JPH05318656A - Production of laminated sheet - Google Patents
Production of laminated sheetInfo
- Publication number
- JPH05318656A JPH05318656A JP3069920A JP6992091A JPH05318656A JP H05318656 A JPH05318656 A JP H05318656A JP 3069920 A JP3069920 A JP 3069920A JP 6992091 A JP6992091 A JP 6992091A JP H05318656 A JPH05318656 A JP H05318656A
- Authority
- JP
- Japan
- Prior art keywords
- double belt
- long
- resin
- laminated sheet
- continuously
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、電子機器、電気機器、
コンビュ−タ−、通信機器等に用いられる積層板の製造
方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to electronic equipment, electric equipment,
The present invention relates to a method for manufacturing a laminated board used for a computer, a communication device and the like.
【０００２】[0002]
【従来の技術】従来、電気用積層板を連続的にダブルベ
ルト成形機で製造する場合、硬化した樹脂、異物等がダ
ブルベルト表面に付着し、成形品である積層板表面にへ
こみ所謂打痕となり、外観不良を発生させていた。2. Description of the Related Art Conventionally, when an electric laminated plate is continuously manufactured by a double belt molding machine, cured resin, foreign matter and the like adhere to the surface of the double belt and a dent is formed on the surface of the laminated plate which is a molded product. Therefore, the appearance was poor.
【０００３】[0003]
【発明が解決しようとする課題】従来の技術で述べたよ
うに、従来のダブルベルト成形機による連続的製造方法
では、外観不良の発生が多い。本発明は従来の技術にお
ける上述の問題点に鑑みてなされたもので、その目的と
するところは不良発生の少ないダブルベルト成形機によ
る積層板の製造方法を提供することにある。As described in the prior art, in the continuous manufacturing method using the conventional double belt molding machine, appearance defects are often generated. The present invention has been made in view of the above-mentioned problems in the prior art, and an object of the present invention is to provide a method for manufacturing a laminated plate by a double belt molding machine that causes less defects.
【０００４】[0004]
【課題を解決するための手段】本発明は、長尺樹脂含浸
基材を所要枚数重ね、更にその上面及び又は下面に長尺
金属箔を、ダブルベルト成形機で連続的に加熱加圧成形
し、成形後のダブルベルト表面を連続的に、離型剤処理
することを特徴とする積層板の製造方法のため、上記目
的を達成することができたもので、以下本発明を詳細に
説明する。According to the present invention, a required number of long resin-impregnated base materials are stacked, and a long metal foil is continuously heat-pressed and molded on the upper surface and / or the lower surface thereof by a double belt molding machine. Since the method for producing a laminated plate is characterized in that the surface of the double belt after molding is continuously treated with a release agent, the above object can be achieved, and the present invention will be described in detail below. ..
【０００５】本発明に用いる長尺樹脂含浸基材は、基材
として長尺のガラス、アスベスト等の無機質繊維や、ポ
リエステル、ポリアミド、ポリアクリル、ポリビニルア
ルコ−ル、ポリイミド、ポリフエニレンサルフアイド、
ポリフエニレンオキサイド、フッ素樹脂等の有機質繊維
や木綿等の天然繊維からなる織布、不織布、マット、紙
等で、長尺基材に含浸させる樹脂としては、フエノ−
ル、エポキシ、不飽和ポリエステル、ポリイミド、ポリ
アミド、ポリフエニレンオキサイド、ポリフエニレンサ
ルフアイド、フッ素樹脂等の単独、変性物、混合物が用
いられ、必要に応じてタルク、クレ−、炭酸カルシュウ
ム、水酸化アルミニュ−ム、シリカ等の無機質粉末充填
剤や、ガラス繊維、アスベスト繊維、パルプ繊維、合成
繊維、セラミック繊維等の繊維質充填剤を添加すること
ができる。更に樹脂は同一の樹脂のみによる含浸でもよ
いが、同系樹脂又は異系樹脂により１次含浸、２次含浸
というように含浸を複数にし、より含浸が均一になるよ
うにしてもよい。The long resin-impregnated base material used in the present invention is a long glass or inorganic fiber such as asbestos as a base material, polyester, polyamide, polyacryl, polyvinyl alcohol, polyimide, polyphenylene sulfide,
Woven cloths, non-woven cloths, mats, papers and the like made of organic fibers such as polyphenylene oxide and fluororesin and natural fibers such as cotton are used as the resin for impregnating the long base material.
, Epoxy, unsaturated polyester, polyimide, polyamide, polyphenylene oxide, polyphenylene sulfide, fluororesin, etc. alone, modified products, mixtures are used, and talc, clay, calcium carbonate, water as necessary. Inorganic powder fillers such as aluminum oxide and silica, and fibrous fillers such as glass fibers, asbestos fibers, pulp fibers, synthetic fibers and ceramic fibers can be added. Further, the resin may be impregnated only with the same resin, but a plurality of impregnations such as primary impregnation and secondary impregnation with the same type resin or different type resin may be performed to make the impregnation more uniform.
【０００６】かくして長尺基材に樹脂を含浸後、必要に
応じて加熱等で乾燥して長尺樹脂含浸基材を得るもので
ある。長尺金属箔としては長尺の銅、アルミニュウム、
真鍮、ニッケル、鉄等の単独、合金、複合箔が用いら
れ、必要に応じて金属箔の片面に接着剤層を設けておく
ことができる。加熱加圧成形の条件は樹脂、基材、厚さ
等で、硬化時間、硬化温度、成形圧力を選択することが
でき、特に限定しない。成形後のダブルベルト表面の離
型剤処理は、ダブルベルト表面に、連続的に流動パラフ
ィン、マイクロワックス等の炭化水素系や、ステアリン
酸、金属石鹸等の脂肪酸系や、シリコンオイル、シリコ
ン樹脂等のシリコン化合物、フッ素化合物等の離型剤を
噴霧、流延、転写、塗布等の任意手段で設ける事により
ダブルベルト成形機の離型性を良くし、樹脂、異物等に
よる外観不良の発生を防止することが出来るものであ
る。Thus, after the long base material is impregnated with the resin, the long base material is dried by heating or the like, if necessary, to obtain a long resin-impregnated base material. As long metal foil, long copper, aluminum,
A single, alloy, or composite foil of brass, nickel, iron, or the like is used, and an adhesive layer can be provided on one side of the metal foil if necessary. The conditions of heat and pressure molding are resin, base material, thickness, etc., and the curing time, curing temperature, and molding pressure can be selected and are not particularly limited. The release agent treatment on the surface of the double belt after molding is performed continuously on the surface of the double belt by a hydrocarbon type such as liquid paraffin and micro wax, a fatty acid type such as stearic acid and metal soap, silicone oil and silicone resin. The mold release property of the double belt molding machine can be improved by providing a mold release agent such as a silicon compound or a fluorine compound by any means such as spraying, casting, transfer, coating, etc. It can be prevented.
【０００７】以下本発明を実施例に基づいて説明する。The present invention will be described below based on examples.
【０００８】[0008]
【実施例】幅１０５ｃｍ、厚さ0.１５ｍｍの長尺エポキ
シ樹脂含浸ガラス織布プリプレグの３枚を重ね、更にそ
の上下面に幅１０５ｃｍ、厚さ０．０３５ｍｍの長尺銅
箔を配設した長尺積層体をダブルベルト成形機に送り、
成形圧力１０Ｋｇ／ｃｍ2、１６５℃で１０分間連続し
て加熱加圧成形し、成形後のダブルベルト表面にはシリ
コンオイル離型剤を塗布しつつ厚さ０．５ｍｍの積層板
を連続的に製造した。[Example] Three pieces of long epoxy resin-impregnated glass woven prepreg having a width of 105 cm and a thickness of 0.15 mm were stacked, and further a long copper foil having a width of 105 cm and a thickness of 0.035 mm was arranged on the upper and lower surfaces thereof. Send the long laminate to the double belt molding machine,
Molding pressure of 10 kg / cm 2 and heat and pressure molding for 10 minutes at 165 ° C. continuously, and a 0.5 mm thick laminated plate is continuously coated on the double belt surface after molding while applying a silicone oil release agent. Manufactured.
【０００９】[0009]
【比較例】成形後のダブルベルト表面に離型剤処理する
ことなく連続的に加熱加圧成形した以外は実施例と同様
に処理して積層板を得た。[Comparative Example] A laminated plate was obtained by the same process as in Example except that the double belt surface after molding was continuously heated and pressed without being treated with a release agent.
【００１０】実施例及び比較例の積層板の性能は第１表
のようである。 The performances of the laminates of Examples and Comparative Examples are shown in Table 1.
【００１１】[0011]
【発明の効果】本発明は上述したごとく構成されてい
る。特許請求の範囲に記載した構成を有する積層板の製
造方法においては、外観不良を大幅に削減することがで
き、本発明の優れていることを確認した。The present invention is constructed as described above. In the method for manufacturing a laminated plate having the structure described in the claims, it has been confirmed that appearance defects can be significantly reduced and the present invention is excellent.
フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 // Ｈ０５Ｋ 3/00 Ｒ 6921−4Ｅ Ｂ２９Ｌ 9:00 4Ｆ Continuation of front page (51) Int.Cl. 5 Identification number Office reference number FI technical display location // H05K 3/00 R 6921-4E B29L 9:00 4F
Claims (1)
その上面及び又は下面に長尺金属箔を配設した長尺積層
体を、ダブルベルト成形機で連続的に加熱加圧成形し、
成形後のダブルベルト表面を連続的に、離型剤処理する
ことを特徴とする積層板の製造方法。1. A long-sized laminate in which a required number of long-sized resin-impregnated base materials are stacked and a long-sized metal foil is disposed on the upper surface and / or the lower surface thereof is continuously heated and pressed by a double belt molding machine. ,
A method for producing a laminated plate, comprising continuously treating the surface of a double belt after molding with a release agent.