JPH05232440A - Liquid crystal display device - Google Patents

Abstract

PURPOSE:To obtain a bright STN liquid crystal display device suppressing crosstalk and with high productivity. CONSTITUTION:This liquid crystal display device has a polarizing means consisting of a multicolor dyestuff dissolved in a liquid crystal compsn. layer 6 or of one polarizer sheet provided in the upper side. XT-matrix electrodes consist of an upper transparent electrode 2 and a lower electrode 7. The lower electrode 7 consists of aluminum having roughened surface or aluminum coated with an aluminum oxide layer laminated on a conductive member having higher hardness than the aluminum. The lower electrode 7 acts as a scanning electrode which is longer than the upper transparent electrode 2.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、表示の均一性と明る
さ，生産性が優れたＳＴＮ（スーパーツイステッドネマ
チック）液晶表示装置に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an STN (Super Twisted Nematic) liquid crystal display device having excellent display uniformity, brightness and productivity.

【０００２】[0002]

【従来の技術】従来のＳＴＮ液晶表示装置は、透明なＩ
ＴＯ電極を備えた一対の透明基板，それを挾持する二枚
の偏光板，それに挾持されたねじれ角の大きな液晶分子
配向（例えば１８０〜２７０度）状態，それらを挾持す
る二枚の偏光板，駆動回路とで構成されているが、透明
電極の抵抗値が高いため、駆動回路からの波形信号が歪
み、明るい背景に暗いあるいは暗い背景に明るいパター
ンを表示する際、このパターンと共通の電極上の表示色
が変わる、いわゆる、クロストークが発生するという問
題があった。これは、同じ明（あるいは暗）表示部で
も、同一電極上の他の画素の表示状態によって印加電圧
波形の周波数成分が異なり、かつ電極の高い抵抗値に伴
う波形歪みによる電圧降下の度合いが異なり、液晶にか
かる電圧に差ができるためである。これに対して、現状
製品では電極の厚みを従来の低時分割表示の場合に比べ
て厚くすることで問題が軽減されている。時計，卓上電
子計算機の場合はその厚みが３００から６００Å程度で
あったのが、最近開発されたパソコン，ワークステーシ
ョン用ＳＴＮ液晶表示装置では２０００Åを超える厚み
になっている。2. Description of the Related Art A conventional STN liquid crystal display device has a transparent I
A pair of transparent substrates with TO electrodes, two polarizing plates holding it, two liquid crystal molecule orientations (eg 180 to 270 degrees) with a large twist angle held between them, two polarizing plates holding them, Although it is composed of a drive circuit, because the resistance value of the transparent electrode is high, the waveform signal from the drive circuit is distorted, and when displaying a dark pattern on a bright background or a bright pattern on a dark background, the pattern on the common electrode There is a problem that so-called crosstalk occurs, in which the display color of is changed. This is because even in the same bright (or dark) display part, the frequency component of the applied voltage waveform differs depending on the display state of other pixels on the same electrode, and the degree of voltage drop due to the waveform distortion due to the high resistance value of the electrode also differs. This is because there can be a difference in the voltage applied to the liquid crystal. On the other hand, in the current product, the problem is alleviated by making the electrode thickness thicker than in the case of the conventional low time division display. In the case of watches and desk-top computers, the thickness was around 300 to 600 Å, but in the recently developed STN liquid crystal display devices for personal computers and workstations, it is over 2000 Å.

【０００３】ＳＴＮ液晶表示装置では、透明なＩＴＯ電
極を備えた一対の透明基板，液晶分子といずれも透明な
媒体を用いている。これは液晶の分子配向状態に応じて
光の透過、或いは、反射特性を変える偏光手段として、
これらの媒体を挾持する二枚の偏光板を用いているから
である。偏光板が二枚存在すると、光は四回偏光板を通
過するので、それだけで光利用率は約４０％に低下す
る。その他液晶組成物，ガラス，電極，位相板，表面反
射等による光の損失を考慮すると光利用率は十数％以下
にまで落ちこみ、暗い表示となる。また従来の反射型デ
ィスプレイの場合、明表示部は白色とはほど遠く、どち
らかというと銀色に近い色をしている。これは反射板の
表面を粗してあるものの、入射光が拡散反射するのでは
なく正反射する光量が多いことが原因である。In the STN liquid crystal display device, a pair of transparent substrates each having a transparent ITO electrode and liquid crystal molecules are used as a transparent medium. This is a polarizing means that changes light transmission or reflection characteristics according to the molecular alignment state of the liquid crystal.
This is because two polarizing plates that hold these media are used. When two polarizing plates are present, light passes through the polarizing plates four times, and thus the light utilization rate is reduced to about 40%. In addition, considering the light loss due to the liquid crystal composition, glass, electrodes, phase plate, surface reflection, etc., the light utilization rate drops to less than 10%, resulting in a dark display. Further, in the case of the conventional reflective display, the bright display portion is far from white, and rather has a color close to silver. This is because although the surface of the reflector is roughened, a large amount of light is specularly reflected instead of diffusely reflected by the incident light.

【０００４】こうした画質，明るさ向上の他に歩留まり
の向上は大変重要な問題で、早急な改善が求められてい
る。Besides the improvement of the image quality and the brightness, the improvement of the yield is a very important problem, and the urgent improvement is required.

【０００５】[0005]

【発明が解決しようとする課題】電極の透明性と低抵抗
性は互いにトレードオフの関係にあり、実用的な透明性
とクロストークを抑制しきる低抵抗性との両立は極めて
困難である。The transparency and low resistance of electrodes are in a trade-off relationship with each other, and it is extremely difficult to achieve both practical transparency and low resistance capable of suppressing crosstalk.

【０００６】そして明るさを獲得するには光を損失する
最大の原因である二枚の偏光板を無くすかまたは減らす
必要がある。さらに、現在使用されている反射板の反射
特性の改善が必要である。In order to obtain the brightness, it is necessary to eliminate or reduce the two polarizing plates, which are the largest causes of light loss. Furthermore, it is necessary to improve the reflection characteristics of currently used reflectors.

【０００７】また液晶パネル製造過程、特に電極をＬＳ
Ｉと接続する工程において、金属電極にアルミニウムの
ようなやわらかい金属を用いると、電極が損傷したり剥
離したりする可能性がある。Also, in the manufacturing process of the liquid crystal panel, especially the electrodes are
If a soft metal such as aluminum is used for the metal electrode in the step of connecting with I, the electrode may be damaged or peeled off.

【０００８】本発明の目的は、このような直接駆動型の
ＳＴＮ液晶表示装置におけるクロストークといった表示
ムラを低減し、かつ明るい表示を得、生産性の高いＳＴ
Ｎ液晶表示装置を提供することにある。It is an object of the present invention to reduce display unevenness such as crosstalk in such a direct drive type STN liquid crystal display device, obtain a bright display, and improve the productivity of the ST.
It is to provide an N liquid crystal display device.

【０００９】[0009]

【課題を解決するための手段】本発明は、上記目的を達
成するために、一方が透明な一対の基板，該基板間に正
の誘電異方性及びカイラル物質をもつ液晶組成物層，Ｘ
Ｙマトリクス電極，界面上の液晶分子に２度以上の傾斜
角を与えかつ基板間で液晶分子ねじれ角を220〜２７０
度とする配向膜，基板間に一定のギャップを与えるスペ
ーサを挾持して成る液晶パネル，前記液晶中に溶解され
た多色性色素または一枚の偏光板，前記ＸＹマトリクス
電極に電荷を与えて前記液晶層を駆動する駆動手段とを
備えた液晶表示装置において、前記ＸＹマトリクス電極
の一方が透明電極でありかつ他方の電極が表面に光散乱
性を示す凹凸を有するアルミニウム電極あるいは、表面
層に酸化アルミニウムを有するアルミニウム電極であ
り、かつより高硬度の導電性部材を電極の上側あるいは
下側に積層した該アルミニウム電極を備えたことを特徴
とする液晶表示装置である。In order to achieve the above object, the present invention provides a pair of substrates, one of which is transparent, a liquid crystal composition layer having a positive dielectric anisotropy and a chiral substance between the substrates, and X.
Y matrix electrode, giving a tilt angle of 2 degrees or more to the liquid crystal molecules on the interface, and setting a liquid crystal molecule twist angle between the substrates of 220 to 270
A liquid crystal panel formed by sandwiching a spacer that gives a certain gap between the substrates, a polychromatic dye dissolved in the liquid crystal or a polarizing plate, and a charge is applied to the XY matrix electrodes. In a liquid crystal display device provided with a driving unit for driving the liquid crystal layer, one of the XY matrix electrodes is a transparent electrode and the other electrode is an aluminum electrode having unevenness showing light scattering properties on the surface or a surface layer. A liquid crystal display device comprising an aluminum electrode having aluminum oxide, and further comprising the aluminum electrode in which a conductive member having a higher hardness is stacked above or below the electrode.

【００１０】[0010]

【作用】本発明では、液晶の分子配向状態に応じて光の
透過、或いは、反射特性を変える偏光手段として、液晶
組成物層中に溶解された多色性色素を用いるか、または
偏光板一枚を用いることにより、偏光板を二枚あるいは
一枚排除し、電極の一方が透明電極であれば他方の電極
は不透明でも良い構成を選定した。従って、透明性の制
約が消失したことから透明電極に低抵抗性という点で透
明電極に比べて桁違いに優れた金属物質を積層すること
ができる。よって従来の透明電極に比べ抵抗値が低くな
りクロストークが抑制できる。In the present invention, the polychromatic dye dissolved in the liquid crystal composition layer is used as the polarizing means for changing the light transmission or reflection characteristics depending on the molecular alignment state of the liquid crystal, or the polarizing plate By using two sheets, two or one polarizing plates are eliminated, and if one of the electrodes is a transparent electrode, the other electrode may be opaque. Therefore, since the restriction on the transparency disappears, it is possible to stack a metal material, which is excellent in terms of low resistance, in the transparent electrode by an order of magnitude better than the transparent electrode. Therefore, the resistance value is lower than that of the conventional transparent electrode, and crosstalk can be suppressed.

【００１１】さらにこのアルミニウム電極の表面を粗し
凹凸を設けるか、表面層に酸化アルミニウムを備えるこ
とで、入射光を正反射でなく拡散反射させ、明状態表示
部がより白く見えるよう処理した。ちなみに反射濃度計
（大日本スクリーン製ＤＭ−４００）で本発明による反
射板と現在製品で使用している反射板との散乱光の反射
率を測定したところ、表面を粗したアルミニウムをＩＴ
Ｏに積層した電極及び表面に酸化アルミニウム層を備え
たアルミニウムをＩＴＯに積層した電極ではいずれも８
２％であり、現製品では２５％であった。Further, the surface of the aluminum electrode was roughened to provide irregularities, or the surface layer was provided with aluminum oxide so that the incident light was diffusely reflected instead of being specularly reflected so that the bright state display portion looked whiter. By the way, the reflectance of scattered light between the reflector according to the present invention and the reflector currently used in the product was measured with a reflection densitometer (DM-400 manufactured by Dainippon Screen).
8 for both the electrode laminated on O and the electrode laminated aluminum on the surface of which aluminum having an aluminum oxide layer is laminated.
2%, and the current product was 25%.

【００１２】金属電極にアルミニウムのようなやわらか
い金属を用いると、液晶パネル製造過程、特に電極をＬ
ＳＩと接続する工程で電極が損傷したり剥離したりする
可能性があるが、アルミニウム電極に高硬度の導電性部
材を積層して用いることにより、仮に接続部に於いてア
ルミニウム電極が剥離しても、その下にある導電性部が
電気的接続状態を保つことができる。さらに、特に好適
な高強度導電性材料としてはＩＴＯ，Ｃｒ等があげられ
るが、導電性と高硬度な特性とを備えたものであれば何
でもかまわない。When a soft metal such as aluminum is used for the metal electrode, the liquid crystal panel manufacturing process, especially the electrode
The electrode may be damaged or peeled off in the process of connecting with SI, but if the aluminum electrode is laminated with a high hardness conductive member, the aluminum electrode is peeled off at the connection portion. However, the conductive portion thereunder can maintain an electrically connected state. Further, particularly preferable high-strength conductive materials include ITO and Cr, but any material having conductivity and high hardness may be used.

【００１３】ここで偏光手段を液晶層に含む多色性色素
とした場合の作用を図５を用いて説明する。図５は本発
明の液晶パネルの部分断面を表す。電圧が印加されてい
ない場合は図５のように液晶がねじれた配向状態をとっ
ており、液晶分子１２及び多色性分子１３が基板面内で
種々の方向性を持つことで光を吸収し、暗くなる。一
方、電圧を印加した場合には液晶分子は立上り、図６の
ように見る方向１５と多色性分子の長軸方向１４とが一
致し、明るい状態となる。このような原理については既
にホワイトとテイラーにより示されている（ジャーナル
・オブ・アプライド・フィジックス，４５巻，４７１８
ページ（１９７４年））。Here, the operation when the polarizing means is a polychromatic dye containing a liquid crystal layer will be described with reference to FIG. FIG. 5 shows a partial cross section of the liquid crystal panel of the present invention. When no voltage is applied, the liquid crystal has a twisted alignment state as shown in FIG. 5, and the liquid crystal molecules 12 and the pleochroic molecules 13 have various directions in the plane of the substrate to absorb light. ,Get dark. On the other hand, when a voltage is applied, the liquid crystal molecules rise and the viewing direction 15 and the long-axis direction 14 of the polychromatic molecule coincide with each other as shown in FIG. 6, resulting in a bright state. Such a principle has already been shown by White and Taylor (Journal of Applied Physics, Vol. 45, 4718).
Page (1974)).

【００１４】また偏光板一枚による表示法としては、例
えば、特開昭56−43681 号公報に記載されている方法が
挙げられる。As a display method using one polarizing plate, for example, the method described in JP-A-56-43681 can be mentioned.

【００１５】本発明では、低抵抗値のアルミニウムをＩ
ＴＯに積層した電極を、高抵抗値の透明電極よりも長く
した走査電極することで、トータルの駆動電圧波形の歪
みをより効果的に抑えている。In the present invention, aluminum having a low resistance value is I
The electrodes laminated on the TO are made scanning electrodes longer than the transparent electrode having a high resistance value, so that the distortion of the total drive voltage waveform is more effectively suppressed.

【００１６】[0016]

【実施例】 （実施例１）以下、本発明の実施例１を図１を用いて具
体的に説明する。EXAMPLE 1 Example 1 of the present invention will be specifically described below with reference to FIG.

【００１７】上側基板に厚みが１.１ mmで表面を研磨し
た透明なガラス基板１を用い、下側基板に厚みが３.３
mmで表面を研磨した不透明なプラスチック基板９を用い
る。ガラス基板１の内側には透明なＩＴＯ電極２を、プ
ラスチック基板９には表面を粗し凹凸を持たせて光を散
乱する性質を持つ白色のアルミニウム電極７をＩＴＯ電
極２の上に積層した電極をＸＹマトリクス状に形成し、
駆動回路１０に接続してある。パネルサイズは１０イン
チで６４０×４００画素を構成している。このＸＹマト
リクス状電極のうち、信号電極は厚みが１２００Åの透
明なＩＴＯ電極２で、走査電極はアルミ電極７を積層し
たＩＴＯ電極２である。この走査電極は、信号電極より
長くなっている。信号電極となる透明なＩＴＯ電極２の
シート抵抗は４８Ω／cm² 、走査電極となるＩＴＯに積
層したアルミ電極７のシート抵抗は０.２Ω／cm²であ
る。尚、信号電極は上下二方向から半分ずつ取り出され
ており、１／２００デューティで駆動される。電極上に
はポリイミド系配向膜３（日立化成製ＬＱ−１８００）
がスピンコート法により約５００Åの厚みで塗布されて
いる。これらの基板間に、ネマチック液晶（メルク社製
ＺＬＩ−３６９５−１０）に二色性色素（三井東圧製Ｓ
−３８７，黒）を３ｗｔ％とカイラル物質（メルク社製
Ｓ−８１１）を少量添加した液晶組成物６を挾みシール
剤５で封入してある。ラビング法により配向膜３は表面
処理され、液晶材料に５度の傾斜角（プレチルト）と２
４０度のねじれ角が生じている。直径６.２ μｍのビー
ズスペーサ（ジビニルベンゼンからなる）４が作用して
一定のギャップ６.１ μｍを保持している。A transparent glass substrate 1 having a thickness of 1.1 mm and a polished surface is used for the upper substrate, and a thickness of 3.3 is used for the lower substrate.
An opaque plastic substrate 9 whose surface is polished by mm is used. An electrode formed by stacking a transparent ITO electrode 2 on the inside of the glass substrate 1 and a white aluminum electrode 7 on the plastic substrate 9 having a rough surface and unevenness to scatter light, on the ITO electrode 2. Is formed into an XY matrix,
It is connected to the drive circuit 10. The panel size is 10 inches and constitutes 640 × 400 pixels. Among the XY matrix electrodes, the signal electrode is the transparent ITO electrode 2 having a thickness of 1200Å, and the scanning electrode is the ITO electrode 2 in which the aluminum electrode 7 is laminated. The scan electrodes are longer than the signal electrodes. The sheet resistance of the transparent ITO electrode 2 serving as the signal electrode is 48 Ω / cm ² , and the sheet resistance of the aluminum electrode 7 laminated on the ITO serving as the scanning electrode is 0.2 Ω / cm ² . The signal electrodes are taken out from the upper and lower directions in half and driven at 1/200 duty. Polyimide-based alignment film 3 (LQ-1800 manufactured by Hitachi Chemical) on the electrodes
Is applied in a thickness of about 500Å by spin coating. Between these substrates, a nematic liquid crystal (ZLI-3695-10 manufactured by Merck) and a dichroic dye (S manufactured by Mitsui Toatsu) are used.
The liquid crystal composition 6 containing 3 wt% of -387, black) and a small amount of the chiral substance (S-811 manufactured by Merck & Co., Inc.) is enclosed with the sandwiching sealant 5. The alignment film 3 is surface-treated by a rubbing method, and the liquid crystal material is provided with a tilt angle (pretilt) of 5 degrees.
There is a twist angle of 40 degrees. A bead spacer (made of divinylbenzene) 4 having a diameter of 6.2 μm acts to maintain a constant gap of 6.1 μm.

【００１８】本実施例の液晶表示装置では、図７に示す
ようなクロストークは十分に低く抑制された。しきい値
の周波数特性は比較例１に比べて改善された。また、パ
ネルの光反射率も２４％に達し、十分に明るい。ここで
光反射率とは標準拡散板（フォトリサーチ社製ＲＳ−
１）に光反射率を１００％とした時の相対値を言う。In the liquid crystal display device of this embodiment, the crosstalk as shown in FIG. 7 was suppressed to a sufficiently low level. The threshold frequency characteristics were improved as compared with Comparative Example 1. Moreover, the light reflectance of the panel reaches 24%, which is sufficiently bright. Here, the light reflectance is a standard diffuser plate (RS-made by Photo Research Co., Ltd.
The relative value when the light reflectance is 100% is referred to in 1).

【００１９】（比較例１）走査電極，信号電極はいずれ
も厚みが１２００ÅのＩＴＯ電極で二枚のガラス基板の
内側に形成されている。液晶は実施例１と同様である
が、二色性色素は含まず、偏光板（日東電工社製ＮＰＦ
−Ｇ１２２５ＤＵ）を二枚、ガラスの外側に一枚ずつ備
えてある。さらに片側の偏光板の外側に反射板を一枚備
えている。以上の点を除けば、他は全て実施例１と同じ
構造をとっている。その結果、図７に示すようなクロス
トークが観測され、そのレベルは実施例１の場合に比較
して明らかに高かった。また、光反射率は１５％であ
り、実施例１の場合に比べて暗かった。(Comparative Example 1) The scanning electrodes and the signal electrodes are both ITO electrodes having a thickness of 1200 Å and are formed inside two glass substrates. The liquid crystal was the same as in Example 1, but did not contain a dichroic dye, and a polarizing plate (NPF manufactured by Nitto Denko Corporation)
-G1225DU), one on the outside of the glass. Furthermore, one reflector is provided outside the polarizing plate on one side. Except for the above points, everything else has the same structure as the first embodiment. As a result, crosstalk as shown in FIG. 7 was observed, and the level was obviously higher than that in the case of Example 1. The light reflectance was 15%, which was darker than that in the case of Example 1.

【００２０】（実施例２）以下、本発明の実施例２を図
２を用いて具体的に説明する。(Embodiment 2) Hereinafter, Embodiment 2 of the present invention will be specifically described with reference to FIG.

【００２１】ガラス基板１の上に偏光板１１（日東電工
社製ＮＰＦ−Ｇ１２２５ＤＵ）一枚が備え付けてあり、
二色性色素を含まない液晶組成物６′が挾持されてい
る。走査電極は表面を酸化し光を散乱する性質を持つ白
色のアルミニウム電極７，８をＣｒ電極２′の上に積層
したものである。ツイスト角は２７０度である。以上の
点を除けば、他は全て実施例１と同じ構造をとってい
る。A sheet of polarizing plate 11 (NPF-G1225DU manufactured by Nitto Denko Corporation) is provided on the glass substrate 1,
A liquid crystal composition 6'containing no dichroic dye is held. The scanning electrode is formed by stacking white aluminum electrodes 7 and 8 having a property of oxidizing the surface to scatter light on the Cr electrode 2 '. The twist angle is 270 degrees. Except for the above points, everything else has the same structure as the first embodiment.

【００２２】本実施例の液晶表示装置では、図７に示す
ようなクロストークは十分に低く抑制された。しきい値
の周波数特性は比較例２に比べて改善された。また、パ
ネルの光反射率も２７％に達し、十分に明るい。In the liquid crystal display device of this embodiment, the crosstalk as shown in FIG. 7 was suppressed to a sufficiently low level. The threshold frequency characteristics were improved as compared with Comparative Example 2. In addition, the light reflectance of the panel reaches 27%, which is sufficiently bright.

【００２３】（比較例２）走査電極，信号電極はいずれ
も厚みが１２００ÅのＩＴＯ電極で二枚のガラス基板の
内側に形成されている。偏光板（日東電工社製ＮＰＦ−
Ｇ１２２５ＤＵ）を二枚、ガラスの外側に一枚ずつ備え
てある。さらに片側の偏光板の外側に反射板を一枚備え
ている。以上の点を除けば、他は全て実施例２と同じ構
造をとっている。その結果、図７に示すようなクロスト
ークが観測され、そのレベルは実施例２の場合に比較し
て明らかに高かった。また、光反射率は１６％であり、
実施例２の場合に比べて暗かった。COMPARATIVE EXAMPLE 2 Both the scanning electrodes and the signal electrodes are ITO electrodes having a thickness of 1200 Å and are formed inside the two glass substrates. Polarizing plate (Nitto Denko NPF-
G1225DU) and two on the outside of the glass. Furthermore, one reflector is provided outside the polarizing plate on one side. Except for the above points, everything else has the same structure as the second embodiment. As a result, crosstalk as shown in FIG. 7 was observed, and the level was obviously higher than that in the case of Example 2. The light reflectance is 16%,
It was darker than that of Example 2.

【００２４】（実施例３）以下、本発明の実施例３を図
３を用いて具体的に説明する。(Embodiment 3) Hereinafter, Embodiment 3 of the present invention will be specifically described with reference to FIG.

【００２５】走査電極は表面を酸化し光を散乱する性質
を持つ白色のアルミニウム電極７，８をＩＴＯ電極２の
上に積層したものであるが、ＩＴＯは表示画面の周辺の
みに設置してある。ツイスト角は２６０度である。以上
の点を除けば、他は全て実施例２と同じ構造をとってい
る。The scanning electrode is formed by laminating white aluminum electrodes 7 and 8 having a property of oxidizing the surface to scatter light, on the ITO electrode 2, and the ITO is provided only on the periphery of the display screen. .. The twist angle is 260 degrees. Except for the above points, everything else has the same structure as the second embodiment.

【００２６】本実施例の液晶表示装置では、図７に示す
ようなクロストークは十分に低く抑制された。しきい値
の周波数特性は比較例３に比べて改善された。また、パ
ネルの光反射率も２７％に達し、十分に明るい。In the liquid crystal display device of this example, the crosstalk as shown in FIG. 7 was suppressed to a sufficiently low level. The threshold frequency characteristics were improved as compared with Comparative Example 3. In addition, the light reflectance of the panel reaches 27%, which is sufficiently bright.

【００２７】（比較例３）走査電極，信号電極はいずれ
も厚みが１２００ÅのＩＴＯ電極で二枚のガラス基板の
内側に形成されている。偏光板（日東電工社製ＮＲＦ−
Ｇ１２２５ＤＵ）を二枚、ガラスの外側に一枚ずつ備え
てある。さらに片側の偏光板の外側に反射板を一枚備え
ている。以上の点を除けば、他は全て実施例３と同じ構
造をとっている。その結果、図７に示すようなクロスト
ークが観測され、そのレベルは実施例３の場合に比較し
て明らかに高かった。また、光反射率は１６％であり、
実施例３の場合に比べて暗かった。Comparative Example 3 Both the scanning electrodes and the signal electrodes are ITO electrodes having a thickness of 1200 Å and are formed inside the two glass substrates. Polarizer (NRF-made by Nitto Denko Corporation
G1225DU) and two on the outside of the glass. Furthermore, one reflector is provided outside the polarizing plate on one side. Except for the above points, everything else has the same structure as the third embodiment. As a result, crosstalk as shown in FIG. 7 was observed, and the level was obviously higher than that in the case of Example 3. The light reflectance is 16%,
It was darker than in the case of Example 3.

【００２８】（実施例４）以下、本発明の実施例４を図
４を用いて説明する。(Fourth Embodiment) A fourth embodiment of the present invention will be described below with reference to FIG.

【００２９】プラスチック基板９に表面を酸化し光を散
乱する性質を持つ白色アルミニウム電極７，８を積層
し、その上にＩＴＯ電極２を積層する。ツイスト角は２
２０度である。以上の点を除けば、他は全て実施例２と
同じ構造をとっている。On the plastic substrate 9, white aluminum electrodes 7 and 8 having the property of oxidizing the surface to scatter light are laminated, and the ITO electrode 2 is laminated thereon. Twist angle is 2
It is 20 degrees. Except for the above points, everything else has the same structure as the second embodiment.

【００３０】本実施例の液晶表示装置では、図７に示す
ようなクロストークは十分に低く抑制された。しきい値
の周波数特性は比較例４に比べて改善された。また、パ
ネルの光反射率も２５％に達し、十分に明るい。In the liquid crystal display device of this example, the crosstalk as shown in FIG. 7 was suppressed to a sufficiently low level. The threshold frequency characteristics were improved as compared with Comparative Example 4. In addition, the light reflectance of the panel reaches 25%, which is sufficiently bright.

【００３１】（比較例４）走査電極，信号電極はいずれ
も厚みが１２００ÅのＩＴＯ電極で二枚のガラス基板の
内側に形成されている。偏光板（日東電工社製ＮＰＦ−
Ｇ１２２５ＤＵ）を二枚、ガラスの外側に一枚ずつ備え
てある。さらに片側の偏光板の外側に反射板を一枚備え
ている。以上の点を除けば、他は全て実施例４と同じ構
造をとっている。その結果、図６に示すようなクロスト
ークが観測され、そのレベルは実施例４の場合に比較し
て明らかに高かった。また、光反射率は１５％であり、
実施例４の場合に比べて暗かった。COMPARATIVE EXAMPLE 4 Both the scanning electrodes and the signal electrodes are ITO electrodes having a thickness of 1200 Å and are formed inside the two glass substrates. Polarizing plate (Nitto Denko NPF-
G1225DU) and two on the outside of the glass. Furthermore, one reflector is provided outside the polarizing plate on one side. Except for the above points, everything else has the same structure as in Example 4. As a result, crosstalk as shown in FIG. 6 was observed, and the level was obviously higher than that in the case of Example 4. The light reflectance is 15%,
It was darker than in the case of Example 4.

【００３２】[0032]

【発明の効果】本発明によれば、クロストークは十分に
低く抑制された均一で明るく、生産性の高いＳＴＮ液晶
表示装置が得られる。According to the present invention, a uniform and bright STN liquid crystal display device in which crosstalk is suppressed sufficiently low can be obtained.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明の実施例１の液晶表示装置を模式的に示
した側断面図。FIG. 1 is a side sectional view schematically showing a liquid crystal display device according to a first embodiment of the present invention.

【図２】本発明の実施例２の液晶表示装置を模式的に示
した側断面図。FIG. 2 is a side sectional view schematically showing a liquid crystal display device according to a second embodiment of the present invention.

【図３】本発明の実施例３の液晶表示装置を模式的に示
した側断面図。FIG. 3 is a side sectional view schematically showing a liquid crystal display device according to a third embodiment of the present invention.

【図４】本発明の実施例４の液晶表示装置を模式的に示
した側断面図。FIG. 4 is a side sectional view schematically showing a liquid crystal display device according to a fourth embodiment of the present invention.

【図５】本発明の作用の説明図。FIG. 5 is an explanatory view of the operation of the present invention.

【図６】クロストーク現象を示した説明図。FIG. 6 is an explanatory diagram showing a crosstalk phenomenon.

【図７】液晶ディスプレイに棒グラフを表示した図。FIG. 7 is a diagram showing a bar graph on a liquid crystal display.

【符号の説明】[Explanation of symbols]

１…ガラス基板、２…ＩＴＯ電極、２′…Ｃｒ電極、３
…配向膜、４…ビーズスペーサ、５…シール剤、６…液
晶組成物、６′…二色性色素を含まない液晶組成物、７
…アルミニウム電極、８…酸化アルミニウム層、９…プ
ラスチック基板、１０…駆動回路、１１…偏光板、１２
…液晶分子、１３…二色性色素、１４…色素の吸収軸方
向、１５…見る方向、１６…クロストーク発生領域、１
７…暗状態表示部、１８…明状態表示部。1 ... Glass substrate, 2 ... ITO electrode, 2 '... Cr electrode, 3
... Alignment film, 4 ... Bead spacers, 5 ... Sealing agent, 6 ... Liquid crystal composition, 6 '... Liquid crystal composition containing no dichroic dye, 7
... aluminum electrode, 8 ... aluminum oxide layer, 9 ... plastic substrate, 10 ... driving circuit, 11 ... polarizing plate, 12
... liquid crystal molecule, 13 ... dichroic dye, 14 ... dye absorption axis direction, 15 ... viewing direction, 16 ... crosstalk generation region, 1
7 ... Dark state display section, 18 ... Bright state display section.

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】一方が透明な一対の基板，前記基板間に正
の誘電異方性及びカイラル物質をもつ液晶組成物層，Ｘ
Ｙマトリクス電極，界面上の液晶分子に２度以上の傾斜
角を与え基板間で液晶分子ねじれ角を２２０〜２７０度
とする配向膜，基板間に一定のギャップを与えるスペー
サを挾持して成る液晶パネル，前記液晶中に溶解されタ
多色性色素または一枚の偏光板，前記ＸＹマトリクス電
極に電荷を与えて前記液晶層を駆動する駆動手段とを備
えた液晶表示装置において、 前記ＸＹマトリクス電極の一方が透明電極であり他方の
電極が表面に光散乱性を示す凹凸をもつアルミニウム電
極あるいは、表面層に酸化アルミニウムを有するアルミ
ニウム電極であり、より高硬度の導電性部材を電極の上
側あるいは下側に積層した前記アルミニウム電極を備え
たことを特徴とする液晶表示装置。1. A pair of substrates, one of which is transparent, a liquid crystal composition layer having a positive dielectric anisotropy and a chiral substance between the substrates, and X.
A liquid crystal formed by sandwiching a Y matrix electrode, an alignment film that gives a tilt angle of 2 degrees or more to liquid crystal molecules on the interface so that the twist angle of liquid crystal molecules is 220 to 270 degrees between substrates, and a spacer that gives a constant gap between the substrates. A liquid crystal display device comprising: a panel, a polychromatic dye dissolved in the liquid crystal or a single polarizing plate, and a driving means for driving the liquid crystal layer by applying an electric charge to the XY matrix electrode, wherein the XY matrix electrode One is a transparent electrode and the other electrode is an aluminum electrode having unevenness showing light scattering properties on the surface or an aluminum electrode having aluminum oxide on the surface layer, and a conductive member having a higher hardness is provided above or below the electrode. A liquid crystal display device comprising the aluminum electrode laminated on the side. 【請求項２】請求項１において、前記アルミニウム電極
がＸＹマトリクスのうちより長い方の電極である液晶表
示装置。2. The liquid crystal display device according to claim 1, wherein the aluminum electrode is a longer electrode of an XY matrix. 【請求項３】請求項１において、前記アルミニウム電極
が走査電極である液晶表示装置。3. The liquid crystal display device according to claim 1, wherein the aluminum electrode is a scanning electrode.