JPH05238150A - Draw-type optical disc corresponding to compact disc or compact disc-rom - Google Patents

Abstract

PURPOSE:To obtain a DRAW-type optical disc capable of preventing recording sensitivity from depending on wavelength and obtaining satisfactory regenerated signal by forming a recording film containing specific two types of phthalocyanine, a reflective film and a protecting film sequentially on a transparent substrate. CONSTITUTION:A recording film formed using a spin coat technique on a transport substrate consists of a phthalocyanine compound expressed by formula I [X1 to X4 are an alkyl group, an alkoxy group, an alkylthio group, etc.; k, l, m, n are an integer of 0 to 2; M1 is Al, Ga, In, Si, Ge, Sn; Z1 is formula II (R1, R2 are an alkyl group, etc.); y1 is an integer of 1 or 2], and a phthalocyanine compound expressed by formula III [X5 to X8, o, p, q, r and M2 are the same as formula I; Z2 is formula IV (R5 is an alkyl group, etc.); y2 is an integer of 1 or 2]. Further, a protecting film is formed on the recording film following the formula of a vacuum-evaporated metal film, using an ultraviolet curable resin under a spin coat system and thus a DRAW-type optical disc is obtained.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、レーザー光による情報
の記録、再生を行う光ディスクに関する。さらに詳しく
はコンパクトディスク（ＣＤ）あるいはコンパクトディ
スク−ＲＯＭ（ＣＤ−ＲＯＭ）対応の追記型光ディスク
に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an optical disk for recording / reproducing information with a laser beam. More specifically, it relates to a write-once optical disc compatible with a compact disc (CD) or a compact disc-ROM (CD-ROM).

【０００２】[0002]

【従来の技術】集光レーザー光による情報記録媒体の中
で、オーデオ等の音楽再生用としてＣＤ、コンピュータ
−ＲＯＭとして（ＣＤ−ＲＯＭ）が広く普及している。
このようなＣＤ、ＣＤ−ＲＯＭは、通常ポリカーボネー
ト等の透明基板表面にＣＤフォーマット信号またはＣＤ
−ＲＯＭフォーマット信号を有するピット列を射出成形
時に形成し、その上からアルミまたは金等を蒸着あるい
はスパッタリングにより反射膜として設け、さらに保護
膜をコートして作成する。2. Description of the Related Art Among information recording media using a focused laser beam, a CD for reproducing music such as audio and a computer-ROM (CD-ROM) are widely used.
Such a CD or a CD-ROM is usually a CD format signal or a CD on the surface of a transparent substrate such as polycarbonate.
A pit train having a ROM format signal is formed at the time of injection molding, aluminum or gold is provided on the pit train as a reflective film by vapor deposition or sputtering, and a protective film is further coated.

【０００３】このようにして作成された光ディスクの基
板裏面から再生レーザー光（７８０ｎｍ半導体レーザー
光）を照射して、ピットの凹凸による反射率の変化から
各信号を読み取り、情報を再生するものである。しか
し、このようなＣＤまたはＣＤ−ＲＯＭは再生専用であ
り、記録ができないため、追記型光ディスクあるいは書
換え可能な光磁気ディスク等のような編集機能がないと
いう不都合さがあった。A reproducing laser beam (780 nm semiconductor laser beam) is irradiated from the back surface of the substrate of the optical disk thus produced, each signal is read from the change in the reflectance due to the unevenness of the pits, and the information is reproduced. .. However, since such a CD or CD-ROM is for reproduction only and cannot be recorded, there is a disadvantage that it does not have an editing function such as a write-once optical disk or a rewritable magneto-optical disk.

【０００４】一方、編集機能を有する追記型光ディスク
あるいは光磁気ディスクとしては、Ｔｅ等のカルコゲナ
イト系化合物、希土類金属化合物もしくはシアニン、ナ
フタロシアニン等の有機化合物を記録膜としたものが実
用化されている。On the other hand, as a write-once optical disk or magneto-optical disk having an editing function, a recording film made of a chalcogenite compound such as Te, a rare earth metal compound or an organic compound such as cyanine or naphthalocyanine has been put into practical use. ..

【０００５】しかしながら、これらの光ディスクは基板
面からの反射率が３０〜４０％であり、現在のＣＤの国
際規格であるレッドブックに記載されている基板面から
の反射率７０％以上には到達しておらず、現状のままＣ
ＤもしくはＣＤ−ＲＯＭの再生装置により信号の再生を
行うことはできないという問題点がある。このような問
題点を解決するために、シアニン等の記録膜の上に金等
の反射膜を設けて、基板面反射率で７０％以上を確保し
て７８０ｎｍでＣＤフォーマットあるいはＣＤ−ＲＯＭ
フォーマット信号を記録し、ＣＤまたはＣＤ−ＲＯＭの
再生装置で情報を読み出す光ディスクおよび方法が提案
されている。However, these optical discs have a reflectance of 30 to 40% from the substrate surface, and reach a reflectance of 70% or more from the substrate surface described in the current CD international standard Red Book. Not done, C as is
There is a problem that the signal cannot be reproduced by the reproducing device of the D or CD-ROM. In order to solve such a problem, a reflective film of gold or the like is provided on a recording film of cyanine or the like to secure a substrate surface reflectance of 70% or more and a CD format or a CD-ROM at 780 nm.
Optical discs and methods have been proposed for recording format signals and reading information with a CD or CD-ROM player.

【０００６】しかしながら、一般にシアニン化合物は光
安定性が悪いため、ＣＤあるいはＣＤ−ＲＯＭのような
単板構成で直接太陽光にさらされるような使用条件下で
は、記録の信頼性に問題が生ずる可能性がある。However, since the cyanine compound generally has poor photostability, it may cause a problem in the reliability of recording under a use condition such as a single plate structure such as a CD or a CD-ROM which is directly exposed to sunlight. There is a nature.

【０００７】そのため、シアニン色素に代えて、化学
的、物理的安定性の優れたフタロシアニン化合物を記録
膜材料に使用する試みが検討されている。このフタロシ
アニン化合物の場合には、吸収バンドが非常にシャープ
であるため、ＣＤドライブのピックアップに搭載される
半導体レーザーの発振波長の許容範囲（７８０〜８００
ｎｍ程度）で安定した光学特性（反射率および吸収）を
得ることが困難であり、記録感度の波長依存性が大き
く、汎用性のある追記型光ディスクに成りにくいという
問題点がある。従って、現状では安定性に優れ、さらに
記録特性も良好なＣＤまたはＣＤ−ＲＯＭ対応の追記型
光ディスクは提供されていない。Therefore, attempts have been made to use a phthalocyanine compound having excellent chemical and physical stability in place of the cyanine dye as a recording film material. In the case of this phthalocyanine compound, since the absorption band is very sharp, the allowable range of the oscillation wavelength of the semiconductor laser mounted in the pickup of the CD drive (780 to 800).
It is difficult to obtain stable optical characteristics (reflectance and absorption) at about (nm), the wavelength sensitivity of the recording sensitivity is large, and it is difficult to form a versatile write-once optical disc. Therefore, at present, no write-once type optical disc compatible with a CD or a CD-ROM, which has excellent stability and good recording characteristics, has been provided.

【０００８】[0008]

【発明が解決しようとする課題】本発明は、従来の追記
機能、編集機能を有するＣＤあるいはＣＤ−ＲＯＭの持
つ欠点を解決し、安定性に優れ、さらに記録特性も良好
なＣＤ対応またはＣＤ−ＲＯＭ対応の追記型光ディスク
は提供するために、化学的、物理的安定性の優れたフタ
ロシアニン化合物を記録膜材料として用いる場合に生ず
る記録感度の波長依存性を防ぎ、良好な再生信号が得ら
れる記録材料について鋭意検討を行った結果、本発明を
得るに至った。DISCLOSURE OF THE INVENTION The present invention solves the drawbacks of the conventional CD or CD-ROM having the write-once function and the edit function, is excellent in stability, and has excellent recording characteristics. In order to provide a write-once optical disc compatible with ROM, the wavelength dependence of the recording sensitivity that occurs when a phthalocyanine compound having excellent chemical and physical stability is used as a recording film material is prevented, and a good reproduction signal is obtained. As a result of earnest studies on the materials, the present invention has been achieved.

【０００９】[0009]

【課題を解決するための手段】上記のような安定性に優
れ、さらに記録特性も良好なＣＤ、またはＣＤ−ＲＯＭ
対応の追記型光ディスクは以下のようにして実現され
る。透明基板／記録膜／反射膜／保護膜からなり、ＣＤ
フォーマット信号またはＣＤ−ＲＯＭフォーマット信号
の記録を行う追記型光ディスクにおいて、その記録膜が
下記一般式［１］で示される化合物および一般式［２］
で示される化合物からそれぞれ選ばれる２種以上のフタ
ロシアニン化合物より構成されることを特徴とするコン
パクトディスク対応またはコンパクトディスク−ＲＯＭ
対応の追記型光ディスク。A CD or CD-ROM excellent in stability as described above and having good recording characteristics.
A corresponding write-once optical disc is realized as follows. CD consisting of transparent substrate / recording film / reflection film / protective film
In a write-once optical disc for recording a format signal or a CD-ROM format signal, the recording film has a compound represented by the following general formula [1] and a general formula [2].
Compact disc-compatible or compact disc-ROM characterized by comprising two or more kinds of phthalocyanine compounds each selected from the compounds shown in
Compatible write-once optical disc.

【００１０】一般式［１］General formula [1]

【化５】 [Chemical 5]

【００１１】［式中、置換基Ｘ¹ 〜Ｘ⁴ は、それぞれ独
立に置換基を有してもよいアルキル基、置換基を有して
もよいアルコキシ基、置換基を有してもよいアルキルチ
オ基、ハロゲン原子、ニトロ基およびシアノ基を表す。
ｋ、ｌ、ｍおよびｎはそれぞれ独立に０〜２の整数であ
り、置換基Ｘ¹ 〜Ｘ⁴の個数を表す。中心金属Ｍ¹ はＡ
ｌ、Ｇａ、Ｉｎ、Ｓｉ、Ｇｅ、Ｓｎを表す。置換基Ｚ¹
は、[In the formula, each of the substituents X ^{1 to} X ⁴ is independently an alkyl group which may have a substituent, an alkoxy group which may have a substituent, or an alkylthio which may have a substituent. Represents a group, a halogen atom, a nitro group and a cyano group.
k, l, m and n are each independently an integer of 0 to 2 and represent the number of substituents X ^{1 to} X ⁴ . Central metal M ¹ is A
It represents 1, Ga, In, Si, Ge, and Sn. Substituent Z ¹
Is

【００１２】[0012]

【化６】 [Chemical 6]

【００１３】を表す。ここでＲ¹ 、Ｒ² 、Ｒ³ およびＲ
⁴ は置換基を有してもよいアルキル基、置換基を有して
もよいアリール基、置換基を有してもよいアルコキシ基
またはアリーロキシ基を表す。ｙ¹ は、１または２の整
数であり置換基Ｚ¹ の個数を表す。］Represents Where R ¹ , R ² , R ³ and R
⁴ represents an alkyl group which may have a substituent, an aryl group which may have a substituent, an alkoxy group which may have a substituent or an aryloxy group. y ¹ is an integer of 1 or 2 and represents the number of substituents Z ¹ . ]

【００１４】一般式［２］General formula [2]

【化７】 [Chemical 7]

【００１５】［式中、置換基Ｘ⁵ 〜Ｘ⁸ は、それぞれ独
立に置換基を有してもよいアルキル基、置換基を有して
もよいアルコキシ基、置換基を有してもよいアルキルチ
オ基、ハロゲン原子、ニトロ基およびシアノ基を表す。
ｏ、ｐ、ｑおよびｒはそれぞれ独立に０〜２の整数であ
り、置換基Ｘ⁵ 〜Ｘ⁸の個数を表す。中心金属Ｍ² はＡ
ｌ、Ｇａ、Ｉｎ、Ｓｉ、Ｇｅ、Ｓｎを表す。置換基Ｚ²
は、[In the formula, each of the substituents X ^{5 to} X ⁸ is independently an alkyl group which may have a substituent, an alkoxy group which may have a substituent, or an alkylthio which may have a substituent. Represents a group, a halogen atom, a nitro group and a cyano group.
o, p, q and r are each independently an integer of 0 to 2 and represent the number of substituents X ^{5 to} X ⁸ . Central metal M ² is A
It represents 1, Ga, In, Si, Ge, and Sn. Substituent Z ²
Is

【００１６】[0016]

【化８】 [Chemical 8]

【００１７】を表す。ここでＲ⁵ は置換基を有してもよ
いアルキル基、置換基を有してもよいアリール基、置換
基を有してもよいアラルキル基を表す。ｙ² は、１また
は２の整数であり置換基Ｚ² の個数を表す。］Represents Here, R ⁵ represents an alkyl group which may have a substituent, an aryl group which may have a substituent, or an aralkyl group which may have a substituent. y ² is an integer of 1 or 2 and represents the number of substituents Z ² . ]

【００１８】第二の発明は、第一の発明において、一般
式［１］のＸ¹ 〜Ｘ⁴ の置換位置が、それぞれＸ¹ が式
中の１位または４位、Ｘ² が式中の５位または８位、Ｘ
³ が式中の９位または１２位、Ｘ⁴ が式中の１３位また
は１６位であることを特徴とするＣＤ対応またはＣＤ−
ＲＯＭ対応の追記型光ディスク。A second invention is the same as the first invention, wherein the substitution positions of X ^{1 to} X ⁴ in the general formula [1] are such that X ¹ is the 1-position or 4-position in the formula and X ² is the formula. 5th or 8th, X
CD-compatible or CD-, characterized in that ³ is the 9th or 12th position in the formula and X ⁴ is the 13th or 16th position in the formula
A write-once optical disc compatible with ROM.

【００１９】第三の発明は、第一の発明において、一般
式［２］のＸ⁵ 〜Ｘ⁸ の置換位置が、それぞれＸ⁵ が式
中の１位または４位、Ｘ⁶ が式中の５位または８位、Ｘ
⁷ が式中の９位または１２位、Ｘ⁸ が式中の１３位また
は１６位であることを特徴とするＣＤ対応またはＣＤ−
ＲＯＭ対応の追記型光ディスク。A third invention is the same as the first invention, wherein the substitution positions of X ^{5 to} X ⁸ in the general formula [2] are such that X ⁵ is the 1-position or 4-position in the formula and X ⁶ is the formula. 5th or 8th, X
CD-compatible or CD-, wherein ⁷ is the 9th or 12th position in the formula and X ⁸ is the 13th or 16th position in the formula
A write-once optical disc compatible with ROM.

【００２０】第四の発明は、第一ないし第三いずれかの
発明において、一般式［１］および一般式［２］のＸ¹
〜Ｘ⁴ 、Ｘ⁵ 〜Ｘ⁸ およびＺ¹ 、Ｚ² のいずれかに、も
しくはすべてにフッ素が含有された有機置換基が導入さ
れることを特徴とするＣＤ対応またはＣＤ−ＲＯＭ対応
の追記型光ディスク。A fourth invention is the invention according to any one of the first to third inventions, wherein X ¹ of the general formula [1] and the general formula [2] is used.
To X ⁴ , X ^{5 to} X ⁸ and any one or all of Z ¹ and Z ² has an organic substituent containing fluorine, which is a write-once type corresponding to CD or CD-ROM. optical disk.

【００２１】本発明の記録膜が、一般式［１］で示され
るフタロシアニン化合物と一般式［２］で示されるフタ
ロシアニン化合物のにより構成することについては、一
般式［１］で示されるフタロシアニン化合物は、リン含
有の軸置換基の効果により吸収波長が長波長にシフト
し、記録レーザーの発振波長域に吸収を有しレーザー光
を吸収し、熱的変化によってピットが形成されるヒート
モード記録において光学的に高感度化に有効である。The recording film of the present invention is composed of the phthalocyanine compound represented by the general formula [1] and the phthalocyanine compound represented by the general formula [2]. The phthalocyanine compound represented by the general formula [1] is , The absorption wavelength shifts to a long wavelength by the effect of the phosphorus-containing axial substituent, absorbs the laser light by absorbing in the oscillation wavelength range of the recording laser, and pits are formed by a thermal change. Is effective for high sensitivity.

【００２２】しかしながら、この一般式［１］のフタロ
シアニン化合物単独ではレーザー波長域の吸光度が大き
すぎて規格を満足する反射率が得られなくなる場合があ
る。それゆえ、軸置換のアシル基の効果により熱分解点
が低く熱的に高感度化が可能である一般式［２］で示さ
れるフタロシアニン化合物を混合することにより、比較
的吸収が少なくて記録が可能になるため、高感度でしか
も高反射率のメディアとなり、さらに再生波形も良好と
なる。However, the phthalocyanine compound represented by the general formula [1] alone may have too large an absorbance in the laser wavelength region and may not be able to obtain a reflectance satisfying the standard. Therefore, by mixing the phthalocyanine compound represented by the general formula [2], which has a low thermal decomposition point due to the effect of the axially-substituted acyl group and is capable of high thermal sensitivity, absorption is relatively small and recording is possible. Since it becomes possible, the medium has high sensitivity and high reflectance, and the reproduced waveform becomes good.

【００２３】また、置換基にフッ素を導入することによ
り、溶解性が向上すると同時に、基板との界面エネルギ
ーによると考えられるが、記録ピットの状態が良好にな
り、記録信号のコントラストが大きく、さらに再生波形
がきれいになる。また、中心金属の軸置換基にリン含有
の置換基を導入することにより、汎用の汎用のアルコー
ル系およびセロソルブ系の溶媒への溶解性が向上し、光
ディスク基板として汎用に使用されているポリカーボネ
ート基板を侵すことなく塗布できる利点がある。Further, by introducing fluorine as a substituent, the solubility is improved, and at the same time, the state of the recording pit is improved and the contrast of the recording signal is large, which is considered to be due to the interfacial energy with the substrate. The playback waveform becomes clear. Also, by introducing a phosphorus-containing substituent into the axial metal substituent of the central metal, the solubility in general-purpose general-purpose alcohol-based and cellosolve-based solvents is improved, and a polycarbonate substrate generally used as an optical disk substrate. There is an advantage that it can be applied without invading.

【００２４】本発明の一般式［１］で示されるフタロシ
アニン化合物に導入されるＸ¹ 〜Ｘ⁴ および一般式
［２］で示されるフタロシアニン化合物に導入されるＸ
⁵ 〜Ｘ⁸を構成する原子および有機置換基の代表例とし
ては、ハロゲン原子としては塩素、臭素、ヨウ素、フッ
素があり、置換基を有してもよいアルキル基としては、
メチル基、ｎ−ブチル基、ｔｅｒｔ−ブチル基、ステア
リル基、トリクロロメチル基、２−メトキシエチル基、
フタルイミドメチル基、置換基を有してもよいアルコキ
シ基としては、メトキシ基、ｎ−ブトキシ基、ｔｅｒｔ
−ブトキシ基、トリクロロメトキシ基、トリフルオロエ
トキシ基、テトラフルオロプロポキシ基、ペンタフルオ
ロプロポキシ基等を、置換基を有してもよいアルキルチ
オ基としては、ヘキシルチオ基、オクチルチオ基、テト
ラフルオロプロピルチオ基等を挙げられるが、これらに
限定されるものではない。X ^{1 to} X ⁴ introduced into the phthalocyanine compound represented by the general formula [1] and X introduced into the phthalocyanine compound represented by the general formula [2] of the present invention.
Typical examples of the atoms and organic substituents constituting ^{5 to} X ⁸ include chlorine, bromine, iodine and fluorine as the halogen atom, and as the alkyl group which may have a substituent,
Methyl group, n-butyl group, tert-butyl group, stearyl group, trichloromethyl group, 2-methoxyethyl group,
The phthalimidomethyl group and the alkoxy group which may have a substituent include a methoxy group, an n-butoxy group and a tert group.
-Butoxy group, trichloromethoxy group, trifluoroethoxy group, tetrafluoropropoxy group, pentafluoropropoxy group and the like, and as the alkylthio group which may have a substituent, a hexylthio group, an octylthio group, a tetrafluoropropylthio group, etc. However, the present invention is not limited to these.

【００２５】本発明に用いられる一般式［１］で示され
るフタロシアニン化合物と一般式［２］で示されるフタ
ロシアニン化合物との混合比率については、化合物の種
類および組み合わせにより異なるが、一般式［１］示さ
れるフタロシアニン化合物／一般式［２］示されるフタ
ロシアニン化合物＝１／９〜９／１の範囲でよく、さら
に３／７〜７／３の範囲が望ましい。また、記録膜に
は、耐光性、耐環境性等の安定性、繰り返し再生の安定
性をさらに向上させる目的で、酸素クエンチャー、紫外
線吸収剤等の添加剤を加えてもよい。例えば一般式
［３］で示されるジインモニウム系化合物および一般式
［４］で示されるアゾベンゼン系化合物があげられる。The mixing ratio of the phthalocyanine compound represented by the general formula [1] and the phthalocyanine compound represented by the general formula [2] used in the present invention varies depending on the kind and combination of the compounds, but the general formula [1] Phthalocyanine compound represented / phthalocyanine compound represented by the general formula [2] = 1/9 to 9/1, and more preferably 3/7 to 7/3. Further, an additive such as an oxygen quencher or an ultraviolet absorber may be added to the recording film for the purpose of further improving stability such as light resistance and environment resistance and stability of repeated reproduction. For example, a diimmonium-based compound represented by the general formula [3] and an azobenzene-based compound represented by the general formula [4] can be mentioned.

【００２６】一般式［３］General formula [3]

【化９】 [Chemical 9]

【００２７】［式中、ｎは１〜４の整数を表す。Ｒ⁶ は
水素原子もしくはアルキル基を表す。Ｘ^9-はハロゲン原
子、過塩素酸、ホウフッ化水素酸、ヘキサフルオロ酢
酸、フッ化アンチモン、フッ化砒素等の陰イオンを表
す。］[In the formula, n represents an integer of 1 to 4. R ⁶ represents a hydrogen atom or an alkyl group. X ^9- represents an anion such as a halogen atom, perchloric acid, hydrofluoric acid, hexafluoroacetic acid, antimony fluoride or arsenic fluoride. ]

【００２８】一般式［４］General formula [4]

【化１０】 [Chemical 10]

【００２９】［式中、Ｒ⁷ は水素原子もしくはアルキル
基を表す。Ｒ⁸ は水酸基、アルコキシ基、アミノ基ある
いはニトロ基を表す。］[In the formula, R ⁷ represents a hydrogen atom or an alkyl group. R ⁸ represents a hydroxyl group, an alkoxy group, an amino group or a nitro group. ]

【００３０】記録膜の成膜方法としては、ドライプロセ
ス、例えば、真空蒸着法、スパッタリング法によっても
可能であるが、ウェットプロセス、例えば、スピンコー
ト法、ディップ法、スプレー法、ロールコート法あるい
はＬＢ（ラングミュア−ブロジェット）法によっても可
能である。The recording film can be formed by a dry process such as vacuum deposition or sputtering, but a wet process such as spin coating, dipping, spraying, roll coating or LB. It is also possible by the (Langmuir-Blodgett) method.

【００３１】本発明の記録膜素材は、汎用の有機溶媒、
例えば、アルコール系、ケトン系、セロソルブ系、ハロ
ゲン化炭化水素系、フロン系等に溶解するため、生産性
および記録膜の均一性からスピンコート法により成膜す
る方法が好ましい。The recording film material of the present invention comprises a general-purpose organic solvent,
For example, since it dissolves in an alcohol type, a ketone type, a cellosolve type, a halogenated hydrocarbon type, a freon type, etc., a method of forming a film by a spin coating method is preferable from the viewpoint of productivity and uniformity of a recording film.

【００３２】このように、いわゆる塗布法で成膜する場
合には、必要に応じて高分子バインダーを加えても良
い。高分子バインダーとしてはアクリル樹脂、ポリカー
ボネート樹脂、ポリエステル樹脂、ポリアミド樹脂、塩
化ビニル系樹脂、酢酸ビニル系樹脂、ニトロセルロー
ス、フェノール樹脂等が挙げられるがこれに限られるも
のではない。高分子バインダーの混合比としては特に制
限はないが、フタロシアニン化合物に対して３０重量％
以下が好ましい。As described above, when the film is formed by the so-called coating method, a polymer binder may be added if necessary. Examples of the polymer binder include acrylic resin, polycarbonate resin, polyester resin, polyamide resin, vinyl chloride resin, vinyl acetate resin, nitrocellulose, and phenol resin, but are not limited thereto. The mixing ratio of the polymer binder is not particularly limited, but is 30% by weight with respect to the phthalocyanine compound.
The following are preferred.

【００３３】本発明の記録膜層の最適膜厚は、記録膜材
料の種類および組合せにより異なるため特に制限はな
く、５００〜３０００Åが好ましく、さらに１０００〜
２５００Åが最適膜厚範囲である。The optimum film thickness of the recording film layer of the present invention is not particularly limited because it varies depending on the type and combination of recording film materials, and is preferably 500 to 3000 Å, more preferably 1000 to
2500Å is the optimum film thickness range.

【００３４】本発明の反射膜素材としては、金、銀、
銅、白金、アルミニウム、コバルト、スズ等の金属およ
びこれらを主成分とした合金、ＭｇＯ、ＺｎＯ、ＳｎＯ
等の金属酸化物、ＳｉＮ₄ 、ＡｌＮ、ＴｉＮ等の窒化物
等が挙げられるが、絶対反射率が高く安定性に優れてい
る点から金が最適である。このように、反射膜素材とし
ては金が最適であるが、金は高価であるため、安価な光
ディスクを得ることが困難となる問題点がある。この問
題を解決する目的で、金の膜厚を最小限に小さくし、膜
厚不足を他の金属（例えば、アルミニウム、銀等）で補
うような金属積層膜を反射膜に用いることも可能であ
る。The reflective film material of the present invention includes gold, silver,
Metals such as copper, platinum, aluminum, cobalt, tin, and alloys containing these as the main components, MgO, ZnO, SnO
Examples thereof include metal oxides such as SiN ₄ , nitrides such as SiN ₄ , AlN, and TiN. Gold is most preferable because of its high absolute reflectance and excellent stability. As described above, gold is the most suitable material for the reflective film, but gold is expensive, which makes it difficult to obtain an inexpensive optical disc. For the purpose of solving this problem, it is possible to use a metal laminated film for the reflective film, in which the film thickness of gold is minimized and the insufficient film thickness is compensated by another metal (for example, aluminum, silver, etc.). is there.

【００３５】なお、この場合、積層する下層（記録膜に
接する層）の金膜厚は、最低２００Å以上必要であり、
金属積層膜の全膜厚は８００〜２５００Åが最適であ
る。また、場合によっては有機系の高反射膜を使用する
こともできる。このような反射膜の成膜方法としては、
ドライプロセス例えば真空蒸着法、スパッタリング法が
最も好ましいがこれに限られるものではない。本発明の
反射膜の最適膜厚については、特に制限はないが４００
〜１３００Åの範囲が好ましい。In this case, the gold film thickness of the lower layer (layer in contact with the recording film) to be laminated must be at least 200 Å or more,
The total thickness of the metal laminated film is optimally 800 to 2500Å. In addition, an organic high reflection film can be used depending on the case. As a method for forming such a reflective film,
A dry process such as a vacuum vapor deposition method or a sputtering method is most preferable, but not limited to this. The optimum film thickness of the reflective film of the present invention is not particularly limited, but 400
The range of 1300Å is preferred.

【００３６】さらに、反射膜の上より、ディスク特に記
録膜層および反射膜層の化学的劣化（例えば酸化、吸水
等）および物理的劣化（例えば傷、けずれ等）を防ぐ目
的でディスクを保護するための保護層を設ける。保護層
用の材料としては、紫外線硬化型樹脂を用いて、スピン
コートにより塗布し、紫外線照射により硬化させる方法
が好ましいがこれに限られるものではない。 保護層の
最適膜厚については、薄い場合には、保護の効果が低下
し、厚い場合には樹脂の硬化時の収縮によりディスクの
そり等の機械特性の悪化の原因になるため、２〜２０ミ
クロンの範囲で成膜することが好ましい。Further, the disk is protected from above the reflective film in order to prevent chemical deterioration (eg, oxidation, water absorption, etc.) and physical deterioration (eg, scratches, scratches, etc.) of the disk, particularly the recording film layer and the reflective film layer. To provide a protective layer. As a material for the protective layer, a method in which an ultraviolet curable resin is used and applied by spin coating and cured by ultraviolet irradiation is preferable, but the material is not limited thereto. Regarding the optimum film thickness of the protective layer, when it is thin, the effect of protection decreases, and when it is thick, it causes deterioration of mechanical properties such as warpage of the disk due to shrinkage during curing of the resin. It is preferable to form a film in the micron range.

【００３７】また、本発明に用いられるディスク基板と
しては信号の書込や読み出しを行うための光の透過率が
好ましくは８５％以上であり、かつ光学異方性の小さい
ものが望ましい。例えば、ガラス、またはアクリル樹
脂、ポリカーボネート樹脂、ポリエステル樹脂、ポリア
ミド樹脂、塩化ビニル系樹脂、酢酸ビニル系樹脂、ポリ
スチレン系樹脂、ポリオレフィン系樹脂（ポリ−４−メ
チルペンテン等）、ポリエーテルスルホン樹脂などの熱
可塑性樹脂やエポキシ樹脂、アリル樹脂等の熱硬化性樹
脂からなる基板が挙げられる。これらの中で、成形のし
やすさ、ＡＴＩＰ用のウォブル信号および案内溝等の付
与のしやすさなどから熱可塑性樹脂からなるものが好ま
しく、さらに光学特性や機械特性およびコストからみて
アクリル樹脂やポリカーボネート樹脂からなるものが特
に好ましい。 また、ＡＴＩＰ用ウォブル信号および案
内溝などの付与は熱可塑性樹脂を成形（射出成形、圧縮
成形）する際にスタンパーなどを用いて付与する方法が
好ましいが、フォトポリマー樹脂を用いるいわゆる２Ｐ
法による方法によっても行うことができる。The disk substrate used in the present invention preferably has a light transmittance of 85% or more for writing and reading signals and a small optical anisotropy. For example, glass, acrylic resin, polycarbonate resin, polyester resin, polyamide resin, vinyl chloride resin, vinyl acetate resin, polystyrene resin, polyolefin resin (poly-4-methylpentene, etc.), polyether sulfone resin, etc. A substrate made of a thermosetting resin such as a thermoplastic resin, an epoxy resin, or an allyl resin can be used. Among these, those made of a thermoplastic resin are preferable from the viewpoint of easiness of molding, provision of wobble signals for ATIP and guide grooves, and the like. Further, acrylic resins and acrylic resins are preferable in view of optical characteristics, mechanical characteristics and cost. Those made of polycarbonate resin are particularly preferable. The wobble signal for ATIP and the guide groove are preferably provided by using a stamper or the like when molding (injection molding, compression molding) a thermoplastic resin, but so-called 2P using a photopolymer resin is preferable.
It can also be carried out by the method according to the law.

【００３８】本発明の案内溝の形状については、特に制
限はなく矩形、台形あるいはＵ字形であってもよい。ま
た、案内溝の寸法については、記録膜材料の種類および
組合せ等により最適値はそれぞれ異なるが、平均溝幅
（溝深さの１／２の位置の幅）が０．３〜０．６ミクロ
ン、また、溝深さが８００〜２０００オングストローム
の範囲が好ましい。The shape of the guide groove of the present invention is not particularly limited and may be rectangular, trapezoidal or U-shaped. The optimum size of the guide groove varies depending on the type and combination of recording film materials, but the average groove width (width at half the groove depth) is 0.3 to 0.6 microns. The groove depth is preferably in the range of 800 to 2000 angstroms.

【００３９】本発明のディスク形態は、記録後ＣＤある
いはＣＤ−ＲＯＭとして機能する必要があるため、ＣＤ
あるいはＣＤ−ＲＯＭの規格（レッドブック）およびＲ
−ＣＤの規格（オレンジブック）に準拠していることが
好ましい。Since the disc form of the present invention must function as a CD or CD-ROM after recording,
Or CD-ROM standard (Red Book) and R
-It is preferable to comply with the CD standard (Orange Book).

【００４０】[0040]

【実施例】以下、実施例により本発明を具体的に説明す
るが、本発明は以下の実施例に限られるものではない。EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to the following examples.

【００４１】実施例１ 深さ１１００オングストローム、幅０．４５ミクロン、
ピッチ１．６ミクロンの案内溝を有する厚さ１．２０ｍ
ｍ、外径１２０ｍｍ、内径１５ｍｍのポリカーボネート
基板上に、フタロシアニン化合物（ａ）および（ｂ）を
１：1 で混合したものを２，２，３，３−テトラフルオ
ロプロパノールに５０ｍｇ／ｍｌの濃度で溶解し、０．
２ミクロンのフィルタリングを行い塗液を調製し、この
塗液を用いて、スピンコーターにより記録膜厚１３００
オングストロームに成膜した。次に、このようにして得
た記録膜の上に真空蒸着により金を膜厚８００オングス
トロームに成膜した。さらに、この上に紫外線硬化型樹
脂により５ミクロンの保護膜を設けて光ディスクを作成
した。このようにして作成した光ディスクの反射率は７
４％であった。このようにして作成した光ディスクを用
い、波長７８５ｎｍの半導体レーザーを使用して線速度
１．４ｍ／ｓｅｃで、ＥＦＭ−ＣＤフォーマット信号を
記録したところ、最適記録レーザーパワーが７．６ｍＷ
で記録が可能であった。次に、この信号をＣＤプレーヤ
ーによりレーザーパワー０．５ｍＷで再生を行ったとこ
ろ、得られた信号は良好であり、市販のＣＤプレーヤー
に十分かかるレベルであった。Example 1 Depth 1100 Å, Width 0.45 μm,
1.20m thickness with guide grooves with pitch of 1.6 microns
m, an outer diameter of 120 mm, an inner diameter of 15 mm, and a mixture of phthalocyanine compounds (a) and (b) at a ratio of 1: 1 in 2,2,3,3-tetrafluoropropanol at a concentration of 50 mg / ml. Dissolve,
A coating liquid was prepared by filtering with a thickness of 2 microns, and a coating film thickness of 1300 was obtained using a spin coater using this coating liquid.
The film was formed in Angstrom. Next, gold was deposited in a thickness of 800 angstrom on the recording film thus obtained by vacuum vapor deposition. Further, a protective film having a thickness of 5 μm was provided on this with an ultraviolet curable resin to prepare an optical disc. The optical disc thus prepared has a reflectance of 7
It was 4%. When an EFM-CD format signal was recorded at a linear velocity of 1.4 m / sec using a semiconductor laser having a wavelength of 785 nm using the optical disc thus prepared, the optimum recording laser power was 7.6 mW.
It was possible to record at. Next, when this signal was reproduced by a CD player with a laser power of 0.5 mW, the obtained signal was good, and the level was sufficiently high for a commercially available CD player.

【００４２】実施例２ 深さ９００オングストローム、幅０．５２ミクロン、ピ
ッチ１．６ミクロンの案内溝を有する厚さ１．２０ｍ
ｍ、外径１２０ｍｍ、内径１５ｍｍのポリカーボネート
基板上に、フタロシアニン化合物（ｃ）および（ｄ）を
５：３で混合したものをジアセトンアルコールに６５ｍ
ｇ／ｍｌの濃度で溶解し、０．２ミクロンのフィルタリ
ングを行い塗液を調製し、この塗液を用いて、スピンコ
ーターにより記録膜厚１４５０オングストロームに成膜
した。次に、このようにして得た記録膜の上に真空蒸着
により金を膜厚５００オングストロームに成膜した。さ
らに、この上に紫外線硬化型樹脂により５ミクロンの保
護膜を設けて光ディスクを作成した。このようにして作
成した光ディスクの反射率は７１％であった。このよう
にして作成した光ディスクを用い、波長７８５ｎｍの半
導体レーザーを使用して線速度１．４ｍ／ｓｅｃで、Ｅ
ＦＭ−ＣＤフォーマット信号を記録したところ、最適記
録レーザーパワーが７．４ｍＷで記録が可能であった。
次に、この信号をＣＤプレーヤーによりレーザーパワー
０．５ｍＷで再生を行ったところ、得られた信号は良好
であり、市販のＣＤプレーヤーに十分かかるレベルであ
った。Example 2 Depth 900 Å, Width 0.52 μm, Pitch 1.6 μm, and Thickness 1.20 m
m, an outer diameter of 120 mm, an inner diameter of 15 mm, and a mixture of phthalocyanine compounds (c) and (d) at 5: 3 in diacetone alcohol (65 m).
It was dissolved at a concentration of g / ml and filtered by 0.2 micron to prepare a coating liquid. Using this coating liquid, a film having a recording film thickness of 1450 angstrom was formed by a spin coater. Next, gold was deposited in a thickness of 500 angstrom on the recording film thus obtained by vacuum vapor deposition. Further, a protective film having a thickness of 5 μm was provided on this with an ultraviolet curable resin to prepare an optical disc. The optical disc produced in this manner had a reflectance of 71%. Using the optical disc prepared in this manner, a semiconductor laser with a wavelength of 785 nm was used, and the linear velocity was 1.4 m / sec.
When an FM-CD format signal was recorded, it was possible to record at an optimum recording laser power of 7.4 mW.
Next, when this signal was reproduced by a CD player with a laser power of 0.5 mW, the obtained signal was good, and the level was sufficiently high for a commercially available CD player.

【００４３】実施例３ 深さ１５５０オングストローム、幅０．５４ミクロン、
ピッチ１．６ミクロンの案内溝を有する厚さ１．２０ｍ
ｍ、外径１２０ｍｍ、内径１５ｍｍのポリカーボネート
基板上に、フタロシアニン化合物（ｅ）および（ｆ）を
７：３で混合したものをジアセトンアルコールに５０ｍ
ｇ／ｍｌの濃度で溶解し、０．２ミクロンのフィルタリ
ングを行い塗液を調製し、この塗液を用いて、スピンコ
ーターにより記録膜厚１７２０オングストロームに成膜
した。次に、このようにして得た記録膜の上に真空蒸着
により金を膜厚５００オングストロームに成膜した。さ
らに、この上に紫外線硬化型樹脂により５ミクロンの保
護膜を設けて光ディスクを作成した。このようにして作
成した光ディスクの反射率は６９％であった。このよう
にして作成した光ディスクを用い、波長７８５ｎｍの半
導体レーザーを使用して線速度１．４ｍ／ｓｅｃで、Ｅ
ＦＭ−ＣＤフォーマット信号を記録したところ、最適記
録レーザーパワーが７．０ｍＷで記録が可能であった。
次に、この信号をＣＤプレーヤーによりレーザーパワー
０．５ｍＷで再生を行ったところ、得られた信号は良好
であり、市販のＣＤプレーヤーに十分かかるレベルであ
った。Example 3 Depth 1550 Å, Width 0.54 μm,
1.20m thickness with guide grooves with pitch of 1.6 microns
m, an outer diameter of 120 mm, an inner diameter of 15 mm, and a mixture of phthalocyanine compounds (e) and (f) in a ratio of 7: 3 on a polycarbonate substrate in diacetone alcohol of 50 m.
It was dissolved at a concentration of g / ml and filtered at 0.2 μm to prepare a coating liquid. Using this coating liquid, a film having a recording film thickness of 1720 angstrom was formed by a spin coater. Next, gold was deposited in a thickness of 500 angstrom on the recording film thus obtained by vacuum vapor deposition. Further, a protective film having a thickness of 5 μm was provided on this with an ultraviolet curable resin to prepare an optical disc. The reflectance of the optical disc thus prepared was 69%. Using the optical disc prepared in this manner, a semiconductor laser with a wavelength of 785 nm was used, and the linear velocity was 1.4 m / sec.
When an FM-CD format signal was recorded, it was possible to record at an optimum recording laser power of 7.0 mW.
Next, when this signal was reproduced by a CD player with a laser power of 0.5 mW, the obtained signal was good, and the level was sufficiently high for a commercially available CD player.

【００４４】実施例４〜８ 深さ１２５０オングストローム、幅０．５０ミクロン、
ピッチ１．６ミクロンの案内溝を有する厚さ１．２０ｍ
ｍ、外径１２０ｍｍ、内径１５ｍｍのポリカーボネート
基板上に表１で示すフタロシアニン化合物の組み合わせ
および条件で成膜した。次に、このようにして得た記録
膜の上に真空蒸着により金を膜厚５００オングストロー
ムに成膜した。さらに、この上に紫外線硬化型樹脂によ
り５ミクロンの保護膜を設けて光ディスクを作成した。
このようにして作成した光ディスクの反射率および実施
例１と同様な方法で記録、再生を行った場合の最適記録
レーザーパワーを表２に示す。Examples 4-8 Depth 1250 Angstroms, Width 0.50 microns,
1.20m thickness with guide grooves with pitch of 1.6 microns
m, an outer diameter of 120 mm, and an inner diameter of 15 mm was used to form a film on the combination of the phthalocyanine compounds shown in Table 1 and conditions. Next, gold was deposited in a thickness of 500 angstrom on the recording film thus obtained by vacuum vapor deposition. Further, a protective film having a thickness of 5 μm was provided on this with an ultraviolet curable resin to prepare an optical disc.
Table 2 shows the reflectance of the optical disk thus prepared and the optimum recording laser power when recording and reproducing are performed in the same manner as in Example 1.

【００４５】[0045]

【化１１】 フタロシアニン化合物（ａ）[Chemical 11] Phthalocyanine compound (a)

【００４６】[0046]

【化１２】 フタロシアニン化合物（ｂ）[Chemical 12] Phthalocyanine compound (b)

【００４７】[0047]

【化１３】 フタロシアニン化合物（ｃ）[Chemical 13] Phthalocyanine compound (c)

【００４８】[0048]

【化１４】 フタロシアニン化合物（ｄ）[Chemical 14] Phthalocyanine compound (d)

【００４９】[0049]

【化１５】 フタロシアニン化合物（ｅ）[Chemical 15] Phthalocyanine compound (e)

【００５０】[0050]

【化１６】 フタロシアニン化合物（ｆ）[Chemical 16] Phthalocyanine compound (f)

【００５１】[0051]

【化１７】 フタロシアニン化合物（ｇ）[Chemical 17] Phthalocyanine compound (g)

【００５２】[0052]

【化１８】 フタロシアニン化合物（ｈ）[Chemical 18] Phthalocyanine compound (h)

【００５３】[0053]

【化１９】 フタロシアニン化合物（ｉ）[Chemical 19] Phthalocyanine compound (i)

【００５４】[0054]

【化２０】 フタロシアニン化合物（ｊ）[Chemical 20] Phthalocyanine compound (j)

【００５５】[0055]

【化２１】 フタロシアニン化合物（ｋ）[Chemical 21] Phthalocyanine compound (k)

【００５６】[0056]

【化２２】 フタロシアニン化合物（ｌ）[Chemical formula 22] Phthalocyanine compound (l)

【００５７】[0057]

【化２３】 フタロシアニン化合物（ｍ）[Chemical formula 23] Phthalocyanine compound (m)

【００５８】[0058]

【化２４】 フタロシアニン化合物（ｎ）[Chemical formula 24] Phthalocyanine compound (n)

【００５９】[0059]

【化２５】 フタロシアニン化合物（ｏ）[Chemical 25] Phthalocyanine compound (o)

【００６０】[0060]

【化２６】 フタロシアニン化合物（ｐ）[Chemical formula 26] Phthalocyanine compound (p)

【００６１】[0061]

【表１】 [Table 1]

【００６２】[0062]

【表２】 [Table 2]

【００６３】[0063]

【発明の効果】本発明により、従来の追記機能、編集機
能を有するＣＤあるいはＣＤ−ＲＯＭの持つ欠点を解決
し、安定性に優れ、さらに記録感度の波長依存性を防
ぎ、良好な再生信号が得られるＣＤあるいはＣＤ−ＲＯ
Ｍを得ることができた。According to the present invention, the drawbacks of the conventional CD or CD-ROM having the write-once function and the edit function are solved, the stability is excellent, the wavelength dependence of the recording sensitivity is prevented, and a good reproduction signal is obtained. Obtained CD or CD-RO
It was possible to obtain M.

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 透明基板／記録膜／反射膜／保護膜から
なり、コンパクトディスクフォーマット信号またはコン
パクトディスク−ＲＯＭフォーマット信号の記録を行う
追記型光ディスクにおいて、その記録膜が下記一般式
［１］で示される化合物および一般式［２］で示される
化合物からそれぞれ選ばれる２種以上のフタロシアニン
化合物より構成されることを特徴とするコンパクトディ
スク対応またはコンパクトディスク−ＲＯＭ対応の追記
型光ディスク。 一般式［１］ 【化１】 ［式中、置換基Ｘ¹ 〜Ｘ⁴ は、それぞれ独立に置換基を
有してもよいアルキル基、置換基を有してもよいアルコ
キシ基、置換基を有してもよいアルキルチオ基、ハロゲ
ン原子、ニトロ基およびシアノ基を表す。ｋ、ｌ、ｍお
よびｎはそれぞれ独立に０〜２の整数であり、置換基Ｘ
¹ 〜Ｘ⁴の個数を表す。中心金属Ｍ¹ はＡｌ、Ｇａ、Ｉ
ｎ、Ｓｉ、Ｇｅ、Ｓｎを表す。置換基Ｚ¹ は、 【化２】 を表す。ここでＲ¹ 、Ｒ² 、Ｒ³ およびＲ⁴ は置換基を
有してもよいアルキル基、置換基を有してもよいアリー
ル基、置換基を有してもよいアルコキシ基またはアリー
ロキシ基を表す。ｙ¹ は、１または２の整数であり置換
基Ｚ¹ の個数を表す。］ 一般式［２］ 【化３】 ［式中、置換基Ｘ⁵ 〜Ｘ⁸ は、それぞれ独立に置換基を
有してもよいアルキル基、置換基を有してもよいアルコ
キシ基、置換基を有してもよいアルキルチオ基、ハロゲ
ン原子、ニトロ基およびシアノ基を表す。ｏ、ｐ、ｑお
よびｒはそれぞれ独立に０〜２の整数であり、置換基Ｘ
⁵ 〜Ｘ⁸の個数を表す。中心金属Ｍ² はＡｌ、Ｇａ、Ｉ
ｎ、Ｓｉ、Ｇｅ、Ｓｎを表す。置換基Ｚ² は、 【化４】 を表す。ここでＲ⁵ は置換基を有してもよいアルキル
基、置換基を有してもよいアリール基、置換基を有して
もよいアラルキル基を表す。ｙ² は、１または２の整数
であり置換基Ｚ² の個数を表す。］1. A write-once optical disc comprising a transparent substrate / recording film / reflection film / protective film for recording a compact disc format signal or a compact disc-ROM format signal, wherein the recording film has the following general formula [1]: A write-once optical disc compatible with a compact disc or a compact disc-ROM, which is composed of two or more kinds of phthalocyanine compounds each selected from the compound represented by the formula and the compound represented by the general formula [2]. General formula [1] [In the formula, each of the substituents X ^{1 to} X ⁴ independently represents an alkyl group which may have a substituent, an alkoxy group which may have a substituent, an alkylthio group which may have a substituent, or a halogen atom. Represents an atom, a nitro group and a cyano group. k, l, m and n are each independently an integer of 0 to 2 and have a substituent X
Represents the number of ^{1 to} X ⁴ . The central metal M ¹ is Al, Ga, I
n, Si, Ge and Sn are represented. The substituent Z ¹ is Represents. Here, R ¹ , R ² , R ³ and R ⁴ represent an alkyl group which may have a substituent, an aryl group which may have a substituent, an alkoxy group which may have a substituent or an aryloxy group. Represent y ¹ is an integer of 1 or 2 and represents the number of substituents Z ¹ . ] General formula [2] [In the formula, each of the substituents X ^{5 to} X ⁸ is independently an alkyl group which may have a substituent, an alkoxy group which may have a substituent, an alkylthio group which may have a substituent, a halogen atom. Represents an atom, a nitro group and a cyano group. o, p, q and r are each independently an integer of 0 to 2 and have a substituent X
^It represents the number of ^{5 to} X ⁸ . The central metal M ² is Al, Ga, I
n, Si, Ge and Sn are represented. The substituent Z ² is Represents. Here, R ⁵ represents an alkyl group which may have a substituent, an aryl group which may have a substituent, or an aralkyl group which may have a substituent. y ² is an integer of 1 or 2 and represents the number of substituents Z ² . ] 【請求項２】 一般式［１］のＸ¹ 〜Ｘ⁴ の置換位置
が、それぞれＸ¹ が式中の１位または４位、Ｘ² が式中
の５位または８位、Ｘ³ が式中の９位または１２位、Ｘ
⁴ が式中の１３位または１６位であることを特徴とする
請求項１記載のコンパクトディスク対応またはコンパク
トディスク−ＲＯＭ対応の追記型光ディスク。2. The substitution positions of X ^{1 to} X ^{4 in} the general formula [1] are such that X ¹ is the 1-position or 4-position in the formula, X ² is the 5-position or 8-position in the formula, and X ³ is the formula. 9th or 12th, X
^4. The write-once type optical disc corresponding to the compact disc or the compact disc-ROM according to claim 1, wherein ⁴ is the 13th or 16th position in the formula. 【請求項３】 一般式［２］のＸ⁵ 〜Ｘ⁸ の置換位置
が、それぞれＸ⁵ が式中の１位または４位、Ｘ⁶ が式中
の５位または８位、Ｘ⁷ が式中の９位または１２位、Ｘ
⁸ が式中の１３位または１６位であることを特徴とする
請求項１記載のコンパクトディスク対応またはコンパク
トディスク−ＲＯＭ対応の追記型光ディスク。3. The substitution positions of X ^{5 to} X ^{8 in} the general formula [2] are such that X ⁵ is the 1-position or 4-position in the formula, X ⁶ is the 5-position or 8-position in the formula, and X ⁷ is the formula. 9th or 12th, X
^8. The write-once optical disc corresponding to the compact disc or the compact disc-ROM according to claim 1, wherein ⁸ is the 13th or 16th position in the formula. 【請求項４】 一般式［１］および一般式［２］のＸ¹
〜Ｘ⁴ 、Ｘ⁵ 〜Ｘ⁸ およびＺ¹ 、Ｚ² のいずれかに、も
しくはすべてにフッ素が含有された有機置換基が導入さ
れることを特徴とする請求項１ないし３いずれか記載の
コンパクトディスク対応またはコンパクトディスク−Ｒ
ＯＭ対応の追記型光ディスク。4. X ^{1 of} general formula [1] and general formula [2]
~X ^4, X ⁵ ~X ⁸ and Z ^1, Z in any one of ^2, or compact according 3 or claims 1, characterized in that fluorine is organic substituents contained is introduced in all Disk compatible or compact disk-R
A write-once optical disc compatible with OM.