JPH057538A - Filter paper for dust collecting bag of vacuum cleaner - Google Patents
Filter paper for dust collecting bag of vacuum cleanerInfo
- Publication number
- JPH057538A JPH057538A JP16258191A JP16258191A JPH057538A JP H057538 A JPH057538 A JP H057538A JP 16258191 A JP16258191 A JP 16258191A JP 16258191 A JP16258191 A JP 16258191A JP H057538 A JPH057538 A JP H057538A
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- dust
- filter paper
- vacuum cleaner
- wood pulp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は電気掃除機に装着して用
いる集塵袋用ろ紙に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a filter paper for a dust bag used by being attached to an electric vacuum cleaner.
【０００２】[0002]
【従来の技術】近年、使い捨て集塵袋を用いた電気掃除
機がごみ処理の簡便さと微細なごみの捕捉性の良さから
広く普及しつつある。従来、この種の掃除機に用いられ
る集塵袋用ろ紙には、木材パルプ、麻パルプ、ガラス繊
維、通常デニール（１デニール（ｄ）以上）の合成ある
いは再生繊維及び少量のＰＶＡ系バインダー繊維よりな
る紙が用いられている。2. Description of the Related Art In recent years, electric vacuum cleaners using disposable dust collection bags have become widely used due to their ease of dust disposal and their ability to capture fine dust. Conventionally, filter paper for dust collecting bags used in this type of vacuum cleaner includes wood pulp, hemp pulp, glass fiber, synthetic or regenerated fiber of normal denier (1 denier (d) or more) and a small amount of PVA binder fiber. Is used.
【０００３】かかる集塵袋用ろ紙は、扁平な木材パルプ
や麻パルプによる目詰まりしやすい構造を１ｄ以上の合
成あるいは再生繊維を配合することにより広げて捕集効
率（集塵率）と圧力損失（通気度）とをバランスさせ、
さらに麻パルプとＰＶＡ系バインダー繊維を配合するこ
とにより紙に強力を付与しようとするものである。The filter paper for such a dust bag expands the structure that is easily clogged with flat wood pulp or hemp pulp by blending synthetic or regenerated fibers of 1 d or more to collect efficiency (dust collection rate) and pressure loss. (Air permeability) and balance,
Furthermore, the hemp pulp and the PVA-based binder fiber are blended to impart strength to the paper.
【０００４】[0004]
【発明が解決しようとする課題】しかしながらかかる集
塵袋用ろ紙は、用いる木材パルプ、麻パルプ、合成ある
いは再生繊維の繊度がいずれも大きく、構成本数の少な
い割には木材パルプ及び麻パルプの扁平効果により捕集
効率は良いものの、圧力損失が大きいという欠点があ
る。However, such filter bags for dust collecting bags have a large fineness of wood pulp, hemp pulp, synthetic or regenerated fibers to be used, and the flatness of the wood pulp and the hemp pulp is small despite the small number of constituents. Although the collection efficiency is good due to the effect, there is a drawback that the pressure loss is large.
【０００５】更に、使い捨て集塵袋は安価であることが
重要であるが、木材パルプ及び麻パルプの目詰り構造を
広げる合成あるいは再生繊維を多量に用いる為に高価に
なるという問題があり、かかるタイプの電気掃除機が快
適な環境と便利さを提供する割には、普及速度が遅いと
いわれる一因になっている。Further, it is important that the disposable dust collecting bag is inexpensive, but there is a problem in that it is expensive because a large amount of synthetic or recycled fiber is used to expand the clogging structure of wood pulp and hemp pulp. This type of vacuum cleaner contributes to the slow spread of the vacuum cleaner while providing a comfortable environment and convenience.
【０００６】従って本発明の目的は、集塵率，通気性及
び強度のいずれにおいても優れ、しかもコストの安価な
使い捨ての為の電気掃除機集塵袋用ろ紙を提供すること
にある。Therefore, an object of the present invention is to provide a filter paper for an electric vacuum cleaner dust bag, which is excellent in all of dust collection rate, air permeability and strength, and is low in cost.
【０００７】[0007]
【問題点を解決する手段】本発明者は、上記の目的を達
成すべく鋭意研究した結果、マーセライズ化された木材
パルプと極細デニールの合成あるいは再生繊維とを特定
の割合で配合するとともに、繊維充填密度（単位容積当
りに占める繊維分の容積）を特定範囲に規定することに
より、集塵率と通気性をバランスさせることができ、更
に熱融着性複合繊維の使用により通気性の低下を招くこ
となく強度を付与できることを見出し本発明を完成させ
たものである。Means for Solving the Problems As a result of intensive studies to achieve the above object, the present inventor has blended a mercerized wood pulp and an ultrafine denier synthetic or recycled fiber in a specific ratio and By setting the packing density (volume of fiber content per unit volume) within a specific range, it is possible to balance the dust collection rate and air permeability. Furthermore, the use of heat-fusible composite fibers reduces air permeability. The present invention has been completed to find that strength can be imparted without inviting.
【０００８】すなわち本発明の電気掃除機集塵袋用ろ紙
は、１デニール未満の合成あるいは再生繊維５〜２０重
量％、２デニール以下の熱融着性複合繊維２０〜５０重
量％、木材パルプ１０〜６５重量％、マーセル化木材パ
ルプ１０〜３０重量％よりなり、坪量３０〜１００ｇ／
ｍ2 、繊維充填密度（単位容積当りに占める繊維分の容
積）０．２〜０．４cm3 ／cm3 としたことを特徴とする
ものである。That is, the filter paper for the vacuum cleaner dust-collecting bag of the present invention comprises 5 to 20% by weight of synthetic or regenerated fiber having a denier of less than 1 to 20% to 50% by weight of heat-fusible composite fiber of 2 denier or less, and 10% of wood pulp. ~ 65 wt%, mercerized wood pulp 10-30 wt%, basis weight 30-100 g /
m 2, and characterized in that it has a (fiber content of volume occupied per unit volume) 0.2~0.4cm 3 / cm 3 fiber packing density.
【０００９】上述したごとき本発明の集塵袋用ろ紙によ
れば、下記 (1)〜(4) のごとき作用効果が得られる。 (1) 木材パルプ（例えばＮＢＫＰ及びマーセル化ＮＢＫ
Ｐ）を主体としているので安価である。 (2) 繊度が小さい為、単位重量当たりの繊維本数が多
く、直径の小さい細デニールの合成あるいは再生繊維を
用いること及びマーセル化木材パルプを用いることによ
り、木材パルプの目詰り構造が適度に広げられ、かつか
かる繊維同志あるいはパルプとマーセル化木材バルプと
の間により形成される多数の立体的構造を持った小さな
網目によって微細塵の捕捉力を高めかつ初期圧力損失も
小さい。 (3) 熱融着性複合繊維が合成あるいは再生繊維やパルプ
との交差点を有効に接着する為に強度が高く、通気性が
高い。 (4) 繊維充填密度を特定の範囲にしたことにより、微細
塵の捕捉力が高い。According to the filter paper for the dust collecting bag of the present invention as described above, the following operational effects (1) to (4) can be obtained. (1) Wood pulp (eg NBKP and mercerized NBK
Since it is mainly based on P), it is inexpensive. (2) Since the fineness is small, the number of fibers per unit weight is large, and by using fine denier synthetic or regenerated fibers with a small diameter and by using mercerized wood pulp, the clogging structure of the wood pulp is appropriately expanded. In addition, the small mesh having a large number of three-dimensional structures formed between the fibers or pulp and the mercerized wood valp enhances the capturing power of fine dust and the initial pressure loss is small. (3) Since the heat-fusible composite fiber effectively adheres to the intersection of the synthetic or regenerated fiber and the pulp, it has high strength and high air permeability. (4) By setting the fiber packing density within a specific range, the ability to capture fine dust is high.
【００１０】本発明においては、木材パルプ、マーセル
化木材パルプ，細デニールの合成あるいは再生繊維、熱
融着性複合繊維を特定の割合で配合するとともに、坪量
と繊維充填密度を特定の範囲にすることが、所期の目的
を達成するために不可欠であるが、細デニールの合成あ
るいは再生繊維の太さ及び配合量とマーセル化木材パル
プの配合量が最も重要なポイントとなるものである。In the present invention, wood pulp, mercerized wood pulp, synthetic or regenerated fibers of fine denier, and heat-fusible composite fibers are blended in a specific ratio, and the basis weight and the fiber packing density are adjusted to specific ranges. It is essential to achieve the intended purpose, but the thickness and blending amount of fine or fine denier synthetic or regenerated fiber and the blending amount of mercerized wood pulp are the most important points.
【００１１】細デニールの合成あるいは再生繊維の繊度
は１ｄ未満であり、好ましくは０．５ｄ程度である。１
ｄ以上になると微細塵の捕捉能力が著しく低下する。ま
たこの細デニールの合成あるいは再生繊維の配合量は５
〜２０％（重量％、以下同じ）である。５％未満では細
デニールの合成あるいは再生繊維の本数が少なくなって
しまうためその効果が現れない。又、２０％を越える
と、本来なら捕集効率が高く圧力損失の小さい集塵袋用
ろ紙が得られるはずであるが、細デニールの合成あるい
は再生繊維の量が多すぎ地合むらができてろ過性能のバ
ラツキが多くなり、商品価値が低下するため好ましくな
く、更に高価にもなる。繊維長は１〜６mm、好ましくは
３〜５mmのものが使用できる。The fineness of fine denier synthetic or regenerated fibers is less than 1d, preferably about 0.5d. 1
If it is more than d, the ability to capture fine dust is significantly reduced. In addition, the amount of synthetic or recycled fiber of this fine denier is 5
20% (% by weight, the same applies hereinafter). If it is less than 5%, the effect does not appear because the number of fine denier synthetic or regenerated fibers decreases. On the other hand, if it exceeds 20%, it should be possible to obtain a filter paper for a dust bag having a high collection efficiency and a small pressure loss, but the fine denier synthesis or the amount of regenerated fiber is too large and uneven texture is formed. It is not preferable because it causes a large variation in filtration performance, which lowers the commercial value, and is also expensive. A fiber having a fiber length of 1 to 6 mm, preferably 3 to 5 mm can be used.
【００１２】かかる細デニールの合成あるいは再生繊維
としては、ＰＶＡ系繊維、ポリアクリロニトリル系繊
維、ポリエステル系繊維、ポリアミド系繊維、レーヨン
等の再生繊維、ガラス繊維等の無機繊維があげられる
が、これらに限定されるものではない。又、断面形状も
問はないし、捲縮の有無も問はない。特に好ましい例
は、ポリエステル繊維であり、後述する熱融着性複合繊
維として好ましく使用される芯部ポリエチレンテレフタ
レート／鞘部変性ポリエステル熱融着性複合繊維との親
和性が良い為、強度が強く微細塵の捕捉力の高い集塵袋
用ろ紙が得られる。Examples of such fine denier synthetic or regenerated fibers include PVA fibers, polyacrylonitrile fibers, polyester fibers, polyamide fibers, regenerated fibers such as rayon, and inorganic fibers such as glass fibers. It is not limited. The cross-sectional shape does not matter, and the presence or absence of crimps does not matter. A particularly preferable example is a polyester fiber, which has a strong affinity with the core polyethylene terephthalate / sheath modified polyester heat-fusible conjugate fiber which is preferably used as the heat-fusible conjugate fiber described later, and therefore has high strength and fineness. A filter paper for a dust bag having a high dust trapping power can be obtained.
【００１３】熱融着性複合繊維の繊度は、２ｄ以下であ
る。これよりより大きくなると、微細塵の捕捉能力が著
しく低下する。又、熱融着性複合繊維の配合量は２０％
〜５０％でなければならない。２０％未満では、熱融着
性複合繊維の本数が少なく、繊維間の交差点を有効に接
着することができず、強度の発現が低くなる。一方、５
０％より多いと強度は向上するものの、バインダー皮膜
を形成し、圧力損失が著しく大きくなり好ましくない。
繊維長は１〜６mm、好ましくは３〜５mmのものが使用で
きる。The fineness of the heat-fusible composite fiber is 2d or less. If it is larger than this, the ability to capture fine dust is significantly reduced. The blending amount of the heat-fusible composite fiber is 20%.
Must be ~ 50%. When it is less than 20%, the number of the heat-fusible composite fibers is small, the crossing points between the fibers cannot be effectively adhered, and the strength development becomes low. Meanwhile, 5
When the content is more than 0%, the strength is improved, but a binder film is formed and the pressure loss is significantly increased, which is not preferable.
A fiber having a fiber length of 1 to 6 mm, preferably 3 to 5 mm can be used.
【００１４】かかる熱融着性複合繊維としては、芯部ポ
リエチレンテレフタレート／鞘部変性ポリエステル，芯
部ポリプロピレン／鞘部ポリエチレン，芯部ポリプロピ
レン／鞘部ポリオレフィンコポリマー，芯部ポリエステ
ル／鞘部ポリエチレン系等があげられるが、これらに限
定されるものではない。特に好ましくは、芯部ポリエチ
レンテレフタレート／鞘部変性ポリエステル熱融着性複
合繊維である。Examples of such heat-fusible conjugate fibers include core polyethylene terephthalate / sheath modified polyester, core polypropylene / sheath polyethylene, core polypropylene / sheath polyolefin copolymer, core polyester / sheath polyethylene. However, the present invention is not limited to these. Particularly preferred is a core polyethylene terephthalate / sheath modified polyester heat-fusible composite fiber.
【００１５】マーセル化木材パルプの配合量は、１０〜
３０％である。１０％未満では、繊維本数が少なくマー
セル化木材パルプの特性である繊維充填密度の低下が発
現しないとともに、安価であるという特徴が消失する。
３０％より多いと繊維充填密度の低下が著しく、圧力損
失の低下は十分発現するが、微細塵の捕捉が低下し、電
気掃除機集塵袋用ろ紙として好ましくない。The blending amount of mercerized wood pulp is 10 to 10.
30%. If it is less than 10%, the number of fibers is small and the decrease in fiber packing density, which is a characteristic of mercerized wood pulp, does not appear, and the feature of being inexpensive disappears.
When it is more than 30%, the fiber packing density is remarkably reduced and the pressure loss is sufficiently reduced, but the trapping of fine dust is lowered, which is not preferable as a filter paper for a vacuum cleaner dust bag.
【００１６】木材パルプの配合量は、１０〜６５％であ
る。１０％未満では、繊維充填密度が低くなりすぎ、微
細塵の捕捉力が著しく低下し好ましくないとともに、安
価であるという特徴が消失する。６５％より多いと、繊
維充填密度が高くなりすぎ微細塵の捕捉力は上昇するも
のの圧力損失が大きくなり、好ましくない。他の非木材
繊維、例えば麻パルプも本発明では木材パルプに代えて
使用できる。The blending amount of wood pulp is 10 to 65%. If it is less than 10%, the fiber packing density becomes too low, the capturing power of fine dust is remarkably lowered, and it is not preferable, and the feature of being inexpensive disappears. When it is more than 65%, the fiber packing density becomes too high and the capturing power of fine dust increases but the pressure loss becomes large, which is not preferable. Other non-wood fibers such as hemp pulp can also be used in the present invention in place of wood pulp.
【００１７】本発明の電気掃除機集塵袋用ろ紙の坪量
は、３０ｇ／ｍ2 〜１００ｇ／ｍ2 である。３０ｇ／ｍ
2 未満では薄すぎて微細塵の捕捉能力が不足し、１００
ｇ／ｍ2 を越えると厚くなりすぎて圧力損失が上昇し好
ましくない。[0017] The basis weight of the vacuum cleaner dust bag filter paper of the present invention is a 30g / m 2 ~100g / m 2 . 30 g / m
If it is less than 2, it is too thin and the ability to capture fine dust is insufficient.
If it exceeds g / m 2 , the thickness becomes too thick and the pressure loss increases, which is not preferable.
【００１８】さらに繊維充填密度は、０．２〜０．４cm
3 ／cm3 である。０．２cm3 ／cm3 未満では、繊維充填
密度が低すぎて微細塵の捕捉能力が不足し、０．４cm3
／cm3 を越えると圧力損失が上昇し好ましくない。Further, the fiber packing density is 0.2 to 0.4 cm.
It is 3 / cm 3 . If it is less than 0.2 cm 3 / cm 3 , the fiber packing density is too low and the ability to capture fine dust is insufficient, resulting in 0.4 cm 3
If it exceeds / cm 3 , the pressure loss increases, which is not preferable.
【００１９】本発明の集塵袋用ろ紙は、通常の湿式抄紙
機で容易に製造できる。用いられる抄紙機は、円網、短
網、長網、バーチフォーマー、ロトフォーマー、ハイド
ロフォーマーなどのいずれでもよく、乾燥機はヤンキー
型、多筒型、スルー型のいずれでも良い。The filter paper for the dust collecting bag of the present invention can be easily manufactured by an ordinary wet paper machine. The paper machine used may be any of a cylinder, a short-mesh, a fourdrinier, a birch former, a rotoformer, a hydroformer, etc., and the dryer may be any of a Yankee type, a multi-cylinder type and a through type.
【００２０】[0020]
【実施例】以下に実施例及び比較例を用いて本発明を具
体的に説明するが、勿論本発明はこれによって限定され
るものではない。EXAMPLES The present invention will be specifically described below with reference to Examples and Comparative Examples, but the present invention is not of course limited thereto.
【００２１】実施例１〜９ ＮＢＫＰ（自製）を離解後、常法により６２０mlまで叩
解し、マーセル化木材パルプ（RAYONIER FOREST PRODUC
TS製、"POROSANIER-J"）も同様に処理した。 Examples 1 to 9 NBKP (manufactured by itself) was disintegrated and beaten up to 620 ml by a conventional method to give mercerized wood pulp (RAYONIER FOREST PRODUC).
"POROSANIER-J" manufactured by TS was treated in the same manner.
【００２２】細デニールの合成あるいは再生繊維として
ポリエチレンテレフタレート繊維（以後ＰＥＴと略記）
（帝人製、“テピルス”、０．５ｄ、繊維長５mm）、熱
融着性複合繊維として芯部ポリエチレンテレフタレート
繊維／鞘部変性ポリエチレンテレフタレート繊維（以後
ＰＥＴ／ＰＥＴと略記）（クラレ製、“ソフィトN72
0”、２ｄ、繊維長５mm）を使用した。Polyethylene terephthalate fiber (hereinafter abbreviated as PET) as fine denier synthetic or recycled fiber
(Made by Teijin, "Tepyrus", 0.5d, fiber length 5mm), core polyethylene terephthalate fiber / sheath modified polyethylene terephthalate fiber (hereinafter abbreviated as PET / PET) as a heat-fusible composite fiber (Kuraray, "Sophito N72
0 ", 2d, fiber length 5 mm) was used.
【００２３】これらの各原料を表１に示す割合で配合
し、種々の坪量の電気掃除機集塵袋用ろ紙を実験室規模
で抄造し、その繊維充填密度、通気度（圧力損失）、集
塵率、破裂強度を測定した。結果を表１に示す。Each of these raw materials was blended in the proportions shown in Table 1, and various types of basis weight filter papers for vacuum cleaner dust collecting bags were produced on a laboratory scale. The fiber packing density, air permeability (pressure loss), The dust collection rate and burst strength were measured. The results are shown in Table 1.
【００２４】なお集塵率は、０．２ｍ／min の流速でJI
S-Z8901 で規定される試験ダスト４種を用い、直径０．
３μm 〜１０μm のダストを発生させて試料サンプルに
通過させたときの、試料入口でのダスト個数と試料サン
プルを通過した試料出口でのダスト個数より下記の式で
算出した。 集塵率（％）＝（１−Ａ／Ｂ）×１００ Ａ：試料出口ダスト個数 Ｂ：試料入口ダスト個数。The dust collection rate is JI at a flow velocity of 0.2 m / min.
Using 4 types of test dust specified by S-Z8901, diameter 0.
It was calculated by the following formula from the number of dusts at the sample inlet and the number of dusts at the sample outlet that passed the sample when the dust of 3 μm to 10 μm was generated and passed through the sample. Dust collection rate (%) = (1−A / B) × 100 A: sample outlet dust number B: sample inlet dust number
【００２５】圧力損失は通気度にて代替し、JIS-L1004
で示されるフラジール型通気性試験機に試料を装着し、
圧力損失１．２７cmＨ2 Ｏ発生時に試料１cm2 を１秒間
に通過する空気量（cm3 ／cm2 ／sec ）とした。破裂強
度は、JIS-P8112 で示されるミューレン破裂強度測定機
を用いて測定した。Pressure loss is replaced by air permeability, JIS-L1004
Attach the sample to the Frazier type breathability tester shown in,
The amount of air (cm 3 / cm 2 / sec) passing through 1 cm 2 of the sample for 1 second when a pressure loss of 1.27 cmH 2 O was generated. The burst strength was measured by using the Murren burst strength measuring machine indicated by JIS-P8112.
【００２６】比較例１〜１２ 実施例１〜９と同様の前処理条件にて調製した各原料を
表２に示す割合で配合し、種々の坪量の電気掃除機集塵
袋用ろ紙を実験室規模で抄造し、その繊維充填密度、通
気度（圧力損失）、集塵率、破裂強度を測定した。結果
を表２に示す。 Comparative Examples 1 to 12 The respective raw materials prepared under the same pretreatment conditions as in Examples 1 to 9 were mixed in the proportions shown in Table 2, and various filter papers for vacuum cleaner dust collecting bags were tested. Fabrication was performed on a room scale, and the fiber packing density, air permeability (pressure loss), dust collection rate, and burst strength were measured. The results are shown in Table 2.
【００２７】 [0027]
【００２８】 [0028]
【００２９】実施例１〜３で得られた本発明の電気掃除
機集塵袋用ろ紙は、比較例１の低坪量品（２０ｇ／
ｍ2 ）に比べ、集塵率が大幅に優ることが確認された。
又、比較例２の高坪量品（１２０ｇ／ｍ2 ）に比べ、通
気度が大幅に優ることが確認された。The filter paper for the vacuum cleaner dust bag of the present invention obtained in Examples 1 to 3 is a low basis weight product of Comparative Example 1 (20 g / g).
compared to m 2), the dust collecting rate was confirmed that over significantly.
It was also confirmed that the air permeability was significantly superior to that of the high basis weight product (120 g / m 2 ) of Comparative Example 2.
【００３０】実施例３で得られた本発明の電気掃除機集
塵袋用ろ紙は、比較例３のＰＥＴ繊維径を０．５ｄから
１．５ｄに置換した物に比べ、集塵率が大幅に優ること
が確認された。The filter paper for the vacuum cleaner dust bag of the present invention obtained in Example 3 has a significantly higher dust collection rate than the filter paper of Comparative Example 3 in which the PET fiber diameter is changed from 0.5d to 1.5d. It was confirmed to be superior to.
【００３１】実施例３〜４で得られた本発明の電気掃除
機集塵袋用ろ紙は、比較例４のＰＥＴ繊維配合率を減少
した物に比べ、通気度，集塵率が大幅に優ることが、更
に比較例５のＰＥＴ繊維配合率を増加した物に比べ、集
塵率，破裂強度が優ることが確認された。The filter papers for vacuum cleaner dust collecting bags of the present invention obtained in Examples 3 to 4 are significantly superior in air permeability and dust collecting rate to those of Comparative Example 4 in which the PET fiber content is reduced. It was confirmed that the dust collection rate and burst strength were superior to those of Comparative Example 5 in which the PET fiber content was increased.
【００３２】実施例５〜６で得られた本発明の電気掃除
機集塵袋用ろ紙は、比較例６の熱融着性複合繊維の繊維
径を２ｄから４ｄに置換した物に比べ、集塵率が大幅に
優ることが確認された。又、比較例７の熱融着性複合繊
維の配合率を増加した物に比べ通気度が大幅に優ること
が、更に比較例８の熱融着性複合繊維の配合率を低下し
た物に比べ破裂強度が大幅に優ることが確認された。The filter papers for the vacuum cleaner dust bag of the present invention obtained in Examples 5 to 6 were more collected than those of Comparative Example 6 in which the fiber diameter of the heat fusible composite fiber was changed from 2d to 4d. It was confirmed that the dust rate was significantly superior. Further, the air permeability is significantly superior to that of Comparative Example 7 in which the blending ratio of the heat-fusible conjugate fiber is increased, and further compared to the product of Comparative Example 8 in which the blending ratio of the heat-fusible conjugate fiber is lowered. It was confirmed that the burst strength was significantly superior.
【００３３】実施例７〜９で得られた本発明の電気掃除
機集塵袋用ろ紙は、比較例９のマーセル化ＮＢＫＰの配
合率を低下したものに比べ通気度が優ることが、更に比
較例１０のマーセル化ＮＢＫＰの配合率を増加した物に
比べ集塵率，破裂強度が優ることが確認された。The filter papers for the vacuum cleaner dust bag of the present invention obtained in Examples 7 to 9 are superior in air permeability as compared with those of Comparative Example 9 in which the blending ratio of the mercerized NBKP is lowered, but further comparison is made. It was confirmed that the dust collection rate and burst strength were superior to those of Example 10 in which the compounding rate of the mercerized NBKP was increased.
【００３４】更に、比較例１１の繊維充填密度低下品
（０．１９cm3 ／cm3 ）に比べ、集塵率の大幅に優るこ
とが確認され、更に比較例１２の繊維充填密度増加品
（０．４２cm3 ／cm3）に比べ通気度が大幅に優ること
が確認された。Further, it was confirmed that the dust collection rate was significantly superior to that of the product of Comparative Example 11 having a reduced fiber packing density (0.19 cm 3 / cm 3 ), and further the product of Comparative Example 12 having an increased fiber packing density (0 It was confirmed that the air permeability was significantly superior to that of 0.42 cm 3 / cm 3 ).
【００３５】[0035]
【発明の効果】以上説明したところからわかるように本
発明によれば、１ｄ未満の合成あるいは再生繊維５〜２
０％、２ｄ以下の熱融着性複合繊維２０〜５０％、木材
パルプ１０〜６５％、及びマーセル化木材パルプ１０〜
３０％を混抄するとともに、坪量３０〜１００ｇ／
ｍ2 、繊維充填密度０．２〜０．４cm3 ／cm3 に設定し
たことにより、安価で微細塵の捕捉力が高く、圧力損失
が小さく、かつ強度の強い優れた性能を有する電気掃除
機集塵袋用ろ紙が得られる。As is apparent from the above description, according to the present invention, synthetic or regenerated fibers of less than 1d 5-2
0%, 2d or less 20 to 50% of heat-fusible composite fiber, 10 to 65% of wood pulp, and 10 to mercerized wood pulp
30% is mixed and the basis weight is 30 to 100 g /
m 2 and fiber packing density of 0.2 to 0.4 cm 3 / cm 3 make it an inexpensive vacuum cleaner with high performance of capturing fine dust, low pressure loss and strong strength. A filter paper for a dust bag is obtained.
【００３６】この様に、本発明は、フィルター性能とり
わけ集塵率及び通気度が極めて良好でしかも安価な電気
掃除機集塵袋用ろ紙を提供するものであり、その工業的
価値は極めて大である。As described above, the present invention provides a filter paper for an electric vacuum cleaner dust collecting bag, which has extremely excellent filter performance, particularly dust collection rate and air permeability, and is inexpensive, and its industrial value is extremely large. is there.
─────────────────────────────────────────────────────
─────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成３年７月１５日[Submission date] July 15, 1991
【手続補正１】[Procedure Amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２４[Correction target item name] 0024
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２４】なお集塵率は、０．２ｍ／sec の流速でJI
S-Z8901 で規定される試験ダスト４種を用い、直径０．
３μm 〜１０μm のダストを発生させて試料サンプルに
通過させたときの、試料入口でのダスト個数と試料サン
プルを通過した試料出口でのダスト個数より下記の式で
算出した。 集塵率（％）＝（１−Ａ／Ｂ）×１００ Ａ：試料出口ダスト個数 Ｂ：試料入口ダスト個数。The dust collection rate is JI at a flow velocity of 0.2 m / sec.
Using 4 types of test dust specified by S-Z8901, diameter 0.
It was calculated by the following formula from the number of dusts at the sample inlet and the number of dusts at the sample outlet that passed the sample when the dust of 3 μm to 10 μm was generated and passed through the sample. Dust collection rate (%) = (1−A / B) × 100 A: sample outlet dust number B: sample inlet dust number
【手続補正２】[Procedure Amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２７[Name of item to be corrected] 0027
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２７】 [0027]
【手続補正３】[Procedure 3]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２８[Correction target item name] 0028
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２８】 [0028]
Claims (1)
〜２０重量％、２デニール以下の熱融着性複合繊維２０
〜５０重量％、木材パルプ１０〜６５重量％、マーセル
化木材パルプ１０〜３０重量％よりなり、坪量３０〜１
００ｇ／ｍ2 、繊維充填密度（単位容積当りに占める繊
維分の容積）０．２〜０．４cm3 ／cm3 としたことを特
徴とする電気掃除機集塵袋用ろ紙。Claims: 1. Synthetic or regenerated fiber 5 having a denier of less than 1.
20 wt%, 2 denier or less of heat-fusible composite fiber 20
-50 wt%, wood pulp 10-65 wt%, mercerized wood pulp 10-30 wt%, basis weight 30-1
00g / m 2, the fiber packing density (fiber content of volume occupied per unit volume) 0.2~0.4cm 3 / cm 3 and to the vacuum cleaner dust bag filter paper, characterized in that the.