JPH05265133A - Production of substrate for photographic printing paper - Google Patents
Production of substrate for photographic printing paperInfo
- Publication number
- JPH05265133A JPH05265133A JP9340592A JP9340592A JPH05265133A JP H05265133 A JPH05265133 A JP H05265133A JP 9340592 A JP9340592 A JP 9340592A JP 9340592 A JP9340592 A JP 9340592A JP H05265133 A JPH05265133 A JP H05265133A
- Authority
- JP
- Japan
- Prior art keywords
- printing paper
- photographic printing
- paper
- base paper
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は写真印画紙用支持体の製
造方法に関し、特に、樹脂層と原紙の密着性に優れる写
真印画紙用支持体の製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a support for photographic printing paper, and more particularly to a method for producing a support for photographic printing paper which is excellent in adhesion between a resin layer and a base paper.
【0002】[0002]
【従来の技術】従来、写真印画紙においては、耐水性と
共に光反射効率を高めるために、原紙の乳剤塗布側の面
に、酸化チタンを混練分散して含有するポリエチレン等
のポリオレフィン樹脂層を被覆することが行われてい
る。この場合、酸化チタンは、特に印画紙の白色度を高
めることによって画像品質を高める一方、印画紙表面の
平面性に対しては、それを劣化させる方に働く。2. Description of the Related Art Conventionally, in photographic printing paper, in order to improve water resistance and light reflection efficiency, the surface of the base paper on which the emulsion is coated is coated with a polyolefin resin layer such as polyethylene containing titanium oxide mixed and dispersed. Is being done. In this case, titanium oxide enhances the image quality by increasing the whiteness of the photographic paper in particular, while it works to deteriorate the flatness of the surface of the photographic paper.
【0003】しかしながら、現在最も賞用されていると
ころの光沢面を有する写真印画紙においては、画像の見
栄えを改善するために、更に印画紙表面の平滑性及び光
沢性を改良することが要望されている。そこで、ポリオ
レフィンの代わりにポリエチレンテレフタレートを使用
することにより、印画紙表面の平滑性及び光沢性を改良
することが提案されている(例えば、特願平3─899
83号)。However, in the photographic printing paper having a glossy surface, which is most widely used at present, it is required to further improve the smoothness and glossiness of the surface of the printing paper in order to improve the appearance of the image. ing. Therefore, it has been proposed to use polyethylene terephthalate instead of polyolefin to improve the smoothness and glossiness of the surface of photographic paper (for example, Japanese Patent Application No. 3-899).
No. 83).
【0004】[0004]
【発明が解決しようとする課題】しかしながら、ポリエ
チレンテレフタレートの樹脂層は、ポリオレフィンの樹
脂層に比べ原紙との密着性が劣るため、現像等の際に印
画紙を長時間水中に浸漬した場合には、樹脂層が原紙か
ら剥離し易くなる(密着性に劣る)という欠点があっ
た。However, since the polyethylene terephthalate resin layer is inferior in adhesiveness to the base paper as compared with the polyolefin resin layer, when the photographic paper is immersed in water for a long time at the time of development or the like, However, there is a drawback that the resin layer is easily peeled off from the base paper (poor adhesion).
【0005】本発明者等は、上記の欠点を解決すべく鋭
意検討した結果、ポリエチレンテレフタレートを10〜
100重量%含有する樹脂に酸化チタンを混合分散した
組成物を、70℃以上に加熱した原紙の表面に流延しラ
ミネートすることによって、ポリエチレンテレフタレー
トの樹脂層と原紙の密着性を改善することができること
を見出し本発明に到達した。従って、本発明の目的は耐
水性、表面平滑性及び光沢性が良好である上、密着性が
優れる写真印画紙用支持体の製造方法を提供することに
ある。The present inventors have conducted extensive studies to solve the above-mentioned drawbacks, and as a result, have found that polyethylene terephthalate is 10
It is possible to improve the adhesiveness between the polyethylene terephthalate resin layer and the base paper by casting and laminating a composition in which titanium oxide is mixed and dispersed in a resin containing 100% by weight on the surface of the base paper heated to 70 ° C. or higher. The inventors have found out what can be done and have reached the present invention. Therefore, it is an object of the present invention to provide a method for producing a support for photographic printing paper, which has excellent water resistance, surface smoothness and glossiness and excellent adhesion.
【0006】[0006]
【課題を解決するための手段】本発明の上記の目的は、
ポリエチレンテレフタレートを10〜100重量%含有
する樹脂に酸化チタンを混合分散した組成物を、溶融押
し出しして原紙の一方の面に被覆せしめる写真印画紙用
支持体の製造方法であって、前記溶融押し出しを、70
℃以上に加熱した原紙の表面に対して行うこと特徴とす
る写真印画紙用支持体の製造方法によって達成された。The above objects of the present invention are as follows.
A method for producing a support for photographic paper, comprising melt-extruding a composition obtained by mixing and dispersing titanium oxide in a resin containing 10 to 100% by weight of polyethylene terephthalate, the melt-extruding method comprising: To 70
It was achieved by a method for producing a support for photographic printing paper, which is characterized in that it is carried out on the surface of a base paper heated above ℃.
【0007】本発明で使用する樹脂は、写真印画紙の光
沢性を良好なものとする観点から、ポリエチレンテレフ
タレートを10〜100重量%含有した樹脂であること
が好ましい。ポリエチレンテレフタレートに加える他の
樹脂(ブレンド樹脂という)は、ポリエチレン、ポリプ
ロピレン等のポリオレフィン樹脂、ポリエチレングリコ
ール、ポリオキシメチレン、ポリオキシプロピレン等の
ポリエーテル樹脂、ポリエステル系ポリウレタン、ポリ
エーテル系ポリウレタン等のウレタン樹脂、ポリカーボ
ネート及びポリスチレン等の、270〜350℃で押出
することのできる樹脂の中から適宜選択して用いること
ができる。上記ブレンド樹脂は、2種類以上を同時に使
用しても良い。The resin used in the present invention is preferably a resin containing 10 to 100% by weight of polyethylene terephthalate from the viewpoint of improving the glossiness of photographic printing paper. Other resins added to polyethylene terephthalate (referred to as blend resins) are polyolefin resins such as polyethylene and polypropylene, polyether resins such as polyethylene glycol, polyoxymethylene and polyoxypropylene, urethane resins such as polyester polyurethane and polyether polyurethane. The resin can be appropriately selected and used from resins that can be extruded at 270 to 350 ° C., such as polycarbonate, polystyrene and the like. Two or more kinds of the above blended resins may be used at the same time.
【0008】ポリエチレンテレフタレートとブレンド樹
脂の混合比は、用いるブレンド樹脂の重合度や種類によ
って適宜決定されるが、ポリオレフィン樹脂の場合に
は、ポリエチレンテレフタレートに対するブレンド樹脂
の混合比を、重量比で100:0〜10:90の範囲と
することが好ましい。ブレンド樹脂を90重量%以上混
合すると、得られる写真印画紙用支持体は、剛性が低下
する上表面光沢性が不十分となる。The mixing ratio of the polyethylene terephthalate and the blended resin is appropriately determined depending on the degree of polymerization and the kind of the blended resin used. In the case of the polyolefin resin, the blending ratio of the blended resin to the polyethylene terephthalate is 100: by weight. It is preferably in the range of 0 to 10:90. When the blended resin is mixed in an amount of 90% by weight or more, the resulting photographic printing paper support has reduced rigidity and insufficient surface gloss.
【0009】また、本発明で使用する酸化チタンの形態
はアナターゼ型であってもルチル型であっても良いが、
その平均粒子サイズは0.1〜0.8μmであることが
好ましい。0.1μm以下の場合には、樹脂層中に均一
に混合分散することが困難となり、また、0.8μm以
上の場合には、写真印画紙用支持体表面の平滑性が得ら
れない上白色度が不十分となる。尚、組成物中における
酸化チタンの含有量は2〜45重量%とすることが好ま
しいが、特に5〜35重量%とすることが好ましい。上
記ポリエチレンテレフタレート等の樹脂と酸化チタンの
混合は、常法に従って容易に行うことができる。The form of titanium oxide used in the present invention may be either anatase type or rutile type.
The average particle size is preferably 0.1 to 0.8 μm. When it is 0.1 μm or less, it becomes difficult to uniformly mix and disperse it in the resin layer, and when it is 0.8 μm or more, the smoothness of the surface of the photographic printing paper support cannot be obtained and it is white. The degree is insufficient. The content of titanium oxide in the composition is preferably 2 to 45% by weight, and particularly preferably 5 to 35% by weight. The mixing of the above-mentioned resin such as polyethylene terephthalate and titanium oxide can be easily performed according to a conventional method.
【0010】本発明においては、ポリエチレンテレフタ
レートを10〜100重量%含有する樹脂に酸化チタン
を混合分散した組成物(樹脂組成物という)を溶融し、
樹脂層と原紙の密着性を良好にする観点から、70℃以
上に加熱した原紙の表面に流延し、ラミネートすること
によって写真印画紙用支持体を製造する。原紙表面の温
度が70℃以下である場合には密着性に対する効果がな
い。特に100℃以上とすると、ポリオレフィンを原紙
にラミネートしたものと同等の密着性が生じる。更に、
140℃以上とした場合には、通常のポリオレフィンを
使用した印画紙以上の密着性が得られる。In the present invention, a composition (referred to as a resin composition) in which titanium oxide is mixed and dispersed in a resin containing 10 to 100% by weight of polyethylene terephthalate is melted,
From the viewpoint of improving the adhesion between the resin layer and the base paper, the support for photographic printing paper is manufactured by casting on the surface of the base paper heated to 70 ° C. or higher and laminating. When the temperature of the base paper surface is 70 ° C. or lower, there is no effect on the adhesiveness. In particular, if the temperature is 100 ° C. or higher, the same adhesiveness as that obtained by laminating a polyolefin on a base paper is produced. Furthermore,
When the temperature is 140 ° C. or higher, the adhesion is better than that of photographic printing paper using ordinary polyolefin.
【0011】前記樹脂組成物を溶融押し出しして原紙に
ラミネートすることは、公知の溶融押し出しラミネート
機を用いて容易に行うことができる。原紙に被覆する樹
脂層の厚さは、5〜50μmの範囲とすることが好まし
く、特に10〜30μmの範囲とすることが好ましい。
厚さを50μm以上とすると、被覆層に割れ等が生じ易
くなり、また、5μm以下とすると、写真印画紙用支持
体の防水性が不十分となる上、剛性が低下するので好ま
しくない。また、巻き癖を十分に防止する観点から、両
面の各被覆層の厚みを略同じにすることが好ましい。The resin composition can be melt-extruded and laminated on the base paper easily by using a known melt-extrusion laminating machine. The thickness of the resin layer coated on the base paper is preferably in the range of 5 to 50 μm, and particularly preferably in the range of 10 to 30 μm.
When the thickness is 50 μm or more, cracks and the like are likely to occur in the coating layer, and when it is 5 μm or less, the waterproof property of the support for photographic printing paper is insufficient and the rigidity is lowered, which is not preferable. Further, from the viewpoint of sufficiently preventing curl, it is preferable that the coating layers on both surfaces have substantially the same thickness.
【0012】原紙に上記混合組成物を被覆するに際して
は、原紙表面を予めコロナ放電処理したり下塗り処理す
ることによって前処理しておいても良い。以上のように
して得られた支持体の、酸化チタン含有被覆層上に、公
知の如く写真乳剤層を塗布することにより、耐水性はも
とより、白色度及び光沢度に優れる上、従来のポリオレ
フィンを用いた写真印画紙と同程度以上の密着性に優れ
た写真印画紙を製造することができる。When the base paper is coated with the above-mentioned mixed composition, the surface of the base paper may be pretreated by corona discharge treatment or undercoating treatment. By coating a photographic emulsion layer on the titanium oxide-containing coating layer of the support obtained as described above in a known manner, not only the water resistance but also the whiteness and glossiness are excellent, and the conventional polyolefin is used. It is possible to manufacture a photographic printing paper that is excellent in adhesiveness to the same extent as the used photographic printing paper.
【0013】[0013]
【発明の効果】本発明の製造方法によると、ポリオレフ
ィンよりも本来的に表面平滑性に優れたポリエチレンテ
レフタレートを含有する樹脂によって原紙表面が被覆さ
れているので、耐水性、白色度及び密着性を従来以上に
保つと共に、表面の平滑性及び光沢度が改善された写真
印画紙用支持体を製造することができる。According to the production method of the present invention, since the base paper surface is coated with a resin containing polyethylene terephthalate, which is inherently superior in surface smoothness to polyolefin, water resistance, whiteness and adhesion are improved. It is possible to produce a support for photographic printing paper which is maintained at a level higher than conventional and has improved surface smoothness and glossiness.
【0014】[0014]
【実施例】以下、本発明を実施例によって更に詳述する
が、本発明はこれによって限定されるものではない。EXAMPLES The present invention will be described in more detail below with reference to examples, but the present invention is not limited thereto.
【0015】実施例1〜4及び比較例1〜3.175g
/m2 の原紙の一方の表面に、表1に示す酸化チタン含
有樹脂組成物を300℃で溶融押し出しし、25〜30
μmのラミネート層を形成した。得られた支持体につい
て下記の評価を行った結果は表1に示した通りである。Examples 1 to 4 and Comparative Examples 1 to 3.175 g
/ M on one surface of the second sheet, the titanium oxide-containing resin composition shown in Table 1 was melt-extruded at 300 ° C., 25 to 30
A μm laminated layer was formed. The results of the following evaluations of the obtained support are as shown in Table 1.
【0016】表面光沢性 ハンディグロスメータHG─246(スガ株式会社製の
商品名)を用いて評価した。The surface gloss was evaluated using a handy gloss meter HG-246 (trade name, manufactured by Suga Co., Ltd.).
【0017】密着性 1cmの巾の粘着テープを樹脂ラミネート層面に貼り、
粘着テープを180度の角度で剥がすことによって、ラ
ミネート層が剥がされる際の剥離力を測定し評価した。Adhesiveness Adhesive tape with a width of 1 cm was attached to the resin laminate layer surface,
By peeling the adhesive tape at an angle of 180 degrees, the peeling force when the laminate layer was peeled off was measured and evaluated.
【0018】[0018]
【表1】 [Table 1]
Claims (1)
00重量%含有する樹脂に酸化チタンを混合分散した組
成物を、溶融押し出しして原紙の一方の面に被覆せしめ
る写真印画紙用支持体の製造方法であって、前記溶融押
し出しを、70℃以上に加熱した原紙の表面に対して行
うことを特徴とする写真印画紙用支持体の製造方法。1. Polyethylene terephthalate 10 to 1
A method for producing a support for photographic printing paper, comprising melt-extruding a composition prepared by mixing and dispersing titanium oxide in a resin containing 100% by weight, the melt-extrusion being performed at 70 ° C. or higher. A method for manufacturing a support for photographic printing paper, which is characterized in that it is carried out on the surface of the base paper heated to above.