JPH05212141A - Golf club shaft - Google Patents
Golf club shaftInfo
- Publication number
- JPH05212141A JPH05212141A JP4296567A JP29656792A JPH05212141A JP H05212141 A JPH05212141 A JP H05212141A JP 4296567 A JP4296567 A JP 4296567A JP 29656792 A JP29656792 A JP 29656792A JP H05212141 A JPH05212141 A JP H05212141A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- resin
- golf club
- prepreg
- club shaft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、複数層の繊維強化複合
樹脂材料層からなるゴルフクラブシャフトに関し、特に
複数層の繊維強化複合樹脂材料層の最外層に、装飾層を
複合化した複合層を積層した外観の美感に優れるゴルフ
クラブシャフトに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a golf club shaft comprising a plurality of fiber reinforced composite resin material layers, and more particularly, a composite layer in which a decorative layer is composited on the outermost layer of the plurality of fiber reinforced composite resin material layers. TECHNICAL FIELD The present invention relates to a golf club shaft having an excellent appearance that is obtained by stacking the golf balls.
【０００２】[0002]
【従来の技術】近年、ゴルフクラブシャフトとして、軽
量で且つ機械的強度が高く、又振動減衰特性が良好であ
るという理由から、強化繊維として炭素繊維を有するプ
リプレグを使用して作成した炭素繊維強化複合樹脂材料
製のシャフトが多く利用されており、良好な結果を納め
ている。2. Description of the Related Art Recently, as a golf club shaft, carbon fiber reinforced by using a prepreg having carbon fiber as a reinforcing fiber because of its light weight, high mechanical strength and good vibration damping characteristics. Shafts made of composite resin materials are widely used and have achieved good results.
【０００３】このようなゴルフクラブシャフトは、複数
層の炭素繊維強化複合樹脂材料層等から構成されるが、
図６に示すように、所定の形状寸法に裁断した炭素繊維
強化プリプレグ１０１を所定枚数だけマンドレル１００
に巻き付け、プリプレグ１０１のマトリクス樹脂を硬化
してプリプレグ１０１を炭素繊維強化複合樹脂材料とす
ることによって形成される。このとき、捩り及び曲げ性
能を向上させるために、炭素繊維強化プリプレグとして
は、図５をも参照すると良く理解されるように、炭素繊
維がゴルフクラブシャフトの軸線に対して互に反対方向
に角度（θ）（通常、θ＝３５°〜４５°）だけ傾斜す
るように配列されたプリプレグ１０１（アングル層１０
１′）と、図７に図示されるように、炭素繊維がゴルフ
クラブシャフトの軸線に対して平行（θ＝０°）に配列
されたプリプレグ１０２（ストレート層１０２′）とが
使用され、基本的には、図５に示されるように、ゴルフ
クラブシャフトの内側層にプリプレグ１０１（アングル
層１０１′）が、外側層にプリプレグ１０２（ストレー
ト層１０２′）が使用されることが多い。Such a golf club shaft is composed of a plurality of carbon fiber reinforced composite resin material layers and the like.
As shown in FIG. 6, a predetermined number of carbon fiber reinforced prepregs 101 cut into a predetermined shape and dimensions are used for the mandrel 100.
It is formed by winding the prepreg 101 into a carbon fiber reinforced composite resin material by winding the prepreg 101 and curing the matrix resin of the prepreg 101. At this time, in order to improve the twisting and bending performance, as the carbon fiber reinforced prepreg, as will be well understood by also referring to FIG. 5, the carbon fibers are angled in opposite directions with respect to the axis of the golf club shaft. The prepreg 101 (angle layer 10) arranged so as to be inclined by (θ) (usually, θ = 35 ° to 45 °).
1 ') and a prepreg 102 (straight layer 102') in which carbon fibers are arranged in parallel (θ = 0 °) to the axis of the golf club shaft as shown in FIG. Specifically, as shown in FIG. 5, a prepreg 101 (angle layer 101 ') is often used as an inner layer and a prepreg 102 (straight layer 102') is used as an outer layer of a golf club shaft.
【０００４】[0004]
【発明が解決しようとする課題】ところで、ゴルフクラ
ブシャフトは、外観の美感に優れることが重要である
が、従来は、プリプレグを型のマンドレル等上に巻回、
積層し、硬化して成形品が得られた後、表面研摩後塗装
等を施すことによって美的外観を付与しており、このた
め美的外観の付与作業に手間がかかる問題があった。又
その外面の塗装等の装飾面も堅固さを欠き、成形品の使
用につれて装飾面の塗装等の剥がれや摩耗が生じて外観
の美感が損なわれる問題もあった。By the way, it is important for a golf club shaft to have an excellent appearance, but conventionally, a prepreg is wound around a mandrel of a mold,
After laminating and curing to obtain a molded product, the surface is polished and then painted to give an aesthetic appearance, and thus there is a problem that it takes time and effort to give the aesthetic appearance. In addition, there is also a problem that the decorative surface such as the coating on the outer surface thereof lacks hardness, and peeling and abrasion of the coating on the decorative surface occur as the molded product is used, and the appearance is impaired.
【０００５】本発明の目的は、手間のかかる塗装等の作
業を行なうことなく、容易に外観の美感を得ることがで
き、その美感も長期に亙って安定して発揮させることが
可能な繊維強化複合樹脂材料製のゴルフクラブシャフト
を提供することである。The object of the present invention is to provide a fiber which can easily obtain a beautiful appearance and which can be stably exhibited for a long period of time without performing a laborious painting work. To provide a golf club shaft made of a reinforced composite resin material.
【０００６】[0006]
【課題を解決するための手段】上記目的は本発明に係る
ゴルフクラブシャフトにて達成される。要約すれば本発
明は、複数層の繊維強化複合樹脂材料層からなるゴルフ
クラブシャフトにおいて、樹脂層、前記樹脂層上に積層
した、図柄を前記樹脂層と反対側に有する装飾層及び前
記装飾層上に積層した透明繊維強化複合樹脂材料層から
なる複合層を、前記複数層の繊維強化複合樹脂材料層の
最外層上に少なくとも１層積層したことを特徴とするゴ
ルフクラブシャフトである。本発明によれば、前記装飾
層と前記透明繊維強化複合樹脂材料層との間に更に透明
樹脂層を積層することができる。The above object can be achieved by a golf club shaft according to the present invention. In summary, the present invention provides a golf club shaft comprising a plurality of fiber-reinforced composite resin material layers, a resin layer, a decorative layer laminated on the resin layer, and a decorative layer having a pattern on the side opposite to the resin layer and the decorative layer. A golf club shaft, wherein at least one composite layer comprising a transparent fiber-reinforced composite resin material layer laminated thereon is laminated on an outermost layer of the plurality of fiber-reinforced composite resin material layers. According to the present invention, a transparent resin layer can be further laminated between the decorative layer and the transparent fiber reinforced composite resin material layer.
【０００７】[0007]
【実施例】以下、本発明に係るゴルフクラブシャフトを
図面に則して詳細に説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A golf club shaft according to the present invention will be described in detail below with reference to the drawings.
【０００８】図１は、本発明のゴルフクラブシャフトの
一実施例を示す断面図である。本発明のゴルフクラブシ
ャフトは、基本的に炭素繊維がゴルフクラブシャフトの
軸線に対して互に角度（θ）（通常、θ＝３５°〜４５
°）だけ傾斜するように配列された繊維強化複合樹脂層
１０１と、炭素繊維がゴルフクラブシャフトの軸線に対
して平行に配列された繊維強化複合樹脂層１０２と、繊
維強化複合樹脂層１０２の最外層に、美感を付与するた
めの複合プリプレグ１が配設され、硬化することによっ
て製造される。FIG. 1 is a sectional view showing an embodiment of the golf club shaft of the present invention. In the golf club shaft of the present invention, basically, the carbon fibers form an angle (θ) with respect to the axis of the golf club shaft (usually θ = 35 ° to 45 °).
Of the fiber-reinforced composite resin layer 101 arranged so as to be inclined by an angle of (°), the fiber-reinforced composite resin layer 102 in which carbon fibers are arranged parallel to the axis of the golf club shaft, and the fiber-reinforced composite resin layer 102. The composite prepreg 1 for imparting an aesthetic effect is disposed on the outer layer and is manufactured by curing.
【０００９】つまり、本発明によると、アングル層１０
１′、ストレ−ト層１０２′、及び複合層１′を備えた
ゴルフクラブシャフトが形成され、複合層１′によって
ゴルフクラブシャフトの外観に美感が付与される。図１
では、アングル層１０１′が内層とされているが、スト
レ−ト層１０２′を内層とすることも可能である。又、
アングル層１０１′及びストレ−ト層１０２′は１層で
ある必要はなく、必要に応じて複数層とすることも可能
である。又場合によっては、ゴルフクラブシャフトの例
えば先後端の強度不足を補うために、その箇所に図示し
ない補強層を加えることができる。That is, according to the present invention, the angle layer 10
A golf club shaft including 1 ', the straight layer 102', and the composite layer 1'is formed, and the composite layer 1'provides a beautiful appearance to the golf club shaft. Figure 1
In the above, the angle layer 101 'is the inner layer, but the straight layer 102' may be the inner layer. or,
The angle layer 101 'and the straight layer 102' do not have to be one layer, and may be a plurality of layers as required. In some cases, a reinforcing layer (not shown) can be added to the front and rear ends of the golf club shaft in order to compensate for insufficient strength.
【００１０】アングル層１０１′及びストレ−ト層１０
２′を形成するための繊維強化複合樹脂層１０１及び１
０２には、通常の炭素繊維強化プリプレグを使用するこ
とができる。つまり、炭素繊維強化プリプレグ１０１、
１０２は、強化繊維としては炭素繊維（黒鉛繊維をも含
む）を使用し、マトリクス樹脂としては、エポキシ樹
脂、不飽和ポリエステル樹脂、ポリウレタン樹脂、ジア
リルフタレ−ト樹脂、フェノ−ル樹脂などの熱硬化性マ
トリクス樹脂が使用可能である。又、更に、硬化温度が
５０〜２００℃となるように硬化剤その他の付与剤、例
えば可撓性付与剤などが適当に添加される。Angle layer 101 'and straight layer 10
Fiber-reinforced composite resin layers 101 and 1 for forming 2 '
For 02, an ordinary carbon fiber reinforced prepreg can be used. That is, the carbon fiber reinforced prepreg 101,
The carbon fiber 102 (including graphite fiber) is used as the reinforcing fiber 102, and the matrix resin is a thermosetting resin such as epoxy resin, unsaturated polyester resin, polyurethane resin, diallyl phthalate resin, or phenol resin. Matrix resin can be used. Further, a curing agent and other imparting agents such as flexibility imparting agent are appropriately added so that the curing temperature is 50 to 200 ° C.
【００１１】勿論、アングル層１０１′及びストレ−ト
層１０２′は、強化繊維として、炭素繊維以外のガラス
繊維などの他の繊維を使用した、当業者には周知の種々
のプリプレグを使用して形成することも可能である。Of course, the angle layer 101 'and the straight layer 102' use various prepregs well known to those skilled in the art in which other fibers such as glass fibers other than carbon fibers are used as reinforcing fibers. It can also be formed.
【００１２】次に、本発明の特徴とする複合層１′につ
いて詳しく説明する。図２は、本発明に係る複合層１′
を形成するために使用される複合プリプレグ１である。Next, the composite layer 1'characteristic of the present invention will be described in detail. FIG. 2 shows a composite layer 1'according to the present invention.
It is a composite prepreg 1 used for forming a.
【００１３】本発明に係る複合プリプレグ１は、樹脂層
２と、樹脂層２上に積層された装飾層３と、装飾層３上
に積層された透明繊維強化樹脂層、つまり透明プリプレ
グ層４とから基本的になっている。複合プリプレグ１全
体は、最下層の樹脂層２を積層した離型紙５上に支持さ
れ、必要に応じて最上層の透明プリプレグ層４上に透明
のカバーフィルム６が被される。The composite prepreg 1 according to the present invention comprises a resin layer 2, a decorative layer 3 laminated on the resin layer 2, a transparent fiber reinforced resin layer laminated on the decorative layer 3, that is, a transparent prepreg layer 4. It is basically from. The entire composite prepreg 1 is supported on a release paper 5 on which a lowermost resin layer 2 is laminated, and a transparent cover film 6 is covered on the uppermost transparent prepreg layer 4 if necessary.
【００１４】樹脂層２は、複合プリプレグ１が積層され
る通常のプリプレグ層の最外層と複合プリプレグ１との
接着性を得るためのもので、熱硬化性のエポキシ樹脂
等、プリプレグに用いられる通常のマトリクス樹脂が使
用できる。樹脂層２は通常透明とされるが、透明である
必要はない。離型紙５上への樹脂層２の目付量は５〜２
００ｇ／ｍ2 とされ、好ましくは目付量１０〜１００ｇ
／ｍ2 に形成される。The resin layer 2 is for obtaining adhesiveness between the composite prepreg 1 and the outermost layer of the normal prepreg layer on which the composite prepreg 1 is laminated, and is usually used for prepreg such as thermosetting epoxy resin. The matrix resin of can be used. The resin layer 2 is usually transparent, but need not be transparent. The basis weight of the resin layer 2 on the release paper 5 is 5 to 2
00 g / m 2 , preferably a basis weight of 10 to 100 g
/ M 2 is formed.
【００１５】装飾層３は、ゴルフクラブシャフトの外観
に美感を付与するためのもので、樹脂層２と反対側の
面、図では上面に図柄７を有している。図柄７として
は、絵、模様又はロゴマーク等が挙げられる。図柄７は
装飾層３の表面の単なる着色であってもよく、その着色
も装飾層３の表面を部分的に着色する部分着色とするこ
とも、全面を着色する全面着色とすることもできる。又
図柄７は、単色で形成しても複数色で形成してもよい。The decorative layer 3 is for imparting a beautiful appearance to the golf club shaft, and has a pattern 7 on the surface opposite to the resin layer 2, that is, on the upper surface in the figure. Examples of the design 7 include a picture, a pattern, a logo mark, and the like. The pattern 7 may be simply colored on the surface of the decorative layer 3, and the coloring may be partial coloring for partially coloring the surface of the decorative layer 3 or full coloring for coloring the entire surface. The design 7 may be formed in a single color or in a plurality of colors.
【００１６】図柄７を有する装飾層３としては、図柄７
を印刷した紙或いは樹脂シートが使用できる。このよう
な図柄７を印刷する基材である紙は、樹脂層２との一体
性を大にするために、樹脂層２からの樹脂が均質に含浸
されるものが好ましい。同様に、上記のシートは樹脂層
２の樹脂と相溶性が高いものが好ましい。As the decorative layer 3 having the pattern 7, the pattern 7
It is possible to use a paper or resin sheet on which is printed. It is preferable that the paper, which is the base material on which the pattern 7 is printed, is uniformly impregnated with the resin from the resin layer 2 in order to increase the integrity with the resin layer 2. Similarly, it is preferable that the above-mentioned sheet has high compatibility with the resin of the resin layer 2.
【００１７】更にこれら装飾層３の基材の紙又は樹脂シ
ートは、樹脂層２からの樹脂の浸透によって透明を呈す
るとなお良い。これによれば、装飾層３の図柄７が透明
基材を背景にして浮いたように見えるので、成形品の外
観に更に優れた美観を付与することが可能となる。この
ような基材としては、薄葉紙、厚み１５〜１００μｍ程
度のナイロン、ＰＥＴなどの熱硬化性樹脂による不織布
が等が挙げられる。Furthermore, it is more preferable that the paper or resin sheet as the base material of the decorative layer 3 is transparent due to the penetration of the resin from the resin layer 2. According to this, the pattern 7 of the decorative layer 3 looks as if it floats with the transparent base material as a background, so that it is possible to impart a more excellent aesthetic appearance to the molded product. Examples of such a substrate include thin paper, nylon having a thickness of about 15 to 100 μm, and nonwoven fabric made of thermosetting resin such as PET.
【００１８】図柄７に使用するインクは、ゴルフクラブ
シャフトを得る際のプリプレグの硬化時の熱により、劣
化して褪色しないものが好ましい。更に下の樹脂層２か
ら装飾層３に浸透した樹脂による図柄７への悪影響を防
止する目的で、図３に示すように、図柄７は、下に樹脂
浸透防止用のインクにより印刷した下地層７ａを有する
ことができる。これによれば、浸透した樹脂により図柄
７が溶かされて濁ったり、剥げたりするのを予防するこ
とができ、図柄７の安定性がなお一層向上する。このよ
うなインクとしは、下地隠蔽用として通常用いられる、
ＴｉＯ2 などの顔料が入った隠蔽力のあるインクを使用
することができる。The ink used for the design 7 is preferably one which does not deteriorate and deteriorate due to heat during curing of the prepreg when obtaining the golf club shaft. Further, as shown in FIG. 3, the design 7 is a base layer printed with an ink for preventing resin penetration below, for the purpose of preventing an adverse effect on the design 7 by the resin that has penetrated from the resin layer 2 below to the decoration layer 3. 7a. According to this, it is possible to prevent the pattern 7 from being melted by the infiltrated resin and becoming muddy or peeled off, and the stability of the pattern 7 is further improved. Such an ink is usually used for hiding the base,
A hiding ink containing a pigment such as TiO 2 can be used.
【００１９】装飾層３の厚みとしては５〜３００μｍ、
好ましくは１０〜１５０μｍ程度がよい。The thickness of the decorative layer 3 is 5 to 300 μm,
It is preferably about 10 to 150 μm.
【００２０】プリプレグ層４は、その下の装飾層３を保
護するためのもので、装飾層３の図柄７がプリプレグ層
４上から見えるようにするために、透明とされている。
このような透明プリプレグ層４としては、透明繊維から
なる強化繊維とマトリクス樹脂とからなる透明プリプレ
グが用いられる。The prepreg layer 4 is for protecting the decorative layer 3 thereunder, and is transparent so that the pattern 7 of the decorative layer 3 can be seen from above the prepreg layer 4.
As such a transparent prepreg layer 4, a transparent prepreg made of reinforcing fibers made of transparent fibers and a matrix resin is used.
【００２１】透明繊維としては、例えばガラス繊維、ア
ルミナ繊維、石英繊維等が用いられる。これらの透明繊
維は単独で使用しても、複数種をハイブリッドで使用し
てもよい。又透明繊維は一方向配列の形態で使用する
他、クロスでも或いはマットの形態でも使用することが
できる。透明繊維がクロス或いはマットの形態とされて
いる場合には、そのクロス又はマットを複数枚、繊維が
同方向に重なるようにラミネートして使用することも、
互に繊維が傾斜して重なるようにハイブリッド化して使
用することもできる。As the transparent fiber, for example, glass fiber, alumina fiber, quartz fiber or the like is used. These transparent fibers may be used alone or in combination of two or more kinds. Further, the transparent fibers can be used not only in the form of unidirectional arrangement but also in the form of cloth or mat. When the transparent fibers are in the form of cloth or mat, it is also possible to use a plurality of cloths or mats laminated so that the fibers overlap in the same direction.
It is also possible to use them by hybridizing them so that the fibers are inclined and overlap each other.
【００２２】マトリクス樹脂は、エポキシ樹脂等の通常
の熱硬化性樹脂ならば原則として使用できるが、プリプ
レグ層４の透明性を与えることから、透明性を欠く樹脂
は除かれる。As the matrix resin, a general thermosetting resin such as an epoxy resin can be used in principle, but the resin lacking transparency is excluded because it provides the prepreg layer 4 with transparency.
【００２３】透明プリプレグ層４の厚みは１０〜２００
μｍ、好ましくは５０〜１００μｍとされる。又透明プ
リプレグ層４中の透明繊維の量は３０〜２００ｇ／ｍ
2 、好ましくは７０〜１２０ｇ／ｍ2 とされる。プリプ
レグ層４中のマトリクス樹脂量は２０〜８０ｗｔ％、好
ましくは３０〜７９ｗｔ％とされる。The thickness of the transparent prepreg layer 4 is 10 to 200.
μm, preferably 50 to 100 μm. The amount of transparent fibers in the transparent prepreg layer 4 is 30 to 200 g / m.
2 , preferably 70 to 120 g / m 2 . The amount of matrix resin in the prepreg layer 4 is set to 20 to 80 wt%, preferably 30 to 79 wt%.
【００２４】複合プリプレグ１の全体の厚みは５０〜５
００μｍにすることが適当である。複合プリプレグ１の
厚みが５０μｍ未満では薄すぎて、プリプレグ１の製造
が困難であるばかりか、最外層に使用してゴルフクラブ
シャフトを作成するのには実用的でない。又厚みが５０
０μｍを超えると厚すぎて、最外層に使用して成形性良
くゴルフクラブシャフトを作成することが難しくなる。The total thickness of the composite prepreg 1 is 50 to 5
It is suitable to set it to 00 μm. If the thickness of the composite prepreg 1 is less than 50 μm, it is too thin to make the prepreg 1 difficult to manufacture, and it is not practical to use it as the outermost layer to make a golf club shaft. Also the thickness is 50
If it exceeds 0 μm, it is too thick, and it becomes difficult to form a golf club shaft with good moldability by using it as the outermost layer.
【００２５】本発明の複合プリプレグ１は、任意の方法
にて製造し得るが、典型的には、樹脂を塗工した樹脂塗
工紙上に、その樹脂層と絵柄７が反対側になるように絵
柄７を印刷した紙又はシートを重ね、その上に透明プリ
プレグを重ねて、透明プリプレグの支持体と樹脂塗工紙
との外側から熱プレスして、樹脂塗工紙上の樹脂、絵柄
７を印刷した紙又はシート及び透明プリプレグを一体化
することにより、製造することができる。The composite prepreg 1 of the present invention can be manufactured by any method, but typically, the resin layer is coated on a resin-coated paper so that the resin layer and the pattern 7 are on opposite sides. The paper or sheet on which the pattern 7 is printed is overlaid, the transparent prepreg is overlaid on it, and the resin on the resin-coated paper and the pattern 7 are printed by hot pressing from the outside of the support of the transparent prepreg and the resin-coated paper. It can be manufactured by integrating the prepared paper or sheet and the transparent prepreg.
【００２６】場合によっては、透明繊維上に樹脂塗工紙
を重ねて熱プレスするとにより透明プリプレグを製造す
る際、他の樹脂塗工紙上に重ねられた絵柄７を印刷した
紙又はシート上に透明繊維を配列し、その繊維上に透明
プリプレグ用の樹脂塗工紙を重ね合わせて、上下の樹脂
塗工紙の外側から熱プレスすることにより、上の樹脂塗
工紙上の樹脂と透明繊維とから透明プリプレグを形成す
ると共に、その透明プリプレグと、絵柄７を印刷した紙
又はシートと、下の樹脂塗工紙上の樹脂とを一体化する
ことにより、製造することもできる。In some cases, when a transparent prepreg is produced by stacking resin-coated paper on transparent fibers and hot-pressing it, it is transparent on the paper or sheet on which the pattern 7 printed on another resin-coated paper is printed. By arranging the fibers, overlaying the resin-coated paper for transparent prepreg on the fibers, and heat-pressing from the outside of the upper and lower resin-coated paper, the resin on the upper resin-coated paper and the transparent fibers It can also be manufactured by forming a transparent prepreg, and integrating the transparent prepreg, the paper or sheet on which the pattern 7 is printed, and the resin on the resin-coated paper below.
【００２７】このような複合プリプレグ１を最外層に１
〜２層巻き付けて製造されたゴルフクラブシャフトによ
れば、軽量で機械的強度が良好であるばかりでなく、最
外層に単層〜複数層に積層された複合プリプレグ１の装
飾層３の絵柄７が、その表面の透明プリプレグ層４によ
る繊維強化複合樹脂材料の薄い透明層を通して透けて見
え、絵柄７が薄い透明層の奥に位置して見えるので、ゴ
ルフクラブシャフトの外観の美感が改善され、外観に容
易に美感が付与される。Such a composite prepreg 1 is used as the outermost layer.
According to the golf club shaft manufactured by winding two layers, not only is it lightweight and has good mechanical strength, but also the pattern 7 of the decorative layer 3 of the composite prepreg 1 laminated in a single layer to a plurality of outermost layers is used. However, since it can be seen through the thin transparent layer of the fiber reinforced composite resin material by the transparent prepreg layer 4 on the surface and the pattern 7 can be seen in the back of the thin transparent layer, the appearance aesthetics of the golf club shaft is improved, Appearance is easily given to the appearance.
【００２８】更に装飾層３の基材を薄葉紙等の樹脂の浸
透により透明を呈するものにした場合には、装飾層３の
図柄７が透明基材を背景にして浮いたように見え、ゴル
フクラブシャフトの外観に更に優れた美観が付与され
る。又図柄７の下に樹脂浸透防止用のインクによる下地
層７ａを設けることにより、装飾層３に浸透した樹脂に
よる悪影響をなくして、図柄７のａ安定性をより一層増
すことができる。Further, when the base material of the decorative layer 3 is made transparent by permeation of resin such as thin paper, the pattern 7 of the decorative layer 3 looks like floating with the transparent base material as a background, and the golf club. A more excellent aesthetic appearance is given to the appearance of the shaft. Further, by providing the underlayer 7a of the ink for preventing resin permeation under the design 7, the adverse effect of the resin that has penetrated into the decorative layer 3 can be eliminated, and the stability a of the design 7 can be further increased.
【００２９】更に又装飾層３が透明プリプレグ層４によ
る繊維強化複合樹脂材料層により極めて堅固に保護され
ているので、装飾層３による美感は従来の塗装等とは違
って、ゴルフクラブシャフトの使用につれて損なわれる
ことがなく、長期に亙って安定して発揮される。又ゴル
フクラブシャフトを製造する際に通常のプリプレグ層の
最外層上に単に複合プリプレグ１を１〜２層積層するだ
けで、ゴルフクラブシャフトに外観の美感を付与できる
ので、塗装等の場合と違って外観の美感を付与するため
に手間がかかる作業を要することがない。Furthermore, since the decorative layer 3 is extremely firmly protected by the fiber reinforced composite resin material layer formed by the transparent prepreg layer 4, the aesthetic appearance of the decorative layer 3 is different from that of conventional painting, and the use of the golf club shaft It will not be damaged as time goes by and will be stably exhibited over a long period of time. Also, when manufacturing a golf club shaft, by simply laminating one or two layers of the composite prepreg 1 on the outermost layer of a normal prepreg layer, it is possible to give the golf club shaft an aesthetic appearance. There is no need for laborious work for imparting a beautiful appearance.
【００３０】図４は、本発明で使用する複合プリプレグ
の他の態様を示す断面図である。本複合プリプレグ１で
は、その装飾層３と透明プリプレグ層４との間に、更に
透明樹脂層８を積層したことが特徴である。FIG. 4 is a sectional view showing another embodiment of the composite prepreg used in the present invention. The present composite prepreg 1 is characterized in that a transparent resin layer 8 is further laminated between the decorative layer 3 and the transparent prepreg layer 4.
【００３１】上記の透明樹脂層８は、絵柄７を印刷した
紙又はシートからなる装飾層３と透明プリプレグ層４と
の接着性をより確実にするためのもので、透明プリプレ
グ４層に用いたのと同じような樹脂が使用できる。透明
樹脂層８の目付量は、１０〜２００ｇ／ｍ2 に形成さ
れ、好ましくは目付量２０〜１００ｇ／ｍ2 とされる。The above-mentioned transparent resin layer 8 is for ensuring the adhesiveness between the decorative layer 3 made of paper or sheet on which the pattern 7 is printed and the transparent prepreg layer 4, and is used for the transparent prepreg 4 layer. Resins similar to the above can be used. The transparent resin layer 8 has a basis weight of 10 to 200 g / m 2 , and preferably a basis weight of 20 to 100 g / m 2 .
【００３２】本複合プリプレグ１を用いこれを、積層さ
れた通常の炭素繊維プリプレグ等の最外層上に１〜２層
積層して製造されたゴルフクラブシャフトによれば、装
飾層３と透明プリプレグ層４との間の接着性が、その間
の透明樹脂層８により一層確実にされているので、装飾
層３がゴルフクラブシャフトの外面にあって外観の美感
をより安定して発揮する。According to the golf club shaft produced by using the present composite prepreg 1 and laminating one or two layers on the outermost layer such as the ordinary laminated carbon fiber prepreg, the decorative layer 3 and the transparent prepreg layer are provided. Since the adhesiveness with 4 is made more reliable by the transparent resin layer 8 between them, the decorative layer 3 is on the outer surface of the golf club shaft, and the appearance aesthetics are more stably exhibited.
【００３３】本複合プリプレグ１においても、先に述べ
たように、装飾層３を構成する基材の紙又は樹脂シート
は、樹脂層２からの樹脂の浸透によって透明を呈するも
のとすることができ、又図柄７の下に樹脂浸透防止用の
インクによる下地層を設けてもよいことは勿論である。Also in the present composite prepreg 1, as described above, the base paper or resin sheet constituting the decorative layer 3 can be made transparent by the penetration of the resin from the resin layer 2. Needless to say, a base layer made of ink for preventing resin permeation may be provided under the pattern 7.
【００３４】本発明を具体的な実施例に基づき更に説明
する。The present invention will be further described based on specific examples.
【００３５】実施例１ 本発明に従い複合プリプレグ１を作成し、それを通常の
プリプレグと組み合わせて使用しゴルフクラブシャフト
を製造した。製造法は次の通りである。Example 1 A composite prepreg 1 was prepared according to the present invention and used in combination with an ordinary prepreg to manufacture a golf club shaft. The manufacturing method is as follows.
【００３６】図６に示すように、ゴルフクラブシャフト
の型のマンドレル１００上に、アングル層１０１′用の
炭素繊維プリプレグ１０１として、厚さ１２０μｍ、樹
脂量３２％のＰＡＮ系炭素繊維プリプレグ（東レ株式会
社製、商品名Ｐ２０５３）を＋４５°、−４５°で合計
８層巻き付け、その上にストレート層１０２′用の炭素
繊維プリプレグ１０２として、厚さ１２０μｍ、樹脂量
３２％のＰＡＮ系炭素繊維プリプレグ（東レ株式会社
製、商品名Ｔ−３００）を２層巻き付け、更にその最外
層に第２のストレート層１′用に、本発明の複合プリプ
レグ１を２層巻き付けた。次いで補強層用にガラス繊維
プリプレグとして、Ｅ−ガラス（旭ファイバーグラス株
式会社製）を使用したプリプレグを巻いて先端チップ部
を補強した後、ポリプロピレンの延伸テープでテーピン
グをして加熱硬化し、その後研摩等の所定の仕上げを行
なって、ゴルフクラブシャフトを作成した。As shown in FIG. 6, a carbon fiber prepreg 101 having a thickness of 120 μm and a resin amount of 32% was used as a carbon fiber prepreg 101 for an angle layer 101 ′ on a mandrel 100 of a golf club shaft type (Toray stock). Company-made, product name P2053) is wound at a total of 8 layers at + 45 ° and −45 °, and a carbon fiber prepreg 102 for a straight layer 102 ′ is formed on the PAN-based carbon fiber prepreg having a thickness of 120 μm and a resin amount of 32% ( Two layers of Toray Co., Ltd., trade name T-300) were wound, and two layers of the composite prepreg 1 of the present invention were wound on the outermost layer for the second straight layer 1 '. Then, as a glass fiber prepreg for the reinforcing layer, a prepreg using E-glass (manufactured by Asahi Fiber Glass Co., Ltd.) was wound to reinforce the tip end portion, and then taped with a polypropylene stretching tape to heat-harden, and then A golf club shaft was prepared by performing a predetermined finishing such as polishing.
【００３７】複合プリプレグ１は、図２に示した装飾層
３上に透明プリプレグ層４が直接積層された態様のもの
を使用した。複合プリプレグ１の樹脂層２は、エポキシ
樹脂で目付量５０ｇ／ｍ2 に形成した。装飾層３には、
厚み６０μｍの普通紙に赤、青、黄色の３色でダイヤの
絵柄を印刷した印刷紙を用いた。透明プリプレグ層４に
は、エポキシ樹脂を用いた一方向ガラス繊維プリプレグ
を使用し、そのガラス繊維の厚みは５０μｍ、ガラス繊
維の量は７０ｇ／ｍ2 、エポキシ樹脂の量は３０ｗｔ％
であった。The composite prepreg 1 used is one in which the transparent prepreg layer 4 is directly laminated on the decorative layer 3 shown in FIG. The resin layer 2 of the composite prepreg 1 was formed of an epoxy resin with a basis weight of 50 g / m 2 . The decorative layer 3 includes
A printing paper in which a diamond pattern was printed in three colors of red, blue, and yellow on plain paper having a thickness of 60 μm was used. For the transparent prepreg layer 4, a unidirectional glass fiber prepreg using an epoxy resin is used, the thickness of the glass fiber is 50 μm, the amount of glass fiber is 70 g / m 2 , and the amount of epoxy resin is 30 wt%.
Met.
【００３８】その結果、得られたゴルフクラブシャフト
は、赤、青、黄色の３色で印刷したダイヤの絵柄がゴル
フクラブシャフトの表面の薄い透明層の奥に位置し、透
明層を通して透けて見えるので、外観が高い美感を呈
し、美的ファッション性に著しく富んだものになった。
又長期間による使用によっても外観の美感は容易に失わ
れなかった。As a result, in the obtained golf club shaft, the diamond pattern printed in three colors of red, blue and yellow is located in the back of the thin transparent layer on the surface of the golf club shaft and can be seen through the transparent layer. Therefore, it has a high appearance and is remarkably rich in aesthetic fashion.
Moreover, the aesthetic appearance was not easily lost even after long-term use.
【００３９】実施例２ 複合プリプレグ１として図３に示した装飾層３と透明プ
リプレグ層４との間に透明樹脂層８が積層された態様の
ものを使用した以外は、実施例１と同様にしてゴルフク
ラブシャフトを作成した。透明樹脂層８はエポキシ樹脂
で、その目付量は５０ｇ／ｍ2 であった。Example 2 Same as Example 1 except that a transparent resin layer 8 was laminated between the decorative layer 3 and the transparent prepreg layer 4 shown in FIG. 3 as the composite prepreg 1. To make a golf club shaft. The transparent resin layer 8 was an epoxy resin and had a basis weight of 50 g / m 2 .
【００４０】得られたゴルフクラブシャフトは、同様
に、赤、青、黄色の３色で印刷したダイヤの絵柄がゴル
フクラブシャフトの表面の薄い透明層の奥に透けて見
え、外観が高い美感を備え、美的ファッション性に著し
く富んだものになった。又長期間による使用によっても
外観の美感は容易に失われなかった。Similarly, in the obtained golf club shaft, the diamond pattern printed in three colors of red, blue and yellow can be seen through the depth of the thin transparent layer on the surface of the golf club shaft, giving a high appearance. As a preparation, it became remarkably rich in aesthetic fashion. Moreover, the aesthetic appearance was not easily lost even after long-term use.
【００４１】実施例３ 装飾層３の基材として厚み３０μｍの薄葉紙を使用し、
赤、青、黄色の３色でダイヤの絵柄を印刷する前に、そ
の下に樹脂浸透防止用インクで下地層を印刷した以外
は、実施例１と同様にして、ゴルフクラブシャフトを製
造した。Example 3 A thin paper having a thickness of 30 μm was used as a base material of the decorative layer 3,
A golf club shaft was manufactured in the same manner as in Example 1 except that before printing the diamond pattern in three colors of red, blue, and yellow, the underlayer was printed with the resin permeation preventive ink thereunder.
【００４２】その結果、ゴルフクラブシャフトは、赤、
青、黄色の３色で印刷したダイヤの絵柄がゴルフクラブ
シャフトの表面の薄い透明層中に浮いて見えるので、更
に好ましい美観が醸し出された。又その絵柄は樹脂によ
る濁り等の悪影響が少しもなかった。As a result, the golf club shaft is red,
The diamond pattern printed in the three colors of blue and yellow appears to float in the thin transparent layer on the surface of the golf club shaft, which further enhances the appearance. The design had no adverse effects such as turbidity due to the resin.
【００４３】[0043]
【発明の効果】以上説明したように、本発明では、繊維
強化複合樹脂材料製のゴルフクラブシャフトを、樹脂
層、その上に積層した図柄を樹脂層と反対側に有する装
飾層及びその装飾層上に積層した透明繊維強化複合樹脂
材料層からなる複合層を、複数層の繊維強化複合樹脂材
料層の最外層上に積層した構成に形成したので、手間の
かかる塗装等の作業を行なうことなく、ゴルフクラブシ
ャフトに容易に外観の美感を得ることができ、その美感
も長期に亙って安定して発揮させることができる。As described above, in the present invention, the golf club shaft made of the fiber-reinforced composite resin material is the resin layer, the decorative layer having the pattern laminated thereon on the side opposite to the resin layer, and the decorative layer thereof. Since the composite layer consisting of the transparent fiber reinforced composite resin material layer laminated on top is formed on the outermost layer of the plurality of fiber reinforced composite resin material layers, there is no need for laborious painting and other work. The appearance of the golf club shaft can be easily obtained, and the appearance can be stably exhibited over a long period of time.
【図１】本発明のゴルフクラブシャフトの一実施例を示
す断面図である。FIG. 1 is a sectional view showing an embodiment of a golf club shaft of the present invention.
【図２】本発明で使用する複合プリプレグを示す断面図
である。FIG. 2 is a cross-sectional view showing a composite prepreg used in the present invention.
【図３】図２の複合プリプレグの装飾層の図柄の下に下
地層を設けたことを示す断面図である。FIG. 3 is a cross-sectional view showing that a base layer is provided below the design of the decorative layer of the composite prepreg of FIG.
【図４】本発明で使用する複合プリプレグの他の実施態
様を示す断面図である。FIG. 4 is a cross-sectional view showing another embodiment of the composite prepreg used in the present invention.
【図５】従来のゴルフクラブシャフトを示す断面図であ
る。FIG. 5 is a sectional view showing a conventional golf club shaft.
【図６】ゴルフクラブシャフトの製造法を示す説明図で
ある。FIG. 6 is an explanatory diagram showing a method of manufacturing a golf club shaft.
【図７】ゴルフクラブシャフトを製造するためのプリプ
レグを示す平面図である。FIG. 7 is a plan view showing a prepreg for manufacturing a golf club shaft.
１ 複合プリプレグ １′ 複合層 ２ 樹脂層 ３ 装飾層 ４ 透明プリプレグ層 ７ 図柄 ７ａ 下地層 ８ 透明樹脂層 １０１′ アングル層 １０２′ ストレート層 DESCRIPTION OF SYMBOLS 1 Composite prepreg 1'Composite layer 2 Resin layer 3 Decorative layer 4 Transparent prepreg layer 7 Design 7a Underlayer 8 Transparent resin layer 101 'Angle layer 102' Straight layer
───────────────────────────────────────────────────── フロントページの続き (72)発明者 井上 寛 埼玉県入間郡大井町西鶴ケ岡１−３−１ 東燃株式会社総合研究所内 ─────────────────────────────────────────────────── ─── Continued Front Page (72) Inventor Hiroshi Inoue 1-3-1 Nishitsurugaoka, Oi-cho, Iruma-gun, Saitama Tonen Research Institute
Claims (2)
るゴルフクラブシャフトにおいて、樹脂層、前記樹脂層
上に積層した、図柄を前記樹脂層と反対側に有する装飾
層及び前記装飾層上に積層した透明繊維強化複合樹脂材
料層からなる複合層を、前記複数層の繊維強化複合樹脂
材料層の最外層上に少なくとも１層積層したことを特徴
とするゴルフクラブシャフト。1. A golf club shaft comprising a plurality of fiber-reinforced composite resin material layers, wherein a resin layer, a decorative layer laminated on the resin layer and having a pattern on the side opposite to the resin layer, and the decorative layer A golf club shaft, wherein at least one composite layer comprising the laminated transparent fiber reinforced composite resin material layers is laminated on the outermost layer of the plurality of fiber reinforced composite resin material layers.
材料層との間に更に透明樹脂層を積層した請求項１のゴ
ルフクラブシャフト。2. The golf club shaft according to claim 1, further comprising a transparent resin layer laminated between the decorative layer and the transparent fiber reinforced composite resin material layer.