JPH05170858A - Resin composition for repair - Google Patents
Resin composition for repairInfo
- Publication number
- JPH05170858A JPH05170858A JP3344289A JP34428991A JPH05170858A JP H05170858 A JPH05170858 A JP H05170858A JP 3344289 A JP3344289 A JP 3344289A JP 34428991 A JP34428991 A JP 34428991A JP H05170858 A JPH05170858 A JP H05170858A
- Authority
- JP
- Japan
- Prior art keywords
- filler
- repairing
- resin composition
- active hydrogen
- diisocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は木材合板等の補修用樹脂
組成物に関するものであり、特に、針葉樹の補修に好適
なウレタン樹脂組成物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a resin composition for repairing wood plywood and the like, and more particularly to a urethane resin composition suitable for repairing softwood.
【0002】[0002]
【従来の技術】従来、木材、合板あるいは合板用単板等
の木質材を補修するために、充填剤を含む樹脂組成物が
利用されている。樹脂としてはエラストマー系の熱可塑
性樹脂、熱可塑性樹脂にアミノ樹脂等を配合したもの、
ウレタン系樹脂などが使用されている。ウレタン樹脂は
高価ではあるが、木材との接着性に優れているので、比
較的高価な木材に使用されている。近年、南洋樹の不足
から針葉樹の需要が増加しつつあるが、針葉樹はフシ穴
が多く、また、合板用単板への加工では、材質が硬いた
め平滑な切削が困難であるので、補修が必要な場合が多
い。このためには接着力の大きいウレタン樹脂が好まし
く使用される。2. Description of the Related Art Conventionally, a resin composition containing a filler has been used to repair wood materials such as wood, plywood or veneer for plywood. As the resin, an elastomeric thermoplastic resin, a thermoplastic resin blended with an amino resin or the like,
Urethane resin is used. Although urethane resin is expensive, it is used for relatively expensive wood because it has excellent adhesion to wood. In recent years, the demand for coniferous trees is increasing due to the shortage of South Sea trees, but coniferous trees have a lot of fungus holes, and in the processing of veneer for plywood, it is difficult to perform smooth cutting because the material is hard, so it is difficult to repair. Often needed. For this purpose, urethane resin having a large adhesive force is preferably used.
【0003】木質材補修用樹脂組成物には、乾燥又は硬
化時、膨張したり、収縮したりしないことが要求され、
また硬化後木質材が反らないこと、樹脂組成物にクラッ
クが入らないことなどが重要である。ウレタン樹脂組成
物は組成物あるいは木材や空気中の水分により発泡して
膨張する、いわゆる「ふくれ」が生じ、更にこれにより
接着力の低下を招く欠点があり、更に柔乾性が十分でな
いので、硬化後反りが生じることが多い。A resin composition for repairing wood materials is required not to expand or contract when dried or cured,
Further, it is important that the wood material does not warp after curing and that the resin composition does not crack. The urethane resin composition has a drawback that it foams and expands due to the composition or wood or moisture in the air, so-called "blister" occurs, which further causes a decrease in adhesive strength, and further the softness is not sufficient. Warpage often occurs.
【0004】[0004]
【発明が解決しようとする課題】本発明は、ウレタン樹
脂系の木質材用補修材の前記の如き欠点を解決するため
に種々検討した結果完成されたもので、特に針葉樹の補
修に適したウレタン樹脂組成物を提供するものである。SUMMARY OF THE INVENTION The present invention has been completed as a result of various studies to solve the above-mentioned drawbacks of urethane resin-based repairing materials for wood materials, and is particularly suitable for repairing softwood. A resin composition is provided.
【0005】[0005]
【課題を解決するための手段】本発明は、(a)活性水素
含有化合物、(b)ポリイソシアネート化合物、(c)充填
剤を必須成分とする木質材補修用樹脂組成物であって、
更に、(d)可塑剤、水分を捕捉する充填剤として(e)酸
化マグネシウム、酸化カルシウム、酸化バリウムの少な
くとも一種が配合されていることを特徴とする木質材補
修用樹脂組成物である。The present invention provides a resin composition for repairing wood materials, which comprises (a) an active hydrogen-containing compound, (b) a polyisocyanate compound, and (c) a filler as essential components,
Further, the resin composition for repairing wood materials is characterized in that (d) a plasticizer and (e) at least one of magnesium oxide, calcium oxide and barium oxide are blended as a filler for trapping water.
【0006】本発明における樹脂組成物に用いる(a)
活性水素含有化合物は、分子中にヒドロキシル基、アミ
ノ基、活性メチレン基などを2個以上有する化合物が使
用できるが、各種ポリエステルポリオール、ポリエーテ
ルポリオール、アクリルポリオール、ウレタンポリオー
ル、エポキシポリオール、端末ヒドロキシルポリブタジ
エン、ポリカーボネートポリオール、エチレングリコー
ル、ブチレングリコール、ジエチレングリコール、ネオ
ペンチルグリコール、トリメチロールエタン、トリメチ
ロールプロパン、グリセリン、ヘキサントリオール、ヒ
マシ油、等が一般に単独又は併用して使用される。Used in the resin composition of the present invention (a)
As the active hydrogen-containing compound, a compound having two or more hydroxyl groups, amino groups, active methylene groups and the like can be used, but various polyester polyols, polyether polyols, acrylic polyols, urethane polyols, epoxy polyols, terminal hydroxyl polybutadienes. , Polycarbonate polyol, ethylene glycol, butylene glycol, diethylene glycol, neopentyl glycol, trimethylolethane, trimethylolpropane, glycerin, hexanetriol, castor oil, etc. are generally used alone or in combination.
【0007】本発明における(b)ポリイソシアネート
化合物としては、分子中に2個以上のイソシアネート基
を有するものである。例えば、ヘキサメチレンジイソシ
アネート、2,4−ジイソシアネート−1−メチルシク
ロヘキサン、2,6−ジイソシアネート−1−メチルシ
クロヘキサン、ジイソシアネートシクロブタン、テトラ
メチレンジイソシアネート、o−,m−及びp−キシリ
レンジイソシアネート、ジシクロヘキシルメタンジイソ
シアネート、ジメチルジシクロヘキシルメタンジイソシ
アネート、及びリジンジイソシアネート、アルステルな
どのような脂肪族または脂環式ジイソシアネート、トリ
レン−2,4−ジイソシアネート、ジフェニルメタン−
4,4′−ジイソシアネート、3−メチルジフェニルメ
タン−4,4′−ジイソシアネート、m−及びp−フェ
ニレンジイソシアネート、クロロフェニレン−2,4−
ジイソシアネート、ナフタリン−1,8−ジイソシアネ
ート−3,3′−ジメチルジフェニル、1,3,5−ト
リイソプロピルベンゼン−2,4−ジイソシアネート、
及びジフェニルエーテルジイソシアネートのような芳香
族ポリイソシアネート及びこれらの混合物であってもよ
い。またこれらのポリイソシアネートの過剰をエチレン
グリコール、ブチレングリコール、ジエチレングリコー
ル、ネオペンチルグリコール、トリメチロールプロパ
ン、グリセリン、ヘキサントリオールのようなポリヒド
ロキシ化合物と反応させることによって得られるポリウ
レタン・ポリイソシアネートであってもよい。また、イ
ソシアヌレート環を含むポリイソシアネート、アロファ
ネート基を含むポリイソシアネート、ビュレット基を含
むポリイソシアネートなども使用することができる。ま
た、場合によっては、ダイマー酸より誘導されたポリイ
ソシアネートも用いることができる。The polyisocyanate compound (b) in the present invention has two or more isocyanate groups in the molecule. For example, hexamethylene diisocyanate, 2,4-diisocyanate-1-methylcyclohexane, 2,6-diisocyanate-1-methylcyclohexane, diisocyanate cyclobutane, tetramethylene diisocyanate, o-, m- and p-xylylene diisocyanate, dicyclohexylmethane diisocyanate. , Dimethyldicyclohexylmethane diisocyanate, and aliphatic or cycloaliphatic diisocyanates such as lysine diisocyanate, alstel, etc., tolylene-2,4-diisocyanate, diphenylmethane-
4,4'-diisocyanate, 3-methyldiphenylmethane-4,4'-diisocyanate, m- and p-phenylene diisocyanate, chlorophenylene-2,4-
Diisocyanate, naphthalene-1,8-diisocyanate-3,3'-dimethyldiphenyl, 1,3,5-triisopropylbenzene-2,4-diisocyanate,
And aromatic polyisocyanates such as diphenyl ether diisocyanate and mixtures thereof. It may also be a polyurethane polyisocyanate obtained by reacting an excess of these polyisocyanates with a polyhydroxy compound such as ethylene glycol, butylene glycol, diethylene glycol, neopentyl glycol, trimethylolpropane, glycerin, and hexanetriol. .. Further, a polyisocyanate containing an isocyanurate ring, a polyisocyanate containing an allophanate group, a polyisocyanate containing a buret group and the like can also be used. Further, in some cases, a polyisocyanate derived from dimer acid can also be used.
【0008】本発明におけるイソシアネート基を活性水
素のモル比、例えば−NCO/−OH当量比は 0.5〜
5の範囲に調合される。−NCO/−OH当量比が 0.
5未満の場合は、硬化が不十分となり、良好な硬化物を
得ることができず、また5以上になると過剰イソシアネ
ート基の反応によって硬化物が硬くなり過ぎたり、接着
強度が低下するなどの問題が生じる。この当量比は好ま
しくは1〜3の範囲であり、この範囲では硬化が十分
で、良好な硬化物が得られる。In the present invention, the molar ratio of isocyanate group to active hydrogen, for example, the --NCO /-OH equivalent ratio, is 0.5 to 0.5.
It is mixed in the range of 5. The -NCO / -OH equivalent ratio is 0.0.
When it is less than 5, curing is insufficient and a good cured product cannot be obtained. When it is 5 or more, the cured product becomes too hard due to the reaction of excess isocyanate groups, and the adhesive strength is lowered. Occurs. This equivalent ratio is preferably in the range of 1 to 3, in which the curing is sufficient and a good cured product is obtained.
【0009】本発明における(c)充填剤としては、無
機充填剤、例えば炭酸カルシウム、タルク、クレー、ベ
ントナイト、石膏、アルミナ、珪藻土、硫酸バリウム、
シリカ、水酸化カルシウム、パーライト、バーミキュラ
イト、マイカ粉、ガラス粉などが使用でき、また、微細
な木粉、籾殻粉、合成樹脂粉末などの有機質充填剤及び
混合充填剤が使用できる。As the filler (c) in the present invention, inorganic fillers such as calcium carbonate, talc, clay, bentonite, gypsum, alumina, diatomaceous earth, barium sulfate,
Silica, calcium hydroxide, perlite, vermiculite, mica powder, glass powder and the like can be used, and also organic fillers and mixed fillers such as fine wood powder, rice husk powder and synthetic resin powder can be used.
【0010】本発明に使用する(d)可塑剤は、ジブチ
ルフタレート、ジオクチルフタレート、ジアリルフタレ
ート等のフタル酸エステル、トリフェニルフォスフェー
ト、ジフェニルクレジルフォスフェート等のリン酸エス
テル等が使用可能である。この中で組成物の粘度を上昇
させず、揮発性が小さく、安価であることから、ジブチ
ルフタレートが最も好ましい。As the plasticizer (d) used in the present invention, phthalic acid esters such as dibutyl phthalate, dioctyl phthalate and diallyl phthalate, and phosphoric acid esters such as triphenyl phosphate and diphenyl cresyl phosphate can be used. .. Of these, dibutyl phthalate is most preferable because it does not increase the viscosity of the composition, has low volatility, and is inexpensive.
【0011】本発明の組成物における(e)酸化カルシ
ウム、酸化マグネシウム、酸化バリウムの少なくとも一
種以上の添加量は、組成物の含有水分量及び木質材の種
類及び含水率に応じて任意に選択することができるが、
硬化時の発泡を効果的に防止するためには組成物中に1
重量%以上含有させることが必要であり、望ましくは2
重量%以上である。また、酸化カルシウム、酸化マグネ
シウム、酸化バリウムは単独或いは任意の割合で混合し
て用いてもよい。充填剤は活性水素含有化合物及びポリ
イソシアネート化合物のいずれか、または両方に添加し
てもよいが、取扱い易さや発泡防止効果から活性水素含
有化合物に添加することが望ましい。本発明の組成物に
おけるその他の添加剤としては、硬化促進剤、シランカ
ップリング剤、着色剤、揺変剤、希釈剤などを必要に応
じて使用する。The addition amount of at least one of (e) calcium oxide, magnesium oxide and barium oxide in the composition of the present invention is arbitrarily selected according to the water content of the composition and the type and water content of the wood material. But you can
In order to effectively prevent foaming during curing, 1 in the composition
It is necessary to contain at least wt%, preferably 2
It is more than weight%. Further, calcium oxide, magnesium oxide, and barium oxide may be used alone or as a mixture at an arbitrary ratio. The filler may be added to either or both of the active hydrogen-containing compound and the polyisocyanate compound, but is preferably added to the active hydrogen-containing compound for ease of handling and foaming prevention effect. As other additives in the composition of the present invention, a curing accelerator, a silane coupling agent, a colorant, a thixotropic agent, a diluent and the like are used as necessary.
【0012】[0012]
【作用】本発明の樹脂組成物は二液硬化型ウレタン系で
あり、通常(a)活性水素含有化合物、(c)充填剤、
(d)可塑剤及びその他の添加剤からなる第一方の液剤
(以下、主剤とよぶ)と(b)ポリイソシアネート化合
物である第二方の液剤(以下、硬化剤とよぶ)を各種混
合機を用いて混合し、ロールコーターやナイフコーター
を用いて木質材に塗布した後常温または加熱下において
反応硬化して使用される。従来の組成物が「ふくれ」を
生じて木材製品の欠陥となり問題となることが多かった
のは、用いられるポリイソシアネート化合物が空気中や
木材中の水分あるいは活性水素含有化合物に含まれる水
分と反応して、硬化時に炭酸ガスを発生し、接着剤層に
大小の気泡を形成して剥離もしくは接着強度の低下をも
たらした結果であり、本発明の組成物は、水分捕捉のた
めの充填剤として酸化カルシウム、酸化マグネシウム、
酸化バリウムの少なくとも一種を添加することにより、
組成物に含有されている水分、混合、塗布工程において
大気中から吸収される水分及び木材に含有されている水
分を水酸化物の形で効果的に除去し、イソシアネートと
水分との反応によって発生する炭酸ガスがもたらす「ふ
くれ」や接着不良による欠陥の問題を解決したものであ
る。The resin composition of the present invention is a two-component curing type urethane system, and usually contains (a) an active hydrogen-containing compound, (c) a filler,
(D) A first liquid agent (hereinafter referred to as a main agent) comprising a plasticizer and other additives and (b) a second liquid agent (hereinafter referred to as a curing agent) which is a polyisocyanate compound are mixed in various mixers. It is used by being mixed by using, and applied to a wood material by using a roll coater or a knife coater, and then reactively cured at room temperature or under heating. It was often the case that the conventional composition causes "blister" and becomes a defect of wood products, and the problem is that the polyisocyanate compound used reacts with the water contained in the air or wood or the water contained in the active hydrogen-containing compound. The result is that carbon dioxide gas is generated at the time of curing, and large and small bubbles are formed in the adhesive layer to cause peeling or a decrease in adhesive strength. The composition of the present invention serves as a filler for capturing water. Calcium oxide, magnesium oxide,
By adding at least one of barium oxide,
Effectively removes water contained in the composition, water absorbed from the atmosphere in the mixing and coating process and water contained in wood in the form of hydroxide, and is generated by the reaction between isocyanate and water. It solves the problems of "blisters" caused by carbon dioxide gas and defective defects due to poor adhesion.
【0013】[0013]
【実施例】以下、本発明を実施例によって具体的に説明
するが、本発明は実施例によって限定されるものではな
い。なお実施例及び比較例に記載されている「部」及び
「%」は「重量部」及び「重量%」を示す。 [実施例1]ビスフェノールAにエチレンオキサイドを
付加して得たポリエーテルポリオール(平均分子量68
0、水酸基価165mg KOH/g)120部、可塑剤として
ジブチルフタレート100部に、充填剤として酸化カル
シウム10部、炭酸カルシウム370部、超微粉末シリ
カ20部、硬化促進剤(ジブチル錫ラウレート)2部を
添加し主剤とした。硬化剤としてポリメリックMDI
(イソシアネート基含有率31%)40部を加え補修用
樹脂組成物とした。このときの−NCO/−OHモル比
は1.3である。この樹脂組成物を、フシ穴が多数あり、
表面に木目が凸部となっている米松の板にナイフコータ
ーにより塗布し、室温下で24時間放置して硬化させ、
表面が平滑化した米松板を得た。 [実施例2及び3]酸化カルシウムを、それぞれ酸化マ
グネシウム、酸化バリウムに代えた以外は実施例1と同
様に行った。 [実施例4]ポリプロピレングリコールにエチレングリ
コールを付加して得たポリエーテルポリオール(平均分
子量1000、水酸基価114mg KOH/g)150部、可
塑剤としてジブチルフタレート100部に、充填剤とし
て酸化カルシウム20部、炭酸カルシウム400部、超
微粉末シリカ20部、硬化促進剤(ジブチル錫ラウレー
ト)2部を添加し主剤とした。硬化剤としてポリメリッ
クMDI(イソシアネート基含有率31%)40部を加
え補修用樹脂組成物とした。このとき−NCO/−OH
モル比は1.3である。以下、実施例1と同様にして米松
板を補修した。 [実施例5及び6]酸化カルシウムを酸化マグネシウ
ム、酸化バリウムに代えた以外は実施例4と同様に行っ
た。 [比較例1]充填剤をすべて炭酸カルシウムとした以外
は実施例1と同様に行った。 [比較例2及び3]充填剤をすべて炭酸カルシウムと
し、可塑剤をそれぞれジエチルフタレート、ジオクチル
フタレートとした以外は実施例1と同様に行った。比較
例3は粘度が高く、塗布がやや困難であった。得られた
米松板について表面状態を目視で観察した。更にフシ穴
の部分の樹脂硬化物の密着性を調べた。その結果を表1
に示す。EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to the examples. The "parts" and "%" described in the examples and comparative examples mean "parts by weight" and "% by weight". Example 1 Polyether polyol obtained by adding ethylene oxide to bisphenol A (average molecular weight 68
0, hydroxyl value 165 mg KOH / g) 120 parts, plasticizer 100 parts dibutylphthalate, filler 10 parts calcium oxide, calcium carbonate 370 parts, ultrafine silica powder 20 parts, curing accelerator (dibutyltin laurate) 2 Was added as a main ingredient. Polymeric MDI as curing agent
(Isocyanate group content 31%) 40 parts was added to give a repairing resin composition. At this time, the -NCO / -OH molar ratio is 1.3. This resin composition has a large number of bush holes,
Apply with a knife coater on a plate of Yonematsu with convex wood grain on the surface, let stand at room temperature for 24 hours to cure,
A pine board with a smooth surface was obtained. [Examples 2 and 3] The same procedure as in Example 1 was repeated except that calcium oxide was replaced with magnesium oxide and barium oxide, respectively. [Example 4] 150 parts of a polyether polyol (average molecular weight 1000, hydroxyl value 114 mg KOH / g) obtained by adding ethylene glycol to polypropylene glycol, 100 parts of dibutyl phthalate as a plasticizer, and 20 parts of calcium oxide as a filler. , 400 parts of calcium carbonate, 20 parts of ultrafine silica powder, and 2 parts of a curing accelerator (dibutyltin laurate) were added to prepare a main agent. 40 parts of polymeric MDI (isocyanate group content 31%) was added as a curing agent to give a repairing resin composition. At this time -NCO / -OH
The molar ratio is 1.3. Thereafter, the pine boards were repaired in the same manner as in Example 1. [Examples 5 and 6] The same procedure as in Example 4 was carried out except that magnesium oxide and barium oxide were used instead of calcium oxide. [Comparative Example 1] The same procedure as in Example 1 was carried out except that the filler was calcium carbonate. [Comparative Examples 2 and 3] The same procedure as in Example 1 was repeated except that the filler was calcium carbonate and the plasticizers were diethyl phthalate and dioctyl phthalate, respectively. Comparative Example 3 had a high viscosity and was slightly difficult to apply. The surface state of the obtained pine boards was visually observed. Further, the adhesiveness of the cured resin product at the bush hole portion was examined. The results are shown in Table 1.
Shown in.
【0014】[0014]
【表1】 [Table 1]
【0015】[0015]
【発明の効果】以上の実施例からも明らかなように、本
発明の木質材補修用樹脂組成物は、従来の欠点であった
「ふくれ」の発生がなく、密着性も良好であり、特に針
葉樹の補修に好適に使用される。As is apparent from the above examples, the resin composition for repairing wood materials according to the present invention does not cause "blister" which is a drawback of the prior art, and has good adhesiveness. It is suitable for repairing conifers.
Claims (1)
ト化合物、充填剤を必須成分とする木質材補修用樹脂組
成物であって、更に、可塑剤、及び水分を捕捉する充填
剤として酸化マグネシウム、酸化カルシウム、酸化バリ
ウムの少なくとも一種が配合されていることを特徴とす
る木質材補修用樹脂組成物。1. A resin composition for repairing wood materials, which contains an active hydrogen-containing compound, a polyisocyanate compound and a filler as essential components, and further comprises a plasticizer and magnesium oxide or calcium oxide as a filler for trapping water. A resin composition for repairing wood materials, comprising at least one kind of barium oxide.