JPH05210835A - Magnetic recording medium - Google Patents
Magnetic recording mediumInfo
- Publication number
- JPH05210835A JPH05210835A JP4014621A JP1462192A JPH05210835A JP H05210835 A JPH05210835 A JP H05210835A JP 4014621 A JP4014621 A JP 4014621A JP 1462192 A JP1462192 A JP 1462192A JP H05210835 A JPH05210835 A JP H05210835A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- inorganic powder
- layer
- recording medium
- intermediate layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、オーディオテープ、ビ
デオテープ、磁気ディスク等に用いる磁気記録媒体に関
するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a magnetic recording medium used for audio tapes, video tapes, magnetic disks and the like.
【０００２】[0002]
【従来の技術】近年、特にビデオテープにおいて長時間
記録を目的として、テープ全厚の薄膜化が進んでいる。
しかしながらテープ全厚の薄膜化に伴いテープ剛性が低
下し、走行耐久性、磁気ヘッドとのなじみ性、出力安定
性が悪化する等の問題が発生していた。これらの問題を
解決するために非磁性支持体と磁性層、または非磁性支
持体とバックコート層との間にテープ剛性の補強を目的
とした中間層を設ける試みがあり、中間層の強度を高め
るために無機質粉体と結合剤を組み合わせるものが多く
提案されている。2. Description of the Related Art In recent years, especially for video tapes, the total thickness of the tape has been made thinner for the purpose of long-time recording.
However, as the total thickness of the tape becomes thinner, the rigidity of the tape decreases, and running durability, compatibility with the magnetic head, and output stability deteriorate. In order to solve these problems, it has been attempted to provide an intermediate layer between the non-magnetic support and the magnetic layer, or between the non-magnetic support and the back coat layer, for the purpose of reinforcing the tape rigidity. Many proposals have been made to combine an inorganic powder and a binder in order to increase the amount.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、上記従
来の構成では、強度向上を図ろうとすると無機質粉体の
高充填化、結合剤の高硬質化により中間層の塗布性が悪
く、また表面性が悪くなる。したがってその上に磁性
層、バックコート層を重層塗布しても磁性層、バックコ
ート層自体の表面性が悪くなり、電磁変換特性を悪化さ
せる結果となってしまっている。However, in the above-mentioned conventional structure, when attempting to improve the strength, the coating property of the intermediate layer is poor and the surface property is poor due to the high packing of the inorganic powder and the high hardness of the binder. become worse. Therefore, even if the magnetic layer and the back coat layer are coated in multiple layers, the surface properties of the magnetic layer and the back coat layer themselves are deteriorated, and the electromagnetic conversion characteristics are deteriorated.
【０００４】本発明は上記課題を解決するものであり、
表面性を劣化させることなく、走行性、走行耐久性等に
優れた磁気記録媒体を提供することを目的とするもので
ある。The present invention is intended to solve the above problems,
An object of the present invention is to provide a magnetic recording medium excellent in running property, running durability and the like without deteriorating surface properties.
【０００５】[0005]
【課題を解決するための手段】上記目的を達成するため
に本発明は、非磁性支持体の一方の面に磁性層を、他方
の面にバックコート層をそれぞれ形成してなる磁気記録
媒体であって、非磁性支持体と磁性層との間および非磁
性支持体と前記バックコート層との間の少なくとも一方
に平板状無機質粉体と粒状無機質粉体を含有した中間層
を介在させてなるものである。To achieve the above object, the present invention provides a magnetic recording medium comprising a non-magnetic support having a magnetic layer formed on one surface and a back coat layer formed on the other surface. And an intermediate layer containing a flat inorganic powder and a granular inorganic powder interposed between at least one of the non-magnetic support and the magnetic layer and between the non-magnetic support and the back coat layer. It is a thing.
【０００６】[0006]
【作用】したがって本発明の構成によれば、非磁性支持
体と、磁性層およびバッコート層の少なくとも一方との
間に設ける中間層中に、平板状無機質粉体と粒状無機質
粉体を含有させることにより長手方向、及び横方向双方
の剛性に優れ、かつ塗布性及び表面性の向上した中間層
を設けることができる。これらの構成により電磁変換特
性の低下を招来することなく、走行性、走行耐久性を向
上することができる。Therefore, according to the constitution of the present invention, the flat inorganic powder and the granular inorganic powder are contained in the intermediate layer provided between the non-magnetic support and at least one of the magnetic layer and the backcoat layer. Thus, it is possible to provide an intermediate layer having excellent rigidity in both the longitudinal direction and the lateral direction and having improved coatability and surface property. With these configurations, it is possible to improve the traveling property and the traveling durability without deteriorating the electromagnetic conversion characteristics.
【０００７】[0007]
【実施例】以下本発明の一実施例について説明する。EXAMPLE An example of the present invention will be described below.
【０００８】本発明に用いる中間層の平板状無機質粉体
としては特に制限はなく、α−Ｆｅ 2Ｏ3、カオリン、雲
母、酸化亜鉛、バリウムフェライト等を単独または複数
種組み合わせて使用することができ、平均直径は０．２
〜３．０μｍ、板状比は５０から１００であることが望
ましい。また、中間層の粒状無機質粉体としても特に制
限はなく、α−Ｆｅ2Ｏ3、酸化チタン、酸化アルミニウ
ム、酸化亜鉛、酸化珪素等を単独または複数種組み合わ
せて使用することができる。平板状無機質粉体の平均直
径が０．２μｍより小さいと剛性を改善することが難し
く、３．０μｍより大きいと中間層の表面平滑性が悪く
なる。また粒状無機質粉体の平均直径が０．０１μｍよ
り小さいと分散が困難になるだけでなく塗布性も困難に
なる。また０．５μｍより大きいと磁性層の表面性が悪
化し、電磁変換特性が悪くなる。粒状無機質粉体の含有
量は全粉体量に対して１０〜６０％が好ましい（本実施
例において含有量とは粒状無機質粉体重量／（粒状無機
質粉体重量＋平板状無機質粉体重量）と定義する。）。
その含有量が１０％より少ないと塗料の塗布性が悪いた
め表面性の改善は困難であり、６０％より多いと剛性が
上がらない。中間層に用いる結合剤としてはポリウレタ
ン系樹脂、ニトロセルロース系樹脂、ポリエステル系樹
脂、塩化ビニル系共重合樹脂等が使用できる。本発明で
得られる磁気記録媒体用磁性層は強磁性粉末、結合剤、
研磨剤、及び必要に応じて加えられる帯電防止剤、潤滑
剤よりなる層を非磁性支持体（通常はプラスチックフィ
ルム）上に公知の方法により形成することができる。非
磁性支持体としては、ＰＥＴ、ＰＥＮ、芳香族ポリアミ
ド、芳香族ポリイミド等がある。The flat inorganic powder for the intermediate layer used in the present invention
Is not particularly limited, and α-Fe 2O3, Kaolin, clouds
Single or multiple mothers, zinc oxide, barium ferrite, etc.
Can be used in combination with seeds and has an average diameter of 0.2
~ 3.0μm, plate ratio should be 50 to 100
Good. In addition, it is especially effective as a granular inorganic powder for the intermediate layer.
There is no limit, α-Fe2O3, Titanium oxide, aluminum oxide
Aluminum, zinc oxide, silicon oxide, etc., alone or in combination.
Can be used. Average straightness of flat inorganic powder
If the diameter is smaller than 0.2 μm, it is difficult to improve the rigidity.
If it is more than 3.0 μm, the surface smoothness of the intermediate layer is poor.
Become. Also, the average diameter of the granular inorganic powder is 0.01 μm.
If it is too small, not only the dispersion becomes difficult but also the coatability becomes difficult.
Become. If it is larger than 0.5 μm, the surface property of the magnetic layer is bad.
And the electromagnetic conversion characteristics deteriorate. Incorporation of granular inorganic powder
The amount is preferably 10 to 60% with respect to the total amount of powder (this implementation
In the examples, the content is the weight of granular inorganic powder / (granular inorganic powder
Fine powder weight + tabular inorganic powder weight). ).
If the content is less than 10%, the coating property of the paint is poor.
Therefore, it is difficult to improve the surface property, and if it exceeds 60%, the rigidity will be
I can't go up. Polyurethane is used as the binder for the intermediate layer.
Resin, nitrocellulose resin, polyester resin
Fats, vinyl chloride copolymer resins, etc. can be used. In the present invention
The magnetic layer for the magnetic recording medium obtained is a ferromagnetic powder, a binder,
Abrasive, antistatic agent added as needed, lubrication
The layer of agent is applied to a non-magnetic support (usually a plastic film).
It can be formed by a known method. Non
As the magnetic support, PET, PEN, aromatic polyamid
And aromatic polyimide.
【０００９】磁性層に用いる強磁性粉末には、メタル磁
性粉、コバルト被着磁性酸化鉄、バリウムフェライト磁
性粉等がある。結合剤としては、ポリウレタン系樹脂、
ニトロセルロース系樹脂、ポリエステル系樹脂、塩化ビ
ニル系共重合樹脂等が使用できる。研磨剤としては、ア
ルミナ、酸化クロム、酸化珪素、ベンガラ等がある。帯
電防止剤としては、導電性カーボンを使用することがで
きる。潤滑剤としては、高級脂肪酸や高級脂肪酸エステ
ル、または各種界面活性剤を単独または複数種を組み合
わせて使用することができる。The ferromagnetic powder used for the magnetic layer includes metal magnetic powder, cobalt-coated magnetic iron oxide, barium ferrite magnetic powder and the like. As the binder, polyurethane resin,
Nitrocellulose resin, polyester resin, vinyl chloride copolymer resin, etc. can be used. Examples of the abrasive include alumina, chromium oxide, silicon oxide, red iron oxide and the like. Conductive carbon can be used as the antistatic agent. As the lubricant, higher fatty acids, higher fatty acid esters, or various surfactants can be used alone or in combination of two or more kinds.
【００１０】（実施例１） 磁性層用塗料の作製 コバルト被着磁性酸化鉄 １００部 （ＢＥＴ ５＊１０4m2／kg） （σｓ １＊１０-4Ｗｂｍ／kg） （Ｈｃ ６．２＊１０4Ａ／ｍ） アルミナ ８部 カーボンブラック １部 塩化ビニル樹脂 １０部 ポリウレタン樹脂 １０部 混合溶剤 ４００部 上記組成を加圧ニーダ、サンドミル等で分散した磁性塗
料にディスパーで攪拌しながら ミリスチン酸 １部 ｎ−ブチルステアレート １部 ポリイソシアネート ５部 を添加し、磁性層用塗料を作製した。この時、樹脂溶液
用の有機溶剤はメチルエチルケトン／トルエン／シクロ
ヘキサノンを重量比で３／２／１にしたものを用いた。
この塗料を６．５μｍ厚のＰＥＴ支持体上に塗布、乾燥
した後、カレンダー処理による鏡面加工を施して厚さ
２．８μｍの磁性層を作製した。Example 1 Preparation of coating material for magnetic layer 100 parts of cobalt-coated magnetic iron oxide (BET 5 * 10 4 m 2 / kg) (σs 1 * 10 −4 Wbm / kg) (Hc 6.2 *) 10 4 A / m) Alumina 8 parts Carbon black 1 part Vinyl chloride resin 10 parts Polyurethane resin 10 parts Mixed solvent 400 parts Myristic acid 1 part while stirring the above composition with a magnetic paint dispersed with a pressure kneader, sand mill, etc. n-Butyl stearate 1 part Polyisocyanate 5 parts was added to prepare a magnetic layer coating material. At this time, the organic solvent for the resin solution used was methyl ethyl ketone / toluene / cyclohexanone in a weight ratio of 3/2/1.
This coating material was applied onto a PET support having a thickness of 6.5 μm, dried, and then mirror-finished by calendering to form a magnetic layer having a thickness of 2.8 μm.
【００１１】 中間層用塗料の作製（全粉体量を１００部とする。） 板状無機質粉体（α−Ｆｅ2Ｏ3） （平均直径０．８０μｍ、板状比４９） ８０部 粒状無機質粉体（α−Ｆｅ2Ｏ3） （平均直径０．１０μｍ） ２０部 塩化ビニル樹脂 ４０部 ポリウレタン樹脂 ４０部 メチルエチルケトン ２００部 トルエン ２００部 上記組成を加圧ニーダ、サンドミル等で分散した塗料に
ディスパーで攪拌しながら ポリイソシアネート ２０部 を添加し、中間層用塗料とした。Preparation of paint for intermediate layer (total powder amount is 100 parts) Plate-like inorganic powder (α-Fe 2 O 3 ) (average diameter 0.80 μm, plate ratio 49) 80 parts Granular inorganic material Powder (α-Fe 2 O 3 ) (average diameter 0.10 μm) 20 parts Vinyl chloride resin 40 parts Polyurethane resin 40 parts Methyl ethyl ketone 200 parts Toluene 200 parts Dispersed in a paint in which the above composition is dispersed with a pressure kneader or a sand mill. While stirring, 20 parts of polyisocyanate was added to obtain a paint for the intermediate layer.
【００１２】 バックコート層用の塗料の作製 カーボンブラック １００部 ニトロセルロース樹脂 ４０部 ポリウレタン樹脂 ４０部 メチルエチルケトン ２００部 トルエン ２００部 上記組成を加圧ニーダ、サンドミル等で分散した塗料に
ディスパーで攪拌しながら ステアリン酸 １部 ポリイソシアネート ２０部 を添加し、バックコート塗料とした。磁性層とは反対側
の非磁性支持体上にこの二つの塗料を塗布、乾燥して
１．０μｍの中間層、０．７μｍ厚のバックコート層を
作製し、１／２インチ幅に切断してビデオテープ試料を
得た。Preparation of paint for back coat layer Carbon black 100 parts Nitrocellulose resin 40 parts Polyurethane resin 40 parts Methyl ethyl ketone 200 parts Toluene 200 parts Stirrer while stirring the above composition in a paint dispersed with a pressure kneader, a sand mill, etc. An acid 1 part and polyisocyanate 20 parts were added to obtain a back coat paint. These two paints were applied on the non-magnetic support on the side opposite to the magnetic layer and dried to form a 1.0 μm intermediate layer and a 0.7 μm thick back coat layer, which were cut into 1/2 inch widths. A videotape sample was obtained.
【００１３】（実施例２）（実施例１）における中間層
用塗料に用いる粒状無機質粉体の含有量を全粉体の５０
％にした。そしてそれ以外はすべて（実施例１）と同様
にしてビデオテープ試料を作製した。(Example 2) The content of the granular inorganic powder used in the coating material for the intermediate layer in (Example 1) is 50% of the total powder.
%. A video tape sample was prepared in the same manner as in (Example 1) except for the above.
【００１４】（実施例３）（実施例１）における中間層
用塗料に用いる板状無機質粉体の平均直径を２．３μ
ｍ、板状比８０とし、粒状無機質粉体の含有量を全粉体
の２０％にした。そしてそれ以外はすべて（実施例１）
と同様にしてビデオテープ試料を作製した。(Example 3) The average diameter of the plate-like inorganic powder used in the coating material for the intermediate layer in (Example 1) is 2.3 μm.
m and plate ratio 80, and the content of the granular inorganic powder was 20% of the total powder. And everything else (Example 1)
A video tape sample was prepared in the same manner as in.
【００１５】（実施例４）（実施例１）における中間層
用塗料に用いる板状無機質粉体の平均直径を２．３μ
ｍ、板状比８０とし、粒状無機質粉体の含有量を全粉体
の５０％にした。そしてそれ以外はすべて（実施例１）
と同様にしてビデオテープ試料を作製した。(Example 4) The average diameter of the plate-like inorganic powder used in the coating material for the intermediate layer in (Example 1) is 2.3 μm.
m, the plate ratio was 80, and the content of the granular inorganic powder was 50% of the total powder. And everything else (Example 1)
A video tape sample was prepared in the same manner as in.
【００１６】（実施例５）（実施例１）におけるバック
コート層側に設けた中間層を磁性層側だけに設けた以外
はすべて（実施例１）と同様にしてビデオテープ試料を
作製した。Example 5 A video tape sample was prepared in the same manner as in Example 1 except that the intermediate layer provided on the back coat layer side in Example 1 was provided only on the magnetic layer side.
【００１７】（実施例６）（実施例１）におけるバック
コート層側に中間層を０．５μｍ、磁性層に０．５μｍ
厚の中間層を設けた以外はすべて（実施例１）と同様に
してビデオテープ試料を作製した。(Example 6) In Example 1, the back coat layer side has an intermediate layer of 0.5 μm and the magnetic layer has a thickness of 0.5 μm.
A video tape sample was prepared in the same manner as in (Example 1) except that a thick intermediate layer was provided.
【００１８】（比較例１）（実施例１）における中間層
用塗料を板状無機質粉体のみで作製した。そしてそれ以
外はすべて（実施例１）と同様にしてビデオテープ試料
を作製した。(Comparative Example 1) The coating material for the intermediate layer in (Example 1) was prepared using only the plate-like inorganic powder. A video tape sample was prepared in the same manner as in (Example 1) except for the above.
【００１９】（比較例２）（実施例１）における中間層
用塗料に用いる粒状無機質粉体の含有量を全粉体の１０
％にした。そしてそれ以外はすべて（実施例１）と同様
にしてビデオテープ試料を作製した。(Comparative Example 2) The content of the granular inorganic powder used in the coating material for the intermediate layer in (Example 1) was 10% of the total powder.
%. A video tape sample was prepared in the same manner as in (Example 1) except for the above.
【００２０】（比較例３）（実施例１）における中間層
用塗料に用いる粒状無機質粉体の含有量を全粉体の７０
％にした。そしてそれ以外はすべて（実施例１）と同様
にしてビデオテープ試料を作製した。(Comparative Example 3) The content of the granular inorganic powder used in the coating material for the intermediate layer in (Example 1) was 70% of the total powder.
%. A video tape sample was prepared in the same manner as in (Example 1) except for the above.
【００２１】（比較例４）（実施例１）における中間層
用塗料を粒状無機質粉体のみで作製した。そしてそれ以
外はすべて（実施例１）と同様にしてビデオテープ試料
を作製した。(Comparative Example 4) The coating material for the intermediate layer in (Example 1) was prepared using only the granular inorganic powder. A video tape sample was prepared in the same manner as in (Example 1) except for the above.
【００２２】（比較例５）（実施例１）における中間層
用塗料を平均直径２．３μｍ、板状比８０の板状無機質
粉体のみを用い作製した。そしてそれ以外はすべて（実
施例１）と同様にしてビデオテープ試料を作製した。以
上の各実施例および各比較例の中間層の粒状無機質粉体
の含有率および板状無機質粉体の平均直径と板状比とを
（表１）に示した。Comparative Example 5 The coating material for the intermediate layer in (Example 1) was prepared using only plate-like inorganic powder having an average diameter of 2.3 μm and a plate-like ratio of 80. A video tape sample was prepared in the same manner as in (Example 1) except for the above. Table 1 shows the content of the granular inorganic powder, the average diameter of the plate-like inorganic powder, and the plate-like ratio in the intermediate layer of each of the above Examples and Comparative Examples.
【００２３】[0023]
【表１】 [Table 1]
【００２４】得られた各試料について以下の評価を行っ
た。 （１）バックコート層の表面粗さ［ｎｍ］ ランク・テーラー・ホブソン社製のタリステップ触針型
表面粗さ計を用いて測定したバックコート層の表面粗
さ。The following evaluations were performed on each of the obtained samples. (1) Surface roughness of backcoat layer [nm] The surface roughness of the backcoat layer measured using a Talystep stylus type surface roughness meter manufactured by Rank Taylor Hobson.
【００２５】（２）テープスティフネス［ｍｇ］ 東洋精機（株）製のループスティフネステスターを用い
テープの長手（ＭＤ）方向、横（ＴＤ）方向のテープス
ティフネス（座屈強度）を求めた。(2) Tape stiffness [mg] The tape stiffness (buckling strength) in the longitudinal (MD) direction and the transverse (TD) direction of the tape was determined using a loop stiffener tester manufactured by Toyo Seiki Co., Ltd.
【００２６】（３）走行耐久性 松下電器産業（株）製Ｓ−ＶＨＳビデオデッキＮＶ−Ｆ
Ｓ１を用いて再生／巻戻し１００パス走行後の、テープ
の目視状態による走行耐久性。(3) Running durability Matsushita Electric Industrial Co., Ltd. S-VHS video deck NV-F
Running durability by visual observation of the tape after 100 passes of reproduction / rewinding using S1.
【００２７】（４）Ｃ／Ｎ［ｄＢ］ 松下電器産業（株）製Ｓ−ＶＨＳビデオデッキＮＶ−Ｆ
Ｓ１を用いて７ＭHzの信号と５ＭHzのノイズの比（Ｃ／
Ｎ）を測定し、松下電器産業（株）製Ｓ−ＶＨＳビデオ
テープＸＤ１２０を０ｄＢとして比較したＣ／Ｎ。(4) C / N [dB] S-VHS video deck NV-F manufactured by Matsushita Electric Industrial Co., Ltd.
Using S1, the ratio of 7MHz signal and 5MHz noise (C /
C / N which measured N) and compared S-VHS video tape XD120 by Matsushita Electric Industrial Co., Ltd. as 0 dB.
【００２８】このように測定して得られた結果を（表
２）に示した。The results obtained by the above measurement are shown in (Table 2).
【００２９】[0029]
【表２】 [Table 2]
【００３０】このように上記実施例によれば、表面性や
テープスティフネスを殆ど低下させることなく、走行耐
久性やＣ／Ｎを向上させることが可能となった。As described above, according to the above-mentioned embodiment, it is possible to improve the running durability and the C / N without substantially reducing the surface property and the tape stiffness.
【００３１】[0031]
【発明の効果】上記実施例より明らかなように本発明
は、非磁性支持体の少なくとも一方の面上に設けた中間
層を平板状無機質粉体及び粒状無機質粉体を含む構成と
していることによって、良好な表面性が得られるととも
にテープの長手方向、及び横方向の両方向の剛性を強化
することが可能となる。これらの構成により電磁変換特
性の低下を招来することなく、走行性、走行耐久性を向
上することができる。As is apparent from the above-described examples, the present invention has a structure in which the intermediate layer provided on at least one surface of the non-magnetic support contains a flat inorganic powder and a granular inorganic powder. In addition, good surface properties can be obtained, and the rigidity of the tape in both the longitudinal direction and the lateral direction can be enhanced. With these configurations, it is possible to improve the traveling property and the traveling durability without deteriorating the electromagnetic conversion characteristics.
Claims (4)
の面にバックコート層をそれぞれ形成してなる磁気記録
媒体であって、前記非磁性支持体と前記磁性層との間お
よび前記非磁性支持体と前記バックコート層との間の少
なくとも一方に平板状無機質粉体と粒状無機質粉体を含
有した中間層を介在させてなる磁気記録媒体。1. A magnetic recording medium comprising a magnetic layer formed on one surface of a non-magnetic support and a back coat layer formed on the other surface of the non-magnetic support, which is between the non-magnetic support and the magnetic layer. And a magnetic recording medium having an intermediate layer containing a flat inorganic powder and a granular inorganic powder interposed between at least one of the non-magnetic support and the back coat layer.
平均直径を有する平板状無機質粉体である請求項１記載
の磁気記録媒体。2. The magnetic recording medium according to claim 1, wherein the flat inorganic powder is a flat inorganic powder having an average diameter of 0.2 to 3.0 μm.
（平均直径／平均厚さ）を有する平板状無機質粉体であ
る請求項１記載の磁気記録媒体。3. The magnetic recording medium according to claim 1, wherein the flat inorganic powder is a flat inorganic powder having a plate ratio (average diameter / average thickness) of 5 to 150.
平均直径を有する粒状無機質粉体である請求項１記載の
磁気記録媒体。4. The magnetic recording medium according to claim 1, wherein the granular inorganic powder is a granular inorganic powder having an average diameter of 0.01 to 0.5 μm.