JPH05239190A - Epoxy resin composition and sealed semiconductor device - Google Patents
Epoxy resin composition and sealed semiconductor deviceInfo
- Publication number
- JPH05239190A JPH05239190A JP7816992A JP7816992A JPH05239190A JP H05239190 A JPH05239190 A JP H05239190A JP 7816992 A JP7816992 A JP 7816992A JP 7816992 A JP7816992 A JP 7816992A JP H05239190 A JPH05239190 A JP H05239190A
- Authority
- JP
- Japan
- Prior art keywords
- epoxy resin
- resin composition
- filler
- resin
- obtuse
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、流動性、耐湿性、耐ク
ラック性に優れ、特性バランスのよいエポキシ樹脂組成
物およびそれによって封止された半導体封止装置に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an epoxy resin composition which is excellent in fluidity, moisture resistance and crack resistance and has a good property balance, and a semiconductor encapsulation device encapsulated by the epoxy resin composition.
【０００２】[0002]
【従来の技術】従来、ダイオード、トランジスタ、集積
回路等の電子部品を、熱硬化性樹脂を用いて封止する方
法が行われてきた。この封止樹脂は、ガラス、金属、セ
ラミックを用いたハーメチックシール方式に比較して経
済的に有利なため、広く実用化されている。封止用樹脂
としては、熱硬化性樹脂の中でも信頼性および価格の点
から、エポキシ樹脂が最も一般的に用いられている。エ
ポキシ樹脂には、酸無水物、芳香族アミン、ノボラック
型フェノール樹脂等の硬化剤が用いられるが、これらの
中でもノボラック型フェノール樹脂を硬化剤としたエポ
キシ樹脂は、他の硬化剤を利用したものに比べて、成形
性、耐湿性に優れ、毒性がなく、かつ安価であるため、
半導体封止用樹脂として広く使用されている。また、充
填剤としては、一般的に溶融シリカ粉末や結晶性シリカ
粉末が前述の硬化剤と共に使用されている。近年、半導
体部品のさらなる大電力化に伴い、熱放散性のよい、低
応力の半導体封止用樹脂の開発が要望されてきた。2. Description of the Related Art Conventionally, a method of sealing electronic parts such as diodes, transistors and integrated circuits with a thermosetting resin has been used. This sealing resin is economically advantageous as compared with the hermetic sealing method using glass, metal, and ceramic, and is therefore widely used. Among thermosetting resins, epoxy resins are most commonly used as the encapsulating resin in terms of reliability and price. Hardeners such as acid anhydrides, aromatic amines, and novolac-type phenolic resins are used as epoxy resins. Among these, epoxy resins using novolac-type phenolic resins as hardeners use other hardeners. Compared to, it has excellent moldability and moisture resistance, is non-toxic, and is inexpensive,
Widely used as a resin for semiconductor encapsulation. As the filler, fused silica powder or crystalline silica powder is generally used together with the above-mentioned curing agent. In recent years, along with the further increase in power consumption of semiconductor components, there has been a demand for the development of a low-stress resin for semiconductor encapsulation that has good heat dissipation.
【０００３】しかしながら、ノボラック型フェノール樹
脂を硬化剤としたエポキシ樹脂と破砕状無機質充填剤と
からなる樹脂組成物は、熱膨脹係数が小さく、耐湿性が
よく、また樹脂クラック、ペレットクラック等に優れて
いるという特徴を有するものの、破砕状無機質充填剤の
配合割合を上げると、成形性が低下しワイヤーフローが
生じるという欠点がある。一方ノボラック型フェノール
樹脂を硬化剤としたエポキシ樹脂と球状無機質充填剤と
からなる樹脂組成物は、成形性、ワイヤーフローが良好
となるが熱膨脹係数が大きく、耐湿性に対する信頼性も
悪くなるという欠点がある。さらにこの樹脂組成物から
得られる封止品は、機械的特性が低下するという欠点が
あった。However, a resin composition comprising an epoxy resin having a novolac type phenolic resin as a curing agent and a crushed inorganic filler has a small coefficient of thermal expansion, good moisture resistance, and is excellent in resin cracks, pellet cracks and the like. However, if the mixing ratio of the crushed inorganic filler is increased, the moldability is lowered and wire flow occurs. On the other hand, a resin composition comprising an epoxy resin having a novolac type phenolic resin as a curing agent and a spherical inorganic filler has a drawback that the moldability and the wire flow are good, but the coefficient of thermal expansion is large and the reliability with respect to moisture resistance is poor. There is. Further, the sealed product obtained from this resin composition has a drawback that mechanical properties are deteriorated.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、上記の欠点
を解消するためになされたもので、耐湿性、成形性、特
に薄肉部の充填性、耐金型摩耗性に優れ、熱膨脹係数が
小さく、耐クラック性がよく、それらの特性バランスの
とれた信頼性の高いエポキシ樹脂組成物および半導体封
止装置を提供しようとするものである。SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned drawbacks, and is excellent in moisture resistance, moldability, especially filling property of thin portion, mold abrasion resistance, and coefficient of thermal expansion. (EN) It is intended to provide an epoxy resin composition and a semiconductor encapsulation device which are small and have good crack resistance and whose characteristics are well balanced and which are highly reliable.
【０００５】[0005]
【課題を解決するための手段】本発明者らは、上記の目
的を達成しようと鋭意研究を重ねた結果、特定の鈍角無
機質充填剤及び微細球状充填剤を配合することによっ
て、上記目的が達成できることを見いだし、本発明を完
成させたものである。Means for Solving the Problems As a result of intensive studies to achieve the above object, the present inventors achieved the above object by blending a specific obtuse angled inorganic filler and a fine spherical filler. The inventors have found what can be done and completed the present invention.
【０００６】即ち、本発明は、（Ａ）エポキシ樹脂、
（Ｂ）ノボラック型フェノール樹脂、（Ｃ）鈍角無機質
充填剤および（Ｄ）平均粒径 0.01 〜 2μm の微細球状
充填剤を必須成分とし、樹脂組成物に対して前記（Ｄ）
微細球状充填剤を 0.1〜60重量％、また前記（Ｃ）及び
（Ｄ）の合計量を50〜90重量％含有してなることを特徴
とするエポキシ樹脂組成物である。またこのエポキシ樹
脂組成物の硬化物で、半導体チップが封止されてなるこ
とを特徴とする半導体封止装置である。That is, the present invention relates to (A) epoxy resin,
(B) a novolac type phenol resin, (C) an obtuse angled inorganic filler, and (D) a fine spherical filler having an average particle diameter of 0.01 to 2 μm as essential components, and the above (D) with respect to the resin composition.
An epoxy resin composition comprising 0.1 to 60% by weight of a fine spherical filler and 50 to 90% by weight of the total amount of (C) and (D). A semiconductor encapsulation device is obtained by encapsulating a semiconductor chip with a cured product of this epoxy resin composition.
【０００７】以下、本発明を詳細に説明する。The present invention will be described in detail below.
【０００８】本発明に用いる（Ａ）エポキシ樹脂として
は、その分子中にエポキシ基を少なくとも 2個有する化
合物で有る限り、分子構造、分子量等に特に制限はな
く、一般に使用されているものを広く包含することがで
きる。例えば、ビスフェノール型の芳香族系、シクロヘ
キサン誘導体等の脂肪族系、さらに次の一般式で示され
るエポキシノボラック系等のエポキシ樹脂が挙げられ
る。As the epoxy resin (A) used in the present invention, as long as it is a compound having at least two epoxy groups in its molecule, the molecular structure, molecular weight and the like are not particularly limited, and widely used resins are widely used. Can be included. For example, bisphenol type aromatic resins, aliphatic compounds such as cyclohexane derivatives, and epoxy novolac resins such as those represented by the following general formula can be used.
【０００９】[0009]
【化１】 （但し、式中Ｒ1 は、水素原子、ハロゲン原子又はアル
キル基を、Ｒ2 は水素原子又はアルキル基を、n は 1以
上の整数を表す）これらのエポキシ樹脂は単独又は 2種
以上混合して使用することができる。[Chemical 1] (Wherein R 1 represents a hydrogen atom, a halogen atom or an alkyl group, R 2 represents a hydrogen atom or an alkyl group, and n represents an integer of 1 or more). These epoxy resins may be used alone or in combination of two or more. Can be used.
【００１０】本発明に用いる（Ｂ）ノボラック型フェノ
ール樹脂としては、フェノール、アルキルフェノール等
のフェノール類と、ホルムアルデヒド或いはパラホルム
アルデヒドを反応させて得られるノボラック型フェノー
ル樹脂およびこれらの変性樹脂、例えばエポキシ化もし
くはブチル化ノボラック型フェノール樹脂等が挙げら
れ、これらは単独又は 2種以上混合して使用することが
できる。ノボラック型フェノール樹脂の配合割合は、前
記（Ａ）のエポキシ樹脂のエポキシ基（a ）と（Ｂ）の
ノボラック型フェノール樹脂のフェノール性水酸基（b
）とのモル比［（a ）／（b ）］が 0.1〜10の範囲内
であることが望ましい。モル比が 0.1未満若しくは10を
超えると耐湿性、成形作業性および硬化物の電気特性が
悪くなり、いずれの場合も好ましくない。The novolak type phenolic resin (B) used in the present invention is a novolak type phenolic resin obtained by reacting phenols such as phenol and alkylphenol with formaldehyde or paraformaldehyde, and modified resins thereof such as epoxidized or Butylated novolac type phenolic resin and the like can be mentioned, and these can be used alone or in combination of two or more kinds. The compounding ratio of the novolac type phenol resin is such that the epoxy group (a) of the epoxy resin (A) and the phenolic hydroxyl group (b) of the novolac type phenol resin (B) are
It is desirable that the molar ratio [(a) / (b)] with () is within the range of 0.1 to 10. If the molar ratio is less than 0.1 or exceeds 10, the moisture resistance, the molding workability and the electrical properties of the cured product deteriorate, which is not preferable in any case.
【００１１】本発明に用いる（Ｃ）鈍角無機質充填剤
は、通常破砕された充填剤と異なって突起が鋭角でなく
鈍角となったものを言い、その材質としては、例えば溶
融シリカ、結晶性シリカ、アルミナ、窒化ケイ素等の無
機質充填剤が挙げられ、これらは単独もしくは 2種以上
混合して使用することができる。この鈍角無機質充填剤
は平均粒径が30μm 以下であることが望ましい。平均粒
径が30μm を超えると成形性、耐クラック性が悪くなり
好ましくない。この鈍角無機質充填剤の配合割合は、樹
脂組成物に対して25〜90重量％の割合で含有することが
望ましい。その割合が25重量％未満では、機械的特性、
耐湿性が悪く、また90重量％を超えると成形性が悪く好
ましくない。The (C) obtuse-angled inorganic filler used in the present invention is one in which the protrusions have an obtuse angle instead of an acute angle, unlike the crushed filler, and the material thereof is, for example, fused silica or crystalline silica. Inorganic fillers such as alumina and silicon nitride can be used, and these can be used alone or in admixture of two or more. The obtuse inorganic filler preferably has an average particle size of 30 μm or less. If the average particle size exceeds 30 μm, moldability and crack resistance are deteriorated, which is not preferable. The blending ratio of this obtuse angled inorganic filler is preferably 25 to 90% by weight based on the resin composition. If the proportion is less than 25% by weight, mechanical properties,
Moisture resistance is poor, and if it exceeds 90% by weight, moldability is poor, which is not preferable.
【００１２】本発明に用いる（Ｄ）平均粒径 0.01 〜 2
μm の微細球状充填剤としては、例えば溶融シリカ、ア
ルミナ、窒化ケイ素等無機質充填剤が挙げられ、これら
は単独もしくは 2種以上混合して使用することができ
る。この微細球状充填剤は平均粒径が 0.01 〜 2μm で
あることが望ましい。平均粒径が 0.01 未満では耐湿性
が悪くなり、機械的特性も低下する。また、平均粒径が
2μm を超えると流動性が低下し好ましくない。微細球
状充填剤の配合割合は、樹脂組成物に対して 0.1〜60重
量％の割合で含有することが望ましい。その割合が 0.1
重量％未満では、流動性に効果なく、また60重量％を超
えると耐湿性、機械的特性が悪く好ましくない。(D) Average particle size 0.01 to 2 used in the present invention
Examples of the μm fine spherical filler include inorganic fillers such as fused silica, alumina, and silicon nitride, and these can be used alone or in combination of two or more. The fine spherical filler preferably has an average particle size of 0.01 to 2 μm. If the average particle size is less than 0.01, the moisture resistance becomes poor and the mechanical properties also deteriorate. Also, if the average particle size is
If it exceeds 2 μm, the fluidity is lowered, which is not preferable. The blending ratio of the fine spherical filler is preferably 0.1 to 60% by weight based on the resin composition. The ratio is 0.1
If it is less than wt%, the fluidity is not effective, and if it exceeds 60 wt%, the moisture resistance and mechanical properties are poor, which is not preferable.
【００１３】本発明のエポキシ樹脂組成物は、エポキシ
樹脂、ノボラック型フェノール樹脂、特定の鈍角無機質
充填剤及び微細球状充填剤を必須成分とするが、本発明
の目的に反しない限度において、また必要に応じて、例
えば天然ワックス、合成ワックス、直鎖脂肪酸の金属
塩、酸アミド類、エステル類、パラフィン類等の離型
剤、塩素化パラフィン、ブロムトルエン、ヘキサブロム
ベンゼン、三酸化アンチモン等の難燃剤、カーボンブラ
ック、ベンガラ等の着色剤、種々の硬化剤等を適宜、添
加配合することができる。The epoxy resin composition of the present invention contains an epoxy resin, a novolac type phenolic resin, a specific obtuse angled inorganic filler and a fine spherical filler as essential components, but they are also required as long as the object of the present invention is not impaired. Depending on the type, for example, natural wax, synthetic wax, metal salt of straight chain fatty acid, acid amides, esters, release agents such as paraffins, chlorinated paraffin, bromtoluene, hexabromobenzene, antimony trioxide, etc. A flame retardant, carbon black, a coloring agent such as red iron oxide, various curing agents, and the like can be appropriately added and blended.
【００１４】本発明のエポキシ樹脂組成物を成形材料と
して調製する場合の一般的な方法としては、エポキシ樹
脂、ノボラック型フェノール樹脂、特定の鈍角無機質充
填剤及び微細球状充填剤、その他を所定の組成比に選択
した原料成分をミキサー等によって十分均一に混合した
後、さらに熱ロールによる混合処理を行い、次いで冷却
固化させ、適当な大きさに粉砕して成形材料とすること
ができる。こうして得られた成形材料は、半導体装置を
はじめとする電子部品あるいは電気部品の封止、被覆、
絶縁等に適用すれば、優れた特性と信頼性を付与させる
ことができる。As a general method for preparing the epoxy resin composition of the present invention as a molding material, an epoxy resin, a novolac type phenol resin, a specific obtuse angled inorganic filler and a fine spherical filler, and others are used in a predetermined composition. After the raw material components selected for the ratio are sufficiently mixed with a mixer or the like, a mixing process with a hot roll is further performed, followed by cooling and solidification, and crushing into an appropriate size to obtain a molding material. The molding material thus obtained is used for sealing and covering electronic parts or electric parts such as semiconductor devices,
If applied to insulation or the like, excellent characteristics and reliability can be imparted.
【００１５】本発明の半導体封止装置は、上述したエポ
キシ樹脂組成物を用いて、半導体チップを封止すること
により容易に製造することができる。封止を行う半導体
チップとしては、例えば集積回路、大規模集積回路、ト
ランジスタ、サイリスタ、ダイオード等で特に限定され
るものではない。封止の最も一般的な方法としては、低
圧トランスファー成形法があるが、射出成形、圧縮成
形、注形等による封止も可能である。エポキシ樹脂組成
物は封止の際に加熱して硬化させ、最終的にはこの組成
物によって封止された半導体封止装置が得られる。加熱
による硬化は、150 ℃以上に加熱して硬化させることが
望ましい。The semiconductor encapsulation device of the present invention can be easily manufactured by encapsulating a semiconductor chip using the epoxy resin composition described above. The semiconductor chip to be sealed is not particularly limited to, for example, an integrated circuit, a large scale integrated circuit, a transistor, a thyristor, a diode and the like. The most common method of sealing is a low-pressure transfer molding method, but sealing by injection molding, compression molding, casting or the like is also possible. The epoxy resin composition is heated and cured during encapsulation, and finally a semiconductor encapsulation device encapsulated with this composition is obtained. For curing by heating, it is desirable to heat and cure at 150 ° C or higher.
【００１６】[0016]
【作用】本発明は、ノボラック型フェノール樹脂を硬化
剤とするエポキシ樹脂組成物において、特定の鈍角無機
質充填剤及び微細球状充填剤を併用したことによって、
耐湿性、耐クラック性、流動性にすぐれ、その他の特性
もバランスよく保持させることができ、この樹脂組成物
を用いることによって信頼性の高い半導体封止装置を製
造することができる。The present invention provides an epoxy resin composition containing a novolac type phenolic resin as a curing agent, in which a specific obtuse angle inorganic filler and a fine spherical filler are used in combination.
It has excellent moisture resistance, crack resistance, and fluidity, and can maintain other characteristics in a well-balanced manner. By using this resin composition, a highly reliable semiconductor encapsulation device can be manufactured.
【００１７】[0017]
【実施例】次に本発明を実施例によって説明するが、本
発明はこれらの実施例よって限定されるものではない。
以下の実施例及び比較例において「％」とは「重量％」
を意味する。EXAMPLES The present invention will now be described with reference to examples, but the present invention is not limited to these examples.
In the following Examples and Comparative Examples, "%" means "% by weight"
Means
【００１８】実施例１ クレゾールノボラックエポキシ樹脂（エポキシ当量 21
5）11％に、ノボラック型フェノール樹脂（フェノール
当量 107） 6％、鈍角溶融シリカ粉末（平均粒径25μm
）70％および微細球状溶融シリカ（平均粒径 0.5μm
）10％および離型剤等 3％を常温で混合し、さらに90
〜95℃で混練してこれを冷却粉砕して成形材料を製造し
た。Example 1 Cresol novolac epoxy resin (epoxy equivalent 21
5) 11%, novolac type phenolic resin (phenol equivalent 107) 6%, obtuse fused silica powder (average particle size 25 μm
) 70% and fine spherical fused silica (average particle size 0.5 μm)
) Mix 10% and 3% release agent at room temperature and
The mixture was kneaded at ˜95 ° C., cooled and pulverized to produce a molding material.
【００１９】実施例２ 実施例１において、鈍角溶融シリカ粉末（平均粒径25μ
m ）70％および微細球状溶融シリカ（平均粒径 0.5μm
）10％の替わりに、鈍角結晶性シリカ粉末（平均粒径3
0μm ）40％、結晶性シリカ粉末（平均粒径 1μm ）35
％と微細球状溶融シリカ（平均粒径 0.8μm ） 5％を用
いた以外は、全て実施例１と同一にして成形材料を製造
した。Example 2 In Example 1, obtuse fused silica powder (average particle size 25 μ
m) 70% and fine spherical fused silica (average particle size 0.5 μm
) Instead of 10%, obtuse crystalline silica powder (average particle size 3
0 μm) 40%, crystalline silica powder (average particle size 1 μm) 35
% And fine spherical fused silica (average particle size 0.8 μm) 5% were used, and a molding material was manufactured in the same manner as in Example 1.
【００２０】実施例３ 実施例１において、鈍角溶融シリカ粉末（平均粒径25μ
m ）70％および微細球状溶融シリカ（平均粒径 0.5μm
）10％の替わりに、鈍角窒化ケイ素粉末（平均粒径25
μm ）70％、微細球状窒化アルミニウム（平均粒径 2μ
m ）10％を用いた以外は、全て実施例１と同一にして成
形材料を製造した。Example 3 In Example 1, obtuse angle fused silica powder (average particle size 25 μ
m) 70% and fine spherical fused silica (average particle size 0.5 μm
) Instead of 10%, obtuse angle silicon nitride powder (average particle size 25
μm) 70%, fine spherical aluminum nitride (average particle size 2μ
A molding material was produced in the same manner as in Example 1, except that 10% of m) was used.
【００２１】比較例１ クレゾールノボラックエポキシ樹脂（エポキシ当量 21
5）11％に、ノボラック型フェノール樹脂（フェノール
当量 107） 6％、溶融シリカ粉末（平均粒径25μm ）80
％および離型剤等 3％を常温で混合し、実施例１と同様
にして成形材料を製造した。Comparative Example 1 Cresol novolac epoxy resin (epoxy equivalent 21
5) 11%, novolac type phenolic resin (phenol equivalent 107) 6%, fused silica powder (average particle size 25 μm) 80
% And a release agent and the like 3% were mixed at room temperature, and a molding material was manufactured in the same manner as in Example 1.
【００２２】比較例２ 比較例１において、溶融シリカ粉末（平均粒径25μm ）
の替わりに、結晶性シリカ粉末（平均粒径28μm ）を用
いた以外は、全て比較例１と同一にして成形材料を製造
した。Comparative Example 2 In Comparative Example 1, fused silica powder (average particle size 25 μm)
A molding material was produced in the same manner as in Comparative Example 1 except that crystalline silica powder (average particle size 28 μm) was used instead of.
【００２３】実施例１〜３及び比較例１〜２で製造した
成形材料を用いて半導体チップを封止し、170 ℃で加熱
硬化させて半導体封止装置を製造した。成形材料及び半
導体封止装置について、諸試験を行ったのでその結果を
表１に示した。本発明のエポキシ樹脂組成物及び半導体
封止装置は、熱的特性がよく、耐湿性、成形性に優れて
おり、本発明の効果を確認することができた。Semiconductor chips were encapsulated using the molding materials produced in Examples 1 to 3 and Comparative Examples 1 and 2, and cured by heating at 170 ° C. to produce semiconductor encapsulation devices. Various tests were conducted on the molding material and the semiconductor encapsulation device, and the results are shown in Table 1. The epoxy resin composition and the semiconductor encapsulation device of the present invention have good thermal characteristics, excellent moisture resistance and moldability, and the effects of the present invention could be confirmed.
【００２４】[0024]
【表１】 ＊1 ：ＪＩＳ−Ｋ−６９１１により測定した。 ＊2 ：半導体封止装置を、迅速熱伝導計（昭和電工社
製、商品名ＱＴＭ−ＭＤ）を用いて室温で測定した。 ＊3 ：120 キャビテイ取りＴＱＦＰ金型（厚さ 1.0mm）
を用いて、成形材料を 170℃で 3分間トランスファー成
形し、充填性を評価した。○印…良好、×印…不良。 ＊4 ：成形材料を用いて、2 本のアルミニウム配線を有
する半導体チップを、170 ℃で 3分間の条件でトランス
ファー成形した後、さらに 8時間エイジングさせた。こ
の半導体封止装置 100個について 127℃の高圧水蒸気中
で耐湿試験を行い、アルミニウム腐食による50％断線
（不良発生）の起こる時間を評価した。 ＊5 ：成形材料をプレヒートし、径 0.5mmの硬質クロム
メッキ材料流動穴を設けた金型により、175 ℃でトラン
スファー成形を行う。穴径が 5％摩耗した時のショット
数によって評価した。[Table 1] * 1: Measured according to JIS-K-6911. * 2: The semiconductor sealing device was measured at room temperature using a rapid thermal conductivity meter (Showa Denko KK, trade name QTM-MD). * 3: 120 Cavity removing TQFP mold (thickness 1.0mm)
The molding material was transfer-molded at 170 ° C. for 3 minutes, and the filling property was evaluated. ○ mark: good, × mark: bad * 4: Using a molding material, a semiconductor chip having two aluminum wirings was transfer-molded at 170 ° C for 3 minutes, and then aged for 8 hours. A humidity resistance test was performed on 100 of these semiconductor encapsulation devices in high-pressure steam at 127 ° C to evaluate the time at which 50% disconnection (defect occurrence) due to aluminum corrosion occurred. * 5: The molding material is preheated, and transfer molding is performed at 175 ° C using a die with a 0.5 mm diameter hard chrome plating material flow hole. It was evaluated by the number of shots when the hole diameter was 5% worn.
【００２５】[0025]
【発明の効果】以上の説明及び表１から明らかなよう
に、本発明のエポキシ樹脂組成物及び半導体封止装置
は、樹脂組成物の耐湿性、成形性、特に薄肉部の充填性
に優れ、耐金型摩耗性に優れ、熱膨脹係数が小さく、耐
クラック性がよく、それらの特性バランスのとれたもの
で、信頼性の高い半導体封止装置が製造できたものであ
る。As is clear from the above description and Table 1, the epoxy resin composition and the semiconductor encapsulating device of the present invention are excellent in the moisture resistance and moldability of the resin composition, particularly the filling property of the thin portion, It is possible to manufacture a highly reliable semiconductor encapsulation device which is excellent in die wear resistance, has a small thermal expansion coefficient, has good crack resistance, and has well-balanced characteristics thereof.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｈ０１Ｌ 23/29 23/31 // Ｂ２９Ｋ 63:00 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Office reference number FI technical display location H01L 23/29 23/31 // B29K 63:00
Claims (2)
型フェノール樹脂、（Ｃ）鈍角無機質充填剤および
（Ｄ）平均粒径 0.01 〜 2μm の微細球状充填剤を必須
成分とし、樹脂組成物に対して前記（Ｄ）微細球状充填
剤を 0.1〜60重量％、また前記（Ｃ）及び（Ｄ）の合計
量を50〜90重量％含有してなることを特徴とするエポキ
シ樹脂組成物。1. A resin composition comprising (A) an epoxy resin, (B) a novolac type phenol resin, (C) an obtuse angled inorganic filler and (D) a fine spherical filler having an average particle diameter of 0.01 to 2 μm as essential components. On the other hand, an epoxy resin composition comprising 0.1 to 60% by weight of the (D) fine spherical filler and 50 to 90% by weight of the total amount of the (C) and (D).
型フェノール樹脂、（Ｃ）鈍角無機質充填剤および
（Ｄ）平均粒径 0.01 〜 2μm の微細球状充填剤を必須
成分とし、樹脂組成物に対して前記（Ｄ）微細球状充填
剤を 0.1〜60重量％、また前記（Ｃ）及び（Ｄ）の合計
量を50〜90重量％含有したエポキシ樹脂組成物の硬化物
で、半導体チップが封止されてなることを特徴とする半
導体封止装置。2. A resin composition comprising (A) an epoxy resin, (B) a novolac type phenol resin, (C) an obtuse angled inorganic filler and (D) a fine spherical filler having an average particle diameter of 0.01 to 2 μm as essential components. On the other hand, the semiconductor chip is a cured product of an epoxy resin composition containing 0.1 to 60% by weight of the (D) fine spherical filler and 50 to 90% by weight of the total amount of the (C) and (D). A semiconductor encapsulation device characterized by being stopped.