JPH05262367A - Lid material - Google Patents
Lid materialInfo
- Publication number
- JPH05262367A JPH05262367A JP9201292A JP9201292A JPH05262367A JP H05262367 A JPH05262367 A JP H05262367A JP 9201292 A JP9201292 A JP 9201292A JP 9201292 A JP9201292 A JP 9201292A JP H05262367 A JPH05262367 A JP H05262367A
- Authority
- JP
- Japan
- Prior art keywords
- resin layer
- resin
- ethylene
- density polyethylene
- laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、容器本体に対して熱接
着される蓋材に関し、容器本体と蓋材との間の熱接着部
からなる封緘部が、易開封性に形成される蓋材を提供す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lid member which is heat-bonded to a container body, and a lid part which is a heat-bonded portion between the container body and the lid member is easily opened. Provide the material.
【０００２】[0002]
【従来の技術】ＨＩＰＳ，ＧＰＰＳ，ＰＰ，ＨＤＰＥ，
ＡＢＳ等によって成形されている容器本体に対する易開
封性の蓋材として、プラスチックフィルムによる支持基
材と、エチレン・酢酸ビニル共重合体樹脂を主成分とす
る易剥離性樹脂層とが、低密度ポリエチレン樹脂による
押出し樹脂層を介して積層されている積層材が利用され
ている。そして、この蓋材と容器本体のフランジ部との
間の熱接着部が、密封容器の封緘部になる。2. Description of the Related Art HIPS, GPPS, PP, HDPE,
A low-density polyethylene comprising a supporting base material made of a plastic film and an easily peelable resin layer containing an ethylene / vinyl acetate copolymer resin as a main component, as an easily-openable lid material for a container body formed of ABS or the like. A laminated material is used which is laminated through an extruded resin layer made of resin. The heat-bonded portion between the lid member and the flange portion of the container body serves as the sealing portion of the sealed container.
【０００３】[0003]
【発明が解決しようとする課題】容器本体のフランジ部
と蓋材とを熱接着させることによって密封容器を成形す
る場合に、容器本体が大型になると、容器本体のフラン
ジ部と蓋材との熱接着の際の押圧力が高くなり、圧力が
集中して掛かるようになると、密封容器における蓋材の
易剥離性樹脂層と容器本体のフランジ部との間の熱接着
強度が増大する。このため、容器本体から蓋材を指先で
剥離させる密封容器の易開封操作の際に、蓋材と容器本
体のフランジ部との間の界面で剥離せずに、蓋材におけ
る易剥離性樹脂層と低密度ポリエチレン樹脂による押出
し樹脂層との間で剥離してしまい、容器本体の開口部が
蓋材中の易剥離性樹脂層で膜状に覆われた状態となるた
め、密封容器の易開封性が果たされなくなる。When a hermetically sealed container is formed by thermally adhering the flange portion of the container body and the lid member, when the container body becomes large, the heat of the flange portion of the container body and the lid member is increased. When the pressing force at the time of bonding becomes high and the pressure is concentrated, the thermal bonding strength between the easily peelable resin layer of the lid member in the sealed container and the flange portion of the container body increases. Therefore, during the easy-opening operation of the sealed container in which the lid material is peeled from the container body with a fingertip, the easily peelable resin layer in the lid material does not peel at the interface between the lid material and the flange portion of the container body. And the extruded resin layer made of low-density polyethylene resin are peeled off, and the opening of the container body is covered with the easily peelable resin layer in the lid material in a film shape. The sex will not be fulfilled.
【０００４】かかる不手際を回避するには、蓋材を得る
工程において、すなわち、プラスチックフィルムによる
支持基材と、エチレン・酢酸ビニル共重合体樹脂を主成
分とする易剥離性樹脂層とを、低密度ポリエチレン樹脂
による押出し樹脂層を介して積層することからなる蓋材
用の積層材を得る工程において、低密度ポリエチレン樹
脂による押出し樹脂層の易剥離性樹脂層と接当する面を
酸化させ、低密度ポリエチレン樹脂による押出し樹脂層
と易剥離性樹脂層との間の接着強度を高めれば良く、例
えば、(1) 低密度ポリエチレン樹脂の押出し温度を極度
に高める、 (2)低密度ポリエチレン樹脂の押出しの際の
Ｔダイスのエアーギャップを大きくする、(3) 低密度ポ
リエチレン樹脂の押出し速度を低くする等の手段を利用
し得る。In order to avoid such inconvenience, in the step of obtaining the lid material, that is, the supporting base material made of a plastic film and the easily peelable resin layer containing an ethylene / vinyl acetate copolymer resin as a main component are reduced. In the step of obtaining a laminated material for a lid material, which is formed by laminating through an extruded resin layer made of a high density polyethylene resin, the surface of the extruded resin layer made of a low density polyethylene resin that contacts the easily peelable resin layer is oxidized to reduce the It suffices if the adhesive strength between the extruded resin layer and the easily peelable resin layer of the density polyethylene resin is increased, for example, (1) the extrusion temperature of the low density polyethylene resin is extremely increased, (2) the extrusion of the low density polyethylene resin. In this case, means such as increasing the air gap of the T die, (3) decreasing the extrusion speed of the low density polyethylene resin, and the like can be used.
【０００５】しかしながら、前記(1) 〜(3) の方法にお
いては、得られる積層材に熱ジワが発生する、ブロッキ
ングのトラブルが発生する、生産性が低下する等の欠点
が伴うため、蓋材の品質の点や経済性の点で満足し得る
ものでは無い。However, in the above methods (1) to (3), there are drawbacks such as heat wrinkles, blocking troubles, and a decrease in productivity in the obtained laminated material. It is not satisfactory in terms of quality and economy.
【０００６】これに対して本発明は、蓋材用の積層材を
得る工程において、前述のような弊害を伴うことが無
く、しかも、易剥離性樹脂層と低密度ポリエチレン樹脂
による押出し樹脂層とが高度の接着強度で積層されてお
り、容器本体と蓋材との間の熱接着部を剥離する際に、
易剥離性樹脂層と低密度ポリエチレン樹脂による押出し
樹脂層との間で分離するようなことのない積層材からな
る蓋材を提供する。On the other hand, according to the present invention, in the step of obtaining the laminated material for the lid material, the above-mentioned harmful effects are not caused, and the easily peelable resin layer and the extruded resin layer of the low density polyethylene resin are provided. Is laminated with a high degree of adhesive strength, and when peeling the heat-bonded part between the container body and the lid material,
Provided is a lid member made of a laminated material that does not separate between an easily peelable resin layer and an extruded resin layer made of a low-density polyethylene resin.
【０００７】[0007]
【課題を解決するための手段】本発明の蓋材は、プラス
チックフィルムによる支持基材と、エチレン・酢酸ビニ
ル共重合体樹脂を主成分とする易剥離性樹脂層とが、１
０〜７０重量％のエチレン・プロピレンゴムと９０〜３
０重量％の低密度ポリエチレン樹脂との混合樹脂の押出
し樹脂層を介して積層されている積層材からなる。The lid member of the present invention comprises a supporting base material made of a plastic film and an easily peelable resin layer containing an ethylene / vinyl acetate copolymer resin as a main component.
0-70 wt% ethylene propylene rubber and 90-3
It is composed of a laminated material which is laminated through an extruded resin layer of a resin mixed with 0% by weight of a low density polyethylene resin.
【０００８】通常、積層樹脂層同士の間の接着強度の向
上を計るためには、１方の樹脂層の樹脂成分を他方の樹
脂層中に混合物として添加することが考えられるが、エ
チレン・酢酸ビニル共重合体樹脂を主成分とする易剥離
性樹脂層と、低密度ポリエチレン樹脂の押出し樹脂層と
の積層構成において、低密度ポリエチレン樹脂の押出し
樹脂層を形成する際に、エチレン・酢酸ビニル共重合体
樹脂が混合されている低密度ポリエチレン樹脂を利用す
ると、低密度ポリエチレン樹脂の溶融温度でエチレン・
酢酸ビニル共重合体樹脂が分解してしまうため、先の目
的を達成することができない。Usually, in order to improve the adhesive strength between the laminated resin layers, it is possible to add the resin component of one resin layer to the other resin layer as a mixture. When forming an extruded resin layer of a low-density polyethylene resin in a laminated structure of an easily peelable resin layer containing a vinyl copolymer resin as a main component and an extruded resin layer of a low-density polyethylene resin, an ethylene / vinyl acetate copolymer When low density polyethylene resin mixed with polymer resin is used, ethylene
Since the vinyl acetate copolymer resin is decomposed, the above object cannot be achieved.
【０００９】これに対して、本発明の蓋材においては、
エチレン・酢酸ビニル共重合体樹脂を主成分とする易剥
離性樹脂層と、１０〜７０重量％のエチレン・プロピレ
ンゴムと９０〜３０重量％の低密度ポリエチレン樹脂と
の混合樹脂の押出し樹脂層との積層構成においては、先
のエチレン・酢酸ビニル共重合体樹脂を利用する場合の
ような弊害が無く、しかも、エチレン・酢酸ビニル共重
合体樹脂を主成分とする易剥離性樹脂層とエチレン・プ
ロピレンゴムと低密度ポリエチレン樹脂との混合樹脂の
押出し樹脂層との間に高度の接着強度が形成される。On the other hand, in the lid material of the present invention,
An easily peelable resin layer containing an ethylene / vinyl acetate copolymer resin as a main component, and an extruded resin layer of a mixed resin of 10 to 70% by weight of ethylene / propylene rubber and 90 to 30% by weight of a low density polyethylene resin. In the laminated structure of the above, there is no adverse effect as in the case of using the above ethylene / vinyl acetate copolymer resin, and moreover, an easily peelable resin layer containing ethylene / vinyl acetate copolymer resin as a main component and an ethylene / vinyl acetate copolymer resin are used. A high degree of adhesive strength is formed between the extruded resin layer of the mixed resin of propylene rubber and low density polyethylene resin.
【００１０】本発明の蓋材において、支持基材は強度保
持の機能を果たし、また、例えば、印刷化粧加工等の印
刷支持基材の機能を果たすもので、一般的には、ポリエ
ステル，延伸ポリプロピレン，ナイロン等による厚さ１
０〜１００μ程度のプラスチックフィルムが利用され
る。In the lid material of the present invention, the supporting base material has a function of maintaining strength, and also a function of a printing supporting base material such as, for example, printing and decorative processing. Generally, polyester or stretched polypropylene is used. , Thickness of nylon, etc. 1
A plastic film of about 0 to 100 μ is used.
【００１１】エチレン・酢酸ビニル共重合体樹脂を主成
分とする易剥離性樹脂層は、易剥離性の接着剤層として
公知のものであり、エチレン・酢酸ビニル共重合体樹脂
と、例えば、粘着付与剤，スリップ剤等との混合物によ
る厚さ１０〜８０μ程度の樹脂層からなる。この易剥離
性樹脂層は、予め押出し成形されている既製のフィル
ム、あるいは、１０〜７０重量％のエチレン・プロピレ
ンゴムと９０〜３０重量％の低密度ポリエチレン樹脂と
の混合樹脂による押出し樹脂層面に対して、押出しコー
トする等によって形成される。すなわち、易剥離性樹脂
層として既製の押出しフィルムを利用する場合には、該
易剥離性樹脂フィルムとプラスチックフィルムによる支
持基材との間に、１０〜７０重量％のエチレン・プロピ
レンゴムと９０〜３０重量％の低密度ポリエチレン樹脂
との混合樹脂の押出し樹脂層を形成することにより、蓋
材用の積層材を得るものであり、また、押出しコート法
で形成される易剥離性樹脂層の場合には、プラスチック
フィルムによる支持基材に対して、１０〜７０重量％の
エチレン・プロピレンゴムと９０〜３０重量％の低密度
ポリエチレン樹脂との混合樹脂の押出し樹脂層を形成し
た後に、該押出し樹脂層の上に、さらに、易剥離性樹脂
層を押出し積層することにより、蓋材用の積層材を得る
ものである。The easily peelable resin layer containing an ethylene / vinyl acetate copolymer resin as a main component is known as an easily peelable adhesive layer, and can be adhered to the ethylene / vinyl acetate copolymer resin with, for example, an adhesive. It is composed of a resin layer having a thickness of about 10 to 80 μm made of a mixture with an imparting agent, a slip agent and the like. This easily peelable resin layer is a ready-made film that has been extruded in advance, or an extruded resin layer surface made of a mixed resin of 10 to 70% by weight of ethylene / propylene rubber and 90 to 30% by weight of a low density polyethylene resin. On the other hand, it is formed by extrusion coating or the like. That is, in the case of using a ready-made extruded film as the easily peelable resin layer, 10 to 70% by weight of ethylene / propylene rubber and 90 to 70% by weight are provided between the easily peelable resin film and the supporting substrate made of a plastic film. A laminated material for a lid material is obtained by forming an extruded resin layer of a mixed resin with 30% by weight of a low density polyethylene resin, and in the case of an easily peelable resin layer formed by an extrusion coating method. Is formed by forming an extruded resin layer of a mixed resin of 10 to 70% by weight of ethylene / propylene rubber and 90 to 30% by weight of a low-density polyethylene resin on a supporting substrate made of a plastic film. A layered material for a lid material is obtained by further extruding and laminating an easily peelable resin layer on the layer.
【００１２】１０〜７０重量％のエチレン・プロピレン
ゴムと９０〜３０重量％の低密度ポリエチレン樹脂との
混合樹脂の押出し樹脂層は、支持基材と易剥離性樹脂層
との間の接着剤層としての機能を果たすものであり、厚
さ１０〜５０μ程度に形成される。エチレン・プロピレ
ンゴムを含有する低密度ポリエチレン樹脂層と支持基材
との間の接着には、エチレン・プロピレンゴムを含有す
る低密度ポリエチレン樹脂層と接当する支持基材の面に
予めアンカーコート層を形成して置いたり、あるいは、
支持基材と接当する側となるエチレン・プロピレンゴム
を含有する低密度ポリエチレン樹脂層面にオゾンガスを
吹き付け、該面を強制酸化処理に付したりした後に、支
持基材とエチレン・プロピレンゴムを含有する低密度ポ
リエチレン樹脂層とを積層するのが好ましい。The extruded resin layer of a mixed resin of 10 to 70% by weight of ethylene-propylene rubber and 90 to 30% by weight of a low density polyethylene resin is an adhesive layer between the supporting substrate and the easily peelable resin layer. And has a thickness of about 10 to 50 μm. For adhesion between the low-density polyethylene resin layer containing ethylene / propylene rubber and the supporting base material, an anchor coat layer is previously formed on the surface of the supporting base material that contacts the low-density polyethylene resin layer containing ethylene / propylene rubber. Form and place, or
A low density polyethylene resin layer surface containing ethylene / propylene rubber that comes into contact with the supporting base material is sprayed with ozone gas, and the surface is subjected to a forced oxidation treatment. It is preferable that the low density polyethylene resin layer is laminated.
【００１３】なお、プラスチックフィルムによる支持基
材とエチレン・酢酸ビニル共重合体樹脂を主成分とする
易剥離性樹脂層との間の接着剤の機能を果たすエチレン
・プロピレンゴムを含有する低密度ポリエチレン樹脂層
の組成成分が、エチレン・プロピレンゴムと低密度ポリ
エチレン樹脂との関係において、エチレン・プロピレン
ゴムが全体の１０重量％未満になると、エチレン・プロ
ピレンゴムの添加の効果が得られ難くなり、また、エチ
レン・プロピレンゴムが全体の７０重量％を超えるよう
になると、接着剤層をエクストルージョンラミネートで
形成する際の発熱に伴う熱分解によってモーター負荷が
大きくなり、また、ネックインが大きくなり過ぎて製膜
性が不安定になり、さらには、コストも高くなる等の弊
害が生ずるために好ましくない。A low-density polyethylene containing ethylene / propylene rubber that functions as an adhesive between a supporting substrate made of a plastic film and an easily peelable resin layer containing ethylene / vinyl acetate copolymer resin as a main component. In the relationship between the ethylene / propylene rubber and the low-density polyethylene resin, the composition component of the resin layer is less than 10% by weight of the total ethylene / propylene rubber, the effect of adding the ethylene / propylene rubber becomes difficult to obtain, and If the ethylene / propylene rubber content exceeds 70% by weight of the whole, the motor load will increase due to thermal decomposition due to the heat generated when the adhesive layer is formed by extrusion lamination, and the neck-in will increase too much. The film-forming property becomes unstable, and further, the cost becomes high, which causes adverse effects. Better wards.
【００１４】[0014]
【実施例】以下本発明の蓋材の具体的な構成を実施例に
基づいて説明し、該蓋材によって奏される作用について
言及する。EXAMPLES The specific constitution of the lid material of the present invention will be described below based on examples, and the action exerted by the lid material will be mentioned.
【００１５】実施例１ 片面がコロナ放電処理に付されている厚さ１６μの２軸
延伸ポリエステルフィルム「東洋紡績 (株) ：Ｔ４１０
０」のコロナ放電処理面に印刷化粧加工を施した後、
４．０ｇ（ｄｒｙ）／ｍ2 のウレタン系接着剤「武田薬
品工業 (株) ：Ａ５１５／Ａ１２」を利用して、厚さ２
５μの２軸延伸ナイロンフィルム「ユニチカ (株) ：エ
ンブレム」を、前記印刷化粧加工面に積層することによ
りて、支持基材を得た。Example 1 A biaxially stretched polyester film having a thickness of 16 μ and having one side subjected to corona discharge treatment “Toyo Boseki Co., Ltd .: T410”.
After applying the makeup treatment to the corona discharge treated surface of "0",
Using urethane adhesive "Takeda Yakuhin Kogyo Co., Ltd .: A515 / A12" of 4.0 g (dry) / m 2 , a thickness of 2
A supporting base material was obtained by laminating a 5 μ biaxially stretched nylon film “Unitika Co., Ltd .: Emblem” on the printed decorative surface.
【００１６】次いで、該支持基材における２軸延伸ナイ
ロンフィルム面にウレタン系のアンカーコート剤「日本
ポリウレタン工業 (株) ：コロネートＬ」をロールコー
ト法にて塗布した。Then, a urethane-based anchor coating agent "Nippon Polyurethane Industry Co., Ltd .: Coronate L" was coated on the surface of the biaxially stretched nylon film of the supporting substrate by a roll coating method.
【００１７】続いて、支持基材のアンカーコート剤の塗
布面と、エチレン・酢酸ビニル共重合体樹脂を主成分と
する既製の易剥離性樹脂フィルム「東セロ化学 (株) ：
ＣＭＰＳ ００７」との間に、低密度ポリエチレン「三
井石油化学工業 (株) ：Ｍ１１Ｐ」６０重量部とエチレ
ン・プロピレンゴム「三井石油化学工業 (株) ：Ａ４０
８５」４０重量部との混合樹脂を、３２０℃で厚さ２０
μに押出し積層することにより、本発明の１実施例品で
ある蓋材に利用される積層材（Ａ）を得た。Subsequently, the surface of the supporting base material to which the anchor coating agent is applied and the ready-to-release resin film "East Cello Chemical Co., Ltd." containing ethylene-vinyl acetate copolymer resin as a main component are prepared.
60 parts by weight of low density polyethylene "Mitsui Petrochemical Industry Co., Ltd .: M11P" and ethylene / propylene rubber "Mitsui Petrochemical Industry Co., Ltd .: A40" between CMPS 007 "and CMPS 007".
85 "40 parts by weight of the mixed resin at 320 ° C to a thickness of 20
By laminating by extrusion into μ, a laminated material (A) used for the lid material, which is an example of the present invention, was obtained.
【００１８】比較例１ 実施例１による積層材（Ａ）の製造工程において、低密
度ポリエチレン「三井石油化学工業 (株) ：Ｍ１１Ｐ」
６０重量部とエチレン・プロピレンゴム「三井石油化学
工業 (株) ：Ａ４０８５」４０重量部との混合樹脂の押
出し工程に代えて、低密度ポリエチレン「三井石油化学
工業 (株) ：Ｍ１１Ｐ」を、３２０℃で厚さ２０μに押
出し積層することにより、比較例品としての蓋材に利用
される積層材（Ｂ）を得た。Comparative Example 1 In the manufacturing process of the laminated material (A) according to Example 1, low density polyethylene "Mitsui Petrochemical Industry Co., Ltd .: M11P" was used.
Instead of the extrusion process of the mixed resin of 60 parts by weight and 40 parts by weight of ethylene-propylene rubber "Mitsui Petrochemical Industry Co., Ltd .: A4085", low density polyethylene "Mitsui Petrochemical Industry Co., Ltd .: M11P" was used. By laminating at 20 ° C. to a thickness of 20 μm and laminating, a laminated material (B) used as a lid material as a comparative example product was obtained.
【００１９】実施例２ 片面がコロナ放電処理に付されている厚さ１６μの２軸
延伸ポリエステルフィルム「東洋紡績 (株) ：Ｔ４１０
０」のコロナ放電処理面に印刷化粧加工を施した後、該
印刷化粧加工面に４．０ｇ（ｄｒｙ）／ｍ2 のウレタン
系接着剤「武田薬品工業 (株) ：Ａ５１５／Ａ１２」を
利用して、厚さ２５μの２軸延伸ナイロンフィルム「ユ
ニチカ (株) ：エンブレム」と積層することにより、支
持基材を得た。Example 2 A biaxially stretched polyester film having a thickness of 16 μ and having one side subjected to corona discharge treatment “TOYOBO CO., LTD .: T410”.
0 "is applied to the corona discharge treated surface, and then 4.0 g (dry) / m 2 of urethane adhesive" Takeda Pharmaceutical Co., Ltd .: A515 / A12 "is used on the printed makeup surface. Then, a supporting substrate was obtained by laminating the film with a biaxially stretched nylon film “Unitika Co., Ltd .: Emblem” having a thickness of 25 μm.
【００２０】次いで、該支持基材における２軸延伸ナイ
ロンフィルム面にウレタン系のアンカーコート剤「日本
ポリウレタン工業 (株) ：コロネートＬ」をロールコー
ト法にて塗布した。Then, a urethane-based anchor coating agent "Nippon Polyurethane Industry Co., Ltd .: Coronate L" was coated on the surface of the biaxially stretched nylon film of the supporting substrate by a roll coating method.
【００２１】続いて、支持基材のアンカーコート剤の塗
布面に、低密度ポリエチレン「三井石油化学工業 (株)
：Ｍ１１Ｐ」６０重量部とエチレン・プロピレンゴム
「三井石油化学工業 (株) ：Ａ４０８５」４０重量部と
の混合樹脂を、３２０℃で厚さ２０μに押出し積層し
た。Then, the low-density polyethylene "Mitsui Petrochemical Industry Co., Ltd."
A mixed resin of 60 parts by weight of "M11P" and 40 parts by weight of ethylene-propylene rubber "Mitsui Petrochemical Industry Co., Ltd .: A4085" was extruded at 320 ° C to a thickness of 20 µm and laminated.
【００２２】しかる後に、該混合樹脂の押出し樹脂層面
に、エチレン・酢酸ビニル共重合体樹脂を主成分とする
易剥離性樹脂層形成用の樹脂「三井石油化学工業 (株)
：Ｖ−７０」を、厚さ３０μに押出し積層することに
より、本発明の１実施例品である蓋材に利用される積層
材（Ｃ）を得た。Thereafter, a resin for forming an easily peelable resin layer containing an ethylene / vinyl acetate copolymer resin as a main component on the extruded resin layer surface of the mixed resin "Mitsui Petrochemical Industry Co., Ltd."
: V-70 "was extruded and laminated to a thickness of 30 µm to obtain a laminated material (C) used for a lid material, which is an example product of the present invention.
【００２３】比較例２ 実施例２による積層材（Ｃ）の製造工程において、低密
度ポリエチレン「三井石油化学工業 (株) ：Ｍ１１Ｐ」
６０重量部とエチレン・プロピレンゴム「三井石油化学
工業 (株) ：Ａ４０８５」４０重量部との混合樹脂の押
出し工程に代えて、低密度ポリエチレン「三井石油化学
工業 (株) ：Ｍ１１Ｐ」を、３２０℃で厚さ２０μに押
出し積層することにより、比較例品としての蓋材に利用
される積層材（Ｄ）を得た。Comparative Example 2 In the manufacturing process of the laminated material (C) according to Example 2, low density polyethylene "Mitsui Petrochemical Industry Co., Ltd .: M11P" was used.
Instead of the extrusion process of the mixed resin of 60 parts by weight and 40 parts by weight of ethylene-propylene rubber "Mitsui Petrochemical Industry Co., Ltd .: A4085", low density polyethylene "Mitsui Petrochemical Industry Co., Ltd .: M11P" was used. By extruding and laminating at 20 ° C. to a thickness of 20 μm, a laminated material (D) used as a lid material as a comparative example product was obtained.
【００２４】比較例３ 実施例２による積層材（Ｃ）の製造工程において、低密
度ポリエチレン「三井石油化学工業 (株) ：Ｍ１１Ｐ」
６０重量部とエチレン・プロピレンゴム「三井石油化学
工業 (株) ：Ａ４０８５」４０重量部との混合樹脂の押
出し工程に代えて、低密度ポリエチレン「三井石油化学
工業 (株) ：Ｍ１１Ｐ」６０重量部とエチレン・酢酸ビ
ニル共重合体樹脂「三井石油化学工業 (株) ：Ｍ−２５
２」４０重量部との混合樹脂を、３２０℃で厚さ２０μ
に押出し積層したところ、混合樹脂中のエチレン・酢酸
ビニル共重合体樹脂が熱分解してしまい、積層界面での
接合が不可能であった。Comparative Example 3 In the manufacturing process of the laminated material (C) according to Example 2, low density polyethylene "Mitsui Petrochemical Industry Co., Ltd .: M11P" was used.
60 parts by weight of low-density polyethylene "M11P" (M11P) instead of the extrusion process of the mixed resin of 60 parts by weight and 40 parts by weight of ethylene-propylene rubber "Mitsui Petrochemical Industry Co., Ltd .: A4085". And ethylene / vinyl acetate copolymer resin "Mitsui Petrochemical Co., Ltd .: M-25
2 "40 parts by weight of the mixed resin, at 320 ℃ thickness 20μ
When it was extruded and laminated, the ethylene / vinyl acetate copolymer resin in the mixed resin was thermally decomposed, and joining at the laminated interface was impossible.
【００２５】［実験１］実施例１〜２及び比較例１〜２
による積層材に対して、エチレン・酢酸ビニル共重合体
樹脂を主成分とする易剥離性樹脂層と、低密度ポリエチ
レン樹脂層あるいはエチレン・プロピレンゴムとの混合
樹脂層（低密度ポリエチレン系樹脂層と略称する）との
間の接着強度の試験を行なった。結果を［表１］に示
す。[Experiment 1] Examples 1 and 2 and Comparative Examples 1 and 2
For the laminated material according to (1), an easily peelable resin layer containing ethylene / vinyl acetate copolymer resin as a main component and a low density polyethylene resin layer or a mixed resin layer of ethylene / propylene rubber (low density polyethylene resin layer and (Abbreviated) was tested. The results are shown in [Table 1].
【００２６】［実験２］容器本体に成形される厚さ１．
０ｍｍのハイインパクトポリスチレンシートと、先の実
施例１〜２及び比較例１〜２による積層材とを、ハイイ
ンパクトポリスチレンシート面と積層材におけるエチレ
ン・酢酸ビニル共重合体樹脂を主成分とする易剥離性樹
脂層面とが接当するようにして重ね合わせ、１４０℃，
４ｋｇ／ｃｍ2 ，２秒間の加熱，加圧条件の下で、線幅
３ｍｍに熱接着し、容器本体のフランジ部と蓋材との間
の封緘部に相応する熱接着部を形成した。[Experiment 2] Thickness formed in container body 1.
A high-impact polystyrene sheet having a thickness of 0 mm and the laminated materials according to Examples 1 and 2 and Comparative Examples 1 and 2 described above are easy to be composed mainly of the high-impact polystyrene sheet surface and the ethylene / vinyl acetate copolymer resin in the laminated material. Overlap so that the surface of the releasable resin layer is in contact, and
Under a condition of heating and pressurizing at 4 kg / cm 2 for 2 seconds, heat bonding was performed to a line width of 3 mm to form a heat bonding portion corresponding to the sealing portion between the flange portion of the container body and the lid member.
【００２７】得られた各試料のハイインパクトポリスチ
レンシートとエチレン・酢酸ビニル共重合体樹脂を主成
分とする易剥離性樹脂層との間の熱接着部を、指先で剥
離させた。そのときの剥離状態を、［表１］に示す。The heat-bonded portion between the high-impact polystyrene sheet of each of the obtained samples and the easily peelable resin layer containing ethylene / vinyl acetate copolymer resin as a main component was peeled with a fingertip. The peeled state at that time is shown in [Table 1].
【００２８】[0028]
【表１】 [Table 1]
【００２９】[0029]
【効果】本発明の蓋材を利用する密封容器においては、
該密封容器の封緘部を熱接着によって形成する際の加
熱，加圧が集中して掛かるような場合においても、蓋材
におけるエチレン・酢酸ビニル共重合体樹脂を主成分と
する易剥離性樹脂層と、エチレン・プロピレンゴムが混
合されている低密度ポリエチレン樹脂の押出し樹脂層と
の間の接着強度の方が、容器本体と蓋材における易剥離
性樹脂層との間の接着強度よりも高くなる。[Effect] In the sealed container using the lid material of the present invention,
An easily peelable resin layer containing an ethylene / vinyl acetate copolymer resin as a main component in the lid material even when heating and pressurization are intensively applied when the sealed portion of the sealed container is formed by thermal bonding. And the extruded resin layer of low density polyethylene resin mixed with ethylene / propylene rubber have higher adhesive strength than the easily peelable resin layer of the container body and the lid material. ..
【００３０】このため、容器本体と蓋材とを分離する密
封容器の開封操作の際に、蓋材における易剥離性樹脂層
と低密度ポリエチレン樹脂による押出し樹脂層との間が
剥離してしまうようなことがなく、密封容器の易開封性
が確実であり、特に大型の容器本体に対して適用される
蓋材の場合に格別の効果を奏する。Therefore, during the opening operation of the sealed container for separating the container body and the lid member, the easily peelable resin layer of the lid member and the extruded resin layer of the low density polyethylene resin may be peeled off from each other. In this case, the ease of opening the hermetically sealed container is ensured, and particularly, in the case of a lid material applied to a large container body, a particular effect is exhibited.
Claims (1)
と、エチレン・酢酸ビニル共重合体樹脂を主成分とする
易剥離性樹脂層とが、１０〜７０重量％のエチレン・プ
ロピレンゴムと９０〜３０重量％の低密度ポリエチレン
樹脂とによる混合樹脂の押出し樹脂層を介して積層され
ている積層材からなることを特徴とする蓋材。1. A supporting base material made of a plastic film and an easily peelable resin layer containing an ethylene / vinyl acetate copolymer resin as a main component are 10 to 70% by weight of ethylene / propylene rubber and 90 to 30% by weight. 2. A lid member comprising a laminated material laminated through an extruded resin layer of a mixed resin of the low density polyethylene resin of.