CN108818816A - A kind of ceramics wood and manufacturing method based on closed NCO - Google Patents
A kind of ceramics wood and manufacturing method based on closed NCO Download PDFInfo
- Publication number
- CN108818816A CN108818816A CN201810375456.4A CN201810375456A CN108818816A CN 108818816 A CN108818816 A CN 108818816A CN 201810375456 A CN201810375456 A CN 201810375456A CN 108818816 A CN108818816 A CN 108818816A
- Authority
- CN
- China
- Prior art keywords
- timber
- wood
- performed polymer
- ceramics
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The ceramic wooden and manufacturing method based on closed NCO group that the invention discloses a kind of, ceramics wood includes timber, and the polyurethane with lumber fibre formation reticular structure is filled in the gap of timber.Manufacturing method is preparation enclosed type performed polymer, and water is then added and forms maceration extract, by timber pickling in maceration extract, heating.Utilize ceramics wood of the invention and the ceramics wood obtained by the manufacturing method, anti-corrosion and waterproof, mothproof, dimensionally stable, long service life as ceramics, performance is good, so that timber is not easy to deform, is mouldy, it is durable simultaneously, and the inner layer of ceramics wood is consistent with outer layer, and it is different with internal layer ceramics wood after will not being buffed off because of cladding material.
Description
Technical field
The present invention relates to ceramic wood and its manufacturing methods.Especially with arrive furniture, ornament materials, construction material, art
Ceramics wood on product.
Background technique
The application of timber is very extensive, such as furniture, ornament materials, construction material, the art work.For being used for a long time
Timber for, generally require and do anti-corrosion and waterproof processing, in carrying out above-mentioned treatment process, generally use anti-corrosion waterproof material
Timber is handled, but current anti-corrosion waterproof material is only on the surface of timber, it is difficult to it enters in the gap of timber, this
Sample, once the anti-corrosion waterproof material of wood surface is destroyed, then the preservation of timber against decay, waterproof performance decline, timber are easy to appear change
Shape, it is mouldy phenomena such as.The anticorrosive wood of market at present is handled using preservative, non-watertight, once preservative fails, is begun to
Burn into is mouldy, is not real anticorrosive wood.
Timber is a kind of organic material of spontaneous growth, is made of polymer substance and lower-molecular substance.It is thin to constitute timber
The main matter of cell wall is three kinds of high polymers, and three kinds of high polymers are respectively cellulose, hemicellulose and lignin, accounts for wood weight
97%-99%.
Cellulose is by many mono- grape pool bases of D by l, 4- β-glucoside linear natural polymer chemical combination made of being keyed
Object plays skeleton function in wood cell wall, typically constitutes from 40% of wood components or more, and 50% or so is accounted in wood cell.
Its chemical property and supramolecular structure have a major impact wood property and processing performance.
Hemicellulose is cementation to be played, mainly by hexose, sweet with the close-connected substance of cellulose in wood cell wall
Reveal five kinds of neutral monosaccharides compositions such as sugar, the gala pool, pentose and Arabic a kind of farm tools, strand is short more than cellulose, and has one
Fixed branch degree.
The aromatic compound that lignin is made of phenylpropane units is deposited on cell in cell formation process
Last a kind of high polymer in wall, they run through mutually cellulose, play a part of to strengthen cell wall.There are three types of basic for lignin
Structure, i.e. guaiacyl structure, lilac based structures and p-hydroxyphenyl structure mainly include alcoholic extract hydroxyl group, phenolic hydroxyl group, carbonyl, carboxylic
A variety of chemical reactions can occur for base and methyl etc..Isocyanate resin fills timber gap primarily from isocyanate group
Reacting between active hydrogen a large amount of in timber is formed by chemical bond, such as the hydroxyl in cellulose, hemicellulose rope, in lignin
Phenolic hydroxyl group, further include a large amount of water contained in timber, they can react with isocyanates, this is isocyanates
Base and substrate active hydrogen reaction form chemical bonds;Secondly, the big polar group of isocyanate resin and the oxygen-containing, nitrogen of substrate etc.
The asking for product for forming Hydrogenbond, isocyanate group itself or isocyanate group and isocyanate group and timber can produce self-crosslinking
Reaction.But in practical applications, the activity of NCO group is very big, directly penetrates into polyisocyanates in timber, NCO base
Group's chance quickly reacts with water, active hydrogen, when to isocyanates not completely into in timber, just has occurred that
Solidification, in this way, polyisocyanates is just difficult to completely penetrate to be filled up completely the gap in timber in timber, in this way, current
Polyisocyanates can only be also confined in the field of adhesive.
Summary of the invention
The ceramic wooden and manufacturing method based on closed NCO that the object of the present invention is to provide a kind of, utilizes pottery of the invention
Porcelain wood and the ceramics wood obtained by the manufacturing method, anti-corrosion and waterproof, mothproof, dimensionally stable, service life as ceramics
Long, performance is good, so that timber is not easy to deform, is mouldy, while durable, and the inner layer of ceramics wood is consistent with outer layer, Bu Huiyin
Cladding material is different with internal layer ceramics wood after being buffed off.
In order to achieve the above objectives, a kind of ceramics wood based on closed NCO group, including timber, in the gap of timber
Filled with the polyurethane for forming reticular structure with lumber fibre, the polyurethane is to be reacted by enclosed type performed polymer with water
High molecular polymer, enclosed type performed polymer is reacted by polyisocyanates and polyether polyol or polyester polyol forms performed polymer
Then blocking agent NCO group is used;The temperature for forming enclosed type performed polymer is 60-100 DEG C, NCO base in enclosed type performed polymer
The content of group accounts for the 5-20% of enclosed type performed polymer, and enclosed type performed polymer molecular weight is 1000-5000, and enclosed type performed polymer contains admittedly
Measure 80% solvent of >:Water, the above percentage are weight percentage.
The above-mentioned manufacturing method based on closed NCO ceramics wood includes the following steps:
(1) performed polymer is prepared, polyisocyanates and polyether polyol or polyester polyol are reacted;
(2) sealer is added in performed polymer, forms enclosed type performed polymer with blocking agent NCO group, reaction equation is:
(3) water is added in enclosed type performed polymer and forms maceration extract;
(3) by timber pickling in maceration extract, maceration extract entered wood by 12-24 hours under the pressure of 1-10MPa
In material;
(4) timber by dipping is taken out, is then placed in heating kettle, heating 10- is carried out to the timber by dipping
20 hours, heating temperature be 100-180 DEG C, heating use segmentally heating, wherein 100-120 DEG C heating 4-8 hours, 120-150
DEG C heating 4-8 hours, 150-180 DEG C heating 2-4 hours, during heating, closed NCO group is unsealed, and is occurred simultaneously
Chemical reaction forms lumber fibre in timber and constitutes the polyurethane of reticular structure and ceramics wood is made;The chemical reaction of generation
Mainly have:
Further, one of polyisocyanates TDI, MDI, HDI, IPDI or several.
Further, sealer is one of imidazoles, gaultherolin, methyl p-hydroxybenzoate.
It further, include reacting the portion formed with hydroxyl in ceramic wood and phenolic hydroxyl group by polyisocyanates in ceramics wood
Point.
Further, it is taken away by moisture for partially enclosed dose.
In the present invention, based on the characteristic in timber with hydroxyl, phenolic hydroxyl group and a large amount of water, and in polyisocyanates
The activity of NCO group has unusual height, for this purpose, the present invention first closes NCO group, enclosed type performed polymer and water is allowed to press
Completely into after in the gap to timber in the time of power and control, NCO group is unsealed by heating, in the mistake of deblocking
Cheng Zhong, NCO group, which react with water, hydroxyl, phenolic hydroxyl group, is formed by curing polyurethane, in the curing process, polyurethane and timber
Fiber forms reticular structure, and in deblocking and solidification process, polyisocyanates fills timber gap primarily from isocyanates
Reacting between base and active hydrogen a large amount of in timber is formed by chemical bond, such as the hydroxyl in cellulose, hemicellulose rope, lignin
In phenolic hydroxyl group, further include a large amount of water contained in timber, they can react with isocyanates, this is isocyanic acid
Ester group and substrate active hydrogen reaction form chemical bonds;Secondly, the big polar group of isocyanate resin and the oxygen-containing, nitrogen of substrate etc.
Group, which forms asking for the product of Hydrogenbond, isocyanate group itself or isocyanate group and isocyanate group and timber, can produce itself friendship
Connection reaction.In this way, being not only filled up completely the gap in timber, but also the inside and outside of timber is allowed to be consistent, makes timber picture ceramic
The same anti-corrosion and waterproof, mothproof, dimensionally stable, long service life, performance is good, so that timber is not easy to deform, is mouldy, while resistance to
With.During heating, it unlocks partially enclosed dose come to enter in wood-fibred, partially enclosed dose high because of temperature of reason quilt
Moisture is taken away, and the purpose using segmentally heating is that small molecule and moisture is allowed all to volatilize, and achievees the purpose that environmental protection.In the present invention
In, by polyisocyanates and polyether polyol or polyester polyol before closing NCO group, in this way, enclosed type pre-polymerization can be improved
The penetrating power and mobility of body allow enclosed type performed polymer more, faster to enter in timber.
Specific embodiment
The present invention will be described in further detail With reference to embodiment.
Ceramics wood based on closed NCO group includes timber, is filled in the gap of timber and is formed with lumber fibre
The polyurethane of reticular structure, the polyurethane are high molecular polymers made of being reacted as enclosed type performed polymer with water, closing
Type performed polymer is reacted by polyisocyanates and polyether polyol or polyester polyol to be formed performed polymer and then uses blocking agent NCO
Group;The temperature for forming enclosed type performed polymer is 60-100 DEG C, and the content of NCO group accounts for enclosed type pre-polymerization in enclosed type performed polymer
The 5-20% of body, enclosed type performed polymer molecular weight are 1000-5000,80% solvent of enclosed type performed polymer solid content >:Water, it is above
Percentage is weight percentage.Polyisocyanates is one of TDI, MDI, HDI, IPDI or several.Sealer be imidazoles,
One of gaultherolin, methyl p-hydroxybenzoate.
Embodiment 1.
Manufacturing method based on closed NCO ceramics wood includes the following steps:
(1) performed polymer is prepared, the polyether polyol of 30% polyisocyanates and 10% is reacted.
(2) 10% sealer is added in performed polymer, forms enclosed type performed polymer with blocking agent NCO group, instead
Ying Shiwei:
(3) water that 50% is added in enclosed type performed polymer forms maceration extract.
(3) by timber pickling in maceration extract, maceration extract entered wood by 12-24 hours under the pressure of 1-10MPa
In material.
(4) timber by dipping is taken out, is then placed in heating kettle, heating 10- is carried out to the timber by dipping
20 hours, heating temperature be 100-180 DEG C, heating use segmentally heating, wherein 100-120 DEG C heating 4-8 hours, 120-150
DEG C heating 4-8 hours, 150-180 DEG C heating 2-4 hours, during heating, closed NCO group is unsealed, and is occurred simultaneously
Chemical reaction forms lumber fibre in timber and constitutes the polyurethane of reticular structure and ceramics wood is made;The chemical reaction of generation
Mainly have:
Above percentage is weight percentage.
Embodiment 2.
Manufacturing method based on closed NCO ceramics wood includes the following steps:
(1) performed polymer is prepared, the polyester polyol of 40% polyisocyanates and 20% is reacted.
(2) 5% sealer is added in performed polymer, forms enclosed type performed polymer, reaction with blocking agent NCO group
Formula is:
(3) water that 35% is added in enclosed type performed polymer forms maceration extract.
(3) by timber pickling in maceration extract, maceration extract entered wood by 12-24 hours under the pressure of 1-10MPa
In material.
(4) timber by dipping is taken out, is then placed in heating kettle, heating 10- is carried out to the timber by dipping
20 hours, heating temperature be 100-180 DEG C, heating use segmentally heating, wherein 100-120 DEG C heating 4-8 hours, 120-150
DEG C heating 4-8 hours, 150-180 DEG C heating 2-4 hours, during heating, closed NCO group is unsealed, and is occurred simultaneously
Chemical reaction forms lumber fibre in timber and constitutes the polyurethane of reticular structure and ceramics wood is made;The chemical reaction of generation
Mainly have:
Above percentage is weight percentage.
In the present invention, based on the characteristic in timber with hydroxyl, phenolic hydroxyl group and a large amount of water, and in polyisocyanates
The activity of NCO group has unusual height, for this purpose, the present invention first closes NCO group, enclosed type performed polymer and water is allowed to press
Completely into after in the gap to timber in the time of power and control, NCO group is unsealed by heating, in the mistake of deblocking
Cheng Zhong, NCO group, which react with water, hydroxyl, phenolic hydroxyl group, is formed by curing polyurethane, in the curing process, polyurethane and timber
Fiber forms reticular structure, and in deblocking and solidification process, polyisocyanates fills timber gap primarily from isocyanates
Reacting between base and active hydrogen a large amount of in timber is formed by chemical bond, such as the hydroxyl in cellulose, hemicellulose rope, lignin
In phenolic hydroxyl group, further include a large amount of water contained in timber, they can react with isocyanates, this is isocyanic acid
Ester group and substrate active hydrogen reaction form chemical bonds;Secondly, the big polar group of isocyanate resin and the oxygen-containing, nitrogen of substrate etc.
Group, which forms asking for the product of Hydrogenbond, isocyanate group itself or isocyanate group and isocyanate group and timber, can produce itself friendship
Connection reaction.In this way, being not only filled up completely the gap in timber, but also the inside and outside of timber is allowed to be consistent, makes timber picture ceramic
The same anti-corrosion and waterproof, mothproof, dimensionally stable, long service life, performance is good, so that timber is not easy to deform, is mouldy, while resistance to
With.During heating, it unlocks partially enclosed dose come to enter in wood-fibred, partially enclosed dose high because of temperature of reason quilt
Moisture is taken away, and the purpose using segmentally heating is that small molecule and moisture is allowed all to volatilize, and achievees the purpose that environmental protection.In the present invention
In, by polyisocyanates and polyether polyol or polyester polyol before closing NCO group, in this way, enclosed type pre-polymerization can be improved
The penetrating power and mobility of body allow enclosed type performed polymer more, faster to enter in timber.
Claims (10)
1. a kind of ceramics wood based on closed NCO group, including timber, it is characterised in that:It is filled in the gap of timber
The polyurethane of reticular structure is formed with lumber fibre, the polyurethane is high score made of being reacted as enclosed type performed polymer with water
Sub- polymer, enclosed type performed polymer is reacted by polyisocyanates and polyether polyol or polyester polyol forms performed polymer then use
Blocking agent NCO group;The temperature for forming enclosed type performed polymer is 60-100 DEG C, and NCO group contains in enclosed type performed polymer
Amount accounts for the 5-20% of enclosed type performed polymer, and enclosed type performed polymer molecular weight is 1000-5000, enclosed type performed polymer solid content >
80% solvent:Water, the above percentage are weight percentage.
2. the ceramics wood according to claim 1 based on closed NCO group, it is characterised in that:Polyisocyanates is
One of TDI, MDI, HDI, IPDI are several.
3. the ceramics wood according to claim 1 based on closed NCO group, it is characterised in that:Sealer is imidazoles, water
One of poplar acid methyl esters, methyl p-hydroxybenzoate.
4. the ceramics wood according to claim 1 based on closed NCO group, it is characterised in that:Include in ceramic wood by
Polyisocyanates reacts the part to be formed with hydroxyl in ceramic wood and phenolic hydroxyl group.
5. the ceramics wood according to claim 1 based on closed NCO group, it is characterised in that:Partially enclosed dose by water
Divide and takes away.
6. a kind of manufacturing method based on closed NCO ceramics wood, it is characterised in that include the following steps:
(1) performed polymer is prepared, polyisocyanates and polyether polyol or polyester polyol are reacted;
(2) sealer is added in performed polymer, forms enclosed type performed polymer with blocking agent NCO group, reaction equation is:
(3) water is added in enclosed type performed polymer and forms maceration extract;
(3) by timber pickling in maceration extract, maceration extract was entered in timber under the pressure of 1-10MPa by 12-24 hours;
(4) timber by dipping is taken out, is then placed in heating kettle, it is small to carry out heating 10-20 to the timber by dipping
When, heating temperature be 100-180 DEG C, heating use segmentally heating, wherein 100-120 DEG C heating 4-8 hours, 120-150 DEG C add
It is 4-8 hours hot, 150-180 DEG C heating 2-4 hours, during heating, closed NCO group is unsealed, while chemistry occurs
Reaction forms lumber fibre in timber and constitutes the polyurethane of reticular structure and ceramics wood is made;The chemical reaction of generation is main
Have:
7. the manufacturing method according to claim 6 based on closed NCO ceramics wood, it is characterised in that:Polyisocyanates
For one of TDI, MDI, HDI, IPDI or several.
8. the manufacturing method according to claim 6 based on closed NCO ceramics wood, it is characterised in that:Sealer is miaow
One of azoles, gaultherolin, methyl p-hydroxybenzoate.
9. the manufacturing method according to claim 6 based on closed NCO ceramics wood, it is characterised in that:It is wrapped in ceramic wood
It includes and reacts the part formed with hydroxyl in ceramic wood and phenolic hydroxyl group by polyisocyanates.
10. the manufacturing method according to claim 6 based on closed NCO ceramics wood, it is characterised in that:Partially enclosed dose
It is taken away by moisture.