JPH0557782A - 扁平容器の射出延伸吹込成形方法 - Google Patents
扁平容器の射出延伸吹込成形方法Info
- Publication number
- JPH0557782A JPH0557782A JP24494191A JP24494191A JPH0557782A JP H0557782 A JPH0557782 A JP H0557782A JP 24494191 A JP24494191 A JP 24494191A JP 24494191 A JP24494191 A JP 24494191A JP H0557782 A JPH0557782 A JP H0557782A
- Authority
- JP
- Japan
- Prior art keywords
- preform
- mold
- temperature
- blow molding
- flat container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
せ、高温のうちに離型して直ちに延伸吹込成形すること
により、扁平容器を短時間で形成する。 【構成】 射出金型内にて、プリフォーム1における扁
平容器2の膨張比率が小なる前後部11,12を形成す
る部分の肉厚を、扁平容器の膨張比率が大なる両側部を
形成する部分よりも厚肉に形成して熱容量を大きくす
る。そのプリフォーム1の射出金型からの離型を、急冷
により表面に生じたスキン層により形状の維持が可能な
状態にあり、かつ内部冷却が未完で高温状態にあるうち
に行う。プリフォームの延伸吹込成形は、自己の内部温
度により上昇するプリフォーム1の表面温度がピーク温
度に達するまでの時間内に行う。
Description
フォームの射出成形から薄肉扁平容器への延伸吹込成形
を連続して行う成形方法に関するものである。
方法としては、特公昭59−4292号に記載された方
法が知られている。
平容器の膨張比率が小なる前後部を形成する部分の肉厚
を、扁平容器の膨張比率が大なる両側部を形成する部分
よりも厚肉に形成して熱容量を大きくし、その厚肉部分
を吹込金型の扁平容器の前後面を形成する型面に臨ませ
て吹込成形する、というものである。
共に離型したのち、直ちに吹込金型に移送して吹込成形
を行う場合と、一旦加熱炉に送って温度調節をしてから
吹込金型に移送して、吹込成形を行う場合のいずれにも
採用できるとされているが、実際には温度調節したのち
に吹込成形を行っている。
を持たせたプリフォームを、そのままの状態で吹込金型
に移行して扁平容器に吹込成形することの困難さは、離
型から吹込成形を行う時間の設定にあり、特にコアと共
に移送した場合には、コア自体の温度の影響を受けて、
満足な扁平容器の吹込成形は一層困難であった。
験を要し、一度に多数個の扁平容器を成形する場合に
は、プリフォームを一本ごとに温調しなければならぬな
ど、極めて手数のかかるものであった。
込成形における課題を解決するために考えられたもので
あって、その目的は、射出成形したプリフォームを直ち
に吹込成形するものでありながら、設計通りの肉厚分布
の薄肉扁平容器を成形することができる新たな扁平容器
の射出延伸吹込成形方法を提供することにある。
脂を射出金型に射出充填して所要のプリフォームに形成
し、そのプリフォームをリップ型により口部を保持して
射出金型から吹込金型に移送し、吹込金型内にて薄肉で
扁平な容器に延伸吹込成形するにあたり、射出金型内に
てプリフォームにおける扁平容器の膨張比率が小なる前
後面を形成する部分の肉厚を、扁平容器の膨張比率が大
なる両側部を形成する部分よりも厚肉に形成して熱容量
を大きくし、そのプリフォームの射出金型からの離型
を、急冷により表面に生じたスキン層により形状の維持
が可能な状態にあり、かつ内部冷却が未完で高温状態に
あるうちに行い、扁平容器への延伸吹込成形を、自己の
内部温度により上昇するプリフォームの表面温度がピー
ク温度に達するまでの時間内にて行うことにある。
冷により型面に接する樹脂が極めて短時間に硬化してス
キン層を形成する。また硬化に伴う収縮により表面が型
面から離れるため、内部に対する冷却は悪くなり、冷却
未完の状態で高温を保っている。
り、離型可能な状態となり、また離型後にも形状が維持
される。このため抜き勾配に左右されず早期の離型が可
能となる。
後においても表面温度がピークに達するまでは、半溶融
状態の内部樹脂がスキン層に包まれた状態にあるから、
スキン層が軟化した時点にて延伸すると、まずスキン層
が内部樹脂を連れて薄く伸びて行く。
によりプリフォーム全体の温度が低下し、内部樹脂の温
度までが延伸に適した温度となる。それまでスキン層に
つれられて延びていた内部樹脂が、途中からスキン層と
同様に薄く伸びるようになり、その結果、プリフォーム
は肉厚分布が均一な成形品となる。
比率が小なる前後面を形成する部分の肉厚を、扁平容器
の膨張比率が大なる両側部を形成する部分よりも厚肉に
形成して熱容量を大きくしたプリフォームにおいても同
様であるが、そこに付与された温度差から、プリフォー
ム全体の延伸状態に差が生じ、延伸は熱容量の高いほう
が先行する。
フォームを射出成形し、このプリフォームを射出金型か
らできるだけ高温のうちに離型して、室温中にそのまま
放置しておくと、プリフォームの表面温度は、図5に示
すように、表面温度の高低差に関係無く、同様な温度変
化を示す。
する迄の時間にある程度の差はあっても、容器の成形に
用いられる熱可塑性樹脂の殆どが同様な経過を示す。こ
の初期の表面温度の上昇原因は、高温離型されたプリフ
ォームでは、金型のキャビティ面やコアと接しているプ
リフォーム表面が、金型の冷却により固化してスキン層
を形成するが、内部冷却は未完で高温で半溶融状態にあ
り、これが離型により冷却を断たれたのちのスキン層を
内部から加熱することにある。
タレートによるプリフォームの離型後の表面温度が80
℃以下であると白濁が発生し易くなる。また離型直後の
プリフォームの表面温度が60℃以上で、極めて短時間
の経過の後に延伸吹込成形を行った場合には、クレージ
ングの発生が殆どないということである。
長く離型直後の温度が60℃以下になると、延伸吹込成
形温度がピーク前の80℃以上であっても、そこに延伸
吹込成形された成形品に白濁が生じ易いことも明らかと
なった。
より成形された肉厚分布が異なるプリフォームでは、最
も薄肉な部分の表面温度が80℃以下にならない範囲
で、しかも図5に示すピーク温度に達する前に、吹込成
形を開始すれば、極めて短時間の間に扁平容器の膨張比
率が小なる前後部を形成する部分の延伸が先行し、次い
で膨張比率が大なる両側部が延伸して、そこに設計肉厚
の扁平容器が得られることになる。
出金型に射出充填し、急冷により図1に示すような細口
のプリフォーム1を成形した。
前部11と後部12は150°角の範囲にて両側部1
3,13より内側を順次厚肉に形成してある。
は、扁平容器の用途上からで、通常の扁平容器では、そ
の両方の肉厚は同一に設計される。
温中(22℃)測定したもので、平均値である。温度測
定器は、デジタル放射温度計IR−AHOT(株式会社
チノン製)を使用した。
持して直ちに吹込金型に移送し、前部11と後部12を
扁平容器の前部と後部とを成形する型面にそれぞれ臨ま
せ、各部の表面温度がピークに達する前の時間内にて延
伸吹込成形を行った結果、図3及び図4に示す形状の扁
平容器2を得た。その際の成形条件は下記のとおりであ
った。
プリフォームを直ちに延伸吹込成形するものでありなが
ら、設計通りの薄肉扁平容器を成形することができる。
またピーク温度に達する前の高温状態にあるうちに延伸
吹込成形を行うため、白化現象も起こらず、延伸吹込成
形に要する時間がこれまでより著しく短くなるので、成
形サイクルも早くなり、時間当たり生産量が増すなどの
利点をも有する。
る。
容器の正面図である。
たプリフォームの表面温度の経時変化図である。
Claims (1)
- 【請求項1】 溶融樹脂を射出金型に射出充填して所要
のプリフォームに形成し、そのプリフォームをリップ型
により口部を保持して射出金型から吹込金型に移送し、
吹込金型内にて薄肉で扁平な容器に延伸吹込成形するに
あたり、射出金型内にてプリフォームにおける扁平容器
の膨張比率が小なる前後部を形成する部分の肉厚を、扁
平容器の膨張比率が大なる両側部を形成する部分よりも
厚肉に形成して熱容量を大きくし、そのプリフォームの
射出金型からの離型を、急冷により表面に生じたスキン
層により形状の維持が可能な状態にあり、かつ内部冷却
が未完で高温状態にあるうちに行い、扁平容器への延伸
吹込成形を、自己の内部温度により上昇するプリフォー
ムの表面温度がピーク温度に達するまでの時間内にて行
うことを特徴とする扁平容器の射出延伸吹込成形方法。