JPH05217225A - Optical recording medium - Google Patents

Abstract

PURPOSE:To prevent wear, damage and head crush by forming a recording layer on a substrate and further forming a protective layer of a curable resin contg. a slipping agent on the recording layer optionally through other layer in-between. CONSTITUTION:When a recording layer is formed on a substrate and a protective layer of a curable resin contg. a slipping agent is further formed on the recording layer optionally with other layer in-between to obtain an optical recording medium, the protective layer is made of a blend of a resin curable with energetic beams such as UV or a thermosetting resin as a so-called hard coating agent with the slipping agent. The resin curable with energetic beams such as UV is preferably based on a compd. having one or more (meth)acrylate groups such as epoxy acrylate or urethane acrylate.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は光記録媒体に係り、特に
磁界変調型光磁気記録に用いて好適な表面の耐久性に優
れ、且つ塵埃付着の少ない記録媒体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an optical recording medium, and more particularly to a recording medium suitable for use in magnetic field modulation type magneto-optical recording, which has excellent surface durability and has little dust adhesion.

【０００２】[0002]

【従来の技術】近年、浮上型磁気ヘッドを用いた磁界変
調記録方式によるオーバライト（重ね書き）を行なう光
記録媒体が種々提案されている（電子材料１９８８年７
月号第７６頁〜８２頁、特開昭６３−２２９６４３号
等）。上記磁界変調記録方式はレーザ光の強度を固定
し、外部印加磁界の向きを変調する方式であり、磁気ヘ
ッドのコイルに流す電流を変調し、外部印加磁界の変調
を行うものである。2. Description of the Related Art In recent years, various optical recording media have been proposed for overwriting by a magnetic field modulation recording method using a floating magnetic head (electronic material 1988, July 1988).
Monthly issue, pages 76 to 82, JP-A-63-229643, etc.). The magnetic field modulation recording method is a method in which the intensity of laser light is fixed and the direction of an externally applied magnetic field is modulated, and the externally applied magnetic field is modulated by modulating the current flowing in the coil of the magnetic head.

【０００３】[0003]

【発明が解決しようとする課題】レーザ光による局部的
に加熱された光磁気記録層の磁化を反転するために必要
な磁界は磁気ヘッドの近傍にのみ発生しており、磁気ヘ
ッドと光磁気記録層の距離はできるだけ近づける必要が
ある。浮上型磁気ヘッドは気体潤滑作用を利用して低浮
上できるものであり、その構成を簡素にするためにコン
タクトスタートストップ（以下ＣＳＳと略す。）方式が
採用されている。この場合、光記録媒体の高速回転によ
る空気との摩擦、あるいはＣＳＳ動作に伴う光記録媒体
と磁気ヘッドの接触等により、光記録媒体に静電気が発
生し、装置内部の塵埃が光記録媒体の表面に捕集される
ことになる。捕集された塵埃が光ヘッドのレンズを汚染
することによって絞り込みスポットの特性が低下し、不
完全記録や再生誤りを発生させたりする。また、光記録
媒体の非運転時、あるいは回転の起動、停止時に該磁気
ヘッドとの接触摺動により、該光記録媒体表面及び磁気
ヘッドに摩耗、損傷等やヘッドクラッシュが発生し易く
なる等という問題点があった。The magnetic field necessary for reversing the magnetization of the magneto-optical recording layer locally heated by the laser beam is generated only near the magnetic head. The layers should be as close together as possible. The levitation type magnetic head is capable of low levitation by utilizing a gas lubrication action, and a contact start stop (hereinafter abbreviated as CSS) system is adopted in order to simplify the configuration. In this case, static electricity is generated in the optical recording medium due to friction with air due to high-speed rotation of the optical recording medium, contact between the optical recording medium and the magnetic head accompanying CSS operation, etc., and dust inside the device causes dust on the surface of the optical recording medium. Will be collected by. The collected dust contaminates the lens of the optical head to deteriorate the characteristics of the narrowed spot, resulting in incomplete recording and reproduction error. Further, when the optical recording medium is not in operation, or when the optical recording medium is started or stopped, the sliding contact with the magnetic head makes it easier for the surface of the optical recording medium and the magnetic head to be worn, damaged, or crushed. There was a problem.

【０００４】[0004]

【課題を解決するための手段】本発明者等は上記した磁
界変調記録方式による光記録媒体の問題点に鑑み、ＣＳ
Ｓ動作によるヘッドクラッシュの発生のない、すなわち
表面硬度が高く、且つ媒体表面に塵埃が付着しにくい光
記録媒体を提供すべく鋭意検討を重ねた結果、基板に設
けた記録層上に特殊の保護層を設けることにより上記目
的が達成できることを見出し、本発明を完成するに至っ
た。In view of the problems of the optical recording medium based on the magnetic field modulation recording method described above, the present inventors have proposed the CS
As a result of intensive studies to provide an optical recording medium that does not cause head crash due to S operation, that is, has high surface hardness and is less likely to have dust attached to the medium surface, special protection is provided on the recording layer provided on the substrate. The inventors have found that the above object can be achieved by providing a layer, and have completed the present invention.

【０００５】すなわち、本発明の要旨は基板上に記録層
を形成し、該記録層上に直接または他の層を介してスリ
ップ剤を含有する硬化性樹脂からなる保護層を設けたこ
とを特徴とする光記録媒体に存する。以下、本発明を詳
細に説明する。本発明において用いられる基板として
は、ポリカーボネート樹脂、アクリル樹脂、ポリオレフ
ィン樹脂等の樹脂基板が挙げられる。この基板の厚みは
１〜２mm程度が一般的である。That is, the gist of the present invention is that a recording layer is formed on a substrate, and a protective layer made of a curable resin containing a slip agent is provided on the recording layer directly or through another layer. Exists in the optical recording medium. Hereinafter, the present invention will be described in detail. Examples of the substrate used in the present invention include resin substrates such as polycarbonate resin, acrylic resin, and polyolefin resin. The thickness of this substrate is generally about 1 to 2 mm.

【０００６】このような樹脂基板上に形成する光磁気記
録層の層構成としては特に制限はなく、公知の光磁気記
録層の層構成を採用することができる。例えばＴｂＦ
ｅ、ＴｂＦｅＣｏ、ＴｂＣｏ、ＤｙＴｂＦｅＣｏ等の希
土類と遷移金属との非晶質磁性合金、ＭｎＢｉ、ＭｎＣ
ｕＢｉ等の多結晶垂直磁化膜等が用いられる。光磁気記
録層としては単一の層を用いても良いし、ＧｄＴｂＦｅ
／ＴｂＦｅのように２層以上の記録層を重ねて用いても
良い。The layer structure of the magneto-optical recording layer formed on such a resin substrate is not particularly limited, and a known layer structure of the magneto-optical recording layer can be adopted. For example, TbF
e, TbFeCo, TbCo, DyTbFeCo, and other amorphous magnetic alloys of rare earths and transition metals, MnBi, MnC
A polycrystalline perpendicular magnetization film such as uBi is used. A single layer may be used as the magneto-optical recording layer, or GdTbFe may be used.
Two or more recording layers such as / TbFe may be stacked and used.

【０００７】上記基板と光磁気記録層との間には、干渉
層を設けることもできる。この層は、高屈折率の透明膜
による光の干渉効果により反射率を落とすことでノイズ
を低下させＣ／Ｎ比を向上させるためのものである。干
渉層は単層膜でも多層膜でも良い。干渉層の構成物質と
しては、金属酸化物や金属窒化物が用いられる。金属酸
化物としてはＡｌ₂ Ｏ₃ 、Ｔａ₂ Ｏ₅ 、ＳｉＯ₂ 、Ｓｉ
Ｏ、ＴｉＯ₂ 等の金属酸化物単独又はこれらの混合物、
或るいはＡｌ−Ｔａ−Ｏの複合酸化物等が挙げられる。
更に、これらの酸化物に、他の元素、例えば、Ｔｉ、Ｚ
ｒ、Ｗ、Ｍｏ、Ｙｂ等が酸化物の形で単独で、或るいは
Ａｌ、Ｔａと複合して酸化物を形成しているものでも良
い。これらの金属酸化物よりなる干渉層は、緻密で外部
からの水分や酸素の侵入を防ぐことができ、また、耐食
性が高く後述の反射層との反応性も小さい。更に、基板
として樹脂基板を使用する場合、基板を構成する樹脂と
の密着性にも優れている。An interference layer may be provided between the substrate and the magneto-optical recording layer. This layer is for reducing the noise and improving the C / N ratio by lowering the reflectance due to the light interference effect of the high refractive index transparent film. The interference layer may be a single layer film or a multilayer film. A metal oxide or a metal nitride is used as a constituent material of the interference layer. As the metal oxide, Al ₂ O ₃ , Ta ₂ O ₅ , SiO ₂ , Si
Metal oxides such as O and TiO ₂ or a mixture thereof,
Or, an Al-Ta-O composite oxide or the like can be used.
In addition to these oxides, other elements such as Ti, Z
R, W, Mo, Yb and the like may be alone in the form of an oxide, or may be those which form an oxide by being combined with Al or Ta. The interference layer made of these metal oxides is dense and can prevent invasion of moisture and oxygen from the outside, has high corrosion resistance, and has low reactivity with the reflection layer described later. Furthermore, when a resin substrate is used as the substrate, it has excellent adhesion to the resin that constitutes the substrate.

【０００８】金属窒化物としては、窒化シリコン、窒化
アルミニウム等が挙げられる。これらの金属窒化物のう
ち、特に緻密で外部からの水分や酸素の侵入を防ぐ効果
に優れることから、窒化シリコンを用いるのが好まし
い。このような金属酸化物又は金属窒化物よりなる干渉
層の膜厚は、その屈折率により最適膜厚が異なるが、通
常４００〜１５００Å程度、特に５００〜１０００Å程
度とするのが適当である。Examples of metal nitrides include silicon nitride and aluminum nitride. Among these metal nitrides, it is preferable to use silicon nitride because it is particularly dense and has an excellent effect of preventing intrusion of moisture or oxygen from the outside. The optimum thickness of the interference layer made of such a metal oxide or metal nitride varies depending on the refractive index thereof, but is usually about 400 to 1500Å, and particularly about 500 to 1000Å.

【０００９】光磁気記録層の干渉層と反対の面には、干
渉層と同様の材質を持つ誘電体よりなる層、即ち誘電体
層を設けるのが望ましい。この誘電体層の膜厚は通常の
場合、５００〜１５００Å程度とする。反射層を設ける
構造の媒体では、記録層に接して、又は数百Åの誘電体
層を介して高反射率の金属（例えばＡｌ、Ｃｕ等）の単
体又はその合金の層を反射層として設ける。反射層の上
に更に誘電体層を設けることもできる。On the surface of the magneto-optical recording layer opposite to the interference layer, it is desirable to provide a layer made of a dielectric material having the same material as the interference layer, that is, a dielectric layer. The thickness of this dielectric layer is usually about 500 to 1500 Å. In a medium having a structure in which a reflective layer is provided, a layer of a simple metal having a high reflectance (eg, Al, Cu, etc.) or its alloy layer is provided as a reflective layer in contact with the recording layer or through a dielectric layer of several hundred liters. .. It is also possible to further provide a dielectric layer on the reflective layer.

【００１０】なお、本発明において、基板上に干渉層、
記録層、誘電体層、反射層、誘電体層等の各層を形成す
る方法としては、スパッタリング等の物理蒸着法（ＰＶ
Ｄ）、プラズマＣＶＤのような化学蒸着法（ＣＶＤ）等
が適用される。また、イオンプレーティングを用いる方
法でも良い。ＰＶＤ法にて干渉層、光磁気記録層、誘電
体層、反射層、誘電体層等を成膜形成するには、所定の
組成をもったターゲットを用いて電子ビーム蒸着又はス
パッタリングにより基板上に各層を堆積するのが通常の
方法である。膜の堆積速度は速すぎると膜応力を増加さ
せ、遅すぎると生産性が低下するので、通常、０．１〜
１００Å／ｓｅｃ程度の範囲で適宜決定される。In the present invention, the interference layer on the substrate,
As a method for forming each layer such as a recording layer, a dielectric layer, a reflective layer, and a dielectric layer, a physical vapor deposition method such as sputtering (PV
D), a chemical vapor deposition method (CVD) such as plasma CVD, or the like is applied. Alternatively, a method using ion plating may be used. In order to form an interference layer, a magneto-optical recording layer, a dielectric layer, a reflection layer, a dielectric layer, etc. by PVD method, a target having a predetermined composition is used to perform electron beam evaporation or sputtering on a substrate. It is common practice to deposit each layer. If the deposition rate of the film is too fast, the film stress will increase, and if it is too slow, the productivity will decrease.
It is appropriately determined within the range of about 100Å / sec.

【００１１】以下、干渉層、光磁気記録層、誘電体層及
び反射層、さらには所望により誘電体層を含めて「記録
層」と称する。本発明の光記録媒体はこのような記録層
を形成した基板の記録層上に直接または他の層を介して
スリップ剤を含有する硬化性樹脂からなる保護層を形成
したことを特徴とするものである。Hereinafter, the interference layer, the magneto-optical recording layer, the dielectric layer and the reflective layer, and if desired, the dielectric layer are collectively referred to as a "recording layer". The optical recording medium of the present invention is characterized in that a protective layer made of a curable resin containing a slip agent is formed on a recording layer of a substrate having such a recording layer directly or through another layer. Is.

【００１２】上記スリップ剤としては流動パラフィン、
天然ワックス、マイクロワックス、ポリエチレンワック
ス等の脂肪族炭化水素系、ステアリン酸、ラウリン酸等
の炭素数１４〜３２の高級脂肪酸系、セチルアルコー
ル、ステアリルアルコール等の炭素数１４以上の脂肪族
アルコール系、ステアリン酸アミド、パルミチン酸アミ
ド、メチレンビスステアロアミド、エチレンビスステア
ロアミド、オレイン酸アミド、エルシン酸アミド等の脂
肪酸アミド系、ブチルステアレートなどの脂肪酸の低級
アルコールエステル、硬化ヒマシ油などの脂肪酸の多価
アルコールエステル及びエチレングリコールモノステア
レートなどの脂肪酸のグリコールエステル等の脂肪酸エ
ステル系、ステアリン酸の金属塩などの炭素数１２〜３
０の脂肪酸から誘導される金属石けん系及びシリコーン
系等があげられる。The slip agent is liquid paraffin,
Aliphatic hydrocarbon type such as natural wax, micro wax, polyethylene wax, higher fatty acid type having 14 to 32 carbon atoms such as stearic acid and lauric acid, aliphatic alcohol type having 14 or more carbon atoms such as cetyl alcohol and stearyl alcohol, Fatty acid amides such as stearic acid amide, palmitic acid amide, methylenebisstearamide, ethylenebisstearamide, oleic acid amide, and erucic acid amide, lower alcohol esters of fatty acids such as butyl stearate, and fatty acids such as hydrogenated castor oil. 12 to 3 carbon atoms such as polyhydric alcohol esters and fatty acid ester systems such as glycol esters of fatty acids such as ethylene glycol monostearate and metal salts of stearic acid
Examples thereof include metallic soap-based and silicone-based derived from 0 fatty acid.

【００１３】上記スリップ剤の配合量は硬化性樹脂の硬
化後の保護層表面の磁気ヘッドとの動摩擦係数が１．０
以下となる量配合するのが望ましく、通常硬化性樹脂成
分１００重量部当り５〜１００重量部の範囲が適当であ
る。上記スリップ剤を硬化性樹脂に配合するに際し、該
樹脂との相溶性を良くするためにスリップ剤を溶媒に溶
解させて用いてもよい。The blending amount of the above slip agent is such that the coefficient of dynamic friction with the magnetic head on the surface of the protective layer after curing of the curable resin is 1.0.
It is desirable to add the following amounts, and usually a range of 5 to 100 parts by weight is suitable per 100 parts by weight of the curable resin component. When the slip agent is blended with the curable resin, the slip agent may be dissolved in a solvent and used in order to improve the compatibility with the resin.

【００１４】該保護層としては上記スリップ剤をエネル
ギー線（例えば、紫外線）硬化型或るいは熱硬化型の硬
化性樹脂からなる所謂ハードコート剤に配合したものが
用いられる。エネルギー線（例えば、紫外線（ＵＶ））
硬化型樹脂としてはアクリレート又はメタアクリレート
基を単一或るいは複数有する化合物よりなるもの、例え
ばエポキシアクリレートやウレタンアクリレート等を主
成分としたものが好適に用いられる。また、熱硬化型樹
脂としてはシリコン系、エポキシ系、チタン系等が用い
られる。As the protective layer, a mixture of the above slip agent with a so-called hard coat agent composed of an energy ray (for example, ultraviolet ray) curable or thermosetting curable resin is used. Energy rays (for example, ultraviolet rays (UV))
As the curable resin, a resin composed of a compound having a single or a plurality of acrylate or methacrylate groups, for example, a resin mainly containing epoxy acrylate or urethane acrylate is preferably used. In addition, as the thermosetting resin, silicon-based resin, epoxy-based resin, titanium-based resin, or the like is used.

【００１５】該硬化樹脂は、ディスク基板の記録層上に
直接又は他の層を介してスピンコーター、ディッピン
グ、スプレー、ロールコーター、フローコーター法等の
コーティング法で均一に塗布することができる。また、
塗膜形成後の塗膜硬化条件は各コート剤に合った硬化方
法を用いれば良く、例えばエネルギー硬化型、すなわち
紫外線（ＵＶ）硬化型であれば紫外線を照射し、電子線
硬化型であれば電子線を照射し、また、熱硬化型であれ
ば加熱処理するなどの方法が採用される。The cured resin can be uniformly applied onto the recording layer of the disk substrate directly or through another layer by a coating method such as a spin coater, dipping, spray, roll coater or flow coater method. Also,
For the coating film curing conditions after coating film formation, a curing method suitable for each coating agent may be used. For example, energy curing type, that is, ultraviolet (UV) curing type is irradiated with ultraviolet rays, and electron beam curing type is used. A method of irradiating with an electron beam, or heat treatment for a thermosetting type is adopted.

【００１６】形成される保護層の厚味（硬化後）は、通
常の場合、０．５〜１００μｍとするのが好ましく、よ
り好ましくは、１〜５０μｍである。更には１〜２０μ
ｍ程度が好ましく、これ以上厚くすると保護層の収縮等
の影響による基板の変形が起る場合があり、この対策を
講じなければならないし、薄すぎれば耐久性が低下す
る。The thickness (after curing) of the protective layer formed is usually preferably 0.5 to 100 μm, more preferably 1 to 50 μm. Furthermore, 1 to 20μ
The thickness is preferably about m, and if the thickness is more than this, the substrate may be deformed due to the influence of shrinkage of the protective layer and the like, and it is necessary to take measures against this.

【００１７】硬化後の保護層としては、その表面硬度が
鉛筆硬度で３Ｈ以上であり、かつ磁気ヘッドとの動摩擦
係数が１．０以下であるのが良い。The protective layer after curing preferably has a surface hardness of 3H or more in pencil hardness and a coefficient of dynamic friction with the magnetic head of 1.0 or less.

【００１８】[0018]

【実施例】以下に実施例をもって本発明をさらに詳細に
説明するが、本発明はその要旨を越えない限り以下の実
施例に限定されるものではない。本明細書及び実施例中
における物性等の測定には以下の装置を使用した。The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to the following examples unless it exceeds the gist thereof. The following devices were used for measuring physical properties and the like in the present specification and examples.

【００１９】（１）動摩擦係数 使用装置名：ＦＳＴ フリクションスティクションテス
ター 装置会社名：松坂貿易（株） ディスク回転数：１８００ｒｐｍ ＣＳＳ回数：０〜５０００回 使用磁気ヘッド：３３７０ミニモノリシック 方法：０，１０００，３０００，５０００ ＣＳＳ時の
磁気ヘッドとの摩擦力を測定(1) Coefficient of dynamic friction Device name: FST Friction stiction tester Device company name: Matsuzaka Trading Co., Ltd. Disk rotation speed: 1800 rpm CSS number: 0 to 5000 times Magnetic head used: 3370 mini monolithic method: 0,1000 , 3000, 5000 Measure the friction force with the magnetic head during CSS

【００２０】（２）表面抵抗値 使用装置名：ＳＭＥ−８３１０超絶縁計 装置会社名：東亜電波工業（株） 方法：試料をリング電極上に乗せ２２℃、４８％ＲＨの
雰囲気下で測定。測定値は測定開始から１分後の値を読
みとった。(2) Surface resistance value Device used: SME-8310 super insulation meter Device company name: Toa Denpa Kogyo Co., Ltd. Method: A sample was placed on a ring electrode and measured in an atmosphere of 22 ° C. and 48% RH. The measured value was read one minute after the start of the measurement.

【００２１】（３）ダスト付着テスト 使用装置名：ＭＴ式ダートチェンバー 装置会社名：植木工作所有限会社 方法：ダート・チェンバー内を温度２５℃、湿度４５〜
５０ＲＨ％、風速０．７ｍ／ｓとし、ダスト粉体として
関東ローム粉体（１０〜２０mg）を用いて該ダート・チ
ェンバー内のクリーン度をクラス５００万以上とした。
このダート・チェンバー内に上記記録媒体を組み込んだ
ドライブを入れ、該ドライブを１８００ｒｐｍで４時間
回転させた後、記録媒体の表面保護層を目視観察し、下
記基準にて評価した。 ○：該表面保護層上にダストがわずか付着し、その下地
がはっきり見える状態 ×：該表面保護層上にダストが真白に付着し、その下地
が全く見えない状態(3) Dust adhesion test Device name: MT type dart chamber Device company name: Limited company owned by Ueki Co., Ltd. Method: Temperature in the dart chamber is 25 ° C, humidity is 45 ~
The cleanliness inside the dirt chamber was set to 5,000,000 or more by using Kanto loam powder (10 to 20 mg) as dust powder at 50 RH% and a wind speed of 0.7 m / s.
A drive incorporating the above recording medium was placed in this dirt chamber, the drive was rotated at 1800 rpm for 4 hours, and then the surface protective layer of the recording medium was visually observed and evaluated according to the following criteria. ◯: A slight amount of dust adhered to the surface protective layer so that the base was clearly visible. ×: Dust adhered to the surface protective layer in pure white, and the base was invisible at all.

【００２２】実施例１ 透明基板として中央に直径１５mmの孔を有する直径１３
０mm、板厚１．２mmの案内溝付き円形平板状のポリカー
ボネート射出成形基板を用い、その上に以下の層構成の
記録膜（カッコ内は膜厚を示す。）を連続スパッタ装置
で成膜して記録ディスクを製造した。Example 1 A transparent substrate having a diameter of 13 mm with a hole having a diameter of 15 mm in the center
A circular flat plate-shaped polycarbonate injection-molded substrate with a guide groove having a thickness of 0 mm and a thickness of 1.2 mm was used, and a recording film having the following layer structure (the film thickness in parentheses is shown) was formed thereon by a continuous sputtering device. To produce a recording disc.

【００２３】基板／ＳｉＮｘ（７５０Å）／ＴｂＦｅＣ
ｏ（３００Å）／ＡｌＳｉ（４００Å）／ＳｉＮｘ（３
５０Å） ＵＶ硬化型樹脂ハードコート剤１００重量部（大日本イ
ンキ社製、商品名ダイキュアクリアＥＸ−７０４）とス
リップ剤１０重量部（オレイン酸アミド）を混合容器に
入れ５０ｒｐｍで６０分かく拌し、コート剤とした。コ
ート剤をスピンコーターにより記録層上に塗布しＵＶ照
射にて保護膜（５μ）を得た。浮上型磁気ヘッドを用い
てＣＳＳテストを行なったところ、５０００回後に於け
る動摩擦係数は０．８を示した（初期の動摩擦係数は
０．３）。ダストの付着も認められず、ヘッドクラッシ
ュを起すこともなかった。結果を表１に示した。Substrate / SiNx (750Å) / TbFeC
o (300Å) / AlSi (400Å) / SiNx (3
50 Å) 100 parts by weight of UV-curable resin hard coating agent (Dai Nippon Ink Co., Ltd., trade name DICURE CLEAR EX-704) and 10 parts by weight of slip agent (oleic acid amide) are placed in a mixing vessel and stirred at 50 rpm for 60 minutes. And used as a coating agent. The coating agent was applied onto the recording layer by a spin coater and UV irradiation was carried out to obtain a protective film (5μ). When a CSS test was performed using a flying magnetic head, the dynamic friction coefficient after 5000 times was 0.8 (the initial dynamic friction coefficient was 0.3). No dust adhesion was observed, and no head crash occurred. The results are shown in Table 1.

【００２４】比較例１及び２ 比較のため、スリップ剤を添加しないコート剤を用いた
ほかは実施例１と同様にして得た記録ディスク（比較例
１）及びコート剤を塗布せず、すなわちハードコート層
を設けなかった記録ディスク（比較例２）についても同
様に物性を測定し、表１に示した。Comparative Examples 1 and 2 For comparison, a recording disk (Comparative Example 1) obtained in the same manner as in Example 1 except that a slip agent was not added and a coating agent were not applied, that is, a hard disk was used. The physical properties of the recording disk having no coat layer (Comparative Example 2) were measured in the same manner and shown in Table 1.

【００２５】[0025]

【表１】 [Table 1]

【００２６】[0026]

【発明の効果】本発明の媒体は表面の動摩擦係数が低い
のでディスクと磁気ヘッドとの接触による発塵が抑制さ
れ、また磁気ヘッドがディスクに吸着しにくい。従って
ＣＳＳによる磁気ヘッドのクラッシュが防止され、実用
上大変良好である。Since the medium of the present invention has a low dynamic friction coefficient on the surface, dust generation due to contact between the disk and the magnetic head is suppressed, and the magnetic head is less likely to be attracted to the disk. Therefore, the magnetic head is prevented from crashing due to CSS, which is very good in practical use.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 小松 昌生 神奈川県横浜市緑区鴨志田町1000番地 三 菱化成株式会社総合研究所内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Masao Komatsu 1000 Kamoshida-cho, Midori-ku, Yokohama-shi, Kanagawa Sanryo Kasei Co., Ltd.

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】 基板上に記録層を形成し、該記録層上に
直接または他の層を介してスリップ剤を含有する硬化性
樹脂からなる保護層を設けたことを特徴とする光記録媒
体。1. An optical recording medium comprising a recording layer formed on a substrate, and a protective layer made of a curable resin containing a slip agent provided on the recording layer directly or through another layer. .. 【請求項２】 請求項１に記載の光記録媒体において、
保護層の磁気ヘッドに対する動摩擦係数が１．０以下
で、且つその表面硬度が３Ｈ以上であることを特徴とす
る光記録媒体。2. The optical recording medium according to claim 1,
An optical recording medium characterized in that the dynamic friction coefficient of the protective layer with respect to the magnetic head is 1.0 or less, and the surface hardness thereof is 3H or more. 【請求項３】 請求項１に記載の光記録媒体において、
浮上型磁気ヘッドを用いて記録・再生を行う光磁気記録
方式に用いる磁界変調型光磁気記録媒体であることを特
徴とする光記録媒体。3. The optical recording medium according to claim 1,
An optical recording medium, which is a magnetic field modulation type magneto-optical recording medium used in a magneto-optical recording method for recording / reproducing using a floating magnetic head.