JPH0473188A - Compact disk and additional recording type optical disk responsive to compact disk-rom - Google Patents
Compact disk and additional recording type optical disk responsive to compact disk-romInfo
- Publication number
- JPH0473188A JPH0473188A JP2186856A JP18685690A JPH0473188A JP H0473188 A JPH0473188 A JP H0473188A JP 2186856 A JP2186856 A JP 2186856A JP 18685690 A JP18685690 A JP 18685690A JP H0473188 A JPH0473188 A JP H0473188A
- Authority
- JP
- Japan
- Prior art keywords
- group
- substituent
- film
- compound
- compact disc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔発明の目的〕
（産業上の利用分野）
本発明は、レーザー光による情報の記録、再生を行う光
ディスクに関する。DETAILED DESCRIPTION OF THE INVENTION [Object of the Invention] (Field of Industrial Application) The present invention relates to an optical disc on which information is recorded and reproduced using laser light.
さらに詳しくはコンパクトディスク（ＣＤ）あるいはコ
ンパクトディスク−ＲＯＭ （ＣＤ−ＲＯＭ）対応の追
記型光ディスクに関する。More specifically, the present invention relates to a write-once optical disc compatible with a compact disc (CD) or a compact disc-ROM (CD-ROM).
（従来の技術）
集光レーザー光による情報記録媒体の中で、オーディオ
等の音楽再生用としてＣＤ、コンピータ用ＲＯＭとして
ＣＤ−ＲＯＭが広く普及している。(Prior Art) Among information recording media using focused laser light, CDs are widely used for reproducing music such as audio, and CD-ROMs are widely used as ROMs for computers.
このようなＣＤおよびＣＤ−ＲＯＭは、通常ポリカーボ
ネート等の透明基板表面にＣＤフォーマット信号を有す
るビット列を射出成形時に形成し、その上からアルミニ
ウムまたは金等を蒸着あるいはスパッタリングにより反
射膜として設け、さらに保護層をコートして作成する。Such CDs and CD-ROMs are usually made by forming a bit string with a CD format signal on the surface of a transparent substrate such as polycarbonate during injection molding, and then applying aluminum or gold as a reflective film by vapor deposition or sputtering over the bit string for further protection. Create by coating layers.
このようにして作成した光ディスクの基板の裏面から再
生レーザー光（７８０ｎｍ半導体レーザー光）を照射し
て、ピットの凹凸による反射率の変化から各信号を読取
り、情報を再生するものである。A reproduction laser beam (780 nm semiconductor laser beam) is irradiated from the back side of the substrate of the optical disk thus prepared, and each signal is read from the change in reflectance due to the unevenness of the pits, thereby reproducing information.
しかし、このようなＣＤ、ＣＤ−ＲＯＭは再生専用であ
り情報の記録ができないため、追記型光ディスクあるい
は書換え可能な光磁気ディスク等のような編集機能かな
いという不都合さかあった。However, since such CDs and CD-ROMs are only for reproduction and cannot record information, they have the inconvenience of not having an editing function like write-once optical discs or rewritable magneto-optical discs.
一方、編集機能を有する追記型光ディスクあるいは光磁
気ディスクとしては、Ｔｅ等カルコケナイト系化合物、
希土類金属化合物もしくはシアニン、ナフタロシアニン
等の有機色素等を記録膜としたものが実用化されている
。On the other hand, write-once optical disks or magneto-optical disks with editing functions are made of chalcokenite compounds such as Te,
Recording films made of rare earth metal compounds or organic dyes such as cyanine and naphthalocyanine have been put into practical use.
しかしながら、これらの光ディスクは、基板面からの反
射率が３０〜４０％てあり、現在のＣＤの国際規格であ
るレッドブックに記載されている基板面からの反射率が
７０９６以上には到達しておらず、現状のままＣＤある
いはＣＤ−ＲＯＭの再生装置により信号の再生を行うこ
とはできないという問題点がある。However, these optical discs have a reflectance from the substrate surface of 30 to 40%, and the reflectance from the substrate surface has not reached 7096 or higher, which is listed in the Red Book, the current international standard for CDs. However, there is a problem in that the signal cannot be reproduced by a CD or CD-ROM reproducing device as it is.
このような問題点を解決するために、シアニン等の記録
膜の上に金等の反射膜を設けて、基板面反射率で７０９
６以上を確保して７８０ｎｍでＣＤフォーマットあるい
はＣＤ−ＲＯＭフォーマット信号を記録し、ＣＤまたは
ＣＤ−ＲＯＭの再生装置で情報を読み出す光ディスクお
よび方法が提案されている。In order to solve these problems, a reflective film such as gold is provided on a recording film such as cyanine, and the reflectance of the substrate surface is 709.
Optical discs and methods have been proposed in which a CD format or CD-ROM format signal is recorded at 780 nm with a wavelength of 6 or more, and the information is read out by a CD or CD-ROM playback device.
このようなＣＤおよびＣＤ−ＲＯＭ対応の追記型光ディ
スクの記録膜材料としては、ＣＤまたはＣＤ−ＲＯＭド
ライブ装置のピックアップのレーザー波長に対して吸収
と反射が微妙な割合で必要になるが、レッドブックに規
定されたピックアップのレーザー波長の使用可能な範囲
が７７０〜８１０ｎｍと非常に広いため、この範囲で安
定した光学特性（吸光度、反射率）を得ることは困難で
あり、現在実用化されているＣＤ対応の光ディスクにお
いても、７７０ｎｍでは反射率が７０％を下回っていた
り、また８１０ｎｍでは十分な記録感度がなかったりし
ており、正確にはレッドブックの規格を満足していない
のが現状である。The recording film material for such write-once optical discs compatible with CDs and CD-ROMs must absorb and reflect at a delicate ratio to the laser wavelength of the pickup of the CD or CD-ROM drive device. The usable range of laser wavelengths for pickups stipulated in Even for optical discs compatible with CDs, the reflectance is less than 70% at 770 nm, and there is insufficient recording sensitivity at 810 nm, so the current situation is that they do not accurately meet the Red Book standards. .
（発明が解決しようとする課題）
本発明は、従来の追記機能、編集機能を有するＣＤある
いはＣＤ−ＲＯＭの持つ欠点を解決し、記録膜の構成を
、吸収を得るのための成分と反射率を得るための成分と
の複合により行うことにより、７７０〜８１０ｎｍの波
長範囲で安定した光学特性を実現し、この波長範囲で完
全に記録再生が可能なレッドブックに準拠した光ディス
クを提供するものである。(Problems to be Solved by the Invention) The present invention solves the drawbacks of conventional CDs or CD-ROMs that have write-once and editing functions, and changes the composition of the recording film to include components for absorption and reflectance. By combining it with a component to obtain the following properties, it is possible to achieve stable optical properties in the wavelength range of 770 to 810 nm, and to provide an optical disc that complies with the Red Book and is fully capable of recording and reproducing in this wavelength range. be.
（課顧を解決する手段）
上記のような７７０〜８１０ｎｍの波長範囲で安定した
光学特性を示し、記録再生が可能なＣＤまたはＣＤ−Ｒ
ＯＭ対応の光ディスクは以下のようにして実現される。(Means for solving the problem) A CD or CD-R that exhibits stable optical characteristics in the wavelength range of 770 to 810 nm and is capable of recording and reproducing.
An OM compatible optical disc is realized as follows.
まず第一の発明は透明基板／記録膜／反射膜からなり、
ＣＤフォーマット信号の記録を行う追記型光ディスクに
おいて、その記録膜が７７０〜８１０ｎｍの波長範囲で
の反射率が２０９６以上である化合物（ａ）、および吸
収係数が７７０〜８１０ｎｍの波長範囲で５×１０３
ｃｍ−’以上である化合物（ｂ）、であることを特徴と
するＣＤおよびＣＤ−ＲＯＭ対応の追記型光ディスク。The first invention consists of a transparent substrate/recording film/reflection film,
In a write-once optical disc for recording CD format signals, the recording film contains a compound (a) having a reflectance of 2096 or more in the wavelength range of 770 to 810 nm, and an absorption coefficient of 5 x 103 in the wavelength range of 770 to 810 nm.
1. A write-once optical disc compatible with CDs and CD-ROMs, characterized in that the compound (b) is a compound (b) having a particle size of cm-' or more.
次に第二の発明は上記光ディスクにおいて、記録膜が下
記一般式［１］で示されるフタロシアニン系色素から選
ばれることを特徴とするＣＤおよびＣＤ−ＲＯＭ対応の
追記型光ディスク。The second invention is a write-once optical disc compatible with CDs and CD-ROMs, wherein the recording film is selected from phthalocyanine dyes represented by the following general formula [1].
一般式［１］
［式中、環Ａ ＋ ”−Ａ−はそれぞれ独立にベンゼン
環、ナフタレン環、ピリジン環、ピラジン環またはキノ
キサリン環を表す。General Formula [1] [In the formula, the rings A + ''-A- each independently represent a benzene ring, a naphthalene ring, a pyridine ring, a pyrazine ring or a quinoxaline ring.
Ｍは水素あるいは金属または金属酸化物を表す。M represents hydrogen, a metal, or a metal oxide.
置換基Ｘ１〜Ｘ４は、それぞれ独立に置換基を有しても
よいアルキル基、置換基を有してもよいアリール基、置
換基を有してもよい複素環残基、ハロゲン原子、ニトロ
基、シアノ基、スルホン酸基、−〇Ｒ’ −３Ｒ２−
Ｃｏ○Ｒ３１°とＲ１１とて、あるいはＲ”とＲ１３と
て、４〜７員環を形成していてもよく、これらの４〜７
員環はさらに窒素原子などのへテロ原子を含む複素環て
あってもよい。Substituents X1 to X4 are each independently an alkyl group which may have a substituent, an aryl group which may have a substituent, a heterocyclic residue which may have a substituent, a halogen atom, a nitro group , cyano group, sulfonic acid group, -〇R' -3R2-
Co○R31° and R11 or R'' and R13 may form a 4- to 7-membered ring;
The membered ring may also be a heterocyclic ring containing a heteroatom such as a nitrogen atom.
Ｙは、置換基を有してもよいアルキル基、水素原子、ハ
ロゲン原子、水酸基、−ＯＲ” −３Ｒ’フ−ＣＨ，
ＮＨＣＯＣＨ２ＮＲ” −ＮＨＣＯＲＩ’−Ｎ＝ＮＲ
” −Ｎ＝ＣＨＲ目を表す。Y is an alkyl group that may have a substituent, a hydrogen atom, a halogen atom, a hydroxyl group, -OR''-3R'-CH,
NHCOCH2NR” -NHCORI'-N=NR
” -N=represents CHR.
Ｒ’ 、Ｒ’ 、Ｒ” 、 Ｒ’ 、 Ｒ’、
Ｒ’ 、ＲフＲ” 、 Ｒ” 、 Ｒ
１０％ Ｒ” 、 Ｒ” 、 Ｒ” 、
ＲＩＪＲ”およびＲ”は、互に同一であっても異なっ
ていてもよく、水素原子、置換基を有していてもよいア
ルキル基、置換基を有していてもよいアリール基、置換
基を有していてもよいアシル基、置換基を有していても
よいシクロアルキル基またはポリエーテル基を表し、ま
たはＲ６とＲ７とで、Ｒす。R', R', R'', R', R',
R', RfuR", R", R
10% R", R", R",
RIJR" and R" may be the same or different and represent a hydrogen atom, an alkyl group that may have a substituent, an aryl group that may have a substituent, and a substituent. represents an acyl group which may have one, a cycloalkyl group which may have a substituent, or a polyether group, or R6 and R7 together represent R.
Ｒ１７は、置換基を有してもよいアルキル基、置換基を
有してもよいアルール基、置換基を有してもよいシクロ
アルキル基、あるいはポリエーテル基を表す。R17 represents an alkyl group that may have a substituent, an allul group that may have a substituent, a cycloalkyl group that may have a substituent, or a polyether group.
Ｒ”、Ｒ１”およびＲ”は、互にに同一であっても異な
っていてもよく置換基を有してもよいアルキル基、置換
基を有してもよいシクロアルキル基、置換基を有しても
よいアリール基、置換基を有してもよいアルコキシ基、
置換基を有してもよいアリーロキシ基、ポリエーテル基
、水酸基または水素原子を表す。R'', R1'' and R'' may be the same or different from each other and are an alkyl group which may have a substituent, a cycloalkyl group which may have a substituent, or a cycloalkyl group which may have a substituent. an aryl group that may have a substituent, an alkoxy group that may have a substituent,
Represents an aryloxy group, polyether group, hydroxyl group, or hydrogen atom that may have a substituent.
Ｒ”、Ｒ２２は、互に同一であっても異なっていてもよ
く、置換基を有してもよいアルキル基、置換基を有して
もよいシクロアルキル基、または置換基を有してもよい
アリール基を表す。ｋ、１、ｍ、ｎは、それぞれ独立に
０〜６の整数であり、それぞれ置換基ＸＩ 、Ｘ２ 、
ｘｓ 、ＸＪの個数を表す。R'' and R22 may be the same or different, and are an alkyl group that may have a substituent, a cycloalkyl group that may have a substituent, or a cycloalkyl group that may have a substituent. Represents a good aryl group. k, 1, m, n are each independently an integer of 0 to 6, and each represents a substituent XI, X2,
xs represents the number of XJ.
Ｚは、０〜２の整数であり、置換基Ｙの個数を表す。］
次に第三の発明は上記光ディスクにおいて、記録膜が（
ａ）および（ｂ）の混合してなる膜であることを特徴と
するＣＤおよびＣＤ−ＲＯＭ対応の追記型光ディスク。Z is an integer of 0 to 2 and represents the number of substituents Y. ] Next, the third invention is the above-mentioned optical disc, wherein the recording film is (
A write-once optical disc compatible with CDs and CD-ROMs, characterized in that the film is a mixture of a) and (b).
次に第四の発明は上記光ディスクにおいて、記録膜が（
ａ）の薄膜および（ｂ）の薄膜にて積層されていること
を特徴とするＣＤおよびＣＤ−ＲＯＭ対応の追記型光デ
ィスク。Next, a fourth invention is the above-mentioned optical disc, wherein the recording film is (
A write-once optical disc compatible with CDs and CD-ROMs, characterized in that it is laminated with the thin film of (a) and the thin film of (b).
本発明の記録膜に用いられる記録膜としては７７０〜８
１０ｎｍの波長範囲に比較的高い反射率を有する成分と
、吸収を有する成分との組合せたものでよく、具体的に
はシアニン色素、クロコニック色素、スクアリリウム色
素、ビリリウム色素、テトラヒドロコリン色素、ナフト
コリン色素、ナフトキノン色素、アントラキノン色素、
ジチオール金属錯体等の使用も可能であるが、化学的、
物理的に安定であり近赤外領域に光学感度を有している
という面からフタロシアニン色素、ナフタロシアニン色
素または含窒素フタロシアニン同構体、含窓素ナフタロ
シアニン同構体の中から選ばれた成分により構成された
ものが最適である。The recording film used in the recording film of the present invention is 770-8
It may be a combination of a component with a relatively high reflectance in the wavelength range of 10 nm and a component with absorption, and specific examples include cyanine dyes, croconic dyes, squarylium dyes, biryllium dyes, tetrahydrocholine dyes, and naphthocholine dyes. , naphthoquinone dye, anthraquinone dye,
It is also possible to use dithiol metal complexes, etc., but chemical
Composed of components selected from phthalocyanine dyes, naphthalocyanine dyes, nitrogen-containing phthalocyanine isostructures, and window-containing naphthalocyanine isostructures in terms of physical stability and optical sensitivity in the near-infrared region. The best one is
フタロシアニン色素、ナフタロシアニン色素または含窒
素フタロシアニン同構体、含窒素ナフタロシアニン同構
体には置換基を有してもよいアルキル基、置換基を有し
てもよいアリール基、置換基を有してもよい芳香族複素
環残基、置換基を有してもよいアルコキシ基、置換基を
有してもよいアルキルチオ基、置換基を有してもよいア
リ一口キシ基、置換基を有してもよいアリールチオ基、
置換基を有してもよいアミノ基、置換基を有してもよい
アゾ基、置換基を有してもよいスルホン酸アミド基、置
換基を有してもよいカルボン酸アミド基等の有機置換基
が導入されていてもよい。また中心元素としてはフタロ
シアニンとキレートを形成する金属があげられる。The phthalocyanine dye, naphthalocyanine dye, nitrogen-containing phthalocyanine isoconstruct, and nitrogen-containing naphthalocyanine isoconstruct include an alkyl group that may have a substituent, an aryl group that may have a substituent, and an aryl group that may have a substituent. Good aromatic heterocyclic residues, alkoxy groups that may have substituents, alkylthio groups that may have substituents, alioxy groups that may have substituents, good arylthio group,
Organic groups such as an amino group which may have a substituent, an azo group which may have a substituent, a sulfonic acid amide group which may have a substituent, a carboxylic acid amide group which may have a substituent, etc. A substituent may be introduced. Further, as the central element, metals that form a chelate with phthalocyanine can be mentioned.
具体的にはＨ，Ｎａ、Ｌｉ、Ｃｕ、Ｆｅ、Ｃｏ、Ｎｉ、
Ｚｎ、Ｍｎ、Ｐｂ、Ｓ １ＳＧｅ、Ｓｎ、Ｍｇ、ＡＩ、
Ｇａ、Ｉｎ、Ｔｉ＝Ｏ１■＝０等である。Specifically, H, Na, Li, Cu, Fe, Co, Ni,
Zn, Mn, Pb, S 1SGe, Sn, Mg, AI,
Ga, In, Ti=O1=0, etc.
また、Ａ１、ＧａＳ Ｉｎ５Ｓｉ、ＧｅまたはＳｎなど
の場合には、軸方向置換基として置換基を有してもよい
シロキシ基（例えば、トリメチルシロキシ基、トリエト
キシシロキシ基、ジメチルｔｅｒｔ−ブチルシロキシ基
等）、置換基を有してもよいゲルモキシ基（例えばトリ
メチルシロキシ基、トリエトキシシロキシ基等）、ある
いは置換基を有してもよいホスフィノキシ基（例えば、
ジメチルホスフィノキシ基、ジフェニルホスフィノキシ
基等）、置換基を有してもよいアルコキシ基、置換基を
有してもよいアリーロキシ基等の有機置換基を導入する
ことができる。In addition, in the case of A1, GaS In5Si, Ge or Sn, a siloxy group which may have a substituent as an axial substituent (for example, a trimethylsiloxy group, a triethoxysiloxy group, a dimethyl tert-butylsiloxy group, etc.) is used. ), a germoxy group that may have a substituent (e.g., trimethylsiloxy group, triethoxysiloxy group, etc.), or a phosphinoxy group that may have a substituent (e.g.,
(dimethylphosphinoxy group, diphenylphosphinoxy group, etc.), an alkoxy group which may have a substituent, an aryloxy group which may have a substituent, and the like can be introduced.
記録膜が７７０〜８１０ｎｍの波長範囲での反射率が２
０９６以上である化合物（ａ）、の代表例としては、次
に示す化合物（Ａ）〜（Ｅ）をあげることができる。The recording film has a reflectance of 2 in the wavelength range of 770 to 810 nm.
Representative examples of the compound (a) having a molecular weight of 096 or higher include the following compounds (A) to (E).
（以下余白）
（Ｂ）
（Ｇ）
吸収係数が７７０〜８１０１ｍの波長範囲で５×１０”
ｃｍ””以上である化合物（ｂ）、の代表例としては、
次に示す化合物（Ｆ）〜（Ｊ）をあげることができる６
（以下余白）
（Ｉ）
記録膜が７７０〜８１０ｎｍの波長範囲での反射率が２
０９６以上である化合物（ａ）、および吸収係数が７７
０〜８１０ｎｍの波長範囲で５×１０３ ｃｍ−’以上
である化合物（ｂ）、との混合比率（化合物（ｂ）／化
合物（ａ））はｏ、ｏｉ 〜ｏ。(Left below) (B) (G) Absorption coefficient is 5×10” in the wavelength range of 770 to 8101 m
Typical examples of compound (b) having a molecular weight of cm"" or more include:
The following compounds (F) to (J) can be mentioned6 (hereinafter blank) (I) The recording film has a reflectance of 2 in the wavelength range of 770 to 810 nm.
Compound (a) having an absorption coefficient of 096 or more and an absorption coefficient of 77
The mixing ratio (compound (b)/compound (a)) with compound (b), which is 5×10 cm or more in the wavelength range of 0 to 810 nm, is o, oi to o.
５が好ましく、さらに好ましくは、０．０５〜０．２で
ある。5 is preferred, and more preferably 0.05 to 0.2.
また、化合物（ａ）および化合物（ｂ）を積層する場合
には、基板に対する積層順序は特に限定はなく、とちら
が下層でも上層でもよいが、基板との界面で記録が行わ
れるような化合物系では、基板に対し、化合物（ｂ）、
次いて化合物（ａ）の順序での積層か好ましく、膜厚比
率は、上記混合して用いた場合と同様である。In addition, when layering compound (a) and compound (b), there is no particular limitation on the order in which they are layered on the substrate, and either may be the lower layer or the upper layer. In the system, compound (b),
Next, the compound (a) is preferably laminated in this order, and the film thickness ratio is the same as in the case where the mixture is used.
このような記録膜の成膜方法としては、ドライプロセス
例えば、真空蒸着法、スパッタリング法によっても可能
である。As a method for forming such a recording film, a dry process such as a vacuum evaporation method or a sputtering method can also be used.
また、ウェットプロセス、例えば、スピンコード法、デ
イツプ法、ロールコート法あるいはＬＢ（ラングミュア
−プロジェット）法によっても可能である。It is also possible to use a wet process, such as a spin-coating method, a dip method, a roll-coating method, or an LB (Langmuir-Prodgett) method.
記録膜材料が汎用の有機溶剤例えば、アルコール系、ケ
トン系、セロソルブ系、ハロゲン化炭化水素系、フロン
系、等の溶剤に可溶な場合は、生産性等からスピンコー
ド法によって成膜する方法が望ましい。If the recording film material is soluble in general-purpose organic solvents, such as alcohol-based, ketone-based, cellosolve-based, halogenated hydrocarbon-based, and fluorocarbon-based solvents, the film can be formed by the spin code method for productivity reasons. is desirable.
また、積層膜の場合には、ドライプロセスで成膜した方
が膜間のにじみがなく均一な積層膜が形成てきる。In addition, in the case of a laminated film, forming the film by a dry process results in a more uniform laminated film without bleeding between the films.
このように、いわゆる塗布法で成膜する場合には、必要
に応じて高分子バインダーを加えてもよい。高分子バイ
ンダーとしては、塩化ビニル系樹脂、アクリル系樹脂、
ポリエステル樹脂、ポリアミド樹脂、ポリカーボネート
樹脂、エポキシ樹脂、メタクリル樹脂、酢酸ビニル系樹
脂、ニトロセルロース、フェノール樹脂なとか挙げられ
る。In this way, when forming a film by a so-called coating method, a polymer binder may be added as necessary. Examples of polymer binders include vinyl chloride resin, acrylic resin,
Examples include polyester resin, polyamide resin, polycarbonate resin, epoxy resin, methacrylic resin, vinyl acetate resin, nitrocellulose, and phenol resin.
高分子バインダーを用いる場合、化合物（ａ）および（
ｂ）に対する高分子バインダーの比率は１０重量９６以
下か好ましい。When using a polymer binder, compounds (a) and (
The ratio of polymeric binder to b) is preferably 10% by weight or less.
また、本発明の記録膜の厚さには特に制限はなく、最適
な膜厚も化合物系によって異なるが５゜Ｏ〜３０００Ａ
が好ましく、１ｏｏｏ〜２Ｓｏ。Further, there is no particular limit to the thickness of the recording film of the present invention, and the optimum film thickness varies depending on the compound type, but is between 5°O and 3000A.
is preferable, and 1ooo to 2So.
人が最適膜厚範囲である。Humans are in the optimal film thickness range.
反射膜素材としては、金、銀、銅、白金、アルミニウム
、コバルト、スズ、等の金属、ＭｇＯ１ＺｎＯ，５ｎＯ
１等の金属酸化物、Ｓ ｉＮ ａ、ＡＩＮ、ＴｉＮ、等
の窒化物等が挙げられるか、絶対反射率が高（安定性に
優れている点から金が最適である。Reflective film materials include metals such as gold, silver, copper, platinum, aluminum, cobalt, tin, MgO1ZnO, 5nO
Examples include metal oxides such as No. 1 metal oxides, nitrides such as SiNa, AIN, TiN, etc. Gold is most suitable because of its high absolute reflectance (excellent stability).
また、場合によっては、有機系の高反射膜を使用するこ
ともてきる。In some cases, an organic highly reflective film may also be used.
このような反射膜の成膜方法としては、ドライプロセス
、例えば真空蒸着法、スパッタリング法が最も好ましい
が、これに限られるものではない。The method for forming such a reflective film is most preferably a dry process, such as a vacuum evaporation method or a sputtering method, but is not limited thereto.
さらに、反射膜の上に化学的劣化（例えば、酸化、吸水
等）および物理的劣化（例えば傷、けずれ等）を防ぐ目
的で膜を保護するためのオーバーコート層を設けてもよ
い。Further, an overcoat layer may be provided on the reflective film to protect the film from chemical deterioration (for example, oxidation, water absorption, etc.) and physical deterioration (for example, scratches, scratches, etc.).
オーバーコート層としては、紫外線硬化型樹脂による方
法が一般的であるが、これに限られるものではない。The overcoat layer is generally formed using an ultraviolet curable resin, but is not limited thereto.
ディスク形態は、情報の記録後ＣＤあるいはＣＤ−ＲＯ
Ｍとして機能する必要があるため、ＣＤあるいはＣＤ−
ＲＯＭの規格（レッドブック）およびＲ−ＣＤの規格（
オレンジブック）に準拠していることが好ましい。The disc format is CD or CD-RO after information is recorded.
CD or CD-
ROM standards (Red Book) and R-CD standards (
It is preferable to comply with the Orange Book).
また、本発明に用いられるディスク基板としては、信号
の書込や読み出しを行うための光の透過率が、好ましく
は８５％以上であり、かつ光学異方性の小さいものが望
ましい。Further, the disk substrate used in the present invention preferably has a light transmittance of 85% or more for writing and reading signals, and has small optical anisotropy.
例えば、ガラス、またはアクリル樹脂、ポリカーボネー
ト樹脂、ポリエステル樹脂、ポリアミド樹脂、塩化ビニ
ル系樹脂、酢酸ビニル系樹脂、ポリスチレン系樹脂、ポ
リオレフィン系樹脂（ポリ−４−メチルペンテン等）、
ポリエーテルスル不ン樹脂なとの熱可塑性樹脂やエポキ
シ樹脂、アリル樹脂等の熱硬化性樹脂からなる基板か挙
げられる。これらの中で、成形のしやすさ、案内溝等の
信号の付与のしやすさなどから熱可塑性樹脂からなるも
のが好ましく、さらに光学特性や機械特性およびコスト
からみてアクリル樹脂やポリカーボネート樹脂からなる
ものが特に好ましい。For example, glass, acrylic resin, polycarbonate resin, polyester resin, polyamide resin, vinyl chloride resin, vinyl acetate resin, polystyrene resin, polyolefin resin (poly-4-methylpentene, etc.),
Examples include substrates made of thermoplastic resins such as polyether sulfur resins, thermosetting resins such as epoxy resins, and allyl resins. Among these, those made of thermoplastic resin are preferable due to ease of molding and ease of providing signals such as guide grooves, and more preferably those made of acrylic resin or polycarbonate resin from the viewpoint of optical properties, mechanical properties, and cost. Particularly preferred.
また、案内溝なとの付与は熱可塑性樹脂を成形（射出成
形、圧縮成形）する際にスタンパ−なとを用いて付与す
るか、またはフォトポリマー樹脂を用いるいわゆる２Ｐ
法による方法が好ましい。In addition, guide grooves can be provided using a stamper when molding thermoplastic resin (injection molding, compression molding), or so-called 2P using photopolymer resin.
The method by method is preferred.
（実施例）
以下に、実施例により本発明を具体的に説明するが、本
発明は以下の実施例に限られるものではない。(Examples) The present invention will be specifically explained below using Examples, but the present invention is not limited to the following Examples.
実施例１
深さ８００人、ピッチ１．６μｍのらせん状案内溝を有
する厚さ１．２ｍｍ、外径１２０ｍｍ、内径１５ｍｍの
ポリカーボネート樹脂基板上に、化合物（Ａ）および化
合物（Ｆ）で示されるフタロシアニン化合物の２０：１
の混合物を、エトキシエタノールにて２．０重量９６溶
液にし、スピンコーターを用いて膜厚１２００人に成膜
した。Example 1 Compounds (A) and (F) were placed on a polycarbonate resin substrate with a thickness of 1.2 mm, an outer diameter of 120 mm, and an inner diameter of 15 mm, having spiral guide grooves with a depth of 800 mm and a pitch of 1.6 μm. 20:1 of phthalocyanine compounds
The mixture was made into a 2.0 weight 96% solution with ethoxyethanol, and a film was formed using a spin coater to a film thickness of 1200mm.
次に、このようにして得た塗布膜の上に金を膜厚８００
人で真空蒸着により成膜した。さらに、この上に紫外線
硬化型樹脂により保護層を設けて光ディスクを作成した
。Next, gold was applied to a thickness of 800 mm on the coating film thus obtained.
The film was formed manually by vacuum evaporation. Further, a protective layer was provided thereon using an ultraviolet curable resin to prepare an optical disc.
このようにして作成した光ディスクの反射スペクトルは
第１図に示すように７７０〜８１０ｎｍの波長範囲で、
対Ａ１の反射率で８５％以上ありＣＤの規格を十分満足
している。The reflection spectrum of the optical disc created in this way is in the wavelength range of 770 to 810 nm, as shown in Figure 1.
The reflectance of A1 is 85% or more, which fully satisfies the CD standard.
また、この光ディスクを用い、波長７８０ｎｍの半導体
レーザーを使用して、線速１．３ｍ／ｓｅｅで９ｍＷの
記録パワーてＥＭＦ−ＣＤフォーマット信号を記録した
ところ記録が可能であった。Furthermore, when an EMF-CD format signal was recorded on this optical disc using a semiconductor laser with a wavelength of 780 nm at a linear velocity of 1.3 m/see and a recording power of 9 mW, recording was possible.
記録されたピット列は、長さ０．９〜３．３μｍ、間隔
０．９〜３．３μｍであった。The recorded pit rows had a length of 0.9 to 3.3 μm and an interval of 0.9 to 3.3 μm.
次に、この信号を市販のＣＤプレーヤーにより、線速１
．３ ｍ／ｓｅｅ 、再生出力０．５ｍＷで再生を行っ
たところ得られた信号は良好であり、ＣＤプレーヤーに
十分かかるレベルであった。Next, this signal is processed using a commercially available CD player at a linear velocity of 1
．． When reproduction was performed at a speed of 3 m/see and a reproduction output of 0.5 mW, the obtained signal was good and at a level sufficient for a CD player.
実施例２
深さ８００人、ピッチ１．６μｍのらせん状案内溝を有
する厚さ１．２ｍｍ、外径１２０ｍｍ、内径１５ｍｍの
ポリカーボネート樹脂基板上に、化合物（Ｂ）および化
合物（Ｇ）で示されるフタロシアニン化合物の１０：ｌ
混合物を、エトキシエタノールにて２．０重量％溶液に
し、スピンコーターを用いて膜厚１１００人に成膜した
。Example 2 Compounds (B) and (G) were placed on a polycarbonate resin substrate with a thickness of 1.2 mm, an outer diameter of 120 mm, and an inner diameter of 15 mm, having spiral guide grooves with a depth of 800 people and a pitch of 1.6 μm. 10:l of phthalocyanine compound
The mixture was made into a 2.0% by weight solution with ethoxyethanol, and a film was formed using a spin coater to a film thickness of 1100 mm.
次に、このようにして得た塗布膜の上に金を膜厚８００
人で真空蒸着により成膜した。さらに、この上に紫外線
硬化型樹脂により保護層を設けて光ディスクを作成した
。Next, gold was applied to a thickness of 800 mm on the coating film thus obtained.
The film was formed manually by vacuum evaporation. Further, a protective layer was provided thereon using an ultraviolet curable resin to prepare an optical disc.
このようにして作成した光ディスクの反射スペクトルは
第２図に示すように７７０〜８１０ｎｍの波長範囲で対
ＡＩの反射率で８２９６以上ありＣＤの規格を十分満足
している。As shown in FIG. 2, the reflection spectrum of the optical disk thus prepared has a reflectance of 8296 or more with respect to AI in the wavelength range of 770 to 810 nm, which fully satisfies the CD standard.
また、この光ディスクを用い、波長７８０ｎｍの半導体
レーザーを使用して、線速１．３ ｍ ／ ｓｅｅで９
ｍＷの記録パワーてＥＭＦ−ＣＤフォーマット信号を記
録したところ記録が可能であった。In addition, using this optical disk, a semiconductor laser with a wavelength of 780 nm was used to record 9 at a linear velocity of 1.3 m/see.
When an EMF-CD format signal was recorded with a recording power of mW, recording was possible.
記録されたピット列は、長さ０．９〜−３．３μｍ、間
隔０．９〜３．３μｍであった。The recorded pit rows had a length of 0.9 to -3.3 μm and an interval of 0.9 to 3.3 μm.
次に、この信号を市販のＣＤプレーヤーにより、線速１
．３ ｍ／ｓｅｅ 、再生出力０．５ｍＷで再生を行っ
たところ得られた信号は良好であり、ＣＤプレーヤーに
十分かかるレベルであった。Next, this signal is processed using a commercially available CD player at a linear velocity of 1
．． When reproduction was performed at a speed of 3 m/see and a reproduction output of 0.5 mW, the obtained signal was good and at a level sufficient for a CD player.
実施例３
深さ８００人、ピッチ１．６μｍのらせん状案内溝を有
する厚さ１．２ｍｍ、外径１２０ｍｍ、内径１５ｍｍの
ポリカーボネート樹脂基板上に化合物（Ｃ）で示される
フタロシアニン化合物と化合物（Ｈ）で示されるナフタ
ロシアニン化合物の１０：ｌ混合物をエトキシエタノー
ルにて２．０重量％溶液にし、スピンコーターを用いて
膜厚１３００人に成膜した。Example 3 A phthalocyanine compound represented by Compound (C) and a compound (H A 10:1 mixture of naphthalocyanine compounds represented by ) was made into a 2.0% by weight solution in ethoxyethanol, and a film was formed using a spin coater to a film thickness of 1300 mm.
次に、このようにして得た塗布膜の上に金を膜厚８００
人で真空蒸着により成膜した。さらに、この上に紫外線
硬化型樹脂により保護層を設けて光ディスクを作成した
。Next, gold was applied to a thickness of 800 mm on the coating film thus obtained.
The film was formed manually by vacuum evaporation. Further, a protective layer was provided thereon using an ultraviolet curable resin to prepare an optical disc.
このようにして作成した光ディスクの反射スペクトルは
第３図に示すように７７０〜８１０ｎｍの波長範囲で対
ＡＩの反射率で８５９６以上ありＣＤの規格を十分満足
している。As shown in FIG. 3, the reflection spectrum of the optical disk thus prepared has a reflectance of 8596 or more with respect to AI in the wavelength range of 770 to 810 nm, which fully satisfies the CD standard.
また、この光ディスクを用い、波長７８０ｎｍの半導体
レーザーを使用して、線速１．３ｍ／ｓｅｅで９ｍＷの
記録パワーでＥＭＦ−ＣＤフォーマット信号を記録した
ところ記録が可能であった。Further, when this optical disk was used to record an EMF-CD format signal using a semiconductor laser with a wavelength of 780 nm at a linear velocity of 1.3 m/see and a recording power of 9 mW, recording was possible.
記録されたピット列は、長さ０．９〜３．３μｍ、間隔
０．９〜３．３μｍであった。The recorded pit rows had a length of 0.9 to 3.3 μm and an interval of 0.9 to 3.3 μm.
次に、この信号を市販ＣＤプレーヤーにより、線速１．
３ｍ／ｓｅｅ、再生出力０．５ｍＷで再生を行ったとこ
ろ、得られた信号は良好であり、ＣＤプレーヤーに十分
かかるレベルであった。Next, this signal is processed using a commercially available CD player at a linear velocity of 1.
When reproduction was performed at 3 m/see and a reproduction output of 0.5 mW, the obtained signal was good and at a level sufficient for a CD player.
実施例４
深さ８００人、ピッチ１．６μｍのらせん状案内溝を有
する厚さ１．２ｍｍ、外径１２０ｍｍ、内径１５ｍｍの
ポリカーボネート樹脂基板上に化合物（Ｄ）で示される
フタロシアニン化合物と化合物（１）で示されるナフタ
ロシアニン化合物の１０：２混合物をエトキンエタノー
ルにて２．０重量９６溶液にし、スピンコーターを用い
て膜厚１２００人に成膜した。Example 4 A phthalocyanine compound represented by Compound (D) and Compound (1) were deposited on a polycarbonate resin substrate with a thickness of 1.2 mm, an outer diameter of 120 mm, and an inner diameter of 15 mm, having spiral guide grooves with a depth of 800 people and a pitch of 1.6 μm. ) A 10:2 mixture of the naphthalocyanine compounds represented by (2) was made into a 2.0 weight 96 solution with Etquin ethanol, and a film was formed to a thickness of 1200 mm using a spin coater.
次に、このようにして得た塗布膜の上に金を膜厚８００
人で真空蒸着により成膜した。さらに、この上に紫外線
硬化型樹脂により保護層を設けて光ディスクを作成した
。Next, gold was applied to a thickness of 800 mm on the coating film thus obtained.
The film was formed manually by vacuum evaporation. Further, a protective layer was provided thereon using an ultraviolet curable resin to prepare an optical disc.
このようにして作成した禿ディスクの反射スペクトルは
第４図に示すように７７０〜８１０ｎｍの波長範囲で対
Ａ１の反射率で７８％以上ありＣＤの規格を十分満足し
ている。As shown in FIG. 4, the reflection spectrum of the thus prepared bald disk has a reflectance of 78% or more relative to A1 in the wavelength range of 770 to 810 nm, which fully satisfies the CD standard.
また、この光ディスクを用い、波長７８０ｎｍの半導体
レーザーを使用して、線速１．３ ｍ ／ ｓｅｃで９
ｍＷの記録パワーでＥＭＦ−ＣＤフォーマット信号を記
録したところ記録が可能であった。In addition, using this optical disk, a semiconductor laser with a wavelength of 780 nm was used to generate 9
When an EMF-CD format signal was recorded with a recording power of mW, recording was possible.
記録されたピット列は、長さ０．９〜３．３μｍ、間隔
０．９〜３．３μｍであった。The recorded pit rows had a length of 0.9 to 3.3 μm and an interval of 0.9 to 3.3 μm.
次に、この信号を市販ＣＤプレーヤーにより、線速１．
３ｍ／ｓｅｃ、再生出力０．５ ｍ Ｗで再生を行った
ところ得られた信号は良好であり、市販のＣＤプレーヤ
ーに十分かかるレベルであった。Next, this signal is processed using a commercially available CD player at a linear velocity of 1.
When the signal was reproduced at 3 m/sec and a reproduction output of 0.5 mW, the signal obtained was good and at a level sufficient for a commercially available CD player.
実施例５
深さ８００人、ピッチ１．６μｍのらせん状案内溝を有
する厚さ１．２ｍｍ、外径１２０ｍｍ、内径１５ｍｍの
ポリカーボネート樹脂基板上に化合物（Ｊ）に示される
ナフタロシアニン化合物をシクロヘキセン１．０重量％
溶液によりスピンコーターを用いて１５０人に成膜した
。次いて、化合物（Ｅ）で示されるフタロシアニン化合
物をエトキシエタノール２．０重量％溶液によりスピン
コーターを用いて膜厚９００人に成膜した。Example 5 A naphthalocyanine compound represented by Compound (J) was coated with cyclohexene 1 on a polycarbonate resin substrate with a thickness of 1.2 mm, an outer diameter of 120 mm, and an inner diameter of 15 mm, which had spiral guide grooves with a depth of 800 people and a pitch of 1.6 μm. .0% by weight
A film was formed on 150 people using a spin coater using a solution. Next, a phthalocyanine compound represented by Compound (E) was formed into a film with a thickness of 900 mm using a spin coater using a 2.0% by weight solution of ethoxyethanol.
次に、このようにして得た積層膜の上に金を膜厚８００
人で真空蒸着により成膜した。さらに、この上に紫外線
硬化型樹脂により保護層を設けて光ディスクを作成した
。Next, gold was applied to a thickness of 800 mm on the thus obtained laminated film.
The film was formed manually by vacuum evaporation. Further, a protective layer was provided thereon using an ultraviolet curable resin to prepare an optical disc.
このようにして作成した光ディスクの反射スペクトルは
第５図に示すように７７０〜８１０ｎｍの波長範囲で対
ＡＩの反射率で８５９６以上ありＣＤの規格を十分満足
している。As shown in FIG. 5, the reflection spectrum of the optical disk thus prepared has a reflectance of 8596 or more with respect to AI in the wavelength range of 770 to 810 nm, which fully satisfies the CD standard.
また、この光ディスクを用い、波長７８０ｎｍの半導体
レーザーを使用して、線速１．３ｍ／ｓｅｃで９ｍＷの
記録パワーでＥＭＦ−ＣＤフォーマット信号を記録した
ところ記録が可能であった。Further, when an EMF-CD format signal was recorded on this optical disc using a semiconductor laser with a wavelength of 780 nm at a linear velocity of 1.3 m/sec and a recording power of 9 mW, recording was possible.
記録されたピット列は、長さ０．９〜３．３μｍ１間隔
０．９〜３．３μｍであった。The recorded pit row had a length of 0.9 to 3.3 μm and an interval of 0.9 to 3.3 μm.
次に、この信号を市販ＣＤプレーヤーにより、線速１．
３ ｍ／ｓｅｃ 、再生出力０．５ｍＷで再生を行った
ところ得られた信号は良好であり、ＣＤプレーヤーに十
分かかるレベルであった。Next, this signal is processed using a commercially available CD player at a linear velocity of 1.
When reproduction was performed at a speed of 3 m/sec and a reproduction output of 0.5 mW, the obtained signal was good and at a level sufficient for a CD player.
（発明の効果）
本発明の構成により光ディスクを作成することにより、
追記機能編集機能を有するＣＤあるいはＣＤ−ＲＯＭ対
応の追記型光ディスクを提供することができる。(Effect of the invention) By creating an optical disc according to the configuration of the present invention,
It is possible to provide a write-once optical disc that is compatible with CDs or CD-ROMs and has a write-once editing function.
さらに、その記録膜が７７０〜８１０ｎｍの波長範囲で
の反射率か２０％以上である化合物、および吸収係数か
７７０〜８１０ｎｍの波長範囲て５×１０３ｃｍ−’以
上である化合物を用いることにより、７７０〜８１０ｎ
ｍの波長範囲で安定した光学特性か得られ、レットブッ
ク、士しンンブノクの規格に完全に準拠した光ディスク
か得られる。Furthermore, by using a compound whose recording film has a reflectance of 20% or more in the wavelength range of 770 to 810 nm, and a compound whose absorption coefficient has a wavelength range of 770 to 810 nm of 5 x 103 cm-' or more, ~810n
Stable optical properties can be obtained in the wavelength range of m, and an optical disc can be obtained that completely complies with the Letbook and Shishinunbunoku standards.
第１図〜第５図は、アルミニウムを対照とした、分光反
射曲線図である。
特許比願人
東洋ｒンキ製造株式会社
第
第
図
３図
（ｎｍ）
第２図
第４
図
（ｎｍＪFIGS. 1 to 5 are spectral reflection curve diagrams using aluminum as a control. Patent applicant: Toyo Runk Manufacturing Co., Ltd. Figure 3 (nm) Figure 2 Figure 4 (nmJ
Claims (1)
ィスクフォーマット信号の記録を行う追記型光ディスク
において、その記録膜が７７０〜８１０ｎｍの波長範囲
での反射率が２０％以上である化合物（ａ）、および吸
収係数が７７０〜８１０ｎｍの波長範囲で５×１０＾３
ｃｍ＾−＾１以上である化合物（ｂ）、であることを特
徴とするコンパクトディスクおよびコンパクトディスク
−ＲＯＭ対応の追記型光ディスク。 ２、記録膜が下記一般式［１］で示されるフタロシアニ
ン系色素から選ばれることを特徴とする請求項１記載の
コンパクトディスクおよびコンパクトディスク−ＲＯＭ
対応の追記型光ディスク。一般式［１］ ▲数式、化学式、表等があります▼ ［式中、環Ａ＿１〜Ａ＿４はそれぞれ独立にベンゼン環
、ナフタレン環、ピリジン環、ピラジン環またはキノキ
サリン環を表す。 Ｍは水素あるいは金属または金属酸化物を表す。置換基
Ｘ＾１〜Ｘ＾４は、それぞれ独立に置換基を有してもよ
いアルキル基、置換基を有してもよいアリール基、置換
基を有してもよい複素環残基、ハロゲン原子、ニトロ基
、シアノ基、スルホン酸基、−ＯＲ＾１、−ＳＲ＾２、
−ＣＯＯＲ＾３、▲数式、化学式、表等があります▼、 ▲数式、化学式、表等があります▼、 −Ｎ＝ＮＲ＾１＾５、−Ｎ＝ＣＨＲ＾１＾６を表す。Ｒ
＾１、Ｒ＾２、Ｒ＾３、Ｒ＾４、Ｒ＾５、Ｒ＾６、Ｒ＾
７、Ｒ＾８、Ｒ＾９、Ｒ＾１＾０、Ｒ＾１＾１、Ｒ＾１
＾２＾、Ｒ＾１＾３＾、Ｒ＾１＾４、Ｒ＾１＾５および
Ｒ＾１＾６は、互に同一であっても異なっていてもよく
、水素原子、置換基を有していてもよいアルキル基、置
換基を有していてもよいアリール基、置換基を有してい
てもよいアシル基、置換基を有していてもよいシクロア
ルキル基またはポリエーテル基を表し、またはＲ＾６と
Ｒ＾７とで、Ｒ＾１＾０とＲ＾１＾１とで、あるいはＲ
＾１＾２とＲ＾１＾３とで、４〜７員環を形成していて
もよく、これらの４〜７員環はさらに窒素原子などのヘ
テロ原子を含む複素環であってもよい。 Ｙは、置換基を有してもよいアルキル基、水素原子、ハ
ロゲン原子、水酸基、−ＯＲ＾１＾７、−ＳＲ＾１＾７
、▲数式、化学式、表等があります▼、 ▲数式、化学式、表等があります▼を表 す。 Ｒ＾１＾７は、置換基を有してもよいアルキル基、置換
基を有してもよいアルール基、置換基を有してもよいシ
クロアルキル基、あるいはポリエーテル基を表す。 Ｒ＾１＾８、Ｒ＾１＾９およびＲ＾２＾０は、互に同一
であっても異なっていてもよく置換基を有してもよいア
ルキル基、置換基を有してもよいシクロアルキル基、置
換基を有してもよいアリール基、置換基を有してもよい
アルコキシ基、置換基を有してもよいアリーロキシ基、
ポリエーテル基、水酸基または水素原子を表す。 Ｒ＾２＾１、Ｒ＾２＾２は、互に同一であっても異なっ
ていてもよく、置換基を有してもよいアルキル基、置換
基を有してもよいシクロアルキル基、または置換基を有
してもよいアリール基を表す。ｋ、ｌ、ｍ、ｎは、それ
ぞれ独立に０〜６の整数であり、それぞれ置換基Ｘ＾１
、Ｘ＾２、Ｘ＾３、Ｘ＾４の個数を表す。 Ｚは、０〜２の整数であり、置換基Ｙの個数を表す。］ ３、記録膜が（ａ）および（ｂ）を混合してなる膜であ
ることを特徴とする請求項１記載のコンパクトディスク
およびコンパクトディスク−ＲＯＭ対応の追記型光ディ
スク。 ４、記録膜が（ａ）の薄膜および（ｂ）の薄膜にて積層
されていることを特徴とするコンパクトディスクおよび
コンパクトディスク−ＲＯＭ対応の追記型光ディスク。[Claims] 1. A write-once optical disc consisting of a transparent substrate/recording film/reflection film and recording compact disc format signals, in which the recording film has a reflectance of 20% or more in the wavelength range of 770 to 810 nm. Compound (a) is
A write-once optical disc compatible with a compact disc and a compact disc-ROM, characterized in that it is a compound (b) having a particle diameter of cm^-^1 or more. 2. The compact disc and compact disc-ROM according to claim 1, wherein the recording film is selected from phthalocyanine dyes represented by the following general formula [1].
Compatible write-once optical disc. General formula [1] ▲ Numerical formula, chemical formula, table, etc.▼ [In the formula, rings A_1 to A_4 each independently represent a benzene ring, a naphthalene ring, a pyridine ring, a pyrazine ring, or a quinoxaline ring. M represents hydrogen, a metal, or a metal oxide. Substituents X^1 to X^4 are each independently an alkyl group which may have a substituent, an aryl group which may have a substituent, a heterocyclic residue which may have a substituent, a halogen Atom, nitro group, cyano group, sulfonic acid group, -OR^1, -SR^2,
-COOR^3, ▲There are mathematical formulas, chemical formulas, tables, etc.▼, ▲There are mathematical formulas, chemical formulas, tables, etc.▼, -N=NR^1^5, -N=CHR^1^6. R
^1, R^2, R^3, R^4, R^5, R^6, R^
7, R^8, R^9, R^1^0, R^1^1, R^1
^2^, R^1^3^, R^1^4, R^1^5 and R^1^6 may be the same or different, and each has a hydrogen atom or a substituent. represents an optionally substituted alkyl group, an optionally substituted aryl group, an optionally substituted acyl group, an optionally substituted cycloalkyl group, or a polyether group. , or R^6 and R^7, R^1^0 and R^1^1, or R
^1^2 and R^1^3 may form a 4- to 7-membered ring, and these 4- to 7-membered rings may further be a heterocycle containing a heteroatom such as a nitrogen atom. . Y is an alkyl group that may have a substituent, a hydrogen atom, a halogen atom, a hydroxyl group, -OR^1^7, -SR^1^7
, ▲There are mathematical formulas, chemical formulas, tables, etc.▼, ▲There are mathematical formulas, chemical formulas, tables, etc.▼. R^1^7 represents an alkyl group which may have a substituent, an allur group which may have a substituent, a cycloalkyl group which may have a substituent, or a polyether group. R^1^8, R^1^9 and R^2^0 are an alkyl group which may be the same or different and may have a substituent, and may have a substituent. Cycloalkyl group, optionally substituted aryl group, optionally substituted alkoxy group, optionally substituted aryloxy group,
Represents a polyether group, hydroxyl group, or hydrogen atom. R^2^1 and R^2^2 may be the same or different, and are an alkyl group that may have a substituent, a cycloalkyl group that may have a substituent, or Represents an aryl group that may have a substituent. k, l, m, n are each independently an integer of 0 to 6, and each represents a substituent X^1
, X^2, X^3, and X^4. Z is an integer of 0 to 2 and represents the number of substituents Y. 3. The compact disc and compact disc-ROM compatible write-once optical disc according to claim 1, wherein the recording film is a film formed by mixing (a) and (b). 4. A compact disc and a compact disc-ROM compatible write-once optical disc, characterized in that the recording film is laminated with the thin film of (a) and the thin film of (b).