。Since such a melt bath or bushing is required to withstand high temperatures, it is mainly made of a platinum alloy having excellent corrosion resistance, and terminals for electrically heating are attached to the side portions thereof. As a result, the glass molded body charged is remelted.
【０００５】[0005]
【発明が解決しようとする課題】ところで一般にガラス
長繊維を製造する場合、ガラスの紡糸温度（１０3 ポイ
ズの粘度を有する温度）と液相温度の差が１００℃以上
であると、溶融工程においてガラスが失透し難く、繊維
化が容易であると言われている。Generally, in the production of long glass fibers, when the difference between the spinning temperature of glass (the temperature having a viscosity of 10 3 poise) and the liquidus temperature is 100 ° C. or more, the melting step is performed. It is said that the glass is hard to devitrify and is easily made into fibers.
【０００６】しかしながらガラス長繊維には、用途に応
じて特性の異なる各種の繊維が存在し、その中には紡糸
温度と液相温度の差が１００℃以下のガラスからなるも
のがあり、このようなガラスの原料バッチを溶融し、マ
ーブルや水砕物等のガラス成形体を作製した後、このガ
ラス成形体を上記のような紡糸炉に投入し再溶融する
と、投入口付近に失透物が生成し易い。失透物が生成す
ると、失透物によって投入口が塞がれたり、あるいは失
透物が未溶解のままブッシングに達し、ノズル詰まりや
糸の切断を引き起こし、生産性が著しく低下する。However, there are various types of long glass fibers having different characteristics depending on the use, and some of them are made of glass having a difference in spinning temperature and liquidus temperature of 100 ° C. or less. After melting a raw material batch of various glass and producing glass moldings such as marble and granulated material, when this glass molding is put into the spinning furnace as described above and remelted, devitrified matter is formed near the charging port. Easy to do. When the devitrified substance is generated, the devitrified substance blocks the charging port, or the devitrified substance reaches the bushing without being melted, which causes nozzle clogging and yarn cutting, resulting in a marked decrease in productivity.
【０００７】本発明は、上記事情に鑑みなされたもので
あり、紡糸温度と液相温度の差が１００℃以下で、失透
し易いガラス成形体を再溶融しても、投入口付近で失透
物が生成することのないガラス繊維紡糸炉を提供するこ
とを目的とするものである。The present invention has been made in view of the above circumstances, and when the difference between the spinning temperature and the liquidus temperature is 100 ° C. or less, even if the glass molded body which is easily devitrified is remelted, it is lost near the charging port. An object of the present invention is to provide a glass fiber spinning furnace that does not generate a transparent material.
【０００８】[0008]
【課題を解決するための手段】本発明者は、上記目的を
達成すべく種々の研究を重ねた結果、ガラスの失透物が
生成する理由は、紡糸炉の投入口から投入されたガラス
成形体によって、投入口付近の溶融ガラスが冷却される
ためであり、このような失透物の生成を防止するために
は、投入口付近の溶融ガラスの温度制御を行うことが必
要であるという知見に基づいて、本発明を提案するに至
った。The inventors of the present invention have conducted various studies to achieve the above object, and as a result, a devitrified substance of glass is formed. The reason for forming the glass is as follows. This is because the body cools the molten glass in the vicinity of the charging port, and it is necessary to control the temperature of the molten glass in the vicinity of the charging port in order to prevent the formation of such devitrified substances. Based on the above, the present invention has been proposed.
【０００９】すなわち本発明のガラス繊維紡糸炉は、上
方にガラス成形体を投入する投入口が形成された溶融漕
と、該溶融漕の底部に取り付けられ、再溶融されたガラ
スを紡糸するためのブッシングを備えてなるガラス繊維
紡糸炉において、投入されたガラス成形体を滞留させ、
加熱するためのバスケット状加熱ヒーターが、投入口に
設置されてなることを特徴とする。That is, the glass fiber spinning furnace of the present invention is provided with a melting tank having a charging port for charging a glass molded body formed above, and for spinning remelted glass attached to the bottom of the melting tank. In a glass fiber spinning furnace equipped with a bushing, the charged glass molding is retained,
A basket-shaped heater for heating is installed at the charging port.
【００１０】また本発明のガラス繊維紡糸炉は、溶融ガ
ラスの液面レベルを測定するための熱電対が、バスケッ
ト状加熱ヒーターの上方に位置するように取り付けられ
てなることを特徴とする。Further, the glass fiber spinning furnace of the present invention is characterized in that a thermocouple for measuring the liquid surface level of the molten glass is attached so as to be located above the basket heater.
【００１１】[0011]
【作用】本発明におけるガラス繊維紡糸炉は、投入口に
バスケット状加熱ヒーターが設置されてなるため、投入
されたガラス成形体は、加熱ヒーター内部で一旦滞留
し、ここでほぼ再溶融されてから溶融漕に入る。従って
本発明のガラス繊維紡糸炉では、すでに溶融炉内で再溶
融されているガラスが、投入されるガラス成形体によっ
て冷却されることはなく、失透物の生成が防止される。In the glass fiber spinning furnace according to the present invention, the basket-shaped heater is installed at the charging port. Therefore, the charged glass molded body temporarily stays inside the heating heater and is almost re-melted here. Enter the melting tank. Therefore, in the glass fiber spinning furnace of the present invention, the glass that has already been remelted in the melting furnace is not cooled by the glass molded body that is charged, and the formation of devitrified substances is prevented.
【００１２】本発明において使用するバスケット状加熱
ヒーターは、耐蝕性に優れた白金あるいは白金合金から
作製され、ガラス成形体を滞留し、しかも投入口内部に
取り付けることが可能な形状を有するものであればいず
れも使用可能であり、例えば有底無蓋の箱型形状を有
し、その底部に多数の小孔が穿孔された形状を有し、そ
の両端にターミナルを取り付けた形態のものが考えられ
る。The basket-shaped heater used in the present invention is made of platinum or a platinum alloy having excellent corrosion resistance, and has a shape capable of retaining a glass molded body and mounting the glass molded body inside the charging port. Any of them can be used, for example, a box-like shape with a bottom and no lid, a shape in which a large number of small holes are perforated at the bottom thereof, and a form in which terminals are attached to both ends thereof can be considered.
【００１３】また図２に示すように、長方形状の白金あ
るいは白金合金の２ケ所を折り曲げて断面がコの字型と
なるように加工し、その中央面を穿孔することによっ
て、多数の小孔１０ａが形成された底部１０ｂと、その
両端に続く一対の側部１０ｃ、１０ｃを備えたバスケッ
トを作製し、その側部１０ｃ、１０ｃの上端に板状のタ
ーミナル１０ｄ、１０ｄを溶接によって取り付けたバス
ケット状加熱ヒーター１０を使用することも可能であ
る。Further, as shown in FIG. 2, two rectangular holes of platinum or platinum alloy are bent and processed to have a U-shaped cross section, and the central surface thereof is perforated to form a large number of small holes. A basket having a bottom portion 10b formed with a portion 10a and a pair of side portions 10c and 10c connected to both ends thereof is manufactured, and plate-shaped terminals 10d and 10d are attached to the upper ends of the side portions 10c and 10c by welding. It is also possible to use the flat heater 10.
【００１４】また本発明においては、バスケット状加熱
ヒーターを、その底部が紡糸炉内の溶融ガラスに浸漬す
るように取り付けるが、溶融ガラスの液面レベルを測定
するための熱電対をバスケット状加熱ヒーターの上方に
取り付けると、ガラス成形体を投入するタイミングが計
れるため好ましい。Further, in the present invention, the basket heater is attached so that the bottom thereof is immersed in the molten glass in the spinning furnace, but a thermocouple for measuring the liquid level of the molten glass is used as the basket heater. It is preferable to attach the glass molded body above the glass molded body because the timing of charging the glass molded body can be measured.
【００１５】すなわち紡糸炉内にガラス成形体を投入す
ると、溶融ガラスの液面レベルが上昇し、ガラスが紡糸
されるに伴って徐々に液面レベルは下降するが、熱電対
の先端部を液面レベルの高低によって浸漬したり、しな
かったりするように取り付けることによって、一定の液
面レベル以下になると、熱電対の先端部が溶融ガラスと
非接触状態となり、温度の測定値が低下することになる
ため、その時にガラス成形体の投入を行うようにすれば
良い。That is, when the glass molding is put into the spinning furnace, the liquid level of the molten glass rises, and the liquid level gradually decreases as the glass is spun. When the liquid level is below a certain level by mounting it so that it may or may not be immersed depending on the level of the surface level, the tip of the thermocouple may not be in contact with the molten glass and the measured temperature value may drop. Therefore, the glass molded body may be charged at that time.
【００１６】[0016]
【実施例】以下、本発明のガラス繊維紡糸炉を実施例に
基づいて詳細に説明する。EXAMPLES The glass fiber spinning furnace of the present invention will be described in detail below based on examples.
【００１７】図１は、本発明に係るガラス繊維紡糸炉１
１の縦断面図を示すものである。FIG. 1 shows a glass fiber spinning furnace 1 according to the present invention.
1 is a vertical sectional view of FIG.
【００１８】紡糸炉１１は、白金−ロジウム合金からな
る溶融漕１２とブッシング１３を備えており、溶融漕１
２は、その側部に取り付けられたターミナル１２ａ、１
２ａによって通電加熱され、内部のガラスが溶融される
ようになっている。またブッシング１３の側部にもター
ミナル１３ａ、１３ａが取り付けられ、通電加熱されて
おり、これによって溶融ガラスＧが紡糸されるのに適し
た温度に保たれている。溶融漕１２とブッシング１３の
間隙には、耐火物１６が介在し、これによって両者は絶
縁され、またブッシング１３の底部には、４００個のノ
ズル１３ｂが形成されており、各ノズル１３ｂからガラ
スが紡糸されている。The spinning furnace 11 is equipped with a melting tank 12 and a bushing 13 made of a platinum-rhodium alloy.
2 is a terminal 12a, 1 attached to the side thereof
2a is electrically heated to melt the glass inside. Terminals 13a, 13a are also attached to the side portions of the bushing 13 and are electrically heated to maintain the temperature suitable for spinning the molten glass G. A refractory material 16 is interposed in the gap between the melting bath 12 and the bushing 13 to insulate them from each other, and 400 nozzles 13b are formed at the bottom of the bushing 13, and the glass is discharged from each nozzle 13b. It is spun.
【００１９】溶融漕１２の上方には、投入口１２ｂが形
成され、この投入口１２ｂには、ターミナル１０ｄ、１
０ｄによって通電加熱されているバスケット状加熱ヒー
ター１０が取り付けられている。バスケット状加熱ヒー
ター１０は、図２に示すような形態を有しており、その
底部１０ｂには、直径約６ｍｍの小孔が多数形成され、
しかも溶融ガラスＧに浸漬した状態になっている。さら
に溶融漕１２とバスケット状加熱ヒーター１０の間隙に
は、耐火物１７が介在し、これによって両者は絶縁され
ている。A charging port 12b is formed above the melting tank 12, and terminals 10d, 1 and 1 are provided in the charging port 12b.
A basket-shaped heater 10 which is electrically heated by 0d is attached. The basket-shaped heater 10 has a form as shown in FIG. 2, and a large number of small holes having a diameter of about 6 mm are formed in the bottom portion 10b thereof.
Moreover, it is in a state of being immersed in the molten glass G. Further, a refractory material 17 is interposed in the gap between the melting tank 12 and the basket-shaped heater 10 to insulate them from each other.
【００２０】また溶融漕１２の投入口１２ｂには、溶融
ガラスＧの液面レベルを測定するための熱電対１８が挿
入され、その先端部がバスケット状加熱ヒーター１０の
底部１０ｂの上方に位置するように取り付けられてい
る。Further, a thermocouple 18 for measuring the liquid level of the molten glass G is inserted into the charging port 12b of the melting tank 12, and its tip is located above the bottom 10b of the basket-shaped heater 10. Is installed as.
【００２１】熱電対１８は、耐火物製の中空棒の内部に
温度計が挿入されたものであり、溶融ガラスＧの液面レ
ベルの移動によって、溶融ガラスＧと接触したり、接触
しなかったりするように取り付けられている。The thermocouple 18 is a hollow rod made of refractory having a thermometer inserted therein, and may or may not come into contact with the molten glass G depending on the movement of the liquid level of the molten glass G. It is installed so that
【００２２】紡糸温度と液相温度との差が約４０℃であ
るガラスの原料バッチを溶融し、水砕することによって
作製したガラス成形体を、上記の紡糸炉１１を用いて再
溶融したところ、投入口１２ｂ付近で失透物が生成する
ことはなく、良好にガラス長繊維を生産することができ
た。A glass molded body produced by melting a raw material batch of glass having a difference between the spinning temperature and the liquidus temperature of about 40 ° C. and granulating the same was remelted using the above spinning furnace 11. Further, devitrified matter was not generated in the vicinity of the charging port 12b, and the long glass fiber could be satisfactorily produced.
【００２３】[0023]
【発明の効果】以上のように本発明のガラス繊維紡糸炉
を用いて、紡糸温度と液相温度の差が１００℃以下で、
失透しやすいガラスを溶融しても、投入口付近で失透物
が生成することがなく、高い効率でガラス長繊維を生産
することが可能である。As described above, using the glass fiber spinning furnace of the present invention, the difference between the spinning temperature and the liquidus temperature is 100 ° C. or less,
Even if glass that is easily devitrified is melted, devitrified substances are not generated near the charging port, and it is possible to produce long glass fibers with high efficiency.
【図１】本発明のガラス繊維紡糸炉の縦断面図である。FIG. 1 is a longitudinal sectional view of a glass fiber spinning furnace of the present invention.
【図２】バスケット状加熱ヒーターの斜視図である。FIG. 2 is a perspective view of a basket-shaped heater.
１０ バスケット状加熱ヒーター １１ ガラス繊維紡糸炉 １２ 溶融漕 １２ｂ 投入口 １３ ブッシング １８ 熱電対 Ｇ 溶融ガラス 10 Basket-shaped heater 11 Glass fiber spinning furnace 12 Melting tank 12b Input port 13 Bushing 18 Thermocouple G Molten glass
Claims (2)
形成された溶融漕と、該溶融漕の底部に取り付けられ、
再溶融されたガラスを紡糸するためのブッシングとから
なるガラス繊維紡糸炉において、投入されたガラス成形
体を滞留させ、加熱するためのバスケット状加熱ヒータ
ーが、投入口に設置されてなることを特徴とするガラス
繊維紡糸炉。1. A melting tank having a charging port for charging a glass molded body formed above, and attached to the bottom of the melting tank,
In a glass fiber spinning furnace consisting of a bushing for spinning the remelted glass, a basket-shaped heating heater for retaining and heating the charged glass molding is provided at the charging port. And a glass fiber spinning furnace.
の熱電対が、バスケット状加熱ヒーターの上方に位置す
るように取り付けられてなることを特徴とする請求項１
のガラス繊維紡糸炉。2. A thermocouple for measuring the liquid level of the molten glass is attached so as to be located above the basket heater.
Glass fiber spinning furnace.