JPH03198857A - 抗菌脱臭性組成物 - Google Patents
抗菌脱臭性組成物Info
- Publication number
- JPH03198857A JPH03198857A JP1336314A JP33631489A JPH03198857A JP H03198857 A JPH03198857 A JP H03198857A JP 1336314 A JP1336314 A JP 1336314A JP 33631489 A JP33631489 A JP 33631489A JP H03198857 A JPH03198857 A JP H03198857A
- Authority
- JP
- Japan
- Prior art keywords
- allophane
- silver
- copper
- zinc
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は持続性のある抗菌性と脱臭性を兼ね備えた組成
物に関する。
物に関する。
銀、銅、亜鉛など一部の金属又は金属イオンに殺菌性が
あることはよく知られている。これらを活性炭などを担
体として担持しても、単に物理的に吸着されているため
溶剤や熱的或いは機械的外力によって容易に担体よシ離
脱して長期間の使用に耐えない。
あることはよく知られている。これらを活性炭などを担
体として担持しても、単に物理的に吸着されているため
溶剤や熱的或いは機械的外力によって容易に担体よシ離
脱して長期間の使用に耐えない。
また近時担体にゼオライトを使用し、ゼオライトのイオ
ン交換能によシ銀、銅、亜鉛などを置換した抗菌性組成
物が開発されたが、脱臭作用は充分でない。殺菌を要す
る箇所には異臭を伴うことが多く、従って殺菌と同時に
脱臭作用があることが望ましい。
ン交換能によシ銀、銅、亜鉛などを置換した抗菌性組成
物が開発されたが、脱臭作用は充分でない。殺菌を要す
る箇所には異臭を伴うことが多く、従って殺菌と同時に
脱臭作用があることが望ましい。
本発明者は上記の事情に鑑み、殺菌と同時に脱臭性を有
する組成物の開発につき鋭意研究を重ねた結果、非晶質
のアルミナシリケートであるアロフェンを基材として使
用することにより目的を達し、本発明を完成した。
する組成物の開発につき鋭意研究を重ねた結果、非晶質
のアルミナシリケートであるアロフェンを基材として使
用することにより目的を達し、本発明を完成した。
すなわち本発明はアロフェンを基体とし、アロフェンの
成分の一部を銀、銅及び亜鉛から選ばれた少なくとも一
種の金属と反応置換して成る抗菌脱臭性組成物である。
成分の一部を銀、銅及び亜鉛から選ばれた少なくとも一
種の金属と反応置換して成る抗菌脱臭性組成物である。
本発明で使用されるアロフェンは天然に存在する鉱石の
一種でありシリカ−アルミナ質ゲル状粘土である。鉱物
学上該粘土は結晶性シリカ−アルミナ金属塩の鉱石から
自然界での風化により生ずるものであり、従ってカオリ
ナイトやゼオライトとは非晶質であることに於て明確に
区別される。
一種でありシリカ−アルミナ質ゲル状粘土である。鉱物
学上該粘土は結晶性シリカ−アルミナ金属塩の鉱石から
自然界での風化により生ずるものであり、従ってカオリ
ナイトやゼオライトとは非晶質であることに於て明確に
区別される。
本発明に用いるアロフェンは天然産のアロフェンをその
まま若しくは精製して用いることができ、また人工的に
合成しても用いられる。アロフェンは表面積が200〜
300rr?/9を有する微粉であるので、特に微粉砕
する必要はなく、そのまま使用できる。
まま若しくは精製して用いることができ、また人工的に
合成しても用いられる。アロフェンは表面積が200〜
300rr?/9を有する微粉であるので、特に微粉砕
する必要はなく、そのまま使用できる。
アロフェンは構造上及び組成上から
(1)多孔性吸着体であり、アンモニア、アミン類、硫
化水素、メルカプタン類などの各種悪臭ガスに対する吸
着能を有するが、その成分の一部に銀、銅、亜鉛等の導
入により、さらに硫化水素、メルカプタン類の如き酸性
ガスとの化学反応性が強化され、それぞれの金属の硫化
物を生成し、固定されることにより強力な脱臭効果が助
長される。
化水素、メルカプタン類などの各種悪臭ガスに対する吸
着能を有するが、その成分の一部に銀、銅、亜鉛等の導
入により、さらに硫化水素、メルカプタン類の如き酸性
ガスとの化学反応性が強化され、それぞれの金属の硫化
物を生成し、固定されることにより強力な脱臭効果が助
長される。
(2)両性イオン反応性を有するので銀、銅、亜鉛等の
酸性水溶性塩との反応により、その成分の一部に酸性基
が導入されるので、アンモニア、アミン類の如き塩基性
ガスとの化学反応性が強化され、強力な脱臭効果を示す
。
酸性水溶性塩との反応により、その成分の一部に酸性基
が導入されるので、アンモニア、アミン類の如き塩基性
ガスとの化学反応性が強化され、強力な脱臭効果を示す
。
このように悪臭ガスが酸性物質であろうと、塩基性物質
であろうと銀、銅、亜鉛等の金属との反応置換でアロフ
ェンの成分の一部に導入されることにより、アロフェン
が本来有している吸着能が一層強化助長され、銀、銅、
亜鉛による殺菌作用のみならず、強力な脱臭が行われる
のである。
であろうと銀、銅、亜鉛等の金属との反応置換でアロフ
ェンの成分の一部に導入されることにより、アロフェン
が本来有している吸着能が一層強化助長され、銀、銅、
亜鉛による殺菌作用のみならず、強力な脱臭が行われる
のである。
銀、銅、亜鉛の添加は酸性水溶性塩の形で行うのが好ま
しく、銀は硝酸銀、銅は硝酸銅、硫酸銅、塩化銅、酢酸
銅、亜鉛は硝酸亜鉛、硫酸亜鉛、塩化亜鉛、酢酸亜鉛が
好適であるが、これらに限定されるものではない。
しく、銀は硝酸銀、銅は硝酸銅、硫酸銅、塩化銅、酢酸
銅、亜鉛は硝酸亜鉛、硫酸亜鉛、塩化亜鉛、酢酸亜鉛が
好適であるが、これらに限定されるものではない。
アロフェンへの添加量はO3σ01〜3重量俤が好まし
く、0.661重量重量溝では効果が少なく、3重量チ
を超えては金属によっては置換可能量に近く、かつ大量
の添加は不経済である。
く、0.661重量重量溝では効果が少なく、3重量チ
を超えては金属によっては置換可能量に近く、かつ大量
の添加は不経済である。
本発明の組成物の製造法の一例を示せば、アロフェノ粉
末を金属の酸性水溶性塩の希薄溶液に投入し、加温又は
加温せずに一定時間攪拌した後、アロフェンを濾過し水
洗する。水洗は水洗液中に金属イオンがなくなる迄行い
、その後一定温度に加温して乾燥すれば組成物が粉末の
形で得られる。更に必要に応じて活性化処理或は焼成処
理される。
末を金属の酸性水溶性塩の希薄溶液に投入し、加温又は
加温せずに一定時間攪拌した後、アロフェンを濾過し水
洗する。水洗は水洗液中に金属イオンがなくなる迄行い
、その後一定温度に加温して乾燥すれば組成物が粉末の
形で得られる。更に必要に応じて活性化処理或は焼成処
理される。
又本粉末は結合剤を用いずとも成型可能であるが、さら
にカルホキ/メチルセルロース、ポリビニルアルコール
等の有機系或は水ガラス等の無機系結合剤を用いて混練
し、ベレット、タブレット等に成型し、乾燥活性化処理
するか、焼成処理して成形品とすることも可能である。
にカルホキ/メチルセルロース、ポリビニルアルコール
等の有機系或は水ガラス等の無機系結合剤を用いて混練
し、ベレット、タブレット等に成型し、乾燥活性化処理
するか、焼成処理して成形品とすることも可能である。
このように粉末その1ま、或は水に懸濁して噴霧するこ
とも可能であり、又成形体として使用できるので各種の
用途及び箇所に使用可能である。例えば壁紙などの紙類
、不織布、布団、靴下などの繊維類への適用や、靴の中
敷や冷蔵庫の脱臭剤として粉末のみならずシート状、ベ
レット等の形体で使用可能であるし、養魚用、生花用や
水処理関係のほかプラスチック容器、フィルム、押入れ
などの抗菌脱臭などに有用である。さらに船底塗料や浴
場の塗料などの塗料類、漁網などにも使用可能で、その
応用範囲は広い。
とも可能であり、又成形体として使用できるので各種の
用途及び箇所に使用可能である。例えば壁紙などの紙類
、不織布、布団、靴下などの繊維類への適用や、靴の中
敷や冷蔵庫の脱臭剤として粉末のみならずシート状、ベ
レット等の形体で使用可能であるし、養魚用、生花用や
水処理関係のほかプラスチック容器、フィルム、押入れ
などの抗菌脱臭などに有用である。さらに船底塗料や浴
場の塗料などの塗料類、漁網などにも使用可能で、その
応用範囲は広い。
抗菌作用について
アロフェン基体はその構成成分中に金属イオンと置換可
能な酸性基と陰イオンと置換可能な水酸基の両者を保有
して居り、置換交換反応により対応する化学結合を生ず
る。
能な酸性基と陰イオンと置換可能な水酸基の両者を保有
して居り、置換交換反応により対応する化学結合を生ず
る。
このアロフェン基体は広表面績であり化学結合せる金属
がイオン解離する事により効率的抗菌作用を呈するもの
と思考される。且つ又アロフェン基体に化学績合せる陰
イオンも解離し抗菌作用を助けているものと思考される
。
がイオン解離する事により効率的抗菌作用を呈するもの
と思考される。且つ又アロフェン基体に化学績合せる陰
イオンも解離し抗菌作用を助けているものと思考される
。
アロフェンそのものは水に不溶性であり、この置換交換
反応物も水中に於ても極めて溶出が少いだめ長期間、水
中に於てもその抗菌効果を持続するものである。
反応物も水中に於ても極めて溶出が少いだめ長期間、水
中に於てもその抗菌効果を持続するものである。
脱臭作用について
アロフェンはゼオライトと異なり非晶質の/リカ、アル
ミナゲルであり、気孔径の分布をゼオライトと異にし極
めて幅広い分布を有する。従って分子の大きさの異なる
各種成分、多成分の悪臭ガスを吸着する特性を有するが
、上記金属イオンの置換導入、陰イオンの置換導入によ
り、夫々酸性ガス、塩基性ガスとの反応固定化が可能と
なる事により更に脱臭性能が強化されるものと思考され
る。
ミナゲルであり、気孔径の分布をゼオライトと異にし極
めて幅広い分布を有する。従って分子の大きさの異なる
各種成分、多成分の悪臭ガスを吸着する特性を有するが
、上記金属イオンの置換導入、陰イオンの置換導入によ
り、夫々酸性ガス、塩基性ガスとの反応固定化が可能と
なる事により更に脱臭性能が強化されるものと思考され
る。
実施例1(製造例)
200≠通過のアロフェン粉末2507を硝酸銀の5チ
水溶液に投入し室温下で12時間攪拌した。反応終了後
アロフェンを1過し水洗した。
水溶液に投入し室温下で12時間攪拌した。反応終了後
アロフェンを1過し水洗した。
水洗は水洗液中に銀イオンが塩化銀試薬で認められなく
なる迄行い、終了すれば引続き120℃で乾燥し、銀含
有アロフェンを得た。
なる迄行い、終了すれば引続き120℃で乾燥し、銀含
有アロフェンを得た。
収量は2207、銀金量は2.3重量係であった。
(試験例)
細菌としてBacillus 5ubtilis AT
CC6633、Escherichia coli
IFO3301、カビとしてAspergillus
niger IFO4407、Penicilli
umゆ c+ tr+ um JFO7784を用い実施例1で
得だ粉末組成物を任意濃度にして添加した液体培地に接
種用菌液を接種培養した。
CC6633、Escherichia coli
IFO3301、カビとしてAspergillus
niger IFO4407、Penicilli
umゆ c+ tr+ um JFO7784を用い実施例1で
得だ粉末組成物を任意濃度にして添加した液体培地に接
種用菌液を接種培養した。
なお接種用菌液は細菌については、継代培養した試験菌
をMueller Hinton Broth(Dir
co)の増菌用培地に接種し35℃、18〜20時間培
養後、菌数が約10〜 になるように増菌用培地で希釈
したものを使用した。又カビについては、継代培養した
試験菌をポテトデキストロース寒天培地の増菌用培地に
接種し25℃、10日間培養後、形成した胞子(分生子
)を滅菌0.05%ポリソルベート80水溶液に約10
’//ff17!になるよう浮遊させたものを使用した
。
をMueller Hinton Broth(Dir
co)の増菌用培地に接種し35℃、18〜20時間培
養後、菌数が約10〜 になるように増菌用培地で希釈
したものを使用した。又カビについては、継代培養した
試験菌をポテトデキストロース寒天培地の増菌用培地に
接種し25℃、10日間培養後、形成した胞子(分生子
)を滅菌0.05%ポリソルベート80水溶液に約10
’//ff17!になるよう浮遊させたものを使用した
。
培養後、発育が阻止される最低濃度をもって最小発育阻
止濃度とした。その結果は第1表に示すとおりである。
止濃度とした。その結果は第1表に示すとおりである。
第 1 表
試 験 菌 最小発育阻止濃度(係)Ba
cillus 5ubtilis O
,06Escherichia coli
Q、OLAspergillus nige
r O,06Penic
illum citrinum Ooo
3実施例2 実施例1の硝酸銀の代りに硝酸銅3係、硝酸銀3.5係
を用いたほか実施例1と同様にして金属含有アロフェン
組成物を得た。銅の含有量は1.2係、銀の含有量は1
.9チであった。
cillus 5ubtilis O
,06Escherichia coli
Q、OLAspergillus nige
r O,06Penic
illum citrinum Ooo
3実施例2 実施例1の硝酸銀の代りに硝酸銅3係、硝酸銀3.5係
を用いたほか実施例1と同様にして金属含有アロフェン
組成物を得た。銅の含有量は1.2係、銀の含有量は1
.9チであった。
これらの組成物について実施例1と同様にして最小発育
阻止濃度を試験した。結果は第2表に示すとおりである
。
阻止濃度を試験した。結果は第2表に示すとおりである
。
(以 下 余 白 )
第 2 表
試 験 菌 最小発育阻止濃度(チ)Bac
illus 5ubtilis Q、0
6Bscherichia coli
Q、Q 2Aspergillus niger
Q、Q 6Penicillum citr
inum Q Q 5実施例3 本発明実施例1.2の脱臭剤を500C,c、の気密ビ
ンに12とり所定の悪臭ガスを注入後、4時間静置し気
中、残留悪臭成分を測定した。
illus 5ubtilis Q、0
6Bscherichia coli
Q、Q 2Aspergillus niger
Q、Q 6Penicillum citr
inum Q Q 5実施例3 本発明実施例1.2の脱臭剤を500C,c、の気密ビ
ンに12とり所定の悪臭ガスを注入後、4時間静置し気
中、残留悪臭成分を測定した。
尚比較のため、アロフェン単独、活性炭の測定結果を比
較のため掲げた。
較のため掲げた。
(以 下 余 白 )
〔発明の効果〕
本発明の抗菌脱臭性組成物は細菌類、カビ類に対し抗菌
防黴作用を有する。本発明組成物は不溶性であり、水に
対し金属イオンの溶出が極微量であるため長期間効果が
持続する。さらに粉末状態では勿論、焼成処理した成形
体はすべて無機物質から構成されるので熱的にも安定で
作用効果を失わない。
防黴作用を有する。本発明組成物は不溶性であり、水に
対し金属イオンの溶出が極微量であるため長期間効果が
持続する。さらに粉末状態では勿論、焼成処理した成形
体はすべて無機物質から構成されるので熱的にも安定で
作用効果を失わない。
Claims (1)
- 【特許請求の範囲】 1、アロフェンを基体とし、アロフェンの成分の一部を
銀、銅及び亜鉛から選ばれた少なくとも一種の金属と反
応置換して成る抗菌脱臭性組成物 2、請求項1項記載の粉体状抗菌脱臭性組成物を結合剤
を用いるか又は用いないで混練成形した後、乾燥活性化
処理するか、又は焼成処理する抗菌脱臭組成物成形体