JPH0431442A - Surface protective film of liquid crystal display panel - Google Patents
Surface protective film of liquid crystal display panelInfo
- Publication number
- JPH0431442A JPH0431442A JP2136382A JP13638290A JPH0431442A JP H0431442 A JPH0431442 A JP H0431442A JP 2136382 A JP2136382 A JP 2136382A JP 13638290 A JP13638290 A JP 13638290A JP H0431442 A JPH0431442 A JP H0431442A
- Authority
- JP
- Japan
- Prior art keywords
- film
- liquid crystal
- polarizing plate
- protective film
- display panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、液晶表示パネルの偏光板の上から貼着するこ
とによって該偏光板表面の保護を図るための保護フィル
ムに関するものである。DETAILED DESCRIPTION OF THE INVENTION Field of Industrial Application The present invention relates to a protective film for protecting the surface of a polarizing plate of a liquid crystal display panel by pasting it over the polarizing plate.
(なお本明細書においては、フィルム、シート、板の用
語を用いているが、これらの間に特別の区別は存在しな
い。)
従来の技術
周知のように液晶セルは、2枚の基板の間に液晶を封入
した構成を有する。液晶表示パネルは、この液晶セルの
少なくとも片面(通常は両面)に偏光板を積層すること
により作製される。液晶セルに対する偏光板の積層は、
通常、粘着剤層付きの偏光板を液晶セルに圧着すること
によりなされる。(Although the terms film, sheet, and plate are used in this specification, there is no special distinction between them.) As is well known in the art, a liquid crystal cell It has a structure in which liquid crystal is sealed inside. A liquid crystal display panel is produced by laminating a polarizing plate on at least one side (usually both sides) of this liquid crystal cell. The stacking of polarizing plates on liquid crystal cells is
Usually, this is done by pressing a polarizing plate with an adhesive layer onto a liquid crystal cell.
なお、液晶セル基板兼用の偏光板も提案されている。Note that a polarizing plate that can also be used as a liquid crystal cell substrate has also been proposed.
いずれにせよ液晶表示パネルの最外層は偏光板で形成さ
れているが、この偏光板としては、偏光素膜の両側に保
護板としてのセルローストリアセテートフィルムを積層
したものが汎用されている。In any case, the outermost layer of the liquid crystal display panel is formed of a polarizing plate, and a commonly used polarizing plate is one in which cellulose triacetate films as protective plates are laminated on both sides of a polarizing element film.
ところが、このセルローストリアセテートフィルムは耐
スクラッチ性や耐水性が劣るので、液晶セルに偏光板を
設置した後は直ちにその上から保護フィルムを被覆し、
爾後の工程や流通過程における偏光板の損傷を防ぐよう
にしている。保護フィルムの設置は塵の付着を防ぐ意味
もある。そして実際に液晶表示パネルを使用するときに
はじめてこの保護フィルムを剥離除去する。However, this cellulose triacetate film has poor scratch resistance and water resistance, so after installing the polarizing plate on the liquid crystal cell, immediately cover it with a protective film.
This is to prevent damage to the polarizing plate during subsequent processes and distribution processes. Installing a protective film also helps prevent dust from adhering. This protective film is peeled off and removed only when the liquid crystal display panel is actually used.
上記保護フィルムとしては、ポリエチレンフィルムやエ
チレン−酢酸ビニル共重合体フィルムの如き熱圧着タイ
プのもの、弱粘着剤層付きポリエステルフィルムの如き
感圧接着タイプのものが使われている。As the above-mentioned protective film, a thermocompression type film such as a polyethylene film or an ethylene-vinyl acetate copolymer film, and a pressure sensitive adhesive type film such as a polyester film with a weak adhesive layer are used.
発明が解決しようとする課題
作製した液晶表示パネルは、表示能力、色相、コントラ
ストなどの評価のために、適時に検査を行うのが通例で
ある。ところが上述の従来の保護フィルムは、このよう
な光学的評価を伴なう検査には支障となるので、検査に
先立ち一旦この保護フィルムを剥離除去し、検査終了後
にもう一度新しい保護フィルムを貼り直すことが行われ
ろ。PROBLEMS TO BE SOLVED BY THE INVENTION It is customary for manufactured liquid crystal display panels to be inspected at appropriate times to evaluate display ability, hue, contrast, and the like. However, the conventional protective film mentioned above is a hindrance to inspections that involve such optical evaluation, so it is necessary to peel off the protective film before the inspection and reapply a new protective film after the inspection. be done.
貼り直しを新しい保護フィルムで行うのは、保護フィル
ムは再貼着性を有しないが、あるいは再貼着可能でも再
貼着すると美麗さが損なわれるからである。The reason why the protective film is reapplied with a new protective film is because the protective film does not have reattachability, or even if it can be reattached, the beauty will be lost if it is reattached.
上述の検査のための保護フィルムの剥離および再貼着は
、工程的に2工程を要するものであり、極限までのコス
ト低下が追求されるこの分野においては大きな支障とな
っているはずであるが、保護フィルムはもともとそのよ
うなものであるとの認識から、その改善については特に
対策はとられていないのが現状である。Peeling off and reapplying the protective film for the above-mentioned inspection requires two steps, which must be a major hindrance in this field where cost reduction is pursued to the utmost. Since it is recognized that protective films are originally like this, no particular measures have been taken at present to improve them.
本発明は、このような状況に鑑み、検査時に剥離を要し
ない表面保護フィルムを提供することを目的になされた
ものである。In view of this situation, the present invention was made for the purpose of providing a surface protection film that does not require peeling during inspection.
課題を解決するための手段
本発明の液晶表示パネルの表面保護フィルムは、液晶表
示パネルの偏光板(2)の上がら貼着することによって
該偏光板(2)表面の保護を図るだめの保護フィルムf
ilであって、該保護フィルム(11が、■ガラス転移
点50’C以下の樹脂または可塑化樹脂からなり、偏光
板(2)に対し貼着性を有すること、■偏光板(2)に
対し貼着する側の面の表面平滑度が0.1μm以下であ
ること、■レターデーション値が30nm以下、可視光
線透過率が75%以上であること、の条件を全て満足す
る光等方性フィルムからなることを特徴とするものであ
る。Means for Solving the Problems The surface protective film for a liquid crystal display panel of the present invention is a protective film that is attached to the top of a polarizing plate (2) of a liquid crystal display panel to protect the surface of the polarizing plate (2). f
il, the protective film (11 is made of a resin or plasticized resin having a glass transition point of 50'C or lower and has adhesive properties to the polarizing plate (2), and ■ the polarizing plate (2) On the other hand, optical isotropy that satisfies all the following conditions: surface smoothness of the side to be adhered is 0.1 μm or less, ■ retardation value is 30 nm or less, and visible light transmittance is 75% or more. It is characterized by being made of film.
以下本発明の詳細な説明する。The present invention will be explained in detail below.
良邑l丞匹ユJ
液晶表示パネルは、後述の第1図のように、液晶セル(
3)の少なくとも片面(通常は両面)に偏光板(2)を
積層することにより作製される。なお、偏光板(2)で
液晶セル基板を兼ねることもできる。As shown in Figure 1 below, a liquid crystal display panel consists of liquid crystal cells (
It is produced by laminating a polarizing plate (2) on at least one side (usually both sides) of 3). Note that the polarizing plate (2) can also serve as a liquid crystal cell substrate.
置屋t’4はL
このうち液晶セル(3)は、ITOなどの透明電極(3
2)付きの2枚の基板(31)をスペーサ(33)を介
して対向配置し、その間隙に液晶(34)を封入した構
成を有する。他に配向膜等も設けるが、詳細は省略する
。The room t'4 is L. Among these, the liquid crystal cell (3) has a transparent electrode such as ITO (3
2) are arranged facing each other with a spacer (33) in between, and a liquid crystal (34) is sealed in the gap between them. Although an alignment film and the like are also provided, the details are omitted.
偏ノC阪工わ−
偏光板(2)は、ビニルアルコール系重合体/ヨウ素系
、ビニルアルコール系重合体/2色性染料系、ビニルア
ルコール系重合体/ポリエン系、ポリハロゲン化ビニル
/ポリエン系、ポリアクリロニトリル/ポリエン系など
の偏光素膜(21)の両側に、セルローストリアセテー
トフィルム、セルロースブチレートアセテートフィルム
などの保護板(22)を積層したものからなる。保護板
(22)としては、セルローストリアセテートフィルム
やセルロースブチレートアセテートフィルムのほか、ポ
リカーボネートフィルム、ポリメタクリル酸メチルフィ
ルム、ポリ塩化ビニルフィルム、エチレン−ビニルアル
コール共重合体フィルム、ポリアミドフィルム、ポリス
チレンフィルムなども使用しつるとされているが、事実
上はセルローストリアセテートフィルムやセルロースブ
チレートアセテートフィルム、殊にセルローストリアセ
テートフィルムに限られる。Polarizing plate (2) is made of vinyl alcohol polymer/iodine, vinyl alcohol polymer/dichroic dye, vinyl alcohol polymer/polyene, polyvinyl halide/polyene. It consists of a protective plate (22) such as a cellulose triacetate film or a cellulose butyrate acetate film laminated on both sides of a polarizing element film (21) made of a polyacrylonitrile/polyene type or the like. As the protective plate (22), in addition to cellulose triacetate film and cellulose butyrate acetate film, polycarbonate film, polymethyl methacrylate film, polyvinyl chloride film, ethylene-vinyl alcohol copolymer film, polyamide film, polystyrene film, etc. Although it is said to be used, it is actually limited to cellulose triacetate films and cellulose butyrate acetate films, particularly cellulose triacetate films.
7/l、Al上
この偏光板(2)の上から保護フィルム(1)が貼着さ
れるが、本発明においては、この保護フィルム(1)と
して。7/l, on Al A protective film (1) is attached from above this polarizing plate (2), and in the present invention, this protective film (1) is used.
■ ガラス転移点50℃以下の樹脂または可塑化樹脂か
らなり、偏光板(2)に対し貼着性を有すること、
■ 偏光板(2)に対し貼着する側の面の表面平滑度が
0.1μm以下であること、
■ レターデーション値が30nm以下、可視光線透過
率が75%以上であること、
の条件を全て満足する光等方性フィルムを用6sる。■ It must be made of a resin or plasticized resin with a glass transition point of 50°C or less, and it must have adhesive properties to the polarizing plate (2). ■ The surface smoothness of the side to be adhered to the polarizing plate (2) must be 0. Use an optically isotropic film that satisfies all of the following conditions: (1) Retardation value is 30 nm or less and visible light transmittance is 75% or more.
■の条件を満足する樹脂フィルムとしては、■ 飽和ポ
リエステル樹脂、ポリウレタン系樹脂、ポリブタジェン
ポリオール、ポリオレフィンポリオール、官能基含有ア
クリル共重合体などの官能基を有する樹脂に硬化剤を配
合して製膜し、部分架橋または不完全架橋させたフィル
ム、■ 軟質ポリ塩化ビニル(ポリ塩化ビニルに可塑剤
をたとえば20重量%以上配合したもの)、ポリウレタ
ン系樹脂と塩化ビニル−酢酸ビニル共重合体とのブレン
ド物などの可塑化樹脂を製膜して得られたフィルム、
■ ブチルゴム、ウレタンゴム、ブタジェン系ゴム(ポ
リブタジェンゴム、スチレン−ブタジェンゴム、スチレ
ン−ブタジェン−スチレンブロック共重合体等)、スチ
レン−イソプレン−スチレンゴムなどの合成ゴムを製膜
して得られたフィルム、
■ 低分子量ポリエチレン、アククチツクポリプロピレ
ン、塩素化ポリプロピレンなとのポリオレフィン系樹脂
を製膜して得られたフィルム、■ エチレン−酢酸ビニ
ル共重合体、エチレン−アクリル酸共重合体、エチレン
−アクリル酸エステル共重合体などのエチレン系共重合
体を製膜して得られたフィルム、
■ アクリル酸エステル系重合体を製膜して得られたフ
ィルム、
■ 飽和ポリエステル系樹脂を製膜して得られたフィル
ム、
などが例示され、これらの中からガラス転移点50℃以
下でかつ偏光板(2)に対し貼着性を有するものを選択
する。A resin film that satisfies the conditions of (2) Soft polyvinyl chloride (polyvinyl chloride mixed with, for example, 20% by weight or more of a plasticizer), polyurethane resin and vinyl chloride-vinyl acetate copolymer; Films obtained by forming plasticized resins such as blends, ■ Butyl rubber, urethane rubber, butadiene rubber (polybutadiene rubber, styrene-butadiene rubber, styrene-butadiene-styrene block copolymer, etc.), styrene- Films obtained by forming films from synthetic rubber such as isoprene-styrene rubber, ■ Films obtained by forming films from polyolefin resins such as low molecular weight polyethylene, acid polypropylene, and chlorinated polypropylene, ■ Ethylene- Films obtained by forming films of ethylene copolymers such as vinyl acetate copolymers, ethylene-acrylic acid copolymers, and ethylene-acrylic ester copolymers; (1) A film obtained by forming a film from a saturated polyester resin; choose something.
上記■の条件を満たすフィルムであっても、その表面状
態によっては偏光板(2)に対する貼着性が不足するこ
とがある。そこで、少なくとも偏光板(2)に対し貼着
する側の面の表面平滑度が0.1μm以下であることが
必要である。ここで表面平滑度とは、JIS B−06
01,1970に規定する平滑度であると定義する。Even if the film satisfies the above condition (2), the adhesion to the polarizing plate (2) may be insufficient depending on its surface condition. Therefore, it is necessary that the surface smoothness of at least the side to be adhered to the polarizing plate (2) is 0.1 μm or less. Here, surface smoothness is defined by JIS B-06
01, 1970.
また、保護フィルム+1)は光等方性を有することが必
要であるので、レターデーション値が30no+以下(
殊に20nm以下)、可視光線透過率が75%以上(殊
に80%以上)であることが要求される。このような光
等方性を有するフィルムは、流延法により製膜すること
により得られるが5レターデーシヨン値および可視光線
透過率が上記の条件を満足していれば、押出法など他の
成形法を採用することもできる。In addition, since the protective film +1) needs to have optical isotropy, the retardation value is 30no+ or less (
In particular, it is required that the visible light transmittance is 75% or more (especially 80% or more). Films with such optical isotropy can be obtained by casting, but if the 5 retardation value and visible light transmittance satisfy the above conditions, other methods such as extrusion can be used. A molding method can also be adopted.
上記条件を全て満足する光等方性フィルムの厚さは、通
常数Jf IIIないし200μm程度に設定するが、
必ずしもこの範囲に限定されない。The thickness of the optically isotropic film that satisfies all of the above conditions is usually set to about several Jf III to 200 μm, but
It is not necessarily limited to this range.
上述の光等方性フィルムからなる本発明の保護フィルム
(1)は、リワーク(rework)性が求められる場
合には可剥性を有するものを選択し、永久接着が求めら
れる場合には強い貼着力が得られるものを選択する。The protective film (1) of the present invention made of the above-mentioned optically isotropic film is selected to have peelability when reworkability is required, and a strong adhesive is selected when permanent adhesion is required. Choose one that will give you strength.
作 用
本発明の保護フィルム(11を使用するにあたっては、
この保護フィルム(1)を液晶表示パネルの偏光板(2
)の表面に圧着または熱圧着する。Function: When using the protective film (11) of the present invention,
Apply this protective film (1) to the polarizing plate (2) of the liquid crystal display panel.
) to be crimped or thermocompressed onto the surface.
表示能力、色相、コントラストなどの評価のための試験
を行うにあたっては、本発明においては液晶表示パネル
の偏光板(2)に貼着した保護フィルム(1)を剥離す
る必要はなく、保護フィルム(1)を貼着した状態のま
まこれらの試験を行えばよい。In conducting tests for evaluating display performance, hue, contrast, etc., in the present invention, it is not necessary to peel off the protective film (1) attached to the polarizing plate (2) of the liquid crystal display panel; These tests may be performed with 1) still attached.
保護フィルム(1)にリワーク(rework)性が求
められる場合には、液晶表示パネルを実際に使用に供す
るに先立ち、保護フィルム(11を剥離除去する。一方
すワーク性が要求されないときには、保護フィルム(1
)を永久接着したまま実際の使用に供する。If reworkability is required for the protective film (1), the protective film (11) is peeled off and removed before the liquid crystal display panel is actually used.On the other hand, when reworkability is not required, the protective film (11) is removed. (1
) is used for actual use with permanent adhesive.
実 施 例 次に実施例をあげて本発明をさらに説明する。Example Next, the present invention will be further explained with reference to Examples.
実施例1
第1図は本発明の表面保護フィルム(11を貼着した液
晶表示パネルの一例を示した断面図である。Example 1 FIG. 1 is a sectional view showing an example of a liquid crystal display panel to which a surface protection film (11) of the present invention is attached.
−) ルム1
飽和ポリエステル樹脂(東洋紡績株式会社のバイロン3
00、ガラス転移点6℃)をトルエン−メチルエチルケ
トン混合溶媒に溶解して25重量%濃度の溶液を調製し
、ついで離型層付き基材フィルム上に流延して製膜する
ことにより、レターデーション値はぼOnm、可視光線
透過率85%、厚さ50uI11の飽和ポリエステル樹
脂フィルムを得た。製膜時の下面側の表面平滑度は0.
031μmであった。-) Lum 1 Saturated polyester resin (Toyobo Co., Ltd.'s Byron 3
00 (glass transition point: 6°C) in a toluene-methyl ethyl ketone mixed solvent to prepare a solution with a concentration of 25% by weight, and then cast onto a base film with a release layer to form a film. A saturated polyester resin film having a value of approximately Onm, a visible light transmittance of 85%, and a thickness of 50 μl was obtained. The surface smoothness of the lower surface during film formation was 0.
It was 0.031 μm.
九五i玉匹ユ五
(3)は液晶セルであり、透明電極(32)付きの2枚
の基板(31)をスペーサ(33)を介して対向配置し
、その間隙に液晶(34)を封入した構成を有する。Nine-Five i Tamada Yu-go (3) is a liquid crystal cell, in which two substrates (31) with transparent electrodes (32) are arranged facing each other with a spacer (33) interposed therebetween, and a liquid crystal (34) is placed in the gap between them. It has an enclosed configuration.
(2)は偏光板であり、たとえば、ポリビニルアルコー
ル/ヨウ素系の厚さ35μ燭の偏光素111 (21)
の両側に、セルローストリアセテートフィルムからなる
厚さ50μmの保護板(22)を感圧性接着剤を用いて
積層したものからなる。 (231はその感圧性接着剤
層である。(2) is a polarizing plate, for example, a 35μ thick polarizing element 111 (21) made of polyvinyl alcohol/iodine.
50 μm thick protective plates (22) made of cellulose triacetate film are laminated on both sides of the plate using a pressure-sensitive adhesive. (231 is the pressure sensitive adhesive layer.
(1)は先に述べた表面保護フィルムであり、偏光板(
2)/液晶セル(3)/偏光板(2)の構成を有する液
晶表示パネルの偏光板(2)上に熱圧着により貼着され
ている。(1) is the surface protection film mentioned earlier, and the polarizing plate (
2)/liquid crystal cell (3)/polarizing plate (2) by thermocompression bonding onto the polarizing plate (2) of the liquid crystal display panel.
液晶表示パネルの偏光板(2)は表面保護フィルム(1
)で覆われているので耐損傷性、耐水性、防塵性が良好
であり、また表面保護フィルム(1)は光等方性を有す
るので、表示能力、色相、コントラストなどの光学的性
能の評価は、この表面保護フィルム(1)を剥離するこ
となく行うことができる。The polarizing plate (2) of the liquid crystal display panel is covered with a surface protection film (1).
), it has good damage resistance, water resistance, and dust resistance, and since the surface protection film (1) has optical isotropy, it is suitable for evaluation of optical performance such as display ability, hue, and contrast. can be carried out without peeling off this surface protection film (1).
この表面保護フィルム(1)は可剥性を有するので、液
晶表示パネルを実際に使用するときにはこれを剥離除去
することができる。ただし、貼着したままにしておいて
も差支えない。Since this surface protection film (1) has peelability, it can be peeled off and removed when the liquid crystal display panel is actually used. However, you can leave it attached.
実施例2
ブチルアクリレート/エチルアクリレート/アクリル酸
の共重合割合が重量比で4/4/2のアクリル共重合体
と、該共重合体のアクリル酸成分に対し当量のポリイソ
シアネート(トリレンジイソシアネート−トリメチロー
ルプロパンアダクト体)とを、トルエン−メチルエチル
ケトン混合溶媒に溶解して30重量%濃度の溶液を調製
し、ついで離型層付きポリエステルフィルム上に流延し
て製膜することにより、ガラス転移点−30℃、レター
デーション値はぼOnm、可視光線透過率90%、厚さ
60μIのアクリル共重合体フィルムを得た。製膜時の
下面側の表面平滑度は0.022μmであった、
この表面保護フィルム(1)は可剥性を有するので、液
晶表示パネルを実際に使用するときには、これを容易に
剥離除去することができる。Example 2 An acrylic copolymer with a copolymerization ratio of butyl acrylate/ethyl acrylate/acrylic acid of 4/4/2 by weight, and an equivalent amount of polyisocyanate (tolylene diisocyanate) to the acrylic acid component of the copolymer. trimethylolpropane adduct) in a mixed solvent of toluene and methyl ethyl ketone to prepare a solution with a concentration of 30% by weight, and then cast it on a polyester film with a release layer to form a film. An acrylic copolymer film having a retardation value of about Onm, a visible light transmittance of 90%, and a thickness of 60 μI was obtained at -30°C. The surface smoothness of the lower surface at the time of film formation was 0.022 μm. Since this surface protection film (1) has peelability, it can be easily peeled off and removed when the liquid crystal display panel is actually used. be able to.
実施例3
重合度600のポリ塩化ビニルとジオクチルフタレート
(可塑剤)との重量比で100 : 50の組成物をテ
トラヒドロフラン−ジオキサン混合溶媒に溶解した後、
流延製膜することにより、ガラス転移点−15℃、レタ
ーデーション値2nm、可視光線透過率89%、厚さ5
011mの軟質ポリ塩化ビニルフィルムを得た。製膜時
の下面側の表面平滑度は0.014μmであった。Example 3 After dissolving a composition of polyvinyl chloride with a degree of polymerization of 600 and dioctyl phthalate (plasticizer) in a weight ratio of 100:50 in a tetrahydrofuran-dioxane mixed solvent,
By casting the film, the glass transition point is -15°C, the retardation value is 2 nm, the visible light transmittance is 89%, and the thickness is 5.
A flexible polyvinyl chloride film of 0.011 m was obtained. The surface smoothness of the lower surface during film formation was 0.014 μm.
この表面保護フィルムfl)は可剥性を有するので、液
晶表示パネルを実際に使用するときには、これを容易に
剥離除去することができる。Since this surface protection film fl) has peelability, it can be easily peeled off and removed when the liquid crystal display panel is actually used.
発明の効果
本発明の表面保護フィルムは、液晶表示パネルの表示能
力、色相、コントラストなどの光学的評価を行う際に保
護フィルムの剥離を必要としないので、従来におけるよ
うな検査時の保護フィルムの剥離操作および再貼着操作
は一切省略できる。Effects of the Invention The surface protective film of the present invention does not require peeling off the protective film when optically evaluating the display ability, hue, contrast, etc. of a liquid crystal display panel. Peeling and reattachment operations can be completely omitted.
従って工程が大幅に簡略化され、製造コストの低減が達
成できる。Therefore, the process is greatly simplified and manufacturing costs can be reduced.
また本発明においては、表面保護フィルム(1)の貼着
により耐損傷性、耐水性、防塵性が得られ、所期の表面
保護効果が奏される。Further, in the present invention, damage resistance, water resistance, and dust resistance are obtained by adhering the surface protection film (1), and the desired surface protection effect is achieved.
第1図は本発明の表面保護フィルム(1)を貼着した液
晶表示パネルの一例を示した断面図である。
(1)・・・保護フィルム、
(2)・・・偏光板、
(21)・・・偏光素膜、
(22)・・・保護板、
(23)・・・感圧性接着剤層、
(3)・・・液晶セル、
(31)・・・基板、
(32)・・・透明電極、
(33)・・・スペーサ、
(34)・・・液晶FIG. 1 is a sectional view showing an example of a liquid crystal display panel to which the surface protection film (1) of the present invention is attached. (1)...protective film, (2)...polarizing plate, (21)...polarizing element film, (22)...protective plate, (23)...pressure sensitive adhesive layer, ( 3)...Liquid crystal cell, (31)...Substrate, (32)...Transparent electrode, (33)...Spacer, (34)...Liquid crystal
Claims (1)
とによって該偏光板(2)表面の保護を図るための保護
フィルム(1)であって、該保護フィルム(1)が、 ガラス転移点50℃以下の樹脂または可塑化樹脂からな
り、偏光板(2)に対し貼着性を有すること、 偏光板(2)に対し貼着する側の面の表面平滑度が0.
1μm以下であること、 レターデーシヨン値が30nm以下、可視光線透過率が
75%以上であること、 の条件を全て満足する光等方性フィルムからなることを
特徴とする液晶表示パネルの表面保護フィルム。[Claims] 1. A protective film (1) for protecting the surface of a polarizing plate (2) of a liquid crystal display panel by pasting it on top of the polarizing plate (2), the protective film (1) is made of a resin or plasticized resin with a glass transition point of 50°C or less, has adhesive properties to the polarizing plate (2), and has a smooth surface on the side to be adhered to the polarizing plate (2). The degree is 0.
A surface protection for a liquid crystal display panel characterized by being made of an optically isotropic film that satisfies all of the following conditions: 1 μm or less, a retardation value of 30 nm or less, and a visible light transmittance of 75% or more. film.