JPH04141304A - Throw away tip - Google Patents
Throw away tipInfo
- Publication number
- JPH04141304A JPH04141304A JP26327790A JP26327790A JPH04141304A JP H04141304 A JPH04141304 A JP H04141304A JP 26327790 A JP26327790 A JP 26327790A JP 26327790 A JP26327790 A JP 26327790A JP H04141304 A JPH04141304 A JP H04141304A
- Authority
- JP
- Japan
- Prior art keywords
- honing
- cutting edge
- portions
- peak
- away tip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
（産業−にの利用分野）
本発明は、スローアウェイチップに関し、特にその切刃
稜にはホーニング処理が施されることにより刃先強化さ
れたものである。DETAILED DESCRIPTION OF THE INVENTION (Field of Industrial Application) The present invention relates to an indexable insert, and in particular, the cutting edge thereof is honed to strengthen the cutting edge.
（従来の技術）
従来、スローアウェイチップの切刃稜に刃先強化を図る
ため、円弧ホーニング、角度ホーニング等を施すことが
行なわれている。そして、特公昭５３− ２５３９２号
公報、特公昭６０− １０８４３弓公報などでは、その
ホーニング量がずくい面側が逃げ面側よりも大きくなる
ようにしたスローアウェイチップが開示されている。こ
の場合、切刃稜に沿う方向では、−・定量になっている
ものである。(Prior Art) Conventionally, in order to strengthen the cutting edge of an indexable insert, arc honing, angle honing, etc. have been performed. Japanese Patent Publications No. 53-25392 and Japanese Patent Publication No. 10843/1984 disclose indexable inserts in which the amount of honing is greater on the flank side than on the flank side. In this case, in the direction along the edge of the cutting edge, the amount is constant.
（発明が解決しようとする課題）
しかしながら、第９図で示されるように被削材（１０）
に対する切込み（ｊが大きく、アップカール気味の切り
くずが発生する切削では、ホーニング量が一定量である
ため、カールした切りくず（１１）が切刃稜（４）に衝
突し、切刃稜（４）が欠ける場合があった。特に、図示
のようにすくい而（５）側で波形を５１する切刃稜（４
）では、切りくずが山部（４ａ）に優先的に衝突し、１
．１．１部（４ａ）が欠けやすいものであった。そして
、欠けを防ぐ最も簡単な方法は、ホーニング処理を施す
ことであるが、ホーニングを大きくすると、同時に耐摩
耗性が低下してしまう問題点があった。(Problem to be solved by the invention) However, as shown in FIG.
In cutting where the depth of cut (j) is large and chips with a slight upcurl are generated, the amount of honing is constant, so the curled chips (11) collide with the cutting edge (4) and the cutting edge ( In particular, the cutting edge (4), which has a waveform of 51 on the rake (5) side as shown in the figure, was sometimes chipped.
), the chips collide preferentially with the mountain part (4a), and 1
．． 1.1 part (4a) was easily chipped. The easiest way to prevent chipping is to perform a honing process, but if the honing process is increased, there is a problem that the wear resistance will decrease at the same time.
このようなことから、本発明では、波形を呈する切刃稜
が備えられたスローアウェイチップにおいて、切りくず
にＪ：る欠けを防ぎ、かつ耐摩耗性を低率させないよう
にホーニング形状を改１９シたものでｉ）る。For this reason, in the present invention, the honing shape has been modified to prevent chips from chipping and to prevent a decrease in wear resistance in an indexable insert equipped with a wavy cutting edge. It is i).
（課題を解決するだめの１段）
発明は、１″述の点に２みなされたもので、山部および
谷部からなる波形の切刃稜を備えたスロアウェイチップ
において、その切刃稜に施されるホーニング処理は、山
部におけるホーニング晴が谷部におけるポ〜ニング：１
；よりも人きくなるように＋ｆ／ｉ成したものである。(One step to solving the problem) The invention is based on the points mentioned in 1. The honing treatment applied to
It is +f/i made to be more personable than ;
（作用）
本発明のスローアウェイチップ！Ｊ、ホーニング処理に
よって耐欠損性が高められ、また山部のホーニング量が
谷部のホーニング：１ｊよりも人きくする構成によって
切りくずのｉ！ＩＩｉ突による１１１部の欠けを防ぐも
のである。また谷部のホーニング量を＋１１部より小さ
くすることで耐摩耗性の低トをてきるだけ防ぐようにし
たものである。(Function) Throw-away tip of the present invention! J. The chipping resistance is improved by the honing process, and the amount of honing on the peaks is more sensitive than the honing on the valleys: 1j, which reduces the amount of chips. This prevents the 111th part from chipping due to IIi impact. Further, by making the amount of honing in the troughs smaller than +11 parts, a drop in wear resistance is prevented as much as possible.
（実施例）
以ト、本発明スローアウェイチップの 実施例について
、図を参照しながら説明する。(Example) Hereinafter, an example of the indexable tip of the present invention will be described with reference to the drawings.
第１図乃至第３図において、（１）は、例えば３角形扱
状をなすスローアウコーイチップであり、その中央ボス
而（２）には、取（−Ｊけ穴（３）が穿設され、その外
部稜線部分には、すくい面側で１１１部（４ａ）お」；
び谷部（４ｂ）を形成するようにした波形の切刃稜（４
）が備えられている３゜
そして、この切刃稜（４）には、ホーニング処理が施さ
れるが、そのホーニング（ｊｔは、第２図おＪ：び第３
図で示されるように山部（４ａ）におけるホーニング」
１１．が谷部（４ｂ）のホーニング宿よりも大きくなっ
ている。この場合、図小では、すくい面（５）側の幅）
、１および１１．て大小関係（＋、、 ｌ＞ １−、２
１が小されている。In Figures 1 to 3, (1) is, for example, a triangular-shaped slow-awake chip, and its central boss (2) has a hole (3) drilled therein. The external ridgeline part has 111 parts (4a) on the rake face side;
The wavy cutting edge (4b) is formed to form a groove (4b).
) and this cutting edge (4) is honed.
Honing at the peak (4a) as shown in the figure
11. is larger than the horning inn in Tanibe (4b). In this case, the width on the rake face (5) side)
, 1 and 11. The magnitude relationship (+,, l> 1-, 2
1 is reduced.
また、第４図乃至第８図では、本発明で適用できるホー
ニング形状がそれぞれ示されている。Further, in FIGS. 4 to 8, honing shapes applicable to the present invention are shown, respectively.
すなわち、第４図では、すくい而（５）側および逃げ面
（６）側で、その幅１．．１”がそれぞれ等しくなるよ
うにした曲率′４６径１≧に」：る円弧型が示されてい
る。また、第５図は、曲率半径をそれぞれＲ，、Ｒ，と
じた大円弧十小円弧Ｊ５す、第６図は、傾斜角θおよび
曲ン平ζｉｔ’径Ｒ，，Ｒ，による角瓜十円弧Ｊ１りが
４＜されている。That is, in FIG. 4, the width of the scoop (5) side and the flank (6) side is 1. ．． A circular arc shape with a radius of curvature of 1 and a diameter of 1 is shown. Furthermore, FIG. 5 shows the large arc and ten small arcs J5 whose curvature radii are R, , R, respectively, and FIG. The arc J1 is 4<.
さらに、第７図は、傾斜角Ｏによる角度型のものであり
、第８図は、すくい而（５）側の幅１５よりも逃げ而（
６）側の幅′「を大きくしたもので、曲率半径Ｒ，，Ｉ
Ｌ２で曲面状とした人円弧十小円弧型のものである１、
なお、本発明のスローアウェイチップでは、ホーニング
：＋；の大きさは、例えばその幅１４でいえばｆｌ、３
ｍｍ以１・て便用されるのが一般的であり、中ても００
３〜Ｔ１．１ｍｍが最も多い９、そして、本発明のスロ
ーアウェイチップでは、内接円φ１２．７ｍｍの場合を
考えると谷部（４ｂ）のホーニング幅Ｉ、２が１４□０
、０３ｍｍ、１１１部（４＋＋）のホーニング幅１１が
１゜０、０５ｍｍ程度の場合、あるいはこれＪ：りも切
削条件をあげたところでは、ｌ ２＝ ０． （１５ｍ
ｍ、１．、＝０．１０ｍｍ程度の組合せが耐欠損性およ
び耐摩耗性をともに満足する。次に、本発明品および従
来品をそれぞれ切削誠験した比較結果について、第１表
および第２表に基づいて説明する。Furthermore, Fig. 7 shows the angle type with the inclination angle O, and Fig. 8 shows the angular type with an inclination angle of O.
6) The side width '' is increased, and the radius of curvature R,,I
In the throw-away tip of the present invention, the size of the honing: +; is, for example, fl, 3 in terms of the width 14.
Generally, it is conveniently used as 1 mm or more, especially 00 mm.
3~T1.1mm is the most common9.And in the indexable tip of the present invention, considering the case where the inscribed circle is φ12.7mm, the honing width I,2 of the valley part (4b) is 14□0
, 03mm, if the honing width 11 of the 111 part (4++) is about 1°0.05mm, or if the cutting conditions are raised, l 2 = 0. (15m
m, 1. , = about 0.10 mm satisfies both chipping resistance and wear resistance. Next, the comparison results of the cutting test of the product of the present invention and the conventional product will be explained based on Tables 1 and 2.
第１表における切削は、切りくずによる耐欠損性を比較
したものである。被削材はＳＣＭ４１５で、スローアウ
コーイチップ（１）の仕様については、いずれもＣＮＭ
Ｇ１２０４圓を基本形状としたデツプブレーカ付きのも
のでｒｉＣ−Ａ℃２０．１の硬質層をコーティングした
ものである。このときの切削条件は、切削速度なｆ５０
ｍ／ｍｉｎ、切込みを４ｍｍ、送りを０５ｍｍ／ｒｃｖ
として５分間切削した。The cutting in Table 1 is a comparison of fracture resistance due to chips. The workpiece material is SCM415, and the specifications of the slow Aukoi tip (1) are CNM.
It has a G1204 round shape as a basic shape and is equipped with a dip breaker, and is coated with a hard layer of riC-A°C of 20.1°C. The cutting conditions at this time are cutting speed f50
m/min, depth of cut 4mm, feed 05mm/rcv
It was cut for 5 minutes.
第１表
この結果は、第１表に示すとおりであり、従来情の欠損
確捧−が８７．５％であったのに対し、本発明’ｉ７＋
の欠損確ヰは０％であった。Table 1 The results are as shown in Table 1, and while the deficit confirmation of the conventional information was 87.5%, the present invention'i7+
The probability of loss was 0%.
また、第２表における切削は、耐摩耗性を比較したもの
であるが、第１表の条件と異なるのは、１、ＩおよびＩ
、２の数値を変更したこと、被削材を３４５Ｃ１送りを
０．３ ｍｍ／ｒｅｖとして３０分間切削した点のみで
ある。この場合、被削材を３４５Ｇとしたのは、硬度を
高めて耐摩耗性の優劣に差をつけるためである。In addition, the cutting conditions in Table 2 compare the wear resistance, but the conditions that differ from those in Table 1 are 1, I, and I.
, 2 were changed, and the work material was cut for 30 minutes with a 345C1 feed of 0.3 mm/rev. In this case, the reason why the work material was 345G was to increase the hardness and differentiate the wear resistance.
第２表
（発明の効果）
本発明は、以」二説明したように、すくい面側で１１１
部（４ａ）および谷部（４ｂ）を形成するようにした波
形を有する切刃稜（４）が備えられているスロアウェイ
チップにおいて、山部（４ａ）におけるホニング量が谷
部（４ｂ）のホーニング量よりも大きくなっているよう
に構成したものである。Table 2 (Effects of the Invention) As explained below, the present invention has a
In the throw-away insert, which is provided with a cutting edge ridge (4) having a waveform forming a portion (4a) and a trough portion (4b), the amount of honing at the crest portion (4a) is equal to that of the trough portion (4b). The honing amount is larger than the honing amount.
したがって、本発明では、山部（４ａ）の切りくずの衝
突による欠けが防止され、また谷部（４ｂ）のホニング
Ｈ，１が山部（４ａ）のホーニング砒よりも小さいこと
で耐摩耗性の低−ドが抑制される利点を有する。Therefore, in the present invention, chipping due to collision of chips at the peaks (4a) is prevented, and the honing H,1 at the valleys (4b) is smaller than the honing arsenal at the peaks (4a), thereby improving wear resistance. This has the advantage of suppressing the low voltage.
第１図（ａ） （ｂｌは、本発明スローアウェイチップ
の−・実施例を示す図であり、第１図ｆａｔ は正面図
、第１図ｆｂｌは一部側面図、第２図は、第１図ｆａｌ
中のＩＩ −ＩＩ線に沿って得られる−６（＜拡大断面
図、第３図は、同じく第１図（ａ）中の＋ｎ−ｍ線に沿
って得られる一部拡大断面図、第４図〜第８図は、本発
明に適用できるホーニング形状をそれぞれ示した一部拡
大断面図、第９図は、切削状態を示す概念図である。
（１）・・・スローアウェイチップ
（４）・・・切刃稜 （４ａ）・・・
＋１．＋部（４ｂ）・・・各部分 （
５）・・・すくい面（６）・・・逃げ面Fig. 1 (a) (bl is a diagram showing an embodiment of the indexable tip of the present invention, Fig. 1 (fat) is a front view, Fig. 1 (fbl) is a partial side view, and Fig. 2 is a 1 figure fal
-6 (<enlarged sectional view, Figure 3 is a partially enlarged sectional view taken along the +n-m line in Figure 1(a), 8 are partially enlarged cross-sectional views showing honing shapes applicable to the present invention, and FIG. 9 is a conceptual diagram showing the cutting state. (1) Throwaway tip (4) ... Cutting edge ridge (4a)...
+1. + part (4b)...each part (
5) Rake face (6) Relief face
Claims (1)
、すくい面（５）側で山部（４ａ）および谷部（４ｂ）
を構成するようにした波形の切刃稜（４）が備えられて
いるスローアウェイチップにおいて、前記切刃稜（４）
に施されるホーニング処理は、波形の山部に（４ａ）に
おけるホーニング量が谷部（４ｂ）のホーニング量より
も大きくなっていることを特徴とするスローアウェイチ
ップ。It is composed of a circular plate and a polygonal plate shape, and its external ridgeline portion has peaks (4a) and valleys (4b) on the rake face (5) side.
In the indexable insert provided with a wave-shaped cutting edge ridge (4), the cutting edge ridge (4)
The honing treatment applied to the indexable tip is such that the amount of honing at the crests (4a) of the waveform is greater than the amount of honing at the troughs (4b).